Patent Grant
7569273
This invention relates generally to rapid prototyping techniques and, more particularly, to a three-dimensional printing material and method using thermoplastic particulate mixtures.
The field of rapid prototyping involves the production of prototype articles and small quantities of functional parts, as well as structural ceramics and ceramic shell molds for metal casting, directly from computer-generated design data.
Two well-known methods for rapid prototyping include a selective laser sintering process and a liquid binder three-dimensional printing process. These techniques are similar to the extent that they both use layering techniques to build three-dimensional articles. Both methods form successive thin cross-sections of the desired article. The individual cross-sections are formed by bonding together adjacent grains of a granular material on a generally planar surface of a bed of the granular material. Each layer is bonded to a previously formed layer to form the desired three-dimensional article at the same time as the grains of each layer are bonded together. The laser-sintering and liquid binder techniques are advantageous, because they create parts directly from computer-generated design data and can produce parts having complex geometries. Moreover, three-dimensional printing can be quicker and less expensive than machining of prototype parts or production of cast or molded parts by conventional “hard” or “soft” tooling techniques, that can take from a few weeks to several months, depending on the complexity of the item.
Three-dimensional printing has been used to make ceramic molds for investment casting, to produce fully functional cast metal parts. Additional uses are contemplated for three-dimensional printing. For example, three-dimensional printing may be useful in design-related fields for visualization, demonstration, and mechanical prototyping. It may also be useful for making patterns for molding processes. Three-dimensional printing techniques may be further useful, for example, in the fields of medicine and dentistry, where expected outcomes may be modeled prior to performing procedures. Other businesses that may benefit from rapid prototyping technology include architectural firms, as well as others in which visualization of a design is useful.
A selective laser sintering process is described in U.S. Pat. No. 4,863,568, incorporated herein by reference in its entirety. The selective laser sintering process has been commercialized by DTM Corporation. The selective laser sintering process involves spreading a thin layer of powder onto a flat surface. The powder is spread using a tool developed for use with the selective laser sintering process, known in the art as a counter-rolling mechanism or counter-roller. Using the counter-roller allows thin layers of material to be spread relatively evenly, without disturbing previous layers. After the layer of powder is spread onto the surface, a laser is used to direct laser energy onto the powder in a predetermined two-dimensional pattern. The laser sinters or fuses the powder together in the areas impinged upon by the laser beam energy. The powder may be plastic, metal, polymer, ceramic or a composite. Successive layers of powder are spread over previous layers using the counter-roller, followed by sintering or fusing with the laser. The process is essentially thermal, requiring delivery by the laser of a sufficient amount of energy to sinter the powder together, and to previous layers, to form the final article.
An early three-dimensional printing technique, described in U.S. Pat. No. 5,204,055, incorporated herein by reference in its entirety, describes the use of an ink-jet style printing head to deliver a liquid or colloidal binder material to sequentially applied layers of powdered material. The three-dimensional ink-jet printing technique or liquid binder method involves applying a layer of a powdered material to a surface using a counter-roller. After the powdered material is applied to the surface, the ink-jet printhead delivers a liquid binder in a predetermined pattern to the layer of powder. The binder infiltrates into gaps in the powder material and hardens to bond the powder material into a solidified layer. The hardened binder also bonds each layer to the previous layer. After the first cross-sectional portion is formed, the previous steps are repeated, building successive cross-sectional portions until the final article is formed. Optionally, an adhesive can be suspended in a carrier that evaporates, leaving the hardened adhesive behind. The powdered material may be ceramic, metal, plastic or a composite material, and may also include fibers. The liquid binder material may be organic or inorganic. Typical organic binder materials used are polymeric resins or ceramic precursors, such as polycarbosilazane. Inorganic binders are used where the binder is incorporated into the final articles; silica is typically used in such an application.
One advantage of using an ink-jet print head, rather than a laser, is that a plurality of spray nozzles used to deliver binder to the powder may be arranged side-by-side in a single print head. In selective laser sintering machines, only one laser is conventionally used to deliver energy to the powder. The combination of several spray nozzles increases the speed of liquid binder printing in comparison to laser-sintering, by allowing a larger area to be printed at one time. In addition, liquid binder printing equipment is much less expensive than the laser equipment, due to the high cost of the laser and the high cost of the related beam deflection optics and controls.
The powders, especially metallic powders, presently used in both selective laser sintering and liquid binder techniques present safety issues that may render them undesirable for use in an office environment. These safety issues may require special clothing and processing facilities to prevent, for example, skin contact or inhalation of toxic materials. In addition, more expense may be incurred through complying with regulations for the disposal of toxic materials. For these reasons, these techniques do not lend themselves to being used in typical office environments, such as architectural and design firms, or doctor's offices.
Another three-dimensional printing technique, described in U.S. Pat. Nos. 5,902,441 and 6,416,850, both references incorporated herein by reference in their entirety, utilizes a powder mixture containing a filler and an activatable adhesive in conjunction with an aqueous fluid that activates the adhesive to bind the filler. The fluid is applied by an ink-jet printhead. The filler and adhesive may each include non-toxic materials such as, for example, water-soluble polymers, carbohydrates, sugars, sugar alcohols, proteins, and some inorganic compounds.
There exists a need in the art for a materials system and method that enables the quick, reliable, safe, and inexpensive fabrication of appearance models and small batches of functional parts in an office environment. Such appearance models and parts need to have good-quality surfaces, to be accurately defined, and to be strong without being brittle. Furthermore, some kinds of models need specific mechanical properties such as flexibility for snap-fits or impact toughness.
The present invention is directed to a materials system and method that satisfies the need for a quick, reliable, safe, and inexpensive method for producing both appearance models and small numbers of functional parts in an office environment. The materials system includes thermoplastic particulate material, allowing the fabrication of appearance models and functional parts that are accurately defined, are strong and tough without being brittle, and have smooth surface finishes with, optionally, thin walls. Thermoplastic materials are used very widely for engineering and consumer products. These materials, therefore, are particularly attractive for prototyping, because they are typically also used in the final manufacturing method.
In an aspect, the invention features a powder adapted for three-dimensional printing. The powder includes a blend of a thermoplastic particulate material, and an adhesive particulate material, with the adhesive particulate material being adapted to bond the thermoplastic particulate material when a fluid activates the adhesive particulate material.
One or more of the following features may be included. The fluid may be aqueous, non-aqueous, and/or non-halogenated. The adhesive particulate material may include the thermoplastic particulate material, so that the thermoplastic particulate material is at least sparingly soluble and adhesive in the activating fluid and is adapted to bond together when the fluid activates the thermoplastic particulate material by at least partially dissolving the thermoplastic particulate material, the thermoplastic particulate material including at least one of the following materials: polymethylmethacrylate, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, poly(acrylonitrile-butadiene-styrene), polyamides, polycondensates of urea-formaldehyde, polystyrene; polyolefin, polyvinyl butyral, polycarbonate, polyvinyl chloride, polyethylene terephthalate, ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, cellulose acetate, hydroxypropylmethyl cellulose, hydroxybutylmethyl cellulose, hydroxyethylmethyl cellulose, ethylhydroxyethyl cellulose, cellulose xanthate, and combinations and copolymers thereof.
The fluid that activates the thermoplastic particulate material may be adapted to be solidifiable by exposure to at least one of ultraviolet light, visible light, heat, and an electron beam. The thermoplastic particulate material may include particles having a mean particle diameter of about 10 micrometers to about 100 micrometers.
The thermoplastic particulate material may include at least one of acetal polyoxymethylene, polylactide, polyethylene, polypropylene, ethylene vinyl acetate, polyphenylene ether, ethylene-acrylic acid copolymer, polyether block amide, polyvinylidene fluoride, polyetherketone, polybutylene terephthalate, polyethylene terephthalate, polycyclohexylenemethylene terephthalate, polyphenylene sulfide, polythalamide, polymethylmethacrylate, polysulfone, polyethersulfone, polyphenylsulfone, polyacrylonitrile, poly(acrylonitrile-butadiene-styrene), polyamide, polycondensates of urea-formaldehyde, polystyrene, polyolefin, polyvinyl butyral, polycarbonate, polyvinyl chlorides, polyethylene terephthalate, ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, cellulose acetate, hydroxypropylmethyl cellulose, hydroxybutylmethyl cellulose, hydroxyethylmethyl cellulose, ethylhydroxyethyl cellulose, cellulose xanthate, and combinations and copolymers thereof.
The adhesive particulate material may include particles having a mean particle diameter of about 10 micrometers to about 100 micrometers.
The adhesive particulate material may include a resin, such as a water-soluble resins or an alkaline-reducible resin, and the fluid may activate the adhesive particulate material by dissolving the adhesive particulate material. The resin may include at least one of the following materials: polyvinyl alcohol, sulfonated polyester polymer, sulfonated polystyrene, octylacrylamide/acrylate/butylaminoethyl methacrylate copolymer, acrylates/octylacrylamide copolymer, polyacrylic acid, polyvinyl pyrrolidone, styrenated polyacrylic acid, polyethylene oxide, sodium polyacrylate, sodium polyacrylate copolymer with maleic acid, polyvinyl pyrrolidone copolymer with vinyl acetate, butylated polyvinylpyrrolidone, polyvinyl alcohol-co-vinyl acetate, starch, modified starch, cationic starch, pregelatinized starch, pregelatinized modified starch, pregelatinized cationic starch, and combinations and copolymers thereof.
The adhesive may include an inorganic adhesive, such as at least one of plaster, bentonite, precipitated sodium silicate, amorphous precipitated silica, amorphous precipitated calcium silicate, amorphous precipitated magnesium silicate, amorphous precipitated lithium silicate, salt, portland cement, magnesium phosphate cement, magnesium oxychloride cement, magnesium oxysulfate cement, zinc phosphate cement, zinc oxide-eugenol cement, aluminum hydroxide, magnesium hydroxide, calcium phosphate, sand, wollastonite, dolomite, amorphous precipitated silicates containing at least two types of ions selected from the group of sodium ions, lithium ions, magnesium ions, and calcium ions, and combinations thereof.
The powder may include a filler material, and the filler material may include particles having a mean particle diameter of about 5 micrometers to about 100 micrometers. The filler material may include an inorganic material, such as aluminum oxide, soda-lime glass, borosilicate glass, silica, aluminosilicate ceramic, limestone, plaster, bentonite, precipitated sodium silicate, amorphous precipitated silica, amorphous precipitated calcium silicate, amorphous precipitated magnesium silicate, amorphous precipitated lithium silicate, salt, portland cement, magnesium phosphate cement, magnesium oxychloride cement, magnesium oxysulfate cement, zinc phosphate cement, zinc oxide-eugenol cement, aluminum hydroxide, magnesium hydroxide, calcium phosphate, sand, wollastonite, dolomite, amorphous precipitated silicates containing at least two type of ions selected from the group of sodium ions, lithium ions, magnesium ions, and calcium ions, and combinations thereof.
The filler material may include an organic material. The organic material may include a carbohydrate, such as starch, modified starch, cellulose, maltodextrin, acacia gum, locust bean gum, pregelatinized starch, acid-modified starch, hydrolyzed starch, sodium carboxymethylecellulose, sodium alginate, hydroxypropyl cellulose, methyl cellulose, chitosan, carrageenan, pectin, agar, gellan gum, gum Arabic, xanthan gum, propylene glycol alginate, guar gum, and combinations thereof. The organic material may include a protein, such as gelatin, rabbit-skin glue, soy protein, and combinations thereof.
The powder may include a processing aid material, such as a viscous liquid and/or a polymer having a low melting point. The processing aid material may include at least one of the following materials: polyethylene glycol, polypropylene glycol, sorbitan monolaurate, sorbitan monooleate, sorbitan trioleate, polysorbate, poly(ethylene oxide) modified silicone, poly (propylene oxide) modified silicone, secondary ethoxylated alcohols, ethoxylated nonylphenols, ethoxylated octylphenols, C8-C10 alcohols, C8-C10 acids, polyethylene oxide modified acetylenic diols, citronellol, ethoxylated silicones, ethylene glycol octanoate, ethylene glycol decanoate, ethoxylated derivatives of 2,4,7,9-tetramethyl-5-decyne-4,7-diol, polyoxyethylene sorbitan mono-oleate, polyethylene glycol, soybean oil, mineral oil, fluroalkyl polyoxyethylene polymers, glycerol triacetate, oleyl alcohol, oleic acid, squalene, squalane, essential oils, esters, terpenes, greases, or waxes, propylene glycol, ethylene glycol, C8-C10 esters of mono, di, or triglycerides, fatty acids, ethoxylated fatty acids, lecithin, modified lecithins, glycerol tributyrate, sodium stearoyl lactylate, diacetyl tartaric esters of mono- and di-glycerides, corn syrup, and combinations thereof.
The powder may include a reinforcing fiber. The reinforcing fiber may include at least one of the following materials: natural polymers, modified natural polymers, synthetic polymers, ceramic, cellulose fiber, silicon carbide fiber, graphite fiber, aluminosilicate fiber, polypropylene fiber, fiberglass, polyamide flock, cellulose, rayon, polyvinylalcohol, and combinations thereof.
The powder may include approximately 50-100% thermoplastic particulate material, 0-20% filler material, 0-30% adhesive particulate material, and 0-2% processing aid material.
In another aspect, the invention features a fluid for three-dimensional printing, the fluid including a first solvent having a first boiling point. The fluid is adapted to activate an adhesive in a powder comprising a blend of a thermoplastic particulate material and an adhesive particulate material.
One or more of the following features may be included. The fluid may be adapted to activate the adhesive by dissolving the adhesive particulate material. The first solvent may include one or more of the following materials: ethanol, isopropanol, n-propanol, methanol, n-butanol, a glycol, an ester, a glycol-ether, a ketone, an aromatic, an aliphatic, an aprotic polar solvent, a terpene, an acrylate, a methacrylate, a vinylether, an oxetane, an epoxy, a low molecular weight polymer, carbonate, n-methylpyrrolidone, acetone, methyl ethyl ketone, dibasic esters, ethyl acetate, dimethyl sulfoxide, dimethyl succinate, and combinations thereof.
The fluid may include a second solvent having a second boiling point. The second boiling point may be higher than the first boiling point, and/or the second solvent may be water-miscible. The second solvent may include one or more of the following materials: butyrolactone, glycerol carbonate, propylene carbonate, ethylene carbonate, dimethyl succinate, dimethyl sulfoxide, n-methyl pyrrolidone, glycerol, 1,4butane diol, polyethylene glycol, diethylene glycol butyl ether, ethylene glycol, diethylene glycol, propylene glycol, polypropylene glycol, polyethylene glycol ethers, polypropylene glycol ethers, tetraethyleneglycol ethers, butylene carbonate, pentanediol, hexanediol, and combinations thereof.
The fluid may include water. The first solvent may be water-miscible. The second solvent may be water-miscible. The second solvent may have a second boiling point that is higher than the first boiling point.
The fluid may include a surfactant. The surfactant may include at least one of the following materials: polyethylene oxide modified acetylenic diols, secondary ethoxylated alcohols, ethoxylated nonylphenols, ethoxylated silicones, ethoxylated fluorinated surfactants, ethoxylated tetramethyldecynediol, ethoxylated tetramethyldodecynediol, polyethermodified polysiloxanes, ethoxylated sorbitan monolaurate, octyl phenoxypolyethoxy-polypropoxy-propanol, sulfonated fatty acids, zwitterionic betaines, sodium di-octyl sulfosuccinate, dimethyl dodecylammoniopropane sulfonate, sodium lauryl sulfate, sodium lauryl benzene sulfonate, sodium p-toluene sulfonate, sodium benzoate, sodium benzene sulfonate, potassium sorbate, sodium 2-ethylhexyl sulfonate, and combinations thereof.
The fluid may include a rheology modifier. The rheology modifier may include at least one of the following materials: polyvinylpyrrolidone, polyacrylamide, polyethylene oxide, hydrophobe modified ethoxy urethanes, polyvinyl alcohol, polyacrylic acid, polymethacrylic acid, alkali and ammonium salts of polyacrylic acid, alkali and ammonium salts of polymethacrylic acid, polyvinylpyrrolidone-co-vinyl acetate, butylated polyvinylpyrrolidone, polyvinylalcohol-co-vinyl acetate, and polyacrylic acid-co-maleic anhydride, sulfonated polystyrene, and combinations and copolymers thereof.
The fluid may include an amine. The amine may include at least one of the following materials: monoisopropanol amine, triethylamine, 2-amino-2-methyl-1-propanol, 1-amino-2-propanol, 2-dimethylamino-2-methyl-1-propanol, N,N-diethylethanolamine, N-methyldiethanolamine, N,N-dimethylethanolamine, triethanolamine, 2-aminoethanol, 1-[bis[3-(dimethylamino)propyl]amino]-2-propanol, 3-amino-1-propanol, 2-(2-aminoethylamino)ethanol, tris(hydroxymethyl)aminomethane, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1,3-propanediol, diethanolamine, 1,3-bis(dimethylamino)-2-propanol, ammonium hydroxide, monoethanolamine, aminomethylpropanol, aminoethylethanolamine, triisopropanolamine, polyoxypropylenetriamine, polyethyleneimine, and combinations thereof.
In another aspect, the invention features a fluid for three-dimensional printing, the fluid including a solvent. The fluid is adapted to activate the adhesive properties of at least a sparingly soluble thermoplastic particulate material.
One or more of the following features may be included. The fluid may be non-aqueous, and it may be non-halogenated. The solvent may include at least one of the following materials: an alcohol, a glycol, an ester, a glycol-ether, a ketone, an aromatic, an aliphatic, an aprotic polar solvent, a terpene, an acrylate, a methacrylate, a vinylether, an oxetane, an epoxy, a low molecular weight polymer, carbonate, and combinations thereof.
The alcohol may include at least one of the following materials: methanol, ethanol, n-propanol, i-propanol, n-butanol and combinations thereof. The glycol may include at least one of the following materials: ethylene glycol, diethylene glycol, propylene glycol, polyethyleneglycol, 1,4-butanediol, pentanediol, hexanediol, and combinations thereof.
The ester may include at least one of the following materials: ethyl acetate, propyleneglycol methylether acetate, amyl acetate, dimethylsuccinate, dimethyl glutarate, dimethyl adipate, diethylene glycol monobutyl ether acetate, n-propyl acetate, i-propyl acetate, i-butyl acetate, n-butyl acetate, t-butyl acetate, 2-ethylhexyl acetate, ethylene glycol diacetate, diethyl succinate, methyl lactate, ethyl lactate, dimethyl tartrate, diethyl tartrate and combinations thereof. The glycol-ether may include at least one of the following materials: dipropylene glycol methyl ether, diethylene glycol butyl ether, diethylene glycol monoethyl ether, propylene glycol methyl ether, ethylene glycol propyl ether and combinations thereof.
The ketone may include at least one of the following materials: acetone, methylethylketone, methylisobutylketone, methyl isopropyl ketone, methyl n-propyl ketone, methyl isoamyl ketone, methyl n-amyl ketone, diisobutyl ketone and combinations thereof. The aromatic may include at least one of the following materials: toluene, xylene, phenol, benzene, styrene, high flash aromatic naptha and combinations thereof.
The aliphatic may include at least one of the following materials: hexane, heptane, cyclohexane and combinations thereof. The aprotic polar solvent may include at least one of the following materials: n-methylpyrrolidone, dimethylsulfoxide, 2-pyrrolidone, butyrolactone and combinations thereof. The terpene may include limonene.
The acrylate may include at least one of the following materials: alkoxylated difunctional acrylate, 2-phenoxyethyl acrylate, tetrahydrofurfuryl acrylate, 2(2 ethoxyethoxy)ethyl acrylate, hexanediol diacrylate, propoxylated neopentyl glycol diacrylate, lauryl acrylate, isodecyl acrylate, tridecyl acrylate, isobornyl acrylate, tripropylene glycol diacrylate, stearyl acrylate, allyl acrylate, isooctylacrylate, caprolactone acrylate, alkoxylated tetrahydrofurfuryl acrylate, butanediol diacrylate, 1,3-butyleneglycol diacrylate, diethylene glycol diacrylate, polyethylene glycol diacrylate, alkoxylated hexanediol diacrylate, alkoxylated cyclohexane dimethanol diacrylate, cyclohexane dimethanol diacrylate, dipropylene glycol diacrylate, ethoxylated bisphenol A diacrylate, neopentyl glycol diacrylate, alkoxylated aliphatic diacrylate, trimethylpropane triacrylate, tris (2-hydroxy ethyl) isocyanurate triacrylate, ethoxylated trimethyl propane triacrylate, propoxylated trimethyl propane triacrylate, propoxylated glyceryl triacrylate, pentaerythritol tetraacrylate, pentaerythritol triacrylate, di-trimethylpropane tetraacrylate, dipentaerythritol pentaacrylate, ethoxylated pentaerythritol tetraacrylate, alkoxylated nonyl phenol acrylate, and combinations thereof.
The methacrylate may include at least one of the following materials: 2-phenoxyethyl methacrylate, tetrahydrofurfuryl methacrylate, hexanediol dimethacrylate, lauryl methacrylate, isodecyl methacrylate, tridecyl methacrylate, isobornyl methacrylate, propylene glycol monomethacrylate, stearyl methacrylate, allyl methacrylate, isooctylmethacrylate, butanediol dimethacrylate, 1,3-butyleneglycol dimethacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol dimethacrylate, cyclohexane dimethanol dimethacrylate, dipropylene glycol dimethacrylate, ethoxylated bisphenol A dimethacrylate, neopentyl glycol dimethacrylate, trimethylpropane trimethacrylate, methoxy polyethylene glycol methacrylate, alkoxylated nonyl phenol methacrylate, ethoxylated hydroxyethyl methacrylate, allyl methacrylate, propoxylated allyl methacrylate, and combinations thereof.
The vinyl ether may include at least one of the following materials: hydroxylbutyl vinyl ether, triethyleneglycol divinylether, cyclohexanedimethanol divinylether, propenylether of propylene carbonate, dodecylvinylether, cyclohexanemethanol monovinylether, cyclohexyl vinyl ether, diethyleneglycol divinylether, 2-ethylhexylvinylether, dipropyleneglycol divinylether, tripropyleneglycol divinyl ether, hexanediol divinyl ether, octadecylvinylether, butanediol divinyl ether, bis[4-(vinyloxy)butyl]isophthalate, bis[4-(vinyloxy)butyl]adipate, and combinations thereof.
The oxetane may include at least one of the following materials: 3-ethyl-3-hydroxymethyl-oxetane, 1,4-bis[(3-ethyl-3-oxetanyl methoxy)methyl]benzene, and combinations thereof. The epoxy may include at least one of the following materials: 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, bis-(3,4-epoxycyclohexyl) adipate, limonene monoxide, 1,2-epoxyhexadecane, and combinations thereof. The low molecular weight polymer may include polyethyleneimine. The carbonate may include ethylene carbonate, propylene carbonate, butylene carbonate, glycerol carbonate, and combinations thereof.
The fluid may include water and the solvent may include a second solvent having a second boiling point. The second solvent may include at least one of the following materials: butyrolactone, glycerol carbonate, propylene carbonate, ethylene carbonate, dimethyl succinate, dimethyl sulfoxide, n-methyl pyrrolidone, glycerol, 1,4 butane diol, polyethylene glycol, diethylene glycol butyl ether, ethylene glycol, diethylene glycol, propylene glycol, polypropylene glycol, polyethylene glycol ethers, polypropylene glycol ethers, tetraethyleneglycol ethers, butylene carbonate, pentanediol, hexanediol, and combinations thereof.
The fluid may include a surfactant. The surfactant may include at least one of the following materials: polyethylene oxide modified acetylenic diols, secondary ethoxylated alcohols, ethoxylated nonylphenols, ethoxylated silicones, ethoxylated fluorinated surfactants, tetramethyldecynediol, ethoxylated tetramethyldecynediol, ethoxylated tetramethyldodecynediol, polyethermodified polysiloxanes, ethoxylated sorbitan monolaurate, octylphenoxypolyethoxy-polypropoxy-propanol, sulfonated fatty acids, zwitterionic betaines, sodium di-octyl sulfosuccinate, dimethyl dodecylammoniopropane sulfonate, sodium lauryl sulfate, sodium lauryl benzene sulfonate, sodium p-toluene sulfonate, sodium benzoate, sodium benzene sulfonate, potassium sorbate, sodium 2-ethylhexyl sulfonate, and combinations thereof.
The fluid may include a rheology modifier. The rheology modifier may include at least one of the following materials: polyvinylpyrrolidone, polyacrylamide, polyethylene oxide, hydrophobe modified ethoxy urethanes, polyvinyl alcohol, polyacrylic acid, polymethacrylic acid, alkali and ammonium salts of polyacrylic acid, alkali and ammonium salts of polymethacrylic acid, polyvinylpyrrolidone-co-vinyl acetate, butylated polyvinylpyrrolidone, polyvinylalcohol-co-vinyl acetate, and polyacrylic acid-co-maleic anhydride, sulfonated polystyrene, and combinations and copolymers thereof.
The fluid may also include a first solvent having a first boiling point, the first boiling point is lower than the second boiling point. The first solvent may include at least one of the following materials: ethanol, isopropanol, n-propanol, methanol, n-butanol, a glycol, an ester, a glycol-ether, a ketone, an aromatic, an aliphatic, an aprotic polar solvent, a terpene, an acrylate, a methacrylate, a vinylether, an oxetane, an epoxy, a low molecular weight polymer, carbonate, acetone, ethyl acetate, dimethyl succinate, and combinations thereof.
The fluid may include an amine. The amine may include at least one of the following materials: monoisopropanol amine, triethylamine, 2-amino-2-methyl-1-propanol, 1-amino-2-propanol, 2-dimethylamino-2-methyl-1-propanol, N,N-diethylethanolamine, N-methyldiethanolamine, N,N-dimethylethanolamine, triethanolamine, 2-aminoethanol, 1-[bis[3-(dimethylamino)propyl]amino]-2-propanol, 3-amino-1-propanol, 2-(2-aminoethylamino)ethanol, tris(hydroxymethyl)aminomethane, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1,3-propanediol, diethanolamine, 1,3-bis(dimethylamino)-2-propanol, ammonium hydroxide, monoethanolamine, aminomethylpropanol, aminoethylethanolamine, triisopropanolamine, polyoxypropylenetriamine, polyethyleneimine, and combinations thereof.
In another aspect, the invention features a fluid for three-dimensional printing, the fluid including water and an amine, and the fluid is adapted to activate the adhesive properties of at least a sparingly soluble alkaline-reducible particulate material.
One or more of the following features may be included. The amine may include at least one of the following materials: monoisopropanol amine, triethylamine, 2-amino-2-methyl-1-propanol, 1-amino-2-propanol, 2-dimethylamino-2-methyl-1-propanol, N,N-diethylethanolamine, N-methyldiethanolamine, N,N-dimethylethanolamine, triethanolamine, 2-aminoethanol, 1-[bis[3-(dimethylamino) propyl]amino]-2-propanol, 3-amino-1-propanol, 2-(2-aminoethylamino) ethanol, tris(hydroxymethyl)aminomethane, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1,3-propanediol, diethanolamine, 1,3-bis(dimethylamino)-2-propanol, ammonium hydroxide, monoethanolamine, aminomethylpropanol, aminoethylethanolamine, triisopropanolamine, polyoxypropylenetriamine, polyethyleneimine, and combinations thereof.
The fluid may include a first solvent having a first boiling point. The first solvent may include at least one of the following materials: ethanol, isopropanol, n-propanol, methanol, n-butanol, a glycol, an ester, a glycol-ether, a ketone, an aromatic, an aliphatic, an aprotic polar solvent, a terpene, an acrylate, a methacrylate, a vinylether, an oxetane, an epoxy, a low molecular weight polymer, carbonate, acetone, ethyl acetate, dimethyl succinate, and combinations thereof.
The fluid may include a second solvent having a second boiling point, with the second boiling point is higher than the first boiling point. The second solvent may include at least one of the following materials: butyrolactone, glycerol carbonate, propylene carbonate, ethylene carbonate, dimethyl succinate, dimethyl sulfoxide, n-methyl pyrrolidone, glycerol, 1,4 butane diol, polyethylene glycol, diethylene glycol butyl ether, ethylene glycol, diethylene glycol, propylene glycol, polypropylene glycol, polyethylene glycol ethers polypropylene glycol ethers, tetraethyleneglycol ethers, butylene carbonate, pentanediol, hexanediol, and combinations thereof.
The fluid may include a surfactant. The surfactant may include at least one of the following materials: polyethylene oxide modified acetylenic diols, secondary ethoxylated alcohols, ethoxylated nonylphenols, ethoxylated silicones, ethoxylated fluorinated surfactants, tetramethyldecynediol, ethoxylated tetramethyldecynediol, ethoxylated tetramethyldodecynediol, polyethermodified polysiloxanes, ethoxylated fluorocarbons, ethoxylated sorbitan monolaurate, octyl phenoxypolyethoxy-polypropoxy-propanol, sulfonated fatty acids, zwitterionic betaines, sodium di-octyl sulfosuccinate, dimethyl dodecylammoniopropane sulfonate, sodium lauryl sulfate, sodium lauryl benzene sulfonate, sodium p-toluene sulfonate, sodium benzoate, sodium benzene sulfonate, potassium sorbate, sodium 2-ethylhexyl sulfonate, and combinations thereof.
The fluid may include a rheology modifier. The rheology modifier may include at least one of the following materials: polyvinylpyrrolidone, polyacrylamide, polyethylene oxide, hydrophobe modified ethoxy urethanes, polyvinyl alcohol, polyacrylic acid, polymethacrylic acid, alkali and ammonium salts of polyacrylic acid, alkali and ammonium salts of polymethacrylic acid, polyvinylpyrrolidone-co-vinyl acetate, butylated polyvinylpyrrolidone, polyvinylalcohol-co-vinyl acetate, and polyacrylic acid-co-maleic anhydride, sulfonated polystyrene, and combinations and copolymers thereof.
In another aspect, the invention features a method for forming an article by three-dimensional printing. The method includes the steps of: providing a plurality of adjacent particles having a mean diameter of about 10 micrometers to about 100 micrometers, the particles including a blend of a thermoplastic particulate material and an adhesive particulate material; and applying to the plurality of particles a fluid, within which the adhesive particulate material is at least partially soluble and the thermoplastic particulate material is substantially inert, the fluid activating the adhesive particulate material from a substantially inert state, in an amount sufficient to bond the plurality of particles together to define a substantially solid, singular article.
The following features may be included. The article may be heated to at least partially sinter the thermoplastic particulate material.
In another aspect, the invention features a method for forming an article by three-dimensional printing. The method includes the steps of: providing a plurality of adjacent particles having a mean diameter of about 10 micrometers to about 100 micrometers, the particles including a blend of a thermoplastic particulate material and an adhesive particulate material; and applying to the plurality of particles a fluid, within which the adhesive particulate material is at least partially soluble and the thermoplastic particulate material is substantially inert, the fluid dissolving the adhesive particulate material, in an amount sufficient to bond the plurality of particles together to define a substantially solid, singular article.
The following feature may be included. The article may be heated to at least partially sinter the thermoplastic particulate material.
In another aspect, the invention features a method for forming an article by three-dimensional printing. The method includes the steps of applying, to a first portion of a first film of particles that includes a plurality of thermoplastic particles and an activatable adhesive, an aqueous fluid that activates the adhesive in an amount sufficient to form an essentially solid, singular article of adhered particles. A second film of the particles is formed on the first film. The aqueous fluid is applied to a first portion of the second film of particles in an amount sufficient to activate the adhesive to the extent that the particles within the first portion of the second film adhere to each other and to at least a portion of the first portion of the first film to form an essentially solid, singular article from the first portion of the first film and the first portion of the second film.
One or more of the following features may be included. The article may be heated to at least partially sinter the thermoplastic particulate material.
In another aspect, the invention features a method for forming an article by three-dimensional printing. The method includes the steps of: applying, to a first portion of a first film of particles that includes a plurality of thermoplastic particles, a non-aqueous fluid that activates the surface of the thermoplastic particles in an amount sufficient to form an essentially solid, singular article of adhered particles. A second film of the particles is formed on the first film. The non-aqueous fluid is applied, to a first portion of the second film of particles, in an amount sufficient to activate the surface of the thermoplastic particles to the extent that the particles within the first portion of the second film adhere to each other and to at least a portion of the first portion of the first film to form an essentially solid, singular article from the first portion of the first film and the first portion of the second film. At least one of an ultraviolet light, visible light, heat, and an electron beam is applied to the printed layer to induce the non-aqueous fluid to solidify.
In another aspect, the invention features an article including a product of: a powder, the powder including (i) a thermoplastic particulate material, and (ii) an adhesive particulate material, and a fluid that activates the adhesive particulate material to form a substantially solid article composed of the powder, the adhesive particulate material being substantially soluble in the fluid. The article includes a plurality of adjacent layers formed by the product, each layer having a contour defining an edge, and a final shape of the article being defined by respective edges of the layers.
One or more of the following features may be included. The powder may include a filler material and/or a processing aid material. The article may include an infiltrant. The infiltrant may include at least one of the following materials: epoxy-amine systems, free radical UV cure acrylate systems, cationic UV cure epoxy systems, two-part urethane systems including isocyanate-polyol and isocyanate-amine, cyanoacrylate, and combinations thereof.
These and other features, aspects and advantages of the present invention will become better understood with reference to the following description and appended claims.
The following drawings are not necessarily to scale, emphasis instead being placed generally upon illustrating the principles of the invention. The foregoing and other features and advantages of the present invention, as well as the invention itself, will be more fully understood from the following description of exemplary and preferred embodiments, when read together with the accompanying drawings, in which:
The present invention relates to a three-dimensional printing material system including a mixture of particles of thermoplastic particulate filler material and an adhesive particulate material, and optionally an additional filler material, a processing aid a reinforcing fiber, and/or a stabilizing fiber; and a fluid adapted to bind the thermoplastic particulate filler material to form an essentially solid article when the fluid activates the adhesive particulate material. The fluid may be aqueous or non-aqueous. As used herein, “aqueous fluid” means a fluid that contains preferably 25% or more water, more preferably 40% or more water, and most preferably 50% or more water. As used herein, “non-aqueous fluid” means a fluid that contains less than 25% water by weight, more preferably less than 10% by weight, and most preferably less than 1% water by weight. If the fluid is non-aqueous, it may include non-halogenated solvents. The present invention also relates to a method of use for such a materials system, and to an article made by the method of the invention. The article of the invention may be formed with excellent accuracy and an exceptional surface finish.
As used herein, “thermoplastic particulate material” is meant to define a filler component that is bonded when the adhesive particulate material is activated by a fluid, the component including a material that may be repeatedly softened by heating and hardened again on cooling. “Adhesive” is meant to define a component that forms a mechanical bridge between components of a network, such as particles, that were separate prior to activation by a fluid, e.g., the thermoplastic particulate material. The formation of the mechanical bridge results in the formation of a solid structure. The adhesive may be a water-soluble resin, and the fluid may activate the adhesive by dissolving the resin. “Resin” is meant to define a material that is a linear or branched chain of organic chemical subunits with a minimum molecular weight of 500 grams per mole. In some embodiments, the adhesive includes the thermoplastic material itself. “Filler” is meant to define a component that is solid prior to application of the activating fluid, which is substantially less soluble in the fluid than the adhesive, and which gives structural integrity to the final article. Fillers in addition to the thermoplastic material may be used, such as various inorganic or organic materials. “Bond” is meant to define the building of a mechanical bridge between separate particles to form a network.
The particulate mixture may include a reinforcing fiber or a reinforcing fibrous component, added to provide structural reinforcement to the final article. As used herein, “fiber” or “fibrous component” is meant to define a component that is solid prior to application of the activating fluid, which may be advantageously, but not necessarily, insoluble in the fluid. The fiber or fibrous component may be added to increase the final article strength. In some embodiments, a stabilizing fiber may be added to the filler to provide dimensional stability to the final article to control the migration of liquid through the bulk powder, and to increase slightly the article strength.
A fiber is a solid component whose primary grains have an average length that is at least 3-4 times longer than their average cross-sectional dimensions. Such materials are very common in industry. For the purposes of three-dimensional printing, fibers are generally useful in a restricted size range, i.e., approximately the thickness of spread layers of powder and smaller.
In some embodiments, a processing aid compound, such as a viscous liquid that serves as a printing aid, may be added to the particulate mixture to prevent or minimize distortions in printing. The processing aid prevents fine particles of the mixture from becoming airborne while the liquid is dispensed from the printhead, which could distort the printed article from the desired configuration.
Referring to
Referring to
The first portion 30 of the particulate mixture is activated by the fluid 26, causing the activated particles to adhere together to form an essentially solid circular layer that becomes a cross-sectional portion of a final article 38 (see, e.g.,
Any unactivated particulate mixture 32 that was not exposed to the fluid remains loose and free-flowing on the movable surface 22. The unactivated particulate mixture is typically left in place until formation of the final article 38 is complete. Leaving the unactivated, loose particulate mixture in place ensures that the article 38 is fully supported during processing, allowing features such as overhangs, undercuts, and cavities to be defined and formed without the need to use supplemental support structures. After formation of the first cross-sectional portion of the final article 38, the movable surface 22 is indexed downwardly, in this embodiment, and the process is repeated.
Using, for example, a counter-rolling mechanism, a second film or layer of the particulate mixture is then applied over the first layer, covering both the rigid first cross-sectional portion, and any proximate loose particulate mixture. A second application of fluid follows in the manner described above, dissolving the adhesive and forming adhesive bonds between at least a portion of the previous cross-sectional formed portion, the thermoplastic particulate material, and, optionally, additional filler and fiber of the second layer, and hardening to form a second rigid cross-sectional portion added to the first rigid cross-sectional portion of the final article. The movable surface 22 is again indexed downward.
The previous steps of applying a layer of particulate mixture, including the adhesive, applying the activating fluid, and indexing the movable surface 22 downward are repeated until the final article 38 is completed. Referring to
Referring to
The method of the present invention is capable of producing features having dimensions on the order of about 250 micrometers (μm) or more. The accuracy achieved by the method of the present invention is in the range of about ±250 μm. Shrinkage of the final article 38 is about 1%, which may easily be factored into the build to increase accuracy. The surface finish is of fine quality, having a porosity of ˜50% and a surface roughness of ˜200 μm. Final article 38 may have thin walls with thicknesses of, for example, ˜1 millimeter (mm).
Powder Constituents
Thermoplastic Particulate Filler Material
Thermoplastic particulate material is a major component of the materials system of the invention. This particulate material may include any thermoplastic material with a mean particle diameter of about 10 μm to about 100 μm, although sizes outside this range are also contemplated.
Some examples of suitable thermoplastic powder material are:
Adhesive
The adhesive particulate material is a compound selected for one or more of the characteristics of high solubility in the activating fluid, low solution viscosity, low hygroscopicity, and high bonding strength. The adhesive is preferably highly soluble in the activating fluid to ensure that it is rapidly and substantially completely incorporated into the fluid. The adhesive is milled very finely prior to admixture with the thermoplastic particulate filler material and/or the filler particles in order to increase the available surface area, enhancing dissolution in the fluid, without being so fine as to cause “caking,” an undesirable article characteristic in which unactivated powder spuriously adheres to the outside surface of the part, resulting in poor surface definition. Typical adhesive particle diameters are about 10 μm to about 100 μm. Low hygroscopicity of the adhesive avoids absorption of excessive moisture from the air, which may also contribute to undesirable caking.
In some embodiments, the adhesive of the present invention is water-soluble, i.e., the adhesive dissolves in an aqueous fluid. Compounds suitable for use as the adhesive of the present invention may be selected from the following non-limiting list: water-soluble polymers, alkaline-reducible resin, carbohydrates, sugars, sugar alcohols, proteins, and some inorganic compounds. Water-soluble polymers with low molecular weights may be preferred in some embodiments because they dissolve more quickly due to smaller molecules diffusing more rapidly in solution. Suitable water-soluble resins include:
The adhesive may include carbohydrates such as starch, cellulose, maltodextrin, acacia gum, locust bean gum, pregelatinized starch, acid-modified starch, hydrolyzed starch, sodium carboxymethylcellulose, sodium alginate, hydroxypropyl cellulose, chitosan, carrageenan, pectin, agar, gellan gum, gum Arabic, xanthan gum, propylene glycol alginate, guar gum, and combinations thereof. Suitable sugars and sugar alcohols include sucrose, dextrose, fructose, lactose, polydextrose, sorbitol, xylitol, cyclodextrans, and combinations thereof. Organic compounds including organic acids may also be used, including citric acid, succinic acid, polyacrylic acidurea, and combinations thereof. Organic compounds may also include proteins such as gelatin, rabbit-skin glue, soy protein, and combinations thereof. Inorganic compounds include plaster, bentonite, precipitated sodium silicate, amorphous precipitated silica, amorphous precipitated calcium silicate, amorphous precipitated magnesium silicate, amorphous precipitated lithium silicate, amorphous precipitated silicates containing a combination of two or more of sodium ions, lithium ions, magnesium ions, and calcium ions, salt, portland cement, magnesium phosphate cement, magnesium oxychloride cement, magnesium oxysulfate cement, zinc phosphate cement, zinc oxide-eugenol cement, aluminum hydroxide, magnesium hydroxide, calcium phosphate, sand, wollastonite, dolomite, and combinations thereof.
Thermoplastic as Adhesive
In some embodiments, a separate ingredient to act as the adhesive is not required. The thermoplastic particulate material may be printed on with a fluid in which the thermoplastic particulate is at least sparingly soluble. Examples of thermoplastic particulate materials that may act as an adhesive include:
Filler
The additional filler of the present invention, other than the thermoplastic particulate filler material, is a compound selected for the characteristics of insolubility or extremely low solubility in the activating fluid, rapid wetting, low hygroscopicity, and high bonding strength. The filler provides mechanical structure to the hardened composition. Sparingly soluble filler material is generally advantageous, but insoluble filler material may be used. The filler particles become adhesively bonded together when the adhesive dries/hardens after the activating fluid has been applied. The filler typically includes a distribution of particle grain sizes, ranging from a practical maximum diameter of about 100 μm downward, to a practical minimum of about 5 μm. Large grain sizes appear to improve the final article quality by forming large pores in the powder through which the fluid may migrate rapidly, permitting production of a more homogeneous material. Smaller grain sizes serve to reinforce article strength. Accordingly, the distribution of grain sizes provides the advantages of both.
Compounds suitable for use as the filler of the present invention may be selected from various general groups, provided that the solubility, hygroscopicity, bonding strength and solution viscosity criteria described above are met. The filler may be inorganic, e.g., aluminum oxide, soda-lime glass, borosilicate glass, silica, aluminosilicate ceramic, limestone, plaster, bentonite, precipitated sodium silicate, amorphous precipitated silica, amorphous precipitated calcium silicate, amorphous precipitated magnesium silicate, amorphous precipitated lithium silicate, amorphous precipitated silicates containing a combination of two or more of sodium ions, lithium ions, magnesium ions, and calcium ions, salt, portland cement, magnesium phosphate cement, magnesium oxychloride cement, magnesium oxysulfate cement, zinc phosphate cement, zinc oxide-eugenol cement, aluminum hydroxide, magnesium hydroxide, calcium phosphate, sand, wollastonite, dolomite, and combinations thereof. Alternatively, the filler may be organic, e.g., a carbohydrate like starch, starch derivatives, cellulose, maltodextrin, and combinations thereof. In general, the selection of the solvent determines which filler may be used. The filler is solid prior to the application of the activating fluid, and is selected so that the filler's solubility in the fluid is substantially less than the adhesive's solubility in the fluid.
Advantageously, the powder constituents, including the filler, have a high absorption capacity and are thereby capable of absorbing and retaining infiltrants.
Fiber
In some embodiments, the particulate mixture may include a reinforcing fiber or a reinforcing fibrous component, added to provide structural reinforcement and structural integrity to the final article. The particulate material may include a plurality of particles of mean diameter of about 10-100 μm. The reinforcing fiber length is generally restricted to a length approximately equal to the thickness of the layer of particulate mixture. The reinforcing fiber length is typically about 60 μm to about 200 μm in length, and is included in an amount not greater than about 50%, by weight, of the total mixture, preferably not greater than 30%, and more preferably not greater than 20%.
The reinforcing fiber of the present invention is preferably either insoluble or substantially slower dissolving than the adhesive in the fluid which activates the adhesive. The reinforcing fiber may be a relatively stiff material chosen to increase the mechanical reinforcement and dimensional control of the final article, without making the powder too difficult to spread. In order to promote wetting of the reinforcing fibers, the chosen fiber advantageously may have a relatively high affinity for the solvent. In one embodiment, a fiber length is approximately equal to the layer thickness, which provides a substantial degree of mechanical reinforcement. Using longer fibers tends to adversely affect the surface finish, and using too much fiber of any length makes spreading the powder increasingly difficult. Fibrous material suitable for reinforcing the present invention includes, but is not limited to, cellulose, polymeric fiber, ceramic fiber, graphite fiber, fiberglass, and combinations thereof. The polymeric fiber may be cellulose and cellulose derivatives or substituted or unsubstituted, straight or branched, alkyl or alkene monomers containing up to eight carbon atoms. Specific useable fibrous materials include, but are not limited to, natural polymers, modified natural polymers, synthetic polymers, ceramic, cellulose fiber, silicon carbide fiber, graphite fiber, aluminosilicate fiber, polypropylene fiber, fiberglass, polyamide flock, cellulose, rayon, polyvinylalcohol, and combinations thereof.
In some embodiments, a stabilizing fiber may be added to the filler to provide dimensional stability to the final article, as well as to increase slightly the article strength. Spreading the particulate mixture with the counter-roller becomes increasingly difficult as friction caused by an excess of stabilizing fiber in the mixture increases, reducing the packing density. Therefore, limiting both the amount and length of the stabilizing fiber increases the packing density of the mixture resulting in finished parts of greater strength. In general, the stabilizing fiber is restricted to a length of less than about half of the reinforcing fiber, in an amount not greater than 50 percent by weight, of the total mixture, preferably not greater than 40 percent by weight, and most preferably not greater than about 30 percent by weight. Optimal values may be determined with routine experimentation using, for example, a counter-roller.
Both the reinforcing fiber and the stabilizing fiber may be cellulose. Some of the useful properties of cellulose making it particularly suitable for use in connection with the invention are low toxicity, biodegradability, low cost, and availability in a wide variety of lengths.
Further considerations in selecting the thermoplastic particulate material, adhesive, filler, and fiber depend on the desired properties of the final article. The final strength of the finished article depends not insubstantially on the quality of the adhesive contacts between the particles of the mixture, and the size of the empty pores that persist in the material after the adhesive has hardened; both of these factors vary with the grain size of the particulate material. In general, the mean size of the grains of particulate material is preferably not larger than the layer thickness. A distribution of grain sizes increases the packing density of the particulate material, which in turn increases both article strength and dimensional control.
Processing Aid
A processing aid for three-dimensional printing is typically a viscous liquid component of the powder material system. It may be a liquid polymer or a polymer having a low melting point. Preferably, it is non-aqueous, thereby not reacting with water-soluble powder components. By loosely bonding the powder, the processing aid keeps the layers from shifting during spreading. The processing aid may also act as a wetting agent, attracting the fluid and allowing the fluid to spread rapidly. Further, the processing aid may reduce dust formation. Examples of materials that may be used as processing aids include polyethylene glycol, polypropylene glycol (PPG), sorbitan monolaurate, sorbitan monooleate, sorbitan trioleate, polysorbate, poly (ethylene oxide) modified silicone, poly (propylene oxide) modified silicone, secondary ethoxylated alcohols, ethoxylated nonylphenols, ethoxylated octylphenols, C8-C10 alcohols, C8-C10 acids, polyethylene oxide modified acetylenic diols, citronellol, ethoxylated silicones, ethylene glycol octanoate, ethylene glycol decanoate, ethoxylated derivatives of 2,4,7,9-tetramethyl-5-decyne-4,7-diol, polyoxyethylene sorbitan mono-oleate, soybean oil, mineral oil, fluroalkyl polyoxyethylene polymers, glycerol triacetate, oleyl alcohol, oleic acid, squalene, squalane, essential oils, esters, terpenes, greases, waxes, propylene glycol, ethylene glycol, C8-C10 esters of mono-, di-, or triglycerides, fatty acids, ethoxylated fatty acids, lecithin, modified lecithins, glycerol tributyrate, sodium stearoyl lactylate, diacetyl tartaric esters of mono- and di-glycerides, corn syrup, and combinations thereof.
Activating Fluid
The fluid of the present invention is selected to comport with the degree of solubility required for the various particulate components of the mixture, as described above. Relatively low solution viscosity ensures that once the adhesive is dissolved in the activating fluid, the fluid migrates quickly to sites in the powder bed to adhesively bond together the thermoplastic filler and reinforcing materials. The fluid may be aqueous or non-aqueous. An aqueous fluid contains preferably 25% or more water, more preferably 40% or more water, and most preferably 50% or more water. A non-aqueous fluid contains less than 25% water by weight, more preferably less than 10% by weight, and most preferably less than 1% water by weight.
First Solvent
The fluid may include a first solvent having a first boiling point in which the adhesive is active, preferably soluble. The first solvent may be adapted to activate the adhesive by dissolving the adhesive particulate material and to assist the dissolution of the fluid. The first solvent may be a non-aqueous material, ethanol, isopropanol, n-propanol, methanol, n-butanol, a glycol, an ester, a glycol-ether, a ketone, an aromatic, an aliphatic, an aprotic polar solvent, a terpene, an acrylate, a methacrylate, a vinylether, an oxetane, an epoxy, a low molecular weight polymer, carbonate, n-methylpyrrolidone, acetone, methyl ethyl ketone, dibasic esters, ethyl acetate, dimethyl sulfoxide, dimethyl succinate, and combinations thereof. Examples of suitable solvents with high boiling points suitable for dissolving certain thermoplastic materials, resulting in the thermoplastic particles adhering together as the solvent dissolves, are:
Second Solvent (Humectant)
A second solvent (humectant) having a second boiling point that may be higher than the first boiling point may be included in the fluid to retard evaporation of the fluid from the printed material, and to prevent drying/clogging of the printhead delivery system. The second solvent may be water-miscible and may include, for example, butyrolactone, glycerol carbonate, propylene carbonate, ethylene carbonate, dimethyl succinate, dimethyl sulfoxide, n-methyl pyrrolidone, glycerol, 1,4-butanediol, polyethylene glycol, diethylene glycol butyl ether, ethylene glycol, diethylene glycol, propylene glycol, polypropylene glycol, polyethylene glycol ethers, polypropylene glycol ethers, tetraethyleneglycol ethers, butylene carbonate, pentanediol, hexanediol, and combinations thereof.
Surfactant
A surfactant may be added to the fluid to reduce its surface tension, thereby assisting it in slipping through the jets of the printhead. The surfactant may be, for example, polyethylene oxide modified acetylenic diols, secondary ethoxylated alcohols, ethoxylated nonylphenols, ethoxylated silicones, ethoxylated fluorinated surfactants, tetramethyldecynediol, ethoxylated tetramethyldecynediol, ethoxylated tetramethyldodecynediol, polyethermodified polysiloxanes, ethoxylated sorbitan monolaurate, octyl phenoxypolyethoxy-polypropoxy-propanol, sulfonated fatty acids, zwitterionic betaines, sodium di-octyl sulfosuccinate, dimethyl dodecylammoniopropane sulfonate, sodium lauryl sulfate, sodium lauryl benzene sulfonate, sodium p-toluene sulfonate, sodium benzoate, sodium benzene sulfonate, potassium sorbate, sodium 2-ethylhexyl sulfonate, and combinations thereof.
Rheology Modifier
A rheology modifier may be added to the fluid to increase viscosity, thereby increasing the efficiency of the printhead and aiding printing. Examples of possible rheology modifiers include polyvinylpyrrolidone, polyacrylamide, polyethylene oxide, hydrophobe modified ethoxy urethanes, polyvinyl alcohol, polyacrylic acid, polymethacrylic acid, alkali and ammonium salts of polyacrylic acid, alkali and ammonium salts of polymethacrylic acid, polyvinylpyrrolidone-co-vinyl acetate, butylated polyvinylpyrrolidone, polyvinylalcohol-co-vinyl acetate, and polyacrylic acid-co-maleic anhydride, sulfonated polystyrene, and combinations and copolymers thereof.
Amines
Amines may be added to the fluid to assist in the dissolution of water-miscible adhesives, such as water-soluble resins. Examples of suitable amines include monoisopropanol amine, triethylamine, 2-amino-2-methyl-1-propanol, 1-amino-2-propanol, 2-dimethylamino-2-methyl-1-propanol, N,N-diethylethanolamine, N-methyldiethanolamine, N,N-dimethylethanolamine, triethanolamine, 2-aminoethanol, 1-[bis [3-(dimethylamino)propyl]amino]-2-propanol, 3-amino-1-propanol, 2-(2-aminoethylamino) ethanol, tris(hydroxymethyl)aminomethane, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1,3-propanediol, diethanolamine, 1,3-bis (dimethylamino)-2-propanol, ammonium hydroxide, monoethanolamine, aminomethylpropanol, aminoethylethanolamine, triisopropanolamine, polyoxypropylenetriamine, polyethylenimine, and combinations thereof.
Fluid for Activating Sparingly Soluble Thermoplastic Particulate Material
Some activating fluids are suitable for activating the adhesive properties of at least a sparingly soluble thermoplastic particulate material. Such an activating fluid softens the surface of the solid particulates, thereby enabling them to be self-adhesive. These fluids are typically non-aqueous, non-halogenated fluids like alcohols, glycols, esters, glycol-ethers, ketones, aromatics, aliphatics, aprotic-polar solvents, terpenes, acrylates, methacrylates, vinylethers, oxetanes, epoxies, low molecular weight polymers, carbonates, and combinations thereof. Some activating fluids that are solvents for the thermoplastic particulate material may be, after dissolving the thermoplastic material, solidified by exposure to ultraviolet light, visible light, heat, or an electron beam, and combinations thereof.
The alcohol may include at least one of the following materials: methanol, ethanol, n-propanol, i-propanol, n-butanol and combinations thereof. The glycol may include at least one of the following materials: ethylene glycol, diethylene glycol, propylene glycol, polyethyleneglycol, butanediol, pentanediol, hexanediol and combinations thereof.
The ester may include at least one of the following materials: ethyl acetate, propyleneglycol methylether acetate, amyl acetate, dimethylsuccinate, dimethyl glutarate, dimethyl adipate, diethylene glycol monobutyl ether acetate, n-propyl acetate, i-propyl acetate, i-butyl acetate, n-butyl acetate, t-butyl acetate, 2-ethylhexyl acetate, ethylene glycol diacetate, diethyl succinate, methyl lactate, ethyl lactate, dimethyl tartrate, diethyl tartrate and combinations thereof. The glycol-ether may include at least one of the following materials: dipropylene glycol methyl ether, diethylene glycol butyl ether, diethylene glycol monoethyl ether, propylene glycol methyl ether, ethylene glycol propyl ether and combinations thereof.
The ketone may include at least one of the following materials: acetone, methylethylketone, methylisobutylketone, methyl isopropyl ketone, methyl n-propyl ketone, methyl isoamyl ketone, methyl n-amyl ketone, diisobutyl ketone and combinations thereof. The aromatic may include at least one of the following materials: toluene, xylene, phenol, benzene, styrene, high flash aromatic naptha and combinations thereof.
The aliphatic may include at least one of the following materials: hexane, heptane, cyclohexane and combinations thereof. The aprotic polar solvent may include at least one of the following materials: n-methylpyrrolidone, dimethylsulfoxide, 2-pyrrolidone, butyrolactone and combinations thereof. The terpene may include limonene.
The acrylate may include at least one of the following materials: alkoxylated difunctional acrylate, 2-phenoxyethyl acrylate, tetrahydrofurfuryl acrylate, 2(2 ethoxyethoxy)ethyl acrylate, hexanediol diacrylate, propoxylated neopentyl glycol diacrylate, lauryl acrylate, isodecyl acrylate, tridecyl acrylate, isobornyl acrylate, tripropylene glycol diacrylate, stearyl acrylate, allyl acrylate, isooctylacrylate, caprolactone acrylate, alkoxylated tetrahydrofurfuryl acrylate, butanediol diacrylate, 1,3-butyleneglycol diacrylate, diethylene glycol diacrylate, polyethylene glycol diacrylate, alkoxylated hexanediol diacrylate, alkoxylated cyclohexane dimethanol diacrylate, cyclohexane dimethanol diacrylate, dipropylene glycol diacrylate, ethoxylated bisphenol A diacrylate, neopentyl glycol diacrylate, alkoxylated aliphatic diacrylate, trimethylpropane triacrylate, tris (2-hydroxy ethyl) isocyanurate triacrylate, ethoxylated trimethyl propane triacrylate, propoxylated trimethyl propane triacrylate, propoxylated glyceryl triacrylate, pentaerythritol tetraacrylate, pentaerythritol triacrylate, di-trimethylpropane tetraacrylate, dipentaerythritol pentaacrylate, ethoxylated pentaerythritol tetraacrylate, alkoxylated nonyl phenol acrylate, and combinations thereof.
The methacrylate may include at least one of the following materials: 2-phenoxyethyl methacrylate, tetrahydrofurfuryl methacrylate, hexanediol dimethacrylate, lauryl methacrylate, isodecyl methacrylate, tridecyl methacrylate, isobornyl methacrylate, propylene glycol monomethacrylate, stearyl methacrylate, allyl methacrylate, isooctylmethacrylate, butanediol dimethacrylate, 1,3-butyleneglycol dimethacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol dimethacrylate, cyclohexane dimethanol dimethacrylate, dipropylene glycol dimethacrylate, ethoxylated bisphenol A dimethacrylate, neopentyl glycol dimethacrylate, trimethylpropane trimethacrylate, methoxy polyethylene glycol methacrylate, alkoxylated nonyl phenol methacrylate, ethoxylated hydroxyethyl methacrylate, allyl methacrylate, propoxylated allyl methacrylate, and combinations thereof.
The vinyl ether may include at least one of the following materials: hydroxylbutyl vinyl ether, triethyleneglycol divinylether, cyclohexanedimethanol divinylether, propenylether of propylene carbonate, dodecylvinylether, cyclohexanemethanol monovinylether, cyclohexyl vinyl ether, diethyleneglycol divinylether, 2-ethylhexylvinylether, dipropyleneglycol divinylether, tripropyleneglycol divinyl ether, hexanediol divinyl ether, octadecylvinylether, butanediol divinyl ether, bis[4-(vinyloxy)butyl]isophthalate, bis[4-(vinyloxy)butyl]adipate, and combinations thereof.
The oxetane may include at least one of the following materials: 3-ethyl-3-hydroxymethyl-oxetane, 1,4-bis[(3-ethyl-3-oxetanyl methoxy)methyl]benzene, and combinations thereof. The epoxy may include at least one of the following materials: 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, bis-(3,4-epoxycyclohexyl) adipate, limonene monoxide, 1,2-epoxyhexadecane, and combinations thereof. The low molecular weight polymer may include polyethyleneimine. The carbonate may include ethylene carbonate, propylene carbonate, butylene carbonate, glycerol carbonate, and combinations thereof.
Some of these activating fluids are reactive monomers that act as solvents for the thermoplastic particulate material. In a first step, the activating fluids may dissolve the thermoplastic material and penetrate into the thermoplastic material. This behavior is facilitated by selecting activating fluids containing monomers with Hansen solubility parameters that match the Hansen solubility parameters of thermoplastic particulate materials. Hansen solubility parameters are quantitative values that describe the solvency behavior of fluids and the solubility characteristics of thermoplastic materials. The monomers of the activiating fluid may be further solidified in a second step by a free radical initiated mechanism, a cationic initiation mechanism, or combinations thereof. Fluids like acrylates, methacrylates, vinylethers, oxetanes, epoxies and combinations thereof are typical reactive monomers that can also act as solvents. Examples of monomers that act as solvents suitable for dissolving certain thermoplastic materials and penetrating into the thermoplastic particle resulting in the thermoplastic particles adhering together as the solvent dissolves are:
After the monomer dissolves and penetrates the thermoplastic particulate material, it may then be solidified by a free radical initiation (in the case of monomers belonging to the acrylate, methacrylate, or vinyl families), or by a cationic initiation (in the case of monomers belonging to the epoxide and oxetane families). The vinyl ether family of monomers may solidified by either free radical or cationic initiation. The solidification of the monomers penetrated into the thermoplastic particulate material creates an interpenetrating polymer network (IPN). An IPN is defined as two or more constituent polymer networks that are polymerized and/or crosslinked in the immediate presence of one another. Preferably, such a polymeric system includes two or more network polymers that interpenetrate each other to some extent and that are not chemically bound but are con-catenated such that they cannot be separated unless chemical bonds are broken. The formation of an IPN between the thermoplastic particulate material and polymerized monomer enables better adhesion and provides increased toughness of the final article.
A summary of one group of preferred materials for a particulate mixture containing both a thermoplastic material and an adhesive and for the activating fluid is given in Table 1. Summaries of two examples of preferred materials for a thermoplastic material that is adapted to bond together when contacted with an activating fluid and for the activating fluid are given in Table 2.
Flowrate Enhancer
The fluid may include a processing aid such as a flowrate enhancer. The flowrate enhancer may have some humectant properties, but serves mainly to alter the hydrodynamic properties or wetting characteristics of the fluid to maximize the volume of fluid delivered by the printhead. Flowrate enhancement is thought to be a viscoelastic phenomena increasing the flow rate of the fluid, allowing thicker layers to be printed, thus allowing the final article to be built more quickly. Preferred compounds that increase the flowrate of the fluid, either by reducing friction between the fluid and the walls of the jet, or by reducing the viscosity of the fluid, include ethylene glycol diacetate, potassium sorbate, and potassium aluminum sulfate. Other suitable compounds for use as the flowrate enhancer can be selected from the following non-limiting list: isopropyl alcohol, ethylene glycol monobutyl ether, diethylene glycol monobutyl ether, dodecyl dimethylammoniopropane sulfonate, glycerol triacetate, ethyl acetoacetate, and water-soluble polymers including polyvinyl pyrrolidone with a molecular weight of about 30,000 units, polyethylene glycol, polyacrylic acid, and sodium polyacrylate. For the ionic polymers, such as sodium polyacrylate, the increase in flow rate varies with pH.
Dyes and Pigments
The fluid of the present invention preferably includes a dye or pigment to provide a visual aid to the operator while building the article. The dye or pigment provides contrast between activated and unactivated powder which allows the operator to monitor the printed layers while building the article. The dye or pigment can be selected from the group including, but not limited to, naphthol blue black, direct red, and dispersions of anionically surface-modified organic pigments like copper phthalocyanine and carbon black. Numerous other dyes and pigments compatible with the fluid will be known to those skilled in the art.
The materials and method of the present invention present numerous advantages over prior three-dimensional printing methods. The materials used in the present invention are inexpensive, and allow the production of strong, thin-walled articles having exceptional surface finishes. Further, the activating fluid may contain a component having a high boiling point that prevents the jets of the printhead from drying out prematurely.
The equipment used in the method of the present invention is reliable, inexpensive, and easy to maintain, making it ideal for use in an office environment. The materials used in the present invention are highly compatible with ink-jet technology. Thus, less equipment maintenance is required, and the reliability of the equipment is increased. Therefore, the method of the present invention involves shorter build times and less labor than prior art methods.
Those skilled in the art will readily appreciate that all parameters listed herein are meant to be exemplary and actual parameters depend upon the specific application for which the methods and materials of the present invention are used. It is, therefore, to be understood that the foregoing embodiments are presented by way of example only and that, within the scope of the appended claims and equivalents thereto, the invention may be practiced otherwise than as specifically described.
This application claims the benefit of U.S. Provisional Application 60/472,221 filed May 21, 2003, the entire disclosure of which is hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2522548 | Streicher | Sep 1950 | A |
| 2662024 | Riddell et al. | Dec 1953 | A |
| 3297601 | Maynard et al. | Jan 1967 | A |
| 3303147 | Elden | Feb 1967 | A |
| 3309328 | Carroll et al. | Mar 1967 | A |
| 3476190 | Jenny et al. | Nov 1969 | A |
| 3525632 | Enoch | Aug 1970 | A |
| 3821006 | Schwartz | Jun 1974 | A |
| 3835074 | Desmarais | Sep 1974 | A |
| 3852083 | Yang | Dec 1974 | A |
| 3870538 | Burkard et al. | Mar 1975 | A |
| 3890305 | Weber et al. | Jun 1975 | A |
| 3926870 | Keegan et al. | Dec 1975 | A |
| 3930872 | Toeniskoetter et al. | Jan 1976 | A |
| 3932923 | DiMatteo | Jan 1976 | A |
| 4041476 | Swainson | Aug 1977 | A |
| 4042408 | Murray et al. | Aug 1977 | A |
| 4061825 | Counsell et al. | Dec 1977 | A |
| 4078229 | Swanson et al. | Mar 1978 | A |
| 4247508 | Housholder | Jan 1981 | A |
| 4288861 | Swainson et al. | Sep 1981 | A |
| 4310996 | Mulvey et al. | Jan 1982 | A |
| 4327156 | Dillon et al. | Apr 1982 | A |
| 4369025 | von der Weid | Jan 1983 | A |
| 4443392 | Becker et al. | Apr 1984 | A |
| 4444594 | Paddison et al. | Apr 1984 | A |
| 4476190 | Clarke et al. | Oct 1984 | A |
| 4575330 | Hull | Mar 1986 | A |
| 4613627 | Sherman et al. | Sep 1986 | A |
| 4618390 | Powell | Oct 1986 | A |
| 4649077 | Lauchenauer | Mar 1987 | A |
| 4665492 | Masters | May 1987 | A |
| 4752352 | Feygin | Jun 1988 | A |
| 4752498 | Fudim | Jun 1988 | A |
| 4755227 | Sherif et al. | Jul 1988 | A |
| 4758278 | Tomic | Jul 1988 | A |
| 4801477 | Fudim | Jan 1989 | A |
| 4844144 | Murphy et al. | Jul 1989 | A |
| 4863538 | Deckard | Sep 1989 | A |
| 4929402 | Hull | May 1990 | A |
| 4938816 | Beaman et al. | Jul 1990 | A |
| 4940412 | Blumenthal et al. | Jul 1990 | A |
| 4942001 | Murphy et al. | Jul 1990 | A |
| 4942003 | Bold et al. | Jul 1990 | A |
| 4942060 | Grossa et al. | Jul 1990 | A |
| 4943928 | Campbell et al. | Jul 1990 | A |
| 4944817 | Bourell et al. | Jul 1990 | A |
| 4945032 | Murphy et al. | Jul 1990 | A |
| 4961154 | Pomerantz et al. | Oct 1990 | A |
| 4996010 | Modrek | Feb 1991 | A |
| 4996282 | Noren et al. | Feb 1991 | A |
| 4999143 | Hull et al. | Mar 1991 | A |
| 5009585 | Hirano et al. | Apr 1991 | A |
| 5011635 | Murphy et al. | Apr 1991 | A |
| 5015312 | Kinzie | May 1991 | A |
| 5015424 | Smalley | May 1991 | A |
| 5017317 | Marcus | May 1991 | A |
| 5017753 | Deckard | May 1991 | A |
| 5031120 | Pomerantz et al. | Jul 1991 | A |
| 5038014 | Pratt et al. | Aug 1991 | A |
| 5040005 | Davidson et al. | Aug 1991 | A |
| 5051334 | Fan | Sep 1991 | A |
| 5053090 | Beaman et al. | Oct 1991 | A |
| 5058988 | Spence | Oct 1991 | A |
| 5059021 | Spence et al. | Oct 1991 | A |
| 5059266 | Yamane et al. | Oct 1991 | A |
| 5059359 | Hull et al. | Oct 1991 | A |
| 5071337 | Heller et al. | Dec 1991 | A |
| 5071503 | Berman et al. | Dec 1991 | A |
| 5076869 | Bourell et al. | Dec 1991 | A |
| 5076974 | Modrek et al. | Dec 1991 | A |
| 5088047 | Bynum | Feb 1992 | A |
| 5089184 | Hirano et al. | Feb 1992 | A |
| 5089185 | Hirano et al. | Feb 1992 | A |
| 5094935 | Vassiliou et al. | Mar 1992 | A |
| 5096491 | Nagai et al. | Mar 1992 | A |
| 5096530 | Cohen | Mar 1992 | A |
| 5104592 | Hull et al. | Apr 1992 | A |
| 5106288 | Hughes et al. | Apr 1992 | A |
| 5121329 | Crump | Jun 1992 | A |
| 5122441 | Lawton et al. | Jun 1992 | A |
| 5123734 | Spence et al. | Jun 1992 | A |
| 5127037 | Bynum | Jun 1992 | A |
| 5128235 | Vassiliou et al. | Jul 1992 | A |
| 5130064 | Smalley et al. | Jul 1992 | A |
| 5132143 | Deckard | Jul 1992 | A |
| 5133987 | Spence et al. | Jul 1992 | A |
| 5134569 | Masters | Jul 1992 | A |
| 5135379 | Fudim | Aug 1992 | A |
| 5135695 | Marcus | Aug 1992 | A |
| 5137662 | Hull et al. | Aug 1992 | A |
| 5139338 | Pomerantz et al. | Aug 1992 | A |
| 5139711 | Nakamura et al. | Aug 1992 | A |
| 5141680 | Almquist et al. | Aug 1992 | A |
| 5143663 | Leyden et al. | Sep 1992 | A |
| 5143817 | Lawton et al. | Sep 1992 | A |
| 5147587 | Marcus et al. | Sep 1992 | A |
| 5149548 | Yamane et al. | Sep 1992 | A |
| 5151813 | Yamamoto et al. | Sep 1992 | A |
| 5154762 | Mitra et al. | Oct 1992 | A |
| 5155321 | Grube et al. | Oct 1992 | A |
| 5155324 | Deckard et al. | Oct 1992 | A |
| 5157423 | Zur | Oct 1992 | A |
| 5158858 | Lawton et al. | Oct 1992 | A |
| 5164882 | Kanai et al. | Nov 1992 | A |
| 5167882 | Jacobine et al. | Dec 1992 | A |
| 5169579 | Marcus et al. | Dec 1992 | A |
| 5171490 | Fudim | Dec 1992 | A |
| 5173220 | Reiff et al. | Dec 1992 | A |
| 5174931 | Almquist et al. | Dec 1992 | A |
| 5174943 | Hull | Dec 1992 | A |
| 5175077 | Grossa et al. | Dec 1992 | A |
| 5176188 | Quinn et al. | Jan 1993 | A |
| 5182055 | Allison et al. | Jan 1993 | A |
| 5182056 | Spence et al. | Jan 1993 | A |
| 5182134 | Sato | Jan 1993 | A |
| 5182715 | Vorgitch et al. | Jan 1993 | A |
| 5183598 | Helle et al. | Feb 1993 | A |
| 5184307 | Hull et al. | Feb 1993 | A |
| 5192469 | Smalley et al. | Mar 1993 | A |
| 5192559 | Hull et al. | Mar 1993 | A |
| 5198159 | Nakamura et al. | Mar 1993 | A |
| 5203944 | Prinz et al. | Apr 1993 | A |
| 5204055 | Sachs et al. | Apr 1993 | A |
| 5204124 | Secretan et al. | Apr 1993 | A |
| 5204823 | Schlotterbeck | Apr 1993 | A |
| 5207371 | Prinz et al. | May 1993 | A |
| 5209878 | Smalley et al. | May 1993 | A |
| 5216616 | Masters | Jun 1993 | A |
| 5217653 | Mashinsky et al. | Jun 1993 | A |
| 5234636 | Hull et al. | Aug 1993 | A |
| 5236637 | Hull | Aug 1993 | A |
| 5236812 | Vassiliou et al. | Aug 1993 | A |
| 5238614 | Uchinono et al. | Aug 1993 | A |
| 5238639 | Vinson et al. | Aug 1993 | A |
| 5247180 | Mitcham et al. | Sep 1993 | A |
| 5248249 | Yamamoto et al. | Sep 1993 | A |
| 5248456 | Evans, Jr. et al. | Sep 1993 | A |
| 5252264 | Forderhase et al. | Oct 1993 | A |
| 5256340 | Allison et al. | Oct 1993 | A |
| 5258146 | Almquist et al. | Nov 1993 | A |
| 5260009 | Penn | Nov 1993 | A |
| 5263130 | Pomerantz et al. | Nov 1993 | A |
| 5264061 | Juskey et al. | Nov 1993 | A |
| 5267013 | Spence | Nov 1993 | A |
| 5273691 | Hull et al. | Dec 1993 | A |
| 5275916 | Kato et al. | Jan 1994 | A |
| 5278442 | Prinz et al. | Jan 1994 | A |
| 5279665 | Yunovich et al. | Jan 1994 | A |
| 5281789 | Merz et al. | Jan 1994 | A |
| 5286573 | Prinz et al. | Feb 1994 | A |
| 5287435 | Cohen et al. | Feb 1994 | A |
| 5289214 | Zur et al. | Feb 1994 | A |
| 5296062 | Bourell et al. | Mar 1994 | A |
| 5296335 | Thomas et al. | Mar 1994 | A |
| 5301415 | Prinz et al. | Apr 1994 | A |
| 5303141 | Batchelder et al. | Apr 1994 | A |
| 5306446 | Howe | Apr 1994 | A |
| 5306447 | Marcus et al. | Apr 1994 | A |
| 5316580 | Deckard | May 1994 | A |
| 5328539 | Sato | Jul 1994 | A |
| 5338611 | Lause et al. | Aug 1994 | A |
| 5340433 | Crump | Aug 1994 | A |
| 5340656 | Sachs et al. | Aug 1994 | A |
| 5342566 | Schafer et al. | Aug 1994 | A |
| 5342919 | Dickens et al. | Aug 1994 | A |
| 5344298 | Hull | Sep 1994 | A |
| 5345391 | Hull et al. | Sep 1994 | A |
| 5345414 | Nakamura et al. | Sep 1994 | A |
| 5348693 | Taylor et al. | Sep 1994 | A |
| 5352310 | Natter | Oct 1994 | A |
| 5352405 | Beaman et al. | Oct 1994 | A |
| 5355318 | Dionnet et al. | Oct 1994 | A |
| 5358673 | Heller et al. | Oct 1994 | A |
| 5364889 | Quinn et al. | Nov 1994 | A |
| 5365996 | Crook | Nov 1994 | A |
| 5370692 | Fink et al. | Dec 1994 | A |
| 5376320 | Tiefenbacher et al. | Dec 1994 | A |
| 5382289 | Bambauer et al. | Jan 1995 | A |
| 5382308 | Bourell et al. | Jan 1995 | A |
| 5385772 | Slovinsky et al. | Jan 1995 | A |
| 5386500 | Pomerantz et al. | Jan 1995 | A |
| 5387380 | Cima et al. | Feb 1995 | A |
| 5391072 | Lawton et al. | Feb 1995 | A |
| 5391460 | Dougherty et al. | Feb 1995 | A |
| 5393613 | MacKay | Feb 1995 | A |
| 5402351 | Batchelder et al. | Mar 1995 | A |
| 5415820 | Furuta et al. | May 1995 | A |
| 5418112 | Mirle et al. | May 1995 | A |
| 5426722 | Batchelder | Jun 1995 | A |
| 5429788 | Ribble et al. | Jul 1995 | A |
| 5429908 | Hokuf et al. | Jul 1995 | A |
| 5430666 | DeAngelis et al. | Jul 1995 | A |
| 5432045 | Narukawa et al. | Jul 1995 | A |
| 5433280 | Smith | Jul 1995 | A |
| 5435902 | Andre, Sr. | Jul 1995 | A |
| 5437964 | Lapin et al. | Aug 1995 | A |
| 5439622 | Pennisi et al. | Aug 1995 | A |
| 5447822 | Hull et al. | Sep 1995 | A |
| 5450205 | Sawin et al. | Sep 1995 | A |
| 5458825 | Grolman et al. | Oct 1995 | A |
| 5460758 | Langer et al. | Oct 1995 | A |
| 5461088 | Wolf et al. | Oct 1995 | A |
| 5468886 | Steinmann et al. | Nov 1995 | A |
| 5470689 | Wolf et al. | Nov 1995 | A |
| 5474719 | Fan et al. | Dec 1995 | A |
| 5482659 | Sauerhoefer | Jan 1996 | A |
| 5490882 | Sachs et al. | Feb 1996 | A |
| 5490962 | Cima et al. | Feb 1996 | A |
| 5491643 | Batchelder | Feb 1996 | A |
| 5494618 | Sitzmann et al. | Feb 1996 | A |
| 5495029 | Steinmann et al. | Feb 1996 | A |
| 5495328 | Spence et al. | Feb 1996 | A |
| 5498782 | Rex | Mar 1996 | A |
| 5500069 | Ogue et al. | Mar 1996 | A |
| 5501824 | Almquist et al. | Mar 1996 | A |
| 5503785 | Crump et al. | Apr 1996 | A |
| 5503793 | Uchinono et al. | Apr 1996 | A |
| 5506046 | Andersen et al. | Apr 1996 | A |
| 5506087 | Lapin et al. | Apr 1996 | A |
| 5506607 | Sanders, Jr. et al. | Apr 1996 | A |
| 5507336 | Tobin | Apr 1996 | A |
| 5510226 | Lapin et al. | Apr 1996 | A |
| 5512162 | Sachs et al. | Apr 1996 | A |
| 5514232 | Burns | May 1996 | A |
| 5514378 | Mikos et al. | May 1996 | A |
| 5518680 | Cima et al. | May 1996 | A |
| 5519816 | Pomerantz et al. | May 1996 | A |
| 5525051 | Takano et al. | Jun 1996 | A |
| 5527877 | Dickens et al. | Jun 1996 | A |
| 5534059 | Immordino, Jr. | Jul 1996 | A |
| 5534104 | Langer et al. | Jul 1996 | A |
| 5536467 | Reichle et al. | Jul 1996 | A |
| 5545367 | Bae et al. | Aug 1996 | A |
| 5554336 | Hull | Sep 1996 | A |
| 5555176 | Menhennett et al. | Sep 1996 | A |
| 5555481 | Rock et al. | Sep 1996 | A |
| 5556590 | Hull | Sep 1996 | A |
| 5569349 | Almquist et al. | Oct 1996 | A |
| 5569431 | Hull | Oct 1996 | A |
| 5571471 | Hull | Nov 1996 | A |
| 5572431 | Brown et al. | Nov 1996 | A |
| 5573721 | Gillette | Nov 1996 | A |
| 5573722 | Hull | Nov 1996 | A |
| 5573889 | Hofmann et al. | Nov 1996 | A |
| 5582876 | Langer et al. | Dec 1996 | A |
| 5587913 | Abrams et al. | Dec 1996 | A |
| 5591563 | Suzuki et al. | Jan 1997 | A |
| 5593531 | Penn | Jan 1997 | A |
| 5594652 | Penn et al. | Jan 1997 | A |
| 5595597 | Fogel et al. | Jan 1997 | A |
| 5595703 | Swaelens et al. | Jan 1997 | A |
| 5596504 | Tata et al. | Jan 1997 | A |
| 5597520 | Smalley et al. | Jan 1997 | A |
| 5597589 | Deckard | Jan 1997 | A |
| 5598340 | Medard et al. | Jan 1997 | A |
| 5599651 | Steinmann et al. | Feb 1997 | A |
| 5603797 | Thomas et al. | Feb 1997 | A |
| 5605941 | Steinmann et al. | Feb 1997 | A |
| 5608814 | Gilmore et al. | Mar 1997 | A |
| 5609812 | Childers et al. | Mar 1997 | A |
| 5609813 | Allison et al. | Mar 1997 | A |
| 5610824 | Vinson et al. | Mar 1997 | A |
| 5611883 | Tompkins et al. | Mar 1997 | A |
| 5614075 | Andre, Sr. | Mar 1997 | A |
| 5616293 | Ashtiani-Zarandi et al. | Apr 1997 | A |
| 5616294 | Deckard | Apr 1997 | A |
| 5622577 | O'Connor | Apr 1997 | A |
| 5622811 | Ogue et al. | Apr 1997 | A |
| 5626919 | Chapman et al. | May 1997 | A |
| 5630981 | Hull | May 1997 | A |
| 5632848 | Richards et al. | May 1997 | A |
| 5633021 | Brown et al. | May 1997 | A |
| 5637169 | Hull et al. | Jun 1997 | A |
| 5637175 | Feygin et al. | Jun 1997 | A |
| 5639070 | Deckard | Jun 1997 | A |
| 5639402 | Barlow et al. | Jun 1997 | A |
| 5639413 | Crivello | Jun 1997 | A |
| 5640667 | Freitag et al. | Jun 1997 | A |
| 5641448 | Yeung et al. | Jun 1997 | A |
| 5645973 | Hofmann et al. | Jul 1997 | A |
| 5648450 | Dickens et al. | Jul 1997 | A |
| 5649277 | Greul et al. | Jul 1997 | A |
| 5650260 | Onishi et al. | Jul 1997 | A |
| 5651934 | Almquist et al. | Jul 1997 | A |
| 5653925 | Batchelder | Aug 1997 | A |
| 5656230 | Khoshevis | Aug 1997 | A |
| 5658412 | Retallick et al. | Aug 1997 | A |
| 5658712 | Steinmann et al. | Aug 1997 | A |
| 5659478 | Pennisi et al. | Aug 1997 | A |
| 5660621 | Bredt | Aug 1997 | A |
| 5660900 | Andersen et al. | Aug 1997 | A |
| 5663883 | Thomas et al. | Sep 1997 | A |
| 5665401 | Serbin et al. | Sep 1997 | A |
| 5667820 | Heller et al. | Sep 1997 | A |
| 5672312 | Almquist et al. | Sep 1997 | A |
| 5674921 | Regula et al. | Oct 1997 | A |
| 5676904 | Almquist et al. | Oct 1997 | A |
| 5677107 | Neckers | Oct 1997 | A |
| 5684713 | Asada et al. | Nov 1997 | A |
| 5688464 | Jacobs et al. | Nov 1997 | A |
| 5693144 | Jacobs et al. | Dec 1997 | A |
| 5695707 | Almquist et al. | Dec 1997 | A |
| 5697043 | Baskaran et al. | Dec 1997 | A |
| 5698485 | Bruck et al. | Dec 1997 | A |
| 5700406 | Menhennett et al. | Dec 1997 | A |
| 5703138 | Cantor et al. | Dec 1997 | A |
| 5705116 | Sitzmann et al. | Jan 1998 | A |
| 5705117 | O'Connor et al. | Jan 1998 | A |
| 5705316 | Steinmann et al. | Jan 1998 | A |
| 5707578 | Johnson et al. | Jan 1998 | A |
| 5707780 | Lawton et al. | Jan 1998 | A |
| 5711911 | Hull | Jan 1998 | A |
| 5713410 | LaSalle et al. | Feb 1998 | A |
| 5717599 | Menhennett et al. | Feb 1998 | A |
| 5718279 | Satoh et al. | Feb 1998 | A |
| 5718757 | Guillou et al. | Feb 1998 | A |
| 5727138 | Harada et al. | Mar 1998 | A |
| 5728345 | Hlavaty et al. | Mar 1998 | A |
| 5730817 | Feygin et al. | Mar 1998 | A |
| 5730925 | Mattes et al. | Mar 1998 | A |
| 5731388 | Suzuki et al. | Mar 1998 | A |
| 5733497 | McAlea et al. | Mar 1998 | A |
| 5738817 | Danforth et al. | Apr 1998 | A |
| 5738921 | Andersen et al. | Apr 1998 | A |
| 5740051 | Sanders, Jr. et al. | Apr 1998 | A |
| 5746844 | Sterett et al. | May 1998 | A |
| 5746967 | Hoy et al. | May 1998 | A |
| 5749041 | Lakshminarayan et al. | May 1998 | A |
| 5753171 | Serbin et al. | May 1998 | A |
| 5753274 | Wilkening et al. | May 1998 | A |
| 5772947 | Hull et al. | Jun 1998 | A |
| 5783358 | Schulthess et al. | Jul 1998 | A |
| 5805971 | Akedo | Sep 1998 | A |
| 5851465 | Bredt | Dec 1998 | A |
| 5870307 | Hull et al. | Feb 1999 | A |
| 5902441 | Bredt et al. | May 1999 | A |
| 5902537 | Almquist et al. | May 1999 | A |
| 5940674 | Sachs et al. | Aug 1999 | A |
| 5943235 | Earl et al. | Aug 1999 | A |
| 5965776 | Leppard et al. | Oct 1999 | A |
| 5976339 | André | Nov 1999 | A |
| 6007318 | Russell et al. | Dec 1999 | A |
| 6077887 | Thuresson et al. | Jun 2000 | A |
| 6112109 | D'Urso | Aug 2000 | A |
| 6136088 | Farrington | Oct 2000 | A |
| 6136948 | Dickens, Jr. et al. | Oct 2000 | A |
| 6147138 | Höochsmann et al. | Nov 2000 | A |
| 6193922 | Ederer | Feb 2001 | B1 |
| 6299677 | Johnson et al. | Oct 2001 | B1 |
| 6348679 | Ryan et al. | Feb 2002 | B1 |
| 6363606 | Johnson, Jr. et al. | Apr 2002 | B1 |
| 6375874 | Russell et al. | Apr 2002 | B1 |
| 6397922 | Sachs et al. | Jun 2002 | B1 |
| 6403002 | van der Geest | Jun 2002 | B1 |
| 6416850 | Bredt et al. | Jul 2002 | B1 |
| 6423255 | Hoechsmann et al. | Jul 2002 | B1 |
| 6433038 | Tanabe et al. | Aug 2002 | B1 |
| 6531086 | Larsson et al. | Mar 2003 | B1 |
| 6540784 | Barlow et al. | Apr 2003 | B2 |
| 6600142 | Ryan et al. | Jul 2003 | B2 |
| 6610429 | Bredt et al. | Aug 2003 | B2 |
| 6713125 | Sherwood et al. | Mar 2004 | B1 |
| 6742456 | Kasperchik et al. | Jun 2004 | B1 |
| 6780368 | Liu et al. | Aug 2004 | B2 |
| 6799959 | Tochimoto et al. | Oct 2004 | B1 |
| 6930144 | Oriakhi | Aug 2005 | B2 |
| 6989115 | Russell et al. | Jan 2006 | B2 |
| 7037382 | Davidson et al. | May 2006 | B2 |
| 7087109 | Bredt et al. | Aug 2006 | B2 |
| 7120512 | Kramer et al. | Oct 2006 | B2 |
| 7285234 | Pfeifer et al. | Oct 2007 | B2 |
| 7300613 | Sano et al. | Nov 2007 | B2 |
| 20010050031 | Bredt et al. | Dec 2001 | A1 |
| 20020016387 | Shen | Feb 2002 | A1 |
| 20020106412 | Rowe et al. | Aug 2002 | A1 |
| 20030090034 | Mulhaupt et al. | May 2003 | A1 |
| 20030143268 | Pryce Lewis et al. | Jul 2003 | A1 |
| 20030173695 | Monkhouse et al. | Sep 2003 | A1 |
| 20040038009 | Leyden et al. | Feb 2004 | A1 |
| 20040056378 | Bredt et al. | Mar 2004 | A1 |
| 20040232583 | Monsheimer et al. | Nov 2004 | A1 |
| 20050001356 | Tochimoto et al. | Jan 2005 | A1 |
| 20050017394 | Hochsmann et al. | Jan 2005 | A1 |
| 20050059757 | Bredt et al. | Mar 2005 | A1 |
| 20050093194 | Oriakhi et al. | May 2005 | A1 |
| 20050110177 | Schulman et al. | May 2005 | A1 |
| 20050179167 | Hachikian | Aug 2005 | A1 |
| 20050197431 | Bredt et al. | Sep 2005 | A1 |
| 20050212163 | Bausinger et al. | Sep 2005 | A1 |
| 20050230870 | Oriakhi | Oct 2005 | A1 |
| 20060071367 | Hunter et al. | Apr 2006 | A1 |
| 20060141145 | Davidson et al. | Jun 2006 | A1 |
| 20060208388 | Bredt et al. | Sep 2006 | A1 |
| 20060230984 | Bredt et al. | Oct 2006 | A1 |
| 20070007698 | Sano | Jan 2007 | A1 |
| 20070029698 | Rynerson et al. | Feb 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| 1810492 | Aug 2006 | CN |
| 1857930 | Oct 2006 | CN |
| 40 12 044 | Oct 1991 | DE |
| 197 27 677 | Jan 1999 | DE |
| 198 53 834 | May 2000 | DE |
| 101 58 233 | Mar 2003 | DE |
| 0 431 924 | Jun 1991 | EP |
| 0 540 203 | May 1993 | EP |
| 1 226 019 | Jul 2002 | EP |
| 1 475 221 | Nov 2004 | EP |
| 1491517 | Dec 2004 | EP |
| 1498277 | Jan 2005 | EP |
| 1512519 | Mar 2005 | EP |
| 1623816 | Feb 2006 | EP |
| 2048235 | Dec 1980 | GB |
| 2155944 | Oct 1985 | GB |
| 3-287683 | Dec 1991 | JP |
| 06 289612 | Oct 1994 | JP |
| 9-241311 | Sep 1997 | JP |
| 11-116875 | Apr 1999 | JP |
| 2001-162351 | Jun 2001 | JP |
| WO-9319019 | Sep 1993 | WO |
| WO 9325336 | Dec 1993 | WO |
| WO-9412328 | Jun 1994 | WO |
| WO 9530503 | Nov 1995 | WO |
| WO-9606881 | Mar 1996 | WO |
| WO-9711835 | Apr 1997 | WO |
| WO 9726302 | Jul 1997 | WO |
| WO 9809798 | Mar 1998 | WO |
| WO 9828124 | Jul 1998 | WO |
| WO 0026026 | May 2000 | WO |
| WO 0134371 | May 2001 | WO |
| WO-0238677 | May 2002 | WO |
| WO-02064354 | Aug 2002 | WO |
| WO-03016030 | Feb 2003 | WO |
| WO-2004048463 | Jun 2004 | WO |
| WO-2004062927 | Jul 2004 | WO |
| WO-2004096514 | Nov 2004 | WO |
| WO-2005011959 | Feb 2005 | WO |
| WO-2005023524 | Mar 2005 | WO |
| WO-2005025074 | Mar 2005 | WO |
| WO-2005090055 | Sep 2005 | WO |
| WO-2005105412 | Nov 2005 | WO |
| WO-2007039450 | Apr 2007 | WO |
| WO-2007147625 | Dec 2007 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20050003189 A1 | Jan 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60472221 | May 2003 | US |