Titanium silicide nitride emitters and method

Information

  • Patent Grant
  • 6323587
  • Patent Number
    6,323,587
  • Date Filed
    Thursday, August 6, 1998
    26 years ago
  • Date Issued
    Tuesday, November 27, 2001
    22 years ago
Abstract
A field emission display apparatus includes a plurality of emitters formed on a substrate. Each of the emitters includes a titanium silicide nitride outer layer so that the emitters are less susceptible to degradation. A dielectric layer is formed on the substrate and the emitters, and an opening is formed in the dielectric layer surrounding each of the emitters. A conductive extraction grid is formed on the dielectric layer substantially in a plane defined by the emitters, and includes an opening surrounding each of the emitters. A cathodoluminescent faceplate having a planar surface is disposed parallel to the substrate.
Description




TECHNICAL FIELD




This invention relates in general to visual displays for electronic devices and more particularly to improved emitters for field emission displays.




BACKGROUND OF THE INVENTION





FIG. 1

is a simplified side cross-sectional view of a portion of a field emission display


10


including a faceplate


20


and a baseplate


21


in accordance with the prior art.

FIG. 1

is not drawn to scale. The faceplate


20


includes a transparent viewing screen


22


, a transparent conductive layer


24


and a cathodoluminescent layer


26


. The transparent viewing screen


22


supports the layers


24


and


26


, acts as a viewing surface and as a wall for a hermetically sealed package formed between the viewing screen


22


and the baseplate


21


. The viewing screen


22


may be formed from glass. The transparent conductive layer


24


may be formed from indium tin oxide. The cathodoluminescent layer


26


may be segmented into pixels yielding different colors for color displays. Materials useful as cathodoluminescent materials in the cathodoluminescent layer


26


include Y


2


O


3


:Eu (red, phosphor P-56), Y


3


(Al, Ga)


5


O


12


:Tb (green, phosphor P-53) and Y


2


(SiO


5


):Ce (blue, phosphor P-47) available from Osram Sylvania of Towanda Pa. or from Nichia of Japan.




The baseplate


21


includes emitters


30


formed on a planar surface of a substrate


32


. The substrate


32


is coated with a dielectric layer


34


. In one embodiment, this is effected by deposition of silicon dioxide via a conventional TEOS process. The dielectric layer


34


is formed to have a thickness that is less than a height of the emitters


30


. This thickness is on the order of 0.4 microns, although greater or lesser thicknesses may be employed. A conductive extraction grid


38


is formed on the dielectric layer


34


. The extraction grid


38


may be formed, for example, as a thin layer of doped polysilicon. The radius of an opening


40


created in the extraction grid


38


, which is also approximately the separation of the extraction grid


38


from the tip of the emitter


30


, is about 0.4 microns, although larger or smaller openings


40


may also be employed.




The baseplate


21


also includes a field effect transistor (“FET”)


50


formed in the surface of the substrate


32


for controlling the supply of electrons to the emitter


30


. The FET


50


includes an n-tank


52


formed in the surface of the substrate


32


beneath the emitter


30


. The n-tank


52


serves as a drain for the FET


50


and may be formed via conventional masking and ion implantation processes. The FET


50


also includes a source


54


and a gate electrode


56


. The gate electrode


56


is separated from the substrate


32


by a gate oxide


57


and a field oxide layer


58


. The emitter


30


is typically about a micron tall, and several emitters


30


are generally included together with each n-tank


52


, although only one emitter


30


is illustrated.




The substrate


32


may be formed from p-type silicon material having an acceptor concentration N


A


ca. 1-5×10


15


/cm


3


, while the n-tank


52


may have a surface donor concentration N


D


ca. 1-2×10


16


/cm


3


.




In operation, the extraction grid


38


is biased to a voltage on the order of 40-80 volts, although higher or lower voltages may be used, while the substrate


32


is maintained at a voltage of about zero volts. Signals coupled to the gate


56


of the FET


50


turn the FET


50


on, allowing electrons to flow from the source


54


to the n-tank


52


and thus to the emitter


30


. Intense electrical fields between the emitter


30


and the extraction grid


38


then cause field emission of electrons from the emitter


30


. A larger positive voltage, ranging up to as much as 5,000 volts or more but often 2,500 volts or less, is applied to the faceplate


20


via the transparent conductive layer


24


. The electrons emitted from the emitter


30


are accelerated to the faceplate


20


by this voltage and strike the cathodoluminescent layer


26


. This causes light emission in selected areas, ie., those areas adjacent to where the FETs


50


are conducting, and forms luminous images such as text, pictures and the like. Integrating the FETs


50


in the substrate


32


to provide an active display


10


(i.e., a display


10


including active circuitry for addressing and providing control signals to specific emitters


30


, etc.) yields advantages in size, simplicity and ease of interconnection of the display


10


to other electronic componentry.




When the emitted electrons strike the cathodoluminescent layer


26


, compounds in the cathodoluminescent layer


26


dissociate. This causes outgassing of materials from the cathodoluminescent layer


26


. When the outgassed materials react with the emitters


30


, a barrier height of the emitters


30


may increase. When the emitter barrier height increases, the emitted current is reduced. This reduces the luminance of the display


10


.




Residual gas analysis indicates that the dominant materials outgassed from some display cathodoluminescent layers


26


include oxygen and hydroxyl radicals. This leads to oxidation of the emitters


30


and especially emitters


30


formed from silicon. Silicon emitters


30


are useful because they are readily formed and integrated with other electronic devices on silicon substrates. Electron emission is reduced when silicon emitters


30


oxidize. This degrades performance of the display


10


.




Therefore there is a need for a way to prevent degradation, and especially oxidation, of emitters


30


used in displays


10


.




SUMMARY OF THE INVENTION




In accordance with an aspect of the invention, a field emission display has a plurality of emitters including titanium silicide nitride. The plurality of emitters is formed on a substrate that is part of a baseplate. A dielectric layer is formed on the substrate, a semiconductor device formed in or on the substrate for controlling the flow of electrons to the emitters, and the plurality of emitters. The display includes an extraction grid formed in a plane defined by tips of the plurality of emitters. The extraction grid includes an opening surrounding and in close proximity to each tip of the plurality of emitters. Significantly, the tips include titanium silicide nitride.




As a result, the emitters are markedly more resistant to reaction with compounds released from the cathodoluminescent layer by electron bombardment than are silicon emitters. This results in a robust display that resists emitter degradation the emitters may also exhibit increased emissivity due to reduced work function provided by titanium silicide nitride compared to the work function of silicon.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a simplified side cross-sectional view of a portion of a display including a faceplate and a baseplate in accordance with the prior art.





FIG. 2

is a simplified side cross-sectional view of a portion of a display according to an embodiment of the present invention.





FIG. 3

is a simplified side cross-sectional view of a portion of a baseplate for the display at one stage in manufacturing according to an embodiment of the present invention.





FIG. 4

is a simplified side cross-sectional view of a portion of a baseplate for the display at a later stage in manufacturing according to an embodiment of the present invention.





FIG. 5

is a simplified side cross-sectional view of a portion of a baseplate for the display at a still later stage in manufacturing according to an embodiment of the present invention.





FIG. 6

is a flow chart of a process for manufacturing a baseplate for the display according to an embodiment of the present invention.





FIG. 7

is a simplified block diagram of a computer using the emitter according to an embodiment of the present invention.











DETAILED DESCRIPTION OF THE INVENTION





FIG. 2

is a simplified side cross-sectional view of a portion of a field emission display


10


′ in accordance with one embodiment of the present invention.

FIG. 2

is not drawn to scale. Many of the components used in the display


10


′ shown in

FIG. 2

are identical to components used in the display


10


of FIG.


1


. Therefore, in the interest of brevity, these components have been provided with the same reference numerals, and an explanation of them will not be repeated.




It has been discovered that coating at least the tips of the emitters


30


with a titanium silicide nitride layer


70


provides significant advantages when the emitter


30


is used in the display


10


′. In one embodiment, the advantages include improved resistance to chemical poisoning of the emitters


30


from materials that are outgassed from the cathodoluminescent layer


26


in response to electron bombardment. This provides improved lifetime for the emitter


30


and therefore for the display


10


′ incorporating the emitter


30


. Coating at least tips of the emitters


30


with the titanium silicide nitride layer


70


also provides a decreased work function compared to silicon emitters


30


, resulting in increased current from each emitter


30


together with reduced turn-on voltage.





FIGS. 3 through 6

illustrate a portion of the baseplate


21


′ for the display


10


′ of

FIG. 2

at various stages in manufacturing according to an embodiment of the present invention. As shown in

FIG. 3

, an emitter


30


has been fabricated on the substrate


32


, and the substrate


32


and the emitters


30


are coated with the dielectric layer


34


. An extraction grid


38


including a conductive layer is then formed on the dielectric layer


34


. The extraction grid


38


may be formed, for example, as a thin layer of doped polysilicon, however, other materials can be employed.




As shown in

FIG. 4

, a conventional chemical-mechanical polish is carried out to remove the “hill” of dielectric material


34


and extraction grid


38


immediately above the tip of the emitter


30


. This is typically carried out via a potassium hydroxide solution that incorporates suspended particles of controlled size, which may be silicon particles. It is important that this chemical-mechanical polish not damage the tips of the emitters


30


, i.e., that the polishing process stops short of reaching these tips.




With reference to

FIG. 5

, following the chemical-mechanical polishing operation, the extraction grid


38


is used as a mask for etching the dielectric layer


34


to expose at least the tips of the emitters


30


in the openings


40


. This has the advantage of not requiring a separate photoresist application, exposure and development, thus reducing labor content and materials requirements. This also promotes increased yields by reducing the number of processing steps. When silicon dioxide is used to form the dielectric layer


34


, this step may be carried out by etching the wafer in a conventional buffered aqueous hydrogen fluoride oxide etch or BOE.




As also shown in

FIG. 5

, following etching of the dielectric layer


34


to expose at least the tip of the emitter


30


, a titanium silicide nitride layer


70


is formed on the emitter


30


by a process explained below with reference to FIG.


6


.





FIG. 6

is a flow chart of a process


80


for manufacturing emitters


30


according to an embodiment of the present invention. The substrate


32


having a plurality of the emitters


30


has been previously formed, and the surface of the substrate


32


and the emitters


30


have been previously coated with the dielectric layer


34


. The extraction grid


38


has been previously deposited, and the chemical-mechanical polish and etch have been previously carried out to expose at least the tips of the emitters


30


. Optional step


82


removes any native oxide from the emitters


30


, via, e.g., a conventional hydrogen fluoride etching step. Other methods for removal of native oxide are also suitable for use with the present invention, provided that the oxide removal process does not blunt the tips of the emitters


30


.




In step


84


, a layer of titanium is formed over the surface of the extraction grid


38


and also over at least the tips of the emitters


30


. The layer of titanium may be applied in any of several ways, including evaporation, chemical vapor deposition and the like, however, sputtering is preferred. The layer of titanium should not be so thick as to distort the tips of the emitters


30


and should be thick enough to ensure coating of the tips, i.e., to obviate formation of pinholes in the titanium layer. In one embodiment, the titanium layer is on the order of five hundred angstroms thick.




The titanium layer is then reacted in step


86


with the silicon forming the emitter


30


to form titanium silicide or TiSi


2


. This may be realized by rapid thermal annealing of the emitters


30


and the titanium layer, for example, at 670° C. for 30 seconds in nitrogen. Unreacted titanium may then be removed in optional step


88


by conventional etching, for example, with NH


4


OH:H


2


O


2


:H


2


O=1:1:5.




The titanium silicide is then reacted with nitrogen to form the titanium silicide nitride layer


70


(

FIG. 5

) in step


90


. This may be effected by rapid thermal annealing at a suitable temperature, such as 1050° C., in ammonia for a suitable period, such as 90 seconds. The process


80


then ends and other conventional processing steps for forming field emission displays


10


′ are carried out.




It will be understood that while rapid thermal annealing is employed in one embodiment, other forms of heat treatment may be used to react the titanium to form titanium silicide and to react the titanium silicide to form titanium silicide nitride. For example, titanium and silicon may be reacted by heating in an oven at 700° C. for half an hour. It will also be understood that emitters


30


including titanium silicide nitride may be made via other processes.




The process


80


illustrated via

FIG. 6

results in an emitter body


30


that is coated with a titanium silicide nitride layer


70


. This provides several advantages. The titanium silicide nitride layer


70


that is formed resists attack by BOE, which is useful in subsequent processing steps when BOE is used to pattern subsequent layers. Measurements of the titanium silicide nitride layers


70


formed by the process


80


provide sheet resistivities on the order of 3.4 ohms per square.




Emitters


30


having a titanium silicide nitride surface layer


70


thus provide lower turn-on voltages and higher currents compared with silicon. Moreover, titanium silicide nitride is very resistant to oxidation, especially when compared to silicon, leading to improved performance and a more robust emitter


30


. However, it will be understood that the emitter


30


may be coated with a work function decreasing layer formed by other materials. Additionally, forming the layer


70


from a layer that is metallurgically alloyed to the emitter


30


provides a robust emitter


30


having reproducible characteristics.




The process


80


does not require any photolithographic steps and therefore has minimal impact on labor content and materials requirements. The process


80


is also consistent with increased yields due to simplification of device processing. It is completely self aligned, promoting higher yields by avoiding some error sources.





FIG. 7

is a simplified block diagram of a portion of a computer


100


using the display


10


′ fabricated as described with reference to

FIGS. 2 through 6

and associated text. The computer


100


includes a central processing unit


102


coupled via a bus


104


to a memory


106


, function circuitry


108


, a user input interface


110


and the display


10


′ including the emitters


30


having the titanium silicide nitride layer


70


according to the embodiments of the present invention. The memory


106


may or may not include a memory management module (not illustrated) and does include ROM for storing instructions providing an operating system and a read-write memory for temporary storage of data. The processor


102


operates on data from the memory


106


in response to input data from the user input interface


110


and displays results on the display


10


′. The processor


102


also stores data in the read-write portion of the memory


106


. Examples of systems where the computer


100


finds application include personal/portable computers, camcorders, televisions, automobile electronic systems, microwave ovens and other home and industrial appliances.




Field emission displays


10


′ for such applications provide significant advantages over other types of displays, including reduced power consumption, improved range of viewing angles, better performance over a wider range of ambient lighting conditions and temperatures and higher speed with which the display can respond. Field emission displays


10


′ find application in most devices where, for example, liquid crystal displays find application.




Although the present invention has been described with reference to specific embodiments, the invention is not limited to these embodiments. Rather, the invention is limited only by the appended claims, which include within their scope all equivalent devices or methods which operate according to the principles of the invention as described.



Claims
  • 1. A field emission display baseplate, comprising:a substrate; a plurality of emitters formed on the substrate; and a layer of material comprised of titanium silicide nitride, the layer of material decreasing a work function of the emitters formed on at least a portion of each of the emitters, and providing oxidation resistance and resisting etching by BOE or HF.
  • 2. The baseplate of claim 1, further comprising:a dielectric layer formed on the substrate, the dielectric layer including an opening surrounding each of the plurality of emitters; and a conductive extraction grid formed on the dielectric layer, the extraction grid substantially in a plane defined by tips of the plurality of emitters and including an opening surrounding each of the plurality of emitters.
  • 3. A field emission display baseplate, comprising:a substrate; a plurality of emitters formed on the substrate; a layer of titanium silicide nitride formed on each of the emitters; dielectric means formed on the substrate, the dielectric means including an opening surrounding each of the plurality of emitters; and extraction grid means including conductive material formed on the dielectric means, the extraction grid means substantially in a plane defined by tips of the plurality of emitters and including an opening surrounding each of the plurality of emitters.
  • 4. The baseplate of claim 3 wherein the emitters are formed from silicon.
  • 5. The apparatus of claim 3 wherein the dielectric means comprises silicon dioxide.
  • 6. The apparatus of claim 3 wherein the extraction grid means comprises a layer of doped polysilicon.
  • 7. A field emission display baseplate, comprising:a substrate; and a plurality of emitters formed on the substrate, each emitter having a titanium silicide nitride layer disposed thereon, the emitters having a work function below that of silicon and providing oxidation resistance and resisting etching by BOE or HF.
  • 8. The baseplate of claim 7, further comprising:a dielectric layer formed on the substrate and the plurality of emitters; and an extraction grid formed on the dielectric layer, the extraction grid including an opening surrounding each of the plurality of emitters.
  • 9. The baseplate of claim 7 wherein the titanium silicide nitride layer has a thickness of about two hundred angstroms.
  • 10. The baseplate of claim 7 wherein the substrate comprises p-type silicon.
  • 11. The baseplate of claim 10, further including a FET comprising:a n-tank disposed beneath one or more of the plurality of emitters, the n-tank forming a drain for the FET; a field oxide formed at an edge of the n-tank; a gate oxide extending from the field oxide onto the substrate; a gate electrode formed on the field oxide and gate oxide; and a source electrode formed at an edge of the gate oxide remote from the n-tank.
  • 12. A computer system comprising:a central processing unit; a memory device coupled to the central processing unit, the memory device storing instructions and data for use by the central processing unit; an input device; and a display, the display including: a cathodoluminescent coated faceplate having a planar surface; a plurality of emitters formed on a surface of a substrate, each of the emitters having an outer surface formed by a layer of titanium silicide nitride; a dielectric layer formed on the substrate, the dielectric layer including an opening surrounding each of the emitters; and a conductive extraction grid formed on the dielectric layer, the extraction grid substantially in a plane defined by tips of the plurality of emitters and including an opening surrounding each of the emitters.
  • 13. The computer system of claim 12 wherein each of the emitters is coupled to a drain of a drive field effect transistor.
GOVERNMENT RIGHTS

This invention was made with government support under Contract No. DABT63-93-C-0025 awarded by Advanced Research Projects Agency (ARPA). The government has certain rights in this invention.

US Referenced Citations (4)
Number Name Date Kind
5229682 Komatsu Jul 1993
5401676 Lee Mar 1995
6008063 Derraa Dec 1999
6028322 Moradi Feb 2000
Non-Patent Literature Citations (5)
Entry
Michiaki Endo et al., “Fabriction of transition metal nitride field emitters,” Applied Surface Science, 94/95:113-116, 1996.
Chalamala, Babu R. and Bruce E. Gnade, “Fed Up With Fat Tubes,” IEEE Spectrum, Apr. 1998, pp. 42-51.
Eung Joon Chi et al., “Electrical Characteristics of Metal Silicide Field Emitters,” 9th International Vacuum Microelectronics Conference, St. Petersburg, 1996, pp. 188-191.
Masayuki Nakamoto et al., “Low Operation Voltage Field Emitter Arrays Using Low Work Function Materials Fabricated by Transfer Mold Technique,” EEDM, pp. 297-300, 1996.
Yukihiro Morimoto et al., “Analysis of Gas Release From Vitreous Silica,” Journal on Non-Crystalline Solids, 139:35-46, 1992.