Patent Grant
8821162
The invention relates to dental prostheses comprising porcelain fused to a metal supporting structure or coping. Particularly, the invention relates to prostheses made by pressing a heated ceramic material into a mold onto said coping, wherein the mold is typically made by the lost wax process.
A majority of crown and bridge restorations of teeth continue to be porcelain fused to a metal supporting structure or coping that provides strength for the prosthesis. While “all-ceramic” prostheses are of increasing importance, porcelain fused to metal (PFM) remains cost effective and provides satisfactory aesthetics.
Since the metal substructures used in these restorations are not naturally tooth colored, esthetic veneering porcelains are applied that mimic the color and form of natural teeth. The veneering process plays a critical role in providing a satisfactory restoration. Typically the process of making a PFM restoration requires an opaque layer for masking the metal coping; a dentin layer that simulates the color of the tooth dentin; and an enamel layer that simulates the transparency and neutral colors of the tooth enamel. Other materials such as stains are typically used to achieve aesthetic effects.
Each layer is typically applied by hand, first requiring mixing of selected porcelain powders and liquids. The result is subject to variability and depends upon careful work of a skilled ceramist. Achieving consistent, aesthetic results is time consuming and adds significant cost to the final product, as well as requiring people who have a scarce skill and necessary experience.
In a continuing drive to simplify processes and reduce labor costs, methods have been developed to replace the multi-stage porcelain veneering process by a process in which the veneer material is pressed onto the metal support. However, a remaining difficulty has been that the initial pressing must still often be followed by a hand layering with enamel porcelain, particularly to develop incisal edge translucency.
It is an object of the present invention to provide porcelain materials and processing methods wherein skilled, intensive, and costly hand layering is further reduced.
The invention is a dental prosthesis that includes a metal coping for supporting said prosthesis on tooth surfaces to be repaired. The metal coping is provided with an opaque layer that covers surfaces of the coping that would interfere with achieving an acceptable tooth-like appearance of the finished PFM. The opaque layer may be formed from a mixture of frits in powder or paste form and applied by spraying, a slurry dip, electrodeposit, or other forms or methods known to those skilled in the art. A porcelain layer, having an optimized, integrated translucency that blends dentin and enamel shades is fused to said opaqued surface by pressing the porcelain material onto said coping contained in a mold at fusing temperatures. The result is a strong and tough dental crown or bridge substructure that is veneered with porcelain having an integrated transparency, blending dentin and enamel character, such that further hand layering processes are eliminated or greatly reduced.
The invention comprises a dental prosthesis, formed of elements, which may be supplied as components of a kit, that provide a porcelain fused to metal (PFM) restoration, using a pressing process to apply a finished surface instead of conventional hand layering of veneering porcelain. The veneering materials of the invention are designed for forming fixed prosthodontics devices that include both anterior and posterior crowns and bridges. Components of the kit, include principally: (1) dentin/enamel ingots having an integrated tooth-like translucency; and (2) opaquing porcelains, in both powder and paste forms, for covering metal coping surfaces that would otherwise be visible through the porcelain veneer. In addition, the kit may include enamel effect porcelains and glaze/stain porcelains for finishing the prosthesis, as necessary.
The veneering kit of the invention is intended for application to a wide range of supporting structure or coping alloys. For example, two commercially available alloys are non-precious NCM Alpha and Advantage, both manufactured by Austenal, formed into a coping by conventional casting techniques, well known to those skilled in the dental arts. The invention may particularly be utilized with conventional PFM alloys, for example, having coefficients of thermal expansion (CTE) of about 14.0 μ/m/K at 500° C. As necessary, the components may be engineered by blending compositions and adjusting their expansion properties to meet the needs of a particular alloy. In general however, the invention may be utilized with current alloys without the need for a new and specialized alloy set.
The press to metal process for making PFM restorations is well known in the art. The invention and its components are readily adapted to the pressing process, providing a significantly improved efficiency to the medium pressure injection molding process.
In the press to metal process, a metal coping is placed in a mold. The coping is then coated with an opaquing porcelain which may be in powder or paste form, applied by spraying, a slurry dip, electrodeposit or in other forms or methods known to those skilled in the art. The opaquing is followed by wax-up and spruing to form a desired finished prosthesis form. The form is then invested, preferably in an all ceramic investment material, and the wax burned out, forming the prosthesis mold. An appropriate amount of integrated translucency porcelain component of the invention is then pressed into the mold, typically under the conditions shown in Table 1 below. The prosthesis is then divested of the molding material for finishing.
The compositions for utilization in the press to metal process are designed such that the prosthesis produced is directly a desired shade match. Of course, the aesthetics may be modified or improved by the use of small amounts of “enamel effect powders”. These are typically applied in small sections at desired areas such as incisal edges, cusps, etc., followed by application of an overglaze or stains, as is well known in the art.
The integrated translucency composition of the invention is preferably utilized in the form of an ingot, preferably composed of a mixture of a dentin frit and a more transparent enamel frit. An example of a preferred frit formula for the ingot, as well as preferred ranges of compositions are listed in Table 2. To make the ingot material into a desired white porcelain, it is preferable to add 0.05% of antimony oxide (Sb2O3) and a fluorescing agent. The ingots are formed of the desired frits, typically in an amount of 2-5 grams, typically by pressing into a desired ingot form, pre-sintering at an initial temperature and further sintering at a higher temperature. The chemical compositions of the ingot white porcelain material together with the two raw frits are listed in Table 3.
The coping opaquer, in powder form, comprises mixing two frits with zirconia (ZrO2). Preferred compositions and ranges are shown in Table 4 and the chemical compositions of powder opaques are listed in Table 5.
An alternative coping opaquer, in paste form, also comprises two frits: Frit 1 and Frit 3, mixed with zirconia (ZrO2), tin oxide (SnO2), cerium oxide (CeO2), titanium oxide (TiO2), and antimony oxide (Sb2O3). The frit mixing formula is listed in Table 6 and the chemical composition of paste opaque is listed in Table 7.
This application is a continuation of application claims the benefit of and priority to U.S. patent application Ser. No. 12/459,783, filed on Jul. 8, 2009, which is a continuation application of U.S. patent application Ser. No. 11/788,600, filed on Apr. 20, 2007, now abandoned, which is herein incorporated by reference for all purposes.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4741699 | Kosmos | May 1988 | A |
| 4828117 | Panzera et al. | May 1989 | A |
| 5173114 | Heurtaux | Dec 1992 | A |
| 5713994 | Kramer et al. | Feb 1998 | A |
| 5788498 | Wohlwend | Aug 1998 | A |
| 20050082702 | Wennermann | Apr 2005 | A1 |
| 20070196788 | Chu et al. | Aug 2007 | A1 |
| 20090274995 | Chu et al. | Nov 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 1072689 | Jun 1967 | GB |
| 02076329 | Oct 2002 | WO |
| 03068100 | Aug 2003 | WO |
| 2006055800 | May 2006 | WO |
| Entry |
|---|
| International Search Report, Application No. 2005/041864, Published Nov. 18, 2005. |
| International Written Opinion, Application No. 2005/041864, Published Nov. 18, 2005. |
| Number | Date | Country | |
|---|---|---|---|
| 20130295522 A1 | Nov 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12459783 | Jul 2009 | US |
| Child | 13934584 | US | |
| Parent | 11788600 | Apr 2007 | US |
| Child | 12459783 | US |