20240133750
The present invention relates to a method for instrumenting a tyre for measuring the temperature inside a rubber compound of said tyre when it is running. The tyres that are primarily of interest are fitted to construction plant vehicles for mining.
For example, such vehicles (dumpers or dump trucks) are used in opencast mines for transporting materials extracted from quarries with loads that can reach a mass of over 350 tonnes. The tyres are sized accordingly, and can each weigh around 5 tonnes.
By way of illustration, a tyre to which the invention relates has a standardized designation according to ETRTO (European Tyre and Rim Technical Organisation) of the 59/80 R 63 type, with an inflation pressure of 650 kPa. The outside diameter of the tyre mounted on a rim and inflated to 650 kPa may measure more than 4 metres. Other diameters of 49 to 57 inches can also be found on these vehicles.
By convention, in a frame of reference (O, t, y, r), the centre O of which coincides with the centre of the tyre, the circumferential direction (O, t), axial direction (O, y) and radial direction (O, r) refer to a direction tangential to the tread surface of the tyre in the direction of rotation, to a direction parallel to the axis of rotation of the tyre, and to a direction orthogonal to the axis of rotation of the tyre, respectively.
Radially inner and radially outer mean closer to and further away from the axis of rotation of the tyre, respectively.
Axially inner and axially outer mean closer to and further away from the equatorial plane of the tyre, respectively, the equatorial plane of the tyre being the plane that passes through the middle of the tread of the tyre and is perpendicular to the axis of rotation of the tyre.
An elastomeric compound, or rubber compound, is understood to be an elastomeric material obtained by blending its various constituents. An elastomeric compound conventionally comprises an elastomer matrix comprising at least one diene elastomer of the natural or synthetic rubber type, at least one reinforcing filler of the carbon black type and/or of the silica type, a crosslinking system that is usually sulphur-based, and protective agents.
An elastomeric compound can be mechanically characterized, in particular after curing, by its dynamic properties, such as a dynamic shear modulus G*=(G′2+G″2)1/2, where G′ is the elastic shear modulus and G″ is the viscous shear modulus, and a dynamic loss tan δ=G″IG′. The dynamic shear modulus G* and the dynamic loss tan δ are measured on a Metravib VA4000 viscosity analyser according to the standard ASTM D 5992-96. The response of a sample of vulcanized elastomeric compound in the form of a cylindrical test specimen with a thickness of 4 mm and a cross section of 400 mm2, subjected to a simple alternating sinusoidal shear stress at a frequency of 10 Hz, with a strain amplitude sweep from 0.1% to 50% (outward cycle) and then from 50% to 0.1% (return cycle), at a given temperature, for example equal to 60° C., is recorded. These dynamic properties are thus measured for a frequency equal to 10 Hz, a strain equal to 50% of the peak-to-peak strain amplitude, and a temperature that can be equal to 60° C. or 100° C.
An elastomeric compound can also be characterized by static mechanical properties. The tensile tests make it possible to determine the elasticity stresses and the properties at break. Unless indicated otherwise, they are carried out in accordance with the French standard NF T 46-002 of September 1988. The secant moduli known as “nominal” secant moduli (or apparent stresses, in MPa) at 10% elongation (denoted “MA10”) and 100% elongation (“MA100”) are measured in second elongation (i.e. after an accommodation cycle). All these tensile measurements are carried out under standard temperature (23±2° C.) and hygrometry (50±5% relative humidity) conditions, according to the French standard NF T 40-101 (December 1979). The stresses at break (in MPa) and the elongations at break (in %) are also measured, at a temperature of 23° C.
Generally, a tyre comprises a tread intended to come into contact with the ground via a tread surface, the two axial ends of which are connected via two sidewalls to two beads that provide the mechanical connection between the tyre and the rim on which it is intended to be mounted.
A radial tyre also comprises a reinforcement made up of a crown reinforcement radially on the inside of the tread and a carcass reinforcement radially on the inside of the crown reinforcement.
The carcass reinforcement of a radial tyre for a heavy-duty vehicle of construction plant type usually comprises at least one carcass layer comprising generally metal reinforcers that are coated in an elastomer compound that is obtained by blending and is known as a coating compound. A carcass layer comprises a main part that joins the two beads together and is generally wound, in each bead, from the inside of the tyre to the outside, around a usually metal circumferential reinforcing element known as a bead wire so as to form a turn-up. The metal reinforcers of a carcass layer are substantially mutually parallel and form an angle of between 85° and 95° with the circumferential direction.
The crown reinforcement of a radial tyre for a heavy-duty vehicle of construction plant type comprises a superposition of circumferentially extending crown layers, radially on the outside of the carcass reinforcement. Each crown layer is made up of generally metal reinforcers that are mutually parallel and coated in a rubber compound known as a coating compound.
Among the crown layers, a distinction is usually made between the protective layers, which make up the protective reinforcement and are radially outermost, and the working layers, which make up the working reinforcement and are radially comprised between the protective reinforcement and the carcass reinforcement.
The protective reinforcement, which comprises at least one protective layer, essentially protects the working layers from mechanical or physicochemical attacks, which are likely to spread through the tread radially towards the inside of the tyre.
The protective reinforcement of tyres of GC type, such as those described above, usually comprises two radially superposed protective layers formed of elastic metal reinforcers that are mutually parallel in each layer and are crossed from one layer to the next, forming angles at least equal to 10° and at most equal to 35° with the circumferential direction.
The working reinforcement, comprising at least two working layers, has the function of belting the tyre and conferring stiffness and road holding on it. It absorbs both mechanical inflation stresses, which are generated by the tyre inflation pressure and transmitted by the carcass reinforcement, and mechanical stresses caused by running, which are generated as the tyre runs over the ground and are transmitted by the tread. It is also intended to withstand oxidation and impacts and puncturing, notably by virtue of its intrinsic design and that of the protective reinforcement.
The working reinforcement usually comprises two radially superposed working layers formed of inextensible metal reinforcers that are mutually parallel in each layer and are crossed from one layer to the next, forming angles at most equal to 60°, and preferably at least equal to 15° and at most equal to 45°, with the circumferential direction. Here, inextensible metal reinforcers are understood to mean a metal reinforcer characterized by an elongation, under a tensile force equal to 10% of the force at break, at most equal to 0.2%.
In order to reduce the mechanical inflation stresses that are transmitted to the working reinforcement, it is known practice to dispose a hoop reinforcement radially on the outside of the carcass reinforcement. The hoop reinforcement, the function of which is to at least partially absorb the mechanical inflation stresses, improves the endurance of the crown reinforcement by stiffening the crown reinforcement. The hoop reinforcement may be positioned radially on the inside of the working reinforcement, between the two working layers of the working reinforcement, or radially on the outside of the working reinforcement.
The hoop reinforcement usually comprises two radially superposed hooping layers formed of metal reinforcers that are mutually parallel in each layer and are crossed from one layer to the next, forming angles at most equal to 10° with the circumferential direction.
Mining consists in extracting minerals, that is to say rocks from the Earth's crust containing useful minerals or metals in a proportion high enough to justify their exploitation.
The transporting step in mining is essential for its economic viability. The vehicles (dumpers or dump trucks) generally operate without stopping in order to obtain maximum productivity by moving the greatest volume of rubble to be processed by mineral processing operations.
The management of the tyres of the vehicle fleet consists in monitoring the inflation pressure, the temperature, and the wear using a predictive maintenance approach, so as to anticipate malfunctions linked to the tyres and thus to avoid stoppage of the vehicle in order to maximize its period of use.
As a result, one of the expectations of clients in the mining sector is the productivity of the exploitation, which should not be affected by defects in the product, and therefore the period of use of the tyres, which should be as long as possible. It is necessary to avoid stoppages of the vehicles and consequently there is a need to develop preventative maintenance for controlled use of the tyres.
The monitoring of the temperature of the tyres in real time is an essential step for managing the vehicle fleet. The temperature is directly linked to the endurance and the service life of the tyres.
Document FR3060463 proposes a method for estimating the harshness of the use conditions of a tyre mounted on a vehicle. One step of this method involves evaluating the temperature inside a compound, but this evaluation is based on a mathematical model which can be complex to implement in certain cases.
The application WO 2008046766A1 discloses a method for indicating the ageing experienced by a tyre, wherein a temperature is measured locally at least at one point on the tyre. This method requires the installation of a temperature sensor directly in the tyre, which can give rise to additional costs.
To obtain temperature measurements inside the rubber compounds of a tyre, there are conventional methods that make use for example of thermocouples, but these approaches require many interventions to install the thermocouples and take measurements. Moreover, these conventional methods assume that the vehicle has stopped in order to measure the temperature and therefore cause the mining productivity to drop for accurate measurements of the temperature.
Within the context of mining, in which profitability is directly linked to the running time of the vehicles, the approaches described above are not suitable.
There is still a need for accessing the temperatures inside the rubber compounds of a tyre when it is running, in a straightforward, nondestructive and automatic way, without stopping the vehicle of which the tyres are measured. It is necessary to be able to locate the areas of the tyre that are most sensitive to heat in order to measure the temperature in real time. To do this, the running conditions such as the nature of the ground, whether it is stony, muddy or tarmacked, the internal structure of the tyre, or else the topography of the mine need to be taken into consideration.
To access the temperatures, the inventors have set themselves the objective of finding a method for instrumenting the tyre that incorporates the conditions mentioned above.
The proposed solution is a method for instrumenting a construction plant tyre for measuring the temperature inside the rubber compounds in the areas most sensitive to heat, while the tyres are running. This method comprises the following steps:
A construction plant tyre comprises a tread intended to be in contact with the ground. The nature of the ground varies depending on the use conditions, which are sometimes muddy, stony or tarmacked. To adapt to the various soil types, the tread has cuts, notably transverse, circumferential or oblique cuts, so as to define blocks of rubber compound that are intended to provide sufficient grip irrespective of the nature of the ground to transmit the torque of the vehicle. The blocks of rubber compound of the tread also have sipes for forming flexibility-enhancing sipe blades with a view to promoting grip on snowy ground, for example.
The first step of the tyre instrumentation method consists in examining the outer surface of the tyre to identify sensor insertion areas. This step is based, for example, on the visual expertise of those skilled in the art during the examination of the outer surface of the tyre to detect the sensor insertion areas.
Preferably, one of the predefined selection criteria for the drilling area for the insertion of a temperature measuring sensor consists in being positioned in the tread of the tyre that is intended to be in contact with the ground. Additional criteria can be defined depending on the running conditions such as the nature of the ground, whether it is stony, muddy or tarmacked, the internal structure of the tyre, or else the topography of the mine.
The blocks of rubber compound of the tread are periodically in contact with the ground, and are subjected to severe stresses during running. It follows that the temperature is often very high in these high-strain areas. To avoid any self-combustion of these blocks of rubber, it is important to be able to know their temperature in the event of severe stresses. The insertion of sensors in these blocks of rubber makes it possible to access their temperature levels in real time.
The invention also provides that the areas of the tyre that are located in the lower part of the tyre at the flange of the rim can also be instrumented. These are areas of great bending caused by the tyre being crushed by the load that is carried, which are also sites of elevated temperature owing to the severe strains experienced.
After identifying the insertion areas, the drilling step is done using a drill fitted with an orientable drill bit. The drilling depth HC depends on the internal structure of the tyre, such as the number and stepped arrangement of the crown layers. For the sake of traceability, the drilling angle, Alpha, which is measured between the drilling direction and the radial direction, is recorded, since it is possible to envisage the withdrawal of the sensors from the tyre after the test sessions.
Advantageously, since the sensor has a cylindrical shape, the drilling step is performed using a drill bit with a diameter at most equal to the diameter of the sensor.
This is because, in this configuration, the introduction of the sensor into the cavity is done with natural clamping when the sensor and the cavity have the same diameter. It is easier to keep the sensor in a fixed position in these conditions.
Before the sensor is inserted, it is activated by cutting the activation wire connected to the electrodes of the sensor. The electronic circuit board is then switched on and the communication means are activated. The temperature is measured and averaged over the time interval between two transmissions.
Following the drilling, after precise cleaning of the cavities by removing the rubber residues left by the drilling operation, each sensor is fixed to the bottom and/or on the walls of the cavity.
Preferably, the fixation of the sensor to the bottom and/or on the walls of the cavity is performed by adhesive bonding.
More preferably, the adhesive bonding is performed with a cold-vulcanizing adhesive, and the setting time for the adhesive bonding is at least 24 hours.
A cold-vulcanizing adhesive is understood to mean an adhesive which causes a chemical reaction consisting in incorporating a vulcanizing agent, usually sulfur, with a crude elastomer so as to form bridges between the molecular chains. This operation notably makes the material less plastic but more elastic.
The inventors have observed that the use of such an adhesive within the context of the invention makes it possible to have high-quality adhesive bonding between the sensor and the rubber compound of the cavity.
A preferred example of adhesive is that sold by Tip Top under the “blue cement” name of adhesive.
The setting time of 24 hours ensures a sufficient level of adhesion for the fixation of the sensor in the rubber compound. The sensor thus adhesively bonded to the rubber compound is prevented from making any movement when the tyre is running.
Advantageously, the insertion of the sensor in the cavity drilled in the tyre interacts with a device for evacuating air that is present in the cavity.
When a sensor is being introduced into a cavity, a volume of air forms between the bottom of the cavity and a pushed-in first face of the sensor facing it. This volume of air resists the advancement of the sensor into the cavity. An air evacuation device must be implemented at the same time as the insertion of the sensor.
In one embodiment of the invention, a device for evacuating air from the cavity while the sensor is being inserted comprises a hollow cylindrical tube formed in the sensor, such that the introduction of the sensor into the cavity is accompanied by the expulsion of air through the hollow tube by virtue of the compression of the volume of air located between a first base of the sensor facing the bottom of the cavity.
Once each sensor has been properly fixed in the cavity, in contact with the bottom and the walls, an empty residual volume remains in the cavity radially on the outside of the sensor, which it is necessary to fill in order to protect the sensor. To protect the sensor and to ensure good leaktightness, filling means are filled into the empty volume using a filling object.
Advantageously, means for filling the cavity drilled in the tyre comprise a stopper fixed by adhesive bonding on the walls of the cavity.
Preferably, said means for filling the cavity drilled in the tyre interact with a device for evacuating air that is present in the cavity.
A device for evacuating air from the cavity that is similar to that described above for inserting the sensor in the cavity can be used to insert said filling means this time.
Advantageously, said means for filling the cavity drilled in the tyre comprise a stopper made of the same rubber compound as that forming the walls of the cavity.
The use of the same compound adhesively bonded using a cold-vulcanizing adhesive promotes the adhesion of the two supports and leads to better fixation.
To obtain temperature measurement results throughout the volume of the tyre, advantageously first sensors are positioned along a circumferential direction with a first distribution pitch, and/or second sensors are positioned in an axial direction with a second distribution pitch.
A temperature measurement operation can last from 10 to 15 days. Another subject of the invention is to be able to recover the sensors after the test sessions. For this, the invention also proposes a method for recovering a sensor after the running of a tyre, said sensor having been inserted according to the instrumentation method in a construction plant tyre as described above, said method for recovering a sensor comprising the following steps:
The gradual wear of the tread could lead to the sensor being ejected into the environment. To avoid this contamination, the sensor is recovered and some of its unaltered components are reused.
Advantageously, the step of recovering the sensor after the running of the tyre comprises a device a step of dissolving the fixing adhesive.
If, for example, the means for filling the cavity are an adhesively bonded stopper as described above, to withdraw the sensor it is necessary first of all to remove the stopper adhesively bonded in the cavity. A dissolution solvent makes it possible to break the adhesion of the adhesive between the stopper and the cavity. The use of a tool in the form of a corkscrew makes it possible to withdraw the stopper. To withdraw the sensor, it is also necessary to use a dissolution solvent to break the adhesion of the adhesive between the surfaces of the sensor and of the cavity. Use is then made of a device comprising a hollow tube which passes through the sensor in the direction of the greatest length of the cavity. Advantageously, the step of recovering the sensor comprises a compressed-air injection device for expelling the sensor. The injection of compressed air into said hollow tube is accompanied by the expulsion of the sensor out of the tyre.
The withdrawal of the stopper, and then of the sensor, results in damage to the tyre. Advantageously, the method for recovering the sensor comprises a step of repairing the tyre after extraction of the stopper and the sensor from the cavity.
The repair step consists for example in filling all of the cavity with a rubber stopper in a manner similar to that described above for the stopper in the instrumentation method. Beforehand, each is cleaned so as to eliminate the residues of rubber compound that may be present there.
The invention also relates to a tyre having a sensor for measuring the internal temperature of a rubber compound, the sensor being installed according to a method as described above for instrumenting a construction plant tyre.
The invention will be better understood on reading the following description, which is given purely by way of nonlimiting example and with reference to
The tyre 20 is mounted on a vehicle fitted with a device for communicating with said sensor.
The reading means positioned in the vehicle store the data in a database, which is accessible by a remote server. The sensor 10 comprises an electronic circuit board with a circuit connecting the components, such as a temperature measuring probe, a microprocessor, a radio transmitter, and a battery.
Upon activation of the sensor, before it is inserted into the rubber compound, the activation wire 12 is cut at its end in contact with the sensor.
The tyre 20 has a tread 201 which is represented by the radially outermost volume, comprising black dots, of the tyre. The crown reinforcement 210 is formed of a working reinforcement 211, a protective reinforcement 212 and a hoop reinforcement 213, which are outwardly radially superposed. Each reinforcement comprises two layers formed of reinforcers coated in rubber compounds. Lastly, in this example the crown reinforcement comprises six radially superposed crown layers, each formed of reinforcers coated in rubber compounds. Radially on the inside of the crown reinforcement 210 is the carcass reinforcement 220, which comprises at least one carcass layer formed of a main strand 217 which surrounds a bead wire 218 axially from the inside to the outside of the bead and is continued radially outwards by a turn-up strand 216. The reinforcers of the carcass layer make an angle of approximately 90° with the circumferential direction.
This architecture optimizes the endurance of the tyre to bear the load required, but has the drawback of being sensitive to temperature, which catalyses the tyre cracking and damage phenomena, notably at the ends of the crown layers.
Still in
The invention has been implemented on a tyre of size 59/80 R63 designated by the ETRTO (European Tyre and Rim Technical Organisation) standard which is fitted to a vehicle of dumper truck type. The tyre tested is inflated to 650 kPa.
The front axle of the dumper truck has been fitted with these sizes of tyre mentioned above. The load on the front axle is 63 tonnes.
The sensors have been positioned to measure the temperature close to the crown layers at the shoulders in the cavities 205 and in the centre of the tyre in the cavities 206. These areas have been identified as being those most sensitive to temperature by a digital simulation, taking account of the use of the tyres and notably of the mine that is worked. The test is run over 10 days.
The sensor comprises an electronic circuit board fitted with a temperature measuring probe and a radio transmitter, which can be interrogated by a reader positioned in the vehicle. The temperature probe, the radio transmitter and the reader have conventional references that are commercially available. The period of transmission of data from the sensor to the vehicle is five minutes.
In
The invention has the advantage of accessing the temperature level in rubber compounds easily and automatically, to the detriment of the conventional approaches, for example using thermocouples which can have an adverse effect on the productivity of mining. This is because the vehicles are not stopped and human interventions are limited in the temperature measurement method proposed by the invention.
The measurement means, the method for inserting them, the means for keeping the sensors in a fixed position, and the means for communicating the measured temperature values are supported by these results.
A first example of applying the results of the invention is to adapt the use conditions of the tyres in real time depending on the average temperature level. Warning devices can be installed to inform the driver when the temperature reaches an excessive level.
The principle of the invention can be extrapolated to different types of tyres to those described here, notably of heavy-duty type, and more generally to tyres of which the radial thickness of the tread is sufficient to implement the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2101822 | Feb 2021 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2022/050259 | 2/14/2022 | WO |