Three-dimensional net-like structure, and method and device for producing three dimensional net-like structure

FIELD OF THE INVENTION

This invention relates to a three-dimensional netted structure used for a cushioning material and the like, and a method of and an apparatus for manufacturing the same.

BACKGROUND OF THE INVENTION

Known methods of manufacturing a void-carrying three-dimensional netted structure include a method disclosed in Japanese Patent Publication KOKOKU No. S50-39185, or a method disclosed in Japanese Patent Laid-Open KOKAI No. S60-11352, etc., which is adapted to manufacture resin cotton on which polyester fibers are bonded with a bonding agent made of, for example, a rubber-based material. There are also methods of or apparatuses for manufacturing a void-carrying three-dimensional netted structure by entangling resin threads by endless belts, and such methods or apparatuses include the invention disclosed in Japanese Patent Laid-Open KOKAI No. H11-241264, etc.

However, the demands for a product of such a three-dimensional netted structure have been diversified. It is necessary that each of netted structures manufactured be finished to one of different shapes by cutting or molding the netted structures to demanded shapes in a later stage of the manufacturing stage. This causes a product finishing operation to become very complicated.

A three-dimensional netted structure manufactured by a prior art method becomes low in density in some cases. Since both surface portions of a bundle contact belt conveyors, outer surfaces of the bundle are substantially flattened. However, left and right end surfaces of the bundle have an irregular, helical shape, and side surfaces thereof have a laterally wavy non-straight shape.

The endless belts mentioned above by which a resin threads are entangled is liable to be damaged due to the heat, etc., so that there is a fear of encountering a problem concerning the durability of the endless belts.

Therefore, the present invention provides a method of and an apparatus for manufacturing a three-dimensional netted structure, capable of rendering it unnecessary to carry out a finishing operation in a later stage, improving the degree of straightness of the side surfaces of the netted structure, meeting a demand for finishing the netted structure to modified shapes, and improving the durability of the netted structure.

SUMMARY OF THE INVENTION

In view of these various problems, the invention is a three-dimensional netted structure manufactured by preparing a thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; and cooling the resultant filaments with water so as to obtain a netted structure having sparse and dense portions arranged alternately in the material extruding direction. This enables the netted structure to be applied to a cushioning material and the like which is made possible to be hung at a sparse portion thereof on a hook.

The invention is a three-dimensional netted structure manufactured by preparing a thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; and cooling the resultant filaments with a liquid so as to obtain a netted structure having hollow portions arranged in the material extruding direction. This enables the hollow portions to be utilized effectively by inserting other members therein or by using the hollow portions in a different manner, and the netted structure to be thereby applied to various uses.

The invention is a three-dimensional netted structure manufactured by preparing a thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; and cooling the resultant filaments with a liquid so as to obtain a sheet having a percentage of void of substantially zero in the material extruding direction. This enables the soundproofing and shock absorbing performance of the sheet to be improved.

The invention is a three-dimensional netted structure manufactured by preparing a thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; and cooling the resultant filaments with a liquid so as to obtain a netted structure having not smaller than two separable regions. This enables the difficulty, which was encountered in a related art netted structure of this kind, in recycling a complex resin and the like to be overcome by providing the netted structure with not smaller than two separable regions.

The invention is a three-dimensional netted structure manufactured by preparing a thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; and cooling the resultant filaments with a liquid so as to obtain an insulating material or a sound absorbing material. This enables the netted structure to be used as a building material, an interior finishing material for automobiles, and materials for similar purposes.

The invention is a three-dimensional netted structure manufactured by preparing a thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; cooling the resultant filaments with a liquid; and applying a fire-resistant material to the cooled filaments or enclosing the cooled filaments with the same material or adding the same material to the cooled filaments. This enables the reliability of an interior heat insulating material, an exterior heat insulating material, an interior finishing material for a side wall and an interior finishing material for automobiles to be improved.

The invention is a three-dimensional netted structure manufactured by preparing a regenerated thermoplastic resin, especially, polyethylene terephthalate as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding; and cooling the resultant filaments with a liquid so as to obtain a recycled netted structure. This enables the recovery of polyethylene terephthalate bottles, etc. to be promoted.

The invention is a three-dimensional netted structure manufactured by preparing a brittleness-causing raw material-containing thermoplastic resin as a raw material or a main raw material; forming the resin into a plurality of helically and randomly entangled, partly and thermally bonded filaments by extrusion molding, and cooling the resultant filaments with a liquid so as to obtain a netted structure capable of being brittle fractured by applying an external force thereto. This enables a shock occurring due to the collision of a vehicle to break the texture of the three-dimensional netted structure, so that damage to a vehicle due to the collision thereof can be prevented.

The invention is an apparatus for manufacturing a three-dimensional netted structure which is obtained by extruding molten filaments of a thermoplastic resin, a raw material or a main raw material downward from a die having a plurality of holes; having the filaments drop naturally between partly-submerged drawing-down units; when a three-dimensional netted structure is manufactured by drawing said filaments between said drawing-down units at a speed lower than a filament dropping speed, a distance between said drawing-down units being set smaller than a width of an assembly of said extruded filaments, said drawing-down units being arranged so that at least three or four surfaces of the assembly of said filaments contact said drawing-down units before or after said drawing-down units are submerged. This renders it unnecessary to carry out a finishing operation in a later stage, and enables the degree of straightness of the side surfaces of the netted structure to be heightened.

The invention is an apparatus for manufacturing a three-dimensional netted structure which is obtained by extruding molten filaments of a thermoplastic resin, a raw material or a main raw material downward from a die having a plurality of holes; having the filaments drop naturally between partly-submerged, slidable surface-carrying plate members a distance between which is set so as to decrease gradually in the downward direction; and drawing said resultant filaments between the plate members at a speed lower than a filament dropping speed, a distance between lower portions of the plate members being set smaller than a width of an assembly of said extruded filaments, at least one surface of the assembly of the filaments contacting the plate members before or after the plate members are submerged. This enables the miniaturization of the apparatus to be attained by reducing or omitting movable parts.

The invention is an apparatus for manufacturing a three-dimensional netted structure which is obtained by extruding molten filaments of a thermoplastic resin, a raw material or a main raw material downward from a die having a plurality of holes; having the filaments drop naturally between partly submerged drawing-down units; and drawing said filaments between said drawing-down units at a speed lower than a filament dropping speed, a distance between said drawing-down units being set smaller than a width of an assembly of said extruded filaments, at least one surface of the assembly of said filaments contacting the drawing-down units before or after said drawing-down units are submerged, a cross section of outer circumferential members of the drawing-down units being set to modified shapes. This enables an operation in a later stage to be omitted.

The invention is an apparatus for manufacturing a three-dimensional netted structure which is obtained by extruding molten filaments of a thermoplastic resin, a raw material or a main raw material downward from a die having a plurality of holes; having the filaments drop naturally between partly-submerged drawing-down units; and drawing said filaments between said drawing-down units at a speed lower than a filament dropping speed, a distance between said drawing-down units being set smaller than a width of an assembly of said extruded filaments, at least one surface of the assembly of said filaments contacting said drawing-down units before or after said drawing-down units are submerged, said die being provided with a complex die which has not smaller than two chambers and a plural-hole-carrying mouthpiece, the molten filaments of a thermoplastic resin, a raw material or a main raw material being extruded downward from the holes of said mouthpiece via different passages isolated from one another by partitions. This enables a separable three-dimensional netted structure to be manufactured.

The invention is an apparatus for manufacturing a three-dimensional netted structure which is obtained by extruding molten filaments of a thermoplastic resin, a raw material or a main raw material downward from a die having a plurality of holes; having the filaments drop naturally between partly-submerged drawing-down units; and drawing said resultant filaments between said drawing-down units at a speed lower than a filament dropping speed, a distance between said drawing-down units being set smaller than a width of an assembly of said extruded filaments, at least one surface of the assembly of the filaments contacting the drawing-down units before or after the drawing-down units are submerged, the drawing-down units being provided with circumferentially moving members, which are provided at circumferences thereof with circumferentially extending metal nets or plate members. This enables the durability of the drawing-down units to be improved.

The invention is an apparatus for manufacturing a three-dimensional netted structure which is obtained by extruding molten filaments of a thermoplastic resin, a raw material or a main raw material downward from a die having a plurality of holes; having the filaments drop naturally between partly-submerged drawing-down units; and drawing said filaments between said drawing-down units at a speed lower than a filament dropping speed, a distance between said drawing-down units being set smaller than a width of an assembly of said extruded filaments, at least one surface of the assembly of the filaments contacting said drawing-down units before or after said drawing-down units are submerged, regions of a high density of holes and regions of a low density of holes being formed on a mouthpiece of said die. This enables the range of designing of the apparatus to be widened.

The invention is a method of manufacturing a three-dimensional netted structure, the method being applied to the inventions described.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of a three-dimensional netted structure of a first mode of embodiment of the present invention;

FIG. 2A is a longitudinal sectional view of the three-dimensional netted structure of the first mode of embodiment of the present invention;

FIG. 2B is a longitudinal sectional view of a three-dimensional netted structure of a second mode of embodiment of the present invention;

FIG. 2C is a longitudinal sectional view of a three-dimensional netted structure of a fourth mode of embodiment of the present invention;

FIG. 2D is a longitudinal sectional view of a three-dimensional netted structure of a fifth mode of embodiment of the present invention;

FIG. 2E is a longitudinal sectional view of a three-dimensional netted structure of a sixth mode of embodiment of the present invention;

FIG. 2F is a longitudinal sectional view of a three-dimensional netted structure of a seventh mode of embodiment of the present invention;

FIG. 2G is a longitudinal sectional view of a three-dimensional netted structure of an eighth mode of embodiment of the present invention;

FIG. 3A is a longitudinal sectional view of the three-dimensional netted structure of a ninth mode of embodiment of the present invention;

FIG. 3B is a side view of the three-dimensional netted structure of the ninth mode of embodiment of the present invention;

FIGS. 4A to 4G are sectional views of a three-dimensional netted structure of a third mode of embodiment of the present invention;

FIG. 5 is a perspective view of an apparatus for manufacturing the three-dimensional netted structure of the first mode of embodiment;

FIG. 6 is an explanatory drawing showing the condition of an operation of the apparatus for manufacturing the three-dimensional netted structure of the first mode of embodiment;

FIGS. 7A and 7B are a side view and a front view of endless conveyors in the same apparatus for manufacturing the three-dimensional netted structure;

FIGS. 8A to 8F are side views of modified modes of endless conveyors in the same apparatus for manufacturing the three-dimensional netted structure;

FIG. 9A is a plan view of endless conveyors for an apparatus for manufacturing a four-surface-molded three-dimensional netted structure;

FIG. 9B is a side view of the same apparatus for manufacturing the three-dimensional netted structure;

FIG. 9C is a side view of another mode of the apparatus for manufacturing a four-surface-molded three-dimensional netted structure;

FIG. 9D is a plan view showing the condition of a four-surface molding operation carried out by the same apparatus for manufacturing the three-dimensional netted structure;

FIG. 9E is a plan view showing the condition of a three-surface molding operation carried out by the same apparatus for manufacturing the three-dimensional netted structure;

FIG. 10A is a plan view of endless conveyors in an apparatus of an independent driving system for manufacturing a four-surface-molded three-dimensional netted structure;

FIG. 10B shows endless conveyors provided with sliding plates at end surfaces thereof in an apparatus for manufacturing a three-dimensional netted structure;

FIGS. 11A to 11H are plan views and a front view showing various modes of mouthpieces of a die;

FIGS. 12A and 12B are front views of modified modes of endless conveyors, which are used for carrying out a four-surface molding operation, in an apparatus for manufacturing a three-dimensional netted structure;

FIG. 13A is a longitudinal sectional view of a three-dimensional netted structure of a tenth mode of embodiment;

FIG. 13B is a longitudinal sectional view of a three-dimensional netted structure of an eleventh mode of embodiment;

FIG. 13C is a longitudinal sectional view of a three-dimensional netted structure of a twelfth mode of embodiment;

FIG. 13D is a longitudinal sectional view of a three-dimensional netted structure of a thirteenth mode of embodiment;

FIG. 14A is a longitudinal sectional view of a three-dimensional netted structure of a fourteenth mode of embodiment;

FIG. 14B is a longitudinal sectional view of a three-dimensional netted structure of a fifteenth mode of embodiment;

FIG. 14C is a longitudinal sectional view of a three-dimensional netted structure of a sixteenth mode of embodiment;

FIG. 15 is a perspective view of the second mode of embodiment of the apparatus for manufacturing a three-dimensional netted structure;

FIG. 16A is a horizontal sectional view showing the portion of a mode of embodiment of the apparatus for manufacturing a three-dimensional netted structure according to the present invention which is in the vicinity of an upper part of a mouthpiece of a complex die;

FIG. 16B is a front view of a lower portion of the complex die;

FIGS. 17A and 17B are explanatory drawings of modified modes of the second mode of embodiment of the apparatus for manufacturing a three-dimensional netted structure;

FIGS. 18A, 18B and 18D are plan views showing various modes of mouthpieces of dies;

FIG. 18C is a front view FIG. 18D;

FIGS. 19A to 19D are plan views showing various modes of the mouthpieces of the dies;

FIG. 20 is an explanatory drawing showing the condition of an operation of the third mode of embodiment of the apparatus for manufacturing a three-dimensional netted structure.

FIGS. 21A and 21B are side views and front views of rolls in the same apparatus for manufacturing a three-dimensional netted structure;

FIGS. 22A to 22G are side views of modified modes of rolls in the same apparatus for manufacturing a three-dimensional netted structure;

FIG. 23A is a front view of the three-dimensional netted structure (applied to a gardening cushioning material and the like) of the seventeenth mode of embodiment;

FIG. 23B is a plan view of the same three-dimensional netted structure;

FIG. 23C is a side view of the same three-dimensional netted structure;

FIG. 23D shows a modified mode of the three-dimensional netted structure;

FIG. 24A is a plan view of a mouthpiece of a die in the fourth mode of embodiment of the apparatus for manufacturing a three-dimensional netted structure;

FIG. 24B is a front view of the same;

FIG. 24C is a plan view of a mouthpiece of another die;

FIG. 24D is a front view of the same;

FIG. 25 is an explanatory drawing showing the condition of use of the seventeenth mode of embodiment of the three-dimensional netted structure;

FIG. 26 is an explanatory drawing showing the condition of another use of the seventeenth mode of embodiment of the three-dimensional netted structure; and

FIG. 27 is a construction diagram of a part of the fourth mode of embodiment of the apparatus for manufacturing a three-dimensional netted structure.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

As shown in FIGS. 1 and 2A, a three-dimensional netted structure 1 of the first mode of embodiment is a three-dimensional netted structure the characteristics of which reside in that the structure is a three-dimensional plate type netted structure formed out of a regenerated thermoplastic resin as a raw material or a main raw material, in which a plurality of filaments are helically and randomly entangled and partly and thermally bonded together and have two side surfaces, left and right end surfaces and upper and lower end surfaces. It is preferable that the density of surface-side portions of three surfaces out of the side surfaces of this three-dimensional netted structure be relatively higher than that of the portion exclusive of the mentioned surface-side portions. Namely, the three-dimensional netted structure 1 (refer to FIG. 2A) of the first mode of embodiment is three-surface-molded. In this structure, regions thereof which extend inward from the opposite surfaces thereof by a predetermined distance are molded to a high density, and the density of a region which extends in a central inner portion of the netted structure is set lower than the mentioned density. Thus, the remaining one surface of the structure has a non-straight extending surface. Therefore, this netted structure has an advantage in being not subjected to a process in a later stage. In short, a pair of surfaces of a large width and one side surface are forcibly molded by endless conveyors and the like which will be described later, and the edges of these surfaces are formed more beautifully than that of the other surface.

In this embodiment, flaked or chipped PET bottles are used as a raw material or a main raw material of the regenerated thermoplastic resin. The raw material is obtained by pulverizing PET bottles as they are, melting the pulverized products, and forming the molten product into flakes. This material is suited to the recycling promoting age. When the material is not a recycled product but a genuine product, the manufacturing cost per 1 m²of the netted structure increases double due to the dry crystallization of or the removal of waste from the material. The material used in this embodiment can exercise its power in the reduction of the product scrapping cost. However, this embodiment can also be applied to a thermoplastic resin and the like other than regenerated materials of this kind. For example, polyolefines, such as polyethylene, polypropylene, etc., polyesters, such as polyethylene terephthalate, etc. polyamides, such as nylon 66, etc, polyvinyl chloride, polystyrene, a copolymer and an elastomer obtained by copolymerizing these resins as base materials, a material obtained by blending these resins, and some other similar materials. The three-dimensional netted structure, is used mainly as a cushioning material, a shock absorbing material, a moisture absorbing material, a sound absorbing material (to be provided under a floor material, in an inner portion of a structure and inside a wall), a heat insulating material (inner and outer heat insulating purposes), a wall surface material, a roof gardening material, a concrete and mortar cracking preventing material, interior finishing material for automobiles, and has some other uses. This netted structure can also be applied to an inner portion of a double wall.

When a fire resistant material is mixed with the three-dimensional netted structure by holding the three-dimensional netted structure between nonwoven cloths or by attaching such cloths thereto, and applying fire resistant paint to the netted structure, so as to give fire resistance to the three-dimensional netted structure, the resultant netted structure becomes more preferable as a heat insulating building material, a sound absorbing building material and the like.

This first mode of embodiment is molded so as to have a substantially uniform density at an inner portion thereof. The apparent density of this embodiment is preferably 0.02 to 0.9 g/cm³(corresponding to a percentage of void of 36 to 98.4%), and specially preferably 0.05 to 0.15 g/cm³. The three-dimensional netted structure 1 preferably has, for example, a width of 0.1 m to 2 m and a thickness of 5 mm to 200 mm, and extends endlessly in the lengthwise direction. The netted structure is cut to a suitable length (for example, 90 mm) but the sizes of the netted structure are not limited to the examples mentioned above.

A three-dimensional netted structure 2 (refer to FIG. 2B) of the second mode of embodiment is four-surface-molded, and all the surfaces of the netted structure extend straight. This netted structure is formed so that the density of the regions thereof which correspond to those of the three-dimensional netted structure 1 of the first mode of embodiment, and which extend inward from the left and right surfaces of the netted structure toward an inner portion thereof by a predetermined distance, becomes high, and so that the density of the region of the netted structure which is at a central inner portion thereof be set lower than the mentioned density. Namely, the regions of the netted structure which extends from all the surfaces thereof except the upper and bottom surfaces thereof to an inner portion of the netted structure by a predetermined distance are molded to a density higher than the above-mentioned density.

A three-dimensional netted structure 3 of the third mode of embodiment has a surface of modified shapes or a polyhedral surface. This type of netted structures include, for example, a netted structure 3A (refer to FIG. 4A) provided with a convex surface, a netted structure 3B (refer to FIG. 4B) provided with a concave surface, a netted structure 3C (refer to FIG. 4C) provided with a plurality of continuously formed projecting and recessed portions, a netted structure 3D (refer to FIG. 4D) provided with a plurality of saw-tooth-like portions, a netted structure 3E (refer to FIG. 4E) provided with a plurality of wavy portions, a netted structure 3F (refer to FIG. 4F) provided with rounded corner portions, a netted structure 3G (refer to FIG. 4G) provided with cut corner portions of a predetermined angle (45°), or a suitable combination thereof, etc. In a job site of the execution of construction work, various modes of netted structures are demanded as products, and this embodiment can meet a demand for such netted structures. It is considered that forming netted structures of complicated shapes causes various uses thereof to be newly found. Especially, forcibly molding three or four surfaces of the three-dimensional netted structure as in the above-described first and second modes of embodiment enables the various demands for the products to be met. Furthermore, in order to obtain netted structures having demanded miscellaneous surface shapes, netted structures are generally cut or molded so as to provide surfaces of modified shapes thereon on a later stage. According to this mode of embodiment, products can be provided instantly without finishing the netted structure as to the shape and sizes, which the products demand, on a later stage, so that a later stage can be rendered unnecessary.

The three-dimensional netted structure 4 (refer to FIG. 2C) of the fourth mode of embodiment is provided with a single or a plurality (two in this embodiment) of hollow portions 4A, 4B, and aims at further reducing the manufacturing cost.

The three-dimensional netted structure 5 (refer to FIG. 2D) of the fifth mode of embodiment has regenerated members 5C, 5D of the same or different materials, such as plate type regenerated veneer members, plate type members of regenerated shredder dust and the like inserted in hollow portions 5A, 5B identical with the hollow portions 4A, 4B of the three-dimensional netted structure of the fourth mode of embodiment. This embodiment aims at improving the sound absorbability, heat insulating characteristics, cushioning characteristics and the like of the netted structure by using regenerated plate members.

In the three-dimensional netted structure 6 (refer to FIG. 2E) of the sixth mode of embodiment, the sound absorbing characteristics, heat insulating characteristics, cushioning characteristics and impact resistance thereof are improved by increasing the density of parts of the inner portion of the same three-dimensional netted structure 1 as in the first mode of embodiment in the direction of the thickness thereof, and thereby partly forming a single or a plurality (three in the sixth embodiment) of beam-like high-density regions 6A, 6B and 6C at predetermined intervals.

In the three-dimensional netted structure 7 (refer to FIG. 2F) of the seventh mode of embodiment, the sound absorbing characteristics, heat insulating characteristics, cushioning characteristics and impact resistance thereof are improved by increasing the density of parts of the inner portion thereof in the widthwise direction thereof, and thereby partly forming a plurality (one in this embodiment) of or a single high-density region 7A.

In the three-dimensional netted structure 8 (refer to FIG. 2G) of the eighth mode of embodiment, the sound absorbing characteristics, heat insulating characteristics, cushioning characteristics and impact resistance thereof are improved by forming a wavy high-density region 8A in an inner portion of the same three-dimensional netted structure as in the seventh mode of embodiment.

In the three-dimensional netted structure 9 (refer to FIG. 3A) of the ninth mode of embodiment, the sound absorbing characteristics, heat insulating characteristics, cushioning characteristics and impact resistance thereof are improved by forming a sheet 9A (non-void-carrying region) in a predetermined widthwise extending inner portion of the same three-dimensional netted structure as those 1, 2. Around the sheet 9A, filaments (resin threads) are entangled with one another. The sheet 9A may be provided fully in the lateral direction as shown in the drawing, and also partly, for example, in the central portion and the like.

The sheet 9A in the three-dimensional netted structure 9 (refer to FIG. 3B) of the ninth mode of embodiment is wave form in general and the sound absorbing characteristics, heat insulating characteristics, cushioning characteristics and impact resistance of the netted structure are improved. The reason why the sheet 9A can be molded in wave form resides in that a draw-down speed of rolls is lower than a resin thread dropping speed as will be described later. The intervals, height and width of the waves of the sheet 9A differ depending upon the manufacturing conditions, and are not limited to those shown in the drawing. When the intervals of the waves of the sheet 9A are small, the waves are bonded to one another in some cases. The ninth mode of embodiment can be manufactured by using a slit (linear through hole) 75a shown in FIG. 11E.

Although illustrations are omitted, the present invention can also be applied to three-dimensional netted structures of modified cross-section shapes, such as a triangular cross-section shape, a Y-type cross-section shape and the like.

(Apparatus for Manufacturing a Three-Dimensional Netted Structure)

An apparatus 10 for manufacturing a three-dimensional netted structure will now be described.

This apparatus 10 for manufacturing a three-dimensional netted structure includes as shown in FIG. 5. an extrusion molding machine 11, a pair of endless conveyors 14, 15 (refer to FIG. 7) provided with endless members 12, 13, a motor 16 adapted to drive the endless members 12, 13, a transmission 17 formed of a chain and a gear and adapted to change a moving speed of the endless members 12, 13, a water tank 18 adapted to partly submerge the two endless conveyors 14, 15 therein, a control unit 19, and other meters, etc.

The endless members 12, 13 are formed by fixing with screws (not shown) a plurality of metal (stainless steel and the like in this embodiment) plate members 21 to a plurality (two for each conveyor) of endless chains 12a, 13a (refer to FIGS. 7A and 7B) with a predetermined width of clearance 22 (refer to FIG. 8A) left therebetween. Instead of these plate members, a belt 23 of a stainless steel mesh (metal net) which does not have the clearance 22 may also be used as shown in FIG. 8B. This mesh belt is formed by combining spiral wires with rods (power ribs), and various types of mesh belts are formed by varying the shapes, diameters and pitch of these two elements. Such mesh belts move smoothly, keep the smooth belt surfaces horizontal excellently, stand use in hot temperature condition excellently, and are repaired simply. As shown by dotted lines in FIG. 7, stainless mesh belts 23 passed around outer circumferences of the endless members 12, 13 can also be used in practice, and are preferably used when it is desirable to prevent the occurrence, which is ascribed to the presence of the clearance 22, of recessed and projecting portions on the mesh belt. The cross section of the plate member 21 is rectangular, and various modified modes of plate members 21 are conceivable which include a convex plate member 24 (refer to FIG. 8C), a concave plate member 25 (refer to FIG. 8D), a saw-tooth plate member 26 (refer to FIG. 8E), a continuously recessed and projecting plate member 27 (refer to FIG. 8F), etc.

As shown in FIG. 7, the endless conveyor 14 is provided with a driving shaft 14b having a sprocket 14a around which the endless chain 12a provided vertically is passed, and a driven shaft 14d having a sprocket 14c. The endless conveyor 15 is driven synchronously with the endless conveyor 14, and provided with a driven shaft 15b mounted with a sprocket 15a around which the endless chain 13a is passed, and a driven shaft 15d mounted with a sprocket 15c.

As shown in FIG. 5, the extrusion molding machine 11 includes a container 31, a raw material feed port 32 provided on an upper portion of the container 31, a die 33, a mouthpiece 34 capable of being fixed detachably to a lower end portion of the die 33. A range of the temperature in an inner portion of the die of the extrusion molding machine 11 can be set to 100 to 400° C., and an extrusion rate of the machine 20 to 200 Kg/hr and the like. A range of the pressure in the die is 0.2 to 25 MPa, which is equal to, for example, a discharge pressure of a 75 mm screw. When the thickness of the three-dimensional netted structure exceeds 100 mm, the equalization of the pressure in the die by a gear pump and the like is needed in some cases. Therefore, it becomes necessary that the pressure in the die be increased by a gear pump and the like so as to discharge filaments uniformly from the whole region of the interior of the die. To meet the requirement, the surfaces of the endless conveyors 14, 15 are formed so that these surfaces can be moved freely so as to set the shape of a three-dimensional netted sheet. This enables a product having desired density and strength to be manufactured in accordance with the shape (density or diameter of the holes H) of the mouthpiece 34 of the die 33 and a transfer speed of the endless conveyors 14, 15, and various demands for the products to be met.

An apparatus 50 for manufacturing a three-dimensional netted structure which is made of such a four-surface-molding machine as shown in FIGS. 9A and 9B will now be described. This apparatus 50 for manufacturing a three-dimensional netted structure is provided with endless conveyors 54, 55 having rotary shafts 54a, 55a which correspond to the endless conveyors 14, 15 used in a two-surface-molding operation shown in FIG. 7, and a pair of rolls 56, 57 disposed at lengthwise end portions of the endless conveyors 54, 55 and having rotary shafts 56a, 57a extending at right angles to the shafts of the endless conveyors. The rotary shaft 54a is mounted with bevel gears 54b, 54c, while the rotary shafts 56a, 57a are also mounted with bevel gears 56b, 57b. The bevel gears 54b, 54c and the bevel gears 56b, 57b are meshed with each other, and the rotary shafts 54a, 55a are driven synchronously by a motor M via a chain C. Therefore, the rotary shafts 56a, 57a are also driven synchronously. The other end portions of the rotary shafts 56a, 57a are supported on bearings 58a, 58b.

As shown in FIG. 9C, the apparatus may be an apparatus formed by arranging a pair of short endless conveyors 59a, 59b, the construction of which is identical with the endless conveyors 54, 55, at right angles to rotary shafts of rolls. In this case, the molding of a product can be done more precisely, and the dimensional accuracy of a product is improved.

As shown in FIG. 9D, the manufacturing of a three-dimensional netted structure can be done by using four-surface-molding techniques. The three-surface-molding of the product can also be done by using the mentioned techniques as shown in FIG. 9E. Namely, when a certain type of three-dimensional netted structure is manufactured, two systems of dies are provided, and filaments are extruded in parallel. As a result, the productive efficiency of the netted structure doubles.

As shown in FIG. 10A, an apparatus of a modified mode can be also used which is formed by providing driving power sources (motors) instead of the previously-mentioned synchronous driving system so that endless conveyors 64, 65 and rolls 66, 67 (endless conveyors also serve the purpose) are driven independently of each other. Namely, in order to carry out three-surface or four-surface-molding operation, endless conveyors 64, 65 having rotary shafts 64a, 65a, and a pair of rolls 66, 67 arranged at lengthwise end portions of these endless conveyors 64, 65, and having rotary shafts 66a, 67a extending at right angles to those of the endless conveyors are provided. The rotary shafts 66a, 67a are also provided with respective motors M so that these rotary shafts are driven independently of each other. The other end portions of the rotary shafts 66a, 67a are supported on bearings 68a, 68b.

As shown in FIG. 10B, which shows another modified mode of the apparatus, in which a driving mechanism can be simplified by removing such two rolls 66, 67, two rotary shafts 66a, 67a, two bearings 68a, 68b and two motors M as are provided in the preceding example, and providing sliding curved plates 69a, 69b, the surfaces of which are coated with polytetrafluoroethylene, in positions in which the rolls 66, 67 were placed. These curved plates 69a, 69b are arcuate in side elevation and positioned so that a distance between these curved plates decreases gradually from upper portions thereof toward lower portions thereof. The curved plates are formed to a rectangular shape in plan.

The holes of the mouthpiece 34 are downwardly made in series, from which filaments come out downward. The holes may be arranged at regular intervals or at non-regular intervals. The holes may employ staggered, orthogonal and various other types of configurations. When it is desired that the arrangement density of the holes be changed, a method of positively increasing the arrangement density thereof in end regions only is used in some cases. Changing the mode of the mouthpiece variously enables various demands for the products to be met. Mouthpieces of a multiplicity of specifications can be used practically which include, for example, a mouthpiece 71 (having holes H accounting for 90% of the area of the mouthpiece 71)(refer to FIG. 11A) of 1.0 m×180 mm in which about 3500 holes H of 0.5 mm in diameter are made, a mouthpiece 72 (refer to FIG. 11B) in which the density of the holes H is set high only in a circumferential portion 72a thereof, a mouthpiece 73 (refer to FIG. 11C) in which the density of the holes H of frame-forming portion 73b is increased so that the frame-forming portion constitutes series-connected frames, a mouthpiece 74 (refer to FIG. 11D) in which slits (linear through holes) 74a to 74c in addition to a multiplicity of holes H are formed so that the slits extend in parallel with shorter sides of the mouthpiece, a mouthpiece 75 (refer to FIG. 11E) in which a slit (linear through hole) 75a in addition to a multiplicity of holes H is formed so that the slit extends in the lengthwise direction of the mouthpiece, a mouthpiece 76 (refer to FIG. 11F) and the like in which a slit (linear through hole) 76a in addition to a multiplicity of holes H is formed so that the slit extends in a position near a lengthwise side of the mouthpiece, and similar other mouthpieces, and a mouthpiece 77 (refer to FIGS. 11G and 11H) and the like which have regions 77c, 77d not provided with the holes H so as to make hollow portions therein, and which is provided under these regions with cross-section square introduction members (pipes, etc.) 77a, 77b projecting downward therefrom. The density of the holes H formed in these mouthpieces is preferably 1 to 5/cm².

(Method of Manufacturing a Three-Dimensional Netted Structure)

This three-dimensional netted structure 1 is manufactured in the following manner. First, flakes of regenerative PET bottles are heated and dried for preventing the same from being hydrolyzed, and chemicals for excellently finishing the resultant product, or an antibacterial agent and the like are added suitably to the same product in some cases. When filaments come out flat from the mouthpiece 34 in the downward direction, the filaments are entangled helically owing to the entangling actions of the endless members 12, 13 of the endless conveyors 14, 15. The filaments start being entangled at the portions thereof which contact the surfaces of the endless members 12, 13 at the entangling-starting time. The density of the portions of the filaments which are entangled is high, and that of the portions thereof which are not entangled is low.

Next, as shown in FIG. 6, a three-dimensional netted structure 1, an object netted structure is manufactured by extruding a molten thermoplastic resin downward from a plurality of dies 33, having the extruded filaments of the resin drop naturally to a position between a pair of partly submerged endless conveyors 14, 15, and drawing down the filaments of the resin at a speed lower than the filament dropping speed. When this netted structure 1 is thus manufactured, the two endless conveyors 14, 15 are arranged so that a distance between the endless conveyors is set smaller than a width of an assembly of the extruded filaments of the molten resin, and so that both or one surface of the assembly of the filaments of the molten resin contacts the endless conveyors 14, 15 before or after these conveyors are submerged.

Both or one of the surface portion of the assembly of the molten thermoplastic resin drops on the endless conveyors 14, 15, and moves to an inner side of the assembly, so that the surface portion of the assembly becomes dense. Therefore, the percentage of void of the surface portion becomes lower than that of a central portion which drops as it is into the water. It is a matter of course that the surface portion in which the percentage of void becomes low comes to have an increased number of nodes as compared with the central portion having a high percentage of voids, and that the tensile strength of the surface portion becomes noticeably high. The surface portion having a low percentage of void comes to have a small area of voids, and forms an impact absorbing layer and a soundproofing layer.

A result showing that a percentage of void of the three-dimensional netted structure 1 as a whole high enough to have the netted structure function well is in the range of 50% to 98%, though these levels differ with the condition of execution of works on a job site was obtained. In short, it is considered that, when the density of the netted structure is high, sounds are blocked. A result showing that, in order to have the three-dimensional netted structure function as a recycled sound absorbing building material, a cushioning material, a heat insulating material and the like, the percentage of void thereof may be set preferably to not lower than 70% was obtained. In short, when the percentage of void is lower than 70%, the impact absorbing effect, soundproofing effect, heat insulating effect and cushioning characteristics of the netted structure are not in some cases so improved as was expected. It is recommended that the three-dimensional netted structure 1 may be designed suitably with the percentage of void set in the range of 70% to 98% in accordance with the use of the netted structure.

A sound absorbing material and a cushioning material have a preferable percentage of void of 85 to 98%, an impact absorbing material to be provided under a floor 40 to 80%, and a collision-preventing impact absorbing material 60 to 90%. A preferable range of the percentage of void varies with the use of the netted structure.

The percentage of void=100−{(B÷A)×100}, wherein A represents a product of the specific gravity of the resin and the volume of the three-dimensional netted structure; and B represents the weight of the netted structure.

The thermoplastic resin used in this method is obtained by pulverizing PET bottles into flakes, which are used as a raw material or a main raw material. However, resins including a polymer, such as polypropylene, etc. or a resin obtained by blending a plurality of kinds of polymers together, etc. may be used as a main raw material without trouble as long as the resin can be processed by a regular extrusion molding machine.

In the step of forming three-dimensional netted structures to final modified shapes, a mechanism for equalizing the inner pressure of the dies, and drawing down an assembly of filaments at two, three or four surfaces thereof or at an intermediate portion thereof is used. This enables such characteristics to be given to this netted structure manufacturing method that include its capability of attaining an apparent density of a product of 0.02 to 0.9 g/cm³, changing the filaments of the molten resin from a randomly and helically entangled state into a state of a flat plate, and turning the surface portions of the three-dimensional netted structure including the front, rear, left end and right end surfaces with respect to the direction of the thickness thereof into flat surfaces and surfaces of modified shapes, i.e. projecting and recessed surfaces. The mouthpiece of a die used to form the three-dimensional netted structure is made so that a netted structure of a rod type shape, modified shapes (shape of a pipe and a shape of the letter “Y”), etc. and a netted structure of various other shapes devised by combining these shapes together can be obtained. The three-dimensional netted structure is subjected to compression by the rolls of a draw-down machine to obtain a super-dense sheet structure. The inner pressure of the dies used to have the regenerated PET resin discharged uniformly from the dies is equalized, and the three or four surfaces of an assembly of filaments of a molten resin extruded when the three-dimensional netted structure is manufactured is brought into contact with the draw-down conveyors by which these surfaces are shaped. In short, the assembly of filaments of the molten regenerated PET resin is formed at the three or four surfaces thereof to shapes of a final product. For example, a resin filament assembly is drawn up as necessary around polygonal conveyors to form a product. In one of the methods of obtaining a three-dimensional netted sheet, filaments of a molten resin are extruded downward from a plurality of dies, and dropped naturally onto water surface or to a position between partly-submerged conveyors. Thus, a randomly and helically entangled filament assembly is made, which forms a three-dimensional netted sheet.

It was ascertained that, when the speed of the endless conveyors was varied, the density of a sheet of 1.0 m in width and 100 mm in thickness varied.

It was further ascertained that the density of the sheet varied in accordance with the variation of a discharge rate of the extruder.

The mouthpiece 34 having about 3500 substantially regularly spaced holes H of 0.5 mm in diameter was fixed to the dies 33 having an area of 1.0 m×180 mm in a uniaxial extruder having a screw of 75 mm in diameter. The water tank 18 having a water level in a position about 120 mm below the dies 33 is provided, and a pair of endless conveyors 14, 15 of 1.2 m in width were installed substantially vertically in the tank with a clearance of 50 mm left therebetween, in such a manner that upper portions of the endless conveyors project upward from the water level by around 40 mm.

In this apparatus, the molten resin filament assembly was extruded from the mouthpiece 34 at an extrusion rate of 120 kg/hr to a position between the endless conveyors 14, 15 so that two surfaces of the molten resin filament assembly dropped on the endless conveyors, by controlling the temperature of the dies 33 so that the temperature of the resin became 240° while plasticizing a regenerated PET resin by heating the same. During this time, the draw-down speed of the endless conveyors 14, 15 was set to 0.7 m/min. The molded product held between the endless conveyors 14, 15 and moved down changed its direction in a lower portion of the interior of the water tank 18, and was moved from the side of the water tank which is opposite to the extruder to the water surface. When the molded product came out of the water tank 18, the water thereon was blown off with compressed air or by a vacuum pump.

The three-dimensional netted structure thus obtained had a width of 1.0 m, a thickness of 50 mm, and a density of 0.07 g/cm³to 0.14 g/cm³. This netted structure may be used as a heat insulating material, a ground material, and a sound absorbing material, and for a drain pipe, etc.

The above-described three-dimensional netted structure 1 and apparatus 10 for manufacturing the same netted structure enable a finishing operation on a later stage to be omitted, the degree of straightness of surfaces of the netted structure to be improved, a demand for a netted structure having modified shapes to be met, and the durability of the netted structure to be improved.

Owing to this mode of embodiment, the PET bottles which do not have uses in the existing circumstances newly find a use as materials for a three-dimensional netted structure, and it is considered that a recovery percentage of the PET bottles will increase. This causes the recycling of the PET bottles to be greatly promoted.

FIG. 12 shows a modified mode of the apparatus 50 for manufacturing a four-surface-molded three-dimensional netted structure, and FIG. 12A is a drawing corresponding to FIG. 9B and shows a pair of rolls 56, 57 as described above which have a single or a plurality of projections 90a to 90c on the respective surfaces thereof (the illustrations of the roll 57 and its projections are omitted). These projections are formed so as to provide recesses in side surfaces of the three-dimensional netted structure. Each of the projections 90a to 90c has angular portions and an arcuate side portion in cross section. Although the recesses referred to above and formed in the side surfaces of the netted structure ought to become rectangular theoretically, the recesses become curvilinear since the resin filaments drop into the space between the endless conveyors from above as above-mentioned, to cause blind regions in which the resin filaments do not enter to occur. In short, the recesses become roundish. FIG. 12B corresponds to FIG. 9C, and shows endless conveyors (the illustrations of the endless conveyor 55 and its projections are omitted) formed by providing a single or a plurality of projections 96 on the surfaces of two endless belt conveyors like those of the above-mentioned belt conveyors 54, 55, etc. This modified apparatus can also be formed by incorporating cams and springs in the rotary bodies, such as the above-mentioned rolls 56, 57 or endless conveyors 54, 55 so that the projections are forced out in the outward direction by the cams synchronously with the rotations of the rotary bodies. This enables the occurrence of blind regions to be reduced, and more precise recesses to be formed. Since the construction of the other parts is identical with that of the corresponding parts of the apparatus shown in FIGS. 9B and 9C, the illustrations and description of the latter will be utilized and quoted.

A second mode of embodiment will now be described. The demands for the recycling of the products of the three-dimensional netted structures have become diversified, and cannot be met under the present circumstances in some cases. For example, when it is desired that a mixture of not smaller than two kinds of regenerated resins be utilized, some of these raw materials prove separable during recycling operations therefor, and some non-separable. In a scene of labor for recycling raw materials, non-separable raw materials are sometimes mixed in a starting material, and the recycling and utilizing of raw materials actually become impossible in some cases in spite of the effort made to recycle the materials. There are various cases where the same raw material is used for a certain purpose, which include a case where changing the shape of a product is desired, such as a case where forming sparse and dense regions is desired, a case where forming hollow portions on a later stage is desired and similar cases, or a case where improving the moldability of the materials is desired.

Therefore, this mode of embodiment is carried out so as to prevent troubles from occurring in the regeneration of a thermoplastic resin, and attain the easiness of changing the shape of a product.

A three-dimensional netted structure 101 of a tenth mode of embodiment is a plate type three-dimensional netted structure, the characteristics of which reside in that the netted structure is formed by using a regenerated thermoplastic resin as a raw material or a main raw material, and has a plurality of filaments helically and randomly entangled and partly and thermally bonded together as shown in FIG. 13A. This netted structure is made of an inner region 101a and an outer region 101b of the same or different raw materials. A boundary between the inner region 101a and outer region 101b is shown by a solid line. The solid line is an imaginary line showing the boundary, and the same applies to the other modes of embodiment which will be described later. It is preferable that the densities of two, three or four surface portions of this three-dimensional netted structure may be relatively higher than that of the portion of the netted structure which is exclusive of these surface portions. Namely, the three-dimensional netted structure 101 (refer to FIG. 13A) of the tenth mode of embodiment is two-surface-molded. This netted structure is molded so that the density of regions thereof which extend from the opposite surfaces thereof toward an inner portion thereof by a predetermined distance is high. The density of an inner part of the central portion thereof is set lower than the mentioned density, and the other non-surface-molded surfaces are not straight-formed. Therefore, it becomes unnecessary that this netted structure may be processed on a later stage. In short, a pair of surfaces of a large width and one side surface of the netted structure are forcibly molded by endless conveyors which will be described later, and edges of these surfaces are set more beautifully than those of the other surfaces.

A three-dimensional netted structure 102 (refer to FIG. 13B) of an eleventh mode of embodiment is a three-surface-molded netted structure, in which all the surfaces except the end surfaces and one side surface are set straight. The regions extending from all the surfaces of the netted structure except the right side surface thereof toward an inner portion thereof by a predetermined distance are molded to a high density. This netted structure is made of an inner region 102a and an outer region 102b of the same or different raw materials.

A three-dimensional netted structure 103 (refer to FIG. 13C) of a twelfth mode of embodiment is four-surface-molded, in which all the surfaces thereof except an end surface thereof are set straight. This netted structure is formed by molding the regions, which extend from the left and right side surfaces of the same netted structure as that of the first mode of embodiment to the inner part of the central portion thereof by a predetermined distance, to a high density with the density of the region in the inner part of the central portion of the netted structure set lower than the mentioned density. Namely, the regions extending from all the side surfaces of the netted structure toward the inner portion thereof by a predetermined distance are molded to a high density. This netted structure is made of an inner region 103a and an outer region 103b of the same or different raw materials.

A three-dimensional netted structure 104 (refer to FIG. 13D) of a thirteenth mode of embodiment is a three-dimensional netted structure provided with a single or a plurality of (one in this embodiment) hollow portions 104c, and formed for the purpose of further reducing the cost and for some other purposes. This netted structure is made of an inner region 104a and an outer region 104b of the same or different raw materials.

A three-dimensional netted structure 105 (refer to FIG. 14A) of a fourteenth mode of embodiment is formed of three layers of regions 105a, 105b and 105c of the same or different raw materials. The raw materials of all of the three layers of regions may be different. The raw materials of the regions 105a, 105c may be identical, and that of the region 105b may be different. The raw materials of the three layers of regions may be all identical. The netted structure is divided into three layers of regions 105a, 105b and 105c in the lengthwise direction thereof.

A three-dimensional netted structure 106 (refer to FIG. 14B) of a fifteenth mode of embodiment is made of two layers of regions 106a, 106b of the same or different raw materials. The raw material of the two layers of regions 106a, 106b may be different or identical. This netted structure is divided into two layers of regions 106a, 106b in the lateral direction thereof.

A three-dimensional netted structure 107 (refer to FIG. 14C) of a sixteenth mode of embodiment is made of two layers of regions 107a, 107b of the same or different raw materials. The raw materials of the two layers of regions 107a, 107b may be different or identical. The direction in which this netted structure is divided into these regions is that of the thickness of the netted structure unlike the direction in which the fourteenth and fifteenth modes of embodiment are divided.

In the embodiment shown in FIG. 3, a high-density sheet 9A (a substantially non-void-carrying filled region) can be provided partly in a predetermined position in the lateral direction in the embodiment by forming the sheet and the other region by different extrusion molding machines through different paths. The description of this embodiment will be quoted from that given previously with respect to the embodiment of FIG. 3.

Beside these netted structures, netted structures of modified cross-section shapes, such as a triangular shape, a shape of the letter “Y”, etc., the illustrations of which are omitted, can also be formed in practice. As mentioned above, when a raw material is supplied to not smaller than two regions provided on the mouthpiece, the regulation of the manufacturing conditions, such as the temperature of the raw material, extrusion rate of the filaments, etc. can be made easily.

An apparatus 110 for manufacturing a three-dimensional netted structure of a second mode of embodiment will now be described.

This apparatus 110 for manufacturing a three-dimensional netted structure include as shown in FIG. 15 an extrusion molding machine 111, a pair of endless conveyors 114, 115 provided with endless members 112, 113, a motor 116 for driving the endless members 112, 113, a transmission 117 formed of chains and gears and adapted to change the moving speed of the endless members 112, 113, a water tank 118 for submerging parts of the endless conveyors 114, 115 therein, a control unit 119 and meters, etc.

The description of endless members 112, 113, etc. will be described by quoting that given previously with respect to the first mode of embodiment.

As shown in FIG. 15, the extrusion molding machine 111 is formed of containers 131a, 131b storing therein the same or different raw thermoplastic resin materials, raw material supply ports 132a, 132b provided at upper portions respectively of the containers 131a, 131b, raw material supply pipes 133a, 133b connected to the containers 131a, 131b respectively, a complex die 135 (refer to FIG. 16) connected to the raw material supply pipes 133a, 133b via packings 134a, 134b, a mouthpiece 136 (refer to FIG. 16) detachably fixable to a lower end portion of the complex die 135, etc. The raw material supply pipe 133a branches at an intermediate portion thereof into a plurality of (four in this embodiment) pipe members striding over the raw material supply pipe 133b. The lower end portions of the branches of the raw material supply pipe 133a are arranged around that of the raw material supply pipe 133b. As shown in FIGS. 16A and 16B, the complex die 135 has a frame type partition wall 139 in an inner region of an outer frame 138 so that the interior of the complex die 135 is divided into two chambers 137a, 137b, i.e., the complex die is formed so that the same kind of raw material or two different kinds of raw materials supplied thereto via the raw material supply pipes 133a, 133b are not mixed with each other. Even when the raw material supplied through these supply pipes is the same, it is preferable to provide the partition wall 139 for the purpose of regulating the extrusion rates separately. The particular parts of the interior of the die of the extrusion molding machine 111 are formed by utilizing the corresponding parts of the first mode of embodiment. Although the raw material supply pipe 133a is made to branch into four members, the pipe may also be made to branch into a suitable number of members, such as two members (refer to FIG. 17A), three members (refer to FIG. 17B), etc.

A mouthpiece 136 has not smaller than two regions so that a raw material is supplied thereto separately. Therefore, the regulation of the extrusion speed or extrusion rate of filaments is made very easily, and the moldability of the raw material is improved remarkably. The details of a description of the mouthpiece will be given by quoting the corresponding parts of the description of the first mode of embodiment. In this embodiment, a mouthpiece 171 (the area of the region thereof which is provided with holes H accounts for 90% of a total area of the mouthpiece 171)(refer to FIG. 18A) having the holes at substantially regular intervals or at suitable intervals is used. In this mouthpiece 171, an inner region 171a and an outer region 171b are defined by a partition wall 171c shown by a broken line, and filaments of the same or different materials are extruded separately and independently from these regions correspondingly to raw material supply pipes 133a, 133b.

A mouthpiece 172 (refer to FIG. 18B) may also be used, in which an inner region 172a and an outer region 172b which are provided with a multiplicity of holes H are defined by a partition wall 172c shown by a broken line. The inner region 172a is formed in a deflected manner with respect to the outer region 172b so that the filaments corresponding to the inner region 172a are separated easily.

A mouthpiece 173 (refer to FIGS. 18C and 18D) may also be used. An inner region 173a and an outer region 173b which are provided with a multiplicity of holes H are defined by a partition wall 173c shown by a broken line. The inner region 173a is held between the pair of outer region 173b. In order to form hollow portions in this mouthpiece, regions 173d, 173e which do not have holes H are provided in the portions thereof which correspond to the hollow portions, and cross-section square introduction members (pipes and the like) 173f, 173g extending downward are provided on lower portions of the two regions.

A mouthpiece 174 (refer to FIG. 19A) may be also used, in which an upper region 174a, a central region 174b and a lower region 174c which are provided with a multiplicity of holes H are defined by partition walls 174d, 174e shown by broken lines to form three stages (three layers) of regions.

A mouthpiece 175 (refer to FIG. 19B) may be also used, in which an upper region 175a and a lower region 175b which are provided with a multiplicity of holes H are defined by a partition wall 175c shown by a broken line to form two stages (two layers) of regions.

A mouthpiece 176 (refer to FIG. 19C) may be also used, in which a left region 176a and a right region 176b which are provided with a multiplicity of holes H are defined by a partition wall 176c shown by a broken line to form two rows (two layers) of regions.

A mouthpiece 177 (refer to FIG. 19D) may be also used, in which a region 177a provided with a multiplicity of holes H, and a slit (linear hole) 177b formed in a suitable portion, such as a central portion, etc. so as to extend parallel to a predetermined direction (lengthwise direction in this example) are defined by partition walls 177c shown by broken lines. The slit 177b exists in a region between the partition walls 177c shown by broken lines. The width, length or position of the slit (linear hole) 177b can be suitably selected. When a raw material is supplied from the same die to the region 177a having many holes H and slit (linear hole) 177b, the wavy form of FIG. 3B is deformed, and the moldability of the material is deteriorated in some cases. However, when the above-mentioned mouthpiece 177 is used, the raw material is supplied from not smaller than two kinds of extrusion molding machines 111 separately and independently to the holes H of the region 177a and slit 177b, so that a suitable wavy form is obtained. Instead of the slit 177b, holes H may be provided. In such a case, it is recommended that the density of the holes H be set high.

Besides these mouthpieces, mouthpieces of various other specifications can be used in practice. The density of the holes H formed in the above-described mouthpieces is preferably set to 1 to 5/cm².

The method of manufacturing a three-dimensional netted structure of the first mode of embodiment, etc. is utilized.

According to the three-dimensional netted structures 101 to 107 of the tenth to sixteenth modes of embodiment, a resin difficult to be separated or a resin impossible to be separated is used to form the first region 101a, while a resin possible to be separated is used to form the second region 101b, this resin being separated during a recycling operation, so that the recycling operation can be carried out repeatedly.

A three-dimensional netted structure divided into regions in accordance with the properties of the thermoplastic resins can be manufactured, and the recycling of the thermoplastic resins can be done smoothly. A simple operation, such as a region separating operation or some other similar operation advantageously makes it possible to change the shape of the netted structure afterward. Since a raw material is supplied to the mouthpiece from a plurality of extruders separately and independently, the moldability of the material for the three-dimensional structure is improved.

An apparatus 210 for manufacturing three-dimensional netted structure of a third mode of embodiment aims at providing a method of and an apparatus for manufacturing a three-dimensional netted structure, capable of preventing the deformation, which causes inconveniences, of the endless belts, omitting a finishing operation on a later stage, improving the degree of straightness of the surfaces of a netted structure, meeting a demand for a netted structure of modified shapes, and manufacturing a netted structure of an improved durability.

The construction of the parts of the apparatus for manufacturing the three-dimensional netted structure 210 which are different from the corresponding parts of the apparatuses of other modes of embodiment will be described by utilizing the description of the first mode of embodiment, etc. The apparatus 210 is formed of an extrusion molding machine 211, a pair of rolls 212, 213 provided in horizontal positions spaced from each other by a predetermined distance, a pair of rolls 214, 215 (refer to FIG. 20 and FIG. 21) provided below and in alignment with the two rolls 212, 213 horizontally so as to be spaced from each other by a predetermined distance, a motor for driving the rolls 212 to 215, a transmission formed of chains and gears and adapted to change the moving speed of the rolls 212 to 215, a water tank for partly submerging of the two rolls 212, 213 and completely submerging the two rolls 214, 215, a control unit, meters, etc. Referring to FIG. 20, a structure provided with three rolls by removing one of the lower rolls may be employed.

The rolls 212, 213 may be formed of cross-section circular rolls 224 (refer to FIG. 22A) as well as rolls of modified shapes. Various modified modes of rolls are conceivable which include, for example, a roll 225 (refer to FIG. 22B) having a cross-section saw-tooth outer circumference, a roll having continuously formed recesses and projections, for example, a roll 226 (refer to FIG. 22C) having an outer circumferential surface similar to that of a gear in section, a roll 227 (refer to FIG. 22D) having not smaller than one projection 227a (for example, a triangular or circular projection) on an outer circumferential surface thereof, a cross-section elliptic roll 228 (refer to FIG. 22E), a cross-section triangular or a hand-made or mechanically molded rice-shaped roll 229 (refer to FIG. 22F), a cross-section polygonal roll, for example, a cross-section octagonal roll 230 (refer to FIG. 22G), etc.

As shown in FIG. 21, the rolls 212 to 215 are provided with driving shafts 212a to 215a respectively. The driving shafts 212a to 215a are supported rotatably on the respective bearings, and driven in the directions of arrows in FIG. 20 by a driving motor via the transmission.

According to the apparatus 210 described above for manufacturing a three-dimensional netted structure, it becomes possible to omit a finishing operation carried out in a later stage, heighten the degree of straightness of surfaces of a netted structure, meet a demand for obtaining netted structures of modified shapes and improve the durability of a netted structure.

A three-dimensional netted structure 401 of a seventeenth mode of embodiment is a netted structure in which sparse portions and dense portions are provided. This netted structure can be applied to, for example, a wall material from which a gardening container is suspended, a deck on which a gardening container is placed, a blind, a screen, a bamboo blind-like article, a fence, and a gardening cushioning material applied to a floral decoration and the like.

The sparse and dense portions of the three-dimensional netted structure 401 are formed through an operation for regulating a transfer speed of the draw-down unit, for example, endless conveyors or rollers, by controlling the rotational speed of the motor. This method enables a netted structure having sparse and dense portions stabler than those of a netted structure manufactured by regulating the liquid pressure of the extrusion molding machine to be obtained.

As shown in FIG. 23A, low-density portions 401a and high-density portions 401b are formed in order and in repetition. In addition, as shown in FIG. 23B, hollow portions 406A, 406B are provided through a netted structure so as to extend in a predetermined direction. A modified mode of this netted structure may be a gardening cushioning material 402 having a plurality of small through holes 407a to 407d extending therethrough in the lengthwise direction as shown in FIG. 23D. The ranges of the density of the sparse portions 401a and dense portions 401b can be set suitably. The raw material of the thermoplastic resin, etc. will be described by utilizing the description of those of the first mode of embodiment.

In order to make hollow portions in the netted structure, regions 477a, 477b not provided with the holes H are formed in the corresponding parts of the mouthpiece 471 as shown in FIG. 24, and downwardly extending cross-section square introduction members (plate members, pipes, etc.) 477c, 477d are provided (refer to FIG. 24B) on lower portions of these regions. There is another example of the mouthpiece which is formed of a mouthpiece 481 (the area of the region thereof which is provided with the holes H accounts for 90% of a total area of the mouthpiece)(refer to FIG. 24C) in which a predetermined number of holes H are formed at substantially regular intervals. In order to form hollow portions in the netted structure, this mouthpiece is provided with regions 487a to 487d not provided with the holes H in the corresponding parts thereof, and downwardly extending cross-section square introduction members (plate members, pipes, etc.) 488a to 488d are provided (refer to FIG. 24D) on lower portions of the mentioned regions. The density of the holes H formed in the mouthpiece is preferably 1 to 5/cm². Besides these mouthpieces, mouthpieces of various specifications can be used in practice.

The three-dimensional netted structure 401 can be used as substitutes for a wall member from which a gardening container is suspended, a wall member for a floral decoration, a blind and a fence. For example, as shown in FIG. 25, piles 480 (posts may be used instead) are driven into the ground and set up, and the resultant piles are thrust into the hollow portions 406A, 406B of the three-dimensional netted structure 401 and fixed. The three-dimensional netted structure 401 may be divided into a plurality of parts, and dimensional selectivity thereof may be secured by combining the divided netted structures with each other. A suitable number of hanging baskets 482 provided with hooks 481 are hung on the sparse portions 401a. The hooks 481 are hung on sparse portions 401a more easily than on dense portions 401b. This netted structure can also be utilized as a deck. For example, a three-dimensional netted structure 490 is not provided with hollow portions but it is manufactured in a step similar to the step of manufacturing the three-dimensional netted structure 401, so that a culture pot 491, a container 492 and the like can be placed thereon. The netted structure 490 can also be applied to a screen, a bamboo blind-like article, a fence, a floral decoration, etc. As shown in FIG. 26, a three-dimensional netted structure 402 can be utilized as a roof, a screen, and a partition for plants in a median strip of a road. The netted structure 402 is formed so that it can be fixed to a structure by a suitable device or by passing connecting members 403, such as strings, rings, pipes and the like through small holes 407a to 407c thereof. When this netted structure is utilized as a partition for the plants in a median strip of a road, a glare-proofing effect is displayed with respect to the light of an automobile.

According to the three-dimensional netted structure 401 described above, it can be applied to a wall member for hanging baskets, a deck, a blind, etc. Moreover, this netted structure reduces the manufacturing cost, and has a durability with respect to the wind and rain and sunlight. The netted structure is not rotted, and the flexure thereof does not occur. The netted structure is rarely discolored. This netted structure can employ various colors, and the coloring of the netted structure can be done freely, so that the range of the selection of colors expands. Moreover, the netted structure has a very high resiliency, and enables a blinding effect to increase and an outer appearance of different sense of quality to be provided, so that the netted structure is very convenient.

The three-dimensional netted structure can also be used as a seedbed for planting a roof with trees. The netted structure is laid in a hole or a recess formed in a suitable position on a gas-permeable and a water-permeable tile. The culture earth is put in the hole or recess, and tree is planted therein.

The three-dimensional netted structure can also be used as a pavement material by pasting gas-permeable and water-permeable tiles on an upper surface thereof. Owing to the netted structure, the temperature can be reduced.

A three-dimensional netted structure can also be manufactured the characteristics of which reside in that the netted structure is formed by preparing as a raw material or a main raw material a thermoplastic resin containing a brittleness causing element, such as an inorganic substance, for example, talc; forming a plurality of helically and randomly entangled and partly and thermally bonded filaments of the raw material by extrusion molding; and cooling these filaments with a liquid, the brittle fracture of the product becoming able to be effected by applying an external force thereto.

A three-dimensional netted structure obtained by preparing a thermoplastic resin as a raw material or a main raw material; forming a plurality of helically and randomly entangled and partly and thermally bonded filaments of the raw material by extrusion molding; cooling these filaments with a liquid, and applying a fire resistant material to the resultant filaments or enclosing the filaments with a nonwoven carbon fiber, or a similar three-dimensional netted structure made of the same thermoplastic resin to which the fire resistant material is added can also be manufactured. The three-dimensional netted structure enclosed with a nonwoven cloth of carbon fiber can be provided in the ceiling and walls.

A three-dimensional netted structure 510 of the fourth mode of embodiment is manufactured by forming a three-dimensional netted structure 501 by using curved plates 582, 583 as shown in FIG. 27, instead of using the endless members and rolls. The curved plates 582, 583 extend perpendicularly to the surface of the drawing, and are given at their outer surfaces a slidability by coating the same with polytetrafluoroethylene. The curved plates are rectangular in side elevation. The curved plates 582, 583 are arranged so that a distance therebetween decreases from upper portions thereof toward lower portions thereof. The curved plates 582, 583 may have a fixed structure, or they may be formed so that the density and shape thereof in the lateral and longitudinal directions can be varied by rendering a distance of the curved plates variable as shown by broken lines by reciprocating driving units 590, 591 (for example, fluid pressure cylinders). A curved plate 584 is also provided below the curved plates 582, 583, and introduces the netted structure 501 suitably to a downstream side draw-down unit.

INDUSTRIAL APPLICABILITY

According to the inventions described in claim 1 tob 19, a method of and an apparatus for manufacturing a three-dimensional netted structure, capable of omitting a finishing operation in a later stage, heightening the degree of straightness of side surfaces of the netted structure, meeting a demand for obtaining netted structure of modified shapes, and improving the durability of the netted structure can be provided, and the value of industrial utilization of these inventions in various kinds of industries is very large.

Number	Date	Country	Kind
2000-072977	Mar 2000	JP	national
2000-279721	Sep 2000	JP	national
2000-279792	Sep 2000	JP	national
2000-281309	Sep 2000	JP	national
2000-281319	Sep 2000	JP	national
2000-281329	Sep 2000	JP	national
2000-281341	Sep 2000	JP	national
2000-285855	Sep 2000	JP	national

Number	Name	Date	Kind
4012249	Stapp	Mar 1977	A
4859516	Yamanaka et al.	Aug 1989	A
5464491	Yamanaka	Nov 1995	A
5639543	Isoda et al.	Jun 1997	A

Number	Date	Country
982435	Mar 2000	EP
2 214 940	Sep 1989	GB
2 224 191	May 1990	GB
2 275 695	Sep 1994	GB
58149362	Sep 1983	JP
62128739	Jun 1987	JP
1207462	Aug 1989	JP
1314771	Dec 1989	JP
380027	Apr 1991	JP
514849	Apr 1993	JP
5106153	Apr 1993	JP
73824	Jan 1995	JP
768061	Mar 1995	JP
768284	Mar 1995	JP
779638	Mar 1995	JP
7189104	Jul 1995	JP
7189106	Jul 1995	JP
7324273	Dec 1995	JP
83456	Jan 1996	JP
874161	Mar 1996	JP
898748	Apr 1996	JP
899093	Apr 1996	JP
921054	Jan 1997	JP
952275	Feb 1997	JP
11241264	Sep 1999	JP
11350326	Dec 1999	JP
2000120743	Apr 2000	JP

Three-dimensional net-like structure, and method and device for producing three dimensional net-like structure

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Term Extension

Abstract

Description

Claims

Priority Claims (8)

PCT Information

US Referenced Citations (4)

Foreign Referenced Citations (27)

Related Publications (1)