THREE-DIMENSIONAL SHAPING METHOD AND THREE-DIMENSIONAL SHAPING DEVICE METHOD

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to three-dimensional shaping methods for deforming and depositing a shaping raw material to obtain a three-dimensional shaped object and, more particularly, to a three-dimensional shaping method for generating a shaped object using multiple shaping raw materials and a three-dimensional shaping device that is suitable for the method.

2. Description of the Related Art

As a technology for forming a three-dimensional solid object, the technology called Rapid Prototyping (RP) is known. This technology uses data (data in Standard Triangulated Language (STL) format), which describes the surface of a single three-dimensional shape as a set of triangles, to calculate the cross-sectional shape, which is sliced thin in a lamination direction, and laminates each layer in accordance with the shape to form the solid object.

Furthermore, as the techniques for forming solid objects are known Fused Deposition Molding (FDM), inkjet techniques, inkjet binder techniques, Stereo Lithography (SL), Selective Laser Sintering (SLS), or the like.

In recent years, there has been an expectation to provide personal three-dimensional shaping devices at a low price, which is capable of colorizing shaped objects. As the methods suitable for colorization, there are inkjet methods and inkjet binder methods; however, there is a problem in that, as special inkjet heads and ink are necessary, devices and shaped objects are expensive.

Conversely, according to the FDM method, for example, a thermoplastic shaping raw material is heated to be in a fluid state, and each layer is sequentially laminated so that a solid object is formed. The FDM method has an advantage in that, as the materials widely used as mechanical components or for injection molding, or the like, may be used as shaping raw materials, shaped objects may be created at relatively low costs. However, it is generally said that the FDM method is not suitable for colorization as compared to the inkjet methods or the inkjet binder methods.

Here, Japanese Unexamined Patent Application Publication No. 2013-86289 describes a FDM-method three-dimensional shaping device that uses shaping materials that have different weights in a unit volume depending on a shaped site.

Specifically, it describes that multiple shaping materials, which have different weights in a unit volume, are sequentially switched to be discharged so that the weight in a unit volume is changed depending on a shaped site (Paragraph 0033, FIG. 3(b)). According to this invention, if multiple shaping materials in different colors are used as the shaping materials, colored shaped objects may be created. However, there is a problem in that the number of colors is limited to the number of heads.

Furthermore, Japanese Unexamined Patent Application Publication No. 2013-86289 describes that the mixture ratio between shaping materials within the heads is adjusted to change the weight of a shaping material in a unit volume (Paragraph 0033, FIG. 3(a)). If multiple shaping materials in different colors are used as the shaping materials, full colorization is possible. However, Japanese Unexamined Patent Application Publication No. 2013-86289 does not consider colorization of shaped objects, and does not mention a specific method of mixing shaping raw materials.

SUMMARY OF THE INVENTION

According to one aspect of the present invention, a three-dimensional shaping method deforms and deposits a plurality of shaping raw materials in a predetermined solid shape. The three-dimensional shaping method includes, by a conveying unit, conveying the plurality of shaping raw materials to a deforming unit. The three-dimensional shaping method further includes, by the deforming unit, deforming the shaping raw materials. The three-dimensional shaping method still further includes, by a shaping-material forming unit, twisting and arranging the deformed shaping raw materials in a helical fashion to form a shaping material. The three-dimensional shaping method still further includes, by a shaping unit, sequentially depositing the shaping material to form a three-dimensional shaped object.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a schematic diagram that illustrates the relationship between the distance from the object and the resolution of the human vision.

FIG. 1B is a table that illustrates the relationship between the distance from the object and the resolution owned by a person with the visual acuity of 1.0.

FIG. 2A is a schematic view of the formed shaping material in a case where there are two types of shaping raw materials.

FIG. 2B is a schematic view of the formed shaping material in a case where there are three types of shaping raw materials.

FIG. 3 is a schematic view of the shaping material that is formed if only the revolving speed is changed.

FIG. 4 is a schematic view of the shaping material that is formed if only the shaping velocity is changed.

FIG. 5 is a schematic view of the shaping material that is formed if only the conveying velocity of a shaping raw material A is changed.

FIG. 6 is a schematic view of the shaping material that is generated while combining the shaping conditions illustrated in FIGS. 3 to 5.

FIG. 7 is a cross-sectional view that schematically illustrates a three-dimensional shaping device according to a second embodiment of the present invention.

FIG. 8 is an enlarged cross-sectional view that schematically illustrates the relevant part of a shaping-material forming section.

FIG. 9 is a perspective view that schematically illustrates the relevant part of the shaping-material forming section.

FIG. 10 is a table that illustrates the relation among the revolving speed, the shaping velocity, and 1 pitch of the shaping material.

FIG. 11A is a longitudinal sectional view that schematically illustrates the relevant part of the shaping-material forming section of the three-dimensional shaping device according to a third embodiment of the present invention.

FIG. 11B is a C-C cross-sectional view of FIG. 11A.

FIG. 12 is a longitudinal sectional view that schematically illustrates the relevant part of the shaping-material forming section, which illustrates a modified example of FIG. 11A.

FIG. 13A is a perspective view that illustrates an example of the three-dimensional shaped object that is formed if the thickness of the shaping material, which forms each layer, is the same.

FIG. 13B is a view of the arrow A and a view of the arrow B of FIG. 13A.

FIG. 14A is a view that illustrates the three-dimensional shaped object that is formed if the thickness of a shaping material which forms each layer, is changed, and corresponds to the view of the arrow A and the view of the arrow B in FIG. 13A.

FIG. 14B is a table that illustrates the relation between the layer angle and the thickness of the shaping material.

FIG. 15A is a schematic view that illustrates a shaping process.

FIG. 15B is a schematic view that illustrates a shaping process.

FIG. 15C is a schematic view that illustrates a shaping process.

FIG. 16 is a functional block diagram that illustrates a configuration of a control unit that performs the process according to a fourth embodiment.

FIG. 17 is the main flowchart that illustrates the fourth embodiment.

FIG. 18 is a flowchart of the subroutine.

FIG. 19 is a functional block diagram that illustrates a modified configuration of the control unit that performs the process according to the fourth embodiment.

FIG. 20 is a flowchart of the subroutine.

FIG. 21 is a side view and a bottom view of the rotary member.

FIG. 22 is a view that corresponds to the D-D cross-sectional surface of a twisting section illustrated in FIG. 8.

FIG. 23 is a view of the state where shaping is conducted in the solid line from (A) to (B) using a conventional shaping method without any rotation mechanisms.

FIG. 24A is a side view that illustrates the state of shaping according to a tenth embodiment.

FIG. 24B is a top view that illustrates the state of shaping according to the tenth embodiment.

FIG. 25 is a view that illustrates shaping according to an eleventh embodiment.

FIG. 26 is a view that illustrates shaping according to the eleventh embodiment.

The accompanying drawings are intended to depict exemplary embodiments of the present invention and should not be interpreted to limit the scope thereof. Identical or similar reference numerals designate identical or similar components throughout the various drawings.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the present invention.

As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.

In describing preferred embodiments illustrated in the drawings, specific terminology may be employed for the sake of clarity. However, the disclosure of this patent specification is not intended to be limited to the specific terminology so selected, and it is to be understood that each specific element includes all technical equivalents that have the same function, operate in a similar manner, and achieve a similar result.

A detailed explanation is given below of the present invention using the embodiments that are illustrated in the drawings. Here, components, types, combinations, shapes, relative arrangements, or the like, described in the embodiments are only examples for explanation unless otherwise specified, and there is no intention to limit the scope of the present invention thereto.

An embodiment has an object to provide a novel three-dimensional shaping method and a three-dimensional shaping device that forms a solid object using a shaping material that is formed from multiple shaping raw materials.

The three-dimensional shaping method according to an embodiment of the present invention has the feature that multiple shaping raw materials with different colors are deformed, conveyed at a predetermined velocity, twisted at a predetermined velocity, and deposited at a predetermined blend ratio in a helical fashion so that a full-color shaping material is formed, and the formed shaping material is sequentially deposited so that a three-dimensional shaped object is obtained. Furthermore, with the three-dimensional shaping method according to the present invention, multiple materials with different tactual senses or multiple conductors with different resistance values are used as shaping raw materials, whereby it is also possible to obtain shaped objects of which the tactual sense or the resistance value is flexibly changed.

[Coloration Interval of Shaping Raw Materials]

First, the resolution of the human vision is explained, and then full colorization of shaping materials is explained. FIG. 1A is a schematic diagram that illustrates the relationship between the distance from the object and the resolution of the human vision, and FIG. 1B is a table that illustrates the relationship between the distance from the object and the resolution owned by a person with the visual acuity of 1.0.

As illustrated in FIG. 1A, if the Landolt ring with a diameter of 7.5 mm, a thickness of 1.5 mm, and a gap of 1.45 mm can be visually recognized at a distance of 5 m, the human visual acuity is 1 degree of the visual angle, i.e., the visual acuity of 1.0. Specifically, if the object is observed at a distance of 5 m, the resolution owned by a person with the visual acuity of 1.0 is 1.45 mm. As illustrated in FIG. 1B, if the object is observed at a distance of 1 m, the resolution owned by a person with the visual acuity of 1.0 is 0.29 mm. In a case where it is assumed that a shaped object is observed at a distance of 1 m, and if multiple colors are arranged within the range of equal to or less than 0.29 mm, the multiple colors are seen as being mixed, and therefore are recognized as a single color by humans. According to each embodiment of the present invention, a pitch P_xof the shaping material, illustrated in FIG. 2, is determined using the human's visual resolution as a reference.

For full colorization of shaping materials, the percentage of shaping raw materials included in the 1 pitch P_xmay be changed. For example, if the subtractive color process is applied, shaping raw materials in four colors, that is, white (or black) in addition to the three primary colors, i.e., cyan, magenta, and yellow, are used, and the percentage of the shaping raw material in each color, arranged in the 1 pitch P_x, is changed so that the shaping materials may be full-colorized.

First Embodiment: Three-Dimensional Shaping Method and Theory Thereof

An explanation is given of the three-dimensional shaping method according to an embodiment of the present invention. FIG. 2 is a schematic view of the shaping material to be formed, where in the case of FIG. 2A, there are 2 types of shaping raw materials, and in the case of FIG. 2B, there are 3 types of shaping raw materials. Furthermore, in the following equations, the subscript index a represents the parameter with regard to a shaping raw material A, the subscript index b represents the parameter with regard to a shaping raw material B, and the subscript index x represents the parameter with regard to the formed shaping material.

First, an explanation is given of a case where there are 2 types of shaping raw materials.

If the operational relationship in FIG. 2A is represented using general equations, the following Equation (1) and Equation (2) are obtained.

Q
_x
=Q
_a
+Q
_b=¼π(d_a²×v_a+d_b²×v_b)=¼π×d_x²×v_x (1)

$\begin{matrix} f_{x} = \frac{V_{x}}{P_{x}} & (2) \end{matrix}$

Here, the conveying flow quantity and the shaping flow quantity: Q [mm³/s]

the conveying velocity and the shaping velocity: v [mm/s]

the width of the shaping raw material and the width of the shaping material: d [mm]

the pitch: P [mm]

the revolving speed (the twisting speed): fx [rps]

Equation (1) indicates that the flow quantity Q is given by “the cross-sectional area×the velocity v”. Here, for simplification of the equations, an explanation is given based on the assumption that the cross-sectional shapes of the shaping raw material and the shaping material are circular.

An explanation is given of a change that occurs in the shaping material when shaping is conducted while each parameter is changed. The parameter of the reference value (before change) is represented using the subscript index “1”, and the parameter (the changed value) that is changed from the reference value is represented using the subscript index “2”.

With the reference value, Equations (1) and (2) are established as described below (Equation (1-1), Equation (2-1)).

Q
_x1
=Q
_s1
+Q
_b1=¼π(d_a1²×v_a1+d_b1²×v_b1)=¼π×d_x1²×v_x1 (1-1)

$\begin{matrix} f_{x} = \frac{V_{x}}{P_{x}} & (2 - 1) \end{matrix}$

With the changed value, Equations (1) and (2) are established as described below (Equation (1-2), Equation (2-2)).

Q
_x2
=Q
_a1
+Q
_b2=¼π(d_a2²×v_a2+d_b2²×v_b2)=¼π×d_x2²×v_x2 (1-2)

$\begin{matrix} f_{x 2} = \frac{V_{x 2}}{P_{x 2}} & (2 - 2) \end{matrix}$

An explanation is given of a change in the pitch P if only the revolving speed f_xis changed from the reference value. FIG. 3 is a schematic view of the shaping material that is formed if only the revolving speed is changed. Here, an explanation is given of a case where, for example, a changed revolving speed f_x2is twice as much as a reference revolving speed f_x1(f_x2=2f_x1). According to Equation (2), Equation (2′) is obtained.

v
_x
=f
_x
×P
_x (2′)

As the shaping velocity v_xis the same (v_x=v_x1=v_x2), each parameter f_x, P, and [f_x2=2f_x1] of the reference value and the changed value are applied to Equation (2′) so that Equation (2′-1) is obtained.

v
_x
f
_x1
×P
_x1
=f
_x2
×P
_x2=2f_x1×P_x2 (2′-1)

Therefore, Equation (3) is obtained.

$\begin{matrix} P_{x 2} = \frac{f_{1}}{f_{2}} \times P_{x 1} = \frac{f_{1}}{2 f_{1}} \times P_{x 1} = \frac{1}{2} \times P_{x 1} & (3) \end{matrix}$

Thus, the changed pitch P_x2is ½ of the reference pitch P_x1, and high-resolution coloration is obtained. That is, the pitch P_xof the shaping material can be changed by changing the revolving speed f_x. Here, the shaping width d_xis not changed.

An explanation is given of a change in the parameter if only the shaping velocity v_xis changed from the reference value. FIG. 4 is a schematic view of the shaping material that is formed if only the shaping velocity is changed. For example, an explanation is given of a case where the changed shaping velocity v_x2is twice as much as the reference shaping velocity v_x1(v_x2=2v_x1).

<<Change in the Pitch>>

An explanation is given of a change in the pitch P. The revolving speed f_xis the same (f_x=f_x1=f_x2); therefore, according to Equation (2), Equation (3-1) is obtained.

$\begin{matrix} f_{x} = \frac{V_{x 1}}{P_{x 1}} = \frac{V_{x 2}}{P_{x 2}} = \frac{2 V_{x 1}}{P_{x 2}} & (3 - 1) \end{matrix}$

If this equation is rearranged, Equation (4) is obtained.

$\begin{matrix} P_{x 2} = \frac{V_{x 2}}{V_{x 1}} \times P_{x 1} = \frac{2 V_{x 1}}{V_{x 1}} \times P_{x 1} = 2 \times P_{x 1} & (4) \end{matrix}$

Thus, the changed pitch P_x2is twice as much as the reference pitch P_x1, and low-resolution coloration is obtained. That is, if the shaping velocity v_xis changed, the pitch P_xof the shaping material may be changed.

<<Change in the Shaping Material Width>>

Next, an explanation is given of a change in the shaping material width d_x. As the shaping flow quantity Q_xis the same (Q_x=Q_x1=Q_x2), [v_x2=2v_x1] is substituted into Equation (1) so that Equation (4-1) is obtained.

Q
_x=¼π×d_x1²×v_x1=¼π×d_x2²×v_x2=¼π×d_x2²×2v_x1 (4-1)

If this equation is rearranged, Equation (4-2) is obtained.

$\begin{matrix} d_{x 2}^{2} = \frac{V_{x 1}}{V_{x 2}} \times d_{x 1}^{2} = \frac{V_{x 1}}{2 V_{x 1}} \times d_{x 1}^{2} = \frac{1}{2} \times d_{x 1}^{2} & (4 - 2) \end{matrix}$

Thus, Equation (5) is obtained.

$\begin{matrix} d_{x 2} = \frac{1}{\sqrt{2}} d_{x 1} & (5) \end{matrix}$

Thus, the changed shaping material width d_x2is the square root of ½ times as much as the reference shaping material width d_x1, and high resolution is obtained. That is, if the shaping velocity v_xis changed, the shaping material width d_xmay be changed.

It is understood that, the pitch P_x2and the shaping material width d_x2can be changed by changing the shaping velocity v_x.

An explanation is given of changes in the shaping material width d_x, the shaping velocity v_x, and the pitch P_xif only the conveying velocity v_aof the shaping raw material A is changed from the reference value. FIG. 5 is a schematic view of the shaping material that is formed if only the conveying velocity of the shaping raw material A is changed. For example, an explanation is given of the case where the changed conveying velocity v_a2is ½ of the reference conveying velocity v_a1(v_a2=v_a1/2).

For simplification of calculation below, the conveying velocity v_b1and the shaping raw material width d_b1of the shaping raw material B are the same as of the shaping raw material A (v_b1=v_a1, d_b1=d_a1). As the shaping raw material width d_aof the shaping raw material A, the shaping raw material width d_bof the shaping raw material B, and the shaping velocity v_bof the shaping raw material B are the same (d_a1=d_a2, d_b1=d_b2, v_b1=v_b2), Equation (5-1) and Equation (5-2) are obtained from Equation (1-1) and Equation (1-2).

Q
_x1=¼π(d_a1²×v_a1+d_b1²×v_b1)=¼π(d_a1²×v_a1+d_a1²×v_a1)= 2/4π(d_a1²×v_a1) (5-1)

Q
_x2=¼π(d_a2²×v_a2+d_b2²×v_b2)=¼π(d_a1²×v_a1+d_a1²×v_a1)=π⅜π(d_a1²×v_a1) (5-2)

Thus, Equation (6) is obtained.

Q
_x2=¾Q_x1 (6)

If the conveying velocity v_aof the shaping raw material A is changed, the shaping flow quantity Q_xis changed. This means that the shaping material width d_xand the pitch P_xmay be changed in accordance with the shaping velocity v_x(or the opposite is established).

Here, the ratio (P_a2:P_b2) between the pitches of the shaping raw materials A and B in the shaping material is equal to the ratio (v_a2:v_b2) between the conveying velocities of the shaping raw materials A and B, and Equation (7) is obtained.

P
_a2
:P
_b2
=v
_a2
:v
_b2=1:2 (7)

<<Change in the Shaping Material Width and the Pitch if the Shaping Velocity is not Changed>>

An explanation is given of the changed shaping material width d_x2if only the conveying velocity v_aof the shaping raw material A is changed and the shaping velocity v_xis the same (v_x1=v_x2). Equation (7-1) is obtained from Equation (1-1).

Q
_x1=¼π×d_x1²×v_x1 (7-1)

If Equation (7-1) is deformed, Equation (8) is obtained.

$\begin{matrix} V_{x 1} = \frac{4}{π} \times \frac{Q_{x 1}}{d_{x 1}^{2}} & (8) \end{matrix}$

Furthermore, Equation (8-1) is obtained from Equation (1-2).

Q
_x2=¼π×d_x2²×v_x2=¼π×d_x2²×v_x1 (8-1)

If Equation (8-1) is deformed, and Equation (6) and Equation (8) are substituted, Equation (8-2) is obtained.

$\begin{matrix} d_{x 2}^{2} = \frac{4}{π} \frac{Q_{x 2}}{V_{x 1}} = \frac{Q_{x 2}}{Q_{x 1}} d_{x 1}^{2} = \frac{\frac{3}{4} Q_{x 1}}{Q_{x 1}} d_{x 1}^{2} = \frac{3}{4} d_{x 1}^{2} & (8 - 2) \end{matrix}$

Thus, Equation (9) is obtained.

$\begin{matrix} d_{x 2} = \frac{\sqrt{3}}{2} d_{x 1} & (9) \end{matrix}$

Thus, the changed shaping material width d_x2is the square root 3/2 times as much as the reference shaping material width d_x1. That is, if the conveying velocity v_aof the shaping raw material A is changed and the shaping velocity v_xis the same, the shaping material width d_xmay be changed.

Furthermore, the pitch P_x2is explained. As the revolving speed f_xis the same (f_x1=f_x2), Equation (9-1) and Equation (10) are obtained from Equation (2-1) and Equation (2-2).

$\begin{matrix} \frac{V_{x 1}}{P_{x 1}} = \frac{V_{x 2}}{P_{x 2}} = \frac{V_{x 1}}{P_{x 2}} & (9 - 1) \end{matrix}$

P
_x2
=P
_x1 (10)

As it is understood from this Equation, the pitch P_xis not changed.

<<Changes in the Shaping Velocity and the Pitch if the Shaping Material Width is not Changed>>

Next, an explanation is given of the changed shaping velocity v_x2if only the conveying velocity v_aof the shaping raw material A is changed and the shaping material width d_xis the same (d_x1=d_x2) Equation (10-1) and Equation (11) are obtained from Equation (1-1).

Q
_x1=¼π×d_x1²×v_x1 (10-1)

$\begin{matrix} d_{x 1}^{2} = \frac{4}{π} \times \frac{Q_{x 1}}{V_{x 1}} & (11) \end{matrix}$

Thus, Equation (11-1) is obtained from Equation (1-2).

Q
_x2=¼π×d_x2²×v_x2=¼π×d_x1²×v_x2 (11-1)

If Equation (11) is substituted after deformation, Equation (11-2) is obtained.

$\begin{matrix} V_{x 2} = \frac{4}{π} \times \frac{Q_{x 2}}{d_{x 1}^{2}} = \frac{Q_{x 2}}{Q_{x 1}} \times V_{x 1} & (11 - 2) \end{matrix}$

If Equation (6) is substituted into Equation (11-2), Equation (12) is obtained.

$\begin{matrix} V_{x 2} = \frac{3}{4} \frac{Q_{x 1}}{Q_{x 1}} V_{x 1} = \frac{3}{4} V_{x 1} & (12) \end{matrix}$

Thus, the changed shaping velocity v_x2is ¾ of the reference shaping velocity v_x1. That is, if the conveying velocity v_aof the shaping raw material A is changed and the shaping material width d_xis the same, the shaping velocity v_xmay be changed.

An explanation is further given of the changed pitch P_x2. As the revolving speed f_xis the same (f_x1=f_x2), Equation (12-1) and Equation (12-2) are obtained from Equation (2-1) and Equation (2-2).

$\begin{matrix} \frac{V_{x 1}}{P_{x 1}} = \frac{V_{x 2}}{P_{x 2}} & (12 - 1) \\ P_{x 2} = \frac{V_{x 2}}{V_{x 1}} P_{x 1} & (12 - 2) \end{matrix}$

If Equation (12) is substituted into Equation (12-2), Equation (13) is obtained.

$\begin{matrix} P_{x 2} = \frac{\frac{3}{4} V_{x 1}}{V_{x 1}} P_{x 1} = \frac{3}{4} P_{x 1} & (13) \end{matrix}$

Thus, the changed pitch P_x2is ¾ of the reference pitch P_x1. That is, if the conveying velocity v_aof the shaping raw material A is changed and the shaping material width d_xis the same, the pitch P_xof the shaping material may be changed.

Furthermore, as described above, the ratio (P_a2:P_b2) between the pitches of the shaping raw materials A and B in the shaping material is equal to the ratio (v_a2:v_b2) between the conveying velocities of the shaping raw materials A and B.

As described above, the ratio between the pitches of the shaping raw materials in the shaping material can be changed flexibly by changing the conveying velocity of some of the shaping raw materials. This method is an important method for adjusting the ratio of deposition of shaping raw materials to generate various colors.

FIG. 6 is a schematic view of the shaping material that is generated while combining the shaping conditions illustrated in FIGS. 3 to 5. As it is understood from this figure, by conducting shaping while changing at least one of the conveying velocity of the shaping raw material, the twisting speed (the revolving speed) of the shaping raw material, and the shaping velocity of the shaping material, or changing in combination, it is possible to obtain shaped objects that use shaping materials with various pitches or shaping widths.

If the operational relationship in FIG. 2B is represented using a general equation, the equation represented by the following Equation (13-1) is obtained.

Q
_x
=Q
_a
+Q
_b
+Q
_c=¼π(d_a²×v_a+d_b²×v_b+d_c²×v_c)=¼π×d_x²×v_x (13-1)

Here, the equation that corresponds to Equation (2) is the same as in the case of FIG. 2A. As it is understood from the above general equation, as is the case with the two colors, if there are three or more colors of shaping raw materials, the shaping material width, the pitch of the shaping raw material included in the shaping material, or the like, can be changed flexibly by appropriately changing the revolving speed f_x, the shaping velocity v_x, and the conveying velocities v_a, v_b, and v_cof the shaping raw materials.

Second Embodiment: Three-Dimensional Shaping Device

With reference to FIGS. 7 to 9, an explanation is given of a three-dimensional shaping device that implements the three-dimensional shaping method. FIG. 7 is a cross-sectional view that schematically illustrates the three-dimensional shaping device according to a second embodiment of the present invention. FIG. 8 is an enlarged cross-sectional view that schematically illustrates the relevant part of a shaping-material forming section. FIG. 9 is a perspective view that schematically illustrates the relevant part of the shaping-material forming section.

A three-dimensional shaping device 1 is a device that forms a three-dimensional shaped object using a fused deposition modeling (FDM) method, in which a shaping raw material 100 is melted (deformed) and deposited in a predetermined solid shape.

The schematic operations of the three-dimensional shaping device 1 are as follows. The three-dimensional shaping device 1 melts the shaping raw material 100 at a heat melting section 31, and introduces the shaping raw materials 100 in combination and with appropriate amounts to a twisting section 40 to achieve the desired coloration. Next, the shaping raw material 100 is twisted at a rotary member 45 of the twisting section 40 so that a shaping material with a predetermined color is formed, and the shaping material is finally discharged onto a shaping stage 71 through a discharge opening 61, whereby the shaping material is shaped on the shaping stage 71.

The three-dimensional shaping device 1 includes a conveying section 10 that includes multiple conveying mechanisms 11 that convey multiple shaping raw materials 100 (100a, 100b, 100c, 100d) with different colors down to the heat melting section 31; a shaping-material forming section 30 that includes the heat melting section 31 that heats and melts each of the shaping raw materials 100 conveyed by the conveying mechanisms 11, and the twisting section 40 that twists and arranges the deformed shaping raw materials 100 in a helical fashion so as to form a multicolor shaping material 101; and a shaping section 70 that sequentially deposits the shaping material 101 to form a three-dimensional shaped object.

The shaping raw material is formed of thermoplastic resin, such as ABS resin. According to the present embodiment, four shaping raw materials in the three primary colors, i.e., cyan (Cyan), magenta (Magenta), and yellow (yellow), and white (or black) are used as the shaping raw materials, and thus full-color shaping materials can be obtained using subtractive color mixing.

The conveying section 10 is a section that conveys the shaping raw material 100 in solid state to the downstream shaping-material forming section 30, and includes the conveying mechanisms 11 that are provided for the shaping raw materials, i.e., for each of the colors. According to the present embodiment, as illustrated in FIG. 9, the four conveying mechanisms 11 are provided to convey the shaping raw materials 100 in 4 types (4 colors). Each of the conveying mechanisms 11 includes a raw-material conveyance path 13, through which the shaping raw material 100 is conveyed; a conveyance gear 15 that is exposed to the raw-material conveyance path 13 to be in contact with the surface of the shaping raw material 100, thereby sequentially delivering the shaping raw material 100 downstream; and a conveyance motor 17 that rotates and drives the conveyance gear 15.

The raw-material conveyance path 13 has substantially a cylindrical shape that has an inner diameter, through which the shaping raw material 100 may be passed. For example, the raw-material conveyance path 13 with an inner diameter φ of 3 mm conveys the shaping raw material with φ 3 mm whose outer diameter is substantially the same as the inner diameter.

The conveyance gear 15 may be a worm gear as illustrated, or may be two rotatable pulleys that are provided such that the outer circumferences are opposed to each other. In the case of the latter, the shaping raw material is conveyed while being sandwiched and held between the outer circumferences of the two pulleys.

The conveyance motor 17 rotates and drives the conveyance gear 15 to convey the amount of shaping raw material that corresponds to the coloration ratio of each of the shaping raw materials 100. The conveyance motor 17 is driven and controlled by a control unit 200.

A heat insulating member 20 is provided between the conveying section 10 and the shaping-material forming section 30. At the conveying section 10, the conveyance gear 15 is brought into contact with the outer surface of the shaping raw material 100 so that the conveyance power is applied; therefore, the shaping raw material needs to be retained in a solid state. The heat insulating member 20 prevents heat of a heater 33 from being transmitted to the conveying section 10 so that the shaping raw material may be retained in a solid state.

In the heat insulating member 20, multiple paths 21 are formed, through which the shaping raw materials 100 in solid state, conveyed from the conveying section 10, are inserted and conveyed. The inner diameter of each of the paths 21 is substantially the same as the inner diameter of each of the raw-material conveyance paths 13.

<Shaping-Material Forming Section>

The shaping-material forming section 30 is a section that melts the shaping raw material 100, conveyed from the conveying section 10, arranges the shaping raw material 100 in a helical fashion while twisting the shaping raw material 100, and ejects the shaping raw material 100 toward the downstream shaping section 70.

The shaping-material forming section 30 includes the heat melting section 31 that conveys the shaping raw materials 100 downstream while heating and melting the shaping raw materials 100; the twisting section 40 that arranges the melted shaping raw materials 100 in a helical fashion while twisting the melted shaping raw materials 100, thereby forming the multicolor shaping material 101; and a head section 60 that ejects the shaping material 101.

The heat melting section 31 includes the heater 33 that heats and melts each of the shaping raw materials 100; and a runner 35 (melted raw-material conveyance path: deformed raw-material conveyance path) that conveys each of the shaping raw materials, heated and melted by the heater 33, to the downstream twisting section 40.

The heater 33 may heat the shaping raw material 100 to such a degree that the shaping raw material 100 may be sufficiently melted. If ABS resin is used as the shaping raw material, the temperature of the heater 33 is set to be 250 degrees C. with which the ABS resin is sufficiently melted. The runner 35 is provided for each shaping raw material. The shaping raw material 100, conveyed from the conveying section 10, is inserted into the runner 35.

The twisting section 40 includes a twisting conveyance path 41, to which each shaping raw material, heated and melted by the heater 33, flows and which deforms the shaping raw materials 100 into the shaping material in the process of conveying the shaping raw materials 100 to the shaping section 70 that is located downstream; and the rotary member 45 that is provided within the twisting conveyance path 41 and that rotates about the axis that is parallel to the conveying direction of the twisting conveyance path 41.

The twisting conveyance path 41 has substantially a cylindrical shape with a hollow, and a gate 43 communicating with the runner 35, is formed on the inner surface of twisting conveyance path 41. The melted shaping raw material, which flows within the runner 35, flows into the twisting conveyance path 41 through the gate 43.

The rotary member 45, provided within the twisting conveyance path 41, includes a drive shaft 46 that is rotated and driven by a twisting motor 49; and a twisting projection 47 that is formed such that the twisting projection 47 projects from an end 46a of the drive shaft 46 downstream in the twisting conveyance path 41 and that is eccentrically positioned with respect to the rotation center of the drive shaft 46. The drive shaft 46 is rotated and driven at the speed that corresponds to the revolving speed f_xof the shaping material (the twisting speed of the shaping raw material). The twisting motor 49 is driven and controlled by the control unit 200.

The head section 60, which has the discharge opening 61 to discharge the shaping material 101, is provided on the most downstream of the twisting conveyance path 41. The discharge opening 61 is formed on a head surface 63 that is opposed to the shaping stage 71.

The end 46a of the drive shaft 46 is located upstream of the gate 43 in the twisting conveyance path 41.

Furthermore, in the illustrated example, the twisting projection 47 is provided such that an end 47a is on the same position as the head surface 63. However, the end 47a of the twisting projection 47 may be provided within the twisting conveyance path 41, or may projects toward the shaping stage 71 from the discharge opening 61. In the case of the former, the twisting projection 47 is provided such that at least the end 47a is located at the same position as the downstream end of the gate 43 in the twisting conveyance path 41 or is located further downstream. In the case of the latter, the amount of projection of the twisting projection 47 is set such that it is not in contact with the shaping stage 71 or the uppermost part of a shaped object 102 that is shaped on the shaping stage 71.

The end 46a of the drive shaft 46 is located upstream of the gate 43 in the twisting conveyance path 41, and the end 47a of the twisting projection 47 is located between the position that is the same as the downstream end of the gate 43 and the position such that the end 47a is not in contact with the shaping stage 71 or the uppermost part of the shaped object 102 that is shaped on the shaping stage 71, whereby flowability (flow distribution) of the shaping material 101, discharged through the discharge opening 61, may be uniform. Thus, high-contrast three-dimensional shaped objects may be obtained.

The shaping section 70 includes the shaping stage 71 that is provided such that the shaping stage 71 is opposed to the discharge opening 61; and a stage drive motor 73 that moves the shaping stage 71 forward and backward relative to the discharge opening 61 in the directions of the X axis, the Y axis, and the Z axis.

The shaping stage 71 is like a flat plate that extends along the XY plane, and the shaping material 101, discharged through the discharge opening 61, is sequentially deposited on the shaping stage 71 so that a three-dimensional shaped object is formed.

The stage drive motor 73 includes an X-direction motor that moves the shaping stage 71 forward and backward in the X-axis direction; a Y-direction motor that moves the shaping stage 71 forward and backward in the Y-axis direction; and a Z-direction motor that moves the shaping stage 71 forward and backward in the Z-axis direction. These motors may be configured using, for example, linear motors. The stage drive motor 73 is driven and controlled by the control unit 200. According to the present embodiment, the shaping velocity is adjusted in accordance with the moving speed of the shaping stage 71.

The three-dimensional shaping device 1 includes the control unit 200 that controls an operation of each unit in the conveying section 10, the shaping-material forming section 30, and the shaping section 70.

The control unit 200 drives and controls the conveyance motor 17 of the conveying section 10, the twisting motor 49 of the shaping-material forming section 30, and the stage drive motor 73 of the shaping stage 71. These motors are appropriately driven and controlled by the control unit 200 in accordance with the width of the shaping material, the pitch, the coloration ratio of the shaping raw material (or the color of the shaping material to be formed), the necessary distance between the shaping stage or the uppermost part of the shaped object and the discharge opening, the discharge position of the shaping material above the shaping stage or the shaped object, or the like.

The control unit 200 is a known computer device, and includes a CPU, a memory (ROM, RAM), or the like. The CPU reads a control program stored in the ROM, loads the control program into the RAM, and executes the control program, thereby controlling an operation of each unit of the image forming apparatus.

Examples of Dimensions

For example, the dimensions of the shaping raw material and the dimensions of each unit included in the three-dimensional shaping device 1 may be set as described below.

Outer diameter of the shaping raw material 100: φ 3 mm

Inner diameter of the raw-material conveyance path 13: φ 3 mm

Inner diameter of the gate 43: φ 0.2 mm

Inner diameters of the twisting conveyance path 41 and the discharge opening 61: φ 0.5 mm

Outer diameter of the drive shaft 46: φ 0.5 mm

Distance between the center of the gate 43 and the end 46a of the drive shaft 46: 0.2 mm

Distance between the center of the gate 43 and the head surface 63: 0.3 mm

Distance between the head surface 63 and the shaping stage 71 or the uppermost part of the shaped object: 0.25 mm

Length of the twisting projection 47: 0.3 mm to 0.7 mm (0.5 mm in FIG. 8)

Revolving speed of the drive shaft 46 (the twisting projection 47): 10 to 200 rps (the speed is increased or decreased with 60 rps as a reference)

Here, the above-described numerical values are only examples.

An operation of the three-dimensional shaping device is explained.

[Conveying Process]

During the conveying process, the shaping raw material 100 is conveyed from the conveying section 10 to the shaping-material forming section 30. Each of the shaping raw materials 100 is conveyed in the raw-material conveyance path 13 such that the sum of the conveying velocities of the shaping raw materials 100 in the raw-material conveyance paths 13 is about 0.28 mm/sec in a case where the inner diameter of the twisting conveyance path 41, which is located downstream of the conveying section 10, and the discharge opening 61 is φ 0.5 mm and the conveying velocity (shaping velocity) of the shaping material in the twisting conveyance path 41 is 10 mm/sec. Here, each of the shaping raw materials 100 is conveyed at the conveying velocity that corresponds to the coloration ratio of each of the shaping raw materials 100 in the shaping material 101. Here, during the conveying process, the shaping raw material 100 is in a solid state.

[Shaping-Material Forming Process]

At the shaping-material forming section 30, each of the shaping raw materials 100 is conveyed in a melted state. Specifically, each of the shaping raw materials 100 is heated and melted at the heat melting section 31, and each shaping raw material in a melted state flows through the runner 35 and flows into the twisting conveyance path 41 through the gate 43.

As the twisting projection 47 rotates within the twisting conveyance path 41, the shaping raw material 100 in each color is twisted in a circumferential direction due to fluid resistance caused by the rotation of the twisting projection 47, and the shaping material with each color arranged in a helical fashion is formed.

Here, FIG. 10 is a table that illustrates the relation among the revolving speed, the shaping velocity, and 1 pitch of the shaping material. Here, the conditions with regard to shaping are illustrated in the above examples of the dimensions. If the twisting projection 47 is rotated at the revolving speed of 60 rps under the above-described conditions, the pitch P_xof the shaping material 101 is 0.17 mm. As the pitch P_xof the shaping material 101 can be reduced by increasing the revolving speed of the twisting projection 47, a shaping material with higher resolution can be obtained.

The shaping material 101, which is formed in the desired multicolor, is discharged from the discharge opening 61 toward the shaping stage 71.

[Shaping Process]

During the shaping process, the stage drive motor 73 is driven and controlled by the control unit 200 on the basis of the three-dimensional drawing data on a shaped object. The shaping stage 71 is moved forward and backward relative to the discharge opening 61 in the directions of the X axis, the Y axis, and the Z axis due to the driving of the stage drive motor 73. The shaping material 101 is deposited on the shaping stage 71 or the uppermost part of the shaped object so that the shaped object is formed.

As described above, with the three-dimensional shaping device according to the present embodiment, shaping may be conducted while changing at least one of the conveying velocity of the shaping raw material, the twisting speed (the revolving speed) of the shaping raw material, and the shaping velocity of the shaping material, or changing in combination, and it is thereby possible to obtain shaped objects that use shaping materials with various pitches or shaping widths.

Third Embodiment: Three-Dimensional Shaping Device

An explanation is given of a three-dimensional shaping device according to a third embodiment of the present invention. FIGS. 11A to 11B are views that schematically illustrate the relevant part of the shaping-material forming section of the three-dimensional shaping device according to the third embodiment of the present invention, FIG. 11A is a longitudinal sectional view, and FIG. 11B is a C-C cross-sectional view of FIG. 11A. Hereafter, the same reference numerals are applied to the same members as in the first embodiment, and the explanations of the same members are omitted.

In the three-dimensional shaping device according to the present embodiment, the twisting section 40 includes a cylindrical rotary member 83 that includes multiple flow paths (conveyance paths) 85 that each convey the deformed shaping raw material 100 in each color; and multiple discharge openings 65 that are provided at one end (the lower end in the drawing) in the axial direction of the rotary member 83 and that discharge the shaping raw material 100 in each color, conveyed through the flow path 85, toward the shaping section 70. The twisting section 40 discharges the shaping raw material through the rotating discharge opening 65 while twisting the shaping raw material, thereby forming the shaping material 101 on the shaping stage 71.

The twisting section 40 includes a cylindrical hollow section 81 that has the gate 43 formed on the inner surface of the cylindrical hollow section 81, through which the shaping raw material 100 in each color flows; and the rotary member 83 that is provided within the hollow section 81 and that has substantially a cylindrical shape.

The gate 43 is provided for each shaping raw material, and the gates 43 are arranged such that the axial-direction positions (the vertical-direction positions in the drawing) of the hollow section 81 are different from each other.

The rotary member 83 is provided within the hollow section 81 such that the rotary member 83 rotates about the axis parallel to the axis of the hollow section 81. Furthermore, the inner diameter of the hollow section 81 is set to be substantially the same as the outer diameter of the rotary member 83. Circular recessed sections 87, which continue in a circumferential direction, are formed on the side surface of the rotary member 83 that is opposed to the gates 43. The number of the formed circular recessed sections 87 is the same as the number of the gates 43, and the formed circular recessed sections 87 correspond to the shaping raw materials 100 in colors on a one-to-one basis.

Within the rotary member 83, the separate flow paths 85 are formed, whose one end is opened at an appropriate position of the circular recessed section 87 and which convey the melted shaping raw material 100. The other end of the flow path communicates with the discharge opening 65 that is provided on an end of the rotary member 83.

As illustrated in FIG. 11A, the discharge opening 65 may protrude toward the shaping stage 71 from the head surface 63, or may be provided in substantially the same position as the head surface 63.

An explanation is given of the aspect in which an operation of the three-dimensional shaping device is different from the first embodiment.

[Shaping-Material Forming Process]

The rotary member 83 is rotated and driven at a predetermined speed within the hollow section 81.

Each of the melted shaping raw materials 100, flowing through the runner 35, flows into the circular recessed section 87, which is opposed to the gate 43, through the gate 43. Furthermore, the shaping raw material 100 is injected into the flow path 85 due to the pressure upon flowing from the circular recessed section 87, and the shaping raw material in each color is independently conveyed to the discharge opening 65.

The shaping raw material 100 in each color is discharged toward the shaping stage 71 through the discharge opening 65.

A frictional resistance acts when the shaping raw material 100 is brought into contact with the shaping stage 71 or the uppermost part of the shaped object, and the shaping raw material 100 is twisted and arranged in a helical fashion due to rotation of the rotary member 83 so that the shaping material 101 is obtained.

[Shaping Process]

Furthermore, during the shaping process, as is the case with the first embodiment, the shaping stage 71 is moved forward and backward relative to the discharge opening 65 in the directions of the X axis, the Y axis, and the Z axis. The shaping material 101 is sequentially deposited on the shaping stage 71 or the uppermost part of the shaped object so that the shaped object is formed.

Modified Example

FIG. 12 is a longitudinal sectional view that schematically illustrates the relevant part of the shaping-material forming section, which illustrates a modified example of FIG. 11A. The present example is different from the twisting section 40 of the shaping-material forming section illustrated in FIG. 11A in that the discharge opening 65 is provided within the hollow section 81 and the discharge opening 65 is retracted from the head surface 63. According to the present example, the shaped object is generated while the shaping material 101, which is ejected and formed on the shaping stage 71 or the uppermost part of the shaped object, is pressed by the head surface 63. The width of the shaping material 101 is adjusted by pressing the shaping material 101 with the head surface 63. That is, the width of the shaping material 101 may be adjusted in accordance with the distance between the shaping stage 71 and the head surface 63.

According to the second embodiment illustrated in FIG. 8, as the shaping material 101 is in contact with the inner wall of the twisting conveyance path 41 in the process of being conveyed through the twisting conveyance path 41, there is a possibility that the color of each of the shaping raw materials 100 is partially mixed. Conversely, according to the present embodiment, as illustrated in FIGS. 11A to 11B and FIG. 12, a configuration is such that each of the shaping raw materials 100 is twisted after being ejected toward the shaping stage 71 through the discharge opening 65; therefore, the shaping raw materials 100 in respective colors are arranged in a helical fashion in a separated state, and the colors are unlikely to be mixed.

Fourth Embodiment

A fourth embodiment of the present invention is explained. The present embodiment has the feature that the width (layer thickness) of the shaping material to be discharged is increased in accordance with the angle of the slope face of the shaped object.

In the following explanation, the “layer thickness” means the thickness of the shaping material that forms each layer (the length in the direction along the direction of the Z axis in FIGS. 13A to 13B and 14A to 14B). Furthermore, the “layer width” means the distance between the edges of the shaping materials that form adjacent layers in the direction along the X-Y plane. Moreover, the “layer angle” means the angle between the edges of the shaping materials that form adjacent layers with respect to the X-Y plane (which corresponds to the elevation angle in the example of FIGS. 13A to 13B and 14A to 14B).

FIGS. 13A to 13B are views that illustrate an example of the three-dimensional shaped object that is formed if the thickness of the shaping material, which forms each layer, is the same, FIG. 13A is a perspective view, and FIG. 13B is a view of the arrow A and a view of the arrow B of FIG. 13A.

With the three-dimensional shaping method (the three-dimensional shaping device) according to each embodiment of the present invention, the shaping material is sequentially stacked in the form of laminae so that the shaped object is formed. Therefore, as illustrated in FIG. 13B, the slope face of the shaped object 102 is a false slope that is formed to be stepwise using the shaping materials 101, and is not continuous. In FIGS. 13A to 13B, the semispherical object, protruding upward, is illustrated as an example of the shaped object with the slope face that is formed by stacking the shaping materials in a stepwise manner.

If the shaped object is generated with the same thickness of the shaping materials, as the layer angle is decreased, the layer width is increased. In other words, if the thickness of the shaping material is the same, as the layer angle is decreased, the resolution in the direction along the X-Y plane (the density between the layers in the direction along the X-Y plane) is decreased. If the layer width is small, there is no major problem; however, if the layer width exceeds a predetermined resolution (here, 0.29 mm), there is a possibility that clearness seems to be lost.

Therefore, according to the present embodiment, the thickness of the shaping material which forms each layer, is adjusted to perform control such that the layer width does not exceed a predetermined resolution. Specifically, in accordance with the angle of the slope face that is formed by the first shaping material which forms the first layer (n layer), and the second shaping material which is laminated on the first shaping material to form the second layer (n+1 layer), the thickness of the second shaping material is controlled.

<Means>

FIGS. 14A to 14B are views that illustrate the three-dimensional shaped object that is formed if the thickness of a shaping material, which forms each layer, is changed, FIG. 14A is a view that corresponds to the view of the arrow A and the view of the arrow B in FIG. 13A, and FIG. 14B is a table that illustrates the relation between the layer angle and the thickness of the shaping material.

According to the present embodiment, if the n+1 layer (the second layer) is laminated on the n layer (the first layer) with the reference layer thickness, the n+1 layer part is divided into multiple layers and the shaping material is laminated while the layer angle θ formed by the n layer and the n+1 layer is retained. Thus, the layer width may be prevented from exceeding a predetermined resolution.

An explanation is given of the method for calculating the layer thickness, or the like.

First, with regard to the n+1 layer (the second layer) that is laminated immediately above the n layer (the first layer), the layer angle θ of the shaped object in a case where the shaped object is shaped with the reference layer thickness d_x(here, 0.29 mm) is obtained from the CAD data on the shaped object, or the like.

If the obtained layer angle θ forms the layer width ΔL that exceeds a predetermined resolution (0.29 mm) in a case where shaping is conducted with the reference layer thickness, the layer thickness d_x′ is determined, which may form the layer width that does not exceed the predetermined resolution, while the layer angle θ is kept.

Specifically, if “d_x/tan θ=layer width ΔL>0.29 mm”, d_x′ is determined such that “layer thickness d_x′≦0.29×tan θ” is satisfied.

Next, the number of divisions of the n+1 layer is determined. Here, the number m of layers generated with the determined layer thickness d_x′, the presence or absence of layer generated with a layer thickness different from the layer thickness d_x′, and the layer thickness d_x″ thereof are obtained using the following Equation (14).

d
_x
=m·d
_x
′+d
_x″ (14)

Here, m is an integer greater than or equal to 1, and 0<d_x″<d_x′.

Finally, shaping is conducted such that the obtained condition is satisfied. The m layers are shaped with the layer thickness d_x′ and, if d_x″ is present, 1 layer is further shaped with the layer thickness d_x″. That is, if d_x″ is not present, the n+1 layer is divided into m layers and shaping is conducted and, if d_x″ is present, the n+1 layer is divided into m+1 layers and shaping is conducted.

A specific example is given; if the layer angle θ is 30 degrees and the reference layer thickness is 0.29 mm, the layer thickness d_x′ is set to be equal to or less than 0.17 mm, as illustrated in the table of FIG. 14B. According to Equation (14), as “0.29 mm=1×0.17 mm+0.12 mm”, 1 layer with the thickness d_x′=0.17 mm may be shaped, and 1 layer with the thickness d_x″=0.12 mm may be shaped.

Furthermore, if the layer angle θ is 20 degrees and the reference layer thickness is 0.29 mm, the layer thickness d_x′ is set to be equal to or less than 0.11 mm, as illustrated in the table of FIG. 14B. According to Equation (14), as “0.29 mm=2×0.11 mm+0.05 mm”, 2 layers with the thickness d_x′=0.11 mm may be shaped, and 1 layer with the thickness d_x″=0.12 mm may be shaped.

As described above, the part with the reference layer thickness is divided into multiple layers and the shaping materials are laminated while the layer angle θ is kept; thus, the layer width may be prevented from exceeding a predetermined resolution.

Here, as it is understood from FIGS. 8, 11A to 11B, and 12, the layer thickness is determined in accordance with any one of the shaping material width of the shaping material discharged through the discharge opening and the distance between the head surface and the shaping stage (or the distance between the head surface and the uppermost part of the shaped object). The control unit controls any one of them to obtain the desired layer thickness.

Roughly speaking, the methods for reducing the shaping material width include the method of increasing the shaping velocity and the method of decreasing the conveying velocity of a shaping raw material. However, as the pitch in the shaping material becomes larger, the resolution is reduced (the resolving power becomes higher); therefore, there is a need to change the shaping material width without changing the pitch. Furthermore, when this control is performed, adjustment needs to be made such that the distance between the discharge opening and the shaping stage becomes shorter in accordance with the shaping material width (layer thickness).

Control Example and Configuration of the Control Unit: 1

An explanation is given of the process of shaping while increasing the shaping velocity as the method for reducing the shaping material width without changing the pitch. FIGS. 15A to 15C are schematic views that illustrate the shaping process. The state illustrated in FIG. 15A is the reference state.

The shaping flow quantity Q_xis given by “the cross-sectional area of the shaping material×the shaping velocity v_x” as represented by Equation (1). In a case where it is considered that the cross-sectional surface of the shaping material is rectangular, if the shaping velocity v_x(the moving speed on the XY plane of the shaping stage) is multiplied by α, as illustrated in FIG. 15B, the shaping material width may be 1/α. However, as the pitch P_xis accordingly multiplied by α according to Equation (2) and the resolution is decreased, the revolving speed f_x(the revolving speed of the rotary member) needs to be set to be α-fold, as illustrated in FIG. 15C, so that shaping is conducted while the pitch P_xis kept.

An explanation is given using a specific example. Here, in the following explanation, the cross-sectional surface of the shaping material is rectangular. The reference layer thickness of the shaped object is 0.25 mm, and the layer angle θ is 20 degrees in a case where the n+1 layer is shaped on the n layer with the reference layer thickness. In this case, the layer thickness of the n+1 layer needs to be set to be equal to or less than 0.11 mm.

With regard to the n+1 layer, as the ratio between the reference layer thickness and the adjusted layer thickness is “0.25 mm/0.11 mm=2.3”, the shaping velocity also needs to be 2.3-fold. If the reference shaping velocity is 10 mm/sec, the shaping velocity is 23 mm/sec. As illustrated in FIG. 10, the revolving speed, with which the pitch satisfies the resolution (0.29 mm), is equal to or more than the revolving speed of 80 rps.

FIG. 16 is a functional block diagram that illustrates a configuration of the control unit that performs the process according to the fourth embodiment. FIG. 16 particularly illustrates the configuration of the control unit that performs the control so as to increase the shaping velocity to reduce the shaping material width without changing the pitch.

Schematically, the control unit 200 includes a drawing-data input unit 201 to which three-dimensional drawing data is input; a shaping-condition calculating unit 210 that calculates a shaping condition on the basis of the drawing data input from the drawing-data input unit 201; and a drive control unit 220 that drives and controls each unit of the three-dimensional shaping device in accordance with the shaping condition calculated by the shaping-condition calculating unit 210.

The shaping-condition calculating unit 210 includes database 211, an angle calculating unit 212, a layer-thickness calculating unit 213, a shaping-velocity calculating unit 214, and a revolving-speed calculating unit 215.

The database 211 stores, as a table, the relation (the data illustrated in FIG. 14B) between the layer angle and the layer thickness, with which the layer width is equal to or less than the predetermined resolution. Furthermore, the database 211 stores, as a table, the relation (the data illustrated in FIG. 10) among the revolving speed, the shaping velocity, and 1 pitch of the shaping material.

The angle calculating unit 212 calculates the layer angle θ in a case where shaping is conducted with the reference layer thickness on the basis of the drawing data input from the drawing-data input unit 201.

The layer-thickness calculating unit 213 reads, from the data stored in the database 211, the layer thickness with which the layer width satisfies the predetermined resolution in a case where shaping is conducted using the layer angle calculated by the angle calculating unit 212.

The shaping-velocity calculating unit 214 calculates the shaping velocity on the basis of the ratio between the reference layer thickness and the adjusted layer thickness.

The revolving-speed calculating unit 215 reads the revolving speed with which 1 pitch satisfies a predetermined resolution from the data stored in the database 211 and the shaping velocity calculated by the shaping-velocity calculating unit 214.

The drive control unit 220 includes a stage-drive motor control unit 221z that drives the Z-direction motor that moves the shaping stage 71 in the direction of the Z axis; a stage-drive motor control unit 221xy that drives the X-direction motor and the Y-direction motor that move the shaping stage 71 in the direction of the X axis and in the direction of the Y axis, respectively; a twisting-motor control unit 222 that drives and controls the twisting motor 49; and a conveyance-motor control unit 223 that drives and controls the conveyance motor 17.

The stage-drive motor control unit 221z drives and controls the Z-direction motor such that the distance between the shaping stage 71 and the discharge opening is the layer thickness calculated by the layer-thickness calculating unit 213. The stage-drive motor control unit 221xy drives and controls the X-direction motor and the Y-direction motor such that the shaping stage 71 moves at the shaping velocity calculated by the shaping-velocity calculating unit 214. The twisting-motor control unit 222 drives and controls the twisting motor 49 such that the rotary member rotates at the revolving speed calculated by the revolving-speed calculating unit 215. The conveyance-motor control unit 223 drives and controls the conveyance motor 17 such that the shaping raw material is conveyed at the conveying velocity calculated by a conveying-velocity calculating unit 216.

FIG. 17 is the main flowchart of this control. FIG. 18 is a flowchart of the subroutine related to this control.

At Step S1, the drawing-data input unit 201 inputs the drawing data to the angle calculating unit 212 in the shaping-condition calculating unit 210.

At Step S3, on the basis of the input drawing data, the angle calculating unit 212 calculates the layer angle θ that is formed between the n+1 layer and the n layer if the n+1 layer is shaped with the reference layer thickness d_x.

At Step S5, the layer-thickness calculating unit 213 determines whether the calculated layer angle θ is equal to or more than a predetermined angle. That is, it is determined whether the calculated layer angle θ forms the layer width which obtains equal to or less than a predetermined resolution if shaping is conducted using the reference layer thickness. For example, in the table of FIG. 14B, it is determined whether the calculated layer angle θ is equal to or more than 45 degrees.

If the calculated layer angle θ is equal to or more than the predetermined angle (Yes at Step S5), the operation at Step S7 is performed.

At Step S7, the drive control unit 220 controls each unit of the three-dimensional shaping device such that the n+1 layer is shaped with the layer thickness d_x. That is, the stage-drive motor control unit 221z drives and controls the Z-direction motor, the stage-drive motor control unit 221xy drives and controls the X-direction motor and the Y-direction motor, the twisting-motor control unit 222 drives and controls the twisting motor 49, and the conveyance-motor control unit 223 drives and controls the conveyance motor 17. After the n+1 layer is shaped, the process is terminated.

If the calculated layer angle θ is less than the predetermined angle (No at Step S5), the operation at Step S9 is performed.

At Step S9, the layer-thickness calculating unit 213 calculates the layer thickness d_x′ that may form the layer width that satisfies a predetermined resolution if shaping is conducted with the layer angle θ. For example, if the predetermined resolution is 0.29 mm, d_x′ is determined such that “layer thickness d_x′≦0.29×tan θ” is satisfied. Here, the database 211 stores, as a table, the relation (the data illustrated in FIG. 14B) between the layer angle and the layer thickness, with which the layer width obtains equal to or less than the predetermined resolution so that the angle calculating unit 212 may refer to the table to determine the layer thickness.

At Step S11, the layer-thickness calculating unit 213 determines the number of divisions of the n+1 layer. Specifically, according to Equation (14), the layer-thickness calculating unit 213 calculates the number m of layers that are shaped with the layer thickness d_x′ and the presence or absence of layers that are shaped with the layer thickness d_x″ that satisfies “0<d_x″<d_x′”.

At Step S20, the subroutine “shaping-condition calculation/shaping process” is performed.

With reference to FIG. 18, “shaping-condition calculation/shaping process” at Step S20 is explained.

At Step S21, the shaping-velocity calculating unit 214 determines the shaping velocities v_x′, v_x″ with which shaping may be conducted with the layer thicknesses d_x′, d_x″. Specifically, in the case of the reference layer thickness d_xand the shaping velocity v_x, the shaping velocity is determined by “v_x′=v_x·(d_x/d_x′)”. Furthermore, the same holds for v_x″.

At Step S23, the revolving-speed calculating unit 215 determines the revolving speeds f_x′, f_x″ that may keep the pitch P_xif shaping is conducted at the shaping velocities v_x′, v_x″. The revolving speed is determined by “f_x′=f_x·(d_x/d_x′)”. Furthermore, the same holds for f_x″.

At Step S25, the drive control unit 220 controls each unit of the three-dimensional shaping device such that the n+1 layer is divided into multiple layers and shaping is conducted in accordance with the determined shaping condition. That is, the stage-drive motor control unit 221z drives and controls the Z-direction motor, the stage-drive motor control unit 221xy drives and controls the X-direction motor and the Y-direction motor, the twisting-motor control unit 222 drives and controls the twisting motor 49, and the conveyance-motor control unit 223 drives and controls the conveyance motor 17. After the thickness corresponding to the n+1 layer is shaped, the process is terminated.

Control Example and Configuration of the Control Unit: 2

An explanation is given of a method for reducing the conveying velocity of the shaping raw material as the method for reducing the shaping material width without changing the pitch. The shaping flow quantity Q_xis the sum of the conveying flow quantities Q_a, Q_b, . . . , of the shaping raw materials, and each conveying flow quantity is given by “the cross-sectional area of the shaping raw material×the conveying velocity v” as represented by Equation (1) (here, the description of the subscript index, indicating the parameter related to the shaping raw material, is omitted). If the conveying velocities of all the shaping raw materials are 1/α, the total conveying flow quantity is 1/α; therefore, the shaping flow quantity Q_xis also 1/α. In a case where the shaping velocity v_xis kept, if the cross-sectional surface of the shaping material is rectangular, the shaping material width is 1/α. Furthermore, in this control example, as neither the shaping velocity v_xnor the revolving speed f_xis changed, the pitch P_xis not changed.

An explanation is given using a specific example. Here, in the following explanation, the cross-sectional surface of the shaping material is rectangular. The reference layer thickness of the shaped object is 0.25 mm, and the layer angle θ is 20 degrees if the n+1 layer is shaped on the n layer with the reference layer thickness. In this case, the layer thickness of the n+1 layer needs to be set to be equal or less than 0.11 mm.

With regard to the n+1 layer, the ratio between the reference layer thickness and the adjusted layer thickness is “0.25 mm/0.11 mm=2.3”; therefore, in this control example, the conveying velocities of all the shaping raw materials may be “1/2.3”-fold.

FIG. 19 is a functional block diagram that illustrates a modified configuration of the control unit that performs the process according to the fourth embodiment. FIG. 19 illustrates particularly the configuration of the control unit that performs a control so as to increase the conveying velocity to reduce the shaping material width without changing the pitch. Here, the same reference numerals are applied to the same components as in FIG. 16, and the explanations of the same components are omitted.

The shaping-condition calculating unit 210 includes the conveying-velocity calculating unit 216 that calculates the conveying velocity of the shaping material in accordance with the ratio between the reference layer thickness and the adjusted layer thickness.

An explanation is given of this control in accordance with the flowcharts of FIGS. 17 and 20. FIG. 20 is a flowchart of the subroutine related to this control. As Steps S1 to S11 illustrated in FIG. 17 are the same as in the case where shaping is conducted while increasing the shaping velocity, the explanations of Steps S1 to S11 are omitted.

The subroutine “shaping-condition calculation/shaping process” at Step S20 is explained with reference to FIG. 20.

At Step S27, the conveying-velocity calculating unit 216 determines the conveying velocities v′, v″ of the shaping raw material with which shaping may be conducted with the layer thickness d_x′, d_x″, respectively (here, the description of the subscript index, indicating the parameter related to the shaping raw material, is omitted). The conveying velocity is determined for each shaping raw material. In the case of the reference layer thickness d_xand the conveying velocity v, the conveying velocity is determined by “v′=v·(d_x′/d_x)”. Furthermore, the same holds for v_x″.

At Step S29, the drive control unit 220 controls each unit of the three-dimensional shaping device such that the n+1 layer is divided into multiple layers and shaping is conducted in accordance with the determined shaping condition. That is, the stage-drive motor control unit 221z drives and controls the Z-direction motor, the stage-drive motor control unit 221xy drives and controls the X-direction motor and the Y-direction motor, the twisting-motor control unit 222 drives and controls the twisting motor 49, and the conveyance-motor control unit 223 drives and controls the conveyance motor 17. After the thickness corresponding to the n+1 layer is shaped, the process is terminated.

As described above, according to the present embodiment, the width (layer thickness) of the shaping material to be discharged is increased in accordance with the angle of the slope face of the shaped object; thus, the layer width does not exceed a predetermined resolution.

Fifth Embodiment

A fifth embodiment of the present invention is explained. The present embodiment is an embodiment according to a modified example of the rotary member that is applied to the three-dimensional shaping device according to the second embodiment illustrated in FIG. 8. FIG. 21 is a side view and a bottom view of the rotary member. Furthermore, the figure illustrates an example of the dimensions of the rotary member.

A rotary member 45A, illustrated in FIG. 21(a), includes a cylindrical twisting projection 47A that projects toward the shaping stage from the end 46a of the cylindrical drive shaft 46. The diameter of the twisting projection 47A is the same in the direction along the rotation center of the drive shaft. Furthermore, the twisting projection 47A is formed at an eccentric position from the rotation center.

A rotary member 45B, illustrated in FIG. 21(b), includes two cylindrical twisting projections 47B that are illustrated in FIG. 21(a). Each of the twisting projections 47B is formed at an eccentric position from the rotation center. With the provision of the twisting projections 47B, the shaping raw material is further mixed.

A rotary member 45C, illustrated in FIG. 21(c), includes two cylindrical twisting projections 47C, 47C that are tapered toward the shaping stage from the end 46a of the cylindrical drive shaft 46. The twisting projection 47C has a taper shape whose diameter is larger at the side of the drive shaft 46 and is smaller at the side of the shaping stage. Each of the twisting projections 47C, 47C is formed at an eccentric position from the rotation center. As the twisting projection 47C has a taper shape, the strength of the twisting projection 47C may be increased, and it is possible to prevent damage due to fluid resistance of the shaping raw material, which is applied during twisting.

A rotary member 45D, illustrated in FIG. 21(d), includes a fan-shaped twisting projection 47D in a cross-sectional shape in the direction perpendicular to the Z axis. The twisting projection 47D includes an outer-circumference side surface 47b and an inner-circumference side surface 47c as two side surfaces that extend along a circumferential direction (rotation direction). As the twisting projection 47D has a predetermined thickness (circumferential-direction length) along the rotation direction of the drive shaft 46, the strength of the twisting projection 47D may be increased, and it is possible to prevent damage due to fluid resistance of the shaping raw material, which is applied during twisting.

The modified examples of the rotary member are explained above and, in order to improve the coloration efficiency of shaping raw materials, it is preferable that the twisting projection is provided on the outer circumference side of the drive shaft. This is because, with regard to the shaped object, the outer side of the shaping material is visually observed, and therefore it is preferable that the coloration efficiency is improved at the outer circumference side rather than the inner side.

Sixth Embodiment

A sixth embodiment of the present invention is explained. The present embodiment is an embodiment according to a modified example of the rotary member that is applied to the three-dimensional shaping device according to the second embodiment illustrated in FIGS. 8 and 9. FIG. 22 is a view that corresponds to the D-D cross-sectional surface of the twisting section illustrated in FIG. 8.

Each of the runners 35 and each of the gates 43 are arranged such that each of the shaping raw materials 100 is caused to flow into the twisting conveyance path 41 in a direction along the twisting direction of the shaping material 101 within the twisting conveyance path 41. As each of the runners 35 conveys the shaping raw material 100 toward the position off the center of the twisting conveyance path 41, the center line of the runner 35 is arranged at the position off the central axis of the twisting conveyance path 41.

In the illustrated example, the shaping raw material 100 files the twisting conveyance path 41 while rotating in a counterclockwise direction due to the inertia force. Therefore, without rotation of the twisting projection 47 of the rotary member 45, the shaping raw material 100 is twisted independently so as to make coloration. According to the present embodiment, as the twisting projection 47 is also rotated in a counterclockwise direction, coloration is further facilitated.

[Aspects and Advantages]

Each of the embodiments of the present invention may be implemented in the following aspects.

The three-dimensional shaping method according to the present aspect is the three-dimensional shaping method for deforming (heating and melting) and depositing the shaping raw material 100 in a predetermined solid shape, and the three-dimensional shaping method has the feature that the three-dimensional shaping method includes a conveying process during which a conveying unit (the conveying section 10) conveys multiple shaping raw materials (the shaping raw materials 100 in different colors) to a deforming unit (the heat melting section 31); a deforming process during which the deforming unit deforms each of the shaping raw materials; a shaping-material forming process during which a shaping-material forming unit (the shaping-material forming section 30) twists and arranges the deformed shaping raw materials in a helical fashion, thereby forming the shaping material 101; and a shaping process during which a shaping unit (the shaping section 70) sequentially deposits the shaping materials to form the three-dimensional shaped object 102.

According to the present aspect, multiple shaping raw materials are twisted and arranged in a helical fashion to form a shaping material, and a shaped object is formed using the shaping materials. If shaping raw materials in different colors are used as the shaping raw materials, a shaped object may be formed by using a shaping material in any color.

The three-dimensional shaping method according to the present aspect has the feature that a three-dimensional shaped object is formed while controlling at least one of the conveying velocity of a shaping raw material during the conveying process, the twisting speed of a shaping raw material during the shaping-material forming process, and the shaping velocity during the shaping process.

According to the present aspect, the conveying velocity, the twisting speed, and the shaping velocity are appropriately adjusted so that the deposition interval or the deposition percentage of shaping raw materials included in the shaping material or the thickness of the shaping material is arbitrarily adjusted. As this control is performed, shaping materials with the desired color and resolution may be generated, and therefore it is possible to obtain three-dimensional shaped objects with higher color representation and higher resolution.

The three-dimensional shaping method according to the present aspect has the feature that the thickness of the second shaping material is controlled in accordance with the angle of the slope face of the shaping material that is formed by the first shaping material, which forms the first layer, and the second shaping material which is laminated on the first shaping material to form the second layer.

According to the present aspect, the thickness of the second shaping material is controlled in accordance with the angle of the slope face of the formed shaped object so that the shaping width may be adjusted. Here, the shaping width is the gap between the edge of the first shaping material, which forms the first layer, and the edge of the second shaping material, which forms the second layer, in a horizontal direction. If a control is performed such that the shaping width is reduced, the resolution of a three-dimensional shaped object may be improved in a lamination direction of each shaping material.

The present aspect is related to the three-dimensional shaping device that implements the three-dimensional shaping method according to the first aspect. Specifically, the present aspect is the three-dimensional shaping device 1 that deforms (heats and melts) and deposits the shaping raw material 100 in a predetermined solid shape, thereby forming a three-dimensional shaped object, and has the feature that three-dimensional shaping device includes multiple conveying units (the conveying section 10) that convey multiple shaping raw materials (the shaping raw materials 100 in different colors) to the deforming unit (the heat melting section 31); the deforming unit (the heat melting section 31) that deforms the shaping raw material that is conveyed by each of the conveying units; the shaping-material forming unit (the shaping-material forming section 30) that twists and arranges the deformed shaping raw materials in a helical fashion, thereby forming the shaping material 101; and the shaping unit (the shaping section 70) that sequentially deposits the shaping materials to form the three-dimensional shaped object 102.

According to the present aspect, in the same manner as the first aspect, multiple shaping raw materials are twisted and arranged in a helical fashion to form a shaping material, and a shaped object is formed using the shaping material. If shaping raw materials in different colors are used as the shaping raw materials, a shaped object may be formed using a shaping material in any color.

In the three-dimensional shaping device according to the present aspect, the shaping-material forming unit (the shaping-material forming section 30) has the feature that the shaping-material forming unit includes the twisting conveyance path 41 that conveys the deformed shaping raw materials 100 while twisting and arranging the shaping raw materials 100 in a helical fashion; and the rotary member 45 that is located upstream in the twisting conveyance path and that is rotated about the axis parallel to the conveying direction of the twisting conveyance path.

Due to the rotation of the rotary member, the three-dimensional shaping device twists and arranges the shaping raw material in a helical fashion. According to the present aspect, shaping raw materials may be twisted with a simple configuration, and colorful three-dimensional shaped objects may be obtained.

In the three-dimensional shaping device according to the present aspect, the rotary member 45 has the feature that the rotary member 45 includes the drive shaft 46 that is rotated and driven; and the twisting projection 47 that is formed to protrude from the end of the drive shaft downstream in the twisting conveyance path 41 and that is eccentrically positioned with respect to the rotation center of the drive shaft.

As the twisting projection is provided in the rotary member, shaping raw materials may be twisted more efficiently.

In the three-dimensional shaping device according to the present aspect, the shaping-material forming unit (the shaping-material forming section 30) has the feature that the shaping-material forming unit includes multiple deformed raw-material conveyance paths (the runners 35) that each convey the deformed shaping raw material; and the gates 43 through which each shaping raw material flows into the twisting conveyance path 41 from each of the deformed raw-material conveyance paths, the end 46a of the drive shaft 46 is located upstream of the gates in the twisting conveyance path, and the end 47a of the twisting projection 47 is located between the position that is substantially the same as the downstream end of each of the gates in the twisting conveyance path and the position such that the end 47a is in contact with the shaping unit (the shaping section 70).

The flowability (flow distribution) of the shaping material, discharged into the shaping unit, may be uniform, and high-contrast three-dimensional shaped objects may be obtained.

In the three-dimensional shaping device according to the present aspect, the gates 43 have the feature that the gates 43 are arranged such that the shaping raw materials 100 are caused to flow into the twisting conveyance path 41 in directions along the twisting direction of the shaping material 101 within the twisting conveyance path 41.

It is possible to obtain a shaping material that is naturally twisted in arrangement due to the inertia force of shaping raw materials.

According to the present aspect, a configuration is such that each shaping raw material is twisted after being discharged toward the shaping unit through the discharge opening; therefore, each shaping raw material is arranged in a helical fashion in a separated state, and colors are unlikely to be mixed.

The present aspect produces an advantage in improving the shape accuracy or the dimension accuracy as well as full-color shaping. The present aspect is the method for controlling the orientation direction of resin by control of the rotation direction of a rotary member to promote averaging of the shrinking rate (prevention of anisotropy).

The problem is explained using the example (FIG. 23). FIG. 23(a) is a view of the state where shaping is conducted in the solid line from (A) (shaping from left to right) to (B) (shaping upward at a right angle) using a conventional shaping method without any rotation mechanisms as viewed diagonally, and FIG. 23(b) is a view as viewed from the top. Here, the shaped object is cooled at room temperature, and the shaped object is deformed in the direction of the dotted line; thus, the dimension accuracy is degraded. This is because the shrinking rate is different in the orientation direction (the shrinking rate is large in the orientation parallel direction, and is small in the orthogonal direction). Here, for convenience of explanation, the difference between the shrinking rate in the orientation parallel direction and the shrinking rate in the orthogonal direction is defined as the shrinking-rate difference. In the corner section, the shrinking-rate difference is large at the outer circumference; therefore, the angle at the corner section is an obtuse angle, and the shape accuracy is degraded.

Conversely, FIGS. 24A to 24B illustrate the state of shaping according to the present aspect. FIG. 24A is a view from the side surface, and FIG. 24B is a view from the top. FIG. 24A illustrates the state of shaping where two types of shaping materials are arranged in a helical fashion in order to easily understand the orientation direction. Here, the orientation of the shaping material during shaping is in the same direction as the arrangement direction of the helix. Furthermore, the shrinking-rate difference is also the same as the arrangement direction of the helix. Furthermore, because of the helical structure, the orientations are in the opposite directions at the front side and the rear side as viewed from the side. The orientations of the upper side and the lower side as viewed from the top are also in the opposite directions. The shrinking-rate difference also exhibits the similar tendency. In the case of the helix, as compared to the one that is not helical, due to the rotation by 360 degrees for the shrinking-rate difference as described above, in total, the shrinking-rate difference for one rotation is small. Particularly, if the helix angle is 45 degrees, the shrinking-rate difference for one rotation is smallest. Therefore, shape deformation is also smallest.

Furthermore, the shape of a shaped object tends to change in the direction in which the helix is loosened due to changes with the passage of long time. Therefore, the lower layer section (the n−1 layer) and the upper layer section (the n layer) of the shaped object are in the opposite helical directions (=the twisting directions of the rotary member are opposite) so that an effect is produced such that each other's shape changing directions are eliminated and the shape is stabilized.

Furthermore, this aspect corresponds to the twisting speed according to claim 2 of the present invention. This aspect is an example where the twisting direction is in an opposite direction.

In the case of the conventional shaping method without any rotation mechanisms, there is a problem in that, as the shaped object lower layer section (the n−1 layer) has a low temperature that is equal to or less than the melt temperature, when the shaped object upper layer (the n layer) is brought into contact with the shaped object lower layer section (the n−1 layer) during shaping, the temperature of the shaped object upper layer is rapidly decreased and the shaped object upper layer is hard to tightly adhere with the help of fusion. The small adherence force between the layers causes a decrease in the mechanical strength of the shaped object.

According to the present aspect, it is possible to produce an advantage in improving the mechanical strength as well as full-color shaping.

The configuration and the operation are described below.

1) The method and the device arranges the twisting projection of the rotary member in the vicinity of the shaped object lower layer to provide the shearing force to increases the adherence force on the interface due to local temperature increase, pressure generation, and mixing, to improve the mechanical strength.

2) The method and the device brings the twisting projection of the rotary member into contact with the shaped object lower layer to scrape the shaped object lower layer to increase the adherence force on the interface due to the roughness of the front surface, to improve the mechanical strength.

An explanation is given of 1) with reference to FIG. 25.

According to the present aspect, as the rotation mechanism is provided, the shearing heat of the shaping material occurs due to rotation of the rotary member. Therefore, the temperature of the shaping material locally increases, and the adherence force with the shaped object lower layer section increases.

As the twisting projection of the rotary member extends to the shaped object lower layer section (the n−1 layer), the pressure and the shearing force are easily transmitted to the shaped object lower layer section (the n−1 layer); therefore, part of the shaped object lower layer section (the n−1 layer) is melted, and is mixed with the shaped object upper layer section (the n layer), and the adherence force further increases. Thus, the adherence force is increased, and the mechanical strength is improved.

An explanation is given of 2) with reference to FIG. 26.

According to the present aspect, a configuration is such that the twisting projection of the rotary member extends into the shaped object lower layer section (the n−1 layer). Therefore, the heat of the twisting projection is easily and directly transmitted to the shaped object lower layer section, and the shaped object lower layer section is easily melted.

Furthermore, due to rotation of the rotary member, shearing heat occurs in the shaped object lower layer section, which facilitates melting.

As shaping materials are continuously supplied in the above-described melting state, the pressure is easily transmitted, and instant abutment is achieved so that the adherence force is improved. Furthermore, even if there is air on the interface, the air may be dispersed due to the rotation mechanism, and the adherence force may be further improved. Thus, the adherence force is increased, and the mechanical strength is improved.

According to an embodiment, multiple deformed shaping raw materials are twisted and arranged in a helical fashion so that a shaping material is formed, and the formed shaping material is sequentially deposited to form a three-dimensional shaped object. It is possible to provide a novel three-dimensional shaping method and a three-dimensional shaping device that forms a solid object using a shaping material that is formed from multiple shaping raw materials.

The above-described embodiments are illustrative and do not limit the present invention. Thus, numerous additional modifications and variations are possible in light of the above teachings. For example, at least one element of different illustrative and exemplary embodiments herein may be combined with each other or substituted for each other within the scope of this disclosure and appended claims. Further, features of components of the embodiments, such as the number, the position, and the shape are not limited the embodiments and thus may be preferably set. It is therefore to be understood that within the scope of the appended claims, the disclosure of the present invention may be practiced otherwise than as specifically described herein.

The method steps, processes, or operations described herein are not to be construed as necessarily requiring their performance in the particular order discussed or illustrated, unless specifically identified as an order of performance or clearly identified through the context. It is also to be understood that additional or alternative steps may be employed.

Each of the functions of the described embodiments may be implemented by one or more processing circuits or circuitry. Processing circuitry includes a programmed processor, as a processor includes circuitry. A processing circuit also includes devices such as an application specific integrated circuit (ASIC), digital signal processor (DSP), field programmable gate array (FPGA) and conventional circuit components arranged to perform the recited functions.

REFERENCE SIGNS LIST

- 1 THREE-DIMENSIONAL SHAPING DEVICE
- 10 CONVEYING SECTION
- 11 CONVEYING MECHANISM
- 13 RAW-MATERIAL CONVEYANCE PATH
- 15 CONVEYANCE GEAR
- 17 CONVEYANCE MOTOR
- 20 HEAT INSULATING MEMBER
- 21 PATH
- 30 SHAPING-MATERIAL FORMING SECTION
- 31 HEAT MELTING SECTION
- 33 HEATER
- 35 RUNNER
- 40 TWISTING SECTION
- 41 TWISTING CONVEYANCE PATH
- 43 GATE
- 45 ROTARY MEMBER
- 46 DRIVE SHAFT
- 46
  a END
- 47 TWISTING PROJECTION
- 47
  a END
- 49 TWISTING MOTOR
- 60 HEAD SECTION
- 61 DISCHARGE OPENING
- 63 HEAD SURFACE
- 65 DISCHARGE OPENING
- 70 SHAPING SECTION
- 71 SHAPING STAGE
- 73 STAGE DRIVE MOTOR
- 81 HOLLOW SECTION
- 83 ROTARY MEMBER
- 85 FLOW PATH
- 87 CIRCULAR RECESSED SECTION
- 100 SHAPING RAW MATERIAL
- 101 SHAPING MATERIAL
- 102 SHAPED OBJECT
- 200 CONTROL UNIT
- 210 SHAPING-CONDITION CALCULATING UNIT
- 211 DATABASE
- 212 ANGLE CALCULATING UNIT
- 213 LAYER-THICKNESS CALCULATING UNIT
- 214 SHAPING-VELOCITY CALCULATING UNIT
- 215 REVOLVING-SPEED CALCULATING UNIT
- 216 CONVEYING-VELOCITY CALCULATING UNIT
- 220 DRIVE CONTROL UNIT
- 221
  xy STAGE-DRIVE MOTOR CONTROL UNIT
- 221
  z STAGE-DRIVE MOTOR CONTROL UNIT
- 222 TWISTING-MOTOR CONTROL UNIT
- 223 CONVEYANCE-MOTOR CONTROL UNIT

	Number	Date	Country
Parent	PCT/JP2015/062346	Apr 2015	US
Child	15386259		US

THREE-DIMENSIONAL SHAPING METHOD AND THREE-DIMENSIONAL SHAPING DEVICE METHOD

Information

Publication Number

Date Filed

Date Published

Inventors

CPC

International Classifications

Abstract

Description

Claims

Priority Claims (1)

CROSS-REFERENCE TO RELATED APPLICATIONS

Continuations (1)