The present disclosure relates to the field of display technology, and particularly relates to a transistor and a manufacturing method thereof, a display substrate and a display device.
Current AMOLED products are developing towards higher definition, larger size and higher refresh frequency, which places higher demands on Thin FilmTransistors (TFTs) of AMOLED drive circuits. Since a Top Gate (Top Gate) oxide semiconductor transistor has an effectively reduced parasitic capacitance, a better refresh frequency, a shorter channel as well as a smaller size, the Top Gate (Top Gate) oxide semiconductor transistors can meet the development requirements of the AMOLED better. As a result, the Top Gate oxide semiconductor transistor has become a key direction for future research and development.
In one aspect, there is provided a transistor, including: a base structure; an active layer on the base structure; and a gate electrode, a source electrode and a drain electrode that are all on a side of the active layer distal to the base structure. The active layer includes a first region corresponding to an orthographic projection of the gate electrode on the base structure and a second region outside the orthographic projection. The active layer in the second region contains a conductorized semiconductor material. A surface of the base structure in contact with the active layer in the first region is not in the same plane as a surface of the base structure in contact with the active layer in the second region. The active layer in the first region has substantially the same thickness as a thickness of the active layer in the second region.
In one embodiment, the base structure includes one or more sub-film layers, wherein at least one sub-film layer of the one or more sub-film layers in the first region has a greater thickness than a thickness of the at least one sub-film layer in the second region.
In one embodiment, the base structure includes one or more sub-film layers, wherein at least one sub-film layer of the one or more sub-film layers is located only in the first region.
In one embodiment, the base structure includes a buffer layer, a light shielding layer, and a substrate arranged sequentially in a direction from the active layer to the substrate. The light shielding layer in the first region has a greater thickness than a thickness of the light shielding layer in the second region.
In one embodiment, the light shielding layer includes a light shielding metal material.
In one embodiment, the base structure includes a buffer layer, a light shielding layer, and a substrate arranged sequentially in a direction from the active layer to the substrate. The buffer layer in the first region has a greater thickness than a thickness of the buffer layer in the second region.
In one embodiment, the base structure includes a buffer layer, a light shielding layer, and a substrate arranged sequentially in a direction from the active layer to the substrate. The substrate in the first region has a greater thickness than a thickness of the substrate in the second region.
In one embodiment, the base structure includes only a substrate, and the substrate in the first region has a greater thickness than a thickness of the substrate in the second region.
In one embodiment, the substrate includes a glass material.
In one embodiment, the transistor further includes: a first insulating layer between the gate electrode and the active layer; and a second insulating layer between the source electrode, drain electrode and the gate electrode. The source electrode and the drain electrode are on a side of the gate electrode distal to the active layer. The source electrode and the drain electrode are in the same layer.
In one embodiment, the active layer includes an oxide semiconductor material.
In one aspect, there is provided a display substrate including the transistor as described above.
In one aspect, there is provided a display device including the display substrate as described above.
In one aspect, there is provided a method for manufacturing a transistor, including: forming a base structure; forming an active layer on the base structure; and forming a. gate electrode, a source electrode and a drain electrode on a side of the active layer distal to the base structure. The active layer includes a first region corresponding to an orthographic projection of the gate electrode on the base structure and a second region outside the orthographic projection. The forming the base structure includes: forming the base structure such that a surface of the base structure in contact with the active layer in the first region is not in the same plane as a surface of the base structure in contact with the active layer in the second region. The forming the active layer on the base structure includes: forming the active layer such that the active layer in the first region has substantially the same thickness as a thickness of the active layer in the second region; and conductorizing the active layer in the second region.
In one embodiment, the forming the base structure includes: forming the base structure including one or more sub-film layers, wherein at least one sub-film layer of the one or more sub-film layers in the first region has a greater thickness than a thickness of the at least one sub-film layer in the second region.
In one embodiment, the forming the base structure including one or more sub-film layers includes: forming the base structure including a buffer layer, a light shielding layer and a substrate, forming the light shielding layer through a halftone mask process such that the light shielding layer in the first region has a greater thickness than a thickness of the light shielding layer in the second region.
In one embodiment, the forming the base structure including one or more sub-film layers includes: forming the base structure including a buffer layer, a light shielding layer and a substrate, and forming the buffer layer through a halftone mask process such that the buffer layer in the first region has a greater thickness than thickness of the buffer layer in the second region.
In one embodiment, the forming the base structure including one or more sub-film layers includes: forming the base structure including a buffer layer, a light shielding layer and a substrate, and forming the substrate through a halftone mask process such that the substrate in the first region has a greater thickness than a thickness of the substrate in the second region.
In one embodiment, the forming the active layer on the base structure further includes: depositing an oxide semiconductor film on the base structure; patterning the oxide semiconductor film through an exposure process, a development process and an etching process to form a pattern of the active layer; forming a pattern of a first insulating layer and a pattern the gate electrode on the pattern of the active layer in the first region; and conductorizing the pattern of the active layer in the second region by bombarding the pattern of the active layer in the second region using helium gas to form the active layer.
In order to ensure a better understanding on the technical solution of the present disclosure for those skilled in the art, a transistor and a manufacturing method thereof, display substrate and display device of the present disclosure will be described in detail below with reference to the accompanying drawings.
Since a Top Gate oxide semiconductor transistors typically has a shorter channel, uniformity of a threshold voltage of the Top Gate oxide semiconductor transistors will be affected by the short channel effect. In particular, during the conductorizing process of an active layer including an oxide semiconductor material (e.g., IGZO) of a transistor, the conductorized regions on opposite sides of the active layer have certain influence on an intermediate non-conductorized region (i.e., an effective channel region). For example, during the conductorizing process, as shown in
In order to ensure the Effective Ch. length of the transistor and thus further improve the uniformity of the threshold voltage of the transistor, it is desired to reduce the influence of the active layer 5 on the intermediate non-conductorized region 9 during the conductorizing process. The structure of a Top Gate oxide semiconductor transistor in the related art is shown in
In one embodiment, a surface of the base structure 1 in contact with the first region 51 is not in the same plane as a surface of the base structure 1 in contact with the second region 52, and the active layer in the first region has substantially the same thickness as that of the active layer in the second region. Alternatively, a surface of the active layer 5 proximal to the base structure 1 in the first region 51 is higher than a surface of the active layer 5 proximal to the base structure 1 in the second region 52, and a surface of the active layer 5 distal to the base structure in the first region 51 is higher than a surface of the active layer 5 distal to the base structure in the second region 52. With such configuration, a height difference is formed between the first region 51 and the second region 52 of the active layer 5 (i.e., the first region 51 and the second region 52 are not on the same plane) such that during the conductorizing process of the second region 52, a path for the active layer material to diffuse from the second region 52 to the first region 51 is lengthened, and more energy is required for the diffusion of the active layer material, and such that during the conductorizing process of the second region 52, the active layer material hardly diffuse into the first region 51. Therefore, the length of the first region 51 is hardly shortened during the conductorizing process of the second region 52, the length of the effective channel of the transistor is hardly shortened during the conductorizing process, thereby finally greatly reducing the influence of the second region 52 on the first region 51 during the conductorizing process, improving the poor uniformity of the threshold voltage of the transistor due to the short channel effect, and avoiding the defects of the transistor.
In this embodiment, a surface of the base structure 1 distal to the active layer 5 is a flat surface. The base structure 1 includes a plurality of sub-film layers, wherein at least one sub-film layer of the plurality of sub-film layers has a greater thickness in the first region 51 than a thickness of the at least one sub-film layer in the second region 52.
In one embodiment, the base structure 1 includes three sub-film layers, i.e., a buffer layer 11, a light shielding layer 12, and a substrate 13, arranged sequentially between the active layer 5 and the base structure 1 along a direction distal to the active layer 5. The light shielding layer 12 in the first region 51 has a greater thickness than that of the light shielding layer 12 in the second region and/or, the buffer layer II in the first region 51 has a greater thickness than that of the buffer layer 11 in the second region 52; and/or, the substrate 13 in the first region 51 has a greater thickness than that of the substrate 13 in the second region 52. That is, the thickness of at least one of the three sub-film layers is not uniform. The at least one sub-film layer in the first region 51 has a greater thickness than that of the at least one sub-film layer in the second region 52 such that a height difference is formed between the first region 51 and the second region 52 of the active layer 5.
In one embodiment, the buffer layer 11 and the substrate 13 each have a uniform thickness in the first region 51 and the second region 52, while the light shielding layer 12 in the first region 51 has a greater thickness than that of the light shielding layer 12 in the second region 52. By setting the light shielding 12 in the first region 51 having a different thickness from that of the light shielding layer 12 in the second region 52, a height difference is formed between the active layer 5 in the first region 51 and the active layer 5 in the second region 52.
In this embodiment, the light shielding layer 12 is made of a light shielding metal material. With the arrangement of the light shielding layer 12, drifting of the threshold voltage of the transistor can be improved or prevented, thereby improving uniformity of the threshold voltage of the transistor.
In one embodiment, the light shielding layer 12 may be located only in the first region 51 and not in the second region 52 such that a height difference can also be formed between the active layer 5 in the first region 51 and the active layer 5 in the second region 52.
The substrate 13 is made of a glass material. A first insulating layer 6 is disposed between the gate electrode 2 and the active layer 5; the source electrode. 3 and the drain electrode 4 are located on a side of the gate electrode 2 distal to the active layer 5 and located in the same layer. A second insulating layer 7 is disposed between the source electrode 3, drain electrode 4 and the gate electrode 2. The active layer 5 is made of an oxide semiconductor material. The active layer 5 made of oxide semiconductor material needs to be conductorized during manufacture.
In another embodiment, in order to make the surface of the base structure 1 in contact with the active layer in the first region 51 not in the same plane as the surface of the base structure 1 in contact with the active layer in the second region 52, a recess may be provided at a position of the base structure 1 corresponding to the first region 51, for example, any one of the sub-film layers of the base structure 1 in the first region 51 has a smaller thickness than that of the sub-film layer in the second region 52 through a halftone mask process. In one embodiment, the light shielding layer 12 in the first region 51 has a smaller thickness than that of the light shielding layer 12 in the second region 52. In one embodiment, the buffer layer 11 in the first region 51 has a smaller thickness than that of the buffer layer 11 in the second region 52. In one embodiment, the substrate 13 in the first region 51 has a smaller thickness than that of the substrate 13 in the second region 52. In this way, it can also achieve that during the conductorizing process of the second region 52, a path for the active layer material to diffuse from the second region 52 to the first region 51 is lengthened, and more energy is required for the diffusion of the active layer material, thereby improving the poor uniformity of the threshold voltage of the transistor due to the short channel effect, and avoiding the defects of the transistor.
Based on the above structure of the transistor, the present embodiment further provides a method for manufacturing the transistor, including forming a base structure, a gate electrode, a source electrode, a drain electrode and an active layer, wherein the step of forming the active layer includes conductorizing the second region of the active layer, and the step of forming the base structure includes making a surface of the base structure in contact with the active layer in the first region not in the same plane as a surface of the base structure in contact with the active layer in the second region.
The step of forming the base structure includes: forming the light shielding layer in the first region and in the second region through a halftone mask process such that the light shielding layer in the first region has a different thickness from that of the light shielding layer in the second region; and/or, forming the buffer layer in the first region and in the second region through a halftone mask process such that the buffer layer in the first region has a different thickness from that of the buffer layer in the second region; and/or, forming the substrate in the first region and in the second region through a halftone mask process such that the substrate in the first region has a different thickness from that of the substrate in the second region.
In one embodiment, the step of forming the base structure includes: forming the light shielding layer in the first region and in the second region through a halftone mask process such that the light shielding layer in the first region has a different thickness from that of the light shielding layer in the second region.
The step of forming the active layer includes: depositing an oxide semiconductor film on the base structure; patterning the oxide semiconductor film through an exposure process, a development process and an etching process to form a pattern of the active layer; forming a pattern of a first insulating layer and a pattern of the gate electrode on the pattern of the active layer in the first region; and bombarding the pattern of the active layer in the second region using helium gas to conductorize the active layer in the second region, thereby forming the active layer.
At step 101, a metal film 120 (e.g., including Mo, Al, etc.) is deposited on the substrate using a magnetron sputtering apparatus, as shown in
At step 102, a buffer layer 11 is formed by depositing an insulating film including silicon oxide, silicon nitride, etc.) by PECVD (plasma enhanced chemical vapor deposition), as shown in
At step 103, an oxide semiconductor film 50 (e.g., including IGZO or ITZO) is deposited on the buffer layer 11, and then oxide semiconductor film 50 is patterned by an exposure process, a development process, and an etching process, as shown in
At step 104, an insulating film (e.g., including silicon oxide, silicon nitride, etc.) is deposited by PECVD on the oxide semiconductor film 50 as a first insulating layer film 60 (as shown in
At step 105, a metal film (e.g., including Cu, Al, etc.) is deposited on the first insulating layer film 60 using a magnetron sputtering apparatus, and then the metal film is patterned to form the gate electrode 2 (as shown in
At step 106, the first insulating layer film 60 is patterned by dry etching to form a first insulating layer 6; and then, the oxide semiconductor film 50 is conductorized to form an active layer 5 (as shown in
At step 107, an insulating film (e.g., including silicon oxide, silicon nitride, etc.) is deposited by PECVD and patterned to form a second insulating layer 7 (as shown in
At step 108, a metal film (e.g., including Cu, Al, etc.) is deposited using a magnetron sputtering apparatus and patterned to form a source electrode 3 and a drain electrode 4 (as shown in
In an embodiment of the present disclosure, there is further provided a transistor. Unlike the above embodiments, the base structure of the transistor includes only one sub-film layer, i.e., the substrate, and the substrate in the first region has a greater thickness than that of the substrate in the second region.
Other structures of the transistor in the present embodiment are the same as those in the above embodiments, and thus are omitted here.
Accordingly, in the method for manufacturing the transistor in the present embodiment, the step of forming the base structure includes: forming the substrate in the first region and in the second region through a halftone mask process such that the substrate in the first region has a different thickness from that of the substrate in the second region.
Other steps in the method for manufacturing the transistor in the present embodiment are the same as those in the above embodiments, and thus are omitted here.
In an embodiment of the present disclosure, there is further provided a transistor. Unlike the above embodiments, the base structure includes a substrate, an active layer on a side of the substrate, and one or more sub-film layers stacked between the substrate and the active layer, wherein at least one sub-film layer is disposed only in the first region.
With such arrangement, a height difference can also be formed between the active layer in the first region and the active layer in the second region.
Other structures of the transistor as well as the manufacturing method thereof in this embodiment are the same as those in the first embodiment, and thus are not repeated here.
In the transistor of the present disclosure, since a surface of the base structure in contact with the active layer in the first region not in the same plane as a surface of the base structure in contact with the active layer in the second region, a height difference is formed between the active layer in the first region and the active layer in the second region, such that during the conductorizing process of the second region, a path for the active layer material to diffuse from the second region to the first region is lengthened, and more energy is required for the diffusion of the active layer material, and such that during the conductorizing process of the second region, the active layer material hardly diffuse into the first region and thus the length of the first region is hardly shortened during the conductorizing process of the second region. That is, the effective channel length of the transistor is hardly shortened during the conductorizing process, thereby finally greatly reducing the influence of the second region on the first region during the conductorizing process of the second region, improving the poor uniformity of the threshold voltage of the transistor due to the short channel effect, and avoiding the defects of the transistor.
The present disclosure further provides a display substrate including the transistor according to any one of the embodiments as described above.
By adopting the transistor according to any one of the embodiments, the display quality of the display substrate is improved.
The present disclosure further provides a display device including the display substrate as described above.
By adopting the display substrate s described above, the display quality of the display device is improved.
The display device according to the present disclosure may be any product or component having a display function, such as an LCD panel, an LCD television, an OLED panel, an OLED television, a displayer, a mobile phone, a navigator or the like, or a semi-finished product of the product or component having a display function.
It should be understood that the above embodiments are merely exemplary embodiments for the purpose of illustrating the principle of the disclosure. However, the present disclosure is not limited thereto. It will be apparent to those skilled in the art that various changes and modifications can be made without departing from the spirit and essence of the present disclosure, and the changes and modifications should be regarded as falling within the scope of the present disclosure.