The invention concerns a turbine engine casing and a method for manufacturing a turbine engine casing.
The ring 103 of the intermediate casing 102 comprises a plurality of fastening elements, which allow the fastening of turbine engine members to the casing 102, such as the accessory drive module (or ADM.)
Such an intermediate casing is for example described in the patent FR2925120 or in the patent application FR1262269.
The intermediate casing 102 is conventionally manufactured by machining into the body of a raw bulk of aluminum, steel or titanium. The members to be assembled are subsequently added to the part formed by machining the bulk.
This solution has several drawbacks.
It involves complex machining steps, which leads to an increase in manufacturing costs.
Furthermore, it is necessary to add the fastening elements to the part, which makes the part heavier due to the weight of the additional washers, screws and flanges that make the assembly possible.
To improve the existing solutions, the invention proposes a method for manufacturing a turbine engine casing, characterized in that it comprises the steps consisting in:
The invention is advantageously completed by the following features, taken alone or in any one of their technically possible combinations:
The invention further concerns a turbine engine casing, characterized in that it comprises a ring composed of an assembly of a plurality of sectors, at least a part of the sectors being manufactured in a single piece with attaching elements on their surface by a casting method.
According to an embodiment, the sectors are made of titanium.
According to an embodiment, the sectors comprise assembling strips at their ends, via which the sectors are assembled.
In particular, the assembling strips have a constant width, and/or the assembling strips have a height, the profile of which follows the variation of the thickness profile of the ends of the sectors.
Finally, the invention concerns a turbine engine comprising a fan and a casing as described previously.
The invention has many advantages.
The manufacturing of the sectors by casting makes it possible to incorporate the attaching elements as from the manufacturing stage, which avoids subsequent steps of joining on and bolting additional parts. The associated weight and costs are thus reduced.
The solution reduces the number and complexity of the machining steps required for the manufacturing of the casing.
In addition the solution offers a good compromise between the weight of the casing and the manufacturing costs.
Furthermore, the casing comprising a plurality of sectors of smaller size than the casing itself, the manufacturing operations can thus be carried out by a greater number of smelters.
The modest size of the sectors thus makes it possible to improve the casting form tolerance.
Finally, the solution is applicable even to casings of large dimensions, the casing being subdivided into several sectors of smaller dimensions.
Other features and advantages of the invention will yet become apparent from the following description, which is purely illustrative and non-limiting, and must be read with reference to the appended drawings wherein:
The figures depict the different steps and elements for manufacturing a turbine engine casing 1.
This can for example be the so-called intermediate casing 1 which is juxtaposed on the fan casing in the turbine engine, as already illustrated in
A plurality of sectors 2, such as those illustrated in
The sectors 2 comprise attaching elements 3 on their surface. These attaching elements 3 notably comprise bosses or clevises for fastening axes, flanges, arms, or any mechanical part of the turbine engine connected to the casing 1. The attaching elements 3 are manufactured in the casting step.
Thanks to the casting process, the sectors 2 are manufactured in a single piece with the attaching elements 3 on their surface, which avoids the steps of bolting and joining on additional parts.
Conventionally, the sectors 2 comprise ribs 7 acting as stiffeners of the structure. These ribs 7 are also manufactured in the casting step.
After manufacturing the sectors 2 by casting, they are assembled end-to-end so as to form a ring 5 of the casing 1.
The assembly of the sectors 2 can for example be carried out by welding. Other assembly operations are possible, such bolting sectors 2 together, for example.
In a variant, the assembly comprises a hot forming operation for improving the circularity of the ring 5 of the casing 1.
In a variant embodiment, a part of the sectors 2 to be assembled is manufactured using a different manufacturing method, such as lamination, particularly of circular type.
The manufacturing of the sectors 2 can comprise obtaining assembling strips 8 at the ends of the sectors 2, via which the sectors 2 are assembled. These strips 8 are obtained by incorporation via casting or by being made as a single part with the sectors 2.
These assembling strips 8 are manufactured in the casting step. Consequently, these are also of a single piece with the sectors 2, and do not require the joining on of additional parts.
These assembling strips 8, present at the ends of the sectors 2 having a raw casting outer face 8a requiring machining. Machining of the raw outer face 8a of the strips 8 (step E2) is performed before assembling the sectors.
The strips 8 notably facilitate the operations of welding or bolting the sectors 2 together, and reducing the variations in thickness at the ends of the sectors 2.
Different shapes of assembling strip 8 can be used. A simple shape is that of a parallelepiped.
According to an exemplary embodiment, the assembling strips 8 have a constant width L. The width is the dimension of the assembly strip 8 along the axis tangential to the ring 5 formed by the sectors 2 (see
This choice of a constant width L allows for better diffusion of the welding energy, or a sufficient distribution of material for bolting forces uniformly distributed and use of identical screws.
The height H of the assembling strips 8 can be constant or variable.
It is preferable that the height H has a variation, the amplitude of which is limited (in particular, sudden variations, of stair step type, are to be avoided), in order to facilitate the welding of the strips 8 together.
According to an exemplary embodiment, the height H has a profile that follows the variation of the thickness profile of the ends of the sectors 2.
The profile of the height H is not strictly identical to the profile of the thicknesses of the ends of the sectors 2, in order to avoid having variations in stair step shape, but follows the general shape of it.
This is notably visible in
The sectors 2 are angular sectors, the angular extent of which varies according to various criteria such as the desired number of sectors of the ring, the diameter of the casing to be manufactured, the manufacturing tolerances of the casting operation, and the position of the attaching elements 3 on the sectors 2.
The ring 5 comprises at least two sectors 2, but can also comprise a higher number of sectors 2 (for example, in the case of a ring of a diameter equal to 2 m, ten or so sectors of a cord of 600 mm approximately).
The angular extent of the sectors 2 is chosen such that the assembling strips 8 located at their ends are not in contact with the attaching elements 3 of the sectors 2.
Furthermore, it is desirable to dispose as many sectors 2 with a same angular extent as possible, in order to reduce the number of different raw bulks required for their manufacturing, and thus the manufacturing costs.
After assembly (step E3) of the sectors 2 via their assembling strips 8, the strips 8 can be, at least partly, machined (step E4). This machining makes it possible to reduce the thickness of the strips 8 to a strict minimum, in order to reduce the weight of the casing 1. Advantageously, the strips 8 are removed by machining (see
Furthermore, the sectors 2 are machined after their assembly so as to form additional fastening elements 12 on the surface of the sectors 2.
These additional elements 12 are for example elements, the manufacturing tolerances of which are narrow and cannot be achieved in the casting step. This is the case, for example, of openings worked in the ribs 7 of the sectors 2.
According to an embodiment, the sectors 2 are made of titanium. Titanium is known for its good mechanical resistance and its good fire resistance. It becomes possible to significantly reduce the thicknesses of flanges or bodies.
This choice of material thus reduces the weight of the casing 1 compared to other known materials, such as aluminum, the use of the latter being less suitable given its lesser mechanical and fire resistance.
Furthermore, the manufacturing of the casing 1 by way of an assembly of a plurality of sectors 2 resulting from a casting method makes it possible to reduce the material needed for the raw bulks, particularly as regards solutions involving machining into the body of a single bulk. Indeed, the ratio of the material of the final part to the material of the raw bulk is clearly more advantageous in this solution than in a machining into the mass of a single bulk.
Consequently, although titanium has a greater cost than aluminum and poses machinability problems, the cost generated by the choice of titanium as the raw bulk material is low, aluminum also posing molding problems in casting operations.
The manufacturing of the sectors 2 by casting also makes it possible to incorporate the attaching elements 3 on the surface of the sectors 2 from the manufacturing stage of the sectors, which avoids subsequent steps of joining and bolting additional parts. The associated weight and costs are thus reduced.
The pre-forming of the sectors 2 by casting further reduces the number and complexity of the machining steps, which further reduces the associated costs.
The solution applies to any turbine engine casing. It is particularly applicable to the intermediate casing of the turbine engine, downstream of the fan casing along the flow direction of the stream.
It is advantageously, but not limitingly, applicable to casings of large dimensions, i.e. with a diameter greater than 1.50 meters.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1357487 | Jul 2013 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2014/051935 | 7/25/2014 | WO | 00 |