The present invention relates to turbine airfoils of composite material, particularly for steam turbines, and methods of manufacturing such airfoils.
In the following description the term “turbine” is used to refer to rotary engines having a rotating part and a stator part force coupled by a fluid medium such as water, steam or gas. Of particular interest for the present invention are axial turbines comprising radially arranged fixed stator blades or vanes alternating with radially arrangements of moving rotor blades. Movements are generally defined as movements relative to a casing or housing.
In large turbines, particularly steam turbines, the moving blades or airfoils are presently manufactured using steel or titanium based alloys. In a multi-stage turbine, the size of the blades increases from stage to stage. In the final stage of the largest low pressure turbines the height of a turbine blade can exceed one meter or more. While it is desirable to increase the size of the turbine stages and thereby increase its flow-off surface and efficiency, the properties of current materials have reached theirs limits mainly because of the large centrifugal forces acting on the rotating blades.
To overcome the barriers set by the materials properties of steel and titanium, composite material airfoils have been proposed using mainly carbon fiber based materials. Though a large number of such designs have been published, real-world applications of such composite blades are currently limited to gas turbines for advanced aircrafts engines.
One of the reasons which so far prevented large-scale adoption of composite blades in the field of electrical power generation is the lack of resistance of the composite materials to erosion. Specifically in the field of steam turbine blades, the material is subject to erosion by water droplet condensing from the steam passing through the turbine over a long period of operation. Under the constant bombardment of the condensate from the water steam, composite material erodes much faster than the currently applied metal alloys and is thus not suitable as airfoil material for large steam turbine blades.
As known solution to the general problem of erosion, the use of protective layers has been suggested since the early thirties in a number of published patent documents such as the German patent DE 536278 C2. For composite blades, protective layers are described for example in published United States patent application US 2008/0152506 A1 and published international patent applications WO 2011/039075 A1 and WO 2010/066648.
Whilst the solution of applying a protective layer or coating may have the potential of reducing erosion at the exposed parts of the turbine blade, further improvements are required to render composite airfoils operational. In particular, it is seen as an object of the present invention to improve the way the protective layer and the composite core of a turbine airfoil are joined.
The present disclosure is directed to a turbine blade having a root, a tip, an airfoil with a core section made of composite material and a protective sheath joined to the composite core at least in an area of the airfoil exposed to erosion. The composite core of the airfoil is continuous from a location in vicinity of the root to a location in a vicinity of the tip of the blade and includes a section which widens from the rotational axis along the length of the airfoil and which ends at the location in the vicinity of the tip of the blade.
The present disclosure is also directed to a method of manufacturing a blade for a steam turbine. The method includes providing a core continuously extending from a location in the vicinity of a root section of the blade to a location in the vicinity of a tip section of the blade and surrounding the core of composite material with a protective sheath of a different material. The method also includes increasing the width of the core of composite material at least at the vicinity of the tip end of the blade.
Exemplary embodiments of the invention will now be described, with reference to the accompanying drawings, in which:
According to an aspect of the present invention, there is provided an airfoil of a turbine blade, preferably the rotating blade, with a root and a tip portion with the airfoil having a continuous core made of composite material and being continuous from the root portion to the tip portion and a protective sheath joined to the composite core at a location or locations exposed to erosion, wherein the core widens at least in proximity of the tip portion.
According to a preferred embodiment of this aspect of the invention a movement of the protective sheath along the core in radially-outward direction is prevented by an interference fit between the widening core and the protective sheath.
When referring to a radial direction, such direction is defined as the radial direction from the rotational axis of the turbine rotor.
In a preferred embodiment of this aspect of the invention, the interference fit is achieved by a continuous or step-wide widening of the composite core with distance from the rotational axis. This widening can result in an increased length of the circumference of cross-sections of the airfoil taken perpendicular to the radial direction or, more specifically to turbine blades, in an increase of the airfoil's chord length or profile thickness in direction towards its tip. In a variant of this embodiment, the chord length, as a function of the radial distance, has at least one section in proximity to the tip where the chord length increases as a function of the radial distance, and may have a first section where the chord length decreases as a function of the radial distance followed by the section where the chord length increases as a function of the radial distance when looking along the blade from its root to the tip.
The airfoil is understood herein as the aerodynamically-formed part of the blade that causes the desired reaction force on the rotor when in motion relative to the surrounding medium. The term excludes the so-called root part of the blade, which is used to anchor the blade in the rotor, and any shroud part, which in some of the known blade designs are used to interlock with the shroud part of the neighboring blades to form a sealing or stabilizing circumferential ring around the assembled blades. The main orientation of the shroud is thus in circumferential direction, whereas the airfoil and any specific tip extensions of the airfoil, such as winglets, are oriented towards the flow direction of the medium. Other stabilizing parts, such as snubbers, are also not included in the term “airfoil” as used herein.
The shape of the new airfoil is typically a complex three-dimensional shape, which widens towards the tip in what could be described as an inverted cone section. The inverted cone shape provides an interference fit preventing any relative motion in the radial direction between the protective sheath and the composite core, thus reinforcing any additional fixing between the two. But it is important to note that the inverted cone shape of the blade can have advantages beyond the improvement to the stability of the joint between the protective sheath and the composite core.
In a preferred variant of this aspect of the invention the widening section of the core ends at the tip or very close to the tip of the airfoil. However, the location of its starting point along the length of the blade is very much subject to design consideration such as stability, weight and desired flow-off area.
In another preferred embodiment of this aspect of the invention the protective sheath is joined with the composite core through a bonding or adhesive layer such as a glue foil. The new design of the blade in accordance with the invention acts to support and, in case of its failure, replaces the foil to prevent a rupture or loosening of the protective sheath.
In a further preferred embodiment the protective sheath is a metal layer. The layer is advantageously assembled from several parts, for example a thick part designed to cover the leading edge of the blade and any adjacent areas of high erosion, a second part designed to cover the trailing edge of the airfoil and two thin sheet-like parts to cover the remaining exposed areas on the pressure and suction side of the airfoil.
The manufacturing of a composite airfoil or blade in accordance with the present invention can generally follow the known manufacturing steps for composite blades. These methods include for example the use of strands or woven pieces of the composite fiber material. In a preferred embodiment of this aspect of the invention, additional fiber material is added at the tip of the airfoil to the strands or woven mats, which make up the main part of fiber material for the continuous core. After adding fiber material at the tip, the core material is impregnated with the matrix material as in conventional designs.
These and further aspects of the invention will be apparent from the following detailed description and drawings as listed below.
Aspects and details of examples of the present invention are described in further details in the following description using the example of a last stage rotor blade for a steam turbine.
Shown in
A horizontal, i.e. perpendicular to the radial direction, cross-section along the arbitrarily chosen line A-B of the airfoil 12 is shown in
In generally, the chord can be regarded as one of the possible measures determining the width of the airfoil. Other such possible measures are the circumference of a horizontal cross-section of the blade or its area, the profile thickness, or the length of the middle or camber line 127. It is possible to refer to the increase of any one of such measures as an increase in width or widening of the airfoil. However, to increase the length of chord or any equivalent thereof towards the tip of the blade is seen as the most effective way of implementing the present invention.
The widening by means of increasing the chord length is illustrated in
Though the true shape of a modern airfoil is a complex three-dimensional shape, the chord length of most modern last stage steam turbine airfoils follows the profile 21. This profile 21 indicates a continuously decreasing chord length as is characteristic of a general conical shape. For the new profile 22-1 however the chord length L increases—in the example shown continuously—toward the tip of the blade. The increase or widening can also start close to the root of the blade. Such an alternative example of the invention is represented by the curve 22-2.
With the widening airfoil design in accordance with the present invention it is possible to reduce the number of blades in the last stage to below 40, and potentially below 35, even for the largest steam turbines.
Another way of visualizing examples of the present invention is chosen in
Though the two-dimensional projection into the paper plane of
Any protective sheath which is wrapped around the core of the new airfoil near the tip is forced into interference fit by the widening of the core at the tip. This interference fit is particularly important in cases where the protective sheath is joined with the core by a bonding or adhesive layer. In operation, such blades are exposed to high temperatures and centrifugal forces and, if the bond fails, the protective sheath could fly off the blade and damage other parts of the turbine.
The interference fit prevents the loosening of the protective sheath unless it disintegrates completely. The design counteracts the forces created by the fast rotation of the blade in operation.
Steps of manufacturing a composite blade in accordance with an example of the present invention are described in the following making reference to
A composite airfoil or blade in accordance with an example of the present invention can for example be prepared using the vacuum infusion process known per se. In such a process a woven mesh of fibers is spread in a die, which approximates the shape of the airfoil to be manufactured. Additional fiber material is added at the tip of the airfoil to the strands or woven mats. After adding fiber material at the tip, the fiber material is impregnated under vacuum conditions in the die with the matrix material such as resin.
Other known manufacturing methods such as hand laminating can be used. Variants such as prepreg or wet layup can also be applied. An overview of known method to produce a core of composite material is published for example in the international patent application WO 2011/039075. However for the purpose of the present invention and the sake of clarity, no further details of these standard methods are reiterated herein.
Once the composite core is prepared and metal sheets which make up the protective layer are formed and cut or machined, both are joined in a combined process involving steps of welding and gluing as described below when making reference to
In
A cross-section of the blade 30 along line A-B is shown in
The airfoil 32 is assembled by joining first the edge cover 34, the covering sheet 35 for the suction side and the trailing edge cover 36 at the two welding seams 381, 382. The core material 33 surrounded by an adhesive layer 39 is then placed into the recess formed by the welded parts and the covering sheet 37 for the pressure side is placed on top to completely enclose the core. The covering sheet 37 for the pressure side is joined at the welding seams 383, 384. These latter welding seams 383, 384 are located at the edges of recesses machined into the leading edge cover 34 and the trailing edge cover 36, respectively, to avoid thermal damage to the adhesive layer and the core during the welding process.
The present invention has been described above purely by way of example, and modifications can be made within the scope of the invention. For example the sheath which surrounds the core can be replaced by a partial cover which while limited to sections of the core particularly exposed to erosion is shaped to maintain interference fit as described.
The invention also consists in any individual features described or implicit herein or shown or implicit in the drawings or any combination of any such features or any generalization of any such features or combination, which extends to equivalents thereof. Thus, the breadth and scope of the present invention should not be limited by any of the above-described exemplary embodiments. Each feature disclosed in the specification, including the drawings, may be replaced by alternative features serving the same, equivalent or similar purposes, unless expressly stated otherwise.
Unless explicitly stated herein, any discussion of the prior art throughout the specification is not an admission that such prior art is widely known or forms part of the common general knowledge in the field.