Trioxane composition and insect-proofing agent

Abstract

Disclosed is a composition comprising trioxane and an assistant aiding in the insect-proofing action of trioxane or controlling its vapor pressure.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a composition comprising trioxane and an assistant aiding in the insect-proofing action of trioxane or controlling its vapor pressure. The invention also relates to an insect-proofing agent composed of this composition.

2. Description of the Prior Art

Sublimable substances such as camphor, naphthalene and p-dichlorobenzene have been used as insect-proofing agents for clothes.

These conventional sublimable substances have the defect of giving off inherent irritating odors which remain in clothes after storage. Camphor and naphthalene have a weak action on clothes harmful insects such as case-making clothes moth (Tinea pellionella Linne) and various carpet beetles such as Attagenus piceus Oliv and Arthrenus verbasci Linne. p-Dichlorobenzene has toxicity and causes environmental pollution, and it has been desired to reduce its amount of use.

The present inventors previously filed a patent application for an insect-proofing agent comprising 1,3,5-trioxane (simply "trioxane" hereinafter) as an active ingredient (Japanese Laid-Open Patent Publication No. 115802/1988). Trioxane exhibits an insect-proofing action even when used alone. If, however, it is possible to increase its insect-proofing action further, its amount used would be able to be decreased.

SUMMARY OF THE INVENTION

The present inventors undertook extensive investigations in order to obtain an insect-proofing agent having a higher insect-proofing action, and found that by mixing trioxane with a certain assistant, a composition can be obtained which has higher insect-proofing action than trioxane used singly. This finding has now led to the accomplishment of the present invention.

It is an object of this invention therefore to provide a novel trioxane composition having an excellent insect-proofing action which continues for a long period of time, and to provide a sublimable insect-proofing agent composed of this composition.

Another object of this invention is to provide a trioxane composition comprising trioxane and as an assistant a component capable of increasing the insect-proofing action of trioxane and controlling the sublimability of trioxane and its sublimation speed.

Still another object of this invention is to provide a trioxane composition whose flash point can be maintained higher than trioxane alone, and as a result, which is easy to store or handle.

A further object of this invention is to provide a sublimable insect-proofing agent which is particularly useful as a clothes insect-proofing agent and a household harmful insect repellent having an excellent insect-proofing action without involving the problem of toxicity and environmental pollution.

Thus, according to this invention, there is provided a trioxane composition comprising as active ingredients

(A) 1,3,5-trioxane, and (B) as an assistant, at least one compound selected from the group consisting of (i) a dibasic acid ester represented by the following formula R.sup.3 OOC--R.sup.1).sub.n COOR.sup.2 ( 1) wherein R.sub.1 represents an alkylene group, carbon atoms, an alkylene group each having 2 to 6 or a phenylene group, n is 0 or 1, and each of R.sup.2 and R.sup.3 represents an alkyl group having not more than 4 carbon atoms, a cycloalkyl group or a phenyl group, (ii) a phenol represented by the following formula ##STR1## wherein R.sup.4 represents an alkyl group, an alkenyl group or an alkoxy group each having not more than 4 carbon atoms, and m is a number of 1 to 3, and when m is a number of 2 or 3, R.sup.4 may be same or different, (iii) an alcohol represented by the following formula R.sup.5 --Z.sup.1 --OH (3) wherein Z.sup.1 represents an alkylene group having 1 to 2 carbon atoms, and R.sup.5 represents a phenyl group, an alkylphenyl group, 1 to 3 hydroxyalkyl group or an alkoxy group, (iv) a monocarboxylic acid ester represented by the following formula R.sup.6 --Z.sup.2).sub.l COOR.sup.7 ( 4) wherein R.sup.6 represents an amino group, a hydrazino group, a phenyl group, a hydroxyphenyl group or an acyloxyphenyl group, Z.sup.2 represents an alkylene group, an alkenylene group or a hydroxyalkylene group each having up to 2 carbon atoms, and l is 0 or 1 or by the following formula ##STR2## wherein R.sup.8 represents an alkylene group or a phenylenemethylene group each having 5 to 7 carbon atoms, (v) a diphenyl compound or a quinone represented by the following formula ##STR3## wherein p, q and s are zero or 1 with the proviso that at least one of them is 1, (vi) a substituted benzene compound represented by the following formula ##STR4## wherein R.sup.9 is an alkyl group, an alkenyl group or an alkoxy group each having 1 carbon atom, and k is an integer of 2 to 4, (vii) an amide represented by the following formula ##STR5## wherein Y represents .dbd.CO or .dbd.SO.sub.2, each of R.sup.11 and R.sup.12 represents a hydrogen atom or an alkyl group having not more than 4 carbon atoms, R.sup.10 represents an alkyl group having not more than 4 carbon atoms or an amino group, and r is a number of 0 or 1, (viii) a heterocyclic compound having a molecular weight of 90 to 200 and containing at least one atom selected from the group consisting of nitrogen, oxygen and sulfur atoms, and (ix) a terpene.

There is also provided a sublimable insect-proofing agent, particularly for clothes and household harmful insect repellent use, comprising the trioxane composition as an active ingredient.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The assistants (i) to (ix) have common properties with respect to trioxane. Specifically, these assistants have the property of increasing the insect-proofing action of trioxane and in some cases, controlling the sublimability of trioxane. These assistants other than p-methylbenzylalcohol do not show an insect-proofing action or shown only a very low insect-proofing action when used singly, but when blended with trioxane, show a high insect-proofing action. The insect-proofing action is evaluated by a feed inhibition ratio on clothes, as will be shown in working examples given hereinafter. The combination of the components in this invention gives a higher feed inhibition ratio than in the case of using either component singly. The second property is closely related to the duration of the insect-proofing action, and furthermore, by using the assistant, the flash point of the composition can be rendered higher than trioxane alone.

The dibasic acid ester (i) is represented by formula (1). The alkylene group R.sup.1 may be, for example, an ethylene or tetramethylene group. The alkenylene group R.sup.1 may be, for example, a cis- or trans-vinylene group or propenylene group. Examples of the phenylene group are o-, m- or p-phenylene groups. The alkyl groups for R.sup.2 and R.sup.3 are preferably a methyl group, but may also be an ethyl, propyl or butyl group. The cycloalkyl group is preferably a cyclohexyl group. Suitable examples of the dibasic acid ester include dialkyl esters of aliphatic dicarboxylic acids having 2 to 8 carbon atoms benzenedicarboxylic acid esters, particularly dimethyl fumarate, diphenyl phthalate, dicyclohexyl phthalate, dimethyl isophthalate, dimethyl terephthalate, dimethyl oxalate and dimethyl itaconate.

The phenol (ii) is represented by general formula (2). Examples of the alkyl group R.sup.4 include methyl, ethyl, isopropyl and butyl groups. The alkoxy group for R.sup.4 may be, for example, a methoxy or ethoxy group. The alkenyl group for R.sup.4 may be, for example, a vinyl or propenyl group. Suitable examples of the phenol (ii) include 2,4-dimethylphenol, 2,5-dimethylphenol, 2,6-dimethylphenol, 3,4-dimethylphenol, 3,5-dimethylphenol, 2,3,5-trimethylphenol, 2,4,6-trimethylphenol, 2,6-di-t-butyl-4-methylphenol, p-methoxyphenol, thymol and eugenol.

The alcohol (iii) is represented by general formula (3). It includes polyhydric alcohols, alkoxyalcohols and araliphtic alcohols. The hydroxyalkyl group for R.sup.5 is preferably a sec- or tert-alkyl group having 1 to 3 hydroxyl groups. The alkoxy group preferably has 2 to 4 carbon atoms. Suitable examples of the alcohol (iii) are neopentyl glycol, 2-ethoxyethanol, pentaerythritol, p-methylbenzyl alcohol, and beta-phenethyl alcohol.

The monocarboxylic acid ester (iv) includes carbamic acid esters, carbazinic acid esters and araliphatic acid esters of general formula (4), and cyclic esters, i.e. lactones, of general formula (5). Suitable examples of the compound (iv) are methyl cinnamate, methyl carbamate, methyl carbazate, methyl mandelate, methyl p-hydroxybenzoate, methyl acetylsalicylate, epsilon-caprolactone and phthalide.

The diphenyl compound or quinone (v) is represented by general formula (6). Examples of the diphenyl compound are benzophenone, benzoin and benzhydrole. Examples of the quinone are quinones having 6 to 14 carbon atoms, particularly anthraquinone.

The substituted benzene compound (vi) is represented by general formula (7), and particularly has 6 to 10 carbon atoms. Examples of the substituted benzene compound are p-dimethoxybenzene and 1,2,4,5-tetramethylbenzene.

The amide (vii) is represented by general formula (8), and includes, for example, aromatic carboxylic acid amides and sulfonic acid amides. Suitable examples are N,N-diethyl-m-toluamide and sulfanilamide.

The heterocyclic compound (viii) is alicyclic or aromatic compounds containing at least one nitrogen, oxygen or sulfur atom in a five-membered ring or a six-membered ring. The heterocycle may contain 1 or 2 fused benzene rings. Suitable examples include N-methylpyrrolidone, hydantoin, dibenzofurane, benzotriazole, indole, imidazole, triethylenediamine and sulfolene.

Terpenes generally having a molecular weight of 136 to 222, preferably (l)-menthol, linalool, geraniol and limonene, may be used as the terpene (ix).

If methyl cinnamate, methyl carbamate, dimethyl fumarate, dicyclohexyl phthalate, dimethyl isophthalate, dimethyl oxalate, p-methylbenzyl alcohol, benzophenone, p-methoxyphenol, thymol or sulfolene is used as an assistant in this invention, the vapor pressure of trioxane is moderately controlled. As a result, the resulting composition attains a moderately high flash point as compared with trioxane alone. Accordingly, such assistant can be more safely used as trioxane vapor generating agents.

Furthermore, a composition of this invention comprising at least one of methyl cinnamate, l-menthol, linalool geraniol, limonene, beta-phenethyl alcohol and eugenol as assistants can be used suitably as a clothes insect-proofing agent because it has a fragrance.

1,3,5-Trioxane is a sublimable solid substance of the chemical formula (CH.sub.2 O).sub.3 which has a melting point of 64.degree. C. and is stable at room temperature in air. Desirably, 1,3,5-trioxane used in this invention is of high purity. Desirable, its formic acid content is not more than 20 ppm, especially not more than 10 ppm, and its formaldehyde content is not more than 50 ppm, especially not more than 20 ppm.

The proportions of trioxane and the assistant in the composition of this invention can be varied over wide ranges. Generally, for the objects of this invention, the composition of this invention contain 5 to 99.8% by weight, especially 10 to 50% by weight, of trioxane (A) and 0.2 to 95% by weight, especially 50 to 90% by weight, of the assistant (B).

The composition of this invention may be suitably obtained by mixing trioxane with the assistant, melting the mixture to form a uniformly dispersed liquid, and cooling the liquid. The cooled composition may be liquid or solid. For example, a mixture of 50 parts by weight of trioxane and 50 parts by weight of dimethyl oxalate melts at 30.degree. C. to form a liquid composition. Generally, however, the composition frequently becomes a solid in the room temperature. There is no particular restriction on the means for mixing the ingredients. For example, the assistant may be dispersed in molten trioxane or trioxane may be dispersed in a molten mass of the assistant. Alternatively, a powdery mixture of both may be co-melted. It should be understood that the composition of this invention is not limited to one obtained by mixing components (A) and (B) in the molten state, and may be a mixture of (A) and (B) in powder form.

The composition of this invention, either singly, or in combination with a known carrier such as silica gel or talc can be formulated in an insect-proofing agent, particularly one for clothes, or a household harmful insect repellent, in various forms. For example, the solid composition may be used in the form of a dust or a molded agent such as tablets, granules and balls. From the viewpoint of the moldability of the composition or the strength of the agent, binders, vehicles, lubricants, fillers, etc. may be incorporated. It is also possible to incorporate, perfumes, stabilizes and dyes. The liquid composition or a solution or dispersion of the composition in a solvent may be used as a liquid preparation by filling up it in a container or an aerosol container. It may also be used in a form occluded in a substrate such as paper or cloth, or in a filler, or may be formed into a solid by using a gelling agent, a resin, etc. and used as a gel or a solid agent.

The trioxane composition of this invention exhibts an excellent insecticidal action or an excellent feed inhibitory action on insects feeding on clothes and also an excellent insect-proofing action on household harmful insects as compared with trioxane alone, and these actions are long-lasting. Accordingly, the trioxane composition of this invention is suitably used as a clothes insect-proofing agent and a household harmful insect repellent.

The trioxane composition of this invention is easy to store or handle because its flash point can be made higher than the flash point of trioxane alone,

In addition, the use of the trioxane composition of this invention can avoid the use of p-dichlorobenzene which gives rise to the problem of toxicity and environmental pollution.

The following examples illustrate the present invention more specifically.

EXAMPLE 1

In each run, 99 parts by weight of trioxane was mixed with 1 part by weight of an assistant. The mixture was melted in a hot water bath to form a uniform liquid. The liquid was cooled to 20.degree. C. to form a solid composition.

The solid composition was processed in a pulverizer to form a uniform powdery trioxane composition.

The trioxane composition prepared was used in the following insect-proofing assay. Six milligrams of the trioxane composition was put at the bottom of a 900 ml. glass bottle. A metallic cage having a diameter of 3 cm containing ten 40-day old larvae of case-making clothes moth (Tinea pellionella Linne) and about 100 mg of square pieces of woollen fabrics each side measuring 3 cm was fixed at a position 5 cm above the composition. The bottle was then sealed up, and left to stand in a constant-temperature chamber at 30.degree. C. for 135 hours. Then, the cage was taken out, and the mortality of the case-making clothes moth larvae, and the amount of eating damage on the woollen fabrics (weight loss) were examined.

The results are evaluated by kill ratio and feed inhibition ratio as follows: ##EQU1##

COMPARATIVE EXAMPLE 1

The same insect-proofing test as in Example 1 was conducted except that 6 mg of trioxane powder alone without an assistant was used.

CONTROL EXAMPLE 1

The same insect-proofing test as in Example 1 was conducted without using any insect-proofing agent.

The results are shown in Tables 1-(1) to 1-(4).

When each of the foregoing assistants was used in an amount of 0.06 mg, no insect-proofing effect was observed.

TABLE 1______________________________________ Amount of Feed Kill eating inhibi-Run ratio damage tionNo. Assistant (%) (mg) ratio (%)______________________________________ 1 methyl cinnamate 0 14.4 62 2 methyl carbamate 20 11.7 69 3 methyl carbazate 20 9.8 74 4 methyl acetyl- 0 9.8 74 salicylate 5 dimethyl fumarate 0 13.2 65 6 diphenyl phthalate 0 15.1 60 7 dicyclohexyl 40 11.3 70 phthalate 8 dimethyl 20 14.4 62 isophthalate 9 dimethyl 0 15.5 59 terephthalate10 .epsilon.-caprolactone 0 10.2 7311 N-methylpyrolidone 0 13.6 6412 N,N-diethyl-m- 0 14.4 62 toluamide13 hydantoin 0 15.1 6014 anthraquinone 10 14.7 6115 benzoin 0 8.3 7816 benzhydral 0 11.7 6917 neopentyl glycol 10 14.4 6218 2-ethoxyethanol 0 9.8 7419 1,2,4,5-tetra- 0 11.7 69 methylbenzene20 2,4-dimethyl- 0 11.3 70 phenol21 2,6-dimethylphenol 0 11.3 7022 3,4-dimethylphenol 0 11.3 7023 2,4,6-trimethyl- 0 3.4 91 phenol24 2,6-di-t-butyl- 0 4.9 87 4-methylphenol25 benzotriazole 0 15.5 5926 indole 10 11.7 6927 triethylenediamine 20 11.3 7028 sulfanilamide 0 13.6 6429 sulfolene 0 9.8 7430 (.lambda.)-menthol 0 15.9 5831 linalool 0 4.9 8732 geraniol 0 14.4 6233 limonene 0 17.0 5534 .beta.-phenethylalcohol 0 9.1 7635 eugenol 0 12.5 67Compar- trioxane alone 0 20.8 45ativeExampleControl no agent 0 37.8 0Example1______________________________________

EXAMPLE 2

In each run, 5 mg of powdery trioxane was mixed with a predetermined amount of an assistant in a petri dish to form a trioxane composition. The petri dish containing the prepared trioxane composition was placed at the bottom of a 900 ml glass bottle, and a metallic cage having a diameter of 3 cm containing ten 40-day old larvae of case-making clothes moth (Tinea pellionella Linne) and about 100 mg of square pieces of woollen fabrics each side measuring 3 cm was fixed at a position 5 cm above the composition. The bottle was then sealed up, and left to stand in a constant-temperature chamber at 30.degree. C. for 120 hours. Then, the cage was taken out, and the mortality of the case-making clothes moth larvae, and the amount of eating damage on the woollen fabrics (weight loss) were examined. The run was conducted twice, and the averaged results are shown in Table 2-(1) and 2-(2).

COMPARATIVE EXAMPLE 2

The same insect-proofing test was conducted as in Example 2 except that trioxane was not used, and the assistants were singly used in the same amounts as used in Runs Nos. 36 to 55. The results are shown in Tables 3-(1) and 3-(2).

TABLE 2______________________________________ Amount of Feed Amount of kill eating inhibi-Run Assistant ratio damage tionNo. Assistant (mg) (%) (mg) ratio (%)______________________________________36 methyl cinnanate 9 40 6.7 8037 methyl 2 30 9.7 71 mandelate38 methyl p-hydroxy- 4 15 9.4 72 benzoate39 methyl acetyl- 5 15 12.1 64 salicylate40 dimethyl fumarate 30 80 0.0 10041 dicyclohexyl 50 25 10.4 69 phthalate42 dimethyl 11 40 6.7 80 isophthalate43 dimethyl oxalate 5 100 0.0 10044 epsilon- 3 75 2.7 92 caprolactone45 phthalide 12 40 16.8 5046 benzophenone 25 5 10.8 6847 benzhydrole 40 15 6.7 8048 neopentyl glycol 60 90 5.0 8549 penta-erythritol 4 15 15.1 5550 2,3,5-trimethyl- 8 55 14.4 57 phenol51 2,6-di-t-butyl- 20 15 16.8 50 4-methylphenol52 p-methoxyphenol 16 85 10.8 6853 dibenzofurane 40 35 4.4 8754 (.lambda.)-menthol 1 80 5.4 8455 p-methyl benzyl 12 100 0.0 100 alcohol______________________________________ TABLE 3______________________________________ Amount of Feed Amount of kill eating inhibi-Run Assistant ratio damage tionNo. Assistant (mg) (%) (mg) ratio (%)______________________________________136 methyl cinnanate 9 0 9.1 73137 methyl 2 0 30.2 10 mandelate138 methyl p-hydroxy- 4 0 30.9 8 benzoate139 methyl acetyl- 5 5 30.2 10 salicylate140 dimethyl fumarate 30 60 1.7 95141 dicyclohexyl 50 0 30.2 10 phthalate142 dimethyl 11 0 31.9 5 isophthalate143 dimethyl oxalate 5 70 1.7 95144 epsilon- 3 30 30.9 8 caprolactone145 phthalide 12 0 33.6 0146 benzophenone 25 0 26.5 21147 benzohydrole 40 0 31.9 5148 neopentyl glycol 60 0 33.3 1149 pentaerythritol 4 0 33.6 0150 2,3,4-trimethyl- 8 10 26.9 20 phenol151 2,6-di-t-butyl- 20 0 33.6 0 4-methylphenol152 p-methoxyphenol 16 40 26.9 12153 dibenzofurane 40 0 15.8 53154 (.lambda.)-memthol 1 50 20.2 40155 p-methyl-benzyl 12 80 11.5 66 alcohol______________________________________

COMPARATIVE EXAMPLE 3

The same experiment as in Example 2 was conducted by using 5 mg of trioxane without adding an assistant. The results are shown in Table 4.

CONTROL EXAMPLE 2

The same experiment as in Example 2 was conducted except that no insect-proofing agent was used. The experiment was conducted twice, and the averaged results are shown in Table 4.

TABLE 4______________________________________ Amount of Feed Insect- eating inhibi- proofing Kill ratio damage tionEx. No. agent (%) (mg) ratio (%)______________________________________Comparative trioxane 0 21.8 35Example 3 aloneControl None 0 33.6 0Example 2______________________________________

EXAMPLE 3

In each run, predetermined amounts of trioxane and an assistant were mixed and melted in a hot water bath to form a uniform liquid. 0.1 g of the liquid was taken out, and impregnated into a square piece of filter paper each side measuring 5 cm. The treated filter paper was placed at the bottom of a 900 ml. glass bottle, and a metallic cage having a diameter of 3 cm containing ten 40-day old larvae of case-making clothes moth (Tinea pellionella Linne) and about 100 mg of square pieces of woollen fabrics each side measuring 3 cm was fixed at a position 5 cm above the filter paper. The bottle was then sealed up, and left to stand in a constant-temperature chamber at 25.degree. C. for 7 hours. Then, the cage was taken out, and the mortality of the case-making clothes moth larvae was examined. Since the testing time was short, the amount of eating damage could not be evaluated. The results are shown in Table 5.

COMPARATIVE EXAMPLE 4

Example 3 was repeated except that 0.1 g of the assistant alone was used. The results are shown in Table 6.

COMPARATIVE EXAMPLE 5

Example 3 was repeated except that 0.1 g of trioxane alone was used without adding an assistant. The results are shown in Table 7.

CONTROL EXAMPLE 3

Example 3 was repeated except that no insect-proofing agent was used. The results are shown in Table 7.

TABLE 5______________________________________ KillRun trioxane assistant ratioNo. Assistant (wt %) (wt %) (%)______________________________________56 methyl carbamate 34 66 10057 dimethyl itaconate 10 90 10058 p-dimethoxybenzene 20 80 10059 2,5-dimethylphenol 70 30 10060 3,4-dimethylphenol 60 40 10061 3,5-dimethylphenol 40 60 10062 p-methoxyphenol 24 76 10063 thymol 20 80 10064 indole 50 50 10065 imidazol 70 30 10066 sulfolene 25 75 10067 p-methyl-benzil 30 70 100 alcohol______________________________________ TABLE 6______________________________________ KillRun ratioNo. Assistant (%)______________________________________156 methyl carbamate 20157 dimethyl itaconate 0158 p-dimethoxybenzene 10159 2,5-dimethylphenol 10160 3,4-dimethylphenol 0161 3,5-dimethylphenol 0162 p-methyoxyphenol 0163 thymol 0164 indole 10165 imidazol 0166 sulfolene 10167 p-methyl-benzil 30 alcohol______________________________________ TABLE 7______________________________________ Insect- Kill proofing ratioEx. No. agent (%)______________________________________Comparative trioxane 60Example 5 aloneControl None 0Example 3______________________________________

The results of the foregoing Examples and Comparative Examples demonstrate that the trioxane compositions of this invention show better insect-proofing activity than trioxane or the assistants each used singly.

EXAMPLE 4

In each run, predetermined amounts of trioxane and an assistant were mixed, and melted in a hot water bath to form a uniform trioxane composition. The flash point of this composition was measured in accordance with ASTM by a Setaflash.RTM. Closed-Cup Apparatus. The results are shown in Table 8.

COMPARATIVE EXAMPLE 6

The flash point of trioxane alone was measured as in Example 4. The result is also shown in Table 8.

TABLE 8______________________________________ flashRun trioxane assistant pointNo. Assistant (wt %) (wt %) (.degree.C.)______________________________________68 methyl cinnamate 37 63 4569 methyl carbamate 34 66 4570 dimethyl phthalate 15 85 4571 dicyclohexyl 10 90 51 phthalate72 dimethyl 32 68 47 isophthalate73 dimethyl oxalate 50 50 4474 benzophenone 17 83 4575 p-methoxyphenol 24 76 4576 thymol 20 80 4577 sulfolene 25 75 4578 p-methyl-benzyl 30 70 51 alcoholComparative trioxane alone 100 0 40Example 6______________________________________

EXAMPLE 5

Trioxane and p-methylbenzyl alcohol were mixed in a weight ratio of 3:7, melted unformly at 70.degree. C., and then cooled to 20.degree. C. to form a solid composition. The solid composition could easily be pulverized to a uniform powder in a mortar.

The resulting composition in powder form (0.5 g) was placed at the bottom of a 500 ml glass bottle, and a metallic cage having a diameter of 3 cm containing ten 35-day old larvae of case-making clothes moth (Tinea pellionella Linne) and about 100 mg of square pieces of woollen fabrics each side measuring 2 cm was fixed at a position 5 cm above the powdery composition. The bottle was then sealed up, and left to stand in a constant-temperature chamber at 30.degree. C. for 5 days. Then, the cage was taken out, and the mortality of the case-making clothes moth larvae, and the amount of eating damage of the woollen fabrics (weight loss) were examined. The results are shown in Table 9.

COMPARATIVE EXAMPLE 7-8

Example 5 was repeated except that p-methylbenzyl alcohol and trioxane in powder form was used respectively alone in the insect-proofing test. The results are shown in Table 9.

COMPARATIVE EXAMPLE 9

Example 5 was repeated except that no insect-proofing agent was used. The results are shown in Table 9.

TABLE 9______________________________________ Number Amount of of dead eatingEx. No Insect-proofing agent insects damage (mg)______________________________________Example p-methylbenzyl alcohol/ 10 05 trioxane composition (7:3 by weight)Compara- p-methylbenzyl alcohol 8 12tive Ex- (alone)ample 7Compara- trioxane 10 0tive Ex- (alone)ample 8Compara- none 0 35tive Ex-ample 9______________________________________

Claims

1. A trioxane composition having increasing insect proofing action of trioxane comprising as active ingredients

(A) 10 to 50% by weight, of the total composition, of 1,3,5-trioxane, and

(B) 50 to 90% by weight, of the total composition, of methyl carbamate as an assistant.