Claims
- 1. Process for preparing a thermotropic copolyester having a mesophase of nematic type, and temperatures of transition from the crystal phase to the mesophase of from about 140.degree. C. up to about 320.degree. C., comprising:
- polymerizing in the molten phase at increasing temperatures of from about 190.degree. C. up to about 320.degree. C. for from 3 to 10 hours a mixture of the following monomers (a), (b), (c) and (d) in the presence of from 0.01 to 1 part by weight per each 100 parts by weight of the monomers of a catalyst selected from the group consisting of the carboxylates of sodium, potassium, calcium and magnesium, the oxides of these metals and oxides of titanium, antimony and tin, with removal of carboxy acid:
- (a) a saturated .alpha., .omega.-dicarboxy aliphatic acid:
- HOOC--(CH.sub.2).sub.n --COOH
- wherein:
- n is a number of from 3 to 8;
- (b) 4,4'-di-acyloxy-diphenyl;
- (c) p-acyloxybenzoic acid; and
- (d) a substituted p-acyloxy-benzoic acid
- wherein the substituted substituent is a halogen atom, or a linear or branched alkyl radical containing from 1 to 4 carbon atoms with the following mutual ratios of the monomers to one another:
- (a)/(b)=1;
- [(c)+(d)]/(a)=1-7;
- (d)/[(c)+(d)]=0.1-1.
- 2. Process according to claim 1, wherein the 4,4'-diacyloxy-diphenyl is 4,4'-diacetoxy-diphenyl, the p-acyloxybenzoic acid is p-acetoxy-benzoic acid, and the substituted p-acyloxy-benzoic acid is a substituted p-acetoxy-benzoic acid, the catalyst is sodium acetate and polymerizing is in the molten phase at increasing temperatures of from about 190.degree. C. up to about 280.degree. C., for from 5 to 7 hours.
- 3. Process according to claim 2, wherein the 4,4'-diacetoxy-diphenyl, p-acetoxy-benzoic acid and substituted p-acetoxy-benzoic acid are formed prior to polymerizing by the reaction of acetic anhydride with 4,4'-dihydroxy-diphenyl, p-hydroxy-benzoic acid and substituted p-hydroxy-benzoic acid.
- 4. Process for preparing a thermotropic copolyester having a mesophase of nematic type, and temperatures of transition from the crystal phase to the mesophase of from about 140.degree. C. up to about 320.degree. C., comprising:
- polymerizing in the molten phase at increasing temperatures of from about 190.degree. C. up to about 320.degree. C. for from 3 to 10 hours a mixture of the following monomers (a), (b), (c) and (d) in the presence of from 0.01 to 1 part by weight per each 100 parts by weight of the monomers of a catalyst selected from the group consisting of the carboxylates of sodium, potassium, calcium and magnesium, the oxides of these metals and oxides of titanium, antimony and tin, with removal of the carboxy acid, and annealing copolymer polymerization product at a temperature of from 130.degree. C. to 210.degree. C. for 1 to 20 hours at a reduced pressure:
- (a) a saturated .alpha., .omega.-dicarboxy aliphatic acid:
- HOOC--(CH.sub.2).sub.n --COOH
- wherein:
- n is a number of from 3 to 8;
- (b) 4,4'-di-acyloxy-diphenyl;
- (c) p-acyloxybenzoic acid; and
- (d) substituted p-acyloxy-benzoic acid
- wherein the substituted substituent is a halogen atom, or a linear or branched alkyl radical containing from 1 to 4 carbon atoms with the following mutual ratios of the monomers to one another:
- (a)/(b)=1;
- [(c)+(d)]/(a)=1-7;
- (d)/[(c)+(d)]=0.1-1.
Priority Claims (1)
Number |
Date |
Country |
Kind |
21079 A/88 |
Jun 1988 |
ITX |
|
Parent Case Info
This is a division of application Ser. No. 07/358,145, filed on May 30, 1989, now U.S. Pat. No. 4,970,285.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4390681 |
Deex |
Jun 1983 |
|
Divisions (1)
|
Number |
Date |
Country |
Parent |
358145 |
May 1989 |
|