Tissue dust reduction

Information

  • Patent Grant
  • 10648133
  • Patent Number
    10,648,133
  • Date Filed
    Monday, May 15, 2017
    7 years ago
  • Date Issued
    Tuesday, May 12, 2020
    4 years ago
Abstract
Methods of reducing paper dusting in a papermaking process, and a low dusting tissue having increased strength are provided. Application of a polymer comprising at least one amine-containing vinylic or allylic monomer to at least one surface of a paper web during the papermaking process reduces the dusting tendency of the paper, and increases both the wet and dry strength of the paper product.
Description
FIELD OF INVENTION

The invention relates to compositions and methods for reducing excessive dusting during the manufacture of paper products.


BACKGROUND OF THE INVENTION

Papermaking involves the preparation of a paper product from an aqueous suspension of cellulosic fibers by forming a mat of interwoven fibers and removal of water from the mat by various dewatering methods including free drainage, vacuum, pressing, and evaporative drying. A problem that is observed during the papermaking process and for the finished paper is the tendency for paper to release fiber and filler particles from the paper surface, leading to the formation of lint and dust. Excessive dusting can pose problems during the manufacture of tissue products, and can result in runnability and quality issues on papermaking machines. Moreover, dust and lint accumulation can create a fire hazard. In papermaking, there is also the potential for workers to be exposed to paper dust. Regular exposure to high levels of dust can affect the respiratory system and cause illness.


Tissue paper is a lightweight paper that can be used to prepare absorbent products such as bath tissue, facial tissue, and absorbent towels. Tissue paper is generally prepared by forming a wet web of wood pulp and transferring the web to a heated cylinder called a Yankee dryer to reduce the moisture content. The tissue paper is subjected to a creping process where the paper is scraped off of the Yankee Dryer by contacting a blade against the dryer. Creping makes the tissue sheets flexible, soft, and absorbent. Ideally, the resulting tissue should have high softness, while also having sufficient strength and resistance to dusting.


The creping process typically suffers from dusting issues, which occurs during contact of the creping blade with the tissue sheet. Loose dust particles are generated when mechanical force is applied to tissue paper, and is more pronounced in processes where tissue sheets are weak or loosely bonded. As generally observed in papermaking processes, the surface and fine fibers of the tissue are dispersed into air and settles on papermaking equipment. High dusting and linting tissue can create a nuisance for consumers with regard to cleanliness of the tissue/towel dispenser and surrounding areas.


A number of methods are used to reduce linting and dusting. Air jets as well as vacuum systems positioned near the papermaking process have been used to remove lint and dust released from the paper substrate, but these methods are generally energy inefficient and do not address dust generated by handling of the finished paper products.


Tissue dusting and linting remain a significant problem in the field and there continues to be a need for new strategies for dust reduction in tissue making.


BRIEF SUMMARY OF THE INVENTION

In an embodiment, the invention provides a method for reducing dust in a tissue making process. The method comprises applying a polymer comprising at least one amine-containing vinylic or allylic monomer to the surface of a tissue web. In certain preferred embodiments, the polymer is applied to the surface of the tissue web prior to drying the tissue web.


In another embodiment, the invention provides a low dust tissue product. The tissue product comprises cellulosic fibers and a polymer comprising at least one amine-containing vinylic or allylic monomer. The polymer is disposed on at least one surface of the tissue product.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a line graph that illustrates the amount of dust collected at the creping blade of a tissue making process when a diallylamine/acrylamide copolymer is applied to a tissue web.



FIG. 2 is a line graph that illustrates the amount of dust collected at the creping blade of a tissue making process when a diallylamine/acrylamide copolymer is applied to a tissue web.



FIG. 3 is a line graph that illustrates the wet strength additive dosage in a tissue papermaking process when a diallylamine/acrylamide copolymer is applied to a tissue web.



FIG. 4 is a line graph that illustrates the wet and dry tensile strengths of a tissue sheet in a tissue making process when a diallylamine/acrylamide copolymer is applied to a tissue web.





DETAILED DESCRIPTION OF THE INVENTION

The following definitions are provided to determine how terms used in this application, and in particular, how the claims are to be construed. The organization of the definitions is for convenience only and is not intended to limit any of the definitions to any particular category.


“Acrylamide monomer” means a monomer of formula




embedded image



wherein R1 is selected from the group consisting of H, C1-C16 alkyl, aryl, arylalkyl, C2-C16 alkenyl, C2-C16 alkynyl, heteroaryl, alkylheteroaryl, C3-C8 cycloalkyl, and halogen; and R2 is selected from the group consisting of hydrogen, C1-C16 alkyl, aryl, arylalkyl, C2-C16 alkenyl, C2-C16 alkynyl, heteroaryl, alkylheteroaryl, and hydroxyl;


“Aldehyde-functionalized polymer” refers to a polymer that results from a reaction between a polymer comprising at least one amide and/or amino group with an aldehyde. An “aldehyde” means a compound containing one or more aldehyde (—CHO) groups, where the aldehyde groups are capable of reacting with the amine group(s) of a polymer comprising an amine group as described herein. Representative aldehydes include formaldehyde, paraformaldehyde, glutaraldehyde, glyoxal, and the like;


“Amine-containing vinylic or allylic monomer” refers to compounds comprising both a nitrogen atom and a vinyl, allyl, or acrylic group. The amine-containing vinylic or allylic monomer generally comprises a primary or secondary amine. Nonlimiting examples include acrylamide compounds and diallylamine compounds;


“Paper” refers to sheet-like masses and molded products made from cellulosic materials which may be derived from natural sources as well as from synthetics. In addition, papers made from combinations of cellulosic and synthetic materials are applicable herein;


“Papermaking process” means a method of making paper and paperboard products from pulp comprising forming an aqueous cellulosic papermaking furnish (optionally, with mineral fillers, such as calcium carbonates, clays, etc.), draining the furnish to form a sheet, and drying the sheet. It should be appreciated that any suitable furnish may be used. Representative furnishes include, for example, virgin pulp, recycled pulp, kraft pulp (bleached and unbleached), sulfite pulp, mechanical pulp, polymeric plastic fibers, and the like, or any combination of the foregoing pulps. The steps of forming the papermaking furnish, draining and drying may be carried out in any manner generally known to those skilled in the art. In addition, other papermaking additives may be utilized in addition to the polymer treatment of this invention. Such papermaking additives include, for example, retention aids (e.g., microparticles, flocculants, polymeric and inorganic coagulants, etc.), wet and dry strength additives (e.g., cationic starches, polyamidoamine epichlorohydrin-based polymers), the like, and combinations thereof;


“Runnability” means the manner in which a sheet of paper or paper material passes trouble free through the stages and equipment in a papermaking process, as well as any subsequent converting processes such as folding, slitting, cutting, and plying. Complications which interrupt “runnability” include but are not limited to sheet breaks, jamming, clogging, fouling equipment, damaging equipment, and/or requiring more energy to pass the sheet of paper or paper precursor through the equipment;


“Surface strength” means the tendency of a paper substrate to resist damage due to abrasive force;


“Tissue paper” or “tissue product” refers to lightweight paper or an article comprising lightweight paper made using a papermaking process. Non-limiting examples of tissue paper or tissue product include toilet paper, paper towels, napkins, and facial tissues;


“Wet strength” means the tendency of a paper substrate to resist damage due to force(s) when rewet;


“Wet web consistency” refers to the percentage of dry fibers, by weight, in a paper web.


The invention provides methods for improving the dusting and strength properties of a paper product. The present invention is also directed to paper products having improved dusting and strength properties. The methods of the present invention include the application of a polymeric additive to the surface of the paper web during manufacture to produce paper that exhibits low dusting and increased strength. The polymeric additive comprises at least one amine-containing vinylic or allylic monomer. Applicants have surprisingly and unexpectedly discovered that when a polymer comprising an amine-containing vinylic or allylic monomer is applied to a paper web, the resulting paper product exhibits low dusting properties and has increased strength. Preferably, the polymeric additive is applied to at least one surface of the web, and in some embodiments, it is applied to both surfaces of the paper or tissue web. In particular, Applicants have discovered that paper products produced by the present methods exhibit lower lint and dust production when under mechanical stress and have greater wet and dry tensile strength than paper produced in the absence of a polymer comprising an amine-containing vinylic or allylic monomer. The present methods are useful for the manufacture of tissue products because tissue is quite susceptible to dusting and linting issues.


The methods of the present invention employ polymers comprising at least one amine-containing vinylic or allylic monomer, and have been found to improve the properties of a tissue web, and the resulting product. It has also been found that the polymeric additive improves the operation of a papermaking machine in some embodiments. In particular, the methods of the present invention produce tissue products that have a reduced tendency to produce dust. The methods of the present invention also reduce the amount of dust that accumulates on papermaking machinery. For example, a tissue making process employing the present methods has a reduced amount of dust accumulation at equipment such as the creping blade and the Yankee dryer.


Applicants have discovered that application of a polymer comprising at least one amine-containing vinylic or allylic monomer to a tissue web imparts beneficial properties to the resulting tissue sheet. Applicants have surprisingly and unexpectedly discovered that methods of the present invention can actually lead to an increase in tissue strength (e.g., wet and dry tensile strength). As a result, the present invention allows for the use of a lower amount of wet strength additive in the manufacture of tissue products. Without wishing to be bound by any particular theory, it is believed that application of a polymer comprising at least one amine-containing vinylic or allylic monomer to the surface of a tissue web reduces dusting by increasing the surface strength of the tissue.


In an embodiment, the invention provides a method for reducing dust in a tissue making process. The method comprises applying a polymer comprising at least one amine-containing vinylic or allylic monomer to the surface of a tissue web. In certain preferred embodiments, the polymer is applied to the surface of the tissue web prior to drying the tissue web.


The methods of the present invention comprise applying a polymer comprising at least one amine-containing vinylic or allylic monomer to a tissue web. The polymer is applied after formation of the tissue web. The methods of the present invention are in contrast to existing methods which incorporate low dusting additives into paper by adding the additive to paper stock, prior to web formation. For the present invention, the web is formed by depositing or spraying a suspension of papermaking fibers (e.g., aqueous suspension) onto a forming fabric or felt and the polymer is applied to the tissue web. The steps of forming the tissue making furnish (e.g., draining and drying) may be carried out in any manner generally known to those skilled in the art.


A polymer comprising at least one amine-containing vinylic or allylic monomer is applied to the surface of the tissue web using any suitable delivery method. In certain preferred embodiments, the polymer is sprayed onto the surface of the tissue web. In certain embodiments, the polymer is sprayed onto the surface of the tissue web using a spray boom. When a spray boom is used, a spray nozzle or multiple spray nozzles are used to spray the polymer onto the surface of the tissue web. In certain preferred embodiments, the polymer is fed through the spray boom at a rate of about 0.01 to about 0.5 gallons per minute. The polymer is disposed on the tissue web in any amount necessary to impart desired strength and dusting properties. The polymer can be applied to a portion of, or over the entire surface of, the tissue web.


The polymers of the present inventive methods are applied to the paper tissue in any form, including as a water-in-oil emulsion, dry powder, dispersion, or aqueous solution. In certain preferred embodiments, the polymer is applied to the surface of the tissue web as an aqueous solution. In certain preferred embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is sprayed onto the surface of a tissue web. In certain preferred embodiments, an aqueous solution of a polymer comprising at least one amine-containing vinylic or allylic monomer is sprayed onto the surface of a tissue web. In certain embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is dissolved in a water-soluble solvent and sprayed onto the surface of a tissue web.


The amount of polymer added to the paper web is not limited. In certain embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is added to the tissue web in from about 0.05 kg to about 5 kg of dry polymer per ton of dry fiber. Thus, in certain embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is added to the tissue web in from about 0.05 kg to about 5 kg of polymer per ton of dry fiber, from about 0.05 kg to about 4 kg of dry polymer per ton of dry fiber, from about 0.05 kg to about 3 kg of dry polymer per ton of dry fiber, from about 0.05 kg to about 2 kg of dry polymer per ton of dry fiber, from about 0.05 kg to about 1 kg of dry polymer per ton of dry fiber, from about 0.5 kg to about 5 kg of dry polymer per ton of dry fiber, or from about 1 kg to about 5 kg of dry polymer per ton of dry fiber. In certain preferred embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is added to the tissue web in from about 0.05 kg to about 3 kg of dry polymer per ton of dry fiber.


The polymer can be applied to the surface of the tissue web as a solution having any suitable concentration. In certain embodiments, the polymer is applied to the tissue web as a solution having a concentration of polymer of from about 0.01% to about 10% by weight based on weight of the solution. In certain embodiments, the polymer is applied to the tissue web as a solution having a concentration of polymer of from about 0.01% to about 5% by weight based on weight of the solution.


In certain embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is applied to a tissue web having a wet web consistency of from about 5% to about 90%. Thus, in certain embodiments, the polymer comprising at least one amine-containing vinylic or allylic monomer is applied to a tissue web having a wet web consistency of from about 5% to about 90%, from about 5% to about 80%, from about 5% to about 70%, from about 5% to about 60%, from about 5% to about 50%, from about 5% to about 40%, from about 5% to about 30%, from about 5% to about 20%, from about 10% to about 90%, from about 20% to about 90%, from about 30% to about 90%, from about 30% to about 80%, from about 30% to about 70%, from about 30% to about 60%, from about 30% to about 50%, from about 40% to about 90%, from about 40% to about 80%, or from about 40% to about 70%. In certain preferred embodiments, the polymer comprising at least one amine-containing vinylic or allylic monomer is applied to a tissue web having a wet web consistency of from about 5% to about 40%.


A polymer comprising an amine-containing vinylic or allylic monomer is applied to the surface of a tissue web. In certain preferred embodiments, the tissue sheet is creped, e.g., produced on a papermaking machine where a partially dried tissue web is adhered to and dried on a cylinder dryer (e.g., Yankee dryer) and removed by the action of a blade (e.g., creping blade). In certain preferred embodiments, the tissue web is treated with the polymer prior to heating with the drying cylinder (e.g., Yankee dryer) and prior to contact with the blade (e.g., creping blade). For example, the polymer can be applied at, e.g., felts, transfer fabrics, TAD fabrics, belts, and textured belts. In certain preferred embodiments, the tissue web is at least partially dried using a Yankee dryer after the polymer is applied to the tissue web.


Treatment of the tissue web with the polymer prior to contact with the creping blade reduces the amount of dusting that occurs during creping. In certain embodiments, a tissue web that has been surface treated with a polymer comprising at least one amine-containing vinylic or allylic monomer produces less dust at the creping blade as compared to tissue prepared in the absence of such surface treatment.


In certain embodiments, the composition and method of the present invention can be applied to tissue that is uncreped. In certain embodiments, uncreped webs may offer some advantages in surface smoothness as compared to creped paper webs.


The methods of the present invention provide tissue paper having increased strength. In certain embodiments, a method comprising applying a polymer comprising at least one amine-containing vinylic or allylic monomer to at least one surface of a tissue web produces tissue paper having greater wet and dry strength. In certain embodiments, applying a polymer comprising at least one amine-containing vinylic or allylic monomer to the surface of a tissue web provides tissue paper having greater wet strength (e.g., wet tensile) than paper produced in the absence of such surface treatment. In certain embodiments, applying a polymer comprising at least one amine-containing vinylic or allylic monomer to at least one surface of a tissue web provides tissue paper having greater dry strength (e.g., dry tensile) than paper produced in the absence of such surface treatment.


The amine-containing vinylic or allylic monomer is not limited, and can be non-ionic, cationic, anionic, and zwitterionic. In certain embodiments, the polymer used in the present inventive methods is a copolymer. In certain embodiments, the polymer used in the present inventive methods can comprise two or more monomeric species.


Representative non-ionic monomers include acrylamide, methacrylamide, N,N-dimethylacrylamide, N,N-diethylacrylamide, N-isopropylacrylamide, N-vinylformamide, N-vinylmethylacetamide, N-vinyl pyrrolidone, hydroxyethyl methacrylate, hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, N-t-butylacrylamide, N-methylolacrylamide, vinyl acetate, vinyl alcohol, similar monomers, and combinations thereof.


Representative anionic monomers include acrylic acid and its salts, including, but not limited to sodium acrylate and ammonium acrylate; methacrylic acid and its salts, including, but not limited to sodium methacrylate and ammonium methacrylate; 2-acrylamido-2-methylpropanesulfonic acid (“AMPS”); the sodium salt of AMPS; sodium vinyl sulfonate; styrene sulfonate; maleic acid and its salts, including, but not limited to the sodium salt, the ammonium salt, sulfonate, itaconate, sulfopropyl acrylate or methacrylate or other water-soluble forms of these or other polymerizable carboxylic or sulfonic acids; sulfomethylated acrylamide; allyl sulfonate; sodium vinyl sulfonate; itaconic acid; acrylamidomethylbutanoic acid; fumaric acid; vinylphosphonic acid; vinylsulfonic acid; allylphosphonic acid; sulfomethylated acrylamide; phosphonomethylated acrylamide; itaconic anhydride; similar monomers, and combinations thereof.


Representative cationic monomers or mer units of the primary or secondary amine include dialkylaminoalkyl acrylates and methacrylates and their quaternary or acid salts, including, but not limited to, dimethylaminoethyl acrylate methyl chloride quaternary salt (“DMAEA⋅MCQ”), dimethylaminoethyl acrylate methyl sulfate quaternary salt, dimethyaminoethyl acrylate benzyl chloride quaternary salt, dimethylaminoethyl acrylate sulfuric acid salt, dimethylaminoethyl acrylate hydrochloric acid salt, dimethylaminoethyl methacrylate methyl chloride quaternary salt, dimethylaminoethyl methacrylate methyl sulfate quaternary salt, dimethylaminoethyl methacrylate benzyl chloride quaternary salt, dimethylaminoethyl methacrylate sulfuric acid salt, dimethylaminoethyl methacrylate hydrochloric acid salt, dialkylaminoalkylacrylamides or methacrylamides and their quaternary or acid salts such as acrylamidopropyltrimethylammonium chloride, dimethylaminopropyl acrylamide methyl sulfate quaternary salt, dimethylaminopropyl acrylamide sulfuric acid salt, dimethylaminopropyl acrylamide hydrochloric acid salt, methacrylamidopropyltrimethylammonium chloride, dimethylaminopropyl methacrylamide methyl sulfate quaternary salt, dimethylaminopropyl methacrylamide sulfuric acid salt, dimethylaminopropyl methacrylamide hydrochloric acid salt, diethylaminoethylacrylate, diethylaminoethylmethacrylate, diallyldiethylammonium chloride and diallyldimethyl ammonium chloride (“DADMAC”), similar monomers, and combinations thereof.


Representative zwitterionic monomers include N,N-dimethyl-N-acryloyloxyethyl-N-(3-sulfopropyl)-ammonium betaine; N,N-dimethyl-N-acrylamidopropyl-N-(2-carboxymethyl)-ammonium betaine; N,N-dimethyl-N-acrylamidopropyl-N-(3-sulfopropyl)-ammonium betaine; N,N-dimethyl-N-acrylamidopropyl-N-(2-carboxymethyl)-ammonium betaine; 2-(methylthio)ethyl methacryloyl-S-(sulfopropyl)-sulfonium betaine; 2-[(2-acryloylethyl)dimethylammonio]ethyl 2-methyl phosphate; 2-(acryloyloxyethyl)-2′-(trimethylammonium)ethyl phosphate; [(2-acryloylethyl)dimethylammonio]methyl phosphonic acid; 2-methacryloyloxyethyl phosphorylcholine (“MPC”); 2-[(3-acrylamidopropyl)dimethylammonio]ethyl 2′-isopropyl phosphate (“AAPI”); 1-vinyl-3-(3-sulfopropyl)imidazolium hydroxide; (2-acryloxyethyl) carboxymethyl methylsulfonium chloride; 1-(3-sulfopropyl)-2-vinylpyridinium betaine; N-(4-sulfobutyl)-N-methyl-N, N-diallylamine ammonium betaine (“MDABS”); N,N-diallyl-N-methyl-N-(2-sulfoethyl) ammonium betaine; similar monomers, and combinations thereof.


In certain preferred embodiments, the polymer comprises an acrylamide monomer. In certain preferred embodiments, the acrylamide monomer is acrylamide, methacrylamide, N,N-dimethylacrylamide, N,N-diethylacrylamide, N-isopropylacrylamide, N-vinylformamide, N-vinylmethylacetamide, N-vinyl pyrrolidone, N-t-butylacrylamide, N-methylolacrylamide, and combinations thereof. In certain preferred embodiments, the acrylamide monomer is acrylamide.


It should be understood that a polymer in accordance with the present method may include at least one amine-containing vinylic or allylic monomer. In certain preferred embodiments, the polymer is a copolymer formed from a diallylamine monomer and an acrylamide monomer. In certain embodiments, the polymer may consist of diallylamine monomer and acrylamide monomer.


In certain embodiments, the polymer of the present inventive method is a copolymer. In certain preferred embodiments, the polymer is a diallylamine acrylamide copolymer. In certain embodiments, the copolymer comprises at least one diallylamine monomer and at least one acrylamide monomer. In certain preferred embodiments, the polymer comprises diallylamine monomer in an amount of from about 0.01 mol % to about 20 mol %. Thus, in certain embodiments, the polymer comprises diallylamine monomer in an amount of from about 0.01 mol % to about 20 mol %, from about 0.01 mol % to about 15 mol %, from about 0.01 mol % to about 10 mol %, or from about 0.01 mol % to about 5 mol %. In certain preferred embodiments, the polymer comprises acrylamide monomer in an amount of from about 0.01 mol % to about 85 mol %. Thus, in certain embodiments, the polymer comprises acrylamide monomer in an amount of from about 0.01 mol % to about 85 mol %, from about 0.01 mol % to about 80 mol %, from about 0.01 mol % to about 70 mol %, from about 0.01 mol % to about 60 mol %, from about 0.01 mol % to about 50 mol %, or from about 0.01 mol % to about 40 mol %. In certain embodiments, the polymer is a diallylamine acrylamide copolymer comprising from about 1 mol % to about 99 mol % diallylamine monomer. In certain embodiments, the diallylamine acrylamide copolymer comprises diallylamine monomers in an amount greater than acrylamide monomers (e.g., about 60 mol % to about 100 mol % diallylamine monomers). In certain embodiments, the diallylamine acrylamide copolymer comprises from about 10 mol % to about 60 mol % diallylamine monomer. In certain embodiments, the diallylamine acrylamide copolymer comprises about 10 mol % to about 40 mol % diallylamine monomer. In certain embodiments, the diallylamine acrylamide copolymer comprises about 0.1 mol % to about 20 mol % diallylamine monomer.


In certain embodiments, the polymer is a copolymer that comprises an amine-containing allylic monomer and at least one of dimethylaminoethylmethacrylate (DMAEM), dimethylaminoethylacrylate (DMAEA), diethylaminoethyl acrylate (DEAEA), or diethylaminoethyl methacrylate (DEAEM). In certain embodiments, the polymer is a copolymer comprising at least one diallyldimethyl-ammonium chloride monomer (DADMAC).


In certain embodiments, the polymer used in the present methods is a homopolymer. In certain embodiments, the homopolymer is an amine-containing allylic monomer. In certain preferred embodiments, the homopolymer is a diallylamine homopolymer.


In certain embodiments, the polymer is a mixture of polymers comprising at least one amine-containing vinylic or allylic monomer. In certain embodiments, the polymer is a polymer mixture comprising a diallylamine homopolymer. In certain embodiments, the polymer is a polymer mixture comprising a diallylamine acrylamide copolymer. In certain preferred embodiments, the polymer is a mixture of a diallylamine homopolymer and a diallylamine acrylamide copolymer.


The polymer comprising an amine-containing vinylic or allylic monomer can be prepared by any suitable method known in the art. In certain embodiments, the polymer is synthesized using water-in-oil polymerization, dispersion polymerization, gel polymerization, solution polymerization method, or a combination thereof.


In certain embodiments, the polymer comprising at least one amine-containing vinylic or allylic monomer is functionalized with an aldehyde. In certain embodiments, the aldehyde-functionalized polymer is formed by reacting a polymer comprising an amine-containing vinylic or allylic monomer with an aldehyde. In certain embodiments, the aldehyde used to form the aldehyde-functionalized polymer is selected from formaldehyde, paraformaldehyde, glutaraldehyde, glyoxal, and combinations thereof. In certain preferred embodiments, the aldehyde-containing polymer is a glyoxalated polyacrylamide polymer. In certain embodiments, the polymer used in the present inventive methods does not comprise an aldehyde-functionalized polymer.


The polymer used in the present methods can be of any suitable molecular weight. In certain embodiments, the polymer has an average molecular weight of from about 10,000 Daltons to about 5,000,000 Daltons. Thus, in certain embodiments, the polymer has an average molecular weight of from about 10,000 Daltons to about 5,000,000 Daltons, from about 10,000 Daltons to about 4,000,000 Daltons, from about 10,000 Daltons to about 3,000,000 Daltons, from about 10,000 Daltons to about 2,000,000 Daltons, from about 10,000 Daltons to about 1,500,000 Daltons, from about 10,000 Daltons to about 1,000,000 Daltons, from about 10,000 Daltons to about 500,000 Daltons, from about 10,000 Daltons to about 400,000 Daltons, from about 10,000 Daltons to about 300,000 Daltons, from about 10,000 Daltons to about 200,000 Daltons, from about 10,000 Daltons to about 100,000 Daltons, from about 10,000 Daltons to about 50,000 Daltons, from about 100,000 Daltons to about 2,000,000 Daltons, from about 100,000 Daltons to about 1,500,000 Daltons, from about 100,000 Daltons to about 1,000,000 Daltons, from about 100,000 Daltons to about 500,000 Daltons, from about 200,000 Daltons to about 1,500,000 Daltons, from about 200,000 Daltons to about 1,000,000 Daltons, or from about 400,000 Daltons to about 1,250,000 Daltons. In certain preferred embodiments, the polymer has an average molecular weight of from about 200,000 Daltons to about 1,750,000 Daltons. In certain preferred embodiments, the polymer has an average molecular weight of from about 400,000 Daltons to about 1,500,000 Daltons. In certain preferred embodiments, the polymer has an average molecular weight of from about 400,000 Daltons to about 800,000 Daltons. In certain preferred embodiments, the polymer has an average molecular weight of from about 1,000,000 Daltons to about 1,750,000 Daltons. In certain embodiments, the polymer is highly charged (e.g., comprises about 20% or more amine-containing allylic monomer) and has an average molecular weight of from about 400,000 Daltons to about 800,000 Daltons. In certain embodiments, the polymer has a low charge (e.g., comprises about 0.01% to about 20% amine-containing allylic monomer) and has an average molecular weight of from about 800,000 Daltons to about 1,750,000 Daltons.


In certain embodiments, the papermaking methods of the present invention may optionally include one or more materials that are cationic in nature or capable of ionizing or dissociating in such a manner as to produce one or more cations or other positively charged moieties. Such cationic agents have been found useful as a means for aiding in the retention of fiber, fines, and filler in paper, and those of skill in the art commonly refer to these as retention agents, aids, packages, and the like. Other cationic agents include, for example, cationic starch derivatives, including primary, secondary, tertiary, or quaternary amine starch derivatives and other cationic nitrogen substituted starch derivatives. Such derivatives may be prepared from all types of starches including corn, tapioca, potato, waxy maize, wheat, and rice. Moreover, they may be in their original granule form or they may be converted to pre-gelatinized, cold water soluble products and/or employed in liquid form. In certain embodiments, the papermaking methods of the present invention may include flocculants, coagulants, microparticles, or combinations thereof.


Other additives may be used in conjunction with the present invention. Additional agents include wet strength aids, dry strength aids, debonding agents, softening agents, adhesive chemicals, sizing agents, dyes, optical brighteners, absorbency aids, and the like. Other additives include odor control materials and deodorants, pigments, humectants, emollients, bactericides, buffers, waxes, zeolites, lotions, perfumes, vegetable and mineral oils, superabsorbents, surfactants, fungicides, moisturizers, and the like.


The wood pulp source used to produce the papermaking fibers is not limited. For example, hardwood and softwood pulps and a combination thereof can be used as a source of papermaking fibers for the tissue webs of the present invention. Useful wood pulps include chemical pulps such as sulfite and sulfate pulps (e.g., Kraft pulp) as well as mechanical pulps including ground wood, ThermoMechanical Pulp, and Chemi-ThermoMechanical Pulp. Papermaking fibers derived from recycled paper can also be used with the present invention. In certain embodiments, the papermaking fibers are virgin chemical wood pulps.


In another embodiment, a low dust tissue product comprises cellulosic fibers and a polymer comprising at least one amine-containing vinylic or allylic monomer, where the polymer is disposed on at least one surface of the tissue product.


The polymer in the low dust tissue product is the same as the polymer applied to the tissue web, as described above. By way of example, and not in limitation, in certain embodiments, the polymer comprises an acrylamide monomer. In certain embodiments, the polymer comprises a diallylamine monomer. In certain embodiments, the polymer is a diallylamine homopolymer. In certain embodiments, the polymer is a mixture of diallylamine homopolymer and diallylamine acrylamide copolymer. In certain preferred embodiments, the polymer is a diallylamine acrylamide copolymer. In certain embodiments, the diallylamine acrylamide copolymer comprises diallylamine monomer in an amount greater than acrylamide monomer. In certain embodiments, the diallylamine acrylamide copolymer comprises from about 10 to about 60 mole percent diallylamine monomer. In certain preferred embodiments, the diallylamine acrylamide copolymer comprises about 5 to about 40 mole percent diallylamine monomer.


In certain preferred embodiments, the tissue product is formed by applying the polymer to a surface of the tissue web. In certain embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is added to the tissue web in from about 0.05 kg to about 5 kg of dry polymer per ton of tissue product. Thus, in certain embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is added to the tissue web in from about 0.05 kg to about 5 kg of dry polymer per ton of tissue product, from about 0.05 kg to about 4 kg of dry polymer per ton of tissue product, from about 0.05 kg to about 3 kg of dry polymer per ton of tissue product, from about 0.05 kg to about 2 kg of dry polymer per ton of tissue product, from about 0.05 kg to about 1 kg of dry polymer per ton of tissue product, from about 0.5 kg to about 5 kg of dry polymer per ton of tissue product, or from about 1 kg to about 5 kg of dry polymer per ton of tissue product. In certain preferred embodiments, a polymer comprising at least one amine-containing vinylic or allylic monomer is added to the tissue web in from about 0.05 kg to about 3 kg of dry polymer per ton of tissue product.


In certain embodiments, the tissue product comprises a tissue sheet having a weight of from about 5 g/m2 to about 40 g/m2. In certain embodiments, the tissue product comprises a tissue sheet having a weight of from about 5 g/m2 to about 20 g/m2. In certain embodiments, the tissue product comprises a tissue sheet having a weight of from about 10 g/m2 to about 30 g/m2.


In certain embodiments, the polymer comprising at least one amine-containing vinylic or allylic monomer is disposed on two surfaces of the tissue product.


The tissue product of the present invention is single-layered or multi-layered. The tissue product can be a single-ply tissue paper in which the web forming the tissue is stratified, i.e., has multiple layers, or a multi-ply tissue product in which the webs forming the multi-ply tissue product may be either single or multi-layered. It should be understood that the tissue paper can include any number of plies or layers. In certain embodiments, a polymer comprising an amine-containing vinylic or allylic monomer is applied to the top layer of the tissue, or to the layer that will ultimately become the top layer of the tissue. In certain embodiments, the polymer may also be applied to the outer layer of a multi-layer tissue.


The tissue product can be any article which comprises tissue paper. In certain embodiments, the tissue product is bathroom tissue, facial tissue, napkin, or an absorbent towel (e.g., paper towels).


The following examples further illustrate the invention but, of course, should not be construed as in any way limiting its scope.


Example 1

This Example illustrates dust generated from tissue produced using a method in accordance with an embodiment of the invention.


A 17.6 g/m2 premium facial tissue sheet on a crescent former tissue making machine was treated with a diallylamine acrylamide copolymer by spraying the polymer on the surface of the tissue web. The tissue web was formed from a fiber stock slurry having a consistency of 0.08%. The web had a two-layer construction consisting of a 55/45 (wt/wt) fiber split. The fiber in the 55 wt % layer consisted of 100% Eucalyptus fibers and the fiber in the 45 wt % layer consisted of 90% softwood and 10% machine broke. The diallylamine acrylamide copolymer was prepared by mixing the polymer with water to obtain an aqueous solution having a concentration of 0.5% (V/V). The diallylamine acrylamide had a molecular weight of about 1,000,000 Daltons and consisted of 15 mol % diallylamine and 85 mol % acrylamide (equivalent to a charge density of about 2 meq/g). The diallylamine acrylamide solution was fed through the spray boom at an application rate of 0.38 pound of dry product to dry ton of fiber in the tissue web. The diallylamine acrylamide polymer solution was sprayed on the sheet side of the felt (Eucalyptus layer), just after the sheet transfer roll. The web consistency at this point in the process is approximately 10% and the web speed was 884 m/min. The apparatus for applying the dust reduction agent was a spray boom consisting of a 1 inch diameter pipe having a total length of 198 inches. Twenty-one spray nozzles were spaced 8 inches apart along the pipe to apply the diallylamine acrylamide copolymer over the 169 inch width of the tissue sheet. The nozzle spray angles were 110 degrees and each delivered 0.1 gallons per minute at the 40 psi boom pressure. The tissue sheet was dried using a Yankee dryer and subjected to a creping process using a flexible creping blade. The tissue sheet moisture at the finished reel was 4.4%. For each sample, dust was collected for a time period of one hour by placing a 9 inch×13 inch pan underneath the creping blade. The amount of dusting at the creping blade was measured gravimetrically. The collected dust was weighed and recorded.


The anti-dusting effect of applying diallylamine acrylamide copolymer to the surface of a tissue web was evaluated through paper machine trials. The amount of dust collected at the creping blade during the trial is shown at FIG. 1, where the sample number is plotted along the horizontal axis and the amount of dust collected at the creping blade is plotted along the vertical axis. For samples 1-15, there was no diallylamine acrylamide copolymer added to the tissue web. The copolymer is added prior to analysis of sample 16 (see A in FIG. 1). At sample 28, the application rate of the copolymer is reduced from about 0.38 lb/ton to about 0.20 lb/ton (see B in FIG. 1). Prior to sample 31, the amount of copolymer is increased from 0.20 lb/ton to about 0.38 lb/ton (see C in FIG. 1). As shown in FIG. 1, the amount of dust collected from the creping blade when the polymeric treatment was applied to the tissue web was from about 20% to 50% less than was collected for tissue prepared in the absence of diallylamine acrylamide copolymer treatment (e.g., sample 15 vs. sample 24). Applicants also observed a reduction in the amount of wet strength additive required to maintain strength. Wet strength additive usage remained very low, averaging about 1.8 gallons per hour.


Example 2

This Example illustrates the dusting and strength properties of a tissue sheet produced using a method in accordance with an embodiment of the invention.


A 17.6 g/m2 premium facial tissue sheet on a crescent former tissue making machine was treated with a diallylamine acrylamide copolymer and subjected to creping in the same manner as the tissue sheet of Example 1. The diallylamine acrylamide copolymer was the same as the copolymer used in Example 1. After the tissue sheet was sprayed with diallylamine acrylamide copolymer, the dust generated during the creping process was measured as done in Example 1. The amount of wet strength additive added to the furnish was also recorded. In addition, the dry and wet tensile strength of the tissue was measured. Dry and wet tensile tests were conducted in a conditioned temperature and humidity room in general accordance with TAPPI standards (e.g., T450 om-03, T494 om-06, and T576 pm-07). The tissue test specimens were 1 inch wide. For wet tensile tests, the strips were wetted in the middle of the span with a brush.


The effect of applying a diallylamine acrylamide copolymer to a tissue web on dusting, wet strength additive dosage, and tensile strength was evaluated through a paper machine trial shown in FIGS. 2-4. “Start of Trial” refers to the point at which the diallylamine acrylamide is applied to the tissue web. The anti-dusting effect of applying a diallylamine acrylamide copolymer to a tissue web is shown in FIG. 2, where the sample number is plotted along the horizontal axis and the amount of dust collected at the creping blade is plotted along the vertical axis. As shown in FIG. 2, the amount of dust collected from the creping blade when the polymeric treatment was applied to the tissue web was less than the amount of dust collected from tissue prepared in the absence of diallylamine acrylamide polymer treatment. The average amount of dust collected prior to adding diallylamine acrylamide copolymer to the tissue web was 84 grams, while the average dust collected after adding diallylamine acrylamide copolymer to the tissue web was 69 grams, resulting in 18% overall dust reduction.


The effect of application of a diallylamine acrylamide copolymer to a tissue web on wet strength additive dosage in a tissue making process was also evaluated during the same trial. FIG. 3 shows the effect of diallylamine acrylamide copolymer on the amount of wet strength additive dosed into the furnish to maintain sufficient tissue strength, where time is plotted along the horizontal axis and the amount of wet strength additive added to the furnish is plotted along the vertical axis. As shown in FIG. 3, the amount of wet strength additive needed to maintain sufficient tissue wet strength decreased when the diallylamine acrylamide copolymer was added to the tissue web.


The effect of application of a diallylamine acrylamide copolymer to a tissue web on wet tensile strength and dry tensile strength was evaluated as shown in FIG. 4, where time is plotted along the horizontal axis and dry tensile strength and wet tensile strength are plotted along the left vertical axis and right vertical axis, respectively. Table 1 shows tensile strength data and wet strength additive dosage for the final data point of the trial shown in FIGS. 3 and 4.


Table 1 shows that the wet and dry tensile strength of the tissue increased with addition of diallylamine acrylamide copolymer to the tissue web in accordance with an embodiment of the invention. As shown in Table 1, the MD dry strength was 408 g/in prior to adding diallylamine acrylamide copolymer to the tissue web (see Pre-trial data). After application of the diallylamine acrylamide copolymer to the tissue web, the MD dry tensile strength increased to 463 Win (see Trial data). Similarly, CD dry tensile strength and CD wet tensile strength increased when the tissue web was treated with diallylamine acrylamide copolymer. The data of FIG. 4 and Table 1 demonstrates that the wet and dry tensile strength of a tissue web increased after treatment of the tissue web with a diallylamine acrylamide copolymer in accordance with an embodiment of the invention. Of particular note, the wet tensile strength of the tissue remained higher than the control even though the amount of wet strength resin added to the furnish was reduced by 43% (i.e., from 3.5 gph to about 2.0 gph).









TABLE I







Trial Data—Effect of Application of Diallylamine


Acrylamide Copolymer to Tissue Web












Wet Strength
MD Dry
CD Dry
CD Wet



Resin Dosage
Tensile
Tensile
Tensile



(grams per
Strength
Strength
Strength



hour)
(g/in.)
(g/in.)
(g/in.)














Pre-trial
3.5
408
216
44


Trial
2.0
463
250
47


% change
−43
+13.5
+15.7
+6.8









The use of the terms “a” and “an” and “the” and “at least one” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The use of the term “at least one” followed by a list of one or more items (for example, “at least one of A and B”) is to be construed to mean one item selected from the listed items (A or B) or any combination of two or more of the listed items (A and B), unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.


Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context.

Claims
  • 1. A method for reducing dust in a tissue making process comprising: applying a polymer comprising at least one amine-containing vinylic or allylic monomer to the surface of a tissue web, wherein the polymer does not comprise an aldehyde-functionalized polymer.
  • 2. The method of claim 1, wherein the polymer is applied by spraying onto a surface of the tissue web.
  • 3. The method of claim 2, wherein the polymer is applied by spraying onto the surface of the tissue web utilizing a spray boom.
  • 4. The method of claim 1, wherein the polymer is applied prior to drying the tissue web.
  • 5. The method of claim 1, wherein the tissue web is at least partially dried after the polymer is applied to the tissue web.
  • 6. The method of claim 1, wherein the tissue web has a wet web consistency of from about 5% to about 40%.
  • 7. The method of claim 1, wherein the polymer is a diallylamine acrylamide copolymer.
  • 8. The method of claim 1, wherein the polymer is applied in combination with a diallylamine homopolymer.
  • 9. The method of claim 1, wherein the polymer comprises about 0.1 mol % to about 20 mol % diallylamine monomer.
  • 10. The method of claim 1, wherein the polymer has an average molecular weight of from about 200,000 Daltons to about 1,500,000 Daltons.
  • 11. The method of claim 1, wherein the polymer is applied to the surface of the tissue web as a solution having a concentration of from about 0.01% to about 10% by weight of the polymer based on the weight of the solution.
Parent Case Info

This application is a nonprovisional application claiming the benefit of U.S. Provisional Patent Application No. 62/336,236, filed May 13, 2016, the disclosure of which is incorporated by reference herein in its entirety.

US Referenced Citations (187)
Number Name Date Kind
2059465 Kress Nov 1936 A
2601597 Daniel, Jr. et al. Jun 1952 A
2765229 McLaughlin Oct 1956 A
2982749 Friedrich et al. May 1961 A
3102064 Wurzburg et al. Aug 1963 A
3233962 Nelson Feb 1966 A
3234076 Goldsmith Feb 1966 A
3284393 Vanderhoff et al. Nov 1966 A
3409500 Strazdins et al. Nov 1968 A
3507847 Coscia Apr 1970 A
3555932 Schwerdhöfer Jan 1971 A
3556932 Coscia et al. Jan 1971 A
3734873 Anderson et al. May 1973 A
3772076 Keim Nov 1973 A
3821069 Wurzburg Jun 1974 A
RE28474 Anderson et al. Jul 1975 E
RE28576 Anderson et al. Oct 1975 E
3951921 Espy Apr 1976 A
3968005 Wurzburg Jul 1976 A
4040900 Mazzarella et al. Aug 1977 A
4210489 Markofsky Jul 1980 A
4493659 Iwashita Jan 1985 A
4533434 Yoshioka et al. Aug 1985 A
4603176 Bjorkquist et al. Jul 1986 A
4605702 Guerro et al. Aug 1986 A
4657946 Rende et al. Apr 1987 A
4915786 Sweeney Apr 1990 A
4919821 Fong et al. Apr 1990 A
4929655 Takeda et al. May 1990 A
4956399 Kozakiewicz et al. Sep 1990 A
5006590 Takeda et al. Apr 1991 A
5147908 Floyd et al. Sep 1992 A
5179150 Furman, Jr. Jan 1993 A
5187219 Furman, Jr. Feb 1993 A
5223092 Grinnell Jun 1993 A
5271806 Deutsch Dec 1993 A
5281307 Smigo et al. Jan 1994 A
5324792 Ford Jun 1994 A
5374334 Sommese Dec 1994 A
5438087 Ikeda et al. Aug 1995 A
5474856 Tamagawa et al. Dec 1995 A
5501774 Burke Mar 1996 A
5571380 Fallon Nov 1996 A
5597858 Ramesh et al. Jan 1997 A
5597859 Hurlock et al. Jan 1997 A
5605970 Selvarajan Feb 1997 A
5654198 Carrier et al. Aug 1997 A
5674362 Underwood et al. Oct 1997 A
5837776 Selvarajan et al. Nov 1998 A
5865951 Kawakami et al. Feb 1999 A
5938937 Sparapany et al. Aug 1999 A
5961782 Luu et al. Oct 1999 A
5985992 Chen Nov 1999 A
6013705 Chen et al. Jan 2000 A
6013708 Mallon et al. Jan 2000 A
6027611 McFarland Feb 2000 A
6077394 Spence et al. Jun 2000 A
6083348 Auhorn et al. Jul 2000 A
6153049 Croft Nov 2000 A
6190499 Oriaran et al. Feb 2001 B1
6238519 Jones May 2001 B1
6238521 Shing et al. May 2001 B1
6245874 Staib et al. Jun 2001 B1
6315866 Sanchez Nov 2001 B1
6348132 Zhang et al. Feb 2002 B1
6426383 Fong et al. Jul 2002 B1
6472487 Schroeder et al. Oct 2002 B2
6491790 Proverb et al. Dec 2002 B1
6592718 Wong Shing et al. Jul 2003 B1
6610209 Sommese et al. Aug 2003 B1
6699359 Luu et al. Mar 2004 B1
6743335 Proverb et al. Jun 2004 B2
6746542 Lorencak et al. Jun 2004 B1
6787574 Anderson et al. Sep 2004 B1
6808595 Burns Oct 2004 B1
6815497 Luu et al. Nov 2004 B1
6939443 Ryan et al. Sep 2005 B2
7034087 Hagiopol et al. Apr 2006 B2
7119148 Hagiopol et al. Oct 2006 B2
7125469 Barcus et al. Oct 2006 B2
7125695 Schellenberger et al. Oct 2006 B2
7323510 Fischer et al. Jan 2008 B2
7455751 Ward et al. Nov 2008 B2
7488403 Hagiopol et al. Feb 2009 B2
7550060 Jacobson et al. Jun 2009 B2
7615135 Harrington et al. Nov 2009 B2
7641766 St. John et al. Jan 2010 B2
7641776 Nagar et al. Jan 2010 B2
7683121 Wei et al. Mar 2010 B2
7740743 Singh et al. Jun 2010 B2
7794565 Shannon et al. Sep 2010 B2
7863395 Hagiopol et al. Jan 2011 B2
7897013 Hagiopol et al. Mar 2011 B2
7914646 Duggirala et al. Mar 2011 B2
7938934 Todorovic et al. May 2011 B2
7972478 Hund et al. Jul 2011 B2
8025924 Ohira et al. Sep 2011 B2
8070914 Ryan et al. Dec 2011 B2
8088213 Cheng et al. Jan 2012 B2
8088250 Cheng et al. Jan 2012 B2
8288502 Bode et al. Oct 2012 B2
8349134 Esser et al. Jan 2013 B2
8382947 Skaggs et al. Feb 2013 B2
8404083 Haehnle et al. Mar 2013 B2
8414739 Kimura et al. Apr 2013 B2
8425724 Ryan et al. Apr 2013 B2
8444818 Sutman et al. May 2013 B2
8454798 Ban et al. Jun 2013 B2
8465623 Zhao et al. Jun 2013 B2
8636875 McKay Jan 2014 B2
8647472 Cheng et al. Feb 2014 B2
8696869 Borkar et al. Apr 2014 B2
8709207 Grimm Apr 2014 B2
8709208 Zhao et al. Apr 2014 B2
RE44936 St. John et al. Jun 2014 E
8747617 Cheng et al. Jun 2014 B2
8753480 Bode et al. Jun 2014 B2
8840759 Benz et al. Sep 2014 B2
8852400 St. John Oct 2014 B2
8882964 Zhao et al. Nov 2014 B2
8894817 Cheng et al. Nov 2014 B1
8920606 Wright Dec 2014 B2
8999111 Castro et al. Apr 2015 B2
9011643 Gu et al. Apr 2015 B2
9034145 Castro et al. May 2015 B2
9051687 Esser et al. Jun 2015 B2
9145646 Benz et al. Sep 2015 B2
9328462 Chen et al. May 2016 B2
9840810 Castro Dec 2017 B2
20020045704 Luu Apr 2002 A1
20020139500 Runge Oct 2002 A1
20030056917 Jimenez Mar 2003 A1
20030224945 Twu et al. Dec 2003 A1
20040060677 Huang Apr 2004 A1
20040084162 Shannon May 2004 A1
20060142535 Cyr et al. Jun 2006 A1
20060201645 Ito Sep 2006 A1
20070000630 Hassler et al. Jan 2007 A1
20080149287 Hagiopol et al. Jun 2008 A1
20080196851 Hund et al. Aug 2008 A1
20080277084 Denowski et al. Nov 2008 A1
20080308242 Lu et al. Dec 2008 A1
20090107644 Cowman et al. Apr 2009 A1
20090145566 Esser et al. Jun 2009 A1
20090165978 Hagiopol et al. Jul 2009 A1
20090281212 Pawlowska et al. Nov 2009 A1
20100018660 Varnell Jan 2010 A1
20100193147 Ryan et al. Aug 2010 A1
20110083821 Wright Apr 2011 A1
20110132559 Haehnle et al. Jun 2011 A1
20110146925 Bode et al. Jun 2011 A1
20110155339 Brungardt Jun 2011 A1
20120035306 Ryan et al. Feb 2012 A1
20120073773 Jehn-Rendu et al. Mar 2012 A1
20120073774 Jehn-Rendu et al. Mar 2012 A1
20120103546 Maniere May 2012 A1
20120103547 Grimm et al. May 2012 A1
20120111517 Borkar et al. May 2012 A1
20120186764 McKay Jul 2012 A1
20130081771 Luo et al. Apr 2013 A1
20130133847 Zhao et al. May 2013 A1
20130139985 Wright Jun 2013 A1
20130160959 Rosencrance et al. Jun 2013 A1
20130192782 Benz et al. Aug 2013 A1
20130306261 Zhao et al. Nov 2013 A1
20140053996 Esser et al. Feb 2014 A1
20140060763 Bode et al. Mar 2014 A1
20140130994 St. John et al. May 2014 A1
20140182799 Castro et al. Jul 2014 A1
20140262091 Lu et al. Sep 2014 A1
20140284011 Krapsch et al. Sep 2014 A1
20140336314 Benz et al. Nov 2014 A1
20150020988 St. John et al. Jan 2015 A1
20150041088 Castro et al. Feb 2015 A1
20150041089 Castro et al. Feb 2015 A1
20150041092 Hietaniemi et al. Feb 2015 A1
20150059998 Zhao et al. Mar 2015 A1
20150176206 Chen et al. Jun 2015 A1
20150191875 Esser et al. Jul 2015 A1
20150197893 Cheng et al. Jul 2015 A1
20150204019 Wright Jul 2015 A1
20150299961 Borkar et al. Oct 2015 A1
20160097160 Castro Apr 2016 A1
20160097161 Benz et al. Apr 2016 A1
20160298297 Borkar Oct 2016 A1
20170328008 Linder, Jr. Nov 2017 A1
20190031802 Gu Jan 2019 A1
Foreign Referenced Citations (23)
Number Date Country
2176898 Oct 2006 CA
4426620 Feb 1995 DE
0151994 Aug 1985 EP
0183466 Jun 1986 EP
0444788 Sep 1991 EP
0630909 Dec 1994 EP
0657478 Jun 1995 EP
1195259 Apr 2002 EP
1579071 Jul 2008 EP
05-247883 Sep 1993 JP
H06-299494 Oct 1994 JP
2005-001197 Jan 2005 JP
2008-049688 Mar 2008 JP
2012-107356 Jun 2012 JP
WO 9705330 Feb 1997 WO
WO 9710387 Mar 1997 WO
WO-0000698 Jan 2000 WO
WO 0011053 Mar 2000 WO
WO 2004061235 Jul 2004 WO
WO 2008028865 Mar 2008 WO
WO 2012007364 Jan 2012 WO
WO 2014078102 May 2014 WO
WO-2017197380 Nov 2017 WO
Non-Patent Literature Citations (27)
Entry
Anon, “Daily-use paper project at Fujian HengLi to enter production,” China Pap. Ind. News, vol. 1, No. 13, p. 2 (May 30, 2006).
Anon, “An Innovative Approach to Fibre Recovery and Ash, Fines and Colloidals Control for Increased Water System Closure,” TAPPSA Journal, pp. 27-32 (Sep. 2009).
Brown, “New Simplified Technology for On-Line Measurement on Tissue Machines,” Process Control News (for the Pulp and Paper Industries), vol. 21, No. 6, pp. 8-9 (Jun. 2001).
Devillers et al, “Fines management for tissue machines” International Paperwork (IPW), No. 1-2, pp. 15-18 (Jan.-Feb. 2014).
Ecolab Global Knowledge Services, Literature Search Report #10261, 38 pp. (Aug. 21, 2015).
European Patent Office, International Search Report in International Patent Application No. PCT/US2017/032616, dated Aug. 7, 2017, 4 pp.
European Patent Office, Written Opinion in Internationai Patent Application No. PCT/US2017/032616, dated Aug. 7, 2017, 5 pp.
Farley et al., “Sizing With Alkenyl Succinic Anhydridge,” The Sizing of Paper, 2nd Ed., Atlanta, GA: TAPPI Press, pp. 51-62 (1989).
Farley et al., “Glyoxalated Polyacrylamide Resin,” Wet-Strength Resins and Their Application, Chapter 3, Atlanta, GA:TAPPI Press, pp. 45-61 (1994).
Friberg et al., “Emulsions,” Encyclopedia of Chemical Technology, 41th Ed., vol. 9, pp. 393-413 (Dec. 4, 2000).
Gruszka et al., “Testing de-ashing of tissue paper through fractionated de-crilling of selected recycled pulp grades;” Przeglad Pap. (Polish Paper Review), vol. 69, No. 2, pp. 131-138 (2013).
Hughson et al. “Characterization of Assessment of Dermal and Inhalable Nickel Exposures in Nickel Production and Primary User Industries,” Ann. Occup. Hyg., vol. 54 , No. 1, pp. 8-22 (2010).
Hunkeler et al., “Mechanism, kinetics and modelling of the inverse-microsuspension homopolymerization of acrylamide,” Polymer, vol. 30, No. 1, pp. 127-142 (Jan. 1989).
Hunkeler et al., “Mechanism, kinetics and modelling of inverse-micorsuspension polymerization: 2. Copolymerization of acrylamide with quaternary ammonium cationic monomers,” Polymer, vol. 32, No. 14, pp. 2626-2640 (1991).
Kraus et al., “Respiratory symptoms and diseases among workers in the soft tissue producing industry,” Occup. Environ. Med., vol. 59, No. 12, pp. 830-835 (2002).
Nalco Chemical Company, Hercobond 1000 Product Analysis, 1 pg. (Feb. 25, 2002).
Nalco Chemical Company, Parez 631 NC Product Analysis, 20 pp. (Aug. 5, 1999).
Panda, “Approaches to high-yield pulping of mechanical pulp types,” Proceedings of the International Workshop on Small Scale Chemical Recovery, High Yield Pulping, and Effluent Treatment, 15 pp. (1991).
Peters, “Optimised fibre yield arid stook mixture,” Wochenbl. Papierfabr., vol. 140, No. 7, pp. 545-546 (Jul. 2012).
Roy et al., “Effect of Nonfibrous Tissue on the Papermaking Properties of Bagasse and Straws,” IPPTA Convention Issue—Annual General Meeting & Seminar on Non-Wood Fibrous Raw Material Pulping and Paper Making, pp. 49-55 (1993-1994).
Sheridan, et al., “Dust—No Longer an Issue for Tissue,” Paper Technology, vol. 46, No. 5, pp. 33-38 (Jun. 2005).
Sheridan et al., “Dust—No Longer an Issue for Tissue,” Tissue World 2005 Conference—The 7th International Conference and Exhibition for the Tissue Business—Preprints, 11 pp. (Apr. 2005).
Snook, “Non-fibrous Additives to Papermaking Stock,” Handbook for Pulp and Paper Technologies, Chapter 15, pp. 220-227 (1992).
Springer et al., “The effect of fibrous fines on tissue properties,” Tappi Journal, vol. 71, No. 2, pp. 99-102 (1988).
St. John, “Ondec-Nalco Technical Exchange,” 5 pp. (Jun. 27, 2002).
Tatum, “Characterization of Particulate Matter in Workplace Atmospheres of Paper Making and Converting Operations,” NCASI Technical Bulletin, No. 873, 36 pp. (Mar. 2004).
Williamson, “Cost-effective automation at SCA,” Paper360, vol. 5, No. 2 pp. 16-17 (Mar.-Apr. 2010).
Related Publications (1)
Number Date Country
20170328008 A1 Nov 2017 US
Provisional Applications (1)
Number Date Country
62336236 May 2016 US