Patent Application
20120199260
The present invention relates to pneumatic tyres comprising a self-sealing layer positioned on their inner wall in order to seal off any perforations in service and more particularly to such pneumatic tyres in which the self-sealing layer is placed in the blank of the pneumatic tyre before the vulcanization thereof.
Many documents present such pneumatic tyres comprising a self-sealing layer over all or part of their inner surface.
By way of example, document U.S. Pat. No. 4,418,093 presents a process for uniformly positioning a layer of self-sealing material on the inner wall of a vulcanized pneumatic tyre by a combination of rotating the pneumatic tyre followed by oscillating movements until the self-sealing material is sufficiently crosslinked so as to no longer flow.
When the self-sealing layer is positioned in the uncured blank of a pneumatic tyre, one of the problems encountered is due to the very tacky nature of the self-sealing layer which adheres strongly to the curing membrane during the vulcanization phase. After the vulcanized pneumatic tyre is removed from the curing mould, parts of the self-sealing layer may remain adhesively bonded to the wall of the membrane and lead to the rapid scrapping thereof. The non-stick agents customarily used such as whitewashes or liquid silicones are completely inadequate for solving this problem.
In order to solve this problem, document US 2009/0084482 A1 discloses a pneumatic tyre with a self-sealing layer that is incorporated during the manufacture of the tyre. This pneumatic tyre comprises an outer rubber tread, a carcass reinforcement, a gastight layer positioned on the inside relative to the carcass reinforcement and a separable protective layer positioned innermost. It also comprises a self-sealing layer adjacent to the separable protective layer and positioned on the inside relative to the gastight layer. The separable protective layer is a thermoplastic film of nylon or of a mixture of nylon and rubber.
The protective layer facilitates the manufacture of the pneumatic tyre by avoiding any contact between the self-sealing layer and the tools for assembling the blank of the pneumatic tyre. This layer is said to be separable, that is to say that it can be removed from the surface of the self-sealing layer after the vulcanization of the tyre without taking off all or part of this layer and without tearing.
The Applicant companies have however noted that, contrary to what is indicated in that document, such a nylon-based thermoplastic film may not be able to be separated from the surface of the self-sealing layer in the case of certain self-sealing layer formulations.
One subject of the invention is a pneumatic tyre similar to that described previously in which the protective layer consists of a thermoplastic film comprising at least one fluoropolymer.
The term “separable” is understood to mean that the protective film can be removed from the surface of the self-sealing layer without taking off all or part of this layer. This has the advantage of reimparting to the surface of this self-sealing layer its entire tacky character, which character is essential in order for it to fulfil its role.
This film can be removed immediately after the vulcanization of the tyre when the self-sealing layer has been assembled before the vulcanization of the tyre as described in US 2009/0084482 A1, it is also, and preferably, possible to retain this film, which then acts as a protective film until the tyre is fitted onto its service rim. The film then has the advantage of protecting the self-sealing layer during all the tyre transport and storage phases.
As fluoropolymers, fluorinated ethylene-propylene (FEP) copolymers may be chosen. Advantageously, the film comprises a copolymer of tetrafluoroethylene (TFE) and hexafluoropropylene (HFP).
These polymers have remarkable non-stick properties.
Preferably, the softening point of the protective film is above 200° C. This enables the film to withstand the customary vulcanization temperatures of pneumatic tyres. Advantageously, the elongation at break of the film in uniaxial extension and at ambient temperature (23° C.) is greater than 180% and preferably greater than 250%. This allows the film to be put in position from the first stage of manufacturing the pneumatic tyre, before shaping during a two-step process.
The thickness of the film is advantageously less than 50 micrometres and preferably between 7 and 30 micrometres. This allows the film to stretch during the pneumatic tyre manufacturing stages, opposing only minimal stresses.
The self-sealing layer may comprise at least (phr signifying parts by weight per 100 parts of solid elastomer) one thermoplastic styrene (TPS) elastomer and more than 200 phr of an extender oil of said elastomer.
The TPS may be the predominant elastomer of the self-sealing layer.
The TPS elastomer may be chosen from the group constituted by styrene/butadiene/styrene (SBS), styrene/isoprene/styrene (SIS), styrene/isoprene/buta-diene/styrene (SIBS), styrene/ethylene/butylene/styrene (SEBS), styrene/ethylene/propylene/styrene (SEPS), and styrene/ethylene/ethylene/propylene/styrene (SEEPS) block copolymers and mixtures of these copolymers.
Advantageously, the TPS elastomer is chosen from the group constituted by SEBS copolymers, SEPS copolymers and mixtures of these copolymers.
According to another embodiment, the self-sealing layer may comprise at least (phr signifying parts by weight per 100 parts of solid elastomer):
The unsaturated diene elastomer is advantageously chosen from the group constituted by polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, isoprene copolymers and mixtures of such elastomers.
The unsaturated diene elastomer may advantageously be an isoprene elastomer, preferably chosen from the group constituted by natural rubber, synthetic polyisoprenes and mixtures of such elastomers.
Advantageously, the content of unsaturated diene elastomer is greater than 50 phr, preferably greater than 70 phr.
Another subject of the invention is a process for fitting a pneumatic tyre with built-in self-sealing layer onto a rim, the pneumatic tyre comprising a separable thermoplastic film positioned adjacent to the self-sealing layer and innermost, in which:
the pneumatic tyre is grasped;
the separable thermoplastic film is separated from the pneumatic tyre; and
the pneumatic tyre is fitted onto the rim.
Another subject of the invention relates to the use, for protecting the surface of a self-sealing layer intended to be integrated into a pneumatic tyre, of a thermoplastic film comprising a fluoropolymer. Preferably, the fluoropolymer is a fluorinated ethylene-propylene (FEP) copolymer.
All the embodiment details are given in the following description, which is supplemented by
This tyre 1 comprises a crown 2 reinforced by a crown reinforcement or belt 6, two sidewalls 3 and two beads 4, each of these beads 4 being reinforced with a bead wire 5. The crown reinforcement 6 is surmounted radially on the outside by a rubbery tread 9. A carcass reinforcement 7 is wound around the two bead wires 5 in each bead 4, the upturn 8 of this reinforcement 7 lying for example towards the outside of the tyre 1. The carcass reinforcement 7 consists, as is known per se, of at least one ply reinforced by cords, called “radial” cords, for example textile or metal cords, i.e. these cords are arranged practically parallel to one another and extend from one bead to the other so as to form an angle of between 80° and 90° with the circumferential mid-plane (the plane perpendicular to the rotational axis of the tyre, which is located at mid-distance of the two beads 4 and passes through the middle of the crown reinforcement 6). An airtight layer 10 extends from one bead to the other radially on the inside relative to the carcass reinforcement 7.
The tyre 1 is such that its inner wall includes a self-sealing layer 11. In accordance with a preferred embodiment of the invention, the self-sealing layer 11 covers the airtight layer 10 in the region of the crown of the pneumatic tyre. The self-sealing layer may also extend from the crown region to mid-points of the sidewalls (equators) of the pneumatic tyre, or even beyond. The self-sealing layer 11 is covered radially on the inside with a separable protective layer 12.
The separable protective layer 12 is a thermoplastic film comprising a fluoropolymer. The thermoplastic film is stretchable with a low stiffness and plastic behaviour. This film should have a softening point above the vulcanization temperature of the pneumatic tyre. One example of a suitable film is the A5000 film from Aerovac Systemes France. This film comprises a fluorinated ethylene-propylene or FEP copolymer. This film has a maximum operating temperature of the order of 204° C. and an elongation at break of greater than 300%. Its thickness is 25 μm. These characteristics enable it to be put in place directly on the building drum of the pneumatic tyre.
The separable protective layer 12 makes it possible for the self-sealing layer to be separated from any contact with the drum for manufacturing the pneumatic tyre then with the curing membrane of the vulcanization mould. The particular nature of this protective film enables it to be removed from the inner surface of the pneumatic tyre after vulcanization. The removal of this protective film reimparts to the self-sealing layer its entire internal mobility and surface mobility and also its tacky character and thus improves its effectiveness at the time of a puncture. The protective film 12 can be removed without tearing.
According to one embodiment, the self-sealing layer 11 comprises a thermoplastic styrene (TPS) elastomer and more than 200 phr of an extender oil of the elastomer. The thermoplastic styrene elastomers are thermoplastic elastomers that are in the form of block copolymers based on styrene.
Having a structure intermediate between thermoplastic polymers and elastomers, they consist, as is known, of hard polystyrene units connected by flexible elastomer, for example polybutadiene, polyisoprene or poly(ethylene/butylene) units. These are often triblock elastomers with two hard segments connected by a soft segment. The hard and soft segments may be arranged linearly, in a star shape or in a branched manner.
The TPS elastomer is chosen from the group constituted by styrene/butadiene/styrene (SBS), styrene/isoprene/styrene (SIS), styrene/isoprene/buta-diene/styrene (SIBS), styrene/ethylene/butylene/styrene (SEBS), styrene/ethylene/propylene/styrene (SEPS), and styrene/ethylene/ethylene/propylene/styrene (SEEPS) block copolymers and mixtures of these copolymers.
More preferably, the elastomer is chosen from the group constituted by SEBS copolymers, SEPS copolymers and mixtures of these copolymers.
The TPS elastomer may constitute the whole of the elastomer matrix or the majority by weight (preferably more than 50%, more preferably more than 70%) of the latter when it comprises one or more other elastomer(s), which are thermoplastic or non-thermoplastic elastomers, for example of diene type.
Examples of such self-sealing layers and of their properties are disclosed in documents FR 2 910 382, FR 2 910 478 and FR 2 925 388.
Such a self-sealing layer may be preformed by extrusion of a flat profiled element to the dimensions suitable for its application onto a building drum. One exemplary embodiment is presented in document FR 2 925 388.
According to another exemplary embodiment, the self-sealing layer 11 consists of an elastomer composition comprising at least, as predominant elastomer (preferably with a content of more than 50 phr), an unsaturated diene elastomer, between 30 and 90 phr of a hydrocarbon resin and a liquid plasticizer, of Tg below −20° C., with a content of between 0 and 60 phr (phr denoting parts by weight per hundred parts of solid elastomer). It has another essential feature of containing no filler or, at the very most, containing less than 30 phr thereof.
The term “diene” elastomer or rubber should be understood, as is known, to mean an elastomer (i.e. a homopolymer or a copolymer) at least partly obtained from diene monomers (i.e. monomers containing two carbon-carbon double bonds, whether conjugated or not).
These diene elastomers may be put into two categories, namely saturated and unsaturated. In the present application, the term “unsaturated” (or “essentially unsaturated”) diene elastomer is understood to mean a diene elastomer that is at least partly obtained from conjugated diene monomers and having a content of units obtained from conjugated dienes of greater than 30 mol %. Thus, excluded from this definition are diene elastomers such as butyl rubbers or copolymers of dienes and alpha-olefins, of the EPDM type, which may be termed “saturated” or “essentially saturated” diene elastomers because of their low content of units of diene origin (always less than 15 mol %).
It is preferred to use an unsaturated diene elastomer with a content (in mol %) of units of diene origin (conjugated dienes) of greater than 50%, such a diene elastomer being more preferably chosen from the group formed by polybutadienes (BR), natural rubber (NR), synthetic polyisoprenes (IR), butadiene copolymers (for example styrene-butadiene rubber or SBR), isoprene copolymers (of course, other than butyl rubber) and blends of such elastomers.
Compared with diene elastomers of the liquid type, the unsaturated diene elastomer of the composition is by definition a solid. Preferably, its number-average molecular weight (Mn) is between 100 000 and 5 000 000, more preferably between 200 000 and 4 000 000 g/mol. The Mn value is determined in a known manner, for example by SEC: tetrahydrofuran solvent; 35° C. temperature; 1 g/l concentration; 1 ml/min flow rate; solution filtered on a filter of 0.45 μm porosity before injection; Moore calibration using standards (for example polyisoprene standards); set of four WATERS columns in series (“STYRAGEL” HMW7, HMW6E, and 2 HT6E); differential refractometer (WATERS 2410) detection and its associated operating software (WATERS EMPOWER).
More preferably, the unsaturated diene elastomer of the composition of the self-sealing layer is an isoprene elastomer. The term “isoprene elastomer” is understood to mean, as is known, an isoprene homopolymer or copolymer, in other words a diene elastomer chosen from the group formed by natural rubber (NR), synthetic polyisoprenes (IR), butadiene-isoprene copolymers (BIR), styrene-isoprene copolymers (SIR), styrene-butadiene-isoprene copolymers (SBIR) and blends of these elastomers.
This isoprene elastomer is preferably natural rubber or a synthetic cis-1,4-polyisoprene. Among these synthetic polyisoprenes, those having a content (in mol %) of cis-1,4 bonds of greater than 90%, more preferably still greater than 95%, especially greater than 98%, are preferably used.
The above unsaturated diene elastomer, especially an isoprene elastomer such as natural rubber, may constitute all of the elastomer matrix or the predominant amount by weight (preferably comprising more than 50%, more preferably more than 70%) of said matrix when it contains one or more other diene elastomers or non-diene elastomers, for example of the thermoplastic elastomer type. In other words, and preferably, in the composition, the content of unsaturated (solid) diene elastomer, especially of isoprene elastomer such as natural rubber, is greater than 50 phr, more preferably greater than 70 phr. More preferably still, this content of unsaturated diene elastomer, especially of isoprene elastomer such as natural rubber, is greater than 80 phr.
According to one particular embodiment, the above unsaturated diene elastomer, especially when it is an isoprene diene elastomer such as natural rubber, is the sole elastomer present in the self-sealing composition. However, it could also, according to other possible embodiments, be combined with other (solid) elastomers in a minor content by weight, whether these be unsaturated diene elastomers (for example BR or SBR) or even saturated diene elastomers (for example butyl), or else elastomers other than diene elastomers, for example thermoplastic styrene (TPS) elastomers, for example chosen from the group formed by styrene/butadiene/styrene (SBS), styrene/isoprene/styrene (SIS), styrene/butadiene/isoprene/styrene (SBIS), styrene/isobutylene/styrene (SIBS), styrene/ethylene/butylene/styrene (SEBS), styrene/ethylene/propylene/styrene (SEPS), styrene/ethylene/ethylene/propylene/styrene (SEEPS) block copolymers and blends of these copolymers.
Surprisingly, this unsaturated diene elastomer, unfilled (or very lightly filled), has proved to be capable, after a thermoplastic hydrocarbon resin has been added in the recommended narrow range, of fulfilling the function of a highly effective self-sealing composition, as will be explained in detail in the rest of the description.
The second essential constituent of the self-sealing composition is a hydrocarbon resin.
The term “resin” is reserved in the present application, by definition, as known to those skilled in the art, to a compound that is solid at room temperature (23° C.), as opposed to a liquid plasticizer compound such as an oil.
Hydrocarbon resins are polymers well known to those skilled in the art, essentially based on carbon and hydrogen, which can be used in particular as plasticizing agents or tackifiers in polymeric matrices. They are by nature miscible (i.e. compatible) in the contents used with the polymer compositions for which they are intended, so as to act as true diluents. They have been described for example in the work entitled “Hydrocarbon Resins” by R. Mildenberg, M. Zander and G. Collin (New York, VCH, 1997, ISBN 3-527-28617-9), Chapter 5 of which is devoted to their applications, especially in rubber tyres (5.5. “Rubber Tires and Mechanical Goods”). They may be aliphatic, cycloaliphatic, aromatic, hydrogenated aromatic, of the aliphatic/aromatic type, i.e. based on aliphatic and/or aromatic monomers. They may be natural or synthetic resins, whether or not based on petroleum (if such is the case, they are also known as petroleum resins).
Their glass transition temperature (Tg) is preferably above 0° C., especially above 20° C. (usually between 30° C. and 95° C.)
As is known, these hydrocarbon resins may also be termed thermoplastic resins in the sense that they soften when heated and may thus be moulded. They may also be defined by a softening point or temperature, at which temperature the product, for example in powder form, cakes together. This softening point tends to replace the melting point, which is quite poorly defined, of resins in general. The softening point of a hydrocarbon resin is generally about 50 to 60° C. higher than the Tg value.
In the composition of the self-sealing layer, the softening point of the resin is preferably above 40° C. (in particular between 40° C. and 140° C.), more preferably above 50° C. (in particular between 50° C. and 135° C.)
Said resin is used in an amount by weight of between 30 and 90 phr. Below 30 phr, the puncture-resistance performance has proved to be insufficient because of excessive stiffness of the composition, whereas above 90 phr, the material has insufficient mechanical strength with, in addition, a risk of its performance being degraded at high temperature (typically above 60° C.). For these reasons, the resin content is preferably between 40 and 80 phr, more preferably still at least equal to 45 phr, especially in the 45 to 75 phr range.
According to a preferred embodiment of the self-sealing layer, the hydrocarbon resin has at least (any) one, and more preferably all, of the following characteristics:
More preferably, this hydrocarbon resin has at least (any) one, and more preferably all, of the following characteristics:
The Tg is measured according to the ASTM D3418 (1999) standard. The softening point is measured according to the ISO 4625 standard (“Ring and Ball” method). The macrostructure (Mw, Mn and Ip) is determined by size exclusion chromatography (SEC): tetrahydrofuran solvent; 35° C. temperature; 1 g/l concentration; 1 ml/min flow rate; solution filtered on a filter of 0.45 μm porosity before injection; Moore calibration using polystyrene standards; set of three WATERS columns in series (“STYRAGEL” HR4E, HR1 and HR0.5); differential refractometer (WATERS 2410) detection and its associated operating software (WATERS EMPOWER).
As examples of such hydrocarbon resins, mention may be made of those chosen from the group formed by cyclopentadiene (abbreviated to CPD) or dicyclopentadiene (abbreviated to DCPD) homopolymer or copolymer resins, terpene homopolymer or copolymer resins, C5-cut homopolymer or copolymer resins, and blends of these resins. Among the above copolymer resins, mention may more particularly be made of those chosen from the group formed by (D)CPD/vinylaromatic copolymer resins, (D)CPD/terpene copolymer resins, (D)CPD/C5-cut copolymer resins, terpene/vinylaromatic copolymer resins, C5-cut/vinylaromatic copolymer resins and blends of these resins.
The term “terpene” includes here, as is known, alpha-pinene, beta-pinene and limonene monomers. It is preferable to use a limonene monomer, a compound which, as is known, can take the form of three possible isomers: L-limonene (laevogyratory enantiomer), D-limonene (dextrogyratory enantiomer), or else dipentene (the racemic mixture of the dextrogyratory and laevogyratory enantiomers). Suitable vinylaromatic monomers are for example: styrene, alpha-methylstyrene, ortho-methylstyrene, meta-methylstyrene and para-methylstyrene, vinyltoluene, para-tert-butylstyrene, methoxystyrenes, chlorostyrenes, hydroxystyrenes, vinylmesitylene, divinylbenzene, vinylnaphthalene and any vinylaromatic monomer derived from a C9-cut (or more generally a C8- to C10-Cut).
More particularly, mention may be made of resins chosen from the group formed by (D)CPD homopolymer resins, (D)CPD/styrene copolymer resins, polylimonene resins, limonene/styrene copolymer resins, limonene/D(CPD) copolymer resins, C5-cut/styrene copolymer resins, C5-cut/C9-cut copolymer resins and blends of these resins.
All the above resins are well known to those skilled in the art and are commercially available, for example sold by DRT under the name “Dercolyte” as regards polylimonene resins, sold by Neville Chemical Company under the name “Super Nevtac” or sold by Kolon under the name “Hikorez” as regards C5-cut/styrene resins or C5-cut/C9-cut resins, or else by Struktol under the name “40 MS” or “40 NS” or by Exxon Mobil under the name “Escorez” (which are blends of aromatic and/or aliphatic resins).
The self-sealing composition has the essential feature of further comprising, with a content of less than 60 phr (in other words between 0 and 60 phr), a plasticizing agent which is liquid (at 23° C.) called a “low Tg” plasticizing agent, the function of which is especially to soften the matrix by diluting the diene elastomer and the hydrocarbon resin, in particular improving the “cold” self-sealing performance (that is to say the performance typically for a temperature below 0° C.). Its Tg is by definition below −20° C. and is preferably below −40° C.
Any liquid elastomer, or any extender oil, whether of aromatic or non-aromatic nature, or more generally any liquid plasticizing agent known for its plasticizing properties with respect to elastomers, especially diene elastomers, can be used. At room temperature (23° C.), these plasticizers or oils, which are relatively viscous, are liquids (that is to say, as a reminder, substances having the capability of eventually adopting the form of their container), as opposed, in particular, to hydrocarbon resins which by their nature are solids at room temperature.
Particularly suitable are liquid elastomers having a low number-average molecular weight (Mn) of typically between 300 and 90 000, more generally between 400 and 50 000, for example in the form of liquid BR, liquid SBR, liquid IR or depolymerized natural rubber, as described for example in the aforementioned patent documents U.S. Pat. No. 4,913,209, U.S. Pat. No. 5,085,942 and U.S. Pat. No. 5,295,525. Blends of such liquid elastomers with oils as described below may also be used.
Also suitable are extender oils, especially those chosen from the group formed by polyolefin oils (i.e. those resulting from the polymerization of olefins, monoolefins or diolefins), paraffinic oils, naphthenic oils (of low or high viscosity, and hydrogenated or non-hydrogenated), aromatic or DAE (distillate aromatic extract) oils, MES (medium extracted solvate) oils, TDAE (treated distillate aromatic extract) oils, mineral oils, vegetable oils (and oligomers thereof, e.g. rapeseed, soybean or sunflower oils) and mixtures of these oils.
According to one particular embodiment, a polybutene-type oil may for example be used, in particular a polyisobutylene (PIB) oil, which has exhibited an excellent compromise of properties in comparison with the other oils tested, especially a conventional paraffinic oil. As examples, PIB oils are sold in particular by Univar under the name “Dynapak Poly” (e.g. “Dynapak Poly 190”), by BASF under the name “Glissopal” (e.g. “Glissopal 1000”) or “Oppanol” (e.g. “Oppanol B12”); paraffinic oils are sold for example by Exxon under the name “Telura 618” or by Repsol under the name “Extensol 51”.
Also suitable, as liquid plasticizers, are ether, ester, phosphate and sulphonate plasticizers, more particularly those chosen from esters and phosphates. As preferred phosphate plasticizers, mention may be made of those that contain between 12 and 30 carbon atoms, for example trioctyl phosphate. As preferred ester plasticizers, mention may in particular be made of compounds chosen from the group formed by trimellitates, pyromellitates, phthalates, 1,2-cyclohexane dicarboxylates, adipates, azelates, sebacates, glycerol triesters and mixtures of these compounds. Among the above triesters, mention may be made as preferred glycerol triesters of those that predominantly comprise (for more than 50% and more preferably for more than 80% by weight) a C18 unsaturated fatty acid, that is to say a fatty acid chosen from the group formed by oleic acid, linoleic acid, linolenic acid and mixtures of these acids. More preferably, the fatty acid used, whether of synthetic or natural origin (the case, for example, of sunflower or rapeseed vegetable oils), is composed of, for more than 50% by weight and even more preferably for more than 80% by weight, oleic acid. Such triesters (trioleates) having a high oleic acid content are well known—they have been described for example in application WO 02/088238 (or US 2004/0127617)—as plasticizing agents in tyre treads.
The number-average molecular weight (Mn) of the liquid plasticizer is preferably between 400 and 25 000 g/mol, more preferably still between 800 and 10 000 g/mol. For excessively low Mn values, there is a risk of the plasticizer migrating to the outside of the composition, whereas excessively high Mn values may result in this composition becoming too stiff. An Mn value between 1000 and 4000 g/mol proves to be an excellent compromise for the intended applications, in particular for use in a pneumatic tyre.
The number-average molecular weight (Mn) of the plasticizer may be determined in a known manner, especially by SEC, the specimen being firstly dissolved in tetrahydrofuran to a concentration of about 1 g/l and then the solution is filtered on a filter of 0.45 μm porosity before injection. The apparatus is the WATERS Alliance chromatograph. The elution solvent is tetrahydrofuran, the flow rate is 1 ml/min, the temperature of the system is 35° C. and the analysis time is 30 min. A set of two WATERS columns with the trade name “STYRAGEL HT6E” is used. The injected volume of the polymer specimen solution is 100 μl. The detector is a WATERS 2410 differential refractometer and its associated software for handling the chromatograph data is the WATERS MILLENIUM system. The calculated average molecular weights are relative to a calibration curve obtained with polystyrene standards.
To summarize, the liquid plasticizer is preferably chosen from the group formed by liquid elastomers, polyolefin oils, naphthenic oils, paraffinic oils, DAE oils, MES oils, TDAE oils, mineral oils, vegetable oils, ether plasticizers, ester plasticizers, phosphate plasticizers, sulphonate plasticizers and mixtures of these compounds. More preferably, this liquid plasticizer is chosen from the group formed by liquid elastomers, polyolefin oils, vegetable oils and mixtures of these compounds.
A person skilled in the art will be able, in the light of the description and the exemplary embodiments that follow, to adjust the amount of liquid plasticizer according to the particular usage conditions of the self-sealing composition, especially of the pneumatic tyre in which it is intended to be used.
Preferably, the liquid plasticizer content is in the 5 to 40 phr range, more preferably in the 10 to 30 phr range. Below the indicated minima, the elastomer composition runs the risk of being too stiff for certain applications, whereas above the recommended maxima there is a risk of insufficient cohesion of the composition and of degraded self-sealing properties.
The composition of the self-sealing layer has the essential feature of being unfilled or only very lightly filled, that is to say containing from 0 to less than 30 phr of filler.
The term “filler” is understood here to mean any type of filler, whether reinforcing (typically nanoparticles with a weight-average size preferably of less than 500 nm, especially between 20 and 200 nm) or whether non-reinforcing or inert (typically microparticles with a weight-average size of greater than 1 μm, for example between 2 and 200 μm).
These fillers, whether reinforcing or not, are essentially there only to give the final composition dimensional stability, i.e. the minimum mechanical integrity required. When the filler is known to be reinforcing vis-à-vis an elastomer, especially an isoprene elastomer such as natural rubber, it is preferable to use an even smaller amount thereof in the composition.
Too high an amount, especially more than 30 phr, no longer makes it possible to achieve the minimum required flexibility, deformability and flow properties. For these reasons, the composition preferably contains 0 to less than 20 phr, more preferably 0 to less than 10 phr, of filler.
As examples of fillers known to those skilled in the art as reinforcing fillers, mention will in particular be made of carbon black nanoparticles or a reinforcing inorganic filler, or a blend of these two types of filler.
For example, as carbon blacks, all carbon blacks, especially blacks of the HAF, ISAF and SAF types that are conventionally used in tyres (these being called tyre-grade blacks), are suitable. Among such blacks, the following will more particularly be mentioned: carbon blacks of the 300, 600 or 700 (ASTM) grade (for example the blacks N326, N330, N347, N375, N683 and N772). Suitable reinforcing inorganic fillers are especially mineral fillers of the silica (SiO2) type, especially precipitated or pyrogenic silica having a BET surface area of less than 450 m2/g, preferably from 30 to 400 m2/g.
As examples of fillers known to those skilled in the art as non-reinforcing or inert fillers, the following will especially be mentioned: microparticles of natural calcium carbonate (chalk) or synthetic calcium carbonate, synthetic or natural silicates (such as kaolin, talc or mica), milled silicas, titanium oxides, aluminas or even aluminosilicates. As examples of platy fillers, graphite particles may also be mentioned. Colouring or coloured fillers could be advantageously used to colour the composition according to the desired colour.
The physical state of the filler does not matter—it could be in the form of powder, microspheres, granules or beads, or any other suitable densified form. Of course, the term “filler” is also understood to mean mixtures of various reinforcing and/or non-reinforcing fillers.
A person skilled in the art will know, in the light of the present description, how to adjust the formulation of the self-sealing composition so as to achieve the desired property levels and to adapt the formulation to the envisaged specific application.
According to one particular advantageous embodiment, if a reinforcing filler is present in the self-sealing composition, its content is preferably less than 5 phr (i.e. between 0 and 5 phr), in particular less than 2 phr (i.e. between 0 and 2 phr). Such contents have proved to be particularly favourable to the process for manufacturing the composition, while still providing it with excellent self-sealing performance. More preferably a content between 0.5 and 2 phr is used, particularly when the filler is carbon black.
The base constituents of the self-sealing layer described above, namely the unsaturated diene elastomer, the hydrocarbon plasticizing resin, the liquid plasticizer and the optional filler, are sufficient in themselves for the self-sealing composition to completely fulfil its puncture-resistance function within the pneumatic tyres in which it is used.
However, various other additives may be added, typically in a small amount (preferably with contents of less than 20 phr, more preferably less than 15 phr), such as for example protective agents, such as UV stabilizers, antioxidants or antiozonants, various other stabilizers, and colouring agents that can be advantageously used to colour the self-sealing composition. Depending on the intended application, fibres, in the form of short fibres or pulp, could optionally be added to give the self-sealing composition greater cohesion.
According to a preferred embodiment, the self-sealing composition further includes a system for crosslinking the unsaturated diene elastomer. This crosslinking system is preferably a sulphur-based crosslinking system, in other words what is called a “vulcanization” system.
Preferably, the sulphur-based vulcanization system includes, as vulcanization activator, a guanidine derivative, i.e. a substituted guanidine. Substituted guanidines are well known to those skilled in the art (see for example WO 00/05300) and non-limiting examples that may be mentioned include: N,N′-diphenylguanidine (abbreviated to DPG), triphenylguanidine or else di-o-tolylguanidine. Preferably, DPG is used.
In this vulcanization system, to obtain optimum self-sealing performance the sulphur content is preferably between 0.1 and 1.5 phr, in particular between 0.2 and 1.2 phr (for example between 0.2 and 1.0 phr) and the guanidine derivative content is itself between 0 and 1.5 phr, in particular between 0 and 1.0 phr (especially in the 0.2 to 0.5 phr range).
Said system does not require a vulcanization accelerator to be present. According to a preferred embodiment, the composition may therefore contain no such accelerator, or at the very most it may contain less than 1 phr, more preferably less than 0.5 phr, thereof. If such an accelerator is used, examples that may be mentioned include any compound (primary or secondary accelerator) capable of acting as a vulcanization accelerator for diene elastomers in the presence of sulphur, especially accelerators of the thiazole type and derivatives thereof, accelerators of the thiuram and zinc dithiocarbamate types. According to another advantageous embodiment, the above vulcanization system may contain no zinc or zinc oxide (these being known as vulcanization activators).
According to another possible embodiment of the self-sealing layer, a sulphur donor may also be used instead of sulphur itself. Sulphur donors are well known to those skilled in the art. Typically, the amount of such a sulphur donor will preferably be adjusted to be between 0.5 and 10 phr, more preferably between 1 and 5 phr, so as to achieve the preferred equivalent sulphur contents indicated above.
After curing, a vulcanization system as described above gives the composition sufficient cohesion, without truly vulcanizing it: the amount of crosslinking, which can be measured using a conventional swelling method known to those skilled in the art, is in fact close to the detection threshold.
Apart from the elastomers described above, the self-sealing composition could also contain, again as a minor weight fraction relative to the unsaturated diene elastomer, polymers other than elastomers such as, for example, thermoplastic polymers compatible with the unsaturated diene elastomer.
The composition of the self-sealing layer described above may be manufactured by any appropriate means, for example by compounding and/or kneading in blade mixers or open mills, until an intimate homogeneous mixture of its various components has been obtained.
However, the following manufacturing problem may arise: in the absence of any filler, or at least an appreciable amount of filler, the composition is not very cohesive. This lack of cohesion may be such that the tack of the composition, due moreover to the presence of a relatively high hydrocarbon resin content, is not compensated for and causes some of the composition to be carried away—it follows that there is a risk of it sticking undesirably on the compounding tools, which situation may be unacceptable under industrial operating conditions.
To alleviate the above problems, the self-sealing composition, when it includes a vulcanization system, may be prepared using a process comprising the following steps:
The above first and second temperatures are of course those of the masterbatch and of the self-sealing composition respectively, these being temperatures measureable in situ and not the set temperatures of the mixers themselves.
The term “masterbatch” should be understood here to mean, by definition, the compound comprising at least the diene elastomer and the hydrocarbon resin, namely the precursor compound for the final self-sealing composition, ready to be used.
The liquid plasticizer may be completely or partly incorporated at any moment, especially during the manufacture of the masterbatch itself (in this case, before, during or after incorporation of the hydrocarbon resin into the diene elastomer), “hot” (i.e. at a temperature above the softening point of the resin), or at a lower temperature, or for example after the manufacture of the masterbatch (in this case, before, during or after addition of the crosslinking system).
Optionally, various additives may be incorporated into this masterbatch, whether these are intended for the masterbatch proper (for example a stabilizing agent, a colorant, a UV stabilizer, an antioxidant, etc.) or for the final self-sealing composition for which the masterbatch is intended.
Such a process has proved to be particularly suitable for rapidly manufacturing, under industrially acceptable operating conditions, an effective self-sealing composition, which composition may have high hydrocarbon resin contents without requiring in particular the use of a liquid plasticizer in a particularly high content.
It is during the hot compounding step a) that the diene elastomer is brought into contact with the hydrocarbon resin in order to manufacture the masterbatch. In the initial state, that is to say before it comes into contact with the elastomer, the resin may be in the solid state or in the liquid state. Preferably, for better compounding, the solid diene elastomer is brought into contact with the hydrocarbon resin in the liquid state. To do this, it suffices to heat the resin to a temperature above its softening point. Depending on the type of hydrocarbon resin used, the hot compounding temperature is typically above 70° C., usually above 90° C., for example between 100° C. and 150° C.
It is preferred for the liquid plasticizer to be at least partly introduced during step a) in the manufacture of the masterbatch itself, more preferably in this case either at the same time as the hydrocarbon resin or after the latter has been introduced. According to one particularly advantageous embodiment, the hydrocarbon resin and the liquid plasticizer may be blended together prior to incorporation into the diene elastomer.
Step b) of incorporating the crosslinking system is carried out at a temperature preferably below 80° C., furthermore preferably below the softening point of the resin. Thus, depending on the type of hydrocarbon resin used, the compounding temperature of step b) is preferably below 50° C., more preferably between 20° C. and 40° C.
If necessary, an intermediate step of cooling the masterbatch may be inserted between the above steps a) and b) so as to bring the masterbatch temperature to a value below 100° C., preferably below 80° C., especially below the softening point of the resin, before introduction (step b)) of the crosslinking system into the masterbatch prepared beforehand.
When a filler such as carbon black is used, it may be introduced during step a), i.e. at the same time as the unsaturated diene elastomer and the hydrocarbon resin, or else during step b), i.e. at the same time as the crosslinking system. It has been found that a very small proportion of carbon black, preferably between 0.5 and 2 phr, further improves the compounding and the manufacture of the composition, and also its final extrudability.
Step a) of manufacturing the masterbatch is preferably carried out in a compounding screw extruder as shown schematically for example in a simplified manner in
The products, driven by the extrusion screw, are intimately compounded under the very high shear provided by the rotation of the screw, thus progressing through the compounder, for example up to a part 24 called the “chopper-homogenizer”, after which zone the final masterbatch 25 thus obtained, progressing in the direction of the arrow F, is finally extruded through a die 26 for extruding the product to the desired dimensions.
The masterbatch thus extruded, ready to be used, is then transferred and cooled, for example on an external mixer of the open mill type for introducing the crosslinking system and the optional filler, the temperature within said external mixer being kept below 100° C., preferably below 80° C. and furthermore being preferably below the softening point of the resin. Advantageously, the rolls of the above open mill are cooled, for example by circulating water, to a temperature below 40° C., preferably to below 30° C., so as to avoid any undesirable sticking of the composition to the walls of the mill.
It is possible for the masterbatch output by the extrusion device 20 to be formed directly, so as to make it easier to transport to and/or place in the external mixer. It is also possible for the external mixer of the open mill type to be continuously fed.
Thanks to the preferred process and specific device described above, it is possible to prepare the composition of the self-sealing layer under satisfactory industrial conditions without running the risk of contaminating the tools due to undesirable sticking of the composition on the walls of the mixers.
The airtight layer 10 (having a thickness of 0.7 to 0.8 mm) in one particular embodiment is based on butyl rubber and has a conventional formulation for an inner liner which usually defines, in a conventional pneumatic tyre, the radially inner face of the tyre intended to protect the carcass reinforcement from the diffusion of air originating from the space inside the pneumatic tyre. This airtight layer 10 therefore allows the pneumatic tyre 1 to be inflated and kept pressurized; its leaktight properties allow it to guarantee a relatively low pressure loss factor, making it possible to keep the tyre inflated, in the normal operating state, for a sufficient duration, normally several weeks or several months.
The pneumatic tyre from
With reference to
In a two-step manufacturing process, the pneumatic tyre blank is then shaped to take the form of a torus. The separable protective layer 12 consisting of a fluorinated thermoplastic film, for example of an FEP copolymer of ethylene and propylene, has a sufficiently low stiffness, sufficient uniaxial and biaxial extensibility and is sufficiently bonded to the surface of the self-sealing layer due to the tack of the latter to follow the movements of the pneumatic tyre blank without detaching or tearing.
After the shaping, the crown plies and the tread are positioned on the pneumatic tyre blank. The thus finished blank is placed in a curing mould and is vulcanized. During the vulcanization, the separable protective layer protects the curing membrane of the mould from any contact with the self-sealing layer.
On exiting the curing mould, the separable protective layer 12 is always attached to the self-sealing layer 11.
The separable protective layer 12 may be easily removed after exiting the vulcanization mould of the pneumatic tyre. It is also possible, and preferable, to leave this protective layer in place during all the pneumatic tyre transport and storage phases. It is then removed during the fitting of the pneumatic tyre onto its service rim. This is the first step of the fitting process.
The pneumatic tyre from
The following table presents a set of thermoplastic films tested. FEP is understood to mean a film comprising a copolymer of fluorinated ethylene and of fluorinated propylene, ETFE is understood to mean an ethylenetetrafluoroethylene, PTFE is understood to mean a polytetrafluoroethylene, PA is understood to mean a polyamide or nylon PA-6 or PA-6,6, and PMP is understood to mean a polymethylpentene.
It should be noted that the only thermoplastic films that were able to be detached from the self-sealing layer are the FEP films. All the others, and especially the films based on polyamide PA-6 and PA-6,6 remained adhesively bonded to the surface of the self-sealing layer after the vulcanization of the pneumatic tyre.
The self-sealing layer 10 presented in
The above self-sealing composition was prepared using a single-screw (L/D=40) extruder as shown schematically in
Similar results were obtained using, as the self-sealing layer, a composition comprising a thermoplastic styrene (TPS) elastomer, as described above.
The above extruder was provided with a die for extruding the masterbatch to the desired dimensions into an external open mill for the final incorporation of the other constituents, namely the vulcanization system based on sulphur (for example 0.5 or 1.2 phr) and DPG (for example 0.3 phr) and carbon black (with a content of 1 phr), at low temperature maintained below +30° C. (by cooling the rolls with circulating water).
The self-sealing layer 11, placed therefore between the airtight layer 10 and the cavity of the tyre, gives the tyre effective protection against loss of pressure due to accidental perforations, enabling these perforations to be automatically sealed off.
If a foreign body, such as a nail, passes through the structure of the pneumatic tyre, for example a wall, such as a sidewall 3 or the crown 6 of the pneumatic tyre 1, the composition serving as self-sealing layer is subjected to several stresses. In reaction to these stresses, and thanks to its advantageous deformability and elasticity properties, said composition creates an airtight contact zone right around the body. It does not matter whether the contour or the profile of said body is uniform or regular, the flexibility of the self-sealing composition enables it to be insinuated into openings of very small size. This interaction between the self-sealing composition and the foreign body seals the zone affected by said body.
In the event of the foreign body being removed, whether accidentally or intentionally, a perforation remains, this being liable to create a relatively large leak, depending on its size. The self-sealing composition, exposed to the hydrostatic pressure, is sufficiently soft and deformable to seal off, by being deformed, the perforation, preventing the inflation gas from leaking. In particular in the case of a pneumatic tyre, it has been shown that the flexibility of the self-sealing composition enables the forces of the surrounding walls to be withstood without any problems, even during phases in which the loaded pneumatic tyre deforms when running.
During tests, pneumatic tyres of the passenger car type, of 205/55 R16 size (Michelin, “Energy 3” brand) were tested. The inner wall of the tyres (already comprising the airtight layer 10) was covered by the self-sealing layer (10a) described above, having a thickness of 3 mm, then the tyres were vulcanized.
On one of the pneumatic tyres, when fitted and inflated, eight perforations 5 mm in diameter were produced through the tread and the crown block on the one hand, and through the sidewalls on the other, using punches that were immediately removed.
Unexpectedly, this tyre withstood being rotated at 150 km/h on a rolling drum under a nominal load of 400 kg without loss of pressure for more than 1500 km, after which distance the rolling was stopped.
On another pneumatic tyre, the test was carried out in the same way but this time leaving the perforating objects in place for one week. The same excellent result was obtained.
Without the self-sealing composition and under the same conditions as above, the pneumatic tyre thus perforated loses its pressure in less than one minute, becoming completely unsuitable for rolling.
Endurance tests were also carried out on pneumatic tyres according to the invention, identical to the previous tyres, but having been run for 750 km, at a speed of 150 km/h, this time leaving the punches in place in their perforations. After the punches had been removed (or after their expulsion as a result of the rolling), these pneumatic tyres of the invention withstood being rotated on a rolling drum without loss of pressure, under the same conditions as previously (distance travelled of 1500 km at a speed of 150 km/h and under a nominal load of 400 kg).
The invention is not limited to the examples described and represented, and various modifications may be made thereto without departing from the scope thereof defined by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0955113 | Jul 2009 | FR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2010/060623 | 7/22/2010 | WO | 00 | 4/20/2012 |