Tire with tread containing styrene, isoprene, butadiene terpolymer rubber

Abstract

A styrene, isoprene, butadiene terpolymer rubber with a characterization according to its glass transition temperatures and unit structure and a pneumatic tire with a tread composed of such terpolymer rubber specifically in combination with selected other rubber which has been observed to provide such tread with enhanced physical properties.

Description

FIELD

This invention relates to styrene, isoprene, butadiene terpolymer rubber and to tires having treads composed of compositions thereof.

BACKGROUND

Pneumatic rubber passenger and truck tires are composed of elements which conventionally include a tread of a rubber composition. The tread rubber is sometimes desirably compounded to provide a tire with a relatively low rolling resistance with reasonable wear and traction.

Although it may be desired to compound the tire's tread composition to reduce the rolling resistance of the tire without substantially reducing the tire's traction features, tire traction might be expected to be somewhat sacrificed as may be evidenced by its decrease in wet and dry skid resistance.

Various rubber compositions have been prepared for various purposes, some of which have included the tire treads. Often tire treads are composed of synthetic rubber or blends of synthetic rubber with natural rubber for the purpose of achieving desirable tire tread characteristics such as wear, traction and reduction in rolling resistance. Various synthetic rubbers have been used in the manufacture of tires with such treads including styrene/butadiene copolymers (prepared by emulsion or solution polymerization methods) sometimes referred to as SBR, high cis 1,4 polybutadiene rubber as well as high and medium vinyl (1,2-) polybutadiene rubbers. Sometimes a synthetic cis 1,4-polyisoprene may, at least in part, be substituted for the natural rubber in tire tread compositions.

Although such rubber compositions are taught to provide various benefits, some for tire treads, it continues to be desirable to provide a pneumatic tire having a rubber tread having an enhanced rolling resistance and/or treadwear commensurate with reasonable traction qualities.

DISCLOSURE AND PRACTICE OF INVENTION

In accordance with this invention, a styrene, isoprene, butadiene terpolymer rubber (hereinafter referred to as SIBR) is provided which is comprised of (A) about 5 to about 40, preferably about 10 to about 35 weight percent bound styrene, (B) about 20 to about 60, preferably about 30 to about 50, weight percent bound isoprene and (C) about 10 to about 50, preferably about 30 to about 40, weight percent bound butadiene and is characterized by having a glass transition temperature (Tg) in the range of about -70.degree. C. to about -5.degree. C. and, further, the said bound butadiene structure contains about 10 to about 50, preferably about 30 to about 40, weight percent 1,2-vinyl units, the said bound isoprene structure contains about 10 to about 40, preferably about 10 to about 30, weight percent 3,4 units and the sum of the weight percent 1,2-vinyl units of the bound butadiene and the weight percent 3,4 units of the bound isoprene is in the range of about 20 to about 90, preferably about 40 to about 70, percent.

In further accordance with this invention, such a SIBR is provided having a Tg in the range of about -10.degree. C. to about -40.degree. C. characterized in that its bound styrene content is in the range of about 30 to about 60 weight percent, and the sum of the weight percent 1,2 vinyl units of the bound butadiene and the weight percent 3,4 units of the bound isoprene is in the range of about 20 to about 45.

In further accordance with this invention, such a SIBR is provided having a Tg in the range of about -10.degree. C. to about -40.degree. C. characterized in that its bound styrene content is in the range of about 10 to about 30 weight percent, and the sum of the weight percent 1,2 vinyl units of the bound butadiene and the weight percent 3,4 units of the bound isoprene is in the range of about 45 to about 90.

In further accordance with this invention, such a SIBR is provided having a Tg in the range of about -50.degree. C. to about -70.degree. C. characterized in that its bound styrene is in the range of about 10 to about 30 weight percent, and the sum of the weight percent 1,2 vinyl units of the bound butadiene and the weight percent 3,4 units of the bound isoprene is in the range of about 20 to about 45.

In further accordance with this invention, a pneumatic tire is provided having an outer circumferential tread where said tread is a sulfur cured rubber composition comprised of, based on 100 parts by weight rubber (phr), (A) about 10 to about 90, preferably about 25 to about 70, parts by weight of the said styrene, isoprene, butadiene terpolymer rubber (SIBR) and (B) about 70 to about 30 weight percent of at least one of cis 1,4-polyisoprene rubber and cis 1,4-polybutadiene rubber.

In the description of this invention, the cis 1,4-polyisoprene rubber includes both natural and synthetic rubber. Often, the natural rubber is preferred. The cis 1,4-polyisoprene rubber, natural or synthetic, typically has a cis 1,4-content of about 96 to about 99 weight percent.

The polybutadiene rubber can be composed of about 95 percent or more of cis 1,4 structure when prepared with Ziegler-type catalyst or can be composed at least about 90 percent cis and trans 1,4 structure when prepared with alkyl lithium catalyst. Both types of rubbers are well known.

The terms butadiene and polybutadiene as used herein refer to 1,3-butadiene and polymers derived from 1,3-butadiene, respectively.

The terms bound styrene, bound butadiene and bound isoprene refer to the structure of such materials when they have been terpolymerized to form the SIBR terpolymer.

The percent 1,2 vinyl units of the bound butadiene is based on the bound butadiene itself and the percent 3,4 units of the bound isoprene is based on the bound isoprene itself and the sum thereof is in the sum of such percentages.

A preferred embodiment of the invention, particularly for tires to be used for somewhat conventional loads and speeds such as passenger vehicle tires, although the embodiment is not necessarily limited to such use, is a pneumatic tire provided with such tread where said tread is a sulfur cured rubber composition comprised of, based on 100 parts by weight rubber, (A) about 20 to about 90 phr of the SIBR and (B) about 10 to about 80 phr of said natural rubber.

Such pneumatic tires are conventionally comprised of a generally toroidal shaped carcass with an outer circumferential tread, adapted to be ground contacting, spaced beads and sidewalls extending radially from and connecting said tread to said beads.

The rubbers used herein, particularly those in the higher ML-4 (Mooney) viscosity range, can optionally be individually oil extended before or during mixing with various rubber compounding materials for ease of processing. If oil extension is used, usually about 10 to about 50 phr of rubber processing oil is used, usually of the aromatic or aromatic/paraffinic oil type, to provided a ML-4 (100.degree. C.) viscosity of about 40 to about 100, preferably about 60 to about 90, for the uncured rubber composition.

It should readily be understood by one having skill in the art that said tread portion of the pneumatic tire as well as the rubber or other material in the basic carcass, which normally contains reinforcing elements in the tread region, can be compounded by methods generally known in the rubber compounding art, such as mixing the various constituent rubbers with various materials such, as for example, curing aids, such as sulfur and accelerators, processing additives, such as oils, resins, silicas, and plasticizers, fillers, pigments, antioxidants and antiozonants and reinforcing materials such as, for example, carbon black.

The tire can be built, shaped, molded and cured by various methods which will be readily apparent to those having skill in the art.

In the practice of this invention, the polymer blend-tread can be integral with and adhered to various tire carcass substrate rubber compositions. Typically, such a rubber composition is at least one of a butadiene/styrene copolymer rubber, cis 1,4 polyisoprene (natural or synthetic rubber) and 1,4 polybutadiene. Optionally, such a blend for a portion of the tread, particularly where the tread is in the region of the sidewall area of the tire may contain one or more of butyl rubber, halobutyl rubber, such as chlorobutyl or bromobutyl rubber, and ethylene/propylene/conjugated diene terpolymer rubber, polyisoprene and polybutadiene rubber.

In the further practice of this invention, the tread can typically be applied in the building of the green tire in which the uncured, shaped tread is built onto the carcass following which the green tire is shaped and cured.

Alternately, the tread can be applied to a cured tire carcass from which the previous tread has been buffed or abraded away and the tread cured thereon as a retread.

In the practice of this invention, the SIBR is a particularly desirable and required feature of the rubber tread. The precise structure of the SIBR rubber itself may not be entirely understood, although the styrene units in the SIBR can be random, block or tapered. It has been observed that its inclusion in the rubber blend of a tire tread has provided a tire with enhanced characteristics as a desirable combination of rolling resistance, skid resistance and treadwear.

The practice of this invention is further illustrated by reference to the following examples which are intended to be representative rather than restrictive of the scope of the invention. Unless otherwise indicated, all parts and percentages are by weight.

EXAMPLE I

Pneumatic tires of conventional construction (grooved tread, sidewalls, spaced beads, and supporting fabric-reinforced carcass) were built, shaped and cured in a conventional tire mold. The tread was built onto the uncured carcass as a pre-extruded element. The tires were of the P195/75R14 type which indicates that they were belted, radial ply passenger type tires.

One tire is identified herein as Control X and experimental tires identified as Experimental Y and Experimental Z.

Control tire X had a tread composed of (A) 50 phr butadiene/styrene rubber and (B) 50 phr natural rubber and is intended to represent a somewhat conventional passenger tire tread.

Experimental tires Y and Z had a tread composed of (A) SIBR having a Tg in the range of about -40.degree. C., and (B) natural rubber with the tread of experimental tire Z also containing a conventional polybutadiene rubber.

Thus, the SIBR, basically, replaced at least a part of the butadiene/styrene rubber in the tread rubber blend.

The tires (X, Y and Z) were mounted on rims, inflated and submitted to testing. The test values for the control were normalized to a value of 100 for comparison purposes. The tire with the experimental tread was tested and its test values compared to the values of the control tire and reported relative to the normalized values of 100.

Surprisingly, the tire with the experimental tread rubber composition Y exhibited an equivalent rolling resistance and skid resistance while providing an improved treadwear as compared to control tire X. The tire with tread Z demonstrated an equivalent skid resistance, and increase in rolling resistance, yet a more improved treadwear as compared to control tire X. These results are considered to be an important departure from results which might ordinarily be expected.

The tread compositions for tires X, Y and Z were comprised of materials shown in the following Table 1.

TABLE 1______________________________________ Parts.sup.1 ExperimentalRubber Compound Control (X) (Y) (Z)______________________________________Butadiene/styrene rubber.sup.2 50 0 0oil extended (70 partsrubber, 26.25 parts oilNatural rubber 50 10 50Polybutadiene rubber.sup.3 0 20 0(1-2% vinyl)SIBR I.sup.4 0 70 0SIBR II.sup.4 0 0 50Oil, aromatic 9 9 9Antioxidant 3.2 3.2 3.2Wax 3.8 3.8 3.8Stearic acid 2 2 2Carbon black 45 45 45Sulfur 0.9 0.9 0.9Accelerator 1.9 1.9 1.9Zinc Oxide 3.5 3.5 3.5______________________________________ .sup.1 Most amounts rounded to nearest tenth of a part. .sup.2 Emulsion polymerization prepared SBR, oil extended with typical aromatic rubber processing oil. .sup.3 Conventional type polybutadiene rubber (low vinyl 1,2 and high cis 1,4). .sup.4 Polymer is composed of about 20 mole percent units derived from styrene, about 40 mole percent units derived from isoprene and about 40 percent units derived from 1,3butadiene and is the SIBR described in this specification, particularly of the type shown in Experiment A of TABLE 2 herein. SIBR I has a Tg of -42.degree. C. and SIBR II had a Tg of -31.degree. C.

Table 2 illustrates various characteristics of the SIBR of this invention, and also the type SIBR used in this Example to prepare the Experimental Y tire, namely, Experiment A:

TABLE 2______________________________________ProductAnalysis Exp A Exp B Exp C Exp D Exp E______________________________________% Styrene 20 20 20 30 30% Buta- 40 40 40 35 35diene% Isoprene 40 40 40 35 35Molecular 350,000 350,000 350,000 350,000 350,000Weight(NumberAverage)Molecular 600,000 600,000 600,000 600,000 600,000Weight(WeightAverage)Glass -40.degree. C. -20.degree. C. -60.degree. C. -40.degree. C. -10.degree. C.TransitionTempera-tureMooney 80 80 80 80 80Viscosity(ML4 at212.degree. F.)______________________________________

Table 3 illustrates various characteristics of the (Control X) and (Experimental Y and Z) rubber compound.

TABLE 3______________________________________Property Control X Exp Y Exp Z______________________________________Tensile (MN/m.sup.2) 21 20 22Elongation (%) 500 450 490Mooney (ML-4) 43 46 39Rebound (0.degree. C.) 28 22 27Rebound (100.degree. C.) 67 70 73Rheology (IV, 0.5% Strain)Tan Delta (0.degree. C.) 0.256 0.308 0.279Tan Delta (60.degree. C.) 0.185 0.167 0.161______________________________________

Table 4 illustrates the rolling resistance, wet and dry skid resistance and treadwear values with the Experimental Tire Y compared to values of Control Tire X normalized to 100.

TABLE 4______________________________________ ExperimentalMeasured Values Control X Y Z______________________________________Rolling resistance 100 .sup. 99.sup.1 107(67" wheel)Twin Roll 100 103 106Wet skid resistance 100 99 100(20 mph)Wet skid resistance 100 98 100(40 mph)Wet skid resistance 100 102 104(60 mph)Treadwear 100 .sup. 105.sup.2 .sup. 110.sup.2______________________________________ .sup.1 a reduction in the Rolling Resistance value is an improvement. .sup.2 an increase in the Treadwear value is an improvement.

The treadwear was evaluated as a measure of reduction in tread depth after about 55,000 kilometers of test on a truck.

In this Example, the rolling resistance was measured by mounting and inflating the tire on a metal rim and allowing it to be turned by a 67 inch diameter dynamometer under about 80 percent of its rated load at a rate equivalent to a vehicular speed of 50 mph and the drag force measured. The test is believed to be somewhat standard.

The skid resistance was a standard test in which the tires are mounted on a weighted, drawn trailer at various speeds and brakes of the trailer applied and skid force (peak and slide) measured.

The treadwear was compared by actually mounting both control and experimental tires on a vehicle and driving it under controlled conditions, with the position of the tires on the vehicle being periodically positionally rotated.

In this Example, the SIBR is prepared by polymerizing styrene, isoprene and 1,3-butadiene in an essentially non-polar aliphatic solvent with an alkyl lithium catalyst, namely, butyl lithium with or without a modifier. Such modifier is usually a polar modifier which has an effect of randomizing or tapering the styrene portion of the rubber depending on the ratio of the lithium to modifier. A recommended weight ratio of lithium to modifier is 2/1 to 6/1, preferably 1.5/1 to 2.5/1 weight ratio.

Representative examples of such solvents are pentane, hexane, heptane, octane, isooctane and cyclohexane, of which hexane is preferred.

Representative examples of alkyl lithium catalysts are methyl lithium, ethyl lithium, propyl lithium, n-butyl lithium, 2-butyl lithium, t-butyl lithium and amyl butyl lithium. The n-butyl lithium is preferred.

The amount of catalyst is dependent upon the molecular weight desired for the polymerization. It is preferred that the temperature of the polymerization is maintained substantially constant throughout the polymerization in the range of about 10.degree. C. to about 120.degree. C., preferably 60.degree. C. to 90.degree. C.

When a polar modifier is used for randomizing or tapering the styrene such as, for example, chelating diamines or polar ether and oxygenated compounds, the amount of polar modifiers used depends largely on the desired Tg glass-transition temperatures. If a high Tg SIBR (-10.degree. C. to -20.degree. C.) is desired, the modifier used can be TMEDA (N,N,N.sup.1,N.sup.1 -tetra ethylene diamine) or diglyme. If no modifier is used, the polymerization temperature can be adjusted to randomize the styrene or taper it. The SIBR randomization without the polar modifier, is conventionally made at polymerization temperature of 90.degree. C. to 150.degree. C. in continuous stirred reactors.

Representative examples of chelating diamines are N,N,N',N'-tetramethylethylenediamine, dipiperdinethane, dimorpholine ethane and bis-dimethylpiperizane.

Representative examples of polar ether compounds are diglyme, monoglyme, tetraglyme and tetrahydrofuran.

Representative examples of oxygenated compounds are 2,3-dimethoxybenzene, tetrahydrofuran, and methylated polyvinyl acetate polymers.

Usually the styrene content tends to control the glass transition temperature. For high Tg (-10.degree. C. to -40.degree. C.) SIBR, the styrene content should be between 30-60 weight percent of the polymer. If a low Tg of the SIBR (-50.degree. C. to -70.degree. C.) is desired the styrene content may vary between 10 to 30 percent.

The resulting SIBR polymer (rubber) can be further characterized by its glass transition temperature based on the 1,2 bound butadiene plus styrene (formed when a modifier is used in the polymerization) in weight percent or 3,4 bound isoprene plus styrene content or both 1,2 bound butadiene and 3,4 bound isoprene plus styrene content.

High Tg SIBR polymer can have a low styrene content with high 3,4 bound isoprene content (from the isoprene component) and 1,2 bound butadiene (from the butadiene component) or high styrene with low 3,4 bound isoprene (in the isoprene component) and 1,2 bound butadiene (in the butadiene component) depending on the desired properties needed to be maximized.

Thus, if a relatively low Tg SIBR is desired, a high styrene content is the primary consideration. If a relatively high Tg SIBR is desired, at a constant or given styrene content, the primary consideration is for a high concentration of the sum of the 1,2-structure of the bound butadiene units plus the 3,4-structure of the bound isoprene units.

Tire treads having a high Tg (-30.degree. C. to -45.degree. C.) SIBR is considered desirable for high traction purpose. A low Tg (-70.degree. C. to -40.degree. C.) SIBR is desirable for tread wear purposes and a balanced property of SIBR of -20.degree. C. to -30.degree. C. is usually good for ice traction.

EXAMPLE II

SIBR was made by polymerizing the styrene, isoprene and 1,3-butadiene monomers with n-butyl lithium catalyst and TMEDA modifier to make a -50.degree. C. Tg and -40.degree. C. Tg and -30.degree. C. Tg and -20.degree. C. Tg rubber terpolymers as illustrated in the following tables and identified as Experiments F through L:

TABLE 5______________________________________ Exp F Exp G Exp H Exp I______________________________________Lithium/ 1/1 1/1.5 1/2 1/2.5Modifier RatioMolecular Weight 250,000 250,000 250,000 250,000(Number Average)Molecular Weight 450,000 450,000 450,000 450,000(Weight Average)Tg (.degree.C.) -50.degree. -40.degree. -30.degree. -20.degree.% Styrene 20 20 20 20% Isoprene 40 40 40 40% Butadiene 40 40 40 40Microstructure% 1,2 structure 30 40 45 50in polybutadiene% 3,4 structure 25 30 35 50in polyisoprene______________________________________

This demonstrates that the microstructure of the polymer (the 1,2 structure in the butadiene portion and/or the 3,4 structure in the isoprene portion) relates to the Tg of the SIBR terpolymer.

TABLE 6______________________________________ Exp J Exp K Exp L______________________________________Lithium/Modifier Ratio 1/1 1/1.5 1/2.5Molecular Weight (Mn) 250,000 250,000 250,000Molecular Weight (Mw) 450,000 450,000 450,000Tg (.degree.C.) -50.degree. -30.degree. -20.degree.% Styrene 30 40 50% Isoprene 35 30 25% Butadiene 35 30 28Microstructure% 1,2 structure 12 12 12in polybutadiene% 3,4 structure 10 10 10in polyisoprene______________________________________

This demonstrates that the styrene content can control the Tg of the SIBR terpolymer.

The glass transition temperature (Tg) can conveniently be determined by method known to those having skill in such art, namely, by differential scanning calorimeter (DSC) at a heating rate of 10.degree. C. per minute. For the SIBR of this invention, basically, single-type Tg's were observed.

While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in this art that various changes and modifications may be made therein without departing from the spirit or scope of the invention.

Claims

1. A pneumatic tire having an outer circumferential tread where said tread is a sulfur cured rubber composition comprised of, based on 100 parts by weight rubber (phr), (A) about 30 to about 70 parts by weight of a styrene, isoprene, butadiene terpolymer rubber (SIBR), and (B) about 70 to about 30 parts by weight of at least one of cis 1,4-polyisoprene rubber and cis 1,4-polybutadiene rubber wherein said SIBR rubber is comprised of (i) about 10 to about 35 weight percent bound styrene, (ii) about 20 to about 60 weight percent bound isoprene, and (iii) about 10 to about 50 weight percent bound butadiene and is characterized by having a single glass transition temperature (Tg) which is in the range of about -70.degree. C. to about -5.degree. C. and, further, the said bound butadiene structure contains about 10 to about 50 weight percent 1,2-vinyl units, the said bound isoprene structure contains about 10 to about 40 weight percent 3,4 units, and the sum of the weight percent 1,2-vinyl units of the bound butadiene and the weight percent 3,4 units of the bound isoprene is in the range of about 20 to about 90 percent.

2. The pneumatic tire of claim 1 wherein said tread rubber consists essentially of said SIBR, cis 1,4-polyisoprene and cis 1,4-polybutadiene.

3. The pneumatic tire of claim 1 wherein said tread rubber consists essentially of said SIBR and cis 1,4-polyisoprene.

4. The tire of claim 2 where said cis 1,4-polyisoprene is natural rubber.

5. The tire of claim 3 where said cis 1,4-polyisoprene is natural rubber.

6. A pneumatic tire having an outer circumferential tread where said tread is a sulfur cured rubber composition comprised of, based on 100 parts by weight rubber (phr), (A) about 30 to about 70 parts by weight of a styrene, isoprene, butadiene terpolymer rubber (SIBR), and (B) about 70 to about 30 parts by weight of at least one of cis 1,4-polyisoprene rubber and cis 1,4-polybutadiene rubber wherein said SIBR rubber is comprised of (i) about 10 to about 30 weight percent bound styrene, (ii) about 20 to about 60 weight percent bound isoprene, and (iii) about 10 to about 50 weight percent bound butadiene and is characterized by having a single glass transition temperature (Tg) which is in the range of about -10.degree. C. to about -40.degree. C. and, further, the said bound butadiene structure contains about 10 to about 50 weight percent 1,2-vinyl units, the said bound isoprene structure contains about 10 to about 40 weight percent 3,4 units, and the sum of the weight percent 1,2-vinyl units of the bound butadiene and the weight percent 3,4 units of the bound isoprene is in the range of about 40 to about 70 percent.

7. The tire of claim 6 where said tread rubber consists essentially of said SIBR, cis 1,4-polyisoprene and cis 1,4-polybutadiene.

8. The tire of claim 7 where said cis 1,4-polyisoprene is natural rubber.

9. The tire of claim 6 where said tread rubber consists essentially of said SIBR and cis 1,4-polyisoprene.

10. The tire of claim 9 where said cis 1,4-polyisoprene is natural rubber.