Patent Application
20210404125
Described herein are thermoplastic compositions for applying to a substrate, for example pavement. In some aspects, the compositions described herein can be useful for sealing joints in pavement.
A longitudinal joint occurs in pavement where a first application of one material, for example, asphalt, is laid adjacent to a second application of a material, for example, an existing lane of asphalt or a second application of new asphalt. The joint is the interface between the materials applied in the two applications. Over time, a longitudinal crack can occur between the two surfaces, permitting the intrusion of water into the pavement, increasing roughness of the pavement, and thus limiting the life of the pavement.
A traverse joint occurs in an asphalt pavement when the paving operation is interrupted for an extended period of time or a portion of the roadway must be repaired after subsurface infrastructure repairs, such as cutting out a road section to repair a subterranean water line.
Conventional sealant materials for the joint of a roadway include applying a tack coat that usually consists of asphalt cement, an emulsion, or hot poured, rubberized asphalt sealer. These conventional sealants require substantial application time and result in significant delays in the use of the roadway. This delay is especially unwelcomed for longitudinal joints where a large portion of the roadway may be closed to normal traffic patterns until the seal of the joint has cured. An improved composition for sealing the joint of a roadway, and methods for applying the same, to provide a stronger seal with reduced downtime for application to the roadway is desired.
This summary is a high-level overview of various aspects of the invention and introduces some of the concepts that are further described in the Detailed Description section below. This summary is not intended to identify key or essential features of the claimed subject matter, nor is it intended to be used in isolation to determine the scope of the claimed subject matter. The subject matter should be understood by reference to appropriate portions of the entire specification, any or all drawings and each claim.
Described herein are thermoplastic compositions for sealing longitudinal joints of different pavement materials, for example asphalt. In some examples, the thermoplastic compositions may comprise a polyamide resin, a modified rosin ester, a modified gum rosin, a pigment, a wax, a plasticizer, and an inorganic filler. In some examples, the pigment may comprise carbon black. Optionally, the thermoplastic compositions may further comprise a copolymer, an antioxidant, and a light stabilizer. In some examples, the copolymer may comprise ethylene vinyl acetate and ethylene maleic anhydride. In some examples, the wax may comprise polyethylene wax. In some examples, the light stabilizer comprises a hindered amine, or hindered amine light stabilizer (HALS). In some examples, the plasticizer comprises one or more of castor oils, other naturally-occurring oils, di-isononyl phthalate, or other phthalates plasticizers. In some examples, the inorganic filler comprises at least one of calcium carbonate, silica, quartzite, marble grit, glass powder, glass cullet, and alumina. In some examples, the thermoplastic composition may further comprise an aggregate which may modify the texture of the seal to increase the roughness and provide a safer non-slip surface at the sealed joint. In some cases, the thermoplastic composition may further comprise an aggregate which may modify the appearance of the seal, specifically, the level of gloss of the seal.
In some examples, a thermoplastic composition for sealing roadway joints, comprising the thermoplastic composition described herein, may be applied to a roadway to form a barrier over a longitudinal joint that is substantially parallel to and located between adjacent lanes of a roadway. In some examples, the thermoplastic composition may protect the edge of the lanes of the roadway from deterioration. Deterioration can include cracking and raveling of the edge of the lane that permits intrusion of water, increases roughness, and limits the life of the roadway.
Also described are methods to make the thermoplastic compositions described herein. In some examples, the method of making a thermoplastic composition comprises adding at least one of a rosin-modified ester or a modified gum rosin to a vessel, adding a wax to the vessel, adding a polyamide resin to the vessel, adding a plasticizer to the vessel, adding a first charge of an inorganic filler to the vessel, adding a second charge of an inorganic filler to the vessel, and mixing the composition. Optionally, the method of making a thermoplastic composition may further comprise adding a copolymer to the vessel, adding an antioxidant to the vessel, and adding a light stabilizer to the vessel.
Also described are methods of using the thermoplastic composition described herein to seal roadway joints. In some examples, a method of sealing roadway joints comprises: (a) heating a thermoplastic composition, where the thermoplastic composition is mixed during the heating, where the mixing is performed by at least one of auger, agitation, or recirculation; and (b) applying the heated thermoplastic composition to a roadway joint, where the thermoplastic composition is applied by extruding, spraying, or other application to the roadway joint, where the roadway joint comprises a longitudinal joint that is substantially parallel to and located between adjacent lanes of a roadway.
The details of one or more embodiments are set forth in the description below. Other features, objects, and advantages will be apparent from the description and from the claims.
Provided herein are thermoplastic compositions and methods that can be used to seal joints, especially longitudinal joints, in asphalt or concrete pavement and roadways. A longitudinal joint occurs, for example, in an asphalt pavement when a first application of asphalt is laid adjacent to a second application of asphalt, for example in some cases, a first lane and a second lane. Paving the width of a roadway in multiple lanes is generally required because paving the full width of the pavement in a single pass is usually impossible. Most single pavers are not wide enough to pave the width of a roadway, thus a seam or joint is created between paving lanes. The joint is the interface between the two asphalt applications, for example, between a first hot-mix asphalt (HMA) mat and a second hot-mix asphalt mat. In some cases, differences in the temperature and mat plasticity can cause an improper bonding of the first and second asphalt applications. For example, the bonding between a fresh application of HMA and an older asphalt lane can cause the longitudinal joint to possess a significantly lower density than the rest of the pavement. Over time, a longitudinal crack usually occurs between the asphalt mats, permitting the intrusion of water, increasing roughness, and potentially limiting the life of the pavement.
In some cases, the quality of the joint may be improved by creating hot joints, which are produced when the adjacent lanes are paved in echelon, i.e. when two pavers are spaced so that the first lane does not cool significantly before the second lane is laid. A hot joint can be essentially seamless and produces higher density joint region when compared to the other joints. However, creating hot joints requires the simultaneous paving of multiple lanes, which is generally not feasible as such paving requires closing of multiple lanes. Not only do work zones constrict traffic flow, but the capacity of asphalt production equipment is often limited to feeding no more than one paver at a time. With these limitations, cold joints are often created during paving projects.
A cold joint is produced when the first paved lane has cooled before the adjacent lane is placed to match it. The temperature gradient at the joint may cause a significant density gradient between the two mats on either side of the joint and result in very low strength in the joint or interface between the two mats. After a short period of time under traffic use, cold joints tend to ravel. In some cases, the raveling may be severe enough to completely erode the mix at the joint. Also, the low density at this joint can permit the seepage of water into the joint which could oxidize the bituminous material. Additional disadvantages with cold joints can include the inability to apply lane markings on the joint.
Conventional sealant materials for the longitudinal joint of a roadway include applying a tack coat that can consist of asphalt cement, emulsion, or hot poured, rubberized asphalt sealer. These conventional sealants require substantial application time and result in significant delays in the use of the roadway. In some cases, a conventional sealant may prevent use of the newly sealed roadway for 30 minutes or more. An improved seal of the longitudinal joint of a roadway that provides a stronger seal with reduced downtime to the roadway for application of the sealant is desirable. A sealant that may be applied without closure of the roadway is desirable. A sealant that allows for immediate application of lane markings is desirable.
According to the Federal Highway Administration, in 2013, there were 4.12 million miles of road in the United States, including Alaska and Hawaii. The core of the nation's highway system is the nearly 48,000 miles of Interstate Highways, which comprise just over 1 percent of highway mileage, but carry one-quarter of all highway traffic. The Interstates plus another 179,650 miles of major roads comprise the National Highway System, which carries most of the highway freight and traffic in the U.S. Of the over 4 million miles of road, about 2.68 million miles are paved. Thus, there is need for an improved composition to seal the longitudinal joints along the millions of miles of highway. This improved joint seal may prolong the life of the sealed roadway and delay costs of resurfacing beyond the expected 10-15 year timeframe.
The composition described herein includes a thermoplastic composition that may have superior properties to conventional sealant materials in the performance of the joint. In some aspects, the thermoplastic compositions described herein can provide limited disruption to traffic use of the roadway. In some aspects, the thermoplastic compositions described herein can minimize negative impacts on the environment and the health and safety of related personnel. The thermoplastic composition described herein comprises 100% solid materials that become a fluid when heated by equipment at the site of application. The thermoplastic composition may be applied in a variety of forms and can rapidly change from fluid phase to a durable solid phase so that it mechanically adheres to a surface when the temperature decreases below the melt temperature of the thermoplastic. Thermoplastics may be hydrocarbon-based, i.e., made from petroleum-derived resins, or alkyd-based, i.e., made from wood-derived resins, a renewable natural resource. Alkyd-based resins can be virtually impervious to oil and diesel fuels, which make them desirable for use in applications exposed to petroleum products. The thermoplastic compositions described herein can be alkyd-based.
In some examples, the composition can be a thermoplastic with fast application times that may minimize disruption to traffic due to construction zones. In some examples, the thermoplastic composition may be sufficiently tack-free in less than 5 minutes, for example, less than 4 minutes, 3 minutes, 2 minutes, or 1 minute, after application of the thermoplastic composition. In some aspects, this fast application time can allow use of the roadway after expiration of this short period of time. In some aspects, other roadway markings can be applied to thermoplastic compositions used to provide the joint seal. In some cases, roadway markings, for example yellow or white lane markings, can be applied to the thermoplastic compositions after the composition is applied, for example after 5 minutes, 4 minutes, 3 minutes, 2 minutes, or 1 minute. The immediacy of the application of roadway markings may provide a significant increase in highway safety and convenience by minimizing disruption of roadway closures.
Furthermore, the thermoplastic composition may provide improved visibility of roadway marking, especially on bridges and roadways with older asphalt that have a lighter color. In some cases, as asphalt ages, the density of the asphalt may change and the asphalt may become lighter in color. This lighter color, especially on bridge decks, reduces the contrast between the roadway and the safety markings on the roadway, for example, a light colored asphalt may have a washed out, white appearance and the road marking have a white color. During certain portions of the day, the two surfaces may not have a sufficient degree of contrast between the two so that a motorist can easily detect the lane marking. Such decrease in contrast can reduce highway safety.
In contrast,
Also described herein are methods of making the thermoplastic composition and methods of using the thermoplastic composition described herein to seal longitudinal joints in pavement.
Compositions and properties of the compositions
In some examples, a thermoplastic composition comprises a polyamide resin, a copolymer, at least one of a rosin-modified ester or a modified gum rosin, a pigment, a wax, an antioxidant, a light stabilizer, a plasticizer, and an inorganic filler. The composition may further comprise at least one of a co-polymer, an antioxidant, or a light stabilizer.
In some examples, a thermoplastic composition comprises a polyamide resin, a copolymer, at least one of a rosin-modified ester or a modified gum rosin, a pigment, a wax, an antioxidant, a light stabilizer, a plasticizer, and an inorganic filler. The pigment may provide color and opacity to the composition. The inorganic filler may add bulk to the composition and provide a composition that has greater elongation properties. The plasticizer and resins may provide toughness, flexibility, and bond strength to the composition, while binding together all the components of thermoplastic composition.
In some embodiments, the thermoplastic composition described herein comprises a polyamide resin in an amount of from about 2 to about 30% (e.g., from 2 to 20%, from 5 to 25%, or from 10 to 20%). In some examples, the thermoplastic composition may include about 2%, 3 %, 4 %, 5 %, 6 %, 7 %, 8 %, 9 %, 10 %, 12 %, 14 %, 16 %, 18 %, 20 %, 22 %, 24 %, 26%, 28%, or 30% polyamide resin. All are expressed in wt. %. In some embodiments, the polyamide resin comprises at least one of polyolefin elastomers, polypropylene copolymers, styrene-butadiene-styrene (SBS) polymers, and styrene-isoprene-styrene (SIS) polymers.
In some embodiments, the thermoplastic composition described herein comprises a copolymer in an amount up to 10% (e.g., from 0 to 5%, from 0.2 to 2.5%, from 0.8 to 2.5%, or from 1 to 6%). In some examples, the thermoplastic composition may include about 0.1%, 0.2%, 0.4%, 0.6%, 0.8%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, 5.5%, 6%, 6.5%, 7%, 7.5%, 8%, 8.5%, 9%, 9.5% or 10% copolymer. All are expressed in wt. %. In certain embodiments, the composition may be substantially free of a copolymer. In some embodiments, the copolymer comprises at least one of ethylene vinyl acetate and ethylene maleic anhydride.
In some embodiments, the thermoplastic composition described herein comprises a rosin-modified ester in an amount up to about 40 wt. % (e.g., from 5 to 15%, from 3 to 18%, or 11 to 25%). In some examples, the thermoplastic composition may include about 1%, 2%, 3%, 4% 5 %, 6 %, 7 %, 8 %, 9 %, 10 %, 12 %, 14 %, 16 %, 18 %, 20 %, 22 %, 24 %, 26 %, 28 %, 30 %, 32%, 34%, 36%, 38% or 40% rosin-modified ester. All are expressed in wt. %. In certain embodiments, the composition may be substantially free of rosin-modified esters. In some embodiments, modified rosin ester comprises tall oil esters, maleic rosin ester, pentaerythritol rosin ester, glycerol rosin ester, disproportionated rosin ester, hydrogenated rosin, or polymerized rosin.
In some embodiments, the thermoplastic composition described herein comprises a modified gum rosin in an amount up to about 40 wt. % (e.g., from 5 to 25%, from 2 to 15%, from 3 to 18%, or from 11 to 25%). In some examples, the thermoplastic composition may include about 1%, 2%, 3%, 4% 5%, 6%, 7%, 8%, 9%, 10%, 12%, 14%, 16%, 18%, 20%, 22%, 24%, 26%, 28%, 30%, 32%, 34%, 36%, 38% or 40% modified gum rosin. All are expressed in wt. %. In certain embodiments, the composition may be substantially free of modified gum rosins. In some embodiments, modified gum rosin comprises glyceryl hydrogenated rosin, rosin modified phenolic resin, pentaerythrityl rosin, glyceryl rosin, disproportionated rosin, polymerized rosin or hydrogenated rosin.
In some embodiments, the thermoplastic composition described herein comprises pigment in an amount of from about 0.1 to about 10 wt. % (e.g., from 0.2 to 1.2%, 0.5 to 2%, or 2 to 5%). In some examples, the thermoplastic composition may include about 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5 %, 5.5%, 6 %, 6.5%, 7 %, 7.5%, 8 %, 8.5%, 9 %, 9.5%, or 10 % pigment. All are expressed in wt. %. In some embodiments, the pigment may comprise carbon black.
In some embodiments, the thermoplastic composition described herein comprises wax in an amount of up to about 20 wt. % (e.g., from 0.5 to 5%, from 1 to 4%, from 1 to 8%, or 5 to 10%) . In some examples, the thermoplastic composition may include about 0.5%, 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 12%, 14%, 16%, 18%, or 20% wax. All are expressed in wt. %. In some embodiments, the wax may comprise polyethylene wax, functionalized PE wax, polypropylene wax and similar formulations.
In some embodiments, the thermoplastic composition described herein comprises an antioxidant in an amount of up to about 3 wt. % (e.g., from 0.1 to 0.4%, from 0.8 to 2%, or 0 to 3%). In some examples, the thermoplastic composition may include about 0.05%, 0.1%, 0.15%, 0.2%, 0.4%, 0.6%, 0.8%, 1%, 1.2%, 1.4%, 1.6%, 1.8%, 2%, 2.2%, 2.4%, 2.5%, 2.6%, 2.7%, 2.8%, 2.9%, or 3% antioxidant. All are expressed in wt. %. In certain embodiments, the composition may be substantially free of an antioxidant.
In some embodiments, the thermoplastic composition described herein comprises a light stabilizer in an amount of up to about 3.5 wt. % (e.g., from 0.2 to 1.6%, from 0.6 to 2.5%, or 0 to 3%). In some examples, the thermoplastic composition may include about 0.05%, 0.1%, 0.2%, 0.4%, 0.6%, 0.8%, 1%, 1.2%, 1.4%, 1.6%, 1.8%, 2%, 2.2%, 2.4%, 2.6%, 2.8%, 3%, 3.2%, 3.4%, or 3.5% light stabilizer. All are expressed in wt. %. In certain embodiments, the composition may be substantially free of a light stabilizer. In some embodiments, the light stabilizer comprises a hindered amine, or hindered amine light stabilizer (HALS).
In some embodiments, the thermoplastic composition described herein comprises a plasticizer in an amount of up to about 10 wt. % (e.g., from 1 to 4%, from 1 to 5%, or from 3 to 7%). In some examples, the thermoplastic composition may include about 0.5%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, 5.5%, 6%, 6.5%, 7%, 7.5%, 8%, 8.5%, 9%, 9.5%, or 10% plasticizer. All are expressed in wt. %. In some embodiments, the plasticizer comprises one or more of castor oils, other naturally-occurring oils, di-isononyl phthalate, or other phthalates plasticizers.
In some embodiments, the thermoplastic composition described herein comprises an inorganic filler in an amount of from about 5 to about 90 wt. % (e.g., from 10 to 50%, from 20 to 50%, or from 40 to 60%). In some examples, the thermoplastic composition may include about 5%, 10%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, or 90% inorganic filler. All are expressed in wt. %. In some embodiments, the inorganic filler comprises one or more of calcium carbonate, silica, quartzite, marble grit, glass powder, glass cullet, and alumina.
In some embodiments, the thermoplastic composition described herein comprises 3 to 10 wt. % polyamide resin, 0.7 to 3 wt. % copolymer, 5 to 20 wt. % rosin-modified ester, 0.2 to 1.5 wt. % pigment, up to 5 wt. % wax, up to 0.5 wt. % antioxidant, up to 0.7 wt. % light stabilizer, up to 4 wt. % plasticizer, and 20 to 80 wt. % inorganic filler. In some embodiments, the thermoplastic composition comprises 100% solid materials.
In some embodiments, the thermoplastic composition described herein comprises 2 to 20 wt. % polyamide resin, 0 to 5 wt. % copolymer, 3 to 18 wt. % rosin-modified ester, 0 to 10 wt. % modified gum rosin, 0.5 to 4 wt. % ethylene vinyl acetate copolymer, 0.5 to 2 wt. % pigment, 0.5 to 5 wt. % wax, up to 3 wt. % antioxidant, up to 3 wt. % light stabilizer, 1 to 5 wt. % plasticizer, 20 to 50 wt. % of a first inorganic filler, and 20 to 50% of a second inorganic filler. In some cases, the first inorganic filler can comprise sand. In some cases, the second inorganic filler can comprise calcium carbonate.
In some embodiments, the thermoplastic composition described herein comprises 2 to 20 wt. % polyamide resin, 0 to 5 wt. % copolymer, 3 to 18 wt. % rosin-modified ester, 0 to 10 wt. % modified gum rosin, 0.5 to 4 wt. % ethylene vinyl acetate copolymer, 0.5 to 2 wt. % pigment, 0.5 to 5 wt. % wax, up to 3 wt. % antioxidant, up to 3 wt. % light stabilizer, 1 to 5 wt. % plasticizer, 20 to 80 wt. % of an inorganic filler. In some cases, the inorganic filler can comprise sand or calcium carbonate.
In some embodiments, the thermoplastic composition described herein comprises 2 to 20 wt. % polyamide resin, 0 to 5 wt. % copolymer, 3 to 18 wt. % rosin-modified ester, 2 to 15 wt. % modified gum rosin, 0.5 to 4 wt. % ethylene vinyl acetate copolymer, 0.5 to 2 wt. % pigment, 0.5 to 5 wt. % wax, up to 3 wt. % antioxidant, up to 3 wt. % light stabilizer, 1 to 5 wt. % plasticizer, 20 to 50 wt. % of a first inorganic filler, and 20 to 50% of a second inorganic filler. In some cases, the first inorganic filler can comprise sand. In some cases, the second inorganic filler can comprise calcium carbonate.
In some embodiments, the thermoplastic composition described herein comprises 2 to 20 wt. % polyamide resin, 0 to 5 wt. % copolymer, 3 to 18 wt. % rosin-modified ester, 2 to 15 wt. % modified gum rosin, 0.5 to 4 wt. % ethylene vinyl acetate copolymer, 0.5 to 2 wt. % pigment, 0.5 to 5 wt. % wax, up to 3 wt. % antioxidant, up to 3 wt. % light stabilizer, 1 to 5 wt. % plasticizer, 20 to 80 wt. % of an inorganic filler. In some cases, the inorganic filler can comprise sand or calcium carbonate.
In some embodiments, the thermoplastic composition may have a viscosity of 1,000 to 50,000 cP, where the viscosity is measured at 425° F. with a Brookfield Viscometer at 6 rpm, #4 or #64 spindle. In some embodiments, the thermoplastic composition may have a viscosity of 1,000 to 40,000 cP, where the viscosity is measured at 425° F. with a Brookfield Viscometer at 12 rpm, #4 or #64 spindle. In some examples, the thermoplastic composition may have a viscosity of 1,000 to 30,000 cP where the viscosity is measured at 425° F. with a Brookfield Viscometer at 30 rpm, #4 or #64 spindle. In some examples, the thermoplastic composition may have a viscosity of 1,000 to 10,000 cP where the viscosity is measured at 425° F. with a Brookfield Viscometer at 60 rpm, #4 or #64 spindle. In some examples, the thermoplastic composition may have a viscosity of 2,500 to 8,000 cP, 4,000 to 12,000 cP, 5,000 to 16,000 cP, or 7,000 to 22,000 cP where the viscosity is measured at 425° F. with a Brookfield Viscometer at 6 rpm, #4 or #64 spindle.
In some embodiments, the thermoplastic composition may have a specific gravity of less than 2.15. In some examples, the thermoplastic composition may have a specific gravity of 1.6 to 2.1. In some embodiments, the thermoplastic composition may have a softening point of 200 to 260° F. (e.g., 200 to 250° F., 212 to 260° F.). In some embodiments, the flash point of the thermoplastic composition may be at least 500° F., as tested by ASTM D92 (2018).
The resilience of the thermoplastic composition can be important for roadway applications that will be subjected to forces from daily vehicular traffic and varying weather conditions as well as snow removal equipment in climates receiving severe winter weather.
In some examples, the thermoplastic composition may have desirable low temperatures stress resistance and may not crack when exposed to temperatures of about 15° F. for about 3 days, as tested according to AASHTO T 250 (2005).
In some examples, the thermoplastic composition may have a minimum impact resistance of 160 psi, measured at 23° C. In some examples, the thermoplastic composition may have a minimum impact resistance of 140 psi, measured at 0° C.
In some examples, the thermoplastic composition may have a hardness of 5 to 75 units, (e.g., 15 to 40 units, 35 to 70 units), measured with 1 kg at 115° F. and shore A durometer.
In some examples, the thermoplastic composition may have a maximum weight loss of 350 mg during abrasion resistance test ASTM D4060, using a Tabor Abraser.
In some examples, after heating the thermoplastic composition for approximately four hours at about 425° F., the bond strength to Portland Cement Concrete may be at least 200 psi, as tested by ASTM D4796 or ASTM C321 (2018).
In some examples, the heated thermoplastic may have a percent elongation of at least 20%, as tested by ASTM D638 (2018). In some examples, the thermoplastic may be tested for flexibility using a Mandrel Bend Test, as tested by ASTM D522-93A(2008). The composition may pass Mandrel Bend Testing at ambient and reduced temperatures, e.g., 5° C.
As described herein, the composition may not exude dangerous fumes upon heating to application temperature. The substantial lack of fumes is important to the health and safety of workers in the vicinity of the hot thermoplastic composition. In some embodiments, improved health and safety can be aided by the thermoplastic composition comprising 100% solids. For example, conventional materials often rely on petroleum-based products that may emit potentially harmful fumes at application temperatures and expose workers in the vicinity of the application of the conventional sealant produce, increasing the workers risk of adverse health effects. In some embodiments, the composition described herein provides a reduced level of exposure to workers in the vicinity of the application of the thermoplastic composition sealant, thus improving worker health and safety.
Methods of making the Composition
In some examples, a method of making a thermoplastic composition described herein comprises adding a wax to the vessel, adding a polyamide resin to the vessel, adding a plasticizer to the vessel, adding a first charge of an inorganic filler to the vessel, adding a second charge of an inorganic filler to the vessel, adding at least one of a rosin-modified ester or a modified gum rosin to a vessel, and mixing the thermoplastic composition. Optionally, the method may further comprise adding a copolymer to the vessel. The method may further comprise adding an antioxidant to the vessel. In some cases, the method may further comprise adding a light stabilizer to the vessel. Optionally, the composition may be blended at ambient temperatures and packaged for future use. In some examples, the method may further comprise adding a pigment to the vessel.
Optionally, the method may further comprise adding a second copolymer to the vessel after the polyamide resin addition. In some embodiments, the first charge of inorganic filler may be at least 50% of a total amount of inorganic filler to be charged. In some examples, the method may further comprise mixing the thermoplastic composition until the thermoplastic composition is an essentially homogeneous mixture or essentially uniform dispersion. The mixing may be performed by at least one of auger, agitation, or recirculation. In some embodiments, the method may further comprise heating the vessel to about 340-450° F.
Methods of using the Composition
The thermoplastic compositions described herein are useful for sealing roadway joints, for example, longitudinal joints. In some examples, the thermoplastic compositions described herein may be used to cover and seal the longitudinal joints of a pavement to prevent water ingress to the longitudinal seam of the pavement. As used herein, the terms joint and seam are interchangeable. As used herein the terms highway, roadway, and pavement are interchangeable.
In some cases, a method of sealing roadway joints may comprise: (a) heating a thermoplastic composition, where the thermoplastic composition is mixed during the heating, where the mixing is performed by at least one of auger, agitation, or recirculation and (b) applying the heated thermoplastic composition to a roadway joint, where the thermoplastic composition is applied by extrusion, spraying, or other application means to the roadway joint. In some cases, the roadway joint comprises a longitudinal joint that is substantially parallel to and located between adjacent lanes of a roadway. In some examples, the method can additionally include cooling the applied thermoplastic composition to form a solid seam on the hot-mix asphalt roadway joint.
In some embodiments, the thermoplastic composition is heated to about 340 to 450° F. (e.g., from about 350 to 400° F.; from 400 to 450° F.; from 375 to 425° F.). The temperature range for heating the thermoplastic composition may be adjusted based on the surface temperature of the roadway and the ambient air temperature to ensure proper adhesion of the thermoplastic composition. The application temperature may be lowered for hot surfaces and may be increased for cooler surfaces. In some cases, both the surface temperature of the roadway and the ambient air temperature, accounting for wind chill, should be at least 50° F. prior to application of the thermoplastic composition.
In some examples, the thermoplastic composition may be applied be standard thermoplastic extrusion equipment. The extrusion die may be configured to extrude the thermoplastic composition at the desired width onto directly onto the roadway at the site of the joint via a mobile extrusion unit.
In some embodiments, the thermoplastic composition may be extruded as wide as 12 inches. For example, the thermoplastic may be extruded at 6 inches, 8 inches, or 10 inches wide. The wider width of the thermoplastic composition joint seal can allow for lane markings to be applied directly to portion of the surface having the joint seal. In some examples, the lane markings can be narrower in width than the joint seal. In some examples, the joint seal can provide an area that provides increased contrast and improved visibility of the yellow or white lane markings against the darker joint seal. The contrast may be more marked for a roadway that has become lighter as a result of aging.
In some examples, the 100% solids formulation of the thermoplastic composition may allow for ease of extrusion. In some embodiments, the thickness of the extruded thermoplastic composition may be about 15 to 150 mils (0.015 to 0.15 inches). For example, the thickness of the extruded application may be about 15 mils, 20 mils, 25 mils, 30 mils, 35 mils, 40 mils, 45 mils, 50 mils, 55 mils, 60 mils, 65 mils, 70 mils, 75 mils, 80 mils, 85 mils, 90 mils, 95 mils, 100 mils, 105 mils, 110 mils, 115 mils, 120 mils, or 125 mils. The durability of the joint seal may be related to the thickness of the thermoplastic composition applied. For example, a 120 mil seal may be expected to experience increased durability as compared to a 60 mil seal.
In some cases, the pavement surface can be prepared prior to application of the thermoplastic composition. In some embodiments, the surface may cleaned of dust or debris. The surface can also be substantially dry prior to application of the thermoplastic composition. In some cases, the moisture content of the surface may also be evaluated prior to application, especially if the dew point is close to the ambient temperature. In some cases, an adhesion test may be performed on a test area that has completely cooled after application to ensure proper binding of the thermoplastic composition to the roadway.
In some examples, joints along aged roadways may be sealed with the thermal composition described herein. The surface may be primed or mechanically abraded prior to sealing. In some examples, joints along new roadways may be sealed with the thermal composition described herein. Application to a new concrete roadway may benefit from a period of cure time and/or abrasion to improve adhesion. In some examples, application to a new HMA roadway may be performed once the new HMA mat has cooled to below 100° F.; however, the application may benefit from an aging period of the HMA mat to allow the HMA to cure and for additives of the HMA such as oils and roller aides time to be tracked off the new surface.
In some examples, an aggregate may be applied to the extruded thermoplastic composition while the composition is cooling. In some embodiments, the application of the aggregate may be performed by dropping the aggregate onto the hot thermoplastic composition. In some cases, the aggregate may comprise different compositions, for example, those with low free silica. The aggregate may modify the texture of the seal to increase the roughness and provide a safer non-slip surface at the sealed joint. The aggregate may also reduce the time that traffic flow is limited on the roadway. Additionally, the aggregate may modify the visual appearance or reflective properties of the composition, making the composition appear less glossy to an observer.
The surface and ambient air temperatures may vary the time for the thermoplastic composition to cool. In some examples, the thermoplastic composition may be sufficiently tack-free in approximately 2 minutes, for example when the surface temperature is approximately 50 ° F. In other examples, the thermoplastic composition may be sufficiently tack-free in approximately 10 minutes, for example when the surface temperature is approximately 130° F.
In some examples, a fan or other means of cooling the composition may be employed to reduce the time for the composition to cool. The reduced cooling time may improve traffic flow in the construction area. The reduced cooling time may further allow for quicker application of lane marking to the sealed joints. The rapid application speed, including extrusion and cooling of the thermoplastic composition, is a dramatic improvement over conventional methods of sealing the joints.
In one example, the thermoplastic composition can include the formulation shown in Table 1.
The composition was applied to an asphalt surface at 380-425° F.
On the other hand,
In
The thermoplastic compositions described herein were applied to a highway. The application using the vehicle-mounted extruder 408 is shown in
The thermoplastic compositions described herein were tested for impact resistance. The composition 602 was applied to a substrate 601 and tested for impact resistance according to ASTM D5420-98a. The composition 602 is shown in Example 1.
Mandrel bend testing was performed on thermoplastic compositions described herein according ASTM D522-93A(2008). Coatings attached to substrates are elongated when the substrates are dimensionally unstable, or when the coatings are abused in service. Mandrel bend testing can be useful in rating attached coatings for their ability to resist cracking when elongated.
Two compositions were evaluated for resistance to cracking using cylinder having a diameter ranging from 0.125 inch to one inch. Sample size was 6-inches×1-inch. Sample 1 had the formulation as set forth in Example 1. The formulation of Sample 2 was similar to Sample 1, but was modified to include 2-15 wt. % modified gum rosin. To evaluate resistance to cracking in different weather applications, mandrel bend testing was conducted at both 24° C. and 5° C. The test results for Sample 1 and Sample 2 at each cylinder diameter for each temperature are provided in Table 2.
Dynamic mechanical analysis (DMA) data was collected using an Anton Paar Rheometer with liquid nitrogen for consistent temperature control. DMA can measure the properties of materials as they are deformed under periodic stress. Samples were cut into rectangular prism shapes with typical dimensions of 40 mm×11 mm×3 mm. A constant oscillating strain while ramping the temperature at 2° C/min provided the modulus and tan 6 values seen in
For roadway applications, two areas of the chart are of interest: 0-40° C. and 40-80° C. For 0-40° C., a lower storage modulus can indicate a composition is more flexible and therefore, more resistant to cracking. For 40-80° C., a higher storage modulus can indicate a composition is more resistant to deformation, which may occur on road markings due to compressive forces from vehicular traffic. While Sample 2 did not perform the same as the control sample, Sample 2 did exhibit a lower storage modulus in the 0-40° C. range as compared to Sample 1, and a higher storage modulus in the 40-80° C. range as compared to Sample 1.
A composition as described herein was applied to roadway surface comprising Superpave asphalt. Two lines of the composition were applied and topped with a layer of aggregate. A X-RITE Colori7 test was used to determine the level of gloss/matte of a given composition. A gloss measurement was conducted on the compositions provided in Examples 1 and 5, where test measured the amount of reflection (gloss) at a 60-degree angle of incidence. This is angle is generally representative of the angle a reflection observed by a driver on a highway. Table 3 provides the results.
As used below, any reference to methods, products, or systems is understood as a reference to each of those methods, products, or systems disjunctively (e.g., “Illustrative embodiment 1-4 is understood as illustrative embodiment 1, 2, 3, or 4.”).
Illustrative embodiment 1 is a thermoplastic composition comprising:
2 to 30 wt. % polyamide resin;
up to 40 wt. % rosin-modified ester;
up to 40 wt. % modified gum rosin;
0.1 to 10 wt. % pigment;
up to 20 wt. % wax;
up to 10 wt. % plasticizer; and
5 to 90 wt. % of at least one inorganic filler.
Illustrative embodiment 2 is the composition of any preceding or subsequent illustrative embodiment, wherein the pigment is carbon black.
Illustrative embodiment 3 is the composition of any preceding or subsequent illustrative embodiment, wherein the modified rosin ester comprises tall oil esters, maleic rosin ester, pentaerythritol rosin ester, glycerol rosin ester, disproportionated rosin ester, hydrogenated rosin, and polymerized rosin.
Illustrative embodiment 4 is the composition of any preceding or subsequent illustrative embodiment, wherein the copolymer comprises one or more of ethylene vinyl acetate and ethylene maleic anhydride.
Illustrative embodiment 5 is the composition of any preceding or subsequent illustrative embodiment, wherein the wax comprises polyethylene wax.
Illustrative embodiment 6 is the composition of any preceding or subsequent illustrative embodiment, further comprising :
up to 10 wt. % copolymer;
up to 3 wt. % antioxidant; and
up to 3.5 wt. % light stabilizer.
Illustrative embodiment 7 is the composition of any preceding or subsequent illustrative embodiment, wherein the light stabilizer comprises a hindered amine.
Illustrative embodiment 8 is the composition of any preceding or subsequent illustrative embodiment, wherein the plasticizer comprises one or more of castor oil and di-isononyl phthalate.
Illustrative embodiment 9 is the composition of any preceding or subsequent illustrative embodiment, wherein the inorganic filler comprises one or more of calcium carbonate, silica, quartzite, marble grit, glass powder, glass cullet, and alumina.
Illustrative embodiment 10 is the composition of any preceding or subsequent illustrative embodiment, wherein the modified gum rosin comprises one or more of glyceryl hydrogenated rosin, rosin modified phenolic resin, pentaerythrityl rosin, glyceryl rosin, disproportionated rosin, polymerized rosin or hydrogenated rosin.
Illustrative embodiment 11 is the composition of any preceding or subsequent illustrative embodiment, wherein the composition has a viscosity of 1,000 to 50,000 cP, wherein the viscosity is measured at 425° F. with a Brookfield Viscometer at 6 rpm, #4 or #64 spindle.
Illustrative embodiment 12 is the composition of any preceding or subsequent illustrative embodiment, wherein the composition has a viscosity of 1,000 to 10,000 cP, wherein the viscosity is measured at 425° F. with a Brookfield Viscometer at 60 rpm, #4 or #64 spindle.
Illustrative embodiment 13 is the composition of any preceding or subsequent illustrative embodiment, wherein the composition has a specific gravity of 1.6 to 2.1.
Illustrative embodiment 14 is the composition of any preceding or subsequent illustrative embodiment, wherein the composition has a hardness of 5 to 75 units measured with 1 kg at 115° F. and shore A durometer.
Illustrative embodiment 15 is the composition of any preceding or subsequent illustrative embodiment, wherein the composition has softening point of 200 to 260° F.
Illustrative embodiment 16 is the composition of any preceding or subsequent illustrative embodiment, wherein the composition has elongation of at least 20 percent.
Illustrative embodiment 17 is the composition of any preceding or subsequent illustrative embodiment, wherein the thermoplastic composition is applied to a roadway comprising a first asphalt and a second asphalt to form a barrier over a longitudinal joint that is substantially parallel to and located between the first asphalt and the second asphalt, and wherein the thermoplastic composition seals an edge between the first asphalt and the second asphalt from deterioration.
Illustrative embodiment 18 is a method of making a thermoplastic composition, the method comprising:
adding a wax to the vessel;
adding a polyamide resin to the vessel;
adding a plasticizer to the vessel;
adding at least one of a modified rosin ester or a modified gum rosin to a vessel;
adding a first charge of an inorganic filler to the vessel;
padding a second charge of an inorganic filler to the vessel;
and mixing the composition.
Illustrative embodiment 19 is the method of any preceding or subsequent illustrative embodiment, further comprising heating the vessel to 340 to 450° F.
Illustrative embodiment 20 is the method of any preceding or subsequent illustrative
embodiment, further comprising
adding a copolymer to the vessel;
adding an antioxidant to the vessel; and
adding a light stabilizer to the vessel.
Illustrative embodiment 21 is the method of any preceding or subsequent illustrative embodiment, further comprising adding a second copolymer to the vessel after the polyamide resin addition.
Illustrative embodiment 22 is a method of sealing roadway joints, the method comprising: heating a thermoplastic composition of claims 1 to 340 to 450° F., wherein the thermoplastic composition is mixed during the heating, wherein the mixing is performed by at least one of auger, agitation, or recirculation; and applying the heated thermoplastic composition to an asphalt roadway joint, wherein the thermoplastic composition is applied by extruding, spraying, or other application means to the asphalt roadway joint, wherein the asphalt roadway joint comprises a longitudinal joint that is substantially parallel to and located between adjacent lanes of an asphalt roadway.
Illustrative embodiment 23 is the method of any preceding or subsequent illustrative embodiment, further comprising applying an aggregate to the applied thermoplastic composition.
While this specification describes the composition being applied to a roadway, a person of ordinary skill in the art would understand that the compositions can be applied to other substrates. Some non-limiting examples of substrates include pavement, roads, parking lots, parking decks, parking blocks, traffic blocks, ramps, bridges, airport runways, docks, tunnels, sidewalks, parks, plazas, green spaces, decorative spaces, floor surfaces, walls, ceilings, and doors. Typical but non-limiting examples of substrate materials include asphalt, concrete, and cement.
As used herein, the terms “invention,” “the invention,” “this invention” and “the present invention” are intended to refer broadly to all of the subject matter of this patent application and the claims below. Statements containing these terms should be understood not to limit the subject matter described herein or to limit the meaning or scope of the patent claims below. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to”) unless otherwise noted.
As used herein, the meaning of “a,” “an,” and “the” includes singular and plural references unless the context clearly dictates otherwise.
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all subranges subsumed therein. For example, a stated range of “1 to 10” should be considered to include any and all subranges between (and inclusive of) the minimum value of 1 and the maximum value of 10; that is, all subranges beginning with a minimum value of 1 or more, e.g. 1 to 6.1, and ending with a maximum value of 10 or less, e.g., 5.5 to 10. Additionally, any reference referred to as being “incorporated herein” is to be understood as being incorporated in its entirety.
Various embodiments of the invention have been described in fulfillment of the various objectives of the invention. It should be recognized that these embodiments are merely illustrative of the principles of the present invention. Numerous modifications and adaptations thereof will be readily apparent to those skilled in the art without departing from the spirit and scope of the present invention as defined in the following claims.
This application is a continuation of U.S. patent application Ser. No. 16/018,504, filed Jun. 26, 2018, which claims the benefit of U.S. Provisional Application No. 62/525,035, filed Jun. 26, 2017, the entirety of all of which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62525035 | Jun 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16018504 | Jun 2018 | US |
| Child | 17468047 | US |