The present invention relates to a thin film battery, a thin film battery manufacturing method and a refine microcrystalline electrode manufacturing method, and more particularly, to a thin film battery of high cycle life, a thin film battery manufacturing method and a refine microcrystalline electrode manufacturing method.
Nowadays, the use of thin film battery systems in wearable electronic devices and medical applications are growing rapidly. However, defects of conventional colloidal or solid electrolyte thin film batteries, for example, a lithium-ion battery, are that capacitance cannot be improved due to low energy density when current density is high, and the use of such batteries with poor capacitance in battery systems will eventually cause the material cost and the volume of the battery systems to increase. Moreover, as batteries with short cycle life will require to be replaced more often, the cost for using such batteries is increased.
Therefore, it is in need of a batteries with high cycle life and high capacitance under high current density that is free from the aforesaid two defects and thus can enhance the industrialization of thin film battery cells.
The present invention provides to a thin film battery, a thin film battery manufacturing method and a refine microcrystalline electrode manufacturing method, which can enable a thin film battery to has good charge-discharge cycle properties and improved capacitance density.
In an embodiment, the present invention provides a thin film battery manufacturing method, which comprises the following steps: depositing an active material on a conductive substrate to formed a first active material electrode layer; enabling the first active material electrode layer to be subjected to an annealing process, while allowing the annealing process to further include the following steps: enabling the first active material electrode layer to be subjected to a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval to form a first active material crystallization precursor; and enabling the first active material crystallization precursor to be subjected to a rapid thermal annealing (RTA) process in the oxygen-containing environment at a second temperature interval to form a first active material coating layer with uniformly distributed fine microcrystal grains, wherein the temperature range of the second temperature interval is greater than the temperature range of the first temperature interval; forming an electrolyte layer on the first active material coating layer; and forming an electrode layer on the electrolyte layer while allowing the electrode layer and the first active material coating layer to have opposite polarities.
In an embodiment, the present invention provides a refine microcrystalline electrode manufacturing method, which comprises the following steps: enabling an active material electrode layer to be subjected to a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval to form an active material crystallization precursor; and enabling the active material crystallization precursor to be subjected to a rapid thermal annealing (RTA) process in the oxygen-containing environment at a second temperature interval to form an active material coating layer with uniformly distributed fine microcrystal grains, wherein the temperature range of the second temperature interval is greater than the temperature range of the first temperature interval.
In an embodiment, the present invention provides a thin film battery, which comprises: a conductive substrate, a first active material coating layer, an electrolyte layer, and an electrode layer. The first active material coating layer is formed on the conductive substrate sequentially, first by a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval, and then by a rapid thermal annealing (RTA) process in the oxygen-containing environment at a second temperature interval, so as to enable the first active material coating layer to be formed with uniformly distributed fine microcrystal grains. The electrolyte layer is formed on the first active material coating layer. The electrode layer is formed on the electrolyte layer. Moreover, the electrode layer is formed with a polarity opposite to that of the first active material coating layer.
In an embodiment of the present invention, the first temperature interval is ranged between 300° C. and 500° C.
In an embodiment of the present invention, the second temperature interval is ranged between 500° C. and 900° C.
In an embodiment of the present invention, after the step for forming the first active material coating layer, a step for enabling the first active material coating layer to formed at least one first protrusion electrode layer is performed.
In an embodiment of the present invention, before the step for depositing the active material on the conductive substrate, the method further comprises the following steps: providing a substrate; and enabling a first collector layer to be formed on the substrate so as to form the conductive substrate.
In an embodiment of the present invention, the forming of the first collector layer on the substrate further comprises the following steps: forming at one first collector protrusion on the first collector layer.
In an embodiment of the present invention, the forming of the electrode layer on the electrolyte layer further comprises the following steps: forming a second active material coating layer on the electrolyte layer; and forming a second collector layer on the second active material coating layer.
In an embodiment of the present invention, before the step for forming the second collector layer on the second active material coating layer, the method further comprises the following steps: forming at least one second collector protrusion on the second collector layer while enabling each second collector protrusion to embed inside the second active material coating layer.
In an embodiment of the present invention, before the step for forming the first active material coating layer, the method further comprises the following steps: depositing an active material on the conductive substrate to form a third active material electrode layer; and enabling the third active electrode layer to be subjected to a conventional thermal annealing (CTA) process in the oxygen-containing environment to form a third active material coating layer with uniformly distributed coarse crystal grains, while enabling the third active material coating layer to be disposed between the conductive substrate and the first active material coating layer.
In an embodiment of the present invention, the conventional thermal annealing (CTA) process for forming the third active material coating layer is performed in a temperature interval ranged between 500° C. and 900° C.
In an embodiment of the present invention, after the step for forming the third active material coating layer, a step for enabling the third active material coating layer to formed at least one third protrusion electrode layer is performed.
In an embodiment of the present invention, the step for forming the electrolyte layer on the first active material coating layer further comprises the following step: forming at least one electrolyte protrusion on the electrolyte layer.
In an embodiment of the present invention, the first active material coating layer includes at least one first protrusion electrode layer.
In an embodiment of the present invention, the first active material coating layer is substantially a laminar electrode.
In an embodiment of the present invention, the first active material coating layer is substantially a protrusion electrode.
In an embodiment of the present invention, the conductive substrate further comprises: a substrate and a first collector layer, wherein the first collector layer is disposed on the substrate.
In an embodiment of the present invention, the first collector layer further comprises: at least one collector protrusion.
In an embodiment of the present invention, the electrolyte layer further comprises: at least one electrolyte protrusion.
In an embodiment of the present invention, the electrode layer further comprises: a second active material coating layer and a second collector layer, wherein the second active material coating layer is disposed on the electrolyte layer while the second collector layer is disposed on the second active material coating layer.
In an embodiment of the present invention, the second collector layer further comprises: at least one second collector protrusion, wherein each second collector protrusion is formed embedded inside the second active material coating layer.
In an embodiment of the present invention, the thin film battery further comprises: a third active material coating layer, formed at a position between the conductive substrate and the first active material coating layer; wherein the third active material coating layer is formed by a conventional thermal annealing (CTA) process in an oxygen-containing environment.
In an embodiment of the present invention, the third active material coating layer further comprises: at least one third protrusion electrode layer.
From the above description, it is noted that the present invention can provide a thin film battery, a thin film battery manufacturing method and a refine microcrystalline electrode manufacturing method. Operationally, there are active material coating layers being formed by a two-stage annealing process. That is, first a conventional thermal annealing (CTA) process is performed in an oxygen-containing environment at a lower first temperature interval so as to form an active material crystallization precursor, by that as the annealing time for the CTA process is comparatively longer and is performed under a slower temperature raising and decreasing rate, the charge-discharge cycle properties of the resulted thin film battery are improved; and then a rapid thermal annealing (RTA) process is performed in the oxygen-containing environment at a higher second temperature interval, by that as the annealing time for the RTA process is comparatively shorter and is performed under a rapid temperature raising and decreasing rate, an active material coating layer with uniformly distributed fine microcrystal grains is formed. It is noted that by the formation of the uniformly distributed fine microcrystal grains, the strength of the polycrystalline materials is enhanced and thus eventually the toughness and formability of the active material coating layer is improved for allowing the same to have more uniform deformation without causing any local stress to be overly concentrated. Therefore, the formation of the active material coating layer can prevent the electrolyte layer from cracking, by that the destructive tree-like channel generally caused by the cracking can be prevented and thus the performance of the thin film battery can be ensured. Overall, the performance of the thin film battery is enhanced and the charge-discharge cycle properties of the resulted thin film battery are improved.
Further scope of applicability of the present application will become more apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.
The present invention will become more fully understood from the detailed is description given herein below and the accompanying drawings which are given by way of illustration only, and thus are not limitative of the present invention and wherein:
For your esteemed members of reviewing committee to further understand and recognize the fulfilled functions and structural characteristics of the invention, several exemplary embodiments cooperating with detailed description are presented as the follows.
In this embodiment, the first active material coating layer 11 is disposed on the first collector layer 104 of the conductive substrate 10, whereas the first active material coating layer 11 is substantially a laminar electrode, i.e. the laminar electrode is a single-layered structure. Moreover, the first active material coating layer 11 is formed on the conductive substrate 10, first by a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval, and then by a rapid thermal annealing (RTA) process in the oxygen-containing environment at a second temperature interval, in that the temperature range of the second temperature interval is greater than the temperature range of the first temperature interval.
In detail, an active material is first being provided to be deposited on a conductive substrate into a first active material coating layer, whereas the active material can be LiMn2O4, LiCoO2, LiFePO4, LiNiO2, C, Si, SnO2, TiO2, or other derivative elements, alloys, or compounds. Then, the first active material coating layer is subjected to a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval ranged between 300° C. and 500° C. for at least 30 min so as to form a first active material crystallization precursor. Thereafter, the first active material crystallization precursor is subjected to a rapid thermal annealing (RTA) process in the oxygen-containing environment at a second temperature interval, that is ranged between 500° C. and 900° C., so as to form the first active material coating layer 11. Moreover, as the RTA process is performed within a very short period of time, the first active material coating layer 11 is formed with uniformly distributed fine microcrystal grains.
In this embodiment, the electrolyte layer 12 is formed on the first active material coating layer 11, whereas the electrolyte layer 12 can be a layer of colloidal or solid electrolyte. The electrode layer 13 is formed on the electrolyte layer 12, in a manner that the electrode layer 13 is formed with a polarity opposite to that of the first active material coating layer 11. For instance, if the electrode layer 13 is an anode electrode layer, the electrode that is the construction of the first active material coating layer 11 and the conductive substrate 10 will be a cathode electrode layer; and vice versa. The electrode layer 13 further includes a second active material coating layer 132 and a second collector layer 134 in a manner that the second active material coating layer 132 is formed on the electrolyte layer 12 while the second collector layer 134 is formed on the second active material coating layer 132. In this embodiment, the second active material coating layer 132 can be formed either by a conventional thermal annealing (CTA) process or by a rapid thermal annealing (RTA) process. Nevertheless, in another embodiment, the second active material coating layer can be formed in a way similar to the formation of the first active material coating layer, so that the formation of the second active material coating layer is not restricted to any specific process.
By the use of the aforesaid configuration, the active material coating layer 11 of the present invention is formed by a two-stage annealing process. That is, first a conventional thermal annealing (CTA) process is performed in an oxygen-containing environment at a lower first temperature interval so as to form an active material crystallization precursor, and then a rapid thermal annealing (RTA) process is performed in the oxygen-containing environment at a higher second temperature interval so as to form the first active material coating layer 11 with uniformly distributed fine microcrystal grains. As the annealing time for the CTA process is comparatively longer and is performed under a slower temperature raising and decreasing rate, the charge-discharge cycle properties of the resulted thin film battery 1 are improved; and moreover, as the annealing time for the RTA process is comparatively shorter and is performed under a rapid temperature raising and decreasing rate, the first active material coating layer 11 can be formed with uniformly distributed fine microcrystal grains. It is noted that by the formation of the uniformly distributed fine microcrystal grains, the strength of the polycrystalline materials is enhanced and thus eventually the toughness and formability of the first active material coating layer 11 is improved for allowing the same to have more uniform deformation without causing any local stress to be overly concentrated. Therefore, the formation of the first active material coating layer 11 can prevent the electrolyte layer 12 from cracking, by that the destructive tree-like channel generally caused by the cracking can be prevented and thus the performance of the thin film battery 1 can be ensured. Overall, the performance of the thin film battery is enhanced and the charge-discharge cycle properties of the resulted thin film battery 1 are improved.
In this embodiment, the third active material coating layer 24 is formed by a conventional thermal annealing (CTA) process in an oxygen-containing environment at a temperature interval ranged between 500° C. and 900° C. for at least 30 min. Comparing to the uniformly distributed fine microcrystal grains of the first active material coating layer 11, the third active material coating layer 24 is formed with crystal grains that are comparatively larger but are also uniformly distributed. Thereby, the thin film battery is substantially a two-layered structure with the first active material coating layer 11 and the third active material coating layer 24.
In this embodiment, the first protrusion electrode layer 313 is formed as a rectangular body, but in other embodiments, it can be formed as a trapezoid-shaped body, a cylinder, a hollow column, a ring, a finger-like body, or any other shapes. In addition, the first protrusion electrode layer 313 can be formed by a masking process, an etching process, a screen-printing process, a nano-imprint process, a photoresist process, or a laser dicing process, that is operating cooperatively with a vacuum thermal evaporation process, a radio-frequency sputtering process, a radio-frequency magnetron sputtering process, a high-frequency sputtering process, a high-frequency magnetron sputtering process, a chemical vapor deposition process, an electrostatic spray deposition process, or a pulsed laser deposition process.
Similarly, in this embodiment, the third protrusion electrode layer 442 is formed as a rectangular body, but in other embodiments, it can be formed as a trapezoid-shaped body, a cylinder, a hollow column, a ring, a finger-like body, or any other shapes. In addition, the third protrusion electrode layer 442 can be formed by a masking process, an etching process, a screen-printing process, a nano-imprint process, a photoresist process, or a laser dicing process, that is operating cooperatively with a vacuum thermal evaporation process, a radio-frequency sputtering process, a radio-frequency magnetron sputtering process, a high-frequency sputtering process, a high-frequency magnetron sputtering process, a chemical vapor deposition process, an electrostatic spray deposition process, or a pulsed laser deposition process.
In this embodiment, the first collector layer 504 includes at least one first collector protrusion 504A, which is formed as a rectangular body, but in other embodiments, it can be formed as a trapezoid-shaped body, a cylinder, a hollow column, a ring, a finger-like body, or any other shapes. In addition, the first collector protrusion 504A can be formed by a masking process, an etching process, a screen-printing process, a nano-imprint process, a photoresist process, or a laser dicing process, that is operating cooperatively with a vacuum thermal evaporation process, a radio-frequency sputtering process, a radio-frequency magnetron sputtering process, a high-frequency sputtering process, a high-frequency magnetron sputtering process, a chemical vapor deposition process, an electrostatic spray deposition process, or a pulsed laser deposition process.
Moreover, in this embodiment, the second collector layer 534 includes at least one second collector protrusion 534A, which is formed as a rectangular body, but in other embodiments, it can be formed as a trapezoid-shaped body, a cylinder, a hollow column, a ring, a finger-like body, or any other shapes. In addition, the second collector protrusion 534A can be formed by a masking process, an etching process, a screen-printing process, a nano-imprint process, a photoresist process, or a laser dicing process, that is operating cooperatively with a vacuum thermal evaporation process, a radio-frequency sputtering process, a radio-frequency magnetron sputtering process, a high-frequency sputtering process, a high-frequency magnetron sputtering process, a chemical vapor deposition process, an electrostatic spray deposition process, or a pulsed laser deposition process.
In this embodiment, the first collector protrusion 504A is embedded inside the first protrusion electrode layer 313 of the first active material coating layer 31, the second collector protrusion 534A is embedded inside the second active material coating layer 132, and the electrolyte protrusion 522 is embedded inside the second active material coating layer 132. Both the first collector protrusion 504A and the second collector protrusion 534A are formed for improving the surface adhesive force between the first active material coating layer 31 to the first collector layer 104 and the surface adhesive force between the second active material coating layer 132 to the second collector layer 134, and thus for enhancing the electron-current/hole-current collecting ability of the first active material coating layer 31 and the second active material coating layer 132.
Moreover, the electrolyte layer 52, the first active material coating layer 31 and the second active material coating layer 132 that are formed as a protrusive structures in this embodiment are designed for increasing the contact areas between the first active material coating layer 31, the second active material coating layer 132 and the electrolyte layer 52, by that a multi-directional ion conduction is enabled so as to improve the conduction efficiency between the electrolyte layer 52. Thereby, not only the capacitance of the thin film battery 5 can be increased for enabling the same to be charging and discharging under high current density, but also the energy density of the thin film battery 5 is increased.
At step S120, the active material electrode layer 80 is subjected to a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval to form a first active material crystallization precursor 82. As shown in
At step S130, the active material crystallization precursor 82 is subjected to a rapid thermal annealing (RTA) process in the oxygen-containing environment at a second temperature interval to form an active material coating layer 84 with uniformly distributed fine microcrystal grains. As shown in
In the embodiment shown in
As shown in
At step S220, the first active material electrode layer 110 is subjected to an annealing process, which can further include the following steps: enabling the first active material electrode layer 110 to be subjected to a conventional thermal annealing (CTA) process in an oxygen-containing environment at a first temperature interval to form a first active material crystallization precursor 112, as shown in
Operationally, the first active material coating layer 11 of the present invention is being formed by a two-stage annealing process as illustrated in step S220. That is, first the first active material electrode layer 110 is subjected to a conventional thermal annealing (CTA) process in an oxygen-containing environment at a lower first temperature interval between 300° C. to 500° C. for at least 30 min so as to form a first active material crystallization precursor 112; and then the first active material crystallization precursor 112 is subjected to a rapid thermal annealing (RTA) process in the oxygen-containing environment at a higher second temperature interval between 500° C. to 900° C. for at most 3 min, so as to form the first active material coating layer 11 with uniformly distributed fine microcrystal grains. Overall, as the annealing time for the CTA process is comparatively longer and is performed under a slower temperature raising and decreasing rate, the charge-discharge cycle properties of the resulted thin film battery are improved, and moreover, as the annealing time for the RTA process is comparatively shorter and is performed under a rapid temperature raising and decreasing rate, the first active material coating layer 11 with uniformly distributed fine microcrystal grains can be formed. It is noted that by the formation of the uniformly distributed fine microcrystal grains, the strength of the polycrystalline materials is enhanced and thus eventually the toughness and formability of the first active material coating layer 11 is improved for allowing the same to have more uniform deformation without causing any local stress to be overly concentrated. Therefore, the formation of the active material coating layer can prevent the electrolyte layer from cracking, by that the destructive tree-like channel generally caused by the cracking can be prevented and thus the performance of the thin film battery can be ensured. Overall, the performance of the thin film battery is enhanced and the charge-discharge cycle properties of the resulted thin film battery are improved.
In another embodiment, before the forming of the first active material coating layer 11, the method of the present invention further include the following steps: depositing an active material on the conductive substrate 10 so as to form a third active material electrode layer 240, as shown in
In an embodiment of the present invention, the conventional thermal annealing (CTA) process for forming the third active material coating layer is performed in a temperature interval ranged between 500° C. and 900° C. Comparing to the uniformly distributed fine microcrystal grains of the first active material coating layer 11, the third active material coating layer 24 is formed with crystal grains that are comparatively larger but are also uniformly distributed. Thereby, a two-layered structure with the first active material coating layer 11 and the third active material coating layer 24 is achieved.
In another embodiment, after the forming of the first active material coating layer 11, the method of the present invention further include the following steps: enabling at least one first protrusion electrode layer 313 to be formed on the first active material coating layer 31, as shown in
In another embodiment, after the forming of the third active material coating layer 44, the method of the present invention further include the following steps: enabling at least one third protrusion electrode layer 442 to be formed on the third active material coating layer 44, as shown in
At step S230, as shown in
In another embodiment of the present invention, the step for forming the electrolyte layer on the first active material coating layer further comprises the following step: forming at least one electrolyte protrusion 552 on the electrolyte layer 52, as shown in
At step S240, as shown in
In this embodiment, the forming of the electrode layer 13 further include the following steps: forming a second active material coating layer 132 on the electrolyte layer 12, as shown in
In another embodiment, the method for manufacturing thin film batteries further includes the following steps: forming at least one first collector protrusion 504A on the first collector layer 504 in a manner that the first collector protrusion 504A is embedded inside the first protrusion electrode layer 313, as shown in
To sum up, the present invention provides a thin film battery, a thin film battery manufacturing method and a refine microcrystalline electrode manufacturing method. Operationally, there are active material coating layers being formed by a two-stage annealing process. That is, first a conventional thermal annealing (CTA) process is performed in an oxygen-containing environment at a lower first temperature interval so as to form an active material crystallization precursor, by that as the annealing time for the CTA process is comparatively longer and is performed under a slower temperature raising and decreasing rate, the charge-discharge cycle properties of the resulted thin film battery are improved; and then a rapid thermal annealing (RTA) process is performed in the oxygen-containing environment at a higher second temperature interval, by that as the annealing time for the RTA process is comparatively shorter and is performed under a rapid temperature raising and decreasing rate, an active material coating layer with uniformly distributed fine microcrystal grains is formed. It is noted that by the formation of the uniformly distributed fine microcrystal grains, the strength of the polycrystalline materials is enhanced and thus eventually the toughness and formability of the active material coating layer is improved for allowing the same to have more uniform deformation without causing any local stress to be overly concentrated. Therefore, the formation of the active material coating layer can prevent the electrolyte layer from cracking, by that the destructive tree-like channel generally caused by the cracking can be prevented and thus the performance of the thin film battery can be ensured. Overall, the performance of the thin film battery is enhanced and the charge-discharge cycle properties of the resulted thin film battery are improved.
In a real-world charging/discharging cycle test, the capacitance of the thin film battery of the invention at its 500 cycle can achieve about 98.7%, which indicates the feasibility of the present invention as the charge-discharge cycle properties of the resulted thin film battery are effectively enhanced. In addition, comparing to the thin film battery that is only manufactured using only RTA process but under the same coating condition, the capacitance density of the thin film battery of the invention is enhanced; and comparing to the thin film battery that is only manufactured using only CTA process, the charge-discharge cycle properties of the resulted thin film battery are improved.
In the present invention, the thin film battery can be achieved by the assembling of single-layered active material coating layers with uniformly distributed fine microcrystal grains, or can be achieved by two-layered structures of an active material coating layers with uniformly distributed fine microcrystal grains and an active material coating layers with uniformly distributed coarse crystal grains. In addition, the protrusion electrodes can be manufactured and provided to form the thin film battery of the invention; or even the collector protrusions can be designed for increasing ion migration paths so as to achieve rapid charging/discharging property while high charge-discharge cycle properties of the thin film battery.
With respect to the above description then, it is to be realized that the optimum dimensional relationships for the parts of the invention, to include variations in size, materials, shape, form, function and manner of operation, assembly and use, are deemed readily apparent and obvious to one skilled in the art, and all equivalent relationships to those illustrated in the drawings and described in the specification are intended to be encompassed by the present invention.