Three-piece solid golf ball

FIELD OF THE INVENTION
The present invention relates to a three-piece solid golf. More particularly, it relates to a three-piece solid golf ball having excellent flying performances, stability upon iron shot and good hit feeling.
BACKGROUND OF THE INVENTION
Recently, a two-piece solid golf ball or a three-piece solid golf ball comprising a cover and a solid core of one or two layers has been particularly popular with average golfers because of its large flying distance.
In the two-piece solid golf ball or three-piece solid golf ball, a high-rigid ionomer resin is normally used as a base resin of the cover so as to enhance impact resilience, thereby increasing flying distance.
However, the two-piece solid golf ball or three-piece solid golf ball using the high-rigid ionomer resin as the base resin of the cover has excellent characteristics that a flying distance is large, but has serious drawbacks as described in the following items (1) and (2).
(1) Since a slip is arisen on the face surface of the iron club at the time of shot, amount of spin largely varies and a flying distance is not stable. Particularly, drop ball, i.e. so-called flyer ball is liable to be arisen because of abnormal deterioration of spin at the time of iron shot from the rough.
(2) Hard hit feeling is obtained at the time of hitting because of the material of the cover, and the hit feeling is inferior.
Therefore, in order to improve the above drawbacks, there have been developed a two-piece solid golf ball using a flexible cover material (see Japanese Kokai Publication Hei 1(1989)-308577).
In the two-piece solid golf ball using a flexible cover material, instability upon iron shot and hard hit feeling caused by the cover have already been solved. However, since a very hard core is used so as to make up for deterioration of impact resilience accompanied with the flexibility of the cover, excessive spin is put on the golf ball, which results in drastic decrease in flying distance. Further, the impact force increases because of hard core, Which results in deterioration of hit feeling.
As described above, a conventional two-piece solid golf ball or three-piece solid golf ball has such a drawback that a golf ball attaining a large flying distance is inferior in stability upon iron shot and hit feeling and, on the contrary, a golf ball having good stability upon iron shot and hit feeling attains a short flying distance. Therefore, there has been no golf ball which satisfies flying distance, stability upon iron shot and hit feeling, simultaneously.
OBJECTS OF THE INVENTION
The main object of the present invention is to provide a solid golf ball having excellent flying performances, stability upon iron shot and good hit feeling, simultaneously, which have never been accomplished by a conventional two-piece solid golf ball or three-piece solid golf ball.
This object as well as other objects and advantages of the present invention will become apparent to those skilled in the art from the following description with reference to the accompanying drawing.

BRIEF EXPLANATION OF DRAWINGS
FIG. 1 is a schematic cross section illustrating one embodiment of the three-piece solid golf ball of the present invention.

SUMMARY OF THE INVENTION
The present invention provides a three-piece solid golf ball comprising a two-piece solid core and a cover for covering the two-piece solid core, the two-piece solid core being composed of a center and an outer shell covering the center, wherein the center, the outer shell and the cover have the following characteristics respectively:
(1): Center
Diameter: 30.7 to 39.5 mm
Physical properties: stiffness: 300 to 2,500 kgf/cm.sup.2
shore D hardness: 30 to 55
Composition: vulcanized rubber obtained from a butadiene rubber, co-crosslinkable monomer, zinc oxide and peroxides as an essential component
(2) Outer shell
Thickness: 1.0 to 4.0 mm
Physical properties: stiffness: 2,500 to 6,000 kgf/cm.sup.2
shore D hardness: 55 to 75
Composition: vulcanized rubber obtained from a butadiene rubber, a co-crosslinkable monomer, zinc oxide and peroxides as an essential component
(3): Cover
Thickness: 0.6 to 2.0 mm
Physical properties: stiffness: 1,000 to 2,500 kgf/cm.sup.2
shore D hardness: 40 to 55
Composition: cover obtained from an ionomer resin or a mixture of the ionomer resin and a flexible resin as a base resin.
That is, the present invention has succeeded in providing a three-piece solid golf ball having stability upon iron shot, excellent flying performances and good hit feeling by exhibiting characteristics of the above center, outer shell and cover.
(1) Stability upon iron shot
As described above, since a low-rigid and flexible cover material having a stiffness of 1,000 to 2,500 kgf/cm.sup.2 and a shore D hardness of 40 to 55 is used as the cover, no slip is arisen at the time of shot and scatter of flying distance is inhibited and, further, stability upon iron shot can be obtained.
(2) Flying performances
By reducing the thickness of the flexible cover which causes deterioration of impact resilience to the utmost and disposing a high-rigid outer shell having excellent impact resilience on the interior of the cover, the impact resilience and initial velocity of the golf ball can be maintained at a suitable level.
Since the high-rigid outer shell is disposed in the vicinity of the exterior of the golf ball and the center has a comparatively large diameter and low rigidity, a local breakage is not arisen in the vicinity of the surface of the golf ball at the time of hitting even if the flexible cover is used, but the whole golf ball is liable to be deformed. Accordingly, since the turning moment, which is produced at a loft of the club when the golf ball is deformed by hitting with the club, becomes small, excessive spin is not arisen and the launch angle becomes large.
That is, regarding the three-piece solid golf ball of the present invention, excessive spin is not arisen even if the flexible cover is used. Therefore, the golf ball has characteristics similar to those of the conventional two-piece solid golf ball using the high-rigid cover in view of initial three elements of flying performances of the golf ball (e.g. initial velocity, launch angle and spin amount), thereby providing a golf ball having a large flying distance.
(3) Hit feeling
Since the center has a low rigidity and is easily deformed, the impact force at the time of hitting is small, thereby affording light hit feeling. Further, good feeling can be obtained by combining with a soft hit feeling of the golf ball with the flexible cover.
DETAILED DESCRIPTION OF THE INVENTION
Next, the construction of the three-piece solid golf ball of the present invention will be explained with reference to the accompanying drawing.
FIG. 1 is a schematic cross section illustrating one embodiment of the three-piece solid golf ball of the present invention. In FIG. 1, 1 is a solid core and the solid core 1 has two layers of a center 1a and an outer shell 1b. Then, 2 is a cover for covering the solid core 1 having the two-layer structure, the cover 2 being provided with a dimple 2a.
Firstly, the cover 2 will be explained. The thickness of the cover 2 is comparatively thin, i.e. 0.6 to 2.0 mm, preferably 0.8 to 1.8 mm. When the thickness of the cover is smaller than 0.6 mm, durability such as cut resistance is deteriorated. On the other hand, when it is larger than 2.0 mm, impact resilience are deteriorated, which results in deterioration of flying distance.
Regarding physical properties of the cover 2, the stiffness is 1,000 to 2,500 kgf/cm.sup.2 and the shore D hardness is 40 to 55. The cover 2 has the stiffness lower than the stiffness (about 3,000 to 4,000 kgf/cm.sup.2) of the golf ball with high-rigid cover and is flexible so that a slip at the time of iron shot is prevented and good hit feeling can be obtained.
Regarding this cover 2, when the stiffness and shore D hardness are larger than the above range, the flexibility is deteriorated and a slip at the time of iron shot can not be prevented. On the contrary, when they are lower than the above range, deterioration of cut resistance and impact resilience is arisen.
Then, the composition of this cover 2 will be explained. As the base resin of this cover 2, there can be used an ionomer resin having excellent impact resilience and cut resistance or a mixture of the ionomer resin and flexible resin. In the present invention, the latter mixture of the ionomer resin and flexible resin is particularly excellent.
Examples of the ionomer resin include high-rigid ionomer resins and low-rigid ionomer resins. Examples of the high-rigid ionomer resin include Hi-milane #1605, #1707 and #1706 (trade name) which are commercially available from Mitsui Du Pont Polychemical Co., Ltd. Examples of the low-rigid ionomer resin include Hi-milane #1855 and #1856 (trade name).
Examples of the flexible resin include ethylene-isobutyl acrylate-methacrylic acid terpolymer resins such as Nucrel AN42121C and Nucrel NO825J (trade name) which are commercially available from Mitsui Du Pont Polychemical Co., Ltd. Other examples of the flexible resin include ethylene-ethyl acrylate-maleic anhydride terpolymer resins such as Bondine AX8390 and TX8030 (trade name) which are commercially available from Sumitomo Chemical Industries Co., Ltd.
When using only ionomer resin as the base resin of the cover 2, the low-rigid ionomer resin may be used alone (using single low-rigid ionomer resin or mixture of low-rigid ionomer resins) or a mixture of the high-rigid ionomer resin and low-rigid ionomer resin may be used. Also, when using the mixture of the ionomer resin and flexible resin as the base resin of the cover 2, a mixture of the high-rigid ionomer resin and flexible resin may be used or a mixture of the high-rigid ionomer resin, low-rigid ionomer resin and flexible resin may be used. Further, when using various reins in combination, metallic neutralization/modification due to magnesium hydroxide may be suitably provided.
A resin composition for the cover 2 may be prepared by formulating pigments such as titanium dioxide, barium sulfate, etc. and, if necessary, antioxidants into the above ionomer resin or the mixture of ionomer resin and flexible resin as a base resin. Further, it is possible to add a suitable amount (40% by weight or less) of the other resin in the base resin unless characteristics of the base resin are deteriorated.
Hereinafter, the thickness, the physical properties and the composition of the outer shell 1b will be explained.
The thickness of the outer shell 1b is 1.0 to 4.0 mm, preferably 1.5 to 3.5 mm. When the thickness of the outer shell 1b is smaller than 1.0 mm, it is impossible to impart a suitable rigidity to the golf ball and, therefore, desired impact resilience can not be obtained. Further, when the thickness of the outer shell 1b is larger than 4.0 mm, the golf ball becomes too hard and the hit feeling becomes inferior. Further, since the diameter of the center 1a becomes small, the deformation of the golf ball at the time of hitting becomes insufficient and excessive spin is liable to be arisen.
Regarding the physical properties of this outer shell 1b, the stiffness is 2,500 to 6,000 kgf/cm.sup.2, preferably 3,000 to 5,500 kgf/cm.sup.2 and the shore D hardness is 55 to 75, preferably 58 to 72. As is apparent from these stiffness value and shore D hardness value, the outer shell 1b has a high rigidity and high hardness. Since the outer shell 1b has these physical properties, deterioration of impact resilience and local collapse of the part in the vicinity of the surface at the time of shot are prevented by the flexible cover in thickness of 1 to 4 mm. Thus, excellent flying performances which are one of the feature of the present invention can be obtained.
This outer shell 1b will be explained in the aspect of the composition. That is, this outer shell 1b is composed of a vulcanized rubber of a rubber composition containing a butadiene rubber, a co-crosslinkable monomer, zinc oxide and peroxides.
The outer shell 1b which is hard and superior in impact resilience and durability can be obtained from this rubber composition.
As the butadiene rubber, a high-cis butadiene rubber having a cis content of 80% or more is preferred. If necessary, natural rubber, isoprene rubber, styrene-butadiene rubber, styrene-propylene-diene rubber (EPDM), etc. can be suitably formulated in the base rubber of butadiene rubber to give a rubber component. As is apparent from this description, the rubber component of the outer shell 1b may contain the butadiene rubber as the base rubber, but the base rubber is not limited to the butadiene rubber.
The co-crosslinkable monomer is a monovalent or divalent metallic salt of .alpha.,.beta.-ethylenically unsaturated carboxylic acid. Examples of this co-crosslinkable monomer include zinc diacrylate, basic zinc methacrylate, zinc dimethacrylate and the like. Among them, zinc diacrylate is particularly preferred. The amount of this co-crosslinkable monomer is not specifically limited and is adjusted so that the stiffness and shore D hardness may be within the above range. For example, the stiffness and shore D hardness within the desired range can be obtained by formulating the co-crosslinkable monomer in the amount of 35 to 65 parts by weight based on 100 parts by weight of the rubber component.
The rubber composition of the outer shell 1b contains zinc oxide and peroxides as the constituent component, in addition to the rubber component containing the butadiene rubber as the constituent component and co-crosslinkable monomer. The zinc oxide is used as a supplement crosslinking agent and filler and is normally formulated in the amount of 5 to 25 parts by weight based on 100 parts by weight of the rubber component. Peroxides act as an initiator for crosslinking and graft polymerization of the rubber and co-crosslinkable monomer, and examples thereof include dicumyl peroxide, 1,1-bis(t-butylperoxy)-3,3,5-trimethylcyclohexane and the like. The amount of peroxides is normally 0.2 to 5 parts by weight based on 100 parts by weight of the rubber component.
For example, fillers (e.g. barium sulfate, etc.), antioxidants, additives (e.g. zinc stearate, etc.) may be formulated in the rubber composition for outer shell 1b, if necessary.
Hereinafter, the diameter, the physical properties and the composition of the center 1a will be explained.
The diameter of the center 1a varies depending on the outer diameter of the golf ball [set outer diameter is within a range of 42.7 mm (+0.1 mm, -0.03 mm)] and the thickness of the cover and outer shell, and is 30.7 to 39.5 mm, preferably 33.1 to 38.1 mm.
Regarding the physical properties of this center 1a, the stiffness is 300 to 2,500 kgf/cm.sup.2, preferably 500 to 2,300 kgf/cm.sup.2 and the shore D hardness is 30 to 55, preferably 32 to 53. As is apparent from these stiffness value and shore D hardness value, the center 1a is comparatively flexible. Since the center 1a has these physical properties, the deformation degree at the time of hitting can be sufficiently increased, thereby decreasing the impact force.
The center 1a is also composed of a vulcanized rubber of a rubber composition containing a butadiene rubber, a co-crosslinkable monomer, zinc oxide and peroxides.
The rubber component and the material of formulation components used for preparing a rubber composition for center 1a are the same as those used for preparing the rubber composition for the outer shell 1b. In order to impart the above-described physical properties such as stiffness, shore D hardness, etc., it is necessary to reduce the amount of the co-crosslinkable monomer in comparison with the outer shell 1b, and the amount of the co-crosslinkable monomer is suitably about 15 to 35 parts by weight based on 100 parts by weight of the rubber component.
The three-piece solid golf ball of the present invention may be prepared, for example, by the following method.
Firstly, a rubber composition for center 1a is normally placed in a mold and subjected to a press molding. The crosslinking condition at the time of press molding is preferably as follows: temperature: 130.degree. to 180.degree. C., time: 10 to 50 minutes. The temperature at the time of press molding is not necessarily constant and it may be changed in two stages or more.
The molding of the outer shell 1b is conducted by laminating a sheet-like rubber composition for outer shell 1a having a desired thickness on an center 1a which has been prepared in advance, followed by press molding, but it is not limited to this method. For example, there can also be used a method comprising molding a couple of half-shells and laminating them each other or a method of molding according to an injection system.
The cover 2 is prepared by covering the solid core 1 having a two-layer structure with a cover composition wherein inorganic oxides such as titanium dioxide, etc., additives such as photostabilizer, etc. are suitably added to the base resin, if necessary. At the time of covering, an injection molding method is normally used but is not specifically limited.
If necessary, desired dimples are formed when the cover is prepared and, after the cover 2 was molded, the golf ball is provided with a painting and stamping, if necessary.
As described above, the three-piece solid golf ball of the present invention having excellent flying performances, stability upon iron shot and good hit feeling.
EXAMPLES
The following Examples and Comparative Examples further illustrate the present invention in detail but are not to be construed to limit the scope thereof.
Examples 1 to 10 and Comparative Examples 1 to 10
Among the above Examples and Comparative Examples, Examples 1 to 10 and Comparative Examples 1 to 8 relate to a three-piece solid golf ball and Comparative Examples 9 to 10 relate to a conventional typical two-piece solid golf ball.
Regarding the three-piece solid golf ball, a rubber composition for center and a rubber composition for outer shell are prepared, respectively, from formulation components described in each table. Then, the rubber composition is crosslinked according to a predetermined condition, and the stiffness and shore D hardness of the resulting crosslinked product are measured. The results are shown in each table. Further, a composition for cover is also prepared from formulation components described in each table, and the stiffness and shore D hardness are measured. The results are shown in each table.
Regarding the two-piece solid golf ball, a rubber composition for core is prepared from formulation components described in Table 16. Then, the rubber composition is crosslinked according to a predetermined condition, and the stiffness and shore D hardness of the resulting crosslinked product are measured. The results are shown in Table 16. Further, a composition for cover is also prepared from formulation components described in Table 17, and the stiffness and shore D hardness are measured. The results are shown in Table 17.
The measuring method of the stiffness and shore D hardness are as follows.
A molded sheet having a thickness of about 2 mm was stored at 23.degree. C. for 2 weeks and the stiffness was measured according to ASTM D-747. The shore D hardness was measured according to ASTM D-2240. In that case, it is difficult to obtain a molded sheet for specimen from the center, outer shell and cover, respectively, so they were prepared as follows.
The molded sheets for specimen of center and outer shell were prepared by subjecting the respective rubber compositions to a heat press molding under the crosslinking condition as described in the table. The molded sheet for specimen of cover was prepared by subjecting the respective cover compositions to a heat press molding as they are.
Amounts in each table are by weight and the common material will be explained only in the first table.
TABLE 1______________________________________ Example Example Example Example 1 2 3 4______________________________________Formulation of centerButadiene rubber *1 100 100 100 100Zinc diacrylate 25 25 25 30Zinc oxide 18.5 18.5 18.5 16.5Antioxidant *2 0.5 0.5 0.5 0.5Dicumyl peroxide 1.2 1.2 1.2 1.2Crosslinking condition 160 .times. 25 160 .times. 25 160 .times. 25 160 .times. 25(.degree.C. .times. minutes)Diameter of center 34.9 34.9 34.9 33.9(mm)Stiffness (kgf/cm.sup.2) 1300 1300 1300 1800Shore D hardness 44 44 44 49______________________________________ *1: Highcis butadiene rubber JSR BR11 (trade name), manufactured by Nihon Synthetic Rubber Co., Ltd. Mooney viscosity ML.sub.1+4 (100.degree. C.) = 43 *2: Yoshinox 425 (trade name), manufactured by Yoshitomi Seiyaku Co., Ltd
TABLE 2______________________________________ Example Example Example Example 1 2 3 4______________________________________Formulation ofouter shellButadiene rubber 100 100 100 100Zinc diacrylate 40 50 60 40Zinc oxide 12.5 9.0 5.0 12.5Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.5 1.5 1.5 1.5Crosslinking condition 160 .times. 20 160 .times. 20 160 .times. 20 160 .times. 20(.degree.C. .times. minutes)Diameter of outer 2.5 2.5 2.5 3.0shell (mm)Stiffness (kgf/cm.sup.2) 3000 4000 4800 3000Shore D hardness 60 65 69 60______________________________________
TABLE 3______________________________________ Example Example Example Example 1 2 3 4______________________________________Formulation of coverHi-milane #1605 *3 20 20 20 20Hi-milane #1706 *4 20 20 20 20Hi-milane #1855 *5 30 30 30 30Nucrel #AN4212C *6 30 30 30 30Titanium dioxide 2.0 2.0 2.0 2.0Barium sulfate 2.0 2.0 2.0 2.0Thickness of cover 1.4 1.4 1.4 1.4(mm)Stiffness (kgf/cm.sup.2) 1500 1500 1500 1500Shore D hardness 49 49 49 4______________________________________ *3: Trade name, ethylenemethacrylic acid ionomer resin obtained by neutralizing with sodium ion, manufactured by Mitsui Du Pont Polychemical Co., MI (melt index) = 2.8, stiffness = 3,100 kgf/cm.sup.2 *4: Trade name, ethylenemethacrylic acid ionomer resin obtained by neutralizing with zinc ion, manufactured by Mitsui Du Pont Polychemical Co., Mi (melt index) = 0.8, stiffness = 2,600 kgf/cm.sup.2 *5: Trade name, ethyleneacrylate-methacrylic acid ionomer resin obtained by neutralizing with zinc ion, manufactured by Mitsui Du Pont Polychemica Co., MI (melt index) = 1.0, stiffness = 900 kgf/cm.sup.2 *6: Trade name, ethyleneisobutyl acrylatemethacrylic acid terpolymer resin, manufactured by Mitsui Du Pont Polychemical Co., MI (melt index) = 12, stiffness = 245 kgf/cm.sup.2
TABLE 4______________________________________ Example Example Example Example 5 6 7 8______________________________________Formulation of centerButadiene rubber 100 100 100 100Zinc diacrylate 30 30 20 25Zinc oxide 16.5 16.5 21.0 17.0Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.2 1.2 1.2 1.2Crosslinking condition 160 .times. 25 160 .times. 25 160 .times. 25 160 .times. 25(.degree.C. .times. minutes)Diameter of center 35.9 35.9 34.9 35.7(mm)Stiffness (kgf/cm.sup.2) 1800 1800 700 1300Shore D hardness 49 49 37 44______________________________________
TABLE 5______________________________________ Example Example Example Example 5 6 7 8______________________________________Formulation ofouter shellButadiene rubber 100 100 100 100Zinc diacrylate 50 60 50 50Zinc oxide 9.0 5.2 9.0 7.5Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.5 1.5 1.5 1.5Crosslinking condition 160 .times. 20 160 .times. 20 160 .times. 20 160 .times. 20(.degree.C. .times. minutes)Diameter of outer 2.0 2.0 2.0 2.0shell (mm)Stiffness (kgf/cm.sup.2) 4000 4800 4000 4000Shore D hardness 65 69 65 65______________________________________
TABLE 6______________________________________ Example Example Example Example 5 6 7 8______________________________________Formulation of coverHi-milane #1605 20 20 20 20Hi-milane #1706 20 20 20 20Hi-milane #1855 30 30 30 30Nucrel #AN4212C 30 30 30 30Titanium dioxide 2.0 2.0 2.0 2.0Barium sulfate 2.0 2.0 2.0 2.0Thickness of cover 1.4 1.4 1.4 1.0(mm)Stiffness (kgf/cm.sup.2) 1500 1500 1500 1500Shore D hardness 49 49 49 49______________________________________
TABLE 7______________________________________ Example 9 Example 10______________________________________Formulation of centerButadiene rubber 100 100Zinc diacrylate 25 25Zinc oxide 18.5 19.0Antioxidant 0.5 0.5Dicumyl peroxide 1.2 1.2Crosslinking condition (.degree.C. .times. minutes) 160 .times. 25 160 .times. 25Diameter of center (mm) 34.9 34.5Stiffness (kgf/cm.sup.2) 1300 1300Shore D hardness 44 44______________________________________
TABLE 8______________________________________ Example 9 Example 10______________________________________Formulation of outer shellButadiene rubber 100 100Zinc diacrylate 50 50Zinc oxide 9.0 10Antioxidant 0.5 0.5Dicumyl peroxide 1.5 1.5Crosslinking condition (.degree.C. .times. minutes) 160 .times. 20 160 .times. 20Diameter of outer shell (mm) 2.5 2.5Stiffness (kgf/cm.sup.2) 4000 4000Stiffness (Shore D hardness) 65 65______________________________________
TABLE 9______________________________________ Example 9 Example 10______________________________________Formulation of coverHi-milane #1605 25 20Hi-milane #1706 25 20Hi-milane #1855 20 30Nucrel #AN4212C 30 30Titanium dioxide 2.0 2.0Barium sulfate 2.0 2.0Thickness of cover (mm) 1.4 1.6Stiffness (kgf/cm.sup.2) 1900 1500Stiffness (Shore D hardness) 52 49______________________________________
TABLE 10__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Formulation of centerButadiene rubber 100 100 100 100Zinc diacrylate 25 50 25 25Zinc oxide 18.5 9.0 18.5 18.5Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.2 1.5 1.2 1.2Crosslinking condition (.degree.C. .times. minutes) 160 .times. 25 160 .times. 25 160 .times. 25 160 .times. 25Diameter of center (mm) 34.9 34.9 27.9 34.9Stiffness (kgf/cm.sup.2) 1300 4000 1300 1300Shore D hardness 44 65 44 44__________________________________________________________________________
TABLE 11__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Formulation of outer shellButadiene rubber 100 100 100 100Zinc diacrylate 30 25 50 50Zinc oxide 16.5 18.5 9.0 9.0Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.2 1.2 1.2 1.2Crosslinking condition (.degree.C. .times. minutes) 160 .times. 20 160 .times. 20 160 .times. 20 160 .times. 20Thickness of outer shell (mm) 2.5 2.5 6.0 2.5Stiffness (kgf/cm.sup.2) 1800 1300 4000 4000Shore D hardness 49 44 65 65__________________________________________________________________________
TABLE 12__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Formulation of coverHi-milane #1605 20 20 20 50Hi-milane #1706 20 20 20 50Hi-milane #1855 30 30 30 --Nucrel #AN4212C 30 30 30 --Titanium dioxide 2.0 2.0 2.0 2.0Barium sulfate 2.0 2.0 2.0 2.0Thickness of cover (mm) 1.4 1.4 1.4 1.4Stiffness (kgf/cm.sup.2) 1500 1500 1500 3400Shore D hardness 49 49 49 63__________________________________________________________________________
TABLE 13__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Formulation of centerButadiene rubber 100 100 100 100Zinc diacrylate 25 10 25 20Zinc oxide 23.0 24.0 17.5 25.7Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.2 1.2 1.2 1.2Crosslinking condition (.degree.C. .times. minutes) 160 .times. 25 160 .times. 25 160 .times. 25 160 .times. 25Diameter of center (mm) 32.9 34.9 34.9 27.0Stiffness (kgf/cm.sup.2) 1350 200 1300 800Shore D hardness 45 28 44 38__________________________________________________________________________
TABLE 14__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Formulation of outer shellButadiene rubber 100 100 100 100Zinc diacrylate 50 50 100 30Zinc oxide 14.0 9.0 5.0 21.0Antioxidant 0.5 0.5 0.5 0.5Dicumyl peroxide 1.5 1.5 1.5 1.5Crosslinking condition (.degree.C. .times. minutes) 160 .times. 20 160 .times. 20 160 .times. 20 160 .times. 20Thickness of outer shell (mm) 2.5 2.5 2.5 5.5Stiffness (kgf/cm.sup.2) 4200 4000 8000 1800Shore D hardness 66 65 80 49__________________________________________________________________________
TABLE 15__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Formulation of coverHi-milane #1605 20 20 20 50Hi-milane #1706 20 20 20 50Hi-milane #1855 30 30 30 --Nucrel #AN4212C 30 30 30 --Titanium dioxide 2.0 2.0 2.0 --Barium sulfate 2.0 2.0 2.0 --Thickness of cover (mm) 2.4 1.4 1.4 2.4Stiffness (kgf/cm.sup.2) 1500 1500 1500 3400Shore D hardness 49 49 49 63__________________________________________________________________________
TABLE 16______________________________________ Comparative Comparative Example 9 Example 10______________________________________Formulation of coreButadiene rubber 100 100Zinc diacrylate 32 38Zinc oxide 20.5 13.5Antioxidant 0.5 0.5Dicumyl peroxide 1.5 1.5Crosslinking condition (.degree.C. .times. 160 .times. 30 160 .times. 30minutes)Diameter of core (mm) 37.9 39.9Stiffness (kgf/cm.sup.2) 2050 2700Shore D hardness 52 57______________________________________
TABLE 17______________________________________ Comparative Comparative Example 9 Example 10______________________________________Formulation of coverHi-milane #1605 50 20Hi-milane #1706 50 20Surlyn #AD8265 *7 -- 60Titanium dioxide 2.0 2.0Barium sulfate 2.0 2.0Thickness of cover (mm) 2.4 1.4Stiffness (kgf/cm.sup.2) 3400 1200Shore D hardness 63 57______________________________________ *7: Trade name, ethylenebutyl acrylatemethacrylic acid terpolymer soft ionomer resin obtained by neutralizing with sodium ion, manufactured by D Pont U.S.A. Co., MI = 1.0, shore D hardness = 47, stiffness = 560 kgf/cm.sup.2
Three-piece solid golf balls and two-piece solid golf balls of the these Examples and Comparative Examples were prepared as follows.
Regarding the three-piece solid golf ball, a rubber composition for center was firstly prepared from formulation components described in each table, and the resulting rubber composition was charged in a die and subjected to a press molding according to the crosslinking condition described in each table to prepare an center Then, a sheet-like rubber composition for outer shell was laminated on this center and the resulting laminate was subjected to a press molding according to the crosslinking condition described in each table to give a solid core. Then, the solid core was coated with a composition for cover having a formulation described in each table using an injection molding method and, after painting and marking, to prepare a three-piece solid golf ball having an outer diameter of 42.7 mm.
Regarding the two-piece solid golf ball, a rubber composition for core was prepared from formulation components described in Table 16, and the resulting rubber composition was charged in a die and subjected to a press molding according to the crosslinking condition described in Table 16 to prepare a solid core. Then, the solid core was coated with a composition for cover having a formulation described in Table 17 using an injection molding method and, after painting and marking, to prepare a two-piece solid golf ball having an outer diameter of 42.7 mm.
The ball weight of the resulting golf ball, the ball initial velocity, the spin and the flying distance (carry) obtained by hitting with a No.1 wood club and a No.9 iron club, and the maximum impact force obtained by hitting with a No.1 wood club were measured.
Regarding the No.9 iron club test, a test was also conducted at the state where a shot mark of a pressure-sensitive paper is adhered on the face surface as the condition wherein a slip is liable to be generated, in addition to the test at a normal state, thereby examining a slip prevention effect at the time of iron shot.
The initial velocity, the spin, the launch angle and the flying distance (carry) were measured by hitting with a No.1 wood club (No.9 iron club) at a head speed of 45 m/second (34.5 m/second) using a swing robot manufactured by True Temper Co.
The maximum impact force was determined by hitting a golf ball with a No.1 wood club of which back surface section of the club head was equipped with an acceleration pickup to measure an acceleration generated in the opposite direction to the forward direction of the head and converting the maximum acceleration into a force.
Further, the hit feeling and the control properties of the resulting golf ball were evaluated according to a practical hitting test by 10 top professional golfers. The evaluation criteria are as follows. The evaluation results are also shown in each table by the same symbol and are based on the fact that not less than 8 out of 10 golfers evaluated with the same criterion.
Evaluation criteria
.smallcircle.: Good, hit feeling and control properties are excellent.
.DELTA.: Control properties are good but it is too hard and the impact is too strong, or it is too soft and heavy, and the hit feeling is inferior.
.times.: Hit feeling and control properties are inferior, simultaneously.
These evaluation results of the golf balls are shown in Tables 18 to 29. Further, "No.9 iron test (1)" means the case that a test is conducted by hitting with a No.9 iron club at a normal state where the face surface is dry. Further, "No.9 iron test (2)" means the case that a test is conducted by hitting with a No.9 iron club at the state where a pressure-sensitive paper "Lite G-42 (trade name)" manufactured by Raito Co., Ltd. is adhered on the face surface on hitting. Furthermore, "difference between No.9 iron test (1) and (2)" means a difference in initial spin and flying distance between test (1) and (2) (test (1)-test (2)).
The results thus obtained are shown in Tables 18 to 29. In Tables 18 to 19, various characteristics of the golf balls of Examples 1 to 4 are shown. In Tables 20 to 21, various characteristics of the golf balls of Examples 5 to 8 are shown. In Tables 22 to 23, various characteristics of the golf balls of Examples 9 to 10 are shown. In Tables 24 to 25, various characteristics of the golf balls of Comparative Examples 1 to 4 are shown. In Tables 26 to 27, various characteristics of the golf balls of Comparative Examples 5 to 8 are shown. In Tables 28 to 29, various characteristics of the golf balls of Comparative Examples 9 to 10 are shown.
TABLE 18__________________________________________________________________________ Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Ball weight (g) 45.4 45.4 45.5 45.4Flying performances when usingNo. 1 wood clubBall initial velocity (m/s) 65.0 65.1 65.2 65.2Initial spin (rpm) 2,700 2,800 2,900 3,000Launch angle (degree) 11.6 11.5 11.4 11.3Flying distance (yard) 230 233 231 230No. 9 iron club test (1)Ball initial velocity (m/s) 43.0 43.2 43.3 43.3Initial spin (rpm) 8,200 8,300 8,400 8,400Launch angle (degree) 24.5 24.4 24.4 24.3Flying distance (yard) 124 124 124 123No. 9 iron club test (2)Ball initial velocity (m/s) 43.0 43.2 43.3 43.3Initial spin (rpm) 8,100 8,100 8,200 8,200Launch angle (degree) 24.6 24.4 24.5 24.4Flying distance (yard) 125 125 125 124__________________________________________________________________________
TABLE 19__________________________________________________________________________ Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Difference between No. 9 iron clubtest (1) and test (2)Initial spin (rpm) -100 -200 -200 -200Flying distance (yard) +1 +1 +1 +1Maximum impact force (kgf) 1,450 1,500 1,550 1,550Hit feeling and control properties .largecircle. .largecircle. .largecircle. .largecircle.__________________________________________________________________________
TABLE 20__________________________________________________________________________ Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Ball weight (g) 45.4 45.5 45.4 45.5Flying performances when usingNo. 1 wood clubBall initial velocity (m/s) 65.2 65.3 64.9 65.0Initial spin (rpm) 2,900 2,900 2,700 2,700Launch angle (degree) 11.4 11.4 11.6 11.6Flying distance (yard) 231 233 230 231No. 9 iron club test (1)Ball initial velocity (m/s) 43.3 43.4 43.1 43.2Initial spin (rpm) 8,300 8,300 8,100 8,200Launch angle (degree) 24.4 24.4 24.7 24.5Flying distance (yard) 124 124 125 125No. 9 iron club test (2)Ball initial velocity (m/s) 43.3 43.4 43.1 43.2Initial spin (rpm) 8,100 8,200 8,100 8,100Launch angle (degree) 24.5 24.4 24.8 24.6Flying distance (yard) 125 124 125 125.5__________________________________________________________________________
TABLE 21__________________________________________________________________________ Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Difference between No. 9 iron clubtest (1) and test (2)Initial spin (rpm) -200 -100 0 -100Flying distance (yard) +1 0 0 +0.5Maximum impact force (kgf) 1,600 1,650 1,400 1,550Hit feeling and control properties .largecircle. .largecircle. .largecircle. .largecircle.__________________________________________________________________________
TABLE 22______________________________________ Example 9 Example 10______________________________________Ball weight (g) 45.4 45.4Flying performances when usingNo. 1 wood clubBall initial velocity (m/s) 65.2 65.0Initial spin (rpm) 2,900 2,800Launch angle (degree) 11.6 11.5Flying distance (yard) 232 232No. 9 iron club test (1)Ball initial velocity (m/s) 43.3 43.1Initial spin (rpm) 8,400 8,300Launch angle (degree) 24.5 24.4Flying distance (yard) 124 124No. 9 iron club test (2)Ball initial velocity (m/s) 43.3 43.1Initial spin (rpm) 8,200 8,200Launch angle (degree) 24.6 24.5Flying distance (yard) 125 125______________________________________
TABLE 23______________________________________ Example 9 Example 10______________________________________Difference between No. 9 iron clubtest (1) and test (2)Initial spin (rpm) -200 -100Flying distance (yard) +1 +1Maximum impact force (kgf) 1,600 1,450Hit feeling and control properties .largecircle. .largecircle.______________________________________
TABLE 24__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Ball weight (g) 45.4 45.4 45.4 45.5Flying performances when usingNo. 1 wood clubBall initial velocity (m/s) 64.3 65.2 65.2 65.3Initial spin (rpm) 2,600 3,800 3,300 2,700Launch angle (degree) 11.6 10.7 11.1 11.7Flying distance (yard) 225 222 228 232No. 9 iron club test (1)Ball initial velocity (m/s) 42.6 43.2 43.2 43.3Initial spin (rpm) 8,000 10,500 9,200 8,000Launch angle (degree) 24.3 21.5 22.8 24.7Flying distance (yard) 118 116 120 125No. 9 iron club test (2)Ball initial velocity (m/s) 42.6 43.3 43.2 43.3Initial spin (rpm) 7,900 10,200 9,000 5,800Launch angle (degree) 24.4 21.7 22.9 25.7Flying distance (yard) 119 117 121 132__________________________________________________________________________
TABLE 25__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4__________________________________________________________________________Difference between No. 9 iron clubtest (1) and test (2)Initial spin (rpm) -100 -300 -200 -2,200Flying distance (yard) +1 +1 +1 +7Maximum impact force (kgf) 1,400 2,200 1,900 1,650Hit feeling and control properties .largecircle. .DELTA. .DELTA. x__________________________________________________________________________
TABLE 26__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Ball weight (g) 45.4 45.4 45.5 45.4Flying performances when usingNo. 1 wood clubBall initial velocity (m/s) 64.6 64.2 65.2 64.9Initial spin (rpm) 3,200 2,600 3,000 2,700Launch angle (degree) 11.2 11.5 11.3 11.7Flying distance (yard) 225 224 230 230No. 9 iron club test (1)Ball initial velocity (m/s) 42.9 42.5 43.2 43.1Initial spin (rpm) 9,000 8,100 8,500 8,000Launch angle (degree) 23.0 24.4 24.2 24.6Flying distance (yard) 119 118 122 124No. 9 iron club test (2)Ball initial velocity (m/s) 43.0 42.5 43.2 43.1Initial spin (rpm) 9,000 8,000 8,300 5,900Launch angle (degree) 23.2 24.4 24.6 25.7Flying distance (yard) 119 118 123 131__________________________________________________________________________
TABLE 27__________________________________________________________________________ Comparative Comparative Comparative Comparative Example 5 Example 6 Example 7 Example 8__________________________________________________________________________Difference between No. 9 iron clubtest (1) and test (2)Initial spin (rpm) 0 -100 -200 -2,100Flying distance (yard) +1 0 +1 +7Maximum impact force (kgf) 1,500 1,300 1,900 1,550Hit feeling and control properties .largecircle. .largecircle. .DELTA. x__________________________________________________________________________
TABLE 28______________________________________ Comparative Comparative Example 9 Example 10______________________________________Ball weight (g) 45.5 45.4Flying performances when usingNo. 1 wood clubBall initial velocity (m/s) 65.1 64.5Initial spin (rpm) 2,800 3,500Launch angle (degree) 11.5 11.0Flying distance (yard) 232 223No. 9 iron club test (1)Ball initial velocity (m/s) 43.2 42.8Initial spin (rpm) 8,300 9,600Launch angle (degree) 24.4 22.5Flying distance (yard) 123 11 8No. 9 iron club test (2)Ball initial velocity (m/s) 43.2 42.9Initial spin (rpm) 6,300 9,400Launch angle (degree) 25.4 22.6Flying distance (yard) 129 118.5______________________________________
TABLE 29______________________________________ Comparative Comparative Example 9 Example 10______________________________________Difference between No. 9 iron clubtest (1) and test (2)Initial spin (rpm) -2,000 -200Flying distance (yard) +6 +0.5Maximum impact force (kgf) 1,600 1,950Hit feeling and control properties x .DELTA.______________________________________
As is apparent from the results shown in the above tables, since the golf bails of Examples 1 to 10 have suitable ball initial velocity, initial spin and launch angle, they exhibited the flying distance which compares with that of the golf balls using the high-rigid cover of Comparative Examples 8 and 9. As is apparent from the fact that the difference between No.9 iron club test (1) and (2), i.e. difference in initial spin and flying distance between tests wherein the shot mark is provided on the No.9 iron club or not is small, the stability upon iron shot was accomplished and they had low impact force, good hit feeling and control properties.
On the contrary, the golf balls of Comparative Examples 1 to 7 were inferior in flying distance, stability upon iron shot or hit feeling.
Further, the three-piece solid golf ball using the high-rigid hard cover of Comparative Example 8 and the typical two-piece solid golf ball using the same high-rigid hard cover of Comparative Example 9 attained large flying distance, but the stability upon iron shot and control properties were inferior. Further, the hit feeling was also inferior because of hardness of the cover.
Regarding the typical two-piece solid golf ball using the flexible cover of Comparative Example 10, scatter of iron shot was small and control properties were good, but the flying distance is drastically deteriorated due to excessive slip. Further, the impact force at the time of hitting was large and the hit feeling was not good.

Number	Name	Date
4714253	Nakahara et al.	Dec 1987
4986545	Sullivan	Jan 1991
5184828	Kim et al.	Feb 1993

Number	Date	Country
2182340	May 1987	GBX
2228874	Dec 1990	GBX
2247682	Nov 1992	GBX
2264302	Aug 1993	GBX

Three-piece solid golf ball

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (3)

Foreign Referenced Citations (4)