Claims
- 1. A process for preparing a thermoplastic resin for use in a coating resin to be coated on a base film of a magnetic recording tape which comprises the steps of:
- (a) copolymerizing 50 to 80% by weight of a vinyl chloride monomer, 20 to 40% by weight of a vinyl ester monomer and 0 to 15% by weight of a comonomer polymerizable with the vinyl chloride monomer to obtain a vinyl chloride copolymer having an average polymerization degree of 200 to 800;
- (b) hydrolyzing said vinyl chloride copolymer dissolved in a solvent in the presence of an alcohol until the absorption ratio of OH/CH of the hydrolyzed product in the infrared absorption spectrum reaches 0.5 to 0.9;
- (c) decoloring the hydrolyzed product;
- (d) cooling and neutralizing with an organic oxide the solution containing the hydrolyzed product of said vinyl chloride copolymer, said organic oxide being selected from the group consisting of propylene oxide and butylene oxide; and
- (e) removing the alcohol by distillation at a temperature of 40.degree. C. to 70.degree. C. under a reduced pressure of 50 to 200 Torr until the content of said alcohol in the solution reaches less than 1% by weight,
- whereby to obtain the hydrolyzed product in the form of a solution.
- 2. A process according to claim 1, wherein said vinyl ester monomer is a vinyl ester of an alkyl carboxylic acid, said acid having 2 or more carbon atoms.
- 3. A process according to claim 2, wherein said vinyl ester monomer is selected from the group consisting of vinyl acetate and vinyl propionate.
- 4. A process according to claim 1, wherein said comonomer is selected from the group consisting of methacrylic acid and esters thereof, acrylic acid and esters thereof, maleic acid, fumaric acid, acrylonitrile, vinylidene chloride and .alpha.-olefins having 2 to 9 carbon atoms.
- 5. A process according to claim 1, wherein said alcohol used in the hydrolyzing step is selected from the group consisting of methyl alcohol, ethyl alcohol and butyl alcohol.
- 6. A process according to claim 5, wherein an acid catalyst is used at the hydrolyzing step.
- 7. A process according to claim 6, wherein said acid catalyst is selected from the group consisting of hydrochloric acid, sulfuric acid and phosphoric acid.
- 8. A process according to claim 7, wherein said acid catalyst is hydrochloric acid and is added such that the quantity of the hydrochloric acid in a pure state ranges about 2 to 5 parts by weight based on 100 parts by weight of the vinyl chloride copolymer.
- 9. A process according to claim 1, wherein the hydrolyzing step is effected at a temperature of 40.degree. C. to 70.degree. C.
- 10. A process according to claim 1, wherein the hydrolyzed product is decolored by adding 1 to 2 parts by weight of an organic peroxide to the solution containing 100 parts by weight of the hydrolyzed product and maintaining the solution at 40.degree. C. to 70.degree. C. for 3 to 4 hours.
- 11. A process according to claim 10, wherein the organic peroxide is benzoyl peroxide.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of application Ser. No. 24,764 filed Mar. 28, 1979, abandoned.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
2512726 |
Penn et al. |
Jun 1950 |
|
3021318 |
Laporta |
Feb 1962 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
862,978 |
Mar 1961 |
GBX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
24764 |
Mar 1979 |
|