The present invention relates to a tire and, in particular, a tire having improved durability of a bead portion.
A product life of a tire before being disposed as waste has been significantly prolonged in recent years due to improvement in wear resistance of tread, and the like. In order to adapt to such a prolonged product life of a tire as described above, the conventional tires have taken measures for addressing troubles such as separation at a bead portion of a tire on the widthwise-outer side of a carcass turn-up portion thereof, separation in a portion covering a carcass main body, of a wire chafer, at the outermost end in the tire radial direction thereof, and the like. However, it has turned out that the aforementioned conventional tires still experience a problem that troubles of a bead portion occur at the outermost end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, at the later stage of a tire product life.
In view of the problem described above, there has been a demand for a tire of which durability of a bead portion is improved by suppressing troubles of the bead portion occurring at the outermost end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, while maintaining durability against separation at the bead portion of the tire on the widthwise-outer side of a carcass turn-up portion thereof and separation in a portion covering the carcass main body, of a wire chafer, at the outermost end in the tire radial direction thereof. In order to meet such a demand as described above, JP 2002-219912 and JP 2008-143291 disclose techniques for improving durability against separation on the outer side of a carcass turn-up portion of a tire and durability against separation in a portion covering a carcass main body, of a wire chafer, at the outermost end in the tire radial direction thereof. However, neither JP 2002-219912 nor JP 2008-143291 can offer sufficient durability at the outermost end in the tire radial direction of a portion covering a carcass main body, of a textile chafer.
In view of the facts above, an object of the present invention is to provide a tire having improved durability of a bead portion.
The inventors of the present invention have discovered, as a result of a keen study of the mechanism of troubles of a bead portion initiated at the outermost end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, that i) in a case where an expansion rate of a textile chafer is relatively large, the textile chafer shrinks during the tire vulcanization process and a crease is generated in an inner liner layer from the outermost end in the tire radial direction of a portion covering a carcass main body, of the textile chafer, due to the shrinkage of the textile chafer; ii) then cracks are generated from the crease as the starting point and coating rubber of a carcass ply deteriorates due to oxygen transmitted through the cracks; and iii) the coating rubber is exfoliated along ply cords of the carcass at the later stage of the product life of the tire, causing troubles of a bead portion. In other words, it has been revealed that such troubles of a bead portion as described above can be prevented from occurring by suppressing an expansion rate of a textile chafer of a tire during the production process. As a result of a further study in view of these discoveries to achieve the aforementioned object, the inventors of the present invention have further discovered that it is possible to provide a tire having enhanced durability of a bead portion and a prolonged product life by suppressing an expansion rate of a textile chafer during the production process of the tire and producing the tire such that, providing that the center of a flange curvature (having a radius r) of a rim is P and the outer most end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, is A, an angle formed by a line passing P and in parallel with the tire rotation axis, with respect to a line linking P and A, is in a predetermined range under predetermined conditions, thereby completing the present invention.
Specifically, the main structure of the present invention is as follows. (1) A tire having: at least one layer of carcass, including a carcass main body extending in a toroidal shape across a pair of bead cores and a carcass turn-up portion wound around each bead core from the inner side toward the outer side in the tire widthwise direction and extending in the tire radial direction; at least two layers of textile chafer extending from the carcass main body toward the carcass turn-up portion so as to cover the carcass; and at least one layer of wire chafer, characterized in that: in a state where the tire is assembled with a “design rim” prescribed in TRA (The Tire and Rim Association, Inc.,) and inflated at an inner pressure of 50 kPa and providing that the center of a flange curvature of a rim is P and the outer most end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, is A, an angle θ formed by a line passing P and in parallel with the tire rotation axis, with respect to a line linking P and A, is in a range of 20°≦θ≦60°.
(2) The tire of (1) above, wherein cords of one layer of the textile chafer extend in a direction intersecting cords of another layer of the textile chafer, and an angle α formed by a cord with respect to a line tangent to a circle coaxial with the outer periphery of the tire at a point on the cord (the circle crosses the cord at the point) is in the range of 20°≦α≦70°.
(3) The tire of (1) or (2) above, wherein, providing that: the angle θ is in the range of 20°≦θ≦30°; tire section height is SH, rim radius is R, rim flange height of the design rim is Hf; position at the tire outer-side surface, where the distance between said position and the tire rotation shaft in the tire radial direction is (R+1.18×Hf), is P1 and position at the tire outer-side surface, where the distance between said position and the tire rotation shaft in the tire radial direction is (R+0.81×Hf), is P2; crossing-point of a first line drawn from P1 to be normal to the carcass main body, with the carcass turn-up portion, is T1 and crossing-point of a second line drawn from P2 to be normal to the carcass main body, with the carcass turn-up portion, is T2; crossing-point of the first line with the carcass main body is M1 and crossing-point of the second line with the carcass main body is M2; and distance between P1 and T1 is W1pt, distance between T1 and M1 is W1tm, distance between P2 and M2 is W2pt, distance between T2 and M2 is W2tm, the parameters satisfy formulae (I) to (IV).
0.053×SH<W1pt<0.068×SH (I)
0.017×SH<W1tm<0.032×SH (II)
0.028×SH<W2tm<0.043×SH (III)
0.010×SH<W1pt−W2pt<0.030×SH (IV)
(4) A method of producing the tire of any one of (1) to (3) above, characterized in that: providing that circumference of a circle having: as radius the distance in the tire radial direction between the radial-direction outermost end of a portion covering the carcass main body, of the textile chafer, and the tire axis S; and as the center thereof the intersection of a line drawn from said outermost end to be normal to the tire axis, with the tire axis, after a tire-molding process, is L, and circumference of a circle having: as radius the distance in the tire radial direction between the radial-direction outermost end of a portion covering the carcass main body, of the textile chafer, and the tire axis S; and as the center thereof the intersection of a line drawn from said outermost end to be normal to the tire axis, with the tire axis, after a tire-vulcanization process, is M, an expansion rate of the textile chafer in a period from the tire-molding process to a finishing stage (M/L×100) is in the range of 100 to110%.
According to the present invention, providing that the center of a flange curvature (having a radius r) of a rim is P and the outer most end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, is A, by setting an angle θ formed by a line passing P and in parallel with the tire rotation axis, with respect to a line linking P and A, in a range of 20°≦θ≦60°, troubles of a bead portion at the outermost end in the tire radial direction of the portion covering the carcass main body, of the textile chafer, is suppressed and a tire having enhanced durability of a bead portion and a prolonged product life can be provided without adding any new member in the bead portion.
The present invention will be described in detail with reference to drawings hereinafter.
In the one example of a tire according to the present invention shown in
It is essentially important that the tire of the present invention is designed such that, in a state where the tire is assembled with a “design rim” prescribed in TRA (The Tire and Rim Association, Inc.,) and inflated at an inner pressure of 50 kPa, and providing that the center of a flange curvature (having a radius r) of the rim is P and the outer most end in the tire radial direction of a portion covering the carcass main body, of the textile chafer, is A, an angle θ formed by a line passing P and in parallel with the tire rotation axis, with respect to a line linking P and A, is set in a range of 20°≦θ≦60°, as shown in
In the present embodiment, the lower positions of the textile chafer 4 and the wire chafer 5 extending toward the carcass turn-up portion are not particularly restricted. Further, the number of layers of the textile chafer is not particularly restricted, either, as long as the textile chafer is constituted of at least two layers.
In the present embodiment, the center P of the flange curvature of the rim represents the center of curvature at the rear end portion of the flange of the rim.
The textile chafer 4 is constituted of parallel-disposed fiber cords and rubber coated thereon. The wire chafer 5 is constituted of parallel-disposed steel cords and rubber coated thereon. The tire of the present invention is preferably designed such that cords of one layer of the textile chafer extend in a direction intersecting cords of another layer of the textile chafer and an angle α formed by a cord Tc with respect to a line Ts tangent to a circle coaxial with the outer periphery of the tire at a point D on the cord (the circle crosses the cord at the point D) is in the range of 20°≦α≦70°, as shown in
In a case where the angle θ is in the range of 20°≦θ≦60°, an expansion rate of the textile chafer in a period from the tire-molding process to the finishing stage (M/L×100) is generally suppressed to 110% or lower, whereby a crease will be hardly generated. However, depending on production conditions, there may be generated slight difference in the expansion rate if the same angle θ is applied. In view of this, in order to reliably prevent troubles from occurring in the bead portion, the method of producing a tire according to the present invention preferably includes setting, providing that circumference of a circle having: as radius the distance in the tire radial direction between the radial-direction outermost end A0 of the textile chafer and the tire axis S; and as the center thereof the intersection of a line drawn from said outermost end A0 to be normal to the tire axis S, with the tire axis S, after a tire-molding process, is L, and circumference of a circle having: as radius the distance in the tire radial direction between the radial-direction outermost end A of the textile chafer and the tire axis S; and as the center thereof the intersection of a line drawn from said outermost end A to be normal to the tire axis S, with the tire axis S, after a tire-vulcanization process, is M, an expansion rate of circumference of the textile chafer in a period from the tire-molding process to the post-vulcanization (a finished state) (M/L×100) in the range of 100 to 110%, as shown in
In the tire of the present invention, a method of setting an expansion rate of the textile chafer within the aforementioned range is not particularly restricted and examples thereof include selecting for use an appropriate member for the textile chafer.
Further, the tire of the present invention is preferably designed such that, providing that: tire section height is SH, rim radius is R, rim flange height of the design rim is Hf; position at the tire outer-side surface, where the distance between said position and the tire rotation shaft in the tire radial direction is (R+1.18×Hf), is P1 and position at the tire outer-side surface, where the distance between said position and the tire rotation shaft in the tire radial direction is (R+0.81×Hf), is P2; crossing-point of a first line drawn from P1 to be normal to the carcass main body, with the carcass turn-up portion, is T1 and crossing-point of a second line drawn from P2 to be normal to the carcass main body, with the carcass turn-up portion, is T2; crossing-point of the first line with the carcass main body is M1 and crossing-point of the second line with the carcass main body is M2; and distance between P1 and T1 is W1pt, distance between T1 and M1 is W1tm, distance between P2 and M2 is W2pt, distance between T2 and M2 is W2tm, the parameters satisfy the aforementioned formulae (I) to (IV), as shown in
The tire of the present invention preferably satisfies the aforementioned formula (I) because then durability on the outer side in the tire widthwise direction of the carcass turn-up potion 3 in the vicinity of T1 can be enhanced without increasing the temperature in the vicinity of T1, as compared with the conventional tires. Further, the tire of the present invention preferably satisfies the aforementioned formula (II) because then durability of a rubber layer between the carcass main body and the carcass turn-up portion can be set at the same level as or higher than that of the conventional tires and durability on the outer side in the tire widthwise direction of the carcass turn-up potion 3 in the vicinity of T1 can be enhanced. Yet further, the tire of the present invention preferably satisfies the aforementioned formula (III) because then durability of the tire against fracture of carcass cords and durability on the outer side in the tire widthwise direction of the carcass turn-up potion 3 in the vicinity of T1 can be both enhanced. Yet further, the tire of the present invention preferably satisfies the aforementioned formula (IV) because there can be obtained a case line of a bead portion, which case line allows the carcass main body 2 and the carcass turn-up potion 3 to be produced without being affected by decrease in W2tm.
Accordingly, in the tire of the present invention, it is possible to simultaneously improve three durability values, i.e. durability on the outer side in the tire widthwise direction of the carcass turn-up potion 3 in the vicinity of T1, durability of a rubber layer between the carcass main body and the carcass turn-up portion, and durability against fracture of carcass cords, by satisfying the aforementioned formulae (I) to (IV). That is, all of the three durability values described above can be improved only by modifying a configuration of a carcass line in the vicinity of the bead portion 6, without adding a new member which does not exist in the conventional tires.
The tire of the present invention is not particularly restricted, except that the tire having: at least one layer of carcass, including a carcass main body extending in a toroidal shape across a pair of bead cores and a carcass turn-up portion continuous with the carcass main body and wound around each bead core from the inner side toward the outer side in the tire widthwise direction to extend in the tire radial direction; at least two layers of textile chafer disposed on the tire-radial direction inner surface of the carcass with respect to the bead core; and at least one layer of wire chafer, is characterized in that: in a state where the tire is assembled with a “design rim” prescribed in TRA and inflated at an inner pressure of 50 kPa and, providing that the center of a flange curvature of the rim is P and the outer most end in the tire radial direction of a portion covering the carcass main body, of the textile chafer, is A, an angle θ formed by a line passing P and in parallel with the tire rotation axis, with respect to a line linking P and A, is in a range of 20°≦θ≦60°. The tire of the present invention can be produced by the known method based on the known tire structure. The tire of the present invention may be either a solid tire or a pneumatic tire. In a case where the tire of the present invention is a pneumatic tire, examples of gas with which the tire is to be filled include ambient air, air having adjusted oxygen partial pressure, and inert gas such as nitrogen, argon, helium, and the like.
The tire of the present invention can be preferably used as a pneumatic radial tire for heavy load which is relatively susceptible to troubles in a bead portion, and in particular, as a pneumatic radial tire for a construction vehicle.
Hereinafter, the present invention will be described further in detail by Examples below. The present invention is not limited to these Examples and may be appropriately changed within the sprit thereof.
A test tire for a construction vehicle having size: 46/90R57 was produced according to the specifications shown in Table 1. Frequency of crease generation in the inner liner layer at the outermost end in the tire radial direction of a portion covering a carcass main body, of a textile chafer, was measured for the tire for a construction vehicle according to the method described below. The results are shown in Table 1.
The inner surface of a tire is visually inspected. In a case where the tire exhibits a crease of which depth exceeds 1 mm, it is judged that a crease has been “generated” in the tire, while in a case where the tire is free of a crease of which depth exceeds 1 mm, it is judged that a crease has “not been generated” in the tire. Frequency of crease generation is calculated based on these evaluation results.
It is understood from Table 1 that crease is not generated when the angle θ is not larger than 60° and the expansion rate is not larger than 110%.
Further, a test tire for a construction vehicle having size: 46/90R57 was produced according to the specifications shown in Table 2. The tire was assembled with a design rim (TRA), inflated at the standard inner pressure (TRA), and subjected to a durability test by using a drum having diameter of 5 m under a load which is 170% of the standard load (TRA) to measure a running time before occurrence of separation on the outer side in the tire widthwise direction of the carcass turn-up portion of the tire. The results are shown in Table 2.
It is understood from Table 2 that, in the examples sharing the same case line of a bead portion (i.e. Examples 2, 3 and 6 and Comp. Example 2), separation is likely to occur on the widthwise-outer side of the carcass turn-up portion when the angle θ is not larger than 30° and the situation further deteriorates when the angle θ is 10°.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-270718 | Oct 2008 | JP | national |
The present application is a divisional of U.S. application Ser. No. 13/125,150 filed Apr. 20, 2011, which is a National Stage of International Application No. PCT/JP2009/065420 filed Sep. 3, 2009, which claims priority from Japanese Patent Application No. 2008-270718 filed Oct. 21, 2008, the contents of all of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13125150 | Apr 2011 | US |
| Child | 14163244 | US |