Thin film magnetic head

Abstract

A thin film magnetic head comprising a substrate, a lower magnetic pole provided on the substrate, a write gap layer located on the lower magnetic pole, and an upper magnetic pole located on the gap layer, the upper magnetic pole including a plating base layer in contact with the gap layer, wherein the plating base layer of the upper magnetic pole is made of a magnetic film having a saturation magnetic flux density of 1.2 T or larger. The thin film magnetic head has an increased recording density, and is adapted to recording at an increased frequency.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates to a thin film magnetic head and, particularly, to a thin film magnetic head characterized by the construction of its plating base layer for providing a magnetic pole core of a thin film magnetic head of an induction type constituting a hard disc drive (HDD) with a high saturation magnetic flux density.

[0003] 2. Description of the Related Art

[0004] Recent hard disc drives, which are external storage devices for computers, have an increasing recording density, and comprise a magnetic head with small elements. Also, recent recording mediums have an increasing coercive force. Under the circumstances, a magnetic head capable of adequately writing records to such a recording medium having a high coercive force are demanded.

[0005] In inductive thin film magnetic heads, a thin film of Ni-Fe alloy is commonly used as a material for a write magnetic pole. Most of the write magnetic poles have a two-layer structure of a layer of Ni50Fe50, i.e., 50 permalloy, provided on a read gap and having a saturation magnetic flux density BS of the order of 1.5 teslas (T) and a thickness of the order of 1 micrometer, and a layer of Ni80Fe20, i.e., 80 permalloy, laminated thereon and having a thickness of 1 to 4 micrometers. This is for the sake of ensuring sufficient recording properties at a strong magnetic field by placing a magnetic material having a saturation magnetic flux density BS higher than 80 permalloy near an upper magnetic pole gap which is the point for finally writing on a recording medium.

[0006] A practical magnetic pole core, which is made up entirely of 50 permalloy having a BS nearly equal to 1.5 T, is known. However, since 50 permalloy has a large magnetostriction, there is a possibility that the 50 permalloy material is strained during processing, and this degrades the magnetic properties of a magnetic pole core.

[0007] Referring to FIGS. 6A to 6C, a process for manufacturing a conventional writing thin film magnetic head is described.

[0008] As shown in FIG. 6A, a plating base layer 32 of Ni80Fe20 and a lower magnetic pole layer 33 of Ni80Fe20 are successively formed on a TiC substrate 31 provided with an Al2O3 film (not shown) (also called Al2O3—TiC substrate). The surface of the magnetic pole layer 33 is then planarized, and a write gap layer 34 consisting of Al2O3 or the like is provided thereon by a sputtering process. There is a case where the write gap layer 34 is subsequently patterned together with the lower magnetic pole layer 33 of Ni80Fe20 and, accordingly, they are depicted to have the same width in the drawing.

[0009] Subsequently, in a region which is not shown in FIG. 6A, a first interlayer insulation film of a resist material or the like, a coil in a shape of horizontal spiral on the first interlayer insulation film, and a second interlayer insulation film of a resist material or the like on the coil are successively formed, the coil being provided at both ends thereof with an electrode.

[0010] A further plating base layer 35 of Ni80Fe20 having a thickness of, for example, 0.1 micrometer is then formed on the write gap layer 34 by a sputtering process, as shown in FIG. 6A.

[0011] Referring to FIG. 6B, a patterned resist layer 36 is then formed and, using the patterned resist layer 36 as a plating frame, an Ni50Fe50 layer 37 having a thickness of, for example, 1 micrometer and an Ni80Fe20 layer 38 having a thickness of, for example, 2.0 micrometers are successively formed by a plating process, to provide an upper magnetic pole 39.

[0012] Referring to FIG. 6C, after the removal of the resist layer 36 (FIG. 6B), exposed portions of the plating base layer 35 of Ni80Fe20, which are shown by the broken lines in FIG. 6C, are removed by ion milling using Ar ions 40.

[0013] Subsequently, an Al2O3 film, as a protective film, is provided on the entire face of the substrate 31 having a laminate structure of formed layers, although not shown in the drawing, and the substrate is cut and subjected to a slider making process which includes grinding for adjusting lengths of write poles, i.e., a gap depth, and polishing, to thereby produce a basic construction of a thin film magnetic head.

[0014] When the thin film magnetic head obtained as described above referring to FIGS. 6A to 6C was used to write a magnetic recording medium having a coercive force HC of 3500 oersteds (Oe), it was found that an overwrite value was −27 dB.

[0015] However, since an overwrite value is generally regarded as being practical when it is −30 dB or lower, the conventional thin film magnetic head as described above was not appropriate as a thin film magnetic head for a recording medium of high recording density having a coercive force HC of the order of 3500 Oe.

[0016] Thus, with the development of recent recording mediums having a higher coercive force, it is necessary to use a material having a higher saturation magnetic flux density BS for an upper magnetic pole core, or for an upper magnetic pole core and a lower magnetic layer, constituting an inductive thin film magnetic head, and with the need of such a higher saturation magnetic flux density, it has been recognized that a magnetic thin film for the upper magnetic pole core and the lower magnetic layer must have a BS nearly equal to 2.0 T at a portion at which a magnetic flux is most concentrated.

[0017] As a magnetic thin film material meeting such a need of higher saturation magnetic flux density, CoNiFe materials were developed (Japanese Patent Application No. 2000-7487, which has not been published at the filing of the present application). The CoNiFe material has magnetic properties superior to those of 80 permalloy and 50 permalloy. For example, Co64Ni12Fe24 has a saturation magnetic flux density BS nearly equal to 2 T, and can provide a thin magnetic head having a head magnetic field which is larger than that of conventional thin film magnetic head.

[0018] Nevertheless, a film of such a CoNiFe material, which is formed by an electroplating process, has an internal stress, which is distributed in the plane of the formed film, of about 0.5 to 10×1010 dyn/cm2, which is large compared to 80 permalloy and 50 permalloy, and when it is formed into a film having a thickness of micron-order, it will give rise to a problem that the formed film is prone to peel. Incidentally, a Co64Ni12Fe24 film has an internal stress of about 7×1010 dyn/cm2.

[0019] When a magnetic thin film is peeled, the peeled magnetic thin film, which represents a metal piece, damages other part or parts of a magnetic head, or leads to the generation of dust in another process, and causes trouble to an apparatus for manufacturing a magnetic head. Consequently, it has been difficult to use a CoNiFe material as a magnetic material for a thin film magnetic head.

SUMMARY OF THE INVENTION

[0020] Thus, the invention aims to enhance a writing capacity of a thin film magnetic head by the use of a magnetic film of high saturation magnetic flux density having a small thickness.

[0021] A thin film magnetic head according to the invention is characterized by comprising a plating base layer, which makes up an upper magnetic pole of the thin film magnetic head, made of a magnetic film having a saturation magnetic flux density of 1.2 teslas (T) or larger, more preferably 1.9 teslas or larger. Thus, the invention provides a thin film magnetic head comprising a substrate, a lower magnetic pole provided on the substrate, a write gap layer located on the lower magnetic pole, and an upper magnetic pole located on the gap layer, the upper magnetic pole including a plating base layer in contact with the gap layer, wherein the plating base layer of the upper magnetic pole is made of a magnetic film having a saturation magnetic flux density of 1.2 T or larger, more preferably 1.9 teslas or larger.

[0022] Preferably, the thin film magnetic head of the invention further comprises a thin magnetic film having a saturation magnetic flux density of 1.2 T or larger, more preferably 1.9 teslas or larger, between the lower magnetic pole and the write gap layer.

[0023] Preferably, at least one of the plating base layer and the thin magnetic film located between the lower magnetic pole and the write gap layer is formed of a magnetic material of alloy containing one or more of elemental Co, Ni, and Fe.

[0024] Preferably, at least one of the plating base layer and the thin magnetic film located between the lower magnetic pole and the write gap layer is formed of a sputtered or evaporated film.

[0025] Preferably, at least one of the plating base layer and the thin magnetic film located between the lower magnetic pole and the write gap layer has a thickness of 0.05 micrometer or more.

[0026] Preferably, the upper magnetic pole comprises an electroplated film having a saturation magnetic flux density of 1.5 T or larger located on the plating base layer.

[0027] Preferably, the electroplated film is formed of a magnetic film having a higher saturation magnetic flux density and a magnetic film having a lower saturation magnetic flux density, the magnetic film having a higher saturation magnetic flux density being located closer to the plating base layer.

[0028] The invention can provide a magnetic storage device using the thin film magnetic head according to the invention, the magnetic storage devise having an enhanced recording capacity and being capable of adequately writing record to a recording medium having a high coercive force.

BRIEF DESCRIPTION OF THE DRAWINGS

[0029] The above and other objects and advantages of the invention will be well understood and appreciated by a person with ordinary skill in the art, from consideration of the following detailed description made by referring to the attached drawings, wherein:

[0030] FIG. 1 schematically shows the principle of the invention,

[0031] FIGS. 2A to 2C illustrate the manufacture of a thin film magnetic head of a first embodiment of the invention,

[0032] FIG. 3A illustrates a thin film magnetic head of a second embodiment of the invention,

[0033] FIG. 3B shows curves of magnetization of the upper magnetic pole of the magnetic head of the second embodiment,

[0034] FIG. 4 is a schematic sectional view of a thin film magnetic head of a third embodiment of the invention,

[0035] FIG. 5 is a schematic sectional view of a thin film magnetic head of a variant of the third embodiment, and

[0036] FIGS. 6A to 6C illustrate the manufacture of a conventional thin film magnetic head.

DETAILED DESCRIPTION OF THE INVENTION

[0037] FIG. 1 schematically shows the principle of the invention. In this drawing, a lower magnetic pole 2, a write gap layer 3, a plating base layer 4, and a film 5 of high saturation magnetic flux density are successively formed on a substrate 1, with the plating base layer and the film 5 of high saturation magnetic flux density forming an upper magnetic pole 6. The substrate 1 may be an Al2O3—TiC substrate, as earlier described, or the like. The write gap layer 3 may be formed of Al2O3 or the like, also as described earlier.

[0038] The thin film magnetic head according to the invention uses, as the plating base layer 4, which forms the upper magnetic pole 6 of the thin film magnetic head, a magnetic film having a saturation magnetic flux density of 1.2 T or larger. By the use of the plating base layer 4 of saturation magnetic flux density of 1.2 T or larger, the thin film magnetic head of the invention can achieve improved overwriting properties even if the film 5 of high saturation magnetic flux density has a small thickness.

[0039] In addition, when such a film having a saturation magnetic flux density BS of 1.2 T or larger is also provided at the side of the lower magnetic pole 2, the thin film magnetic head of the invention can have a further improved magnetic properties.

[0040] It is preferable that the magnetic film having a saturation magnetic flux density BS of 1.2 T or larger has a thickness of 0.05 micrometer or more in order to display an improvement in the saturation magnetic flux density.

[0041] Referring to FIG. 2, the manufacturing process of a thin film magnetic head of a first embodiment of the invention will be described.

[0042] As illustrated in FIG. 2A, a first plating base layer 12 of Ni80Fe20 and a lower magnetic pole layer 13 of Ni80Fe20 are successively formed on a TiC substrate 11 provided with an Al2O3 film (not shown) (also called Al2O3—TiC substrate). The surface of the magnetic pole layer 13 is then planarized, and a write gap layer 14 consisting of Al2O3 is formed thereon by a sputtering process. There is a case where the write gap layer 14 is subsequently patterned together with the lower magnetic pole layer 13 of Ni80Fe20 and, accordingly, they are depicted to have the same width in the drawing.

[0043] Subsequently, in a region which is not shown in FIG. 2A, a first interlayer insulation film of a resist material or the like, a coil in a shape of horizontal spiral on the first interlayer insulation film, and a second interlayer insulation film of a resist material or the like on the coil are successively formed, the coil being provided at both ends thereof with an electrode.

[0044] A second plating base layer 15 of Co63Ni11Fe26 having a thickness of 0.05 micrometer or more, for example, 0.1 micrometer, is then formed on the write gap layer 14 by a sputtering process, as shown in FIG. 2A. It should be noted that, since a CoNiFe film formed by a sputtering process has a saturation magnetic flux density BS which is a little lower than that of a CoNiFe film formed by an electroplating process, the second plating base layer 15 has a little larger Fe composition compared to the Co64Ni12Fe24 film referred to above, in order to achieve a saturation magnetic flux density BS of about 2 T.

[0045] Subsequently, a patterned resist layer 16 is then formed, as illustrated in FIG. 2B, and using the patterned resist layer 16 as a plating frame, an Ni50Fe50 layer 17 having a thickness of, for example, 1 micrometer and an Ni80Fe20 layer 18 having a thickness of, for example, 2.0 micrometers are successively formed by a plating process, to provide an upper magnetic pole 19.

[0046] The resist layer 16 is then removed and, thereafter, as illustrated in FIG. 2C, exposed portions of the second plating base layer 15 of Co63Ni11Fe26, which is shown by the broken lines in the drawing, are removed by ion milling using Ar ions 20.

[0047] Subsequently, an Al2O3 film (not shown), as a protective film, is provided on the entire face of the substrate 31 having a laminate structure of formed layers, and the substrate is then cut, and is subjected to a slider making process which includes grinding for adjusting lengths of write poles, i.e., a gap depth, and polishing, to thereby produce a basic construction of a thin film magnetic head, as in the manufacture of conventional thin film magnetic heads.

[0048] When the resultant thin film magnetic head was used to write a magnetic recording medium having a coercive force HC of 3500 oersteds (Oe), it was found that an overwrite value was −35 dB, which was improved and was larger by 8 dB compared to the overwrite value of the thin film magnetic head using the Co64Ni12Fe24 film formed by an electroplating process referred to above, and was sufficiently meet the requirement of practical overwrite value of −30 dB or smaller.

[0049] Formerly, an Ni80Fe20 layer was used as a plating base layer by paying attention only to ease of the production of thin film magnetic heads. In contrast, in the thin film magnetic head of the first embodiment of the invention described above, attention is paid to a saturation magnetic flux density of a plating base layer, to which no attention has been paid hitherto, and the magnetic film having a saturation magnetic flux density of 2.0 T is used as the plating base layer, so that the thin film magnetic head can have improved writing properties and a high recording capacity.

[0050] Referring to FIG. 3, a thin film magnetic head of a second embodiment of the invention will now be described.

[0051] FIG. 3A schematically shows a sectional view of a thin film magnetic head of a second embodiment of the invention. The process for manufacturing it is the same as that for the thin film magnetic head of the first embodiment and, accordingly, is not described here.

[0052] The thin film magnetic head of the second embodiment of the invention uses, as a film of high saturation magnetic flux density forming an upper magnetic pole, a layer 21 of Co64Ni11Fe25 having a saturation magnetic flux density BS of about 2 T. Other components in the thin film magnetic head of this embodiment are the same as those of the first embodiment as described above, and are indicated by the same reference numerals in FIGS. 2A to 2C.

[0053] FIG. 3B shows curves of magnetization of the upper magnetic pole in the second embodiment, which consists of a plating base layer 15 of Co63Ni11Fe26 and the upper magnetic pole layer 21 of Co64Ni11Fe25. A coercive force HC in the direction of axis of difference of magnetization of the Co63Ni11Fe26 film 15, which was formed by a sputtering process, is 33 Oe, which is very large, whereas a coercive force HC in the direction of axis of difference of magnetization of the Co64Ni11Fe25 film 21, which was formed by an electroplating, is very small. Accordingly, the coercive force HC in the direction of axis of difference of magnetization of the entire upper magnetic pole is practical value of 2 Oe, and inferior magnetic properties of the plating base layer is compensated. In other words, a magnetic material forming a thin film magnetic head must have a coercive force HC in the direction of axis of difference of magnetization of 10 Oe or smaller, more preferably 2 Oe or smaller, and, in the second embodiment of the invention, the upper magnetic pole has a coercive force of 2 Oe as a whole, which is in a practical range, so that it can adequately meet such a need.

[0054] On the other hand, both films 15 and 21 have a saturation magnetic flux density BS of about 2 T, and the upper magnetic pole formed of these films also has a saturation magnetic flux density BS of about 2 T as a whole. Accordingly, the entire upper magnetic pole in the second embodiment can have a saturation magnetic flux density which is improved by about 0.1 T compared to a magnetic pole using a plating base layer of low saturation magnetic flux density, to thereby have a high recording capacity.

[0055] Thus, in the second embodiment of the invention, the film of high saturation magnetic flux density forming the upper magnetic pole is made of the Co64Ni11Fe25 film having a large saturation magnetic flux density than that of an Ni50Fe50 film and, accordingly, the upper magnetic pole can achieve sufficient magnetic properties even if it has a little smaller thickness.

[0056] In addition, the Co64Ni11Fe25 film has a saturation magnetostriction λ, which is smaller than that of an Ni50Fe50 film and is close to that of an Ni80Fe20 film. From this point of view, magnetic properties of the Co64Ni11Fe25 film are not degraded by strain induced during the processing, even if the film is formed in a little larger thickness.

[0057] A thin film magnetic head of a third embodiment of the invention, which will now be described by referring to FIG. 4, illustrates a schematic sectional view of the magnetic head. In this embodiment, a layer 22 of Co63Ni11Fe26 having a high saturation magnetic flux density is provided on a lower magnetic pole 13 of Ni80Fe20. Other components and the formation thereof in the thin film magnetic head of this embodiment are the same as those of the second embodiment as described above, and are indicated by the same reference numerals in FIG. 3A.

[0058] In this embodiment, following the formation of the lower magnetic pole 13 of Ni80Fe20, the surface thereof is planarized, and a layer 22 of Co63Ni11Fe26 having a thickness of 0.05 micrometer or more, for example, 0.1 micrometer, is then deposited by a sputtering process, after which the step of forming a write gap layer 14 and following steps as earlier described for the second embodiment can be carried out.

[0059] Thus, in the third embodiment of the invention, the layer 22 of Co63Ni11Fe26, which has a saturation magnetic flux density BS of about 2 T and is in contact with the write gap layer 14 of the lower magnetic pole side, is provided. This layer 22 makes it possible to provide, in combination with the layer 21 of high saturation magnetic flux density of the upper magnetic pole, the thin film magnetic head of the embodiment with a still higher recording capacity.

[0060] There can be a variant of the thin film magnetic head of the third embodiment of the invention and this is illustrated in a schematic sectional view of FIG. 5. In this variant, an additional upper magnetic pole layer 23 of Ni50Fe50 is provided on the upper magnetic pole layer 21 of Co64Ni11Fe25 in the third embodiment. Other components and the formation thereof in the thin film magnetic head of this variant are the same as those of the third embodiment as described above, and are indicated by the same reference numerals in FIG. 4.

[0061] In this variant, during the formation of the upper magnetic pole by an electroplating process using a patterned resist layer as a plating frame, an additional upper magnetic pole layer 23 of Ni50Fe50 having a thickness of, for example, 1 micrometer may be formed following the formation of the upper magnetic pole layer 21 of Co64Ni11Fe25 having a thickness of, for example, 1 micrometer.

[0062] According to a current electroplating process, it is difficult, due to an internal stress and the like, to form, through simple steps, a layer of Co64Ni11Fe25 having a stable thickness of 1 micrometer or more in a condition where good magnetic properties are preserved, and, consequently, there is a possibility that a thin film magnetic head using such a layer of Co64Ni11Fe25 cannot generate an adequate magnetic field. Contrarily, in the variant of the third embodiment of the invention as described, since the additional upper magnetic pole layer 23 of Ni50Fe50, which has a saturation magnetic flux density BS of about 1.5 T, is provided on the upper magnetic pole layer 21 of Co64Ni11Fe25, the thin film magnetic head of this variant can generate a sufficiently strong magnetic field.

[0063] As will be well understood by those skilled in the art, the invention is not limited to the embodiments and variant as described above, and various modifications and changes may be made without departing from the scope and spirit of the invention.

[0064] For example, although the above embodiments and variant use a Co63Ni11Fe26 layer as a magnetic film of high saturation magnetic flux density to be provided on the plating base layer of the upper magnetic pole side or the lower magnetic pole, the magnetic film of high saturation magnetic flux density in the invention is not limited to a CoNiFe layer having such a composition, and may be formed of a material selected from various CoNiFe materials having different compositions.

[0065] Further, the magnetic film of high saturation magnetic flux density in the invention is not only formed of a CoNiFe material but also may be formed of another material, provided that the another material has a saturation magnetic flux density BS of 1.2 T or larger, more preferably 1.9 T or larger. For example, the magnetic film of high saturation magnetic flux density may be formed of an FeAlN material, which is a ferrous material having aluminum and nitrogen added, Ni50Fe50 or the like.

[0066] Also, although the upper magnetic pole layer is made up of the Co64Ni11Fe25 film in the second and third embodiments described above, the material for the upper magnetic pole layer in the invention is not limited to a CoNiFe material having such a composition, and may be formed of a material selected from various CoNiFe materials having different compositions.

[0067] In addition, the material having a high saturation magnetic flux density in the invention is not limited to a ternary metal material of CoNiFe, and a material, in which Cr, Mo, and/or a non-magnetic metal element, such as W, is added to the ternary CoNiFe, may be used as the material having a high saturation magnetic flux density. Although such a material based on CoNiFe and containing an additive element provide a magnetic film having a saturation magnetic flux density which is a little lower than 1.9 T, the material can provide a magnetic film with an enhanced resistivity.

[0068] Also, although the Ni50Fe50 film is used in the variant of the third embodiment described above, as an additional magnetic film to supplement the thickness of the upper magnetic pole, the material for the supplementation is not limited to Ni50Fe50, and various magnetic materials may be used therefor. For example, a film of Ni80Fe20, which has a saturation magnetostriction λ smaller than that of the film of Ni50Fe50, despite a saturation magnetic flux density BS smaller than that of the Ni50Fe50 film, can be used to have a thickness of 1 micrometer or larger.

[0069] Also, although the upper magnetic pole in the second embodiment described above is made up only of the layer of Co64Ni11Fe25, a film of Ni50Fe50 or Ni80Fe20 may be laminated on the layer of Co64Ni11Fe25 to supplement the thickness of the upper magnetic pole.

[0070] Also, although the write gap layer in the first embodiment described above is provided directly on the lower magnetic pole, a magnetic film having a high saturation magnetic flux density, such a film of Co63Ni11Fe26, may be provided on the lower magnetic pole by a sputtering process, which makes it possible to improve the overwrite value of the thin film magnetic head.

[0071] In addition, although the film of Co63Ni11Fe26 is formed by a sputtering process in the respective embodiments described above, the process for the formation of the film is not limited to a sputtering process, and an evaporation process may be used.

[0072] Further, although the embodiments described above illustrate a single inductive thin film magnetic head, those skilled in the art would easily understand that the invention could apply to an inductive thin film magnetic head of a composite thin film magnetic head in which the inductive thin film magnetic head and a magnetoresistive (MR) head are combined.

[0073] Also, although the plating base layer is provided directly on the Al2O3 film of the Al2O3—TiC substrate in the above embodiment described above for simplicity, a thin film of Ti or the like may be interposed between the Al2O3 film and the plating base layer to improve adhesion of the plating base layer to the substrate.

[0074] As described, the thin film magnetic head according to the invention, in which a film having a saturation magnetic flux density of 1.2 T or larger is used as a plating base layer for the formation of an upper magnetic pole by an electroplating process, can have an improved recording capacity. Thus, the invention largely contributes to providing a thin film magnetic head adapted to recording in an increased frequency and having an increased recording density and, further, to the performance of magnetic storage devices in which an HDD device, or the like, of high performance is incorporated.

Claims

1. A thin film magnetic head comprising a substrate, a lower magnetic pole provided on the substrate, a write gap layer located on the lower magnetic pole, and an upper magnetic pole located on the gap layer, the upper magnetic pole including a plating base layer in contact with the gap layer, wherein the plating base layer of the upper magnetic pole is made of a magnetic film having a saturation magnetic flux density of 1.2 T or larger.

2. The thin film magnetic head of claim 1, wherein a thin magnetic film having a saturation magnetic flux density of 1.2 T or larger is provided between the lower magnetic pole and the write gap layer.

3. The thin film magnetic head of claim 1, wherein the plating base layer is formed of a magnetic material of alloy containing one or more of elemental Co, Ni, and Fe.

4. The thin film magnetic head of claim 2, wherein the thin magnetic film is formed of a magnetic material of alloy containing one or more of elemental Co, Ni, and Fe.

5. The thin film magnetic head of claim 1, wherein the plating base layer is formed of a sputtered or evaporated film.

6. The thin film magnetic head of claim 2, wherein the thin magnetic film is a sputtered or evaporated film.

7. The thin film magnetic head of claim 1, wherein the plating base layer has a thickness of 0.05 micrometer or more.

8. The thin film magnetic head of claim 2, wherein the thin magnetic film has a thickness of 0.05 micrometer or more.

9. The thin film magnetic head of claim 1, wherein the upper magnetic pole comprises an electroplated film having a saturation magnetic flux density of 1.5 T or larger located on the plating base layer.

10. The thin film magnetic head of claim 9, wherein the electroplated film is formed of a magnetic film having a higher saturation magnetic flux density and a magnetic film having a lower saturation magnetic flux density, the magnetic film having a higher saturation magnetic flux density being located closer to the plating base layer.

11. A magnetic recording device comprising the thin film magnetic head of claim 1.