Top coated PVC articles

BACKGROUND OF THE INVENTION
Polyvinylchloride (PVC) is a widely used plastic in industrial and consumer products. Rigid PVC is used for structural members, piece parts, pipes and tubing, etc. Semirigid PVC is widely used for flooring, siding and other building materials. Flexible PVC is used widely for fabrics, wall coverings and electrical wire insulation. Other uses are too numerous to mention.
Flexible PVC is made using a range of types and amounts of plasticizers. These materials soften the normally rigid PVC and impart the desired degree of flexibility. However, the plasticizers are rarely very soluble in PVC, and they tend to migrate out of the host material and enter the environment. This is an important consequence if the plasticizer material is environmentally unsafe or unwanted. Migration is also a problem from a cosmetic standpoint because the plasticizers commonly used absorb stains during use and migrate back into the surface of the plastic along with the staining substance where they cannot be removed conveniently but are nevertheless visible.
Among the important uses of flexible PVC mentioned earlier is wire insulation. The following description is framed in terms of this use, but it should be understood that virtually all uses for flexible PVC share common circumstances within the context of this invention. Therefore the invention is to be construed as directed toward any article of manufacture comprising plasticized PVC.
Electrical wire insulated with polyvinylchloride (PVC) is used widely for many applications and often for plug-in cords for consumer appliances. It is also used widely for cords connecting telephone station equipment with wall or floor line junctions. In these applications the cords typically have high visibility coupled with high exposure to wear, staining and environmental degradation. Black cords suffer little from staining and only moderately from degradation. However, the increasing demand for cords that are coordinated in color with appliances or interior decor places stringent demands on the PVC insulation. Staining and discoloration are significant problems, especially with equipment that receives heavy use and has a long service life. To reduce inventory necessary to provide a full range of color selection it is sometimes desirable to offer a universal cord with insulation made of clear plastic. Clear plastic insulation has been found to have more market acceptance than black or a neutral color. However, the clear plastic insulation also suffers from the problems enumerated before.
As indicated earlier, staining of light colored and clear PVC cords is often due to the plasticizer required to impart flexibility to the PVC. The stain combines with the plasticizer and migrates back into the plastic where it cannot be removed, even with abrasive type cleaners, but can still be seen.
In accordance with one aspect of this invention the problem of staining is overcome by coating the clear or colored PVC with a plasticizer barrier to prevent interaction between the plasticizer and a potential staining substance. The barrier is a coating of a polyester blend that itself is clear as applied to the cord, and which adheres well to plasticized PVC, is abrasion resistant, flexible, has long term stability against heat and light, can be processed by conventional extrusion, and is itself resistant to stains and discoloration.
While this description has centered about PVC insulated electrical cords, and in particular, telephone mounting cords, it should be understood that the coating materials described and claimed are similarly useful for any PVC product. Top coatings for vinyl upholstery and fabrics are typical of such related uses. These applications often involve the same kind of performance factors for the PVC that are enumerated above.
SUMMARY OF THE INVENTION
Superior top coatings for PVC are polyesters, especially a polyester blend of a terpolymer of tetramethylene glycol reacted with terephthalic acid, isophthalic acid, and azelaic acid, and a copolymer of ethylene glycol reacted with terephthalic acid and sebasic acid.
In an effort to demonstrate the barrier effect tests were conducted with a large number and variety of plastic coating materials. In the course of the investigation other advantages were revealed. For example, it was found that the pull strength of a connector attached to a polyester coated PVC cord was significantly improved over the uncoated cord. During investigations of processing the material it was found that the top-coating of the invention can be extruded in a dual line extrusion system along with the underlying PVC insulation and, when properly quenched, remains essentially clear. This contrasts with the common tendency of extruded plastics to crystallize in a structure that is, to varying degrees, opaque. The top coating was also found to improve the scuff resistance and the crush resistance of the PVC cord. Moreover, the use of a plasticizer barrier allows greater flexibility in the choice of plasticizers used for the PVC. Plasticizers that are hazardous because they migrate to the surface of the plastic and mar furniture finish, or evaporate and thereby contaminate the atmosphere, or are hazardous to the skin upon handling, can in many cases be used safely if the barrier layer is applied. For example, phosphate plasticizers are not only useful for imparting flexibility to PVC, but are known to be effective in retarding smoke that is evolved when PVC burns. However, phosphates are environmentally hazardous. Prevention of environmental contamination by a plasticizer barrier restores the potential of this valuable plasticizer for safe use.

BRIEF DESCRIPTION OF THE DRAWING
FIGS. 1A-1B are cross sections of typically insulated wire configurations coated with polyester top coats according to one embodiment of the invention;
FIG. 2 is a schematic representation of an extrusion line useful for applying the coatings of the inventors; and
FIG. 3 is a sectional view of the extrusion head of FIG. 2.

In arriving at the top coating formulation of the invention several different types of polymers were investigated. In addition a wide range of molecular weights were evaluated for each polymer-type studied. The candidates were evaluated on the basis of the following properties:
(1) Barrier to plasticizer migration,
(2) Gloss,
(3) Clarity,
(4) Adhesion to plasticized PVC,
(5) heat and light stability,
(6) Abrasion resistance,
(7) Flexibility.
The types of polymers evaluated consisted of:
(1) Nylons, nylon copolymers, nylon blends,
(2) Polyolefins,
(3) Low plasticized vinyls,
(4) Polyurethanes,
(5) Acrylics, acrylic blends,
(6) Acrylic--vinyl blends,
(7) Polyesters, polyester blends.
The nylons and polyolefins tested were shown to be unsatisfactory as top-coating polymer candidates as a result of poor adhesion performance as evidenced by flex testing experiments, and were not evaluated further. The degree to which plasticizer migration is retarded was measured by soaking top-coated PVC plaques plasticized with DOP (Di-2-ethylhexyl phthalate) in hexane over a 10 day period. The DOP content of the extractant was monitored daily by chromatography. The following table summarizes the barrier properties of top-coat candidates from each polymer class. The greater of percent loss of DOP plasticizer, the less efficient the barrier properties to the top-coat. All samples are normalized against the uncoated control plaque which was rated as 100 percent plasticizer loss.
TABLE 1______________________________________ PercentCoating PlasticizerDesignation Description Loss______________________________________Uncoated Plasticized PVC 100Control 60 phr DOPLow Plasticizer Plasticized PVC 87Vinyl-1 40 phr DOPLow Plasticizer Plasticized PVC 65Vinyl-2 30 phr DOPLow Plasticizer Plasticized PVC 43Vinyl-3 20 phr DOPU-493 MMW Ether Aliphatic 49 Urethane ANFX 3699 MMW Ether Aliphatic 33 Urethane BU6729 MMW Ether Aliphatic 48 Urethane CU10-011 MMW Ether Aliphatic 45 Urethane DLR 18-1 HMW Ether Aliphatic 31 UrethaneU-314 MMW Ester Aliphatic 42 Urethane ALR 18-8 MMW Ester Aliphatic 58 Urethane BU-344 HMW Ester Aromatic 67 UrethaneLR 18-3 HMW Ester Aliphatic 25 Urethane ALR 18-4.sub.1 HMW Ester Aliphatic 20 Urethane BLR 18-4.sub.2 MI = 80 HMW Ester 27 Aliphatic Urethane CLR 18-4.sub.3 MI = 130 HMW Ester 35 Aliphatic Urethane DLR 18-4.sub.4 MI = 200 HMW Ester 41 Aliphatic Urethane FElvacite 2009 MMW Methyl 0* Methacrylate AElvacite 2010 MMW Methyl 0* Methacrylate BElvacite 2041 HMW Methyl 0* MethacrylateElvacite 2042 HMW Ethyl 0* MethacrylateElvacite 2044 HMW n-Butyl 14 MethacrylateElvacite 2013 LMW Methyl/n-Butyl 21 CopolymerPlasticized 2009 25 phr Santicizer 160 29Elvacite 6014 MMW Methyl Copolymer 246014/2042 (2:1) Acrylic Blend A 17Acrylic 17c Acrylic Blend B 112041/VUHH (1:2) Acrylic-Vinyl Blend A 292042/VUHH (2:1) Acrylic-Vinyl Blend B 192009/VUNS (2:1) Acrylic-Vinyl Blend C 12158-1 (3:2) Acrylic-Vinyl Blend D 10158-2 (1:1) Acrylic-Vinyl Blend E 21158-3 (2:3) Acrylic-Vinyl Blend F 17158-4 (1:3) Acrylic-Vinyl Blend G 75Polyester 17B Polyester Copolymer A 0Polyester 17F Polyester Copolymer B 4Polyester 17H Polyester Copolymer 0 Blend A & BPE 200 LMW Polyester A 7PE 222 LMW Polyester B 9Polyester 1671 LMW Polyester 4 Terpolymer APolyester 1296 LMW Polyester 6 Terpolymer BPolyester 5126 MMW Polyester 2 Terpolymer APolyester 5146 MMW Polyester 3 Terpolymer BPolyester 4980 HMW Polyester 0 Copolymer APolyester 400 HMW Polyester 0 Copolymer BPolyester 415 HMW Polyester 0 Copolymer C5126/1296 (1:1) Polyester Blend A 35126/1296 (2:1) Polyester Blend B 35126/1296 (3:1) Polyester Blend C 14980/415 (1:1) Polyester Blend D 05126/415 (2:1) Polyester Blend E 05126/415 (3:1) Polyester Blend F 05126/415 (4:1) Polyester Blend G 0______________________________________ *Cracked - must be plasticized or blended with vinyl.
The following conclusions were drawn from the migration data:
(1) Low plasticized vinyl coatings exhibit unacceptable plasticizer migration resistance coupled with significantly limited processing performance and physical properties.
(2) Urethanes reduce migration by approximately 50 percent. As can be seen in samples LR 18-4.sub.1 -LR 18-4.sub.4 (MI increases, MW decreases), the higher molecular weight candidates exhibited improved plasticizer migration resistance as compared to lower molecular weight urethane candidates.
(3) Suitable acrylics, acrylic blends and acrylic-vinyl blends improve migration resistance by as much as 90 percent; barrier properties are improved as MW increases and vinyl content decreases. Such coatings show top-coat potential.
(4) Polyesters proved to be the most impervious polymer-type to plasticizer migration as measured by extraction. HMW polyesters and polyester blends showed as much as 100 percent improvement in barrier properties.
The resistance to cigarette smoke permeation was also investigated as a means for evaluating the stain resistance of various potential top-coat materials, Top-coated plaques were placed in a smoke chamber at a constant smoke density for 96 hours. Samples were then washed in soap and water and rated by the change in yellowness (smoke permeation). The samples were measured for yellowness on a Hunter D25D3 colorimeter with (M) head reflectance attachment. As can be seen in Table 2, the same relative barrier properties are attributed on the candidates as in the extraction work. HMW polyesters and polyester blends proved to be the most effective barrier to cigarette smoke permeation serving as another measure of top-coat effectiveness.
TABLE 2______________________________________Cigarette Smoke Staining (Plaque)Description Smoke Pickup______________________________________Plasticized PVC (60 phr) 100Plasticized PVC (40 phr) 96Plasticized PVC (30 phr) 71Plasticized PVC (20 phr) 56MMW Ether Aliphatic Urethane B 58HMW Ester Aliphatic Urethane A 42HMW Ester Aliphatic Urethane B 34Acrylic Blend B 16Acrylic/Vinyl Blend C 24Acrylic/Vinyl Blend H 30Acrylic/Vinyl Vinyl Blend B 54Acrylic/Vinyl Blend D 22Polyester Copolymer A 19Polyester Copolymer C 11Polyester Copolymer Blend A & C 12MMW Polyester terpolymer A 5Polyester Blend B 6Polyester Blend E 0Polyester Blend F 0______________________________________
Top-coated clear samples were stained with black ball point pens and red lipstick and allowed to stand at room temperature for 96 hours. Then the samples were wiped with towels soaked in soap and water. Table 3 shows the results of the evaluation. HMW acrylics, acrylic-vinyl blends, polyesters and polyester blends proved to be superior, (0=excellent, 5=unacceptable) (3=marginal).
TABLE 3______________________________________Ink and Lipstick Staining Relative Rating*Description Ink Lipstick______________________________________Plasticized PVC (60 phr) 5 5PVC (40 phr) 4 4PVC (30 phr) 4 4PVC (20 phr) 4 3MMW Ether Aliphatic Urethane B 3 5HMW Ester Aliphatic Urethane A 2 5HMW Ester Aliphatic Urethane B 3 4Acrylic Blend B 2 0Acrylic/Vinyl Blend C 1 0Acrylic/Vinyl Blend H 1 1Acrylic/Vinyl Blend B 1 0Acrylic/Vinyl Blend D 0 0Polyester Copolymer A 0 0Polyester Copolymer C 0 0Polyester Copolymer Blend A & C 0 0MMW Polyester terpolymer A 0 0Polyester Blend B 1 0Polyester Blend E 0 0Polyester Blend F 0 0______________________________________ *0 = virgin, 5 = deeply and permanently stained.
It was concluded from the above testing that HMW polyesters serve most effectively in protecting PVC from the environment. In particular, a blend designated VAR 5825 was found to provide excellent barrier and stain resistant qualities.
VAR 5825 is a code designation for a polyester blend of: (1) a terpolymer of tetramethylene glycol reacted with an acid mixture of 70% terepthalic acid, 10% isopthalic acid, and 20% azelaic acid and (2) a copolymer of ethylene glycol reacted with 50% terephthalic acid and 50% sebasic acid. Obviously the proportions of the reactants can vary within reasonable limits without affecting materially the functional properties of the polyester blend. Specifically, it would be expected that the polyester would exhibit the desired characteristics when the above reactants in each of the polymers are varied over ranges of the order of .+-.50% of the recited percentages.
Ingredient 1 above will be referred to herein as VAR 5126 and ingredient 2 as VMR 415. Both materials are available from Goodyear Tire and Rubber Co.
The specifics of the preparation of the terpolymer VAR 5126 are contained in U.S. Pat. No. 3,423,281 and details on the preparation of VMR 415 appear in U.S. Pat. Nos. 2,765,250 and 2,765,251.
To demonstrate the importance of the blend ratio of the two constituents various ratios were made and tested from the standpoint of plasticizer barrier effectiveness, staining, and discoloration. The test data appears in the following tables. Table 4 indicates the plasticizer permeation resistance in terms of plasticizer weight gain for seven polyester samples, each measured with respect to three different commonly used plasticizer materials. The first two samples were of the unblended constituents and the remaining samples of blends using various ratios of the constituents ranging from 1:1 to 5:1.
TABLE 4______________________________________PLASTICIZER PERMEATION RESISTANCE Plasticizer (% Wt. Gain) Santicizer Santicizer KrontexSample 141 148 100______________________________________VFR 5126 11.10(10.70)** 10.79 13.21VMF 415 15.70(15.12) 15.25 17.94(5126/415) Blends1:1 13.92(12.97) 13.80 16.102:1 9.32(7.50) 9.15 10.133:1 6.66(3.20) 6.15 7.414:1 8.90(6.60) 8.30 9.455:1 12.05(11.65) 11.91 14.25______________________________________ *Non-oriented 5 mil coating films **Coating films after orientation
It is evident from the results that blends having ratios of from 2:1 to 4:1 are most effective.
Staining in the same group of samples was measured by exposing the samples to dense cigarette smoke for a period of 48 hours at a temperature of 100.degree. F. The results are given in the following table in terms of an arbitrary index of discoloration.
TABLE 5______________________________________CIGARETTE SMOKE PICKUP (48 Hrs., 100 E.)Samples* .DELTA. Yellowness Index (%)______________________________________VFR 5126 36VMF 415 68(5126/415)Blends1:1 432:1 273:1 154:1 245:1 39______________________________________ *Oriented coating films
Again it is evident that the blends with ratios of 2:1 to 4:1 are most effectve.
Discoloration on aging was measured by an accelerated test in which oven aging was used to simulate long term exposure to air. In this case only one blend was tested, that indicated as VAR 5825, which is a blend with a ratio of VFR 5126/VMF 415 of 3:1. The data is given in the following table. The results are terms of light transmission after aging at 200.degree. F. for 200 hours.
TABLE 6______________________________________LIGHT TRANSMISSION AFTER OVEN AGING** (%) TransmissionSample* Int. Final______________________________________VFR 5126 79 61VMF 415 83 67VAR 5825 85 80______________________________________ *Oriented polymer films **200 hrs. at 200 F.
It is clear that the blend ages better in this test than either of the constituents.
Proper extrusion of the coating polymer is important in obtaining the correct physical requirements of the universal mounting cord. Quench temperature, draw down ratio, line speed and polymer melt temperature play an important role in determining end product properties. To this end an extrusion profile of 350.degree. F. for both the top-coating and the PVC is etilized, which ensures maximum adhesion between the polymers and limits degradation of the vinyl. Optimization of the extrusion parameters enable production of a clear coating at a line speed of 360'/min, quench water temperature of 50 degrees F, and a draw down ratio of 4:1. Upon heat setting or oven aging at 170 degrees F. no large crystal sites are formed, maintaining a clear polyester film. This is unexpected since both the VMF 415 and VFR 5126 coating components become opaque due to growth of large crystals after extrusion. The VAR 5825 coating shows no such growth and maintains clarity. Normally orientation of such polymers is not achieved above the polymer melting point (334.degree. F.), however, the blend achieves a degree of orientation unsuspected from the performance of either of the components.
VAR 5825 can be stabilized against heat and light degradation via a system consisting of one-half percent by weight Irganox 1093, a high molecular weight hindered phenolic antioxidant, and one percent by weight Tinuvin P, a substituted hydroxyphenyl benzothiazole UV absorber. This stabilizer design was selected not only because of its performance but also because both of the ingredients have been tested and dermatologically cleared for usage based on human patch testing. The exact chemical structures are as follows: Irganox 1093 is o-di-n-octadecyl-3, 5-di-tert-butyl-4 hydroxy-benzyl phosphonate; Tinuvin P is 2(2'-hydroxy-5'-methyl phenyl) benzotriazole. However, other suitable stabilizers can be used as well. The barrier properties do not appear to rely on either stabilizer just mentioned but rather on the polyester constituent.
The concentration of stabilizer used was predicated on equaling or improving the heat aging and UV aging characteristics of the underlying PVC material. Oven aging tests over the temperature range of 150 degrees F.-290 degrees F., show the polyester blend (VAR 5825) to yellow at least ten times slower than the vinyl formulation. UV aging via RS sunlamp show the polyester blend very similar or just marginally worse than the vinyl formulations. This can be improved by the addition of more Tinuvin P to the polyester formulation. Physical properties of the coating polymer are shown in Table 7.
TABLE 7______________________________________Physical PropertiesProperty VAR 5825 Method______________________________________Specific Gravity 1.26 ASTM D-792Shore D Hardness 59 ASTM D-785Tensile Strength (psi) 3,280 ASTM D-412Elongation (%) 360 ASTM D-573LTB (degree C.) >-20 ASTM D-746mp (degree C.) 160 DSCTorsional Modulus (psi) at 23 degrees C. 6,940 at -10 degrees C. 44,760 at -20 degrees C. 68,000Stiffness Modulus (psi) 28,900 ASTM D-747Crystallization, degrees C.(onset)Melt-Slow Cool 143Fast Quench-Slow Heat 23______________________________________
Table 8 shows the chemical resistance of the top-coating material, VAR 5825 to a wide range of substances from household cleaning items such as sodium hypochlorite and perchloro ethylene (dry cleaning fluid); common petroleum products such as, gasoline, ethanol, hexane, mineral oil; plasticizers such as DOP, Santicizer 141, Santicizer 148; and highly active solvents such as acetone, toluene, phenol and benzene. As can be seen the top-coating shows stability to all materials under the severe test conditions while being swollen only by the active solvents and these are not normally encountered in service. Extraction of the plasticizer system through the top-coating or softening of the coatings by common household items seems unlikely based on these results.
TABLE 8______________________________________Chemical ResistanceConditions: 5 mil VAR 5825 film, immersed in concentratedsolution, RmT C, wiped dry, weighed. Exposure (%)Chemical Time Wt. Gain Appearance______________________________________Acetone 4 weeks 5.76 slightly swollenConc. Ammonium 4 weeks <1.00 unchangedHydroxideBenzene 4 weeks 3.26 slightly swollenDiethyl Ether 4 weeks <1.00 unchangedDOP (plasticizer) 4 weeks 0.00 unchangedHexane 4 weeks 1.35 unchangedH.sub.2 O 4 weeks 0.00 unchanged50% Aqueous Ethanol 4 weeks <1.00 unchangedGasoline 4 weeks 0.00 unchangedConc. HCl 4 weeks <1.00 stained brown28% Hydrogen 4 weeks <1.00 unchangedPeroxideMineral Oil 4 weeks 0.00 unchangedPerchloro Ethylene 4 weeks <1.00 unchangedPhenol 4 weeks 8.96 swollen10% Sodium 4 weeks <1.00 unchangedChloride31/2% Sodium 4 weeks <1.00 unchangedHypochlorite30% Sulfuric Acid 4 weeks <1.00 unchangedSanticizer 141 1 week <1.00 unchanged(plasticizer)Santicizer 148 1 week <1.00 unchanged(plasticizer)Toluene 4 weeks 1.80 unchanged______________________________________
To demonstrate the manufacturability of electrical cords coated in accordance with one embodiment of the invention an engineerinng dual extrusion pilot line was developed as shown in FIG. 2 consisting of individual barrel pay-off positions for insulated conductors 90, (Hytrel 7246 silver pigmented insulated tinsel conductors) one PVC extruder 91 and a coating extruder 92 connected to a dual purpose head, a water cooling trough 93 containing chilled quench water (50.degree. F.) and a capstan 94 equipped with a barrel take-up system 95. Dual extrusion of the polyester top-coating polymer utilized two separate extruders, one for metering the clear PVC jacket compound and the other for metering the polyester coating. The PVC extruder design consisted of a 31/2 inch diameter machine having a (24/1) L/D barrel and a 4:1 compression ratio screw. The polyester coating extruder consisted of a 11/2 inch diameter machine having a (30/1) L/D barrel and a 1.7:1 compression ratio screw. Both extruders were connected to a common head containing a dual cavity tooling design. The dual extruding head is shown in FIG. 3.
The function of the dual cavity head 40 is to simultaneously (1) pressure extrude the PVC jacket compound 41 completely encapsulating the four parallel insulated conductors 42 in the primary cavity, while (2) applying a continuous coating of polyester polymer 43 over the entire PVC jacket conductor substrate in the secondary cavity 44. The die configuration of the primary cavity has an oval shape with an orifice dimension of 0.099.times.0.199 inches. The coating die also involves an oval shape design having an orifice dimension of 0.099.times.0.208 inches. The coating die was notched in order to develop a ridge in the coating polymer as a tracer for identification of conductors for termination. pg,23
Operating conditions for the polyester-PVC dual extrusion coating line were:
______________________________________TEMPERATURE PROFILES PolyesterMain PVC Extruder Coating Extruder______________________________________Zone 1 (feed) 350 degrees F. 330 degrees F.Zone 2 350 degrees F. 340 degrees F.Zone 3 350 degrees F. 350 degrees F. Crossover TubeZone 4 350 degrees F. 365 degrees G.(dual head) 370 degrees F. 370 degrees F.Screw Speed 16 rpm 25.0 rpmAir Gap-Distance between die and quench water (4) inchesLine Speed-300 fpmChilled Water 50 degrees F. (in cooling trough)PVC Jacket type-458 clear compoundPolyester Coating-Polyester blend VAR 5825 (Goodyear)______________________________________
The polyester coating polymer undergoes a fairly rapid transition between liquid and solid phases. Crystallization rate and spherulitic structure of the coating polymer is basically a function of temperature difference and rate of quench. Spherulites are composite structures made up of crystalline (ordered) and amorphous (disordered) regions in which the crystalline regions or crystallites are arranged in an essentially radial fashion with respect to the center of growth. This arrangement results in an extinction pattern in the shape of a Maltese Cross when viewed in a microscope between crossed polaroids. By optimizing the various quench parameters the desired crystallinity and related physical properties of the polymer were obtained.
Three parameters were initially evaluated including the effects of quench temperature and heat aging on the transmission properties of PE films and the differential scanning calorimeteric readings for quenched and slow cooled samples. The results show that:
(1) A quench temperature of 100 degrees F. or less will generally provide clear polyester. However a quench temperature of less than 50 degrees F. is preferred.
(2) The clear quenched polymer is crystalline, crystallizing at room temperature over a 24 hour period.
(3) Heat aging at higher temperatures does not increase the opacity of the films.
A chilled water quench (50 degrees F.) located approximately four inches from the die was utilized to insure a rapid quench of the coating polymer. This parameter was utilized to reduce the size of the spherulites formed in order to assure a clear flexible coating.
The polyester coating polymer being a hydroscopic material will readily absorb water vapor from the atmosphere. The polymer during extrusion will undergo substantial reduction in melt viscosity when not properly dried.
In order to characterize the polyester VAR 5825 for the effect of moisture, residence time and melt temperature were evaluated via capillary rheometer.
A number of points were obvious:
(1) The pellets must be dry and kept dry to insure against severe process degradation. (2) Long residence time is no problem for dry materials. (3) The melt temperature should be 176 degree C. or higher for sample flow out.
When wet polymer is used the reduction in melt viscosity of the polymers causes a wide variation in polymer delivery from the coating extruder and an imbalance of hydrodynamic pressures in the die cavity between both the type 458 PVC jacket and polyester coating polymer. As a result, extreme variations in coating thickness including partial starving out as well as over application of the coating polymer is realized. In addition, a substantial reduction in melt viscosity and melt pressure of the coating polymer necessitates a significant increase in coating polymer delivery to supplement coating which over penetrates and fuses into the PVC interface. Therefore, it is important to extrude a dry polymer in order to develop and maintain the desired melt viscosity profile. By maintaining a balance of melt pressures between the jacket compound and the polyester coating polymer in the secondary cavity, in conjunction with proper quenching of the extrudate from the die, a clear flexible coating having a thickness of (0.003.+-.0.002) inches was consistently achieved. From this work it is estimated that this technique is easily capable of producing coatings with a thickness in the range 0.001 to 0.005 inches.
The coated clear mounting cord exhibited significant improvement in both physical properties and mechanical performance as compared to that of the uncoated clear mounting cord design.
One piece (6.times.4) plug pull-out strength was measured for both coated and uncoated cordage. This test utilizes a continuous increasing load on a terminated plug. The coated cordage exhibited a pull-out strength of 41 pounds as compared to 33 pounds for the uncoated cordage. This increase in pull-out strength is attributed to the resistance to cold flow, increased tensile properties and hardness of the coating polymer.
A comparison of floor scuff resistance and twist resistance of coated and noncoated cords was performed. The coated cord during scuff resistance testing obtained 4394 cycles as compared to 2540 cycles for the uncoated cord before conductor failure. Twist performance of the coated vs. noncoated cordage resulted in 1373 cycles as compared to 888 cycles before conductor failure. The top-coated cordage demonstrated approximately a 54 percent improvement in twist resistance and 72 percent improvement in scuff resistance over the uncoated cordage.
A comparison of crush resistance of coated vs. uncoated cordage demonstrated, using instron techniques, an improvement of 75 percent over that of the uncoated cordage.
In addition the clear top-coated mounting cord construction was dermatologically acceptable by the conventional environmental test standard.
Extensive evaluation of candidate flame retardant plasticizer systems demonstrated that alky diaryl phosphates exhibit superior vertical burn performance as compared to other systems tested. A new clear PVC jacket compound was developed utilizing about 30% by weight of an alky diaryl phosphate (2-ethylhexyl diphenyl phosphate-Santicizer 141) as the sole plasticizer. The new flame retardant compound exhibited improved low temperature brittleness, oxygen index and heat stability.
As indicated earlier the use of a top-coating enables more flexibility in the choice of the plasticizer used for the polyvinylchloride. For example, even though phosphate plasticizers may be environmentally hazardous, (especially where the phosphate constituent comprises more than 20% of the overall composition) a coated platicized product according to the invention is completely safe. Moreover, as just indicated, phosphate impart an effective degree of flame retardancy to the vinyl.
Various additional modifications and extensions of this invention will become apparent to those skilled in the art. All such variations and deviations which basically rely on the teachings through which this invention has advanced the art are properly considered to be within the spirit and scope of the invention.

Number	Name	Date
2731060	Rowe	Jan 1956
2994632	Brown et al.	Aug 1961
3075863	Frey	Jan 1963
3129816	Bone et al.	Apr 1964
3264372	Deicher et al.	Aug 1966
3271178	Nadeau et al.	Sep 1966
3284277	Bonacci et al.	Nov 1966
3421973	Kamal et al.	Jan 1969
3562095	Rahl et al.	Feb 1971

Top coated PVC articles

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

US Referenced Citations (9)