Thermoplastic endodontic composition having improved melt flow index

Abstract

A novel process for providing a thermoplastic polymer having unique thermal characteristics including the step of cooling the polymer during extended mastication until the melt index of the polymer is substantially increased.

Description

TECHNICAL FIELD

The present invention relates generally to endodontia methodologies and procedures. More particularly, the present invention relates to the use of thermoplastic polymers in endodontia methodologies and procedures. Specifically, the present invention relates to a process for producing thermoplastic polymers to provide a thermoplastic polymer having a much improved melt flow index so that it is particularly suited for the obturation of root canals.

BACKGROUND ART

Endodontia is a branch of dentistry specializing in diseases of the tooth pulp. A primary corrective procedure for diseased pulp is to remove it, clean out and shape the resulting root canal and then obturate the root canal space. The obturation procedure is critical because if the apical seal is not adequate, the tissues underlying the root canal may be exposed to foreign, deleterious matter.

Obturation of the root canal system typically involves the insertion of a material within the root canal, which material must sealably adhere to the dentin walls. Of particular concern is a fluid-tight seal between the inserted material and the apical foramen region. Additionally, endodontic therapy requires that the inserted material conform, and effect a seal, to the dentin wall irregularities as well as any lateral canals. Various methodologies for obturating root canals have been developed and are disclosed in the prior art. A thorough understanding of these procedures is necessary to appreciate the significance and novelty of the present invention.

While many types of obturating material have been used, modern endodontia techniques utilize trans-polyisoprenes such as gutta-percha and balata or other species thereof. In order to avoid a repetitively detailed identification of the trans-polyisoprenes utilized, the specification will hereinafter simply refer to gutta-percha. Gutta-percha, chemically, is the trans- isomer of natural rubber and is a tough, crystalline, thermoplastic polymer. The thermoplastic characteristic of gutta-percha makes it a particularly useful endodontia material, because in the plasticized state gutta-percha readily adapts to the contour of the dentin walls and tends to retain its shape after cooling, albeit with some shrinkage.

Verification of the effectiveness of a particular obturation technique may be performed in vitro using dye penetrant, radiotracer penetrant, microscopic examination, sectioning, X-ray analysis or scanning electron microscope analysis, among others. Though in vivo assessment is possible, a much greater period of time is required before the results are available. The particular analysis technique utilized will, in part, be determined by which aspect of the obturation seal may be of interest, as well known and understood by those skilled in the art.

One obturation technique involves the use of gutta-percha cones, or points, usually made in standard sizes, a plurality of which are fitted into the root canal which has itself been generally conically shaped to facilitate acceptance of the cones. After the canal has been cleaned and shaped, the dentin walls are typically coated with a sealer and a point is inserted. The inserted point is then condensed with finger pluggers to force the tip of the point into conformation with the apical region of the root canal. With this technique the gutta-percha point typically is not heated, and a second step, lateral condensation, is required. Lateral condensation is effected by inserting additional points into the canal and compacting them with heated finger pluggers to force the point material into lateral conformity with the canal wall, and hopefully to conform the point material not only to the irregularities therein but also to any laterally extending canals. Numerous difficulties can arise with this method. A major inconvenience is having to impart a particular shape to the apex of the canal in order that it can accept a standard gutta-percha point. Irregularities in the dentin walls may allow for a less than satisfactory adaptation of the point to the canal cavity. Also, the sealer may not be uniformly distributed within the interface between the point and the dentin walls.

Another obturation technique is generally referred to as vertical condensation and utilizes heated gutta-percha. The canal is prepared and a sealer introduced, as previously described. The gutta-percha to be introduced into the canal, however, is first heated. A plurality of warmed gutta-percha segments may be compactably inserted into the canal chamber. Heating the gutta-percha reduces its viscosity and thereby allows the material more readily to adapt to the dentin walls than unheated gutta-percha. Unexpectedly, however, the degree of lateral condensation, or conformity, has been found to be reduced.

When employing this technique, it has been found that the material extruded into lateral canals consists primarily of sealer. As anticipated, fillings made by vertical condensation techniques show close adaptation of the gutta-percha to the dentin walls. However, voids are often seen, possibly due to reduced lateral condensation, and the root canal sealer is not always present at the interface. The gutta-percha also tends to cool quickly, particularly during the considerable time required for the vertical condensation technique. Once the material cools, viscosity increases and lateral flow is substantially reduced. Also, seams have been observed which may be indicative of incomplete conjoining of different gutta-percha segments.

A third technique uses a solvent such as chloroform to soften the gutta-percha. While this technique shows good adaptation in the apical region, voids are often seen coronal to this section. The surface of the filling is often wrinkled which is most probably due to shrinkage of the material. Such shrinkage is an undesirable feature as it may reduce the integrity of the required seal between the filling material and the obturated canal. Shrinkage may also occur in the vertical condensation technique during cooling.

The use of plasticizers or other additives in the nature of processing aids has been considered, but there are three major drawbacks. First, it would require lengthy governmental testing and subsequent approval to assure that the processing additives are not deleterious for use in endodontic therapy. Second, even though such approval might be acquired there would be a reluctance on the part of the majority of practitioners to accept a new product without considerable clinical evidence of its satisfactory performance without incident. Third, processing additives appear to create unfavorable shrinkage characteristics which would work to destroy the seal required to obturate a root canal.

Although the above obturation techniques--with perhaps the noted exception as to the use of additives--generally provide reasonably acceptable results when performed properly, the methods are time consuming, and, therefore, costly, and require considerable care to effectuate a fluid-tight seal, particularly at the apical foramen.

One of the most promising obturation techniques is generally referred to as thermoplastic injection of a polymeric material such as gutta-percha. The important feature of this technique is that the polymer is heated to its molten, or plasticized, state--typically about +160.degree. C. The polymer is then forced, under mechanically generated pressure, into the root canal system.

One of the earlier methods for in vitro "thermoplastic injection" is described by Yee, et al, Three-Dimensional Obturation of the Root Canal Using Injection-Molded, Thermoplasticized Dental Gutta-Percha, JOURNAL OF ENDODONTICS, Vol. 3, No. 5, May, 1977. The root canal system is shaped and cleaned using conventional techniques. The gutta-percha is next introduced into the root canal cavity using an endodontic pressure syringe. An 18-gauge needle may typically be used inasmuch as it is the maximum size that fits conveniently into the root canal in human anterior teeth.

To prepare for the injection technique, gutta-percha cones are manually loaded into a syringe, and the barrel, with the needle attached, is then heated in a glycerine bath until an unrestrained flow can be achieved. This occurs at about +160.degree. C. The needle is then inserted into the cavity and the gutta-percha extruded therethrough to fill the cavity. When a slight resistance from the injected material is felt, the needle is withdrawn a few millimeters coronally and more material is extruded. This process continues until the canal is completely obturated.

Analysis of the results by obturation by this technique shows few voids and excellent adaptation of the polymer to the dentin walls. A particular advantage is that the plasticized polymer flows both vertically and laterally. Moreover, the sealer tends to be evenly distributed and lateral canals can be effectively obturated.

While the above-described method is useful for in vitro analysis of injection-molded thermoplasticized polymers, clinical application is severely limited due to the excessively high temperatures required to plasticize gutta-percha and similar polymers. These temperatures make handling of the applicator and working in the periapical and oral regions somewhat difficult and possibly unacceptable because of the fear in the mind of the clinician that its use could, even remotely, be injurious to the patient.

In order to circumvent the high temperature related problems which make the injection process clinically undesirable and impractical, much work has been dedicated to developing more feasible delivery systems. One such system is described by Marlin, et al, Clinical Use of Injection-Molded Thermoplasticized Gutta Percha for Obturation of the Root Canal System: A Preliminary Report, JOURNAL OF ENDODONTICS, Vol. 7, No. 6, June, 1981. The equipment includes an injection syringe and an electrical heating unit. The barrel of the syringe carries an electrical heating element and is insulated not only to minimize heat dissipation but also to protect the clinician and patient. The level of heat is variable depending, in part, on the needle gauge. Standard gutta-percha points are loaded into the syringe, plasticized, and the gutta-percha is then inserted in a manner similar to the Yee, et al in vitro technique hereinbefore described.

While this method of delivery is an improvement on some aspects of prior known systems, it does necessitate the use of a considerably more complex and expensive delivery system. It must be understood, however, that this method is only a delivery system; it is not a filling system. Tests have revealed that by this procedure the plasticized gutta-percha is delivered only one-half (1/2) the distance between the tip of the injection needle and the apex of the canal. Further manipulation, as with finger pluggers, is required to assure that the canal is completely filled. Moreover, the high temperatures at which the gutta-percha must be delivered by this procedure appears, itself, to engender two major drawbacks. First, mental unacceptability--the clinician remains fearful of injecting material at such high temperature into a human patient. Second, questionable operability--it appears that the high temperature differential between the injected gutta-percha and its surrounding environment likely results in excessive shrinkage of the gutta-percha as it cools.

Another method is recounted by Lugassy, et al, Root Canal Obturation with Gutta-Percha; A scanning Electron Microscope Comparison of Vertical Compaction and Automated Thermatic Condensation, JOURNAL OF ENDODONTICS, Vol. 8, No. 3, March, 1982. The technique was developed by McSpadden and is generally referred to as automated thermatic condensation. This technique uses a compactor, similar to a Hedstroem file, mounted on a contra-angle. The compactor plasticizes the gutta-percha within the root canal system and provides lateral as well as vertical compaction.

According to this technique, after the root canal is shaped and prepared, a compactor size is selected one size smaller than the largest reamer used near the apical constriction. A standard gutta-percha point is inserted into the canal, and the compactor is then rotated at a speed of approximately 10,000-15,000 r.p.m. The direction of rotation must be such as to assure an apical vector for the gutta-percha compaction. Essentially, the rotary tool provides frictional heat whereby the gutta-percha is plasticized and adequate lateral and vertical condensation is achieved.

While the McSpadden technique is an improved method for avoiding the excessive heat problem, the technique still requires sophisticated hardware, consummate skill and strict adherence to specific guidelines to obtain predicted results.

It is clear, therefore, that a viable need exists for an improvement in the art of endodontia whereby thermoplastic polymers can be quickly and inexpensively injected with a minimal risk from excessive temperatures and without elaborate delivery system.

DISCLOSURE OF THE INVENTION

It is, therefore, a primary object of the present invention to provide an improved process for preparing a material for use in root canal obturation.

It is another object of the invention to provide an obturating material which plasticizes at a clinically feasible temperature and which can be delivered to fill a root canal by virtue of a standard syringe.

It is still another object of the invention to provide a novel improvement to a method of obturating root canals.

It is a further object of the invention to provide a process by which the melt index of a thermoplastic polymer can be substantially increased.

It is yet another object of the present invention to provide an improved process for preparing a thermoplastic material so that the material exhibits minimal shrinkage during cooling.

These and other objects of the invention, as well as the advantages thereof over existing and prior art forms, which will be apparent in view of the following specification, are accomplished by means hereinafter described and claimed.

In general, the present invention relates to a process of plasticization of thermoplastic polymers selected from the group consisting of gutta-percha, balata and synthetic trans-polyisoprene having an unprocessed melt flow index falling within the range of approximately 0.2 to 0.8 grams per 10 minutes comprising the steps of masticating the polymer with sufficient shear to heat the polymer, cooling the polymer to about 60.degree. C. while continuing to masticate and, discontinuing the mastication of the polymer when the melt index reaches the desired level.

A related process for the plasticization of thermoplastic polymers of the foregoing type comprises the steps of masticating the polymer with sufficient shear to heat the polymer to a range of from about 90.degree. to 110.degree. C., cooling the polymer and monitoring the temperature thereof as it is masticated and, discontinuing the masticating step when the temperature of the polymer drops to a range of from about 60.degree. to 72.degree. C.

A related process for the plasticization of the foregoing thermoplastic polymers comprises the step of masticating the polymer with sufficient shear to create heat, cooling the polymer and continuing the mastication for at least about 15 hours and, thereafter discontinuing the mastication.

The application of the aforesaid processes to thermoplastic polymers selected from the group consisting of natural and synthetic trans- polyisoprenes results in a product having novel characteristics including a melt flow index exceeding at least about 10 grams per 10 minutes and which can reach 500 grams per 10 minutes or higher. As such, these polymers are particularly suited for the obturation of root canals. One unique property is an extremely high melt flow index despite the fact that plasticizers, chemical processing aids and solvents are not employed. Typical examples of the trans-species include gutta-percha and balata, although the present invention is not limited to these. As noted hereinabove, reference has been made throughout the specification to gutta-percha as a matter of convenience and because it has been exemplified hereinbelow. Nevertheless, it is to be understood that practice of the present invention is more broadly directed toward the foregoing trans- polyisoprenes.

When these materials are processed it has been found that the heat produced by mastication raises the temperature of the polymer being masticated to approximately the upper reach of the range of approximately 90.degree. to 110.degree. C. The temperature will slowly decrease during continued mastication, while remaining within the stated range, until such time as the rate of change of the melt flow index undergoes a quantum change. However, the process of the present invention employs a novel cooling step during mastication which reduces the time somewhat for the temperature reduction to occur. Generally coincident with the quantum change in the rate of change of the melt flow index, as hereinafter more fully explained, the temperature will have reduced approximately twenty to forty-five percent (20-45%) from its highest reading. This brings the temperature of the material being masticated down to the range of 60.degree. to 72.degree. C.

Embodiments of the processes for producing the novel polymer incorporating the concepts of the present invention are disclosed herein by way of example without attempting to disclose all of the various forms and modifications in which the invention may be carried out; the invention being measured by the appended claims and not by the details of the specification.

BRIEF DESCRIPTION OF THE DRAWING

The drawing figure constitutes a graph in which the most critical quality of the novel polymer--the melt flow index--is plotted against time of mastication.

PREFERRED EMBODIMENT OF THE INVENTION

The plasticization of the thermoplastic polymer according to the concept of the present invention provides a polymer having novel characteristics that are particularly suited for obturating root canals by injection techniques. Specifically, the plasticized polymer so processed will flow sufficiently free from a needle to fill the full apical cavity and flow laterally to fill any and all irregularities within the canal, and generally even including lateral canals. Moreover, such materials have been found to perfect an effective seal to the dentin walls such that a sealer need not even be employed.

One suitable parameter by which to measure the relative acceptability of a polymer for use as a material by which to fill a root canal is its viscosity. A standardized scale by which to characterize the viscosity of a thermoplastic polymer is its melt flow index.

The melt index is the amount, in grams, of a thermoplastic resin which can be forced through an orifice of 0.0825 inch diameter (2.09 mm) when subjected to a force of 2160 grams in 10 minutes at +105.degree. C. Polymers possessing higher melt flow indices--i.e., on the order of two to three orders of magnitude greater than the normal 0.2 gms/10 min--readily conform to the cavity into which they are injected, and if the melt flow index could be maintained in such an elevated state during the time it takes to perform the filling procedure, the polymer would flow sufficiently to fill the full extent of the canal. Heretofore, a sufficiently high melt flow index could be achieved only by elevating the temperatures of the polymer, but unfortunately, the sufficiently higher melt flow index could not be maintained for a period of time to achieve a satisfactory filling of the canal solely by virtue of the flow of the polymer.

According to the concept of the present invention the melt flow index of a thermoplastic polymer such as gutta-percha, balata and the like can be radically and unexpectedly increased by masticating the material for a markedly extended period of time. The masticating operation may be performed with any conventional milling or mixing apparatus, either internal or external, as more fully hereinafter discussed, but the duration of the masticating process is uniquely and substantially modified in a novel way and clearly distinguishable from conventional milling processes.

Milling is one of the well-known processes for masticating, and/or mixing, viscous and elastic materials. A typical two-roll, open mill--as used for mixing, warm-up, feeding and cracking in the rubber industry--may be employed. Such a mill includes two surface rolls, set horizontally close together. The stock material is forced between the rolls, which run at different speeds and form a band of material about at least one of the rolls.

Mastication can also be provided in an internal mixer such as a double arm mixer which employs a pair of blades which communicate with each other as well as the internal walls of the mixer. Such apparatus can be heated or cooled externally as a means of controlling the temperature of the material within.

Whether milling, mixing or other apparatus is employed, the shearing action of the mastication process generates considerable heat. Moreover, while a typical mixing operation on a mill may require only a few minutes, the processing of a polymer according to the concept of the present invention takes a considerably extended period of time, as hereinafter more fully explained.

Although the preferred embodiment is hereafter described with particularity in reference to gutta-percha and/or balata, this is to be construed as exemplary only, and not intended to be, in any sense, limiting.

When polymers such as gutta-percha or balata are prepared as the stock material in making "points", cones and the like for endodontic therapy, numerous fillers may be added to the gutta-percha or balata, including barium sulfate, zinc oxide or titanium oxide. The final compound typically is mixed in a conventional milling operation for approximately 20 minutes to an hour.

However, according to the concept of the present invention the polymer is extensively masticated prior to intermixing the fillers normally employed. It should be appreciated that the fillers could well be introduced prior to mastication, but inasmuch as the final product will contain on the order of 19-21 percent gutta-percha, it is more efficient to process the gutta-percha prior to intermixing the standard fillers. Moreover, it has also been found that the process of increasing the melt flow index is facilitated by cooling the polymer as it is masticated.

By way of example, unprocessed gutta-percha has a melt flow index of approximately 0.2 grams per 10 minutes. The normal milling time to intermix the various fillers (20 to 60 minutes) leaves the melt flow index virtually unchanged. In fact, during the first several hours of mastication the melt flow index shows a very modest increase. However, at some point between approximately the 10th and 20th hours there is a totally unexpected quantum increase to the rate of change of the melt flow index per hour of mastication such as continued mastication for an additional, comparable period of time effects change in the melt flow index on the order of at least two orders of magnitude.

Shearing of the polymer during masticating will cause the temperature of the polymer being masticated to rise initially to a range of from about 90.degree. to 110.degree. C. This appears to be an effective temperature for the initial mastication of gutta-percha in a closed internal mixer as well as an open mill.

Although heat is therefore not required during mastication, the mixing apparatus can be warmed initially to bring the temperature of the polymer from ambient up to a suitable mixing or milling temperature at which the polymer mass is sheared. Such a suitable temperature would be up to about 90.degree. to 110.degree. C., the temperature that results from shearing and can eliminate 30 to 45 minutes of mastication time that is normally required for this temperature to be obtained solely by mastication.

Once this range is reached, the process of the present invention calls for a cooling step that not only inhibits further temperature increase but also aids in reducing the temperature of the polymer. When the melt flow index has been markedly increased, the temperature induced by the shear of the mastication is greatly reduced. In fact, the temperature of the gutta-percha has been found to display an overall decrease on the order of 20% to 45% at or shortly after the aforedescribed quantum increase in the rate of change of the melt flow index--even as the mastication process is continued. Specifically, the temperature of the gutta-percha is reduced to the range of from about 60.degree. to 72.degree. C.

Although this temperature reduction occurs in the polymer when the melt flow index has been greatly increased, it has now been found that a step of cooling the polymer during mastication will decrease the time of mastication. The present invention is not limited to any particular apparatus or process whereby cooling is imparted as those skilled in the art will appreciate and be able to select equipment compatible with their mastication apparatus. Generally, the temperature of the polymer should be maintained at about 60.degree. C. and can vary by at least .+-.10.degree. C.

While care must be taken not to cool the polymer to such a degree that it no longer sticks to the shearing elements, i.e., blades or rolls, of the mastication apparatus, there is still a relatively wide range of temperature over which the mastication step can be conducted as compared to the range that would exist during most of the mastication process without cooling--about 90.degree. to 110.degree. C. It has now been found that the duration of the mastication step, once the polymer has reached its shearing temperature, is shortened by about two hours or more if the polymer is cooled as noted hereinabove. However, a point is reached where too much cooling will again lengthen the mastication step and therefore, the operator can expect optimum efficiency at a temperature close to 60.degree. C. By shearing temperature, is meant the temperature that is imparted to the polymer solely by the mechanical forces of shearing in the apparatus.

In a similar vein, the mastication step is conducted for at least about 10 hours or until the desired level of melt flow index is obtained, i.e., the level at which a root canal can successfully be obturated. As noted hereinabove, the initial melt flow index of these polymers is on the order of 0.2 to 0.8 grams per 10 minutes and conventional processing, relying on chemical additives has provided only about 10 grams per 10 minutes. The majority of dental practitioners are accustomed to using a product having this melt flow index as the design of existing equipment and root canal techniques will attest. However, practice of the present invention will provide polymers having melt flow indices of 20 grams, 50 grams, 100 grams, 250 grams, even 500 grams per 10 minutes and all ranges therebetween.

The desired level of melt flow index is a function of many factors including the anatomy of the root canal; the equipment that is selected and the desired techniques of the clinician. A primary objective is that the polymer be deliverable in a flowable state which requires heat. While a polymer having a melt flow index of 500 will flow at a lower temperature than one where the melt flow index is 50, the clinician may prefer to use a higher temperature, or to alter the flow characteristics of the polymer. If the technique involves condensing, to move the material into the canal laterally, a lower melt flow index or less flowable material could be selected.

Thus, it should be understood that a variety of melt flow indices can be useful and that the mastication time is a function of the melt flow index obtained. Generally, after about 15 hours the melt flow index will continue to increase dramatically with time such that a melt flow index of about 500 grams/10 minutes will be obtained at about 30 hours. While greater values can be obtained, the usefulness of such products for obturating root canals may be minimal. Nevertheless, such a product could have other uses and therefore, the present invention should not be limited to 30 hours or melt flow indices of 500 grams/10 minutes as other levels may be desired and can be obtained following these teachings.

In order to quantify this wholly unexpected result, several 1100-1600 gram batches of unprocessed gutta-percha were continuously masticated in an internal mixer for varying periods of time. The temperature of the gutta-percha was noted at various intervals and a sample of the gutta-percha was then taken and tested by the standard procedure described above to determine the melt flow index. Those results are set forth below in Tables I-III.

In Table I, melt flow indices for three samples of gutta-percha, Examples Nos. 1-3, were determined with polymer mixing begun without any initial heating to bring the polymer to 94.degree. C. Once this temperature was obtained by shearing action, cold water circulation about the exterior of the apparatus was begun to chill the stock during the successive hours of mastication. In each instance, approximately 30 minutes of initial mastication was required to take the polymer from ambient to about 94.degree. C.

In Table II, melt flow indices for two additional samples of gutta-percha, Examples Nos. 4-5, were determined for polymers heated at the beginning of the mastication to bring their temperature quickly to about 91.degree. C. after which cooling followed. In both instances the temperature was obtained in about 15 minutes.

In Table III, Example Nos. 6-8 are presented. Each polymer was subjected to a heat start as explained for Table II of about 15 minutes. Subsequent mixing time with chilling is reported as are melt flow indices of approximately 50, 100 and 250 grams/10 minutes.

TABLE I______________________________________Melt Flow Index and Polymer TemperatureDuring Mastication Without Initial HeatingTime Temperature Melt Flow Index(Hours) .degree.C. (Gms/10 min)______________________________________ExampleNo. 1 0 94 0.2 .08 94 -- .17 94 -- .25 94 -- .33 94 -- .42 94 -- .50 99 -- 1.0 96 -- 1.5 93 -- 2.0 88 -- 2.5 86 -- 4.0 77 -- 5.0 72 -- 6.0 69 -- 7.0 65 4.0 22.75 61 221.9 25.25 60 272.7 29.75 59 409.8 31.5 59 470.0ExampleNo. 2 0 0.2 6.75 62 7.2 23.5 62 170.5 25.5 62 201.9 27.0 62 227.4 29.0 62 261.3 30.5 61 283.6 32.5 61 325.0 37.25 61 443.8 37.75 61 465.0ExampleNo. 3 0 92 0.2 .08 92 -- .17 92 -- .25 92 -- .33 92 -- .42 92 -- .50 102 -- 1.0 98 -- 1.5 98 -- 2.0 92 0.7 2.5 88 -- 4.0 79 -- 5.0 75 2.6 6.0 70 -- 7.0 65 8.4 22.75 61 186.0 26.0 60 223.2 28.0 60 310.3 30.5 59 387.1 33.5 59 479.3______________________________________ TABLE II______________________________________Melt Flow Index and Polymer TemperatureDuring Mastication With Initial HeatingTime Temperature Melt Flow Index(Hours) .degree.C. (Gms/10 Mins)______________________________________ExampleNo. 4 0 0.2 .75 91 -- 2.0 91 -- 4.5 80 1.2 6.0 77 -- 7.25 73 2.4 10.0 71 6.0 23.0 59 -- 23.25 59 133.91 24.25 61 158.8 26.0 61 203.1 28.2 61 280.1 30.0 62 345.4 31.0 62 387.9 31.7 62 409.8 33.75 62 495.0ExampleNo. 5 0 91 0.2 .75 91 -- 1.5 91 0.4 3.5 81 1.2 5.0 75 2.5 6.5 70 4.5 10.5 61 -- 22.0 60 246.9 23.5 60 282.1 25.0 60 335.7 27.5 60 429.6 29.0 60 507.7______________________________________ TABLE III______________________________________Paticular Melt Flow lndex and Polymer TemperatureDuring Mastication With Initial HeatingTime Temperature Melt Flow Index(Hours) .degree.C. (Gms/10 Mins)______________________________________ExampleNo. 6 0 0.2 16.0 57 18.5 17.0 57 25.2 18.0 56 33.3 19.0 54 47.5ExampleNo. 7 0 0.2 2.0 78 0.6 6.0 69 1.7 8.0 69 2.9 23.5 69 106.2ExampleNo. 8 0 0.2 1.1 79 0.6 4.1 71 2.6 20.1 59 176.0 21.1 59 150.0 22.0 58 157.0 23.0 58 182.0 24.0 59 221.0 25.0 60 240.0______________________________________ With reference first to Tables I and II, the change in the melt flow index observed during the first several hours would provide no motivation to continue the mastication procedure. What is, therefore, unexpected is that by continuing for what might have been deemed an inordinate period of time one can perceive an increase in the melt flow index from the approximate 0.2 gms/10 minute for unprocessed gutta-percha up to approximately 500 gms/10 minutes--a 2500 fold increase.

Also by comparing the results of Table I with Tables II and III, it can be seen that the time periods were generally about two hours shorter to obtain a melt flow index of 450 grams and above with the initial heating step than where it was omitted.

Mastication of Example No. 1 was begun at room temperature and raised to 94.degree. C. during shearing and then cooled over the next 31.5 hours. Cooling was gradual for the first few hours as evidenced by the polymer temperatures. However, after 22 hours, the temperature of the polymer dropped several degrees, commensurate with the considerably increased melt index values. Generally, the same temperature profile was observed for Examples No. 2 and 3, the differences being that a warmer temperature of water was employed which resulted in a lower melt index at 22.75 hours than in Example 1 and a longer total mixing time. Example 1 also reached a melt index of 470 after 31.5 hours while Example 3 required 33.5 hours to reach 479 and Example 2 had only a melt index of 465 after 37.75 hours.

Examples 4 and 5 in Table II were begun with heat as previously noted and it can be seen that the time was further shortened in Example 4 to 29 hours to reach a melt flow index of 507. Finally, with respect to the data in Table III, three different ranges of melt flow index having been provided which establish that desired values falling between the broad ranges of 20 and 500 grams/10 minutes can be obtained controlling the time of mastication.

With reference to the drawing figure, a plot of melt flow index versus time has been provided using values from Examples 1-8. Mastication for approximately that period of time represented between points A and B on the curve revealed the existence of a generally linear relationship between the melt flow index and the time of mastication. Between points B and C a pronounced change occurred which is the "knee" of the curve, and it represents a transitional range heretofore designated as the quantum change. This knee was found to occur within a total range of between 10 to 20 hours, with the majority of the samplings reflecting the occurrence of the knee within an approximate range of from 14 to 19 hours. It was also noted that the knee was fairly well developed by the time the melt flow index reached approximately 20-25 grams/10 minutes, irrespective of the mastication time required to being the melt flow index to that level.

Finally, from point C to, and past, point D the plot had a totally different slope than encountered between points A and B. A generally linear relationship was thus also determined to exist between the melt flow index and the time of mastication beyond the "knee."

Comparing the slope of the linear relationship between points A and B and the slope of the linear relationship between points C and D a change in excess of two orders of magnitude can be determined. Within the time frame from points A to B, there is no indication that continued mastication would produce the transitional rate of change represented by the knee nor that the plot would thereafter slope more favorably to reflect markedly higher and higher melt flow indices with respect to relatively modes further mastication time.

Following processing, the customary additives, such as those identified above, can be intermixed into the gutta-percha by a 20 to 60 minute milling or other mixing process. The additives will tend to reduce the melt flow index on the order of at least 50% but this decrease can be obviated by additional mastication. Those skilled in the art will readily appreciate that various means of providing additional mastication can be employed.

Gutta-percha having such a markedly increased melt flow index may be heated to approximately 70.degree. C. and injected through a needle fully to fill the entire cavity of a root canal. The gutta-percha so processed flows the full distance from the needle to the apex of the canal. Moreover, gutta-percha so processed will flow fully to the apex and laterally into any and all irregularities, usually including lateral canals, all without requiring additional manipulation with finger pluggers or the like.

Gutta-percha with such an increased melt flow index also appears more effectively to "wet" the dentin wall and seal the same without the necessity of employing a separate sealer. Finally, the gutta-percha so processed does not as readily pull away from the walls as a result of shrinkage as it cools, thus maintaining the necessary seal.

The significance of this novel process is critical in fields such as endodontia. By increasing the melt index of the polymer, thermoplastic injection molding can be performed at much lower and safer temperatures, such as about 66.degree. C. Such lower plasticization temperatures make clinical application of this technique readily available and obviate the need for sophisticated delivery systems or alternative obturation techniques. By processing the gutta-percha in accord with the novel process disclosed herein, the polymer can be plasticized at a clinically more acceptable temperature. The lower temperature also minimizes shrinkage of the material upon cooling, thus improving the integrity of the seal. It will also be appreciated by one skilled in the art that use of a higher melt-index polymer with other obturation techniques such as, for example, lateral and vertical condensation and automated thermatic condensation, will greatly enhance the utility of those techniques.

The exact mixing or milling criteria will, of course, be dependent on the particular flow characteristic desired for the material and the particular use to be made thereof. Inasmuch as the present invention is subject to many variations and changes in detail, a number of which have been expressly stated herein, it is intended that all matter described throughout this entire specification be interpreted as illustrative rather than limiting.

It must be appreciated that for the endodontic procedures presently contemplated a melt flow index of 500 grams per 10 minutes has been found to be perfectly adequate. As a result, no attempts have been made to continue mastication beyond that point. It should also be understood that there have been no indications that would dissuade one from believing that even higher melt flow indices would be obtained by approximately increased mastication times.

It should thus be evident that a material prepared according to the concepts of the present invention, or reasonably equivalent methods, will accomplish the objects of the present invention and otherwise substantially improve the art of thermoplastic polymers.

Claims

1. A novel endodontic thermoplastic polymer composition, consisting essentially of a thermoplastic polymer selected from the group consisting of synthetic and natural trans-polyisoprene having a melt flow index exceeding at least about 10 grams per 10 minutes at 105.degree. C.

2. A novel endodontic thermoplastic polymer composition, as set forth in claim 1, wherein said melt flow index of said thermoplastic polymer is approximately 50 grams per 10 minutes.

3. A novel endodontic thermoplastic polymer composition, as set forth in claim 1, wherein said melt flow index of said thermoplastic polymer is approximately 100 grams per 10 minutes.

4. A novel endodontic thermoplastic polymer composition, as set forth in claim 1, wherein said melt flow index of said thermoplastic polymer is approximately 250 grams per 10 minutes.

5. A novel endodontic thermoplastic polymer composition, as set forth in claim 1, wherein said melt flow index of said thermoplastic polymer is approximately 500 grams per 10 minutes.

6. A novel endodontic thermoplastic polymer composition, as set forth in claim 1, wherein said thermoplastic polymer is selected from the group consisting of gutta-percha and balata.