This invention relates to providing a system for improved thermoplastic induction-welding. More particularly, this invention relates to new compositions of matter that can be used to induction-weld seams in polymer pipes.
Since the earliest days of plumbing, water and drainage pipes have been made of metal and connected by welding or threading. Threaded pipes are difficult to assemble and manufacture, and welding requires substantial skill and risks causing fire or other property damage due to extreme heat and hazardous fumes. More recently, plastic pipes such as PVC (polyvinyl chloride), ABS (acrylonitrile butadience styrene), and PE (polyethylene) pipes have been implemented; however, these require volatile, messy, and toxic solvents in order to bond properly. Improvements in bonding methodology would be helpful to improve bond quality and to reduce installation hazards.
The present invention provides a system overcoming the above-mentioned problems, which can be used to induction-weld seams in polymer pipes. The invention further provides such a system that is efficient, inexpensive, and handy to use.
In accordance with one aspect, this invention provides a system for thermoplastic induction welding of polymer pipes, including a flexible ferromagnetic strip configured to fit within a coupling of a polymer pipe; an electromagnetic induction coil configured to surround said coupling; and a power supply electrically connectable to said electromagnetic induction coil and configured to cause said coil to generate an electromagnetic field upon energizing thereof by said power supply; whereby a flow of current is induced in said ferromagnetic strip to heat said strip, resulting in thermoplastic welding of separate polymer pipe segments located within the coupling.
In accordance with another aspect, this invention provides a flexible ferromagnetic strip configured to fit within a coupling of a polymer pipe to cause thermoplastic induction welding of separate polymer pipe segments within the coupling upon heating of the strip by electromagnetic induction current, the ferromagnetic strip containing a polymer binder combined with at least one surfactant and at least one ferromagnetic material.
In a preferred embodiment of the present invention, a flexible ferromagnetic strip 102, consisting substantially of ferromagnetic particles embedded in a low-density polyethylene (LDPE) material, is preferably formed into a ring shape, as shown in
A preferred composition of ferromagnetic strip material is a low-density polyethylene (LDPE) binder combined with at least one surfactant and at least one ferromagnetic material. More specifically, the preferred material composition is a blend of strontium ferrite, a surfactant and an LDPE binder. Tables 1-5 below present preferred example compositions according to exemplary embodiments of the invention. A preferred ferromagnetic material is a sheet-grade strontium ferrite (sold under the tradename HM410 “Starbond” strontium ferrite powder by Hoosier Magnetics, Inc.) comprising “large” particle size.
Upon reading this specification, those with ordinary skill in the art will now appreciate that, under appropriate circumstances, considering such issues as user preferences, cost, structural requirements, available materials, technological advances, etc., other material compositions such as, for example, MDPE binders, HDPE binders, etc., may suffice.
Through extensive experimental testing, applicant determined that a strontium ferrite loading of greater than or equal to about 50 vol % is most preferred. Applicant determined that a strontium ferrite loading of less than about 30 vol % fails to produce an adequate thermal weld and is therefore less preferred. The composition is also less preferred if the coupler strip is too brittle (that is, the sheet must wrap around a cylinder having an outer diameter of about 4½ inches). General mechanical properties of the preferred compositions are provided in Tables 6-8 below.
Flexible ferromagnetic strip 102 is preferably formed using one of several preferred processes.
Applicant determined that better loading ferromagnetic material was achieved when LDPE is used. Furthermore, applicant determined that the resulting product was less brittle. The filler dispersing agent (surfactant) allows higher loadings of the strontium ferrite in polyethylene while maintaining good flexibility. The surfactant increases the toughness, tear strength, and elongation of the coupler strip/sheet. A preferred surfactant is an organic surfactant, preferably comprising a polyester resin such as BioRez® 66-116-A, commercially available from Advanced Images Resources, Alpharetta, Ga. Alternately preferably, the surfactant preferably comprises stearic acid. Alternately preferably, the surfactant comprises calcium stearate. Alternately preferably, the surfactant comprises at least one tackifying resin such as at least one abietic acid ester, at least one rosin ester, or at least one terpene phenolic resin. Such at least one rosin ester preferably comprises rosin esters sold under the trademark Foral® or Pentrex™. Alternately preferably, the surfactant comprises at least one styrene-acrylate copolymer such as Pliolite® AC-L. Alternately preferably, the surfactant comprises at least one acrylate copolymer resin such as Pliolite® LV72. Alternately preferably, the polymer binder comprises other thermoplastics or thermoplastic combinations.
In testing, successful joining of pipe members was achieved using an induction frequency of about 400 Hz, which was observed to produce melt temperatures within the region of the ferromagnetic material of about 300-degree Fahrenheit (F). In an alternate preferred embodiment of the present system, the ferromagnetic material is preferably set into an additional wire mesh located inside the coupler to control field, flow, and physical position of the thermoplastic forming the pipe fitting.
Although applicant has described applicant's preferred embodiments of this invention, it will be understood that the broadest scope of this invention includes modifications such as diverse shapes, sizes, and materials. Such scope is limited only by the below claims as read in connection with the above specification. Further, many other advantages of applicant's invention will be apparent to those skilled in the art from the above descriptions and the below claims.