Claims
- 1. A process for producing pigmentary titanium dioxide which comprises:
- (a) reacting titanium tetrachloride and an oxygen containing gas in the vapor phase,
- at a reaction zone temperature of at least about 800.degree. C., and a pressure of at least 10 pounds per square inch gage,
- in the presence of water vapor in the amount of about 50-100,000 parts per million, based on the weight of the TiO.sub.2 under production, and a nucleant consisting essentially of a cesium substance wherein the cesium substance is present in the amount of about 8-2,000 parts per million, based on the weight of the TiO.sub.2 under production, and
- (b) thereafter recovering the resulting titanium dioxide pigment.
- 2. The process of claim 1 wherein the cesium substance is present in an amount of about 8-500 parts per million.
- 3. The process of claim 1 wherein the pressure is about 10-200 PSIG, the temperature is about 800.degree.-1800.degree. C., and the cesium substance is present in an amount of about 8-250 parts per million.
- 4. The process of claim 1 wherein the pressure is about 10-200 PSIG, the temperature is about 800.degree.-1800.degree. C., and the reaction is carried out in the presence of vaporous AlCl.sub.3 in the amount of about 0.1-10% by weight, based on the weight of the titanium tetrachloride and the cesium substance is present in an amount of about 8-200 parts per million.
- 5. The process of claim 4 wherein a spacing gas is introduced into the reaction zone in the amount of about 5-200 mole percent, based on the titanium tetrachloride and oxygen reactants.
- 6. The process of claim 1 wherein the pressure is about 15-200 PSIG.
- 7. The process of claim 2 wherein the pressure is about 15-200 PSIG
- 8. The process of claim 3 wherein the pressure is about 15-200 PSIG.
- 9. The process of claim 4 wherein the pressure is about 15-200 PSIG.
- 10. The process of claim 5 wherein the pressure is about 15-200 PSIG.
- 11. The process of claim 1 wherein the pressure is about 20-200 PSIG.
- 12. The process of claim 2 wherein the pressure is about 20-200 PSIG.
- 13. The process of claim 3 wherein the pressure is about 20-200 PSIG.
- 14. The process of claim 4 wherein the pressure is about 20-200 PSIG.
- 15. The process of claim 5 wherein the pressure is about 20-200 PSIG.
- 16. In a process for producing pigmentary titanium dioxide involving reacting titanium tetrachloride in the vapor state and an oxygen containing gas in the presence of water vapor and nucleant, the specific improvement comprising:
- (a) mixing and reacting the titanium tetrachloride and the oxygen containing gas with a residence time of reactants in the mixing zone of the reactor of from about 1 to 16 milliseconds at a reaction zone temperature of at least about 800.degree. C. and a pressure of at least 10 pounds per square inch gage, in the presence of water vapor in the amount of about 50 to 100,000 parts per million, based on the weight of the TiO.sub.2 under production, and in the presence of an effective amount of a nucleant consisting essentially of a cesium substance to achieve improved CBU and improved specific surface area, wherein the cesium substance is present in the amount of about 8 to 2,000 part per million, based on the weight of the TiO.sub.2 under productions, and
- (b) thereafter recovering the resulting titanium dioxide pigment characterized by improved CBU, gloss and specific surface area.
- 17. The improved process of claim 16 wherein the residence time of the reactants in the mixing zone of the reactor is about 2-14 milliseconds.
- 18. The improved process of claim 16 wherein the residence time of the reactants in the mixing zone of the reactor is about 3-12 milliseconds.
- 19. A process for producing pigmentary titanium dioxide which comprises:
- (a) reacting titanium tetrachloride and an oxygen containing gas in the vapor phase,
- at a reaction zone temperature of at least about 800.degree. C., and at a residence time of the reactants in the mixing zone of the reactor of about 1-16 milliseconds,
- in the presence of water vapor in the amount of about 50-100,000 parts per million, based on the weight of TiO.sub.2 under production, and a nucleant consisting essentially of a cesium substance wherein the cesium substance is present in an amount of about 8-2,000 parts per million, based on the weight of the TiO.sub.2 under production, and
- (b) thereafter recovering the resulting titanium dioxide pigment.
- 20. The process of claim 19 wherein the residence time of the reactants in the mixing zone of the reactor is about 2-14 milliseconds.
- 21. The process of claim 19 wherein the residence time of the reactants in the mixing zone of the reactor is about 3-12 milliseconds.
- 22. The process of claim 19 wherein the TiO.sub.2 nucleant is present in an amount of about 8-500 parts per million.
- 23. The process of claim 19 wherein the temperature is about 800.degree.-1800.degree. C. and the cesium substance is present in an amount of about 8-250 parts per million.
- 24. The process of any one of claims 19-23 wherein the temperature is about 800.degree.-1800.degree. C., and the reaction is carried out in the presence of vaporous AlCl.sub.3 in the amount of about 0.1-10% by weight, based on the weight of the titanium tetrachloride.
- 25. The process of any one of claims 19-23 wherein a spacing gas is introduced into the reaction zone in the amount of about 5-200 mole percent, based on the titanium tetrachloride and oxygen reactants, the temperature is about 800.degree.-1800.degree. C., and the reaction is carried out in the presence of vaporous AlCl.sub.3 in the amount of about 0.1-10% by weight based on the weight of the titanium tetrachloride.
Parent Case Info
This is a continuation of application Ser. No. 07/641,804, filed Jan. 16, 1991, which is a continuation of application Ser. No. 07/430,895, filed Oct. 31, 1989, which is a continuation of application Ser. No. 07/298,809, filed Jan. 18, 1989, which is a continuation of application Ser. No. 07/060,875, filed Jun. 12, 1987, which is a continuation-in-part of application Ser. No. 853,423, filed Apr. 18, 1986, all of which are abandoned.
US Referenced Citations (9)
Foreign Referenced Citations (1)
Number |
Date |
Country |
0876672 |
Sep 1961 |
GBX |
Continuations (4)
|
Number |
Date |
Country |
Parent |
641804 |
Jan 1991 |
|
Parent |
430895 |
Oct 1989 |
|
Parent |
298809 |
Jan 1989 |
|
Parent |
60875 |
Jun 1987 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
853423 |
Apr 1986 |
|