Patent Application
20060148945
1. Field of the Invention
This invention is directed to tread-cap compositions and products, and more particularly, to tread-cap compositions and products that include one or more macro-fillers.
2. Description of Related Art
In developing a tread cap that provides an enhanced performance characteristic, a tread cap formulation has been proposed that includes an ultra high molecular weight polyethylene macro filler and a carbon black reinforcing filler.
While such a formulation may provide an enhanced performance characteristic, it does so at the expense of other desirable properties. For example, the composition may have an undesirable compound stiffness. In addition, other performance characteristics may be less than desirable. Therefore, there is a need for improved tread cap formulations.
A tread cap composition, in accordance with the principles of the invention, may be a composition resulting from the combination of components including: a conjugated diene-based elastomer; a reinforcing filler; a mineral- or vegetable-oil softener; a silane coupling agent; and an ultra high molecular weight polyethylene (“UHMWPE”).
One aspect of the invention is directed to a method of making a tread-cap composition. The method includes the steps of: mixing, at a temperature in a range of from about 135° C. to about 180° C., ingredients including: 100 phr of at least one conjugated diene-based elastomer; from about 30 to about 130 phr of at least one reinforcing filler; from about 2 to about 55 phr of at least one oil softener, the oil softener selected from the group consisting of a mineral oil having a PCA content of less than about 3% by weight, a vegetable oil, and combinations thereof; and from about 4 to about 20 phr of at least one silane coupling agent, thereby forming a first mixture. The method further includes the step of subsequently mixing, at a temperature of less than about 135° C., ingredients including: the first mixture; and from about 2 to about 50 phr of an ultrahigh molecular weight polyethylene (“UHMWPE”), thereby forming a tread-cap composition.
Other aspects of the invention include a tread-cap composition, a tread cap made from a tread-cap composition, and a tire that includes such a tread cap.
A tread cap composition, in accordance with the principles of the invention, may be a composition resulting from the combination of components including: a conjugated diene-based elastomer; a reinforcing filler; a mineral oil softener; a silane coupling agent; and an ultra high molecular weight polyethylene (“UHMWPE”). As used herein, the term “ultra high molecular weight” means a molecular weight of about 500,000 or more.
The conjugated diene-based elastomer may be any suitable elastomer or combination of elastomers. Examples include polybutadiene rubber (including high cis and high vinyl), polyisoprene, natural rubber, isoprene-butadiene copolymer, emulsion-polymerized styrene-butadiene rubber, and solution-polymerized styrene-butadiene rubber (including low, mid, and high vinyl). Advantageously, the conjugated diene-based elastomer may be a sulfur-vulcanizable elastomer containing olefinic unsaturation.
The reinforcing filler may be any suitable reinforcing filler or combination of fillers. For example, the filler may include silica and/or carbon black. If desired, the reinforcing filler may be present in an amount of from about 30 to about 130 phr.
The oil softener may be any suitable mineral- or vegetable-oil softener or combination of such oil softeners. Examples of mineral oil softeners include a treated distillate aromatic extract (“TDAE”) oil, a mild extraction solvate (“MES”) oil, and a special residual aromatic extract (“S-RAE”). Advantageously, the mineral oil softener may have a polycyclic aromatic composition (“PCA”) content of less than about 3% by weight. Also, if desired, the softener or combination of softeners may be present in an amount of from about 2 to about 55 phr. Examples of commercially available TDAE, MES, and S-RAE oils include Vivatec 500 oil from H&R Wasag A G (a TDAE oil), Catenex SNR oil from Shell (an MES oil), and NC140 oil from Japan Energy Corp. (an S-RAE oil).
The silane coupling agent may be any suitable agent or combination of agents. Examples include bis-3-(triethoxysilylpropyl) disulfide (“TESPD”), bis-3-(triethoxysilylpropyl)tetrasulfide (“TESPT”), and/or a blocked mercaptosilane. Advantageously, the blocked mercaptosilane is one or more of NXT or NXT-LoV from GE Silicones. If desired the silane coupling agent may be present in an amount of from about 4 to about 20 phr.
The UHMWPE may be any suitable UHMWPE. If desired, the UHMWPE may have a size in a range of from about 10 to about 200 micrometers, a molecular weight in a range of from about 500,000 to about 11,000,000, a standard bulk density of about 0.4 g/cm3 or greater, and a low bulk density of about 0.25 g/cm3 or less. If desired, the UHMWPE may be present in an amount of from about 2 to about 50 phr, advantageously from about 5 to about 13 phr. Also, if desired, the UHMWPE may be present in an amount of from about 5 to about 50 phr, or in an amount of from about 2 to about 3 phr. One example of a suitable UHMWPE is GUR® 4120 from the Ticona Company. GUR® 4120 has an average molecular weight of 5,000,000 g/mol, as calculated using Margolies' equation (M=5.37·104[η]1.49 where η is in dl/g).
The following example further illustrates several aspects of the invention. However, the invention is not limited by the example.
In this example, tread cap compositions that included an amount of UHMWPE, and in some cases, an additional amount of a mineral oil softener, were compared with a tread cap composition that did not include these ingredients. In addition, tread cap compositions in which the UHMWPE was added during a first non-productive mix stage were compared with tread cap compositions in which the UHMWPE was added in a subsequent cold-remilling stage.
With reference to Table I, sample A was the control sample, and did not include any UHMWPE or additional mineral oil softener. In the first non-productive mix stage, ingredients were added to a lab Banbury mixer in the amounts shown in Table I, and mixed for about 4.5 minutes to a temperature of about 160° C. In a second non-productive mix stage, the mixture resulting from the first non-productive mix stage was mixed for about 4.5 minutes to a temperature of about 160° C.
The contents of the mixer then were cooled to a temperature of about 23° C. over a period of about 600 minutes. Then the productive-mix-stage ingredients were added to the mixture, in the amounts shown in Table I; and the ingredients were mixed for about 2 minutes to a temperature of about 110° C.
With reference to Table I, samples B and D were prepared using processing parameters identical to those of sample A. Samples C and E were prepared using those same processing parameters, as well as a third non-productive mix stage. This third mix stage was a cold remill of the second mix stage, with the ingredients being mixed for about 2 minutes to a temperature of about 110° C. In samples B and D, the UHMWPE was added during the first non-productive mix stage; whereas in samples C and E, the UHMWPE was added during the third non-productive mix stage. Also, samples D and E included an additional amount (5 phr) of the mineral oil softener.
1Budene 1207
2SLR 4630
36-PPD (2.5 phr), refined paraffin wax (0.5 phr), and microcrystalline wax (1 phr)
4Vivatec 500
5Stearic acid
6X-266S
7GUR 4120
8Degussa VN-2 type (125 m2/g)
9DTPD (mixed aryl-p-phenylenediamines)
10Untreated French Process
11CBS
12diphenylguanidine
With reference to Table II, the experimental results show that samples B-E performed quite well in comparison with the control (sample A). For example, the G′-30° C. and tan 6 -20° C. data for these samples (B-E) are comparable with the control, indicating that such tread caps would perform well in wet and/or winter conditions. At the same time, the hardness values for samples C-E, and the Mooney viscosity values for samples C and E, remained relatively low.
While the present invention has been illustrated by the description of embodiments, and while the illustrative embodiments have been described in considerable detail, it is not the intention of the inventors to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications readily will appear to those skilled in the art. The invention in its broader aspects is therefore not limited to the specific details, representative apparatus and methods, and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the spirit or scope of the inventors' general inventive concept.
This patent document claims the benefit of the filing date of Provisional U.S. Patent Application No. 60/640,788 entitled “Tread Cap Composition” and filed on Dec. 30, 2004. The entire disclosure of Provisional U.S. Patent Application No. 60/640,788 is incorporated into this patent document by reference.