Thick-film pastes containing lead-tellurium-boron-oxides, and their use in the manufacture of semiconductor devices

Information

  • Patent Grant
  • 10559703
  • Patent Number
    10,559,703
  • Date Filed
    Wednesday, March 13, 2013
    11 years ago
  • Date Issued
    Tuesday, February 11, 2020
    4 years ago
Abstract
The present invention provides a thick-film paste for printing the front side of a solar cell device having one or more insulating layers. The thick-film paste comprises an electrically conductive metal and a lead-tellurium-boron-oxide dispersed in an organic medium.
Description
FIELD OF THE INVENTION

The present invention provides a thick-film paste for printing the front side of a solar cell device having one or more insulating layers. The thick-film paste includes an electrically conductive metal or derivative thereof, and a lead-tellurium-boron-oxide dispersed in an organic medium.


TECHNICAL BACKGROUND

A conventional solar cell structure with a p-type base has a negative electrode that is typically on the front side (sun side) of the cell and a positive electrode on the back-side. Radiation of an appropriate wavelength falling on a p-n junction of a semiconductor body serves as a source of external energy to generate electron-hole pair charge carriers. These electron-hole pair charge carriers migrate in the electric field generated by the p-n semiconductor junction and are collected by a conductive grid or metal contact applied to the surface of the semiconductor. The current generated flows to the external circuit.


Conductive pastes (also known as inks) are typically used to form the conductive grids or metal contacts. Conductive pastes typically include a glass frit, a conductive species (e.g., silver particles), and an organic medium. To form the metal contacts, conductive pastes are printed onto a substrate as grid lines or other patterns and then fired, during which electrical contact is made between the grid lines and the semiconductor substrate.


However, crystalline silicon PV cells are typically coated with an anti-reflective coating such as silicon nitride, titanium oxide, or silicon oxide to promote light adsorption, which increases the cells' efficiency. Such anti-reflective coatings also act as an insulator, which impairs the flow of electrons from the substrate to the metal contacts. To overcome this problem, the conductive paste should penetrate the anti-reflective coating during firing to form metal contacts having electrical contact with the semiconductor substrate. Formation of a strong bond between the metal contact and the substrate i.e., adhesion) and solderability are also desirable.


The ability to penetrate the anti-reflective coating and form a strong bond with the substrate upon firing is highly dependent on the composition of the conductive paste and firing conditions. Efficiency, a key measure of PV cell performance, is also influenced by the quality of the electrical contact made between the fired conductive paste and the substrate.


To provide an economical process for manufacturing PV cells with good efficiency, there is a need for thick-film paste compositions that can be fired at low temperatures to penetrate an anti-reflective coating and provide good electrical contact with the semiconductor substrate.


SUMMARY

One aspect of the present invention is a thick-film paste composition comprising:

    • a) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • b) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide; and
    • c) an organic medium.


A further aspect of the present invention is a thick-film paste composition comprising:

    • a) 84.5 to 99% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • b) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide;
    • c) 0.5 to 15% by weight based on solids of a lead-tellurium-lithium-titanium-oxide; and
    • d) an organic medium.


Another aspect of the present invention is a process comprising:

  • (a) providing a semiconductor substrate comprising one or more insulating films deposited onto at least one surface of the semiconductor substrate;
  • (b) applying a thick-film paste composition onto the one or more insulating films to form a layered structure, wherein the thick-film paste composition includes:
    • i) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • ii) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide; and
    • iii) an organic medium; and
  • (c) firing the semiconductor substrate, one or more insulating films, and thick-film paste, forming an electrode in contact with the one or more insulating layers and in electrical contact with the semiconductor substrate.


Another aspect of the present invention is a process comprising:

  • (a) providing a semiconductor substrate comprising one or more insulating films deposited onto at least one surface of the semiconductor substrate;
  • (b) applying a thick-film paste composition onto the one or more insulating films to form a layered structure, wherein the thick-film paste composition includes:
    • i) 84.5 to 99% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • ii) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide;
    • iii) 0.5 to 15% by weight based on solids of lead-tellurium-lithium-titanium-oxide; and
    • iv) an organic medium; and
  • (c) firing the semiconductor substrate, one or more insulating films, and thick-film paste, forming an electrode in contact with the one or more insulating layers and in electrical contact with the semiconductor substrate.


Another aspect of this invention is an article comprising:

    • a) a semiconductor substrate;
    • b) one or more insulating layers on the semiconductor substrate; and
    • c) an electrode in contact with the one or more insulating layers and in electrical contact with the semiconductor substrate, the electrode comprising an electrically conductive metal and a lead-tellurium-boron-oxide.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a process flow diagram illustrating the fabrication of a semiconductor device. Reference numerals shown in FIG. 1 are explained below.








  • 10: p-type silicon substrate


  • 20: n-type diffusion layer


  • 30: insulating film


  • 40: p+ layer (back surface field, BSF)


  • 60: aluminum paste deposited on back side


  • 61: aluminum back electrode (obtained by firing back-side aluminum paste)


  • 70: silver or silver/aluminum paste deposited on back side


  • 71: silver or silver/aluminum back electrode (obtained by firing back-side silver paste)


  • 500: thick-film paste deposited on front side


  • 501: front electrode (formed by firing the thick-film paste)




FIG. 1(a) shows a single-crystal silicon or multi-crystalline silicon p-type substrate 10.


In FIG. 1(b), an n-type diffusion layer 20 of the reverse polarity is formed to create a p-n junction. The n-type diffusion layer 20 can be formed by thermal diffusion of phosphorus (P) using phosphorus oxychloride (POCl3) as the phosphorus source. In the absence of any particular modifications, the n-type diffusion layer 20 is formed over the entire surface of the silicon p-type substrate. The depth of the diffusion layer can be varied by controlling the diffusion temperature and time, and is generally formed in a thickness range of about 0.3 to 0.5 microns. The n-type diffusion layer may have a sheet resistivity of several tens of ohms per square up to about 120 ohms per square.


After protecting one surface of the n-type diffusion layer 20 with a resist or the like, as shown in FIG. 1(c), the n-type diffusion layer 20 is removed from most surfaces by etching so that it remains only on one main surface. The resist is then removed using an organic solvent or the like.


Next, in FIG. 1(d), an insulating layer 30 which also functions as an anti-reflection coating is formed on the n-type diffusion layer 20. The insulating layer is commonly silicon nitride, but can also be a SiNx:H film (i.e., the insulating film includes hydrogen for passivation during subsequent firing processing), a titanium oxide film, a silicon oxide film, silicon carbon oxynitride, a silicon nitride film containing carbon, a silicon oxide film containing carbon, or a silicon oxide/titanium oxide film. A thickness of about 700 to 900 Å of a silicon nitride film is suitable for a refractive index of about 1.9 to 2.0. Deposition of the insulating layer 30 can be by sputtering, chemical vapor deposition, or other methods.


Next, electrodes are formed. As shown in FIG. 1(e), a thick-film paste composition of this invention is screen-printed on the insulating film 30, and then dried. In addition, aluminum paste 60 and back-side silver paste 70 are screen-printed onto the back side of the substrate, and successively dried. Firing is carried out at a temperature of 750 to 850° C. for a period of from several seconds to several tens of minutes.


Consequently, as shown in FIG. 1(f), during firing, aluminum diffuses from the aluminum paste into the silicon substrate on the back side, thereby forming a p+ layer 40, containing a high concentration of aluminum dopant. This layer is generally called the back surface field (BSF) layer, and helps to improve the energy conversion efficiency of the solar cell. Firing converts the dried aluminum paste 60 to an aluminum back electrode 61. The back-side silver paste 70 is fired at the same time, becoming a silver or silver/aluminum back electrode 71. During firing, the boundary between the back-side aluminum and the back-side silver assumes the state of an alloy, thereby achieving electrical connection. Most areas of the back electrode are occupied by the aluminum electrode, owing in part to the need to form a p+ layer 40. At the same time, because soldering to an aluminum electrode is impossible, the silver or silver/aluminum back electrode is formed on limited areas of the back side as an electrode for interconnecting solar cells by means of copper ribbon or the like.


On the front side, the thick-film paste composition 500 of the present invention sinters and penetrates through the insulating film 30 during firing, and thereby achieves electrical contact with the n-type diffusion layer 20. This type of process is generally called “fire through.” This fired-through state, i.e., the extent to which the paste melts and passes through the insulating film 30, depends on the quality and thickness of the insulating film 30, the composition of the paste, and on the firing conditions. When fired, the paste 500 becomes the electrode 501, as shown in FIG. 1(f).


DETAILED DESCRIPTION

Solar-powered photovoltaic systems are considered to be environmentally friendly in that they reduce the need for fossil fuels.


The present invention provides compositions that can be used to manufacture photovoltaic devices with improved electrical performance. The thick-film paste composition includes:

    • a) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • b) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide, and
    • c) an organic medium.


      The thick-film paste composition may further include 0.5 to 15% by weight based on solids of a lead-tellurium-lithium-titanium-oxide.


As defined herein, the organic medium is not considered to be part of the solids in the thick-film paste composition.


Electrically Conductive Metal


The electrically conductive metal is selected from the group consisting of silver, copper, and palladium. The electrically conductive metal can be in a flake form, a spherical form, a granular form, a crystalline form, a powder, or other irregular forms and mixtures thereof. The electrically conductive metal can be provided in a colloidal suspension.


When the metal is silver, it can be in the form of silver metal, silver derivatives, or mixtures thereof. Exemplary derivatives include: alloys of silver, silver oxide (Ag2O), silver salts such as AgCl, AgNO3, AgOOCCH3 (silver acetate), AgOOCF3 (silver trifluoroacetate), silver orthophosphate (Ag3PO4), for example. Other forms of silver compatible with the other thick-film paste components can also be used.


In one embodiment, the electrically conductive metal or derivatives thereof is from about 85 to about 99.5 wt % of the solid components of the thick-film paste composition. In a further embodiment, the electrically conductive metal or derivatives thereof is from about 90 to about 95 wt % of the solid components of the thick-film paste composition.


In an embodiment, the solids portion of the thick-film paste composition includes about 85 to about 99.5 wt % spherical silver particles. In one embodiment, the solids portion of the thick-film paste composition includes about 85 to about 90 wt % silver particles and about 1 to about 9.5 wt % silver flakes.


In one embodiment, the thick-film paste composition includes coated silver particles that are electrically conductive. Suitable coatings include phosphate and surfactants. Suitable surfactants include polyethyleneoxide, polyethyleneglycol, benzotriazole, poly(ethyleneglycol)acetic acid, lauric acid, oleic acid, capric acid, myristic acid, linolic acid, stearic acid, palmitic acid, stearate salts, palmitate salts, and mixtures thereof. The salt counter-ions can be ammonium, sodium, potassium, and mixtures thereof.


The particle size of the silver is not subject to any particular limitation. In one embodiment, an average particle size is 0.5-10 microns; in another embodiment, the average particle size is 1-5 microns. As used herein, “particle size” or “D50” is intended to mean “average particle size”; “average particle size” means the 50% volume distribution size. Volume distribution size may be determined by LASER diffraction and dispersion method using a Microtrac particle size analyzer.


Lead-Tellurium-Boron-Oxide Compositions


An aspect of the invention relates to lead-tellurium-boron-oxide (Pb—Te—B—O) compositions. In an embodiment, these compositions may be glass compositions. In a further embodiment, these compositions may be crystalline, partially crystalline, amorphous, partially amorphous, or combinations thereof. In an embodiment, the Pb—Te—B—O composition may include more than one glass composition. In an embodiment, the Pb—Te—B—O composition may include a glass composition and an additional composition, such as a crystalline composition. The terms “glass” or “glass composition” will be used herein to represent any of the above combinations of amorphous and crystalline materials.


In an embodiment, glass compositions described herein include lead-tellurium-boron-oxide. The glass compositions may also include additional components such as silicon, silver, tin, bismuth, aluminum, titanium, copper, lithium, cerium, zirconium, sodium, vanadium, zinc, flourine, and the like.


The lead-tellurium-boron-oxide (Pb—Te—B—O) may be prepared by mixing PbO, TeO2, and B2O3 (or other materials that decompose into the desired oxides when heated) using techniques understood by one of ordinary skill in the art. Such preparation techniques may involve heating the mixture in air or an oxygen-containing atmosphere to form a melt, quenching the melt, and grinding, milling, and/or screening the quenched material to provide a powder with the desired particle size. Melting the mixture of lead, tellurium, and boron oxides is typically conducted to a peak temperature of 800 to 1200° C. The molten mixture can be quenched, for example, on a stainless steel platen or between counter-rotating stainless steel rollers to form a platelet. The resulting platelet can be milled to form a powder. Typically, the milled powder has a D50 of 0.1 to 3.0 microns. One skilled in the art of producing glass frit may employ alternative synthesis techniques such as but not limited to water quenching, sol-gel, spray pyrolysis, quenching by splat cooling on a metal platen, or others appropriate for making powder forms of glass.


In an embodiment, the starting mixture used to make the Pb—Te—B—O may include (based on the weight of the total starting mixture): PbO that may be 25 to 75 wt %, 30 to 60 wt %, or 30 to 50 wt %; TeO2 that may be 10 to 70 wt %, 25 to 60 wt %, or 40 to 60 wt %; B2O3 that may be 0.1 to 15 wt %, 0.25 to 5 wt %, or 0.4 to 2 wt %.


In an embodiment, PbO, TeO2, and B2O3 may be 80-100 wt % of the Pb—Te—B—O composition. In a further embodiment, PbO, TeO2, and B2O3 may be 85-100 wt % or 90-100 wt % of the Pb—Te—B—O composition.


In a further embodiment, in addition to the above PbO, TeO2, and B2O3, the starting mixture used to make the Pb—Te—B—O may include one or more of PbF2, SiO2, BiF3, SnO2, Li2O, Bi2O3, ZnO, V2O5, Na2O, TiO2, Al2O3, CuO, ZrO2, CeO2, or Ag2O. In an embodiment, one or more of these components may be 0-20 wt %, 0-15 wt %, or 0-10 wt % of the Pb—Te—B—O composition. In aspects of this embodiment (based on the weight of the total starting mixture):


the PbF2 may be 0 to 20 wt %, 0 to 15 wt %, or 5 to 10 wt %;


the SiO2 may be 0 to 11 wt %, 0 to 5 wt %, 0.25 to 4 wt %, or 0 to 0.5 wt %;


the BiF3 may be 0 to 15 wt %, 0 to 10 wt %, or 1 to 10 wt %;


the SnO2 may be 0 to 5 wt %, 0 to 2 wt %, or 0.5 to 1.5 wt %;


the ZnO may be 0 to 5 wt %, 0 to 3 wt %, or 2 to 3 wt %;


the V2O5 may be 0 to 5 wt %, 0 to 1 wt %, or 0.5 to 1 wt %;


the Na2O may be 0 to 5 wt %, 0 to 3 wt %, or 0.1 to 1.5 wt %;


the CuO may be 0 to 5 wt %, 0 to 3 wt %, or 2 to 3 wt %;


the ZrO2 may be 0 to 3 wt %, 0 to 2 wt %, or 0.1 to 1 wt %;


the CeO2 may be 0 to 5 wt %, 0 to 3 wt %, or 0.1 to 2.5 wt %;


the Li2O may be 0 to 5 wt %, 0.1 to 3 wt %, or 0.25 to 2 wt %;


the Bi2O3 may be 0 to 15 wt %, 0 to 10 wt %, or 5 to 8 wt %;


the TiO2 may be 0 to 5 wt %, 0.25 to 5 wt %, or 0.25 to 2.5 wt %;


the Al2O3 may be 0 to 3 wt %, 0 to 2 wt % or 0.1 to 2 wt %; and


the Ag2O may be 0 to 10 wt %, 1 to 10 wt %, or 1 to 8 wt %.


In an embodiment, the Pb—Te—B—O may be a homogenous powder. In a further embodiment, the Pb—Te—B—O may be a combination of more than one powder, wherein each powder may separately be a homogenous population. The composition of the overall combination of the multiple powders is within the ranges described above. For example, the Pb—Te—B—O may include a combination of two or more different powders; separately, these powders may have different compositions, and may or may not be within the ranges described above; however, the combination of these powders is within the ranges described above.


In an embodiment, the Pb—Te—B—O composition may include one powder which includes a homogenous powder including some but not all of the elements of the group Pb, Te, B, and O, and a second powder, which includes one or more of the elements of the group Pb, Te, B, and O. For example, the Pb—Te—B—O composition may include a first powder including Pb, Te, and O, and a second powder including B2O3. In an aspect of this embodiment, the powders may be melted together to form a uniform composition. In a further aspect of this embodiment, the powders may be added separately to a thick-film composition.


In an embodiment, some or all of the Li2O may be replaced with Na2O, K2O, Cs2O, or Rb2O, resulting in a glass composition with properties similar to the compositions listed above. In this embodiment, the total alkali metal oxide content may be 0 to 5 wt %, 0.1 to 3 wt %, or 0.25 to 3 wt %.


In a further embodiment, the Pb—Te—B—O composition(s) herein may include one or more of a third set of components: GeO2, Ga2O3, In2O3, NiO, CoO, ZnO, CaO, MgO, SrO, MnO, BaO, SeO2, MoO3, WO3, Y2O3, As2O3, La2O3, Nd2O3, Bi2O3, Ta2O5, V2O5, FeO, HfO2, Cr2O3, CdO, Sb2O3, PbF2, ZrO2, Mn2O3, P2O5, CuO, Pr2O3, Gd2O3, Sm2O3, Dy2O3, Eu2O3, Ho2O3, Yb2O3, Lu2O3, CeO2, BiF3, SnO, SiO2, Ag2O, Nb2O5, TiO2, Rb2O, SiO2, Na2O, K2O, Cs2O, Lu2O3, SnO2, and metal halides (e.g., NaCl, KBr, NaI, LiF, ZnF2).


Therefore as used herein, the term “Pb—Te—B—O” may also include metal oxides that contain one or more oxides of elements selected from the group consisting of Si, Sn, Li, Ti, Ag, Na, K, Rb, Cs, Ge, Ga, In, Ni, Zn, Ca, Mg, Sr, Ba, Se, Mo, W, Y, As, La, Nd, Co, Pr, Gd, Sm, Dy, Eu, Ho, Yb, Lu, Bi, Ta, V, Fe, Hf, Cr, Cd, Sb, Bi, F, Zr, Mn, P, Cu, Ce, and Nb.


Table 1 lists some examples of powder mixtures containing PbO, TeO2, B2O3, and other optional compounds that can be used to make lead-tellurium-boron-oxides. This list is meant to be illustrative, not limiting. In Table 1, the amounts of the compounds are shown as weight percent, based on the weight of the total glass composition.


Typically, the mixture of PbO and TeO2 powders includes 5 to 95 mol % of lead oxide and 5 to 95 mol % of tellurium oxide, based on the combined powders. In an embodiment the mole ratio of lead to tellurium of the lead-tellurium-boron-oxide is between 5/95 and 95/5. In one embodiment, the mixture of PbO and TeO2 powders includes 30 to 85 mol % of lead oxide and 15 to 70 mol % of tellurium oxide, based on the combined powders.


Glass compositions, also termed glass frits, are described herein as including percentages of certain components. Specifically, the percentages are the percentages of the components used in the starting material that was subsequently processed as described herein to form a glass composition. Such nomenclature is conventional to one of skill in the art. In other words, the composition contains certain components, and the percentages of those components are expressed as a percentage of the corresponding oxide form. As recognized by one of ordinary skill in the art in glass chemistry, a certain portion of volatile species may be released during the process of making the glass. An example of a volatile species is oxygen.


If starting with a fired glass, one of ordinary skill in the art may calculate the percentages of starting components described herein using methods known to one of skill in the art including, but not limited to: Inductively Coupled Plasma-Emission Spectroscopy (ICPES), Inductively Coupled Plasma-Atomic Emission Spectroscopy (ICP-AES), and the like. In addition, the following exemplary techniques may be used: X-Ray Fluorescence spectroscopy (XRF); Nuclear Magnetic Resonance spectroscopy (NMR); Electron Paramagnetic Resonance spectroscopy (EPR); Mössbauer spectroscopy; electron microprobe Energy Dispersive Spectroscopy (EDS); electron microprobe Wavelength Dispersive Spectroscopy (WDS); Cathodo-Luminescence (CL).


One of ordinary skill in the art would recognize that the choice of raw materials could unintentionally include impurities that may be incorporated into the glass during processing. For example, the impurities may be present in the range of hundreds to thousands ppm.


The presence of the impurities would not alter the properties of the glass, the thick-film composition, or the fired device. For example, a solar cell containing the thick-film composition may have the efficiency described herein, even if the thick-film composition includes impurities.


Lead-Tellurium-Boron-Oxide and Lead-Tellurium-Lithium-Titanium-Oxide Compositions


An aspect of the invention relates to lead-tellurium-boron-oxide (Pb—Te—B—O) and lead-tellurium-lithium-titanium-oxide (Pb—Te—Li—Ti—O) compositions. In an embodiment, these compositions may be glass compositions. In a further embodiment, these compositions may be crystalline, partially crystalline, amorphous, partially amorphous, or combinations thereof. An embodiment relates to mixtures of Pb—Te—B—O and Pb—Te—Li—Ti—O compositions.


An embodiment of the invention relates to pastes including Pb—Te—B—O and Pb—Te—Li—Ti—O. It is contemplated that the pastes including Pb—Te—B—O pastes described herein may also include Pb—Te—Li—Ti—O.


In an embodiment, the Pb—Te—Li—Ti—O composition may include more than one glass composition. In an embodiment, the Pb—Te—Li—Ti—O composition may include a glass composition and an additional composition, such as a crystalline composition.


The Pb—Te—Li—Ti—O may also include oxides of additional components such as silicon, boron, silver, tin, and the like.


The lead-tellurium-lithium-titanium-oxide (Pb—Te—Li—Ti—O) may be prepared in an analogous manner to that described above for Pb—Te—B—O.


In an embodiment, the starting mixture used to make the Pb—Te—Li—Ti—O may include (based on the weight of the total starting mixture): PbO that may be 25 to 80 wt %, 30 to 60 wt %, or 30 to 50 wt %; TeO2 that may be 10 to 70 wt %, 30 to 65 wt %, or 50 to 65 wt %; Li2O that may be 0.1 to 5 wt %, 0.25 to 3 wt %, or 0.5 to 2.5 wt %; TiO2 that may be 0.1 to 5 wt %, 0.25 to 5 wt %, or 0.5 to 3 wt %.


In an embodiment, PbO, TeO2, Li2O, and TiO2 may be 80-100 wt % 85-100 wt %, or 90-100 wt %, of the Pb—Te—Li—Ti—O composition.


In a further embodiment, in addition to the above PbO, TeO2, Li2O, and TiO2, the starting mixture used to make the Pb—Te—Li—Ti—O may include one or more of SiO2, SnO2, B2O3, or Ag2O. In an embodiment, one or more of these components may be 0-20 wt %, 0-15 wt %, or 0-10 wt % of the Pb—Te—Li—Ti—O composition. In aspects of this embodiment (based on the weight of the total starting mixture):


the SiO2 may be 0 to 10 wt %, 0 to 9 wt %, or 2 to 9 wt %;


the SnO2 may be 0 to 5 wt %, 0 to 4 wt %, or 0.5 to 1.5 wt %;


the B2O3 may be 0 to 10 wt %, 0 to 5 wt %, or 1 to 5 wt %; and


the Ag2O may be 0 to 30 wt %, 0 to 20 wt %, or 3 to 15 wt %.


In an embodiment, the Pb—Te—Li—Ti—O may be a homogenous powder. In a further embodiment, the Pb—Te—Li—Ti—O may be a combination of more than one powder, wherein each powder may separately be a homogenous population. The composition of the overall combination of the two or more powders is within the ranges described above. For example, the Pb—Te—Li—Ti—O may include a combination of two or more different powders; separately, these powders may have different compositions, and may or may not be within the ranges described above; however, the combination of these powders is within the ranges described above.


In an embodiment, the Pb—Te—Li—Ti—O composition may include one powder which includes a homogenous powder including some but not all of the elements of the group Pb, Te, Li, Ti, and O, and a second powder, which includes one or more of the elements of the group Pb, Te, Li, Ti, and O. For example, the Pb—Te—Li—Ti—O composition may include a first powder including Pb, Te, Li, and O, and a second powder including TiO2. In an aspect of this embodiment, the powders may be melted together to form a uniform composition. In a further aspect of this embodiment, the powders may be added separately to a thick-film composition.


In an embodiment, some or all of the Li2O may be replaced with Na2O, K2O, Cs2O, or Rb2O, resulting in a glass composition with properties similar to the compositions listed above. In this embodiment, the total alkali metal oxide content may be 0 to 5 wt %, 0.1 to 3 wt %, or 0.25 to 3 wt %.


In a further embodiment, the Pb—Te—Li—Ti—O composition(s) herein may include one or more of a third set of components: GeO2, Ga2O3, In2O3, NiO, CoO, ZnO, CaO, MgO, SrO, MnO, BaO, SeO2, MoO3, WO3, Y2O3, As2O3, La2O3, Nd2O3, Bi2O3, Ta2O5, V2O5, FeO, HfO2, Cr2O3, CdO, Sb2O3, PbF2, ZrO2, Mn2O3, P2O5, CuO, Pr2O3, Gd2O3, Sm2O3, Dy2O3, Eu2O3, Ho2O3, Yb2O3, Lu2O3, CeO2, BiF3, SnO, SiO2, Ag2O, Nb2O5, TiO2, Rb2O, SiO2, Na2O, K2O, Cs2O, Lu2O3, SnO2, and metal halides (e.g., NaCl, KBr, NaI, LiF, ZnF2).


Therefore as used herein, the term “Pb—Te—Li—Ti—O” may also include one or more oxides of the elements selected from the group consisting of Si, Sn, B, Ag, Na, K, Rb, Cs, Ge, Ga, In, Ni, Co, Zn, Ca, Mg, Sr, Ba, Se, Mo, W, Y, As, La, Nd, Bi, Ta, V, Fe, Hf, Pr, Gd, Sm, Dy, Eu, Ho, Yb, Lu, Ti, Cr, Cd, Sb, Bi, F, Zr, Mn, P, Cu, Ce, and Nb.


Table 3 lists some examples of powder mixtures containing PbO, TeO2, Li2O, TiO2, and other optional compounds that can be used to make lead-tellurium-lithium-titanium oxides. This list is meant to be illustrative, not limiting. In Table 3, the amounts of the compounds are shown as weight percent, based on the weight of the total glass composition.


In an embodiment, the mixture of PbO and TeO2 powders includes 5 to 95 mol % of lead oxide and 5 to 95 mol % of tellurium oxide, based on the combined powders. In an embodiment the mole ratio of lead to tellurium of the lead-tellurium-lithium-titanium-oxide is between 5/95 and 95/5. In one embodiment, the mixture of PbO and TeO2 powders include 30 to 85 mol % of lead oxide and 15 to 70 mol % of tellurium oxide, based on the combined powders.


Organic Medium


The inorganic components of the thick-film paste composition are mixed with an organic medium to form viscous pastes having suitable consistency and rheology for printing. A wide variety of inert viscous materials can be used as the organic medium. The organic medium can be one in which the inorganic components are dispersible with an adequate degree of stability during manufacturing, shipping, and storage of the pastes, as well as on the printing screen during a screen-printing process.


Suitable organic media have rheological properties that provide stable dispersion of solids, appropriate viscosity and thixotropy for screen printing, appropriate wettability of the substrate and the paste solids, a good drying rate, and good firing properties. The organic medium can contain thickeners, stabilizers, surfactants, and/or other common additives. The organic medium can be a solution of polymer(s) in solvent(s). Suitable polymers include ethyl cellulose, ethylhydroxyethyl cellulose, wood rosin, mixtures of ethyl cellulose and phenolic resins, polymethacrylates of lower alcohols, and the monobutyl ether of ethylene glycol monoacetate. Suitable solvents include terpenes such as alpha- or beta-terpineol or mixtures thereof with other solvents such as kerosene, dibutylphthalate, butyl carbitol, butyl carbitol acetate, hexylene glycol and alcohols with boiling points above 150° C., and alcohol esters. Other suitable organic medium components include: bis(2-(2-butoxyethoxy)ethyl adipate, dibasic esters such as DBE, DBE-2, DBE-3, DBE-4, DBE-5, DBE-6, DBE-9, and DBE 1B, octyl epoxy tallate, isotetradecanol, and pentaerythritol ester of hydrogenated rosin. The organic medium can also include volatile liquids to promote rapid hardening after application of the thick-film paste composition on a substrate.


The optimal amount of organic medium in the thick-film paste composition is dependent on the method of applying the paste and the specific organic medium used. Typically, the thick-film paste composition contains 70 to 95 wt % of inorganic components and 5 to 30 wt % of organic medium.


If the organic medium includes a polymer, the organic composition may include 8 to 15 wt % polymer.


Preparation of the Thick-Film Paste Composition


In one embodiment, the thick-film paste composition can be prepared by mixing the conductive metal powder, the Pb—Te—B—O powder, and the organic medium in any order. In an embodiment, the thick-film paste composition may also include Pb—Te—Li—Ti—O. In some embodiments, the inorganic materials are mixed first, and they are then added to the organic medium. The viscosity can be adjusted, if needed, by the addition of one or more solvents. Mixing methods that provide high shear may be useful.


Another aspect of the present invention is a process comprising:

  • (a) providing a semiconductor substrate comprising one or more insulating films deposited onto at least one surface of the semiconductor substrate;
  • (b) applying a thick-film paste composition onto at least a portion of the one or more insulating films to form a layered structure, wherein the thick-film paste composition includes:
    • i) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • ii) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide; and
    • iii) an organic medium; and
  • (c) firing the semiconductor substrate, one or more insulating films, and thick-film paste, forming an electrode in contact with the one or more insulating layers and in electrical contact with the semiconductor substrate.


A further aspect of the present invention is a process comprising:

  • (a) providing a semiconductor substrate comprising one or more insulating films deposited onto at least one surface of the semiconductor substrate;
  • (b) applying a thick-film paste composition onto at least a portion of the one or more insulating films to form a layered structure, wherein the thick-film paste composition includes:
    • i) 84.5 to 99% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;
    • ii) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide;
    • iii) 0.5 to 15% by weight based on solids of a lead-tellurium-lithium-titanium-oxide; and
    • iv) an organic medium; and
  • (c) firing the semiconductor substrate, one or more insulating films, and thick-film paste, forming an electrode in contact with the one or more insulating layers and in electrical contact with the semiconductor substrate.


In an embodiment, the thick-film paste may include lead-tellurium-boron-oxide in an amount of 0.5 to 15%, 0.5 to 7%, or 1 to 3% by weight based on solids.


In one embodiment, a semiconductor device is manufactured from an article comprising a junction-bearing semiconductor substrate and a silicon nitride insulating film formed on a main surface thereof. The process includes the steps of applying (for example, coating or screen-printing) onto the insulating film, in a predetermined shape and thickness and at a predetermined position, the thick-film paste composition having the ability to penetrate the insulating layer, then firing so that thick-film paste composition reacts with the insulating film and penetrates the insulating film, thereby effecting electrical contact with the silicon substrate.


One embodiment of this process is illustrated in FIG. 1.



FIG. 1(a) shows a single-crystal n or multi-crystalline silicon p-type substrate 10.


In FIG. 1(b), an n-type diffusion layer 20 of the reverse polarity is formed to create a p-n junction. The n-type diffusion layer 20 can be formed by thermal diffusion of phosphorus (P) using phosphorus oxychloride (POCl3) as the phosphorus source. In the absence of any particular modifications, the n-type diffusion layer 20 is formed over the entire surface of the silicon p-type substrate. The depth of the diffusion layer can be varied by controlling the diffusion temperature and time, and is generally formed in a thickness range of about 0.3 to 0.5 microns. The n-type diffusion layer may have a sheet resistivity of several tens of ohms per square up to about 120 ohms per square.


After protecting one surface of the n-type diffusion layer 20 with a resist or the like, as shown in FIG. 1(c), the n-type diffusion layer 20 is removed from most surfaces by etching so that it remains only on one main surface. The resist is then removed using an organic solvent or the like.


Next, in FIG. 1(d), an insulating layer 30 which also functions as an anti-reflection coating is formed on the n-type diffusion layer 20. The insulating layer is commonly silicon nitride, but can also be a SiNx:H film (i.e., the insulating film includes hydrogen for passivation during subsequent firing processing), a titanium oxide film, a silicon oxide film, silicon carbon oxynitride, a silicon nitride film containing carbon, a silicon oxide film containing carbon, or a silicon oxide/titanium oxide film. A thickness of about 700 to 900 Å of a silicon nitride film is suitable for a refractive index of about 1.9 to 2.0, Deposition of the insulating layer 30 can be by sputtering, chemical vapor deposition, or other methods.


Next, electrodes are formed. As shown in FIG. 1(e), a thick-film paste composition of this invention is screen-printed on the insulating film 30, and then dried. In addition, aluminum paste 60 and back-side silver paste 70 are screen-printed onto the back side of the substrate, and successively dried. Firing is carried out at a temperature of 750 to 850° C. for a period of from several seconds to several tens of minutes.


Consequently, as shown in FIG. 1(f), during firing, aluminum diffuses from the aluminum paste into the silicon substrate on the back side, thereby forming a p+ layer 40, containing a high concentration of aluminum dopant. This layer is generally called the back surface field (BSF) layer, and helps to improve the energy conversion efficiency of the solar cell. Firing converts the dried aluminum paste 60 to an aluminum back electrode 61. The back-side silver paste 70 is fired at the same time, becoming a silver or silver/aluminum back electrode 71. During firing, the boundary between the back-side aluminum and the back-side silver assumes the state of an alloy, thereby achieving electrical connection. Most areas of the back electrode are occupied by the aluminum electrode, owing in part to the need to form a p+ layer 40. At the same time, because soldering to an aluminum electrode is impossible, the silver or silver/aluminum back electrode is formed on limited areas of the back side as an electrode for interconnecting solar cells by means of copper ribbon or the like.


On the front side, the thick-film paste composition 500 of the present invention sinters and penetrates through the insulating film 30 during firing, and thereby achieves electrical contact with the n-type diffusion layer 20. This type of process is generally called “fire through.” This fired-through state, i.e., the extent to which the paste melts and passes through the insulating film 30, depends on the quality and thickness of the insulating film 30, the composition of the paste, and on the firing conditions. When fired, the paste 500 becomes the electrode 501, as shown in FIG. 1(f).


In one embodiment, the insulating film is selected from titanium oxide, aluminum oxide, silicon nitride, SiNx:H, silicon oxide, silicon carbon oxynitride, a silicon nitride film containing carbon, a silicon oxide film containing carbon, and silicon oxide/titanium oxide films. The silicon nitride film can be formed by sputtering, plasma-enhanced chemical vapor deposition (PECVD), or a thermal CVD process. In one embodiment, the silicon oxide film is formed by thermal oxidation, sputtering, or thermal CVD or plasma CVD. The titanium oxide film can be formed by coating a titanium-containing organic liquid material onto the semiconductor substrate and firing, or by thermal CVD.


In one embodiment of this process, the semiconductor substrate can be single-crystal or multi-crystalline silicon.


Suitable insulating films include one or more components selected from: aluminum oxide, titanium oxide, silicon nitride, SiHx:H, silicon oxide, and silicon oxide/titanium oxide. In one embodiment of the invention, the insulating film is an anti-reflection coating (ARC). The insulating film can be applied to a semiconductor substrate, or it can be naturally forming, such as in the case of silicon oxide.


In one embodiment, the insulating film includes a layer of silicon nitride. The silicon nitride can be deposited by CVD (chemical vapor deposition), PECVD (plasma-enhanced chemical vapor deposition), sputtering, or other methods.


In one embodiment, the silicon nitride of the insulating layer is treated to remove at least a portion of the silicon nitride. The treatment can be a chemical treatment. The removal of at least a portion of the silicon nitride may result in an improved electrical contact between the conductor of the thick-film paste composition and the semiconductor substrate. This may result in improved efficiency of the semiconductor device.


In one embodiment, the silicon nitride of the insulating film is part of an anti-reflective coating.


The thick-film paste composition can be printed on the insulating film in a pattern, e.g., bus bars with connecting lines. The printing can be by screen-printing, plating, extrusion, inkjet, shaped or multiple printing, or ribbons.


In this electrode-forming process, the thick-film paste composition is heated to remove the organic medium and sinter the metal powder. The heating can be carried out in air or an oxygen-containing atmosphere. This step is commonly referred to as “firing.” The firing temperature profile is typically set so as to enable the burnout of organic binder materials from the dried thick-film paste composition, as well as any other organic materials present. In one embodiment, the firing temperature is 750 to 950° C. The firing can be conducted in a belt furnace using high transport rates, for example, 100-500 cm/min, with resulting hold-up times of 0.05 to 5 minutes. Multiple temperature zones, for example 3 to 11 zones, can be used to control the desired thermal profile.


Upon firing, the electrically conductive metal and Pb—Te—B—O mixture penetrate the insulating film. The penetration of the insulating film results in an electrical contact between the electrode and the semiconductor substrate. After firing, an interlayer may be formed between the semiconductor substrate and the electrode, wherein the interlayer includes one or more of tellurium, tellurium compounds, lead, lead compounds, boron compounds, and silicon compounds, where the silicon may originate from the silicon substrate and/or the insulating layer(s). After firing, the electrode includes sintered metal that contacts the one or more insulating layers, and may also contact the underlying semiconductor substrate.


Another aspect of the present invention is an article formed by a process comprising:

  • (a) providing a semiconductor substrate comprising one or more insulating films deposited onto at least one surface of the semiconductor substrate:
  • (b) applying a thick-film paste composition onto at least a portion of the one or more insulating films to form a layered structure,


    wherein the thick-film paste composition includes:
    • i) 85 to 99.5% by weight of electrically conductive metal or derivative thereof, based on total solids in the composition;
    • ii) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide; and
    • iii) an organic medium; and
  • (c) firing the semiconductor substrate, one or more insulating films, and thick-film paste, forming an electrode in contact with the one or more insulating layers and in electrical contact with the semiconductor substrate.


Such articles may be useful in the manufacture of photovoltaic devices. In one embodiment, the article is a semiconductor device comprising an electrode formed from the thick-film paste composition. In one embodiment, the electrode is a front-side electrode on a silicon solar cell. In one embodiment, the article further includes a back electrode.


EXAMPLES

Illustrative preparations and evaluations of thick-film paste compositions are described below.


Example I
Lead-Tellurium-Boron-Oxide Preparation

Lead-Tellurium-Boron-Oxide Preparation of Glasses 36-54, and 76 of Table 1 and the Lasses of Table 3


The lead-tellurium-boron-oxide (Pb—Te—B—O) compositions, glasses numbered 36-54, and 76 of Table 1 and glasses numbered 56-75 of Table 3 were prepared by mixing and blending Pb3O4, TeO2, and B2O3 powders, and optionally, as shown in Table 1, Li2O, Bi2O3, TiO2, Al2O3 PbF2, SiO2, BiF3, SnO2, ZnO, V2O5, Na2O, CuO, ZrO2, CeO2, and/or Ag2O. The blended powder batch materials were loaded into a platinum alloy crucible and then inserted into a furnace at 900-1000° C. using an air- or O2-containing atmosphere. The duration of the heat treatment was 20 minutes following the attainment of a full solution of the constituents. The resulting low viscosity liquid resulting from the fusion of the constituents was then quenched by metal roller. The quenched glass was then milled, and screened to provide a powder with a D50 of 0.1 to 3.0 microns.









TABLE 1







Glass frit compositions in weight percent









Weight %

























Glass #
PbO
TeO2
PbF2
SiO2
Bi2O3
BiF3
Li2O
SnO2
Ag2O
ZnO
V2O5
Al2O3
B2O3
Na2O
TiO2
CuO
ZrO2
CeO2




























1
43.35
46.50


6.86

0.44





0.51

2.35





2
43.36
46.51


7.07

0.45




1.55
1.06







3
43.72
46.89


6.91

0.44




1.51
0.52







4
29.24
47.14
16.15

6.56

0.42





0.49







5
43.98
47.18


6.75

0.43





0.50

1.16





6
44.27
47.49


6.79

0.43





1.01







7
44.47
47.74


6.83

0.45





0.50







8
45.89
49.22


3.43

0.44





1.02







9
46.18
49.54


3.35

0.43





0.50







10
47.54
50.99




0.44





1.03







11
47.76
51.18










1.06







12
47.14
50.57










2.28







13
46.09
49.44










4.47







14
51.43
36.78



8.19
0.47





3.13







15
54.20
26.83



14.91






4.07







16
55.22
27.34


13.30







4.14







17
52.19
42.66




0.50





4.66







18
51.93
42.44




1.00





4.63







19
46.38
52.12




0.46





1.04







20
51.91
42.42










4.63
1.04






21
51.32
41.95










4.58
2.15






22
46.87
43.09


6.99

0.47




1.53
1.05







23
45.90
42.20



9.38
0.59




0.89
1.04







24
40.83
50.56
6.44



0.52




0.61
1.04







25
40.47
50.13
6.39



0.52





1.04



1.45



26
47.28
49.27

0.40


0.45




0.31
1.05

0.48

0.75



27
41.07
48.93
6.56
0.41


0.45




0.31
1.04

0.48

0.75



28
47.50
48.51




0.46





1.06


2.47




29
46.89
50.76




0.47




0.31
1.05

0.52





30
40.71
50.38
6.59



0.46




0.30
1.04

0.51





31
83.50
4.98

7.87


0.47




0.32
1.09

1.00

0.77



32
46.89
50.32




0.46




1.25
1.07







33
47.17
50.61









1.19
1.02







34
56.56
40.44




0.45




1.52
1.04







35
56.89
40.67









1.45
0.99







36
48.16
51.65










0.19







37
42.28
55.43




0.91





0.21

0.93


0.22


38
53.21
45.88




0.44





0.48







39
44.51
47.74


6.83

0.44





0.48







40
44.31
50.17




0.46

3.57



0.52

0.96





41
42.92
54.44




0.78





0.54

1.31





42
37.19
57.62




1.97



0.63

0.56




2.03


43
45.58
51.19




1.18





0.60

1.05


0.40


44
50.38
48.11




0.91





0.60







45
48.99
48.74




0.93





0.61

0.74





46
45.73
50.02




0.42





0.84
0.43
0.48


2.07


47
45.26
49.53




0.55


2.25


0.86

0.49


1.06


48
64.85
25.88

7.88


0.10




0.10
0.93
0.05


0.21



49
47.25
49.69




0.84





0.98

1.24





50
45.77
51.64




0.80





1.09

0.71





51
47.24
50.67




1.00





1.09







52
44.08
39.96
12.96



0.52




0.50
1.21

0.78





53
40.44
54.68




1.23





1.38




2.27


54
66.47
11.13

10.98


0.16
1.05
7.66


0.20
1.84
0.08


0.42



55
60.36
32.38

4.06


0.47




1.62
1.11







76
47.80
51.27




0.45





0.49





Note:


the compositions in the table are displayed as weight percent, based on the weight of the total glass composition.







Lead-Tellurium-Boron-Oxide Preparation of Glasses 1-35 & 55 of Table 1 and Glasses 77-90 of Table 2


Mixtures of TeO2 powder (99+% purity), PbO or Pb3O4 powder, and B2O3 powder (ACS reagent grade, 99+% purity) and optionally Bi2O3, Li2O, Li2CO3, Al2O3, TiO2, CuO, ZrO2, Na2O, Na2CO3, BiF3, SiO2, and/or PbF2 were tumbled in a suitable container for 15 to 30 minutes to mix the starting powders. The starting powder mixture was placed in a platinum crucible and heated in air at a heating rate of 10° C./min to 900° C. and then held at 900° C. for one hour to melt the mixture. The melt was quenched from 900° C. by removing the platinum crucible from the furnace and pouring the melt onto a stainless steel platen. The resulting material was ground in a mortar and pestle to less than 100 mesh. The ground material was then ball-milled in a polyethylene container with zirconia balls and isopropyl alcohol until the D50 was 0.5-0.7 microns. The ball-milled material was then separated from the milling balls, dried, and run through a 230 mesh screen to provide the powders used in the thick-film paste preparations.









TABLE 2







Glass frit compositions in weight percent










TeO2/PbO
Weight %

















Glass #
(mole ratio)
PbO
TeO2
PbF2
Bi2O3
Li2O
Al2O3
B2O3
TiO2
CuO





77
2.54
34.80
63.21


0.70

0.54
0.75



78
2.44
35.49
61.92


0.71

1.11
0.76



79
2.34
36.21
60.59


0.73

1.69
0.78



80
1.95
40.95
57.10


0.69

0.53
0.73



81
1.87
41.74
55.72


0.70

1.09
0.75



82
1.78
42.57
54.29


0.71

1.66
0.76



83
1.53
46.85
51.23


0.67

0.52
0.72



84
1.46
47.76
49.76


0.69

1.07
0.73



85
1.39
48.68
48.24


0.70

1.63
0.75



86
1.51
46.84
50.71


0.45

1.04

0.97


87
1.59
45.97
52.13


0.44

0.52

0.95


88
1.49
47.06
49.99


0.45

1.05
0.48
0.97


89
1.50
43.36
46.51

7.07
0.45
1.55
1.06




90
1.50
43.72
46.89

6.91
0.44
1.51
0.52





Note:


the compositions in the table are displayed as weight percent, based on the weight of the total glass composition. The TeO2/PbO ratios are a molar ratio between only TeO2 and PbO of the composition













TABLE 3







Glass frit compositions in weight percent















Frit ID
SiO2
PbO
B2O3
Li2O
TiO2
Ag2O
SnO2
TeO2


















56
8.40
60.90

1.47
0.93

0.70
27.60


57

46.04

0.40
4.18


49.38


58

46.78

0.83
2.22


50.17


59

47.43

0.85
0.84


50.88


60

33.77

2.39
2.13


61.71


61

45.35

0.48
0.43


53.74


62

36.19

1.99
1.77


60.05


63

37.35

2.39
2.13


58.13


64

36.19

1.82
3.06


58.94


65

40.81

2.39
2.13


54.67


66

44.28

0.16
0.42
12.29

42.84


67

40.81

0.59
1.57
9.08

47.95


68

40.81

1.90
1.12


56.16


69

45.77
1.09
0.80
0.71


51.64


70

41.20

0.34
2.30


56.16


71

44.31
0.52
0.46
0.96
3.57

50.17


72

42.92
0.54
0.78
1.31


54.44


73

42.22

0.91
1.53


55.35


74

48.25





51.75


75

48.04

0.42



51.54





Note:


the compositions in the table are displayed as weight percent, based on the weight of the total glass composition.






Example II
Paste Preparation

Paste Preparation for Tables 5, 6, and 7


Paste preparations, in general, were prepared using the following procedure: The appropriate amount of solvent, medium, and surfactant from Table 4 were weighed and mixed in a mixing can for 15 minutes.












TABLE 4







Component
Wt. %









2,2,4-trimethyl-1,3-pentanediol monoisobutyrate
5.57



Ethyl Cellulose (50-52% ethoxyl)
0.14



Ethyl Cellulose (48-50% ethoxyl)
0.04



N-tallow-1,3-diaminopropane dioleate
1.00



Hydrogenated castor oil
0.50



Pentaerythritol tetraester of perhydroabietic acid
1.25



Dimethyl adipate
3.15



Dimethyl glutarate
0.35










Since Ag is the major part of the solids, it was added incrementally to ensure better wetting. When well mixed, the paste was repeatedly passed through a 3-roll mill at progressively increasing pressures from 0 to 250 psi. The gap of the rolls was set to 2 mils. The paste viscosity was measured using a Brookfield viscometer and appropriate amounts of solvent and resin were added to adjust the paste viscosity toward a target of between 230 and 280 P·sec. The degree of dispersion was measured by fineness of grind (FOG). A typical FOG value for a paste is less than 20 microns for the fourth longest, continuous scratch and less than 10 microns for the point at which 50% of the paste is scratched.


To make the final pastes used to generate the data in Tables 5, 6, and 7, 2 wt % of a frit or frits from Table 1 was mixed into a portion of the Ag paste and dispersed by shear between rotating glass plates known to one skilled in the art as a muller.


The paste examples of Tables 5, 6, and 7 were made using the procedure described above for making the paste compositions listed in the table according to the following details. Tested pastes contained 85 to 88% silver powder. The examples used a singular spherical silver with a D50=2.0 μm.


The paste examples of Table 11 were made using by mixing one or two different frit powders as described in the table to appropriate amount of medium of Table 4 then roll milled with a 2 mil gap at progressively increasing pressure from 0 to over 250 psi to make a precursor paste. Then Ag powder was added incrementally and mixed into the precursor paste to ensure proper wetting of the Ag powder. The Ag powder was 85 to 88% of the paste composition. The paste with all the Ag powder added was again roll milled with a 2 mil gap at progressive pressure from 0 to 75 psi. Resin and solvent were added to adjust to the viscosity between 230 and 280 Pa·sec. This example used a singular spherical silver powder with a D50=2.0 um.


Thick-Film Paste Preparation of Examples in Tables 8, 9, and 10


The organic components (˜4.6 g), as described in Table 4, were put into a Thinky mixing jar (Thinky USA, Inc.) and Thinky-mixed at 2000 RPM for 2 to 4 minutes until well blended. The inorganic components (Pb—Te—B—O powders and silver conductive powders) were tumble-mixed in a glass jar for 15 min. The total weight of the inorganic components was 44 g, of which 42.5-43.5 g was silver powder and 0.5-1.5 g was the mixture of PbO, TeO2, and B2O3 powders. One third of inorganic components were then added to the Thinky jar containing the organic components and mixed for 1 minute at 2000 RPM. This was repeated until all of the inorganic components were added and mixed. The paste was cooled and the viscosity was adjusted to between 200 and 500 Pa·s by adding solvent and then mixing for 1 minute at 2000 RPM. This step was repeated until the desired viscosity was achieved. The paste was then roll-milled at a 1 mil gap for 3 passes at 0 psi and 3 passes at 75 psi. The degree of dispersion was measured by fineness of grind (FOG). The FOG value is typically equal to or less than 20/10 for thick-film pastes. The viscosity of the paste was adjusted after 24 hrs at room temperature to between 200 and 320 Pa·s. Viscosity was measured after 3 minutes at 10 RPM in a viscometer. The viscosity of each paste was measured on a Brookfield viscometer (Brookfield, Inc., Middleboro, Mass.) with a #14 spindle and a #6 cup.


Example III
Solar Cell Preparation

Solar Cell Preparation of the Examples in Tables 5, 6, and 7


For the examples in Tables 5, 6, and 7, multi-crystalline silicon wafers with a 65Ω/□ phosphorous-doped emitter layer were obtained from Gintech Energy Corporation (Taiwan) or DeutscheCell (Germany). 6 inch (152 mm) square wafers were cut down to 1.1 inch (28 mm) squares with a dicing saw.


The solar cells used were textured by isotropic acid etching and had an anti-reflection coating (ARC) of SiNx:H. Efficiency and fill factor were measured for each sample. Each sample was made by screen-printing using an ETP model L555 printer set with a squeegee speed of 250 mm/sec. The screen used had a pattern of 11 finger lines with a 100 μm opening and 1 bus bar with a 1.5 mm opening on a 20 μm emulsion in a screen with 325 mesh and 23 μm wires. A commercially available AI paste, DuPont PV381, was printed on the non-illuminated (back) side of the device.


The device with the printed patterns on both sides was then dried for 10 minutes in a drying oven with a 250° C. peak temperature. The substrates were then fired sun-side up with a CF7214 Despatch 6-zone IR furnace using a 560 cm/min belt speed and the first five zones were set to 550-600-650-700-800 and the sixth zone was set to the temperatures indicated in Tables 5, 6, and 7. The actual temperature of the part was measured during processing. The estimated peak temperature of each part was 770-780° C. and each part was above 650° C. for a total time of 4 seconds. The fully processed samples were then tested for PV performance using a calibrated ST-1000 tester.


Efficiency and fill factor were measured for each sample, as shown in Tables 5, 6, and 7. For each paste, the mean and median values of the efficiency and fill factor for 6 to 10 samples are shown.


Solar Cell Preparation of the Examples of Tables 8, 9, and 10


Solar cells for testing the performance of the thick-film paste were made from 200 micron DeutscheCell multi-crystalline silicon wafers with a 65 ohm/sq. phosphorous-doped emitter layer which had an acid-etched textured surface and 70 nm thick PECVD SiNx anti-reflective coating. The wafers were cut into 28 mm×28 mm wafers using a diamond wafering saw. Wafers were screen-printed after being cut down using an AMI-Presco MSP-485 screen printer to provide a bus bar, eleven conductor lines at a 0.254 cm pitch, and a full ground-plane, screen-printed aluminum back-side conductor. After printing and drying, cells were fired in a BTU International rapid thermal processing belt furnace. The firing temperatures shown in Tables 8, 9, and 10 were the furnace setpoint temperatures of the final, peak zone, which were approximately 125° C. greater than the actual wafer temperature. The fired conductor line median line width was 120 microns and mean line height was 15 microns. The median line resistivity was 3.0×10−6 ohm·cm. Performance of the 28 mm×28 mm cells is expected to be impacted by edge effects that reduce the overall solar cell fill factor (FF) by ˜5%.


Solar Cell Preparation of the Examples of Table 11


Solar cells for testing the performance of the thick-film pastes of Table 11 were made from full 6″×6″ (152 mm×152 mm) 65Ω/□ mono-crystalline cells that were alkaline textured supplied by Gintech Energy Corporation, Taiwan. A 65 line pattern of the pastes described in Table 6 were applied by screen printing to the front side of the cells using a screen with 80 μm openings in a 325 mesh, 23 μm wire diameter screen with a 25 μm emulsion. An aluminum back-side paste and a commercially available tabbing paste, DuPont PV505, were applied to the back side of the cells. Mean and median efficiency and fill factor were measured using I-V techniques and are shown in Table 11.


Example IV
Solar Cell Performance: Efficiency and Fill Factor

Solar Cell Performance: Efficiency and Fill Factor for Tables 5, 6, 7, and 11


The solar cells built according to the method described herein were tested for conversion efficiency. An exemplary method of testing efficiency is provided below.


In an embodiment, the solar cells built according to the method described herein were placed in a commercial LV tester for measuring efficiencies (Telecom STV, model ST-1000). The Xe arc lamp in the I-V tester simulated the sunlight with a known intensity, AM 1.5, and irradiated the front surface of the cell. The tester used a multi-point contact method to measure current (I) and voltage (V) at approximately 400 load resistance settings to determine the cell's LV curve. Both fill factor (FF) and efficiency (Eff) were calculated from the I-V curve.


Solar Cell Performance: Efficiency and Fill Factor for Tables 8, 9, and 10


Solar cell performance of the examples of Tables 8, 9, and 10 was measured using a ST-1000, Telecom STV Co. IV tester at 25° C.±1.0° C. The Xe arc lamp in the IV tester simulated sunlight with a known intensity, and irradiated the front surface of the cell. The tester used a four-contact method to measure current (I) and voltage (V) at approximately 400 load resistance settings to determine the cell's I-V curve. Solar cell efficiency (Eff), fill factor (FF), and series resistance (Rs) (data not shown for Rs) were calculated from the I-V curve. Ideality factor was determined using the Suns-VOC technique (Suns-VOC data not shown).


Median and mean values for efficiency and fill factor for these examples are shown in Tables 8, 9, and 10.









TABLE 5







Eff % and FF results of paste using select glass frits of Table 1










Efficiency Eff %
Fill Factor FF















Frit level
905 C.
920 C.
940-945 C.
905 C.
920 C.
940-945 C.





















Example #
Glass #
(wt %)
Mean
Median
Mean
Median
Mean
Median
Mean
Median
Mean
Median
Mean
Median





1
41
2
13.96
14.03


15.04
15.07
71.5
71.7


75.0
75.3


2
38
2
14.82
14.89


15.40
15.41
74.0
74.3


76.1
76.4


3
52
2
12.97
12.84


14.44
14.52
64.2
63.1


70.9
70.9


4
40
2
14.47
14.52


15.40
15.41
72.2
72.3


76.0
75.9


5
39
2


14.41
14.71
14.52
14.59


74.3
74.8
76.3
76.3


6
54
2


11.80
11.81
10.95
11.01


59.4
59.3
56.6
57.1


7
48
2
12.68
12.83


14.49
14.79
64.9
65.6


73.5
74.1


8
51
2
15.08
15.08


15.25
15.18
76.3
76.4


76.7
77.1


9
50
2
14.87
14.92


15.17
15.13
75.4
75.6


76.6
76.7
















TABLE 6







Eff % results of paste using select glass frits









Efficiency (Eff %)











Frit level
905 C.
945 C.













Example #
Glass #
(wt %)
Mean
Median
Mean
Median





40
45
2
13.00
13.76
14.96
14.89


41
76
2
14.38
14.33
15.17
15.07


42
49
2
12.60
12.71
15.12
15.27


43
37
2
13.15
13.25
15.53
15.53


44
43
2
13.65
13.68
15.19
15.22
















TABLE 7







Fill Factor results of paste using select glass frits









Fill Factor (FF)











Frit level
905 C.
945 C.













Example #
Glass #
(wt %)
Mean
Median
Mean
Median





40
76
2
71.93
72.28
75.78
75.93


41
43
2
68.10
69.63
76.39
76.47


42
45
2
66.10
69.77
75.70
75.93


43
49
2
63.83
66.23
75.86
76.38


44
37
2
66.01
65.93
76.57
76.80
















TABLE 8





Eff % and FF results of paste using select glass frits of Table 1

















Efficiency Eff %














Frit level
910 C.
920 C.
930 C.
940 C.
950 C.



















Example #
Glass #
(wt %)
Mean
Median
Mean
Median
Mean
Median
Mean
Median
Mean
Median





10
11
2


13.45
15.13
15.05
15.06
15.41
15.42
15.25
15.25


11
13
2


8.48
8.75
9.91
10.11
9.41
9.26
8.57
8.66


12
14
2
14.61
14.54
12.98
13.79
14.14
14.09
14.23
14.36




13
16
2.5
10.17
10.28
10.73
10.81
12.45
12.67
10.93
12.06
11.62
11.11


14
19
2
15.00
14.93
15.16
15.26
15.12
15.20
15.59
15.68
15.28
15.10


15
23
2
15.18
15.28
15.16
15.20
14.98
15.23
15.07
15.21




16
28
2.5
14.81
14.73
14.77
14.73
14.92
15.05
15.09
15.14
13.93
13.68


17
29
2.5
14.82
14.75
15.02
14.94
14.69
14.93
14.19
14.55




18
30
2
14.01
14.27
13.92
13.89
13.71
13.68
14.10
13.97




19
10
2
15.10
15.10
15.50
15.40
15.00
15.10
15.30
15.40




20
7
2
15.19
15.30
15.31
15.30
15.30
15.20
15.50
15.50
15.50
15.40


21
7
2
15.30
15.50
15.60
15.70
15.40
15.40
15.70
15.70




22
6
2
15.30
15.50
15.80
15.80
15.60
15.60
15.50
15.50




23
5
2
15.40
15.50
15.60
15.70
15.80
15.80
15.60
15.70




24
1
2
15.30
15.30
15.50
15.40
15.30
15.40
15.40
15.50












Fill Factor FF














Frit level
910 C.
920 C.
930 C.
940 C.
950 C.



















Example #
Glass #
(wt %)
Mean
Median
Mean
Median
Mean
Median
Mean
Median
Mean
Median





10
11
2


69.82
77.00
77.92
78.40
78.84
78.80
78.56
78.60


11
13
2


46.34
47.70
51.26
52.70
49.28
49.70
45.16
45.90


12
14
2
76.28
76.20
72.40
73.50
73.70
75.20
74.84
75.00




13
16
2.5
52.90
53.40
62.30
58.60
64.10
64.60
60.22
61.70
60.02
59.80


14
19
2
77.84
78.00
79.12
79.10
79.24
79.10
79.50
79.60
79.50
79.50


15
23
2
78.22
78.00
78.08
77.90
76.68
77.30
77.52
78.60




16
28
2.5
77.84
77.90
77.82
77.70
78.04
78.20
77.90
78.60
74.64
74.60


17
29
2.5
76.64
76.70
77.80
77.60
75.24
76.20
72.50
74.30




18
30
2
71.40
71.60
71.38
72.60
70.12
70.50
71.92
71.30




19
10
2
77.56
77.00
79.40
79.40
78.80
79.30
79.30
79.30




20
7
2
79.00
79.20
78.90
78.60
78.70
78.70
79.00
79.00
79.20
79.30


21
7
2
78.70
78.40
79.50
79.50
78.10
78.20
79.20
79.10




22
6
2
79.30
79.20
79.20
79.40
79.20
79.20
78.80
79.00




23
5
2
78.50
78.60
78.50
78.50
79.00
79.00
79.00
79.00




24
1
2
78.50
78.50
79.00
78.90
78.80
78.60
79.00
79.00
















TABLE 9







Eff % results of paste using select glass frits














900 C.
910 C.
915 C.
920 C.
930 C.






















Glass
Eff.

Eff.

Eff.

Eff.

Eff.

940 C.
945 C.























Example
Glass
amount
(%)
Eff. (%)
(%)
Eff. (%)
(%)
Eff. (%)
(%)
Eff. (%)
(%)
Eff. (%)
Eff. (%)
Eff. (%)
Eff. (%)
Eff. (%)


Number
#
(wt %)
mean
median
mean
median
mean
median
mean
median
mean
median
mean
median
mean
median


























29
89
2
14.93
14.97
15.14
15.24


15.04
15.02
15.00
15.07
15.31
15.31




30
90
2
14.85
14.87
15.00
15.16


15.01
14.99
15.24
15.26
15.12
15.14




31
77
1.93




16.81
16.76


16.99
16.91


17.39
17.46


32
78
1.93




15.77
15.73


16.46
16.37


16.55
16.56


33
79
1.93




14.99
15.51


16.09
16.05


16.68
16.69


34
80
1.93




17.11
17.19


17.48
17.58


17.59
17.57


35
81
1.93




15.91
16.10


16.55
16.60


16.26
16.34


36
82
1.93




15.68
16.10


15.96
15.83


16.34
16.45


37
83
1.93




17.38
17.40


17.59
17.60


17.69
17.75


38
84
1.93




17.23
17.25


17.32
17.35


17.38
17.41


39
85
1.93




16.79
16.76


17.01
17.07


16.87
16.89
















TABLE 10







Fill factor results of paste using select glass frits
















Glass
900 C.
910 C.
915 C.
920 C.
930 C.
940 C.
945 C.























Example

amount
FF
FF
FF
FF
FF
FF
FF
FF
FF
FF
FF
FF
FF
FF


Number
Glass #
(wt %)
mean
median
mean
median
mean
median
mean
median
mean
median
mean
median
mean
median


























29
89
2
78.62
77.80
78.46
78.50


77.00
77.10
77.38
77.20
78.38
78.40




30
90
2
78.54
78.60
78.74
78.70


78.70
78.60
78.70
78.60
78.82
79.00




31
77
1.93




71.50
71.56


72.41
72.05


73.71
73.81


32
78
1.93




67.22
67.14


70.12
69.88


70.70
70.60


33
79
1.93




64.08
65.98


68.72
68.76


70.84
70.95


34
80
1.93




72.58
72.70


74.02
74.26


74.66
74.66


35
81
1.93




68.01
68.58


70.39
70.57


69.56
69.75


36
82
1.93




66.91
68.53


67.90
67.31


69.76
70.14


37
83
1.93




73.93
73.99


74.40
74.44


75.22
75.22


38
84
1.93




73.33
73.64


73.66
73.85


73.94
73.98


39
85
1.93




71.63
71.50


72.38
72.45


72.15
72.20
















TABLE 11







Eff % and FF results of paste containing a mixture of the glass frits from Table 1 and Table 3













Glass A

Glass B
Efficiency Eff %
Fill Factor FF





















Frit level

Frit level
890 C.
905 C.
920 C.
935 C.
890 C.
905 C.
920 C.
935 C.


Example #
Glass A #
(wt %)
Glass B #
(wt %)
Mean
Mean
Mean
Mean
Mean
Mean
Mean
Mean






















25
60
2


18.00
18.06
18.07
17.93
78.4
78.6
78.7
78.6


26
39
2


18.08
18.07
18.13
18.03
78.8
78.9
79.0
79.0


27
39
1.5
60
0.5
18.03
18.07
18.09
17.98
78.7
78.8
78.9
78.7


28
39
1
60
1
17.93
18.02
18.01
17.96
78.3
78.6
78.8
78.7









Comparative Example I: Bismuth-Tellurium-Boron-Oxide

Preparation of Bismuth-Tellurium-Boron-Oxide


A bismuth-tellurium-boron-oxide (Bi—Te—B—O) containing composition as shown in Table 12 was prepared using boron oxide (B2O3), zinc oxide (ZnO), titanium oxide (TiO2), bismuth oxide (B2O3), tellurium oxide (TeO2), lithium carbonate (LiCO3), and lithium phosphate (LiPO4) and by the procedure described above in Example I: Lead-tellurium-boron-oxide preparation of glasses 36-54, and 76 of Table 1, and the glasses of Table 3.









TABLE 12







Bismuth-tellurium-boron-oxide composition in


weight percent of the oxides









Glass A



(wt %)














B2O3
2.09



ZnO
0.98



TiO2
0.48



Bi2O3
26.64



TeO2
67.22



P2O5
0.43



Li2O
2.16







Note:



the composition in the table are displayed as weight percent, based on the weight of the total glass composition







Paste Preparation


Pastes using glass A were made by the following procedure. A paste was made by mixing the appropriate amount of organic vehicle (Table 4) and Ag powder. The Ag paste was passed through a 3-roll mill at progressively increasing pressures from 0 to 75 psi. The Ag paste viscosity was measured using a Brookfield viscometer and appropriate amounts of solvent and resin were added to adjust the paste viscosity toward a target of between 230 and 280 Pa·sec. Another paste was made by mixing the appropriate amount of organic vehicle (Table 4) and glass powder A. The frit paste was passed through a 3-roll mill at progressively increasing pressures from 0 to 250 psi. The degree of dispersion of each paste was measured by fineness of grind (FOG). A typical FOG value for a paste is less than 20 microns for the fourth longest, continuous scratch and less than 10 microns for the point at which 50% of the paste is scratched.


Ag and frit pastes were mixed with a mixed together using a planetary centrifugal mixer (Thinky Corporation, Tokyo, Japan) to make the final paste recipes displayed in Table 13.


Solar Cell Preparation and Efficiency and Fill Factor Measurement


Pastes were applied to 1.1″×1.1″ dicing-saw-cut multi-crystalline silicon solar cells with a phosphorous-doped emitter on a p-type base. The pastes were applied to a DeutscheCell (DeutscheCell, Germany) multi-crystalline wafer with a 62Ω/□ emitter. The solar cells used were textured by isotropic acid etching and had an anti-reflection coating (ARC) of SiNx:H. Efficiency and fill factor, as shown in Table 13, were measured for each sample. Each sample was made by screen-printing using a ETP model L555 printer set with a squeegee speed of 200 mm/sec. The screen used had a pattern of 11 finger lines with a 100 μm opening and 1 bus bar with a 1.5 mm opening on a 20 μm emulsion in a screen with 325 mesh and 23 μm wires. A commercially available AI paste, DuPont PV381, was printed on the non-illuminated (back) side of the device.


The device with the printed patterns on both sides was then dried for 10 minutes in a drying oven with a 250° C. peak temperature. The substrates were then fired sun-side up with a CF7214 Despatch 6 zone IR furnace using a 560 cm/min belt speed and 500-550-610-700-800-HZ6 temperature set points, where HZ6=885, 900 & 915° C. The actual temperature of the part was measured during processing. The estimated peak temperature of each part was 745-775° C. and each part was above 650° C. for a total time of 4 seconds. The fully processed samples were then tested for PV performance using a calibrated ST-1000 tester.


Efficiency and fill factor, shown in Table 13, were measured for each sample. For each paste, the mean and median values of the efficiency and fill factor for 6 samples are shown.









TABLE 13







Comparative Example: Recipe and electrical performance for pastes containing the bismuth-tellurium-boron-oxide


glass A of Table 12










Efficiency (Eff %)
Fill Factor (FF)
















Ag
Frit
900
915
930
900
915
930





















Glass #
wt %
wt %
Mean
Median
Mean
Median
Mean
Median
Mean
Median
Mean
Median
Mean
Median
























A
88.6
2.1
10.04
10.13
12.46
13.01
12.61
12.98
52.8
53.5
65.1
67.3
64.2
65.6


A
86.3
4.2
1.14
0.83
1.45
1.42
2.93
2.79
28.7
29.7
29.4
29.5
30.7
30.1








Claims
  • 1. A thick-film paste composition comprising: a) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;b) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide, wherein the lead-tellurium-boron-oxide comprises 25 to 60 wt % PbO, greater than 25 to 70 wt % TeO2, 0.1 to less than 5 wt % B2O3, and 0 to 15 wt. % V2O5; andc) an organic medium.
  • 2. The thick-film paste of claim 1, wherein the electrically conductive metal comprises silver.
  • 3. The thick-film paste of claim 1, wherein the mole ratio of lead to tellurium of the lead-tellurium-boron-oxide is between 5/95 and 95/5.
  • 4. The thick-film paste of claim 1, wherein the lead-tellurium-boron-oxide comprises 0-20.0 wt % of components selected from the group of PbF2, SiO2, Bi2O3, BiF3, LiO2, SnO2, AgO2, ZnO, Al2O3, Na2O, TiO2, CuO, ZrO2, and CeO2.
  • 5. The thick-film paste of claim 4, wherein the lead-tellurium-boron-oxide further comprises: 0.1-5 wt % TiO2.
  • 6. The thick-film paste of claim 1, wherein the organic medium further comprises one or more additives selected from the group consisting of solvents, stabilizers, surfactants, and thickeners.
  • 7. The thick-film paste of claim 1, wherein the electrically conductive metal is 90-95 wt % of the solids.
  • 8. The thick-film paste of claim 1, wherein the lead-tellurium-boron-oxide is at least partially crystalline.
  • 9. The thick-film paste of claim 4, further comprising an additive selected from the group consisting of: PbF2, SiO2, Na2O, K2O, Rb2O, Cs2O, Al2O3, MgO, CaO, SrO, BaO, V2O5, ZrO2, MoO3, Mn2O3, Ag2O, ZnO, Ga2O3, GeO2, In2O3, SnO2, Sb2O3, Bi2O3, BiF3, P2O5, CuO, NiO, Cr2O3, Fe2O3, CoO, Co2O3, and CeO2.
  • 10. The thick film paste of claim 1, wherein the lead-tellurium-boron-oxide further comprises oxides of one or more elements selected from the group consisting of Si, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, V, Zr, Mo, Mn, Zn, B, P, Se, Sn, Ga, Ge, In, Sb, Bi, Ce, Cu, F, Ni, Cr, Fe, Co, and Ag.
  • 11. A process comprising: (a) providing a semiconductor substrate comprising one or more insulating films deposited onto at least one surface of the semiconductor substrate;(b) applying a thick-film paste composition onto at least a portion of the insulating film to form a layered structure, wherein the thick-film paste composition comprises: i) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;ii) 0.5 to 15% by weight based on solids of a lead-tellurium-boron-oxide, wherein the lead-tellurium-boron-oxide comprises 25 to 60 wt % PbO, greater than 25 to 70 wt % TeO2, 0.1 to 5 wt % B2O3, and 0 to 15 wt. % V2O5; andiii) an organic medium; and(c) firing the semiconductor substrate, insulating film, and thick-film paste, to form an electrode in contact with the insulating layer and in electrical contact with the semiconductor substrate.
  • 12. The process of claim 11, wherein the thick-film paste composition is applied pattern-wise onto the insulating film.
  • 13. The process of claim 11, wherein the firing is carried out in air or an oxygen-containing atmosphere.
  • 14. The process of claim 11, wherein the thick-film paste composition further comprises: 0.5 to 15% by weight based on solids of a lead-tellurium-lithium-titanium-oxide.
  • 15. An article comprising: (a) a semiconductor substrate;(b) an insulating layer on the semiconductor substrate; and(c) an electrode in contact with the insulating layer and in electrical contact with the semiconductor substrate, the electrode comprising an electrically conductive metal and lead-tellurium-boron-oxide, wherein the lead-tellurium-boron-oxide comprises 25 to 60 wt % PbO, greater than 25 to 70 wt % TeO2, 0.1 to less than 5 wt, and 0 to 15 wt. % V2O5.
  • 16. The article of claim 15, wherein the electrode further comprises lithium and titanium.
  • 17. The article of claim 15, wherein the article is a semiconductor device.
  • 18. The article of claim 17, wherein the semiconductor device is a solar cell.
  • 19. The article of claim 16, wherein the article is a semiconductor device.
  • 20. The article of claim 19, wherein the semiconductor device is a solar cell.
  • 21. The thick-film paste composition of claim 1, wherein the lead-tellurium-boron-oxide comprises 0.25 to less than 5 wt % B2O3.
  • 22. The thick-film paste composition of claim 1, wherein the lead-tellurium-boron-oxide comprises greater than 25 to 60 wt % TeO2.
  • 23. A thick-film paste composition comprising: a) 85 to 99.5% by weight of an electrically conductive metal or derivative thereof, based on total solids in the composition;b) 0.5 to 7% by weight based on solids of a lead-tellurium-boron-oxide, wherein the lead-tellurium-boron-oxide comprises 25 to 50 wt % PbO, 40 to 70 wt % TeO2, 0 to 10 wt % V2O5, and 0.1 to 15 wt % B2O3; andc) an organic medium.
  • 24. The thick-film paste composition of claim 23, wherein the lead-tellurium-boron-oxide comprises 40 to 60 wt % TeO2.
  • 25. The thick thick-film paste composition of claim 23, comprising 0.5 to 3% by weight based on solids of the lead-tellurium-boron-oxide.
  • 26. The thick-film paste of claim 23, wherein the lead-tellurium-boron-oxide comprises 0-20.0 wt % of components selected from the group of PbF2, SiO2, Bi2O3, BiF3, LiO2, SnO2, AgO2, ZnO, Al2O3, Na2O, TiO2, CuO, ZrO2, and CeO2.
  • 27. The thick-film paste of claim 1, wherein the lead-tellurium-boron-oxide comprises 0.1 to 4.6 wt % B2O3.
  • 28. The thick-film paste of claim 1, wherein the lead-tellurium-boron-oxide comprises 0 to 10 wt. % V2O5.
  • 29. The thick-film paste composition of claim 1, comprising 0.5 to 7% by weight based on solids of the lead-tellurium-boron-oxide.
  • 30. The thick-film paste composition of claim 1, comprising 0.5 to 3% by weight based on solids of the lead-tellurium-boron-oxide.
  • 31. The thick-film paste composition of claim 23, comprising 0.5 to 3% by weight based on solids of the lead-tellurium-boron-oxide.
US Referenced Citations (72)
Number Name Date Kind
4293451 Ross Oct 1981 A
4643913 Okunaka et al. Feb 1987 A
4945071 Friesen et al. Jul 1990 A
5013697 Akhtar May 1991 A
5066621 Akhtar Nov 1991 A
5118362 St. Angelo et al. Jun 1992 A
5188990 Dumesnil et al. Feb 1993 A
5240884 Herrington et al. Aug 1993 A
5245492 Mizuno Sep 1993 A
5334558 Dietz et al. Aug 1994 A
5336644 Akhtar et al. Aug 1994 A
5594406 Koyama Jan 1997 A
5616173 Okamoto et al. Apr 1997 A
5663109 Dietz et al. Sep 1997 A
6204443 Kiso et al. Mar 2001 B1
7494607 Wang et al. Feb 2009 B2
7537713 Satou et al. May 2009 B2
7608206 Vernooy et al. Oct 2009 B1
7736546 Prunchak Jun 2010 B2
7871949 Lee et al. Jan 2011 B2
7910393 Kim et al. Mar 2011 B2
7951311 Vernooy et al. May 2011 B2
8313673 Wang et al. Nov 2012 B2
8383017 Carroll et al. Feb 2013 B2
8470723 Naito et al. Jun 2013 B2
8497420 Carroll et al. Jul 2013 B2
8512463 Hang Aug 2013 B2
8546281 Lee et al. Oct 2013 B2
8696948 Hang et al. Apr 2014 B2
8771554 Rajendran Jul 2014 B2
8889041 Sridharan et al. Nov 2014 B2
8889979 Carroll et al. Nov 2014 B2
8889980 Carroll et al. Nov 2014 B2
8895843 Carroll et al. Nov 2014 B2
9722100 Carroll et al. Aug 2017 B2
20060102228 Sridharan et al. May 2006 A1
20060231800 Wang et al. Oct 2006 A1
20060231803 Wang et al. Oct 2006 A1
20060231804 Wang et al. Oct 2006 A1
20060272700 Young et al. Dec 2006 A1
20080223446 Wang et al. Sep 2008 A1
20080254597 Akiyama et al. Oct 2008 A1
20090095344 Machida et al. Apr 2009 A1
20090189126 Prunchak Jul 2009 A1
20090199897 Naito et al. Aug 2009 A1
20090255584 Carroll Oct 2009 A1
20090298283 Akimoto et al. Dec 2009 A1
20100135849 Gu et al. Jun 2010 A1
20100163101 Kumar et al. Jul 2010 A1
20100180934 Naito et al. Jul 2010 A1
20100275987 Sakamoto et al. Nov 2010 A1
20110094578 Akimoto et al. Apr 2011 A1
20110095240 Nakamura et al. Apr 2011 A1
20110192456 Hang et al. Aug 2011 A1
20110192457 Nakayama et al. Aug 2011 A1
20110232746 Carroll et al. Sep 2011 A1
20110232747 Mikeska et al. Sep 2011 A1
20110308595 Carroll et al. Dec 2011 A1
20110308596 Carroll et al. Dec 2011 A1
20110308597 Carroll et al. Dec 2011 A1
20110315937 Aoyagi et al. Dec 2011 A1
20120067415 Tachizono et al. Mar 2012 A1
20130049148 Hang et al. Feb 2013 A1
20130099177 Rajendran Apr 2013 A1
20130099178 Hang et al. Apr 2013 A1
20130186463 Wang et al. Jul 2013 A1
20130255767 Carroll et al. Oct 2013 A1
20130255768 Carroll et al. Oct 2013 A1
20130255769 Carroll et al. Oct 2013 A1
20130255770 Carroll et al. Oct 2013 A1
20130298982 Hang et al. Nov 2013 A1
20180301574 Torardi et al. Oct 2018 A1
Foreign Referenced Citations (64)
Number Date Country
1060280 Apr 1992 CN
1873836 Dec 2006 CN
101055896 Oct 2007 CN
101164934 Apr 2008 CN
101379620 Mar 2009 CN
102496404 Jun 2012 CN
104726085 Jun 2015 CN
107424662 Dec 2017 CN
108735334 Nov 2018 CN
800312258 Nov 2018 CN
109014180 Dec 2018 CN
0430206 Jun 1991 EP
0 463 826 Jan 1992 EP
0463826 Jan 1992 EP
0466295 Jan 1992 EP
0537886 Apr 1993 EP
0393416 Jun 1993 EP
1713091 Sep 2010 EP
59033869 Feb 1984 JP
62-036040 Feb 1987 JP
01-138150 May 1989 JP
02-293344 Apr 1990 JP
03-218943 Sep 1991 JP
04-224178 Aug 1992 JP
04-270140 Sep 1992 JP
05-105484 Apr 1993 JP
5-175254 Jul 1993 JP
08-097011 Apr 1996 JP
08-138438 May 1996 JP
09-092027 Apr 1997 JP
10-340621 Dec 1998 JP
2011118425 Apr 2001 JP
2001284754 Oct 2001 JP
2001-313400 Nov 2001 JP
2006-093433 Apr 2006 JP
2006-302890 Nov 2006 JP
2006-302891 Nov 2006 JP
2008-520094 Jun 2008 JP
2009-099781 May 2009 JP
2010-238955 Oct 2010 JP
2010-251645 Nov 2010 JP
2010-283340 Dec 2010 JP
2011-018425 Jan 2011 JP
2014-093312 May 2014 JP
2018-182331 Nov 2018 JP
10-1990-0016060 Nov 1990 KR
10-2006-0108547 Oct 2006 KR
10-2008-0022088 Mar 2008 KR
10-2014-0030009 Mar 2014 KR
10-2016-0148536 Dec 2016 KR
I611428 Jan 2018 TW
9200924 Jan 1992 WO
9200925 Jan 1992 WO
WO 92-00925 Jan 1992 WO
0076948 Dec 2000 WO
2006132766 Dec 2006 WO
2007105814 Sep 2007 WO
2008134417 Nov 2008 WO
2009052356 Apr 2009 WO
20101016186 Feb 2010 WO
2010123967 Oct 2010 WO
2012099877 Jul 2012 WO
2012116052 Aug 2012 WO
2012129554 Sep 2012 WO
Non-Patent Literature Citations (42)
Entry
English Machine translation for JP 2009-099781 (Year: 2009).
U.S. Appl. No. 13/100,533, filed May 4, 2011, Carroll et al.
U.S. Appl. No. 13/100,540, filed May 4, 2011, Carroll et al.
U.S. Appl. No. 13/801,036, filed Mar. 13, 2013, Carroll et al.
U.S. Appl. No. 13/100,550, filed May 4, 2011, Carroll et al.
U.S. Appl. No. 13/800,861, filed Mar. 13, 2013, Carroll et al.
U.S. Appl. No. 13/100,563, filed May 4, 2011, Carroll et al.
U.S. Appl. No. 13/801,248, filed Mar. 14, 2013, Carroll et al.
Journal of the Ceramic Association, Japan, 1968, vol. 76 (873), p. 160-172.
(JP Patent Application No. 2013-509214)—Information Offer Form.
(U.S. Appl. No. 13/100,543, filed May 4, 2011) Non-Final Office Action dated May 22, 2014.
(EP Patent Aplication No. 11731163.9 )—Communication from EPO.
Application No. 201180032701.8—Office Action dated Aug. 4, 2014.
Application No. 201180031225.8—Office Action dated Aug. 5, 2014.
Application No. 201180032359.1—Office Action dated Aug. 19, 2014.
Application No. 201180031184.2—Office Action dated Aug. 20, 2014.
International Search Report dated Aug. 3, 2012, International Application No. PCT/US2012/026085.
International Search Report dated Oct. 18, 2012, International Application No. PCT/US2012/030475.
International Search Report, US Commissioner for Patents, Alexandria, Virginia, in PCT/US2011/035167, PCT Counterpart of the Present U.S. Appl. No. 13/100,619.
International Search Report, US Commissioner for Patents, Alexandria, Virginia, in PCT/US2011/035139, PCT Counterpart of the Present U.S. Appl. No. 13/100,550.
Kurihara, Yasutoshi et al., “Ag—Pd Thick Film Conductor for AIN Ceramics”, IEEE Transactions on Components, Hybrids, and Manufacturing Technology, vol. 13(2), 1990, 306-312.
Zhang, Y. et al., “Thermal Properties of Glass Frit and Effects on SI Solar Cells”, Materials Chemist and Physics, vol. 114 (1), 2009, 319-322.
Non-Final Office Action dated May 14, 2013, in U.S. Appl. No. 13/401,191.
Non-Final Office Action dated Dec. 22, 2011, in U.S. Appl. No. 13/100,619.
Non-Final Office Action dated Jul. 19, 2012, in U.S. Appl. No. 13/100,619.
Final Office Action dated Mar. 28, 2013, in U.S. Appl. No. 13/100,619.
Non-Final Office Action dated May 10, 2012, in U.S. Appl. No. 13/100,540.
Final Office Action dated Mar. 14, 2013, in U.S. Appl. No. 13/100,540.
Non-Final Office Action dated Dec. 22, 2011, in U.S. Appl. No. 13/100,550.
Non-Final Office Action dated Sep. 6, 2012, in U.S. Appl. No. 13/100,550.
Final Office Action dated Mar. 1, 2013, in U.S. Appl. No. 13/100,540.
Non-Final Office Action dated May 11, 2012, in U.S. Appl. No. 13/100,563.
Final Office Action dated Mar. 1, 2013, in U.S. Appl. No. 13/100,563.
Zhang, “Effect of interface glass on electrical performance of screen printed AG thick-film contacts of Si Solar Cells”, Thin Solid Films, 518( 2010) pp. e111-e113.
International Search Report, US Commissioner for Patents, Alexandria, Virginia, in PCT/US2011/035154, PCT Counterpart to the U.S. Appl. No. 13/100,533.
International Search Report, US Commissioner for Patents, Alexandria, Virginia, in PCT/US2011/035131, PCT Counterpart of the U.S. Appl. No. 13/100,540.
International Search Report, US Commissioner for Patents, Alexandria, Virginia, in PCT/US2011/035145, PCT Counterpart of the U.S. Appl. No. 13/100,563.
PCT International Search Report.
Rane, B. et al., “Firing and processing effects on microstructure of fitted silver thick film electrode materials for solar cells”, Materials Chemistry and Physics, vol. 82, 2003, pp. 237-245.
Larry, J. R., et al., “Thick-Film Technology: An Introduction to the Materials”, IEEE Transactions on Components, Hybrids, and Manufacturing Technology, vol. CHMT-3, No. 2, Jun. 1980.
Hilali, M., “Understanding and Development of Manufacturable Screen-Printed Contacts on High Sheet-Resistance Emitter for Low-Cost Silicon Solar Cells”, A Thesis Presented to the Academic Faculty, Georgia Institute of Technology, Aug. 2005.
Scotten W. Jones, “Diffusion in Silicon”, IC Knowledge LLC, Apr. 25, 2008.
Related Publications (1)
Number Date Country
20130255768 A1 Oct 2013 US
Provisional Applications (4)
Number Date Country
61331006 May 2010 US
61440117 Feb 2011 US
61445508 Feb 2011 US
61467003 Mar 2011 US
Continuations (1)
Number Date Country
Parent 13100550 May 2011 US
Child 13800861 US