Patent Application
20170042664
1. Field of the Invention
The present invention relates to implantable prostheses. More particularly, the present invention relates to implantable breast prostheses designed to eliminate encapsulation and reduce scarring, and to replace tissue removed for purposes of biopsy or lumpectomy.
2. Description of the Related Art
Breast prostheses are utilized for augmentation mammoplasty and in cosmetic surgery. Prostheses are also indicated in breast cancer surgery, such as lumpectomies, where a portion of the breast is removed and can leave some disfigurement if not replaced by a similar amount of tissue and/or augmentation material.
Similarly, biopsies can leave small dimples or imperfections if remedial steps are not taken. About 1 million breast biopsies are performed in the United States annually. As a result, some 200,000 new breast cancers are diagnosed each year.
Known methods of augmentation mammoplasty utilize silicone or saline implants. These methods have been complicated post-operatively by encapsulation of the implants, which can occur to varying degrees. Encapsulation produces a hard area of scar tissue around the implant, resulting in a rigid, abnormally-shaped mount beneath the breast tissue or pectoralis muscle, depending upon the placement of the implant.
Moreover, the known implant materials may not be indicated for replacement of smaller amounts of tissue, as would be required to prevent dimpling after biopsies, for example. Further, the known implant materials are not amenable to resizing. In addition, known implants are not capable of being implanted through a cannula or needle, and are not readily instilled with medicaments or chemical agents that would be useful in treating the patient.
Accordingly, a need exists for implants and methods that can be adapted for replacement of small as well as large amounts of tissue. A need also exists for implants that can be delivered through cannulae or needles, as well as being able to significantly reduce or eliminate encapsulation, resulting in a prolonged, aesthetically pleasing, soft mound below the breast tissue or pectoralis muscle. In addition, a need exists for implants into which useful substances, such as beneficial medications, chemical agents, hormonal treatments, stem cells, such as adipocytes, cellular precursors and components, and radiation media can be instilled to enhance the treatment capabilities of the implant in cancer and other breast pathology.
The present invention overcomes deficiency of the prior art, such as those noted above, by providing an implant in which at least the outer portion of the implant, and as much as the entire implant, is made of a resorbable material. The implant is sized and shaped to reduce excised tissue. Preferably, the implant provides a support structure in the form of a framework or scaffold for the surrounding tissue after implantation. The support structure preferably is porous to permit the in-growth of fibrous replacement tissue. Advantageously, replacement tissue in-growth takes place without encapsulation and with reduced scarring.
The invention, in one form thereof, is directed to an implant for marking an area within a living body. The implant includes a matrix material and a marking material. The implant is formable to fit the shape and size of a cavity in the human body. The implant is configured to support tissue surrounding the cavity and to allow in-growth of fibrous tissue into and replace at least a portion of the matrix material.
The invention, in another form thereof, is directed to a tissue marking implant. The tissue marking implant includes a matrix and a dye marker. A matrix is collagen material. The matrix has a porous structure for supporting surrounding tissue of a breast and is configured to provide a framework for the in-growth of fibrous tissue into the matrix. The dye marker is supported by the matrix for dispersion into the tissue.
According to an embodiment of the invention, excised tissue is replaced by installing an implant having at least an outer shell of resorbable material. The implant is sized and shaped to replace the excised tissue. The implant supports surrounding tissue while fibrous tissue replaces the resorbable portion of the implant.
In a further development, at least a portion of the implant can be provided in the form of a compressible or non-compressible sponge or foam, or a self-expanding sponge or foam. The sponge or foam provides a porous support matrix for surrounding and in-growing tissue. In the form of a compressible, expandable, or self-expanding sponge or foam, the implant advantageously can be inserted through a cannula or a needle, or optionally can be directly inserted. Additionally, the implant can be instilled with beneficial materials, such as indicated medicaments, therapeutics, or diagnostic agents, as well as matrix enhancing additives.
Other features and advantages of the present invention will become apparent from the following description of the invention which refers to the accompanying drawings.
Referring initially to
Outer shell 4 is made entirely of biosorbable materials, such as collagens or polyglycolic acids, for example. Over a period of approximately three weeks to six months, the outer shell dissolves, leaving the inner contents 6 present inside the breast. Hard encapsulation will not occur because there is not a foreign body contained within the prosthetic space.
Referring to
Advantageously, the proportions and spacing of the two types of materials can be altered to provide the desired properties of containment using a minimal amount of nonabsorbable material. Accordingly, the non-absorbable fibers 8 which remain after the biosorbable materials resorb will act as a scaffolding to allow the prosthesis to hold its shape; however, because of the limited amount of foreign material, encapsulation and scarring are decreased.
Referring to
After implantation, outer capsule 12 dissolves, thus preventing hardening by encapsulation of the prosthesis. The supply of fluid 16 between the capsules (a few to several c.c.'s) is absorbed by the body once released by the dissolution of outer capsule 12.
Referring to
According to a preferred embodiment, the implant is provided in the form of a foam or sponge which can be modified by a surgeon prior to implantation, such as at a lumpectomy or biopsy site, simply by trimming the sponge to the appropriate size and shape. Alternatively, the implant can be a pre-shaped prosthesis of appropriate size, or an appropriate amount of foam or foam-forming materials. Optionally, the foam can be provided as a self-expanding matrix that either is compressed, or forms in situ. Advantageously, the implant can be modified to correspond to the breast tissue that either has been removed, requires replacement, or requires augmentation. The foam or sponge matrix is sufficiently resilient to support the surrounding tissue without collapsing.
A preferred embodiment of implantation is illustrated schematically in
The force for advancing the sponge or foam material through the cannula can be applied directly to the implant, or indirectly using fluids, for example. Advantageously, the implant can be used in conjunction with stereotactic biopsy instrumentation, such as the ABBI® System, the MIB System by US Surgical, or the Mammotome® System by Johnson and Johnson.
As a further alternative, the sponge or foam implant of the present invention can form all or part of a larger implant, such as those described above. Accordingly, the tissue supporting sponge or foam or foam matrix will form, for example, all or part of the outer shell 4 of implant 2. Implantation using open procedures usually would be indicated when the sponge implant of the present invention is used as all or part of a larger implant. Accordingly, the sponge or implant would be placed directly into the biopsy or lumpectomy cavity.
In addition, the implant 20 can be provided in the form of a self-expanding foam, which can be injected through a tubular member 22 such as a needle or cannula in a metered amount. An appropriate amount of foam-forming materials can be inserted through cannula 22 and allowed to expand or form a matrix within the cavity created by the excised tissue. Alternatively, a specialized, applicator may be used to inject the desired amount of the foam. The amount of foam is preselected to allow sufficient expansion to fill the void left by the excision and support the surrounding tissue to prevent dimpling.
Following insertion of the implant, such as by an open method or one of the stereotactic methods described above, the resorbable implant occupies the breast tissue cavity and supports the surrounding tissue until such time as it resorbs or biodegrades. After initial implantation, the patient's own fluids, fibroblast, and stem cells, such adipocytes, vascular stem cells, and others, permeates the sponge prosthesis. In the case of a small implant, such permeation would occur naturally, subsequent to implantation. In the case of a larger implant, providing the implant at least partially filled with fluids prior to implantation may be indicated.
Advantageously, the new prosthesis decreases encapsulation after implantation. Various biosorbable materials can be used in the implant of the present invention. Known biosorbable materials include polyglycolic acid (Dexon, Davis & Geck); polyglactin material (Vicryl, Ethicon); poliglecaprone (Monocryl, Ethicon); and synthetic absorbable lactomer 9-1 (Polysorb, United States Surgical Corporation)
Other foamable materials that can be utilized in the present invention include, without limitation, proteins such as collagen, fibronectin, laminin and fibrin, most preferably collagen, and high molecular weight polysaccharides, such as heparan sulphate, chondroitin sulphate, hyaluronic acid and dermatan sulphate. Mixtures of any of the aforementioned materials also can be used, as required.
The materials can be modified, by cross-linking for example, to control degradation rates over varying lengths of time, after which they are substantially or completely resorbed.
Foams can be formed by various means known to those skilled in the art, including injecting an aerosol into a gel, and freeze-drying aqueous dispersions of the foam-forming material. Foaming agents can be included to promote formation of the foam. In addition, stabilizing agents can be included to enhance foam stability. The foams can be extruded or formed in situ.
According to the present invention, these products may be mixed with one another or combined to provide various resorption times or gradients, and/or may be interrelated with non-absorbable materials, such as polypropylene or PTFE (polytetrafluoroethylene) sold as (Gore-Tex®) material, for example. In an instance where a non-absorbable material is utilized, the non-resorbable implant section will remain partially intact as a permanent structure.
In each of the embodiment, the resorbable portions of the prosthesis ultimately biodegrades, and the patient is left with autologous tissue, some of which may have been implanted, or a permanent implant such as saline, as a filler for the biopsy cavity, thus preserving the contour of the breast and preventing indentation of the overlying skin.
The implants of the present invention further can be instilled, before or after implantation, with indicated medicines and other chemical or diagnostic agents. Examples of such agents include, but are not limited to, antibiotics, chemotherapies, other cancer therapies, brachytherapeutic material for local radiation effect, x-ray opaque or metallic material for identification of the area, hemostatic material for control of bleeding, growth factor hormones, immune system factors, gene therapies, biochemical indicators or vectors, and other types of therapeutic or diagnostic materials which may enhance the treatment of the patient.
The breast implant preferably includes a permanent or temporary dye marker such as, but not limited to, indigo carmine or methylene blue. This marker serves as a visual identification of the area that has been biopsied or a lumpectomy has been performed so that in the future an operating surgeon can identify the surrounding tissue before he violates the previously biopsied cavity. These dyes leach into the breast tissue giving the surgeon an indication when he is nearing the point of interest, that being a previous biopsy site particularly if it is positive for a cancer or if it is a site for which a lumpectomy has been previously performed and the pathologist advises us that there is residual cancer. The surgeon can thus remove any of the surrounding breast tissue that contains dye and depending upon its concentration and the distance that it has traveled from the biopsy site will give us an indication of how much tissue should appropriately be removed.
This dye may be integrated with a bioabsorbable material such as, but not limited to collagen or may be in a separate capsule that is inserted with the bioabsorbable material as well as a metallic device for radiographic identification.
These two dyes are very dark colored dyes and these do leach through the breast tissue but will not stain the overlying skin.
The present invention has been described particularly in connection with a breast implant, but it will be obvious to those of skill in the art that the invention can have application to other parts of the body, such as the face, and generally to other soft tissue or bone. Accordingly, the invention is applicable to replacing missing or damaged soft tissue, structural tissue or bone, or for cosmetic tissue or bone replacement.
Although the present invention has been described in relation to particular embodiments thereof, many other variations and modifications and other uses will become apparent to those skilled in the art. It is preferred, therefore, that the present invention be limited not only by the specific disclosure herein, but only by the appended claims.
This application is continuation of application Ser. No. 12/589,413, filed Oct. 23, 2009, which is a divisional of application Ser. No. 11/108,785, filed Apr. 19, 2005, now U.S. Pat. No. 7,637,948, which is a continuation-in-part of U.S. patent application Ser. No. 10/627,718, filed Jul. 28, 2003, now U.S. Pat. No. 6,881,226, which is continuation of application Ser. No. 09/828,806, filed Apr. 10, 2001, now U.S. Pat. No. 6,638,308, which is a divisional of U.S. patent application Ser. No. 09/169,351, filed Oct. 9, 1998, now U.S. Pat. No. 6,214,045, which claims the benefit of U.S. Provisional Application Ser. No. 60/061,588, filed Oct. 10, 1997, U.S. Provisional Application Ser. No. 60/077,639, filed Mar. 11, 1998, and U.S. Provisional Application Ser. No. 60/091,306, filed Jun. 30, 1998, the disclosures of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 60061588 | Oct 1997 | US | |
| 60077639 | Mar 1998 | US | |
| 60091306 | Jun 1998 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14714748 | May 2015 | US |
| Child | 15334445 | US | |
| Parent | 11108785 | Apr 2005 | US |
| Child | 12589413 | US | |
| Parent | 09828806 | Apr 2001 | US |
| Child | 10627718 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14166328 | Jan 2014 | US |
| Child | 14714748 | US | |
| Parent | 13426061 | Mar 2012 | US |
| Child | 14166328 | US | |
| Parent | 12965405 | Dec 2010 | US |
| Child | 13426061 | US | |
| Parent | 12589413 | Oct 2009 | US |
| Child | 12965405 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10627718 | Jul 2003 | US |
| Child | 11108785 | US | |
| Parent | 09169351 | Oct 1998 | US |
| Child | 09828806 | US |