Tunable devices incorporating cacu3ti4o12

Abstract

This invention provides tunable devices incorporating the dielectric CaCu3Ti4O12. CaCu3Ti4O12 is especially useful in tunable devices such as phase shifters, matching networks, oscillators, filters, resonators, and antennas comprising interdigital and trilayer capacitors, coplanar waveguides and microstrips.

Description

FIELD OF THE INVENTION

[0001] This invention provides tunable devices incorporating the dielectric material CaCu3Ti4O12.

BACKGROUND OF THE INVENTION

[0002] The use of dielectric materials to increase capacitance is well known and long-used. Earlier capacitor dielectrics fell into two categories. The first category of dielectrics has a relatively temperature-independent dielectric constant but the value of the dielectric constant is low, e.g., 5-10. Materials such as electrical porcelain and mica fall in this category. The second category of dielectrics has very high dielectric constant, e.g., 1000 or more, but they are quite temperature dependent. An example is barium titanate, BaTiO3.

[0003] Since the capacitance is proportional to the dielectric constant, high dielectric constant materials are desired. In order to perform acceptably in tuning or resonance circuits the dielectric must have a dielectric constant that exhibits minimal temperature dependence; otherwise small changes in ambient temperature throw the circuit out of resonance. Other applications require a dielectric constant that exhibits minimal frequency dependence. It is also desirable to have the loss or dissipation factor as small as possible.

[0004] For many microwave devices the important material features are the dielectric tunability, i. e., the change in dielectric constant with applied voltage, and low dielectric loss. Barium strontium titanate, Ba1−xSrxTiO3, has been used in some such applications but the need persists for materials with better properties.

[0005] Deschanvres et al., Bull. Soc. Chim. Fr. 4077 (1967) report the preparation of CaCu3Ti4O12 with the perovskite structure and a lattice constant of 0.7393 nm.

[0006] Bochu et al., J. Solid State Chem. 29, 291 (1979) disclose the synthesis and structure of CaCu3Ti4O12 and related titanates and report the lattice constant to be 0.7391 nm.

[0007] Yandrofski et al., U.S. Pat. No. 5,472,935, disclose tunable microwave and millimeter wave devices incorporating tunable ferroelectrics.

SUMMARY OF THE INVENTION

[0008] This invention provides tunable devices incorporating the dielectric CaCu3Ti4O12. CaCu3Ti4O12 is especially useful in tunable devices such as phase shifters, matching networks, oscillators, filters, resonators, and antennas comprising interdigital and trilayer capacitors, coplanar waveguides and microstrips.

[0009] This invention also provides electrical devices requiring a dielectric material with a dielectric constant above 9000 wherein the dielectric is CaCu3Ti4O12.

DETAILED DESCRIPTION

[0010] CaCu3Ti4O12 has dielectric properties that provide advantages in devices requiring a high dielectric constant as well as in tunable devices. CaCu3Ti4O12 has a dielectric constant above 9000 over a frequency range of 1 kHz to 1 MHz.

[0011] CaCu3Ti4O12 can be synthesized by the following procedure. Stoichiometric amounts of the precursors are thoroughly mixed. The precursors CaCO3, CuO and TiO2 are preferred. The mixed precursor powder is calcined at about 1000° C. for about 12 hours. The calcined powder is reground and pressed to 12.7 mm diameter/1-2 mm thick disks. The disks are sintered in air at about 1100° C. for 24 hours. In both the calcining and sintering steps, the temperature ramping up rate is about 200° C./hour from room temperature, i.e., about 20° C., to the calcining or sintering temperature and the cooling rate is about 150° C./hour from the calcining or sintering temperature to room temperature, i.e., about 20° C.

[0012] CaCu3Ti4O12 crystallizes in a cubic perovskite Im3 structure.

[0013] Dielectric measurements were carried out on the disk samples. The faces of the disk-shaped samples were polished with a fine-grit sand or emery paper. Silver paint electrodes were applied on the faces and dried at 70-100° C. The capacitance and the dielectric loss measurements were performed by the two-terminal method using Hewlett-Packard 4275A and 4284A LCR bridges at a temperature of 25° C. over a frequency range of from 1 kHz to 1 MHz. The capacitance, C, and the dissipation factor are read directly from the bridge. The dielectric constant (K) was calculated from the measured capacitance, C in picofarads, from the relationship, K=(100 C t)/(8.854 A), where t is thickness of the disk shaped sample in cm and A is the area of the electrode in cm2. Voltages were applied across the flat electroded faces of the disks and tunability was calculated by measuring the change in dielectric constant with applied voltage. The tunability, T, is calculated from the equation T=[K(0)−K(V)]/K(0)] where K(0) is the dielectric constant when there is no applied voltage and K(V) is the dielectric constant when there is an applied voltage V. The tunability is usually expressed as a percent for a given applied electric field so that the above result for T is multiplied by 100 or it is written as T=(constant) E where T is the tunability in %, E is the electric field and the constant is characteristic of the particular material.

EXAMPLE OF THE INVENTION

[0014] CaCu3Ti4O12 was prepared by the following procedure. Appropriate amounts of the starting carbonate and oxides CaCO3, CuO and TiO2 were weighed according to the stoichiometric ratios and mixed thoroughly in an agate mortar. The gram amounts of the precursors used are shown in Table 1. The mixed powder was calcined at 1000° C. for 12 hours. The calcined powder was reground and pressed to 12.7 mm diameter/1-2 mm thick disks. The disks were sintered in air at 1100° C. for 24 hours. In both the calcining and sintering steps, the temperature was increased from room temperature, i.e., about 20° C., to the calcining or sintering temperature at a rate of 200° C./hour and the temperature was decreased from the calcining or sintering temperature to room temperature, i.e., about 20° C., at a rate of 150° C./hour.

[0015] X-ray powder diffraction patterns were recorded with a Siemens D5000 diffractometer. The data showed that CaCu3Ti4O12 crystallized in a cubic perovskite related Im3 structure. The measured lattice parameter and the literature value are listed in Table 1.

	TABLE 1
	CaCO3	0.2502	g
	CuO	0.5966	g
	TiO2	0.799	g
	a, measured	.7391(1)	nm
	lattice parameter
	a, literature value	.7391	nm
	lattice parameter

[0016] The disk samples were polished to produce flat uniform surfaces and electroded with silver paint. The painted samples were dried at 70-100° C. overnight. Capacitance and loss tangent measurements were taken on a

[0017] HP-4284A LCR meter at room temperature, i.e., about 20° C., over a frequency range of from 1 kHz to 1 MHz. The results are shown in Table 2.

TABLE 2
Frequency	Dielectric	Loss
(Hz)	Constant	Tangent
1	k	12334	0.105
10	k	11087	0.0695
100	k	10286	0.0674
1	M	9211	0.232

[0018] Voltages up to 100V were applied across the flat electroded faces of the disks using an Keithley 228A voltage/current source and the dielectric constant was measured as a function of applied voltage at room temperature using a HP-4275A LCR meter. The percent tunability and the applied electric filed to obtain that magnitude tunability are shown in Table 3 over a frequency range of from 1 kHz to 1 MHz. The tunability equation written in the form T=(constant) E is also given in Table 3 for each frequency.

TABLE 3
Electric	Frequency
Field (V/μm)	10 k	100 k	1 M	10 M
0	0.000	0.000	0.000	0.000
0.017182	1.149	1.015	0.805	0.328
0.034364	2.546	2.258	1.849	0.786
0.051546	3.924	3.491	2.926	1.290
0.068729	5.244	4.676	3.896	1.841
0.081615	6.201	5.536	4.627	2.182
Tunability	T = 77.0 × E	T = 68.8 × E	T = 57.7 × E	T = 27.5 × E
(T: tunability in %, E: electric field in V/μm)

[0019] The results show that CaCu3Ti4O12 has a high tunability along with a high dielectric constant.

Claims

1. A tunable electric device comprising CaCu3Ti4O12.

2. A tunable electrical device requiring a dielectric material with a dielectric constant above 9000 comprising the dielectric CaCu3Ti4O12.