Patent Application
20200025012
The present disclosure relates generally to gas turbine engines, and more specifically to shrouds that radially encompass the turbine in gas turbine engines.
Gas turbine engines are capable of higher efficiencies when operated at higher temperatures. However, operation of the engine at such higher temperatures may negatively affect the properties of metal components traditionally used in gas turbine engines. Even with the introduction of complex cooling systems, there remains a practical maximum operating temperature for gas turbine engines constructed primarily from metal alloys and, consequently, a ceiling on the efficiency of such engines.
One alternative to improve the efficiency of gas turbine engines is to use ceramic matrix composite (CMC) materials for certain components in the engine that have traditionally been formed from metal alloys. CMC materials are not as susceptible as metallic components to the degradation of material properties caused by the high operating temperatures that are desired to improve the efficiency of the engine. However, despite favorable thermal properties of the CMC material components, the CMC material components have an allowable stress which is an order of magnitude lower than the component formed from metal alloys, a high degree of stiffness, and a significantly lower thermal expansion rate than metallic components, leading to poor load distribution at transfer points. With these limitations, CMC material components cannot merely be substituted for equivalent metal alloy components of identical geometric structures and subjected to the same pressure loading without exceeding the allowable stresses of the CMC material.
Despite these limitations, the advantages of CMC materials in high temperature applications have led to their limited use in gas turbine components such as turbine blade track sealing segments. Circumferentially surrounding a rotating turbine blade wheel, a static blade track sealing shroud is designed to maximize the working air flowing through the turbine blades by minimizing the amount of air which leaks by the blade tips, thereby increasing the efficiency of the engine. Such sealing shrouds are frequently composed of a plurality of segments positioned around the turbine axis. Due to the segmented nature of the shroud, the shroud requires seals between the segments in order to block air from escaping the working air flow path through any potential segment-to-segment gaps.
A typical CMC sealing segment comprises a u-shaped component. The thin, flanged edges of the u-shaped sealing segment are machined with holes and slots for mounting pin attachment. While machining CMC materials is not desirable as they are susceptible to shorter lifespans due to recession in the hot, humid gas turbine environment, the u-shaped design requires machining of holes and, in particular, a slot to allow relative motion between the CMC sealing segment and metal alloy support structures due to different rates of thermal expansion between these materials. Additional machining of u-shaped CMC segments is required to support inter-segment seals. Further, using thin walls in the sealing segment subjects the CMC material to high edge loading stresses due to the small contact area between the CMC wall and the mounting pin. These high stresses severely limit any residual load capacity in the CMC material such that it is limited to use in low pressure applications.
There exists a need for novel CMC structures and mounting techniques which allow the use of CMC materials in high pressure, high temperature gas turbine seal segment applications.
The present application discloses one or more of the features recited in the appended claims and/or the following features which, alone or in any combination, may comprise patentable subject matter.
According to an aspect of the present disclosure, a segmented turbine shroud for radially encasing a rotatable turbine in a gas turbine engine comprises a carrier, a ceramic matrix composite (CMC) seal segment, and an elongated pin. The carrier comprises at least one generally planar flange extending radially inward toward the turbine perpendicular to the axis of rotation of the turbine, the flange comprising a portion defining a pin-receiving carrier bore having an axis parallel to the axis of rotation of the turbine. The CMC seal segment comprises a portion defining a pin-receiving seal segment bore. The elongated pin extends through the carrier bore and the seal segment bore. The carrier portion defining the pin-receiving carrier bore includes a member extending axially from the flange to thereby define the carrier bore having a length greater than the axial dimension of the flange, the member having a length sufficient to effect radial flexion between the member and the pin received within the carrier bore during operation of the gas turbine engine.
In some embodiments, the length of the carrier bore is at least 120% of the axial dimension of the flange. In some embodiments, the carrier portion defines a carrier bore comprising a continuously curved lateral cross-section, while in other embodiments the carrier portion defines a carrier bore having a circular lateral cross-section. In some embodiments, the carrier bore is adapted to receive an elongated pin comprising a lateral cross-sectional dimension of at least three eighths inches.
In some embodiments, the elongated pin is hollow. In some embodiments, the shroud further comprises a bushing disposed around the elongated pin within the carrier bore. In some embodiments, the carrier bore comprises a chamfered end. In some embodiments, the carrier bore comprises a minimum lateral cross-sectional dimension of at least three eighths inches.
According to an aspect of the present disclosure, a segmented turbine shroud for radially encasing a rotatable turbine in a gas turbine engine comprises a plurality of cartridges, and one or more of the plurality of cartridges comprises a carrier segment, a ceramic matrix composite (CMC) seal segment, and a plurality of elongated pins. The carrier segment comprises a plurality of opposing portion pairs, each portion defining a pin-receiving carrier bore having a circular lateral cross-section, each opposing portion pair being aligned to receive a single elongated pin within the opposing pin-receiving carrier bores defined thereby. The CMC seal segment comprises a plurality of portions each defining a pin-receiving seal segment bore. The plurality of elongated pins each extend through a pair of opposing pin receiving carrier bores and one or more of the seal segment bores, and the carrier segment carries a single CMC seal segment by one or more of the elongated pins.
In some embodiments, each of the carrier bores is adapted to receive an elongated pin comprising a lateral cross-sectional dimension of at least three eighths inches. In some embodiments, the carrier portion defining the pin-receiving carrier bore comprises a generally planar flange extending radially inward toward the turbine perpendicular to the axis of rotation of the turbine and a member extending axially from the flange to thereby define the carrier bore has a length greater than the axial dimension of the flange.
In some embodiments, the length of the carrier bore is at least 120% of the axial dimension of the flange. In some embodiments, the shroud further comprises a radially compressible bushing disposed around the elongated pin within the carrier bore. In some embodiments, the carrier bore comprises opposing ends which are chamfered. In some embodiments, the carrier segment comprises at least three opposing portion pairs, each portion defining a pin-receiving carrier bore having a circular lateral cross-section, each opposing portion pair being aligned to receive a single elongated pin within the opposing pin-receiving carrier bores defined thereby.
According to an aspect of the present disclosure, a segmented turbine shroud for radially encasing a rotatable turbine in a gas turbine engine comprises a carrier, a ceramic matrix composite (CMC) seal segment, and an elongated pin. The carrier comprises a portion defining a pin-receiving carrier bore. The CMC seal segment comprises a portion defining a pin-receiving seal segment bore. The elongated pin extends through the carrier bore and the seal segment bore. The carrier portion defining the carrier bore further comprises at least one linear aperture proximate the carrier bore adapted to effect radial flexion between the carrier portion defining the carrier bore and the pin received therein during operation of the gas turbine engine.
In some embodiments, the carrier portion comprises a plurality of linear apertures proximate the carrier bore adapted to effect radial flexion between the carrier portion defining the carrier bore and the pin received therein during operation of the gas turbine engine. In some embodiments, the carrier bore comprises a minimum lateral cross-section dimension of at least three eighths inches.
The following will be apparent from elements of the figures, which are provided for illustrative purposes and are not necessarily to scale.
While the present disclosure is susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and will be described in detail herein. It should be understood, however, that the present disclosure is not intended to be limited to the particular forms disclosed. Rather, the present disclosure is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the disclosure as defined by the appended claims.
For the purposes of promoting an understanding of the principles of the disclosure, reference will now be made to a number of illustrative embodiments illustrated in the drawings and specific language will be used to describe the same.
This disclosure presents numerous embodiments to overcome the aforementioned deficiencies of CMC components when used in gas turbine engines. More specifically, this disclosure is directed to gas turbine shrouds which accommodate the low stress allowable, high stiffness, and lower thermal expansion of CMC components when compared to traditional metal alloy components.
An illustrative aerospace gas turbine engine cut-away in
Referring now to
The turbine 18 also includes a turbine shroud 110 that extends around turbine wheel assembly 26 to block combustion products from leaking past the blades 36 without pushing the blades 36 to rotate the wheel assembly 26 as shown in
The turbine shroud 110 illustratively includes a mount ring 112, a retainer ring 114, and a plurality of shroud segments 120 as shown in
One embodiment of the present disclosure is directed to a system and method for reducing the radial pressure load on a CMC seal segment in a turbine shroud segment. As illustrated in
As a first example, an embodiment is presented in
In this embodiment, carrier segment 134 comprises an axial flange 150 and one or more lateral flanges extending radially inward from the axial flange 150. In some embodiments, carrier segment 134 has a leading edge lateral flange 171, trailing edge lateral flange 172, first side lateral flange 168, and second side lateral flange 169. In other embodiments, carrier segment 134 comprises an axial flange 150 having a single, continuous lateral flange extending radially inward along the entire perimeter of axial flange 150. In some embodiments, carrier segment 134 is formed from high temperature nickel alloy.
The axial flange 150 extends axially along the axis 20 (which is the axis of the rotation of the turbine) and is adapted to engage the mount ring 112 and to support the CMC seal segments 136 as shown in
In some embodiments, leading edge lateral flange 171 defines a leading edge carrier bore 190 and trailing edge lateral flange 172 defines a trailing edge carrier bore 191. Each lateral flange 171, 172, 168, 169 has a radially inward-facing surface 173 (as shown in
In one embodiment, a CMC seal segment 136 comprises an arcuate flange 162 and one or more pin bore flanges 180. The arcuate flange 162 extends around the blades 36 of the turbine wheel assembly 26 and blocks gasses from passing around the blades 36. Accordingly, the arcuate flanges 162 of each CMC seal segment 136 cooperate to define the outer edge of the flow path for air moving through the turbine 18. As illustrated in
The one or more pin bore flanges 180 each define a segment bore 181 and extend outward in the radial direction from arcuate flange 162. In some embodiments, a pin bore flange 180 and spacing flange 183 are collectively referred to as a radial member. The CMC seal segment 136 illustrated in
As another example, an embodiment is presented wherein a CMC seal segment 136 is carried by carrier segment 134 by a forward hanger arm 164 and an aft hanger arm 166.
In some embodiments, leading edge lateral flange 171 includes a leading edge hanger bracket 156 and trailing edge lateral flange 172 includes a trailing edge hanger bracket 158 adapted to support CMC seal segment 136. Each lateral flange 171, 172, 168, 169 has a radially inward-facing surface 173 (as shown in
As illustrated in
The forward and the aft hanger arms 164, 166 support the arcuate flange 162 relative to a corresponding carrier segment 134. The forward hanger arm 164 is adapted to engage the leading edge hanger bracket 156 of carrier segment 134. The aft hanger arm 166 is adapted to engage the trailing edge hanger bracket 158 of carrier segment 134.
In other embodiments, the direction of the axial extension of one or both of the forward and the aft hanger arms 164, 166 may be reversed. In one example, the forward hanger arm 164 could extend rearward in the axial direction and the aft hanger arm 166 could also extend rearward. In another example, both the forward hanger arm 164 and the aft hanger arm 166 could extend forward in the axial direction.
The carrier segment 134 of the above embodiments is illustratively made from a metal alloy but in some embodiments may be made from a ceramic material, a composite material such as a CMC material, or another suitable material. The CMC seal segment 136 of each shroud segment 120 is illustratively a monolithic ceramic component made from ceramic-matrix-composite materials (CMCs) that are adapted to withstand high temperature environments. In other embodiments, the CMC seal segment 136 of each shroud segment 120 may be made from other materials.
The embodiments of
In some embodiments, first pressurized air and second pressurized air supplied to first conduit 202 and second conduit 204, respectively are supplied from the same pressurized air supply such that channel 175 is buffered at an equal pressure throughout. For example, first pressurized air and second pressurized air can both be supplied from compressor 14 discharge air or from the pressurized air of the seventh stage of compressor 14, designated HP7. In other embodiments, first pressurized air is supplied from a different pressurized air supply than second pressurized air, such that channel 175 is buffered at an unequal pressure throughout. For example, first pressurized air can be supplied from compressor 14 discharge air while second pressurized air can be supplied from the pressurized air of the seventh stage of compressor 14, designated HP7. As another example, first pressurized air can be supplied from the pressurized air of the seventh stage of compressor 14, designated HP7, while second pressurized air can be supplied from the pressurized air of the third stage of compressor 14, designated HP3. Effective buffering can still be achieved while supplying different air pressures to the leading and trailing edge channels 175 because the flowpath pressure of the combustion products drops across the turbine blades 36.
In general, it is desirable to provide pressurized air to channel 175 at a higher pressure than the pressure of the combustion products passing over the blades 36, which is referred to as the flow path air pressure. Buffering channel 175 with air at a greater pressure than flow path air pressure aids in reducing leakage of flow path air from the flow path.
In some embodiments, first pressurized air and second pressurized air supplied to first conduit 202 and second conduit 204, respectively, are at a different pressure than third pressurized air supplied to third conduit 206 such that channel 175 and cavity 170 are buffered at different pressures. For example, first pressurized air and second pressurized air can be supplied from compressor 14 discharge air while third pressurized air is supplied from the pressurized air of the seventh stage of compressor 14, designated HP7. As another example, first pressurized air and second pressurized air can be supplied from the pressurized air of the seventh stage of compressor 14, designated HP7, while third pressurized air can be supplied from the pressurized air of the third stage of compressor 14, designated HP3. In some embodiments, the third air pressure is supplied at a pressure lower than the pressure of the flow path combustion products. In other embodiments, the third pressurized air may be supplied from the compressor discharge or an intermediate stage at a pressure higher than that supplied to the first or second pressurized air.
In other embodiments, first pressurized air, second pressurized air, supplied to first conduit 202 and second conduit 204, respectively, and third pressurized air supplied to third conduit 206 are supplied from the same pressurized air source or are supplied by pressurized air sources at the same pressure such that channel 175 and cavity 170 are buffered at equal pressures.
In some embodiments, a compressible mating element 176 is disposed in each of first portion 198 and second portion 199. In other embodiments, one or both of first portion 198 and second portion 199 do not contain a compressible mating element 176. With an unsealed second portion 199, cavity 170 is vented to the flow path.
In some buffered embodiments, first portion 198 and second portion 199 are supplied with pressurized air from the same pressurized air source, such that first portion 198 and second portion 199 are buffered at equal pressures. For example, first portion 198 and second portion 199 can both be supplied with pressurized air from compressor 14 discharge air or from the pressurized air of the seventh stage of compressor 14, designated HP7. In other buffered embodiments, first portion 198 and second portion 199 are supplied with pressurized air from different pressurized air sources such that first portion 198 and second portion 199 are buffered at unequal pressures. For example, first portion 198 can be supplied with pressurized air from compressor 14 discharge air while second portion 199 can be supplied with pressurized air from the seventh stage of compressor 14, designated HP7. As another example, first portion 198 can be supplied with pressurized air from the seventh stage of compressor 14, designated HP7, while second portion 199 can be supplied with pressurized air from the third stage of compressor 14, designated HP3. Where second portion 199 is supplied with pressurized air at a lower pressure than cavity 170, cavity 170 is vented through the second portion 199 to the flow path. In some embodiments, the cavity 170 is vented to the trailing edge of the second portion through an additional channel or conduit (not shown) in the aft lateral flange 172. This embodiment may also be utilized when the channel 175 is not divided into a first and second portion 198, 199.
In further embodiments, first portion 198 is supplied with a first pressurized air while second portion 199 is not supplied with pressurized air. With an unbuffered second portion 199, cavity 170 is vented to the flow path. In some embodiments, the cavity 170 is vented to the trailing edge of the second portion through an additional channel or conduit (not shown) in the aft lateral flange 172. This embodiment may also be utilized when the channel 175 is not divided into a first and second portion 198, 199.
In still further embodiments, first portion 198 and cavity 170 are supplied with pressurized air at the same pressure while second portion 199 is supplied with pressurized air at a lower pressure. For example, first portion 198 and cavity 170 are supplied with discharge air of compressor 14 while second portion 199 is supplied with the pressurized air of the seventh stage of compressor 14, designated HP7. In such an embodiment, cavity 170 is vented through the second portion 199 to the flow path. In some embodiments, the cavity 170 is vented to the trailing edge of the second portion through an additional channel or conduit (not shown) in the aft lateral flange 172. This embodiment may also be utilized when the channel 175 is not divided into a first and second portion 198, 199.
In some embodiments it is desirable to supply pressurized air to channel 175 at a higher pressure than the pressurized air supplied to the cavity 170 in order to prevent leakage from the flow path into the cavity 170.
Traditional designs of cartridge-style CMC seal segments 136 and carrier segments 134 require discharge air from the compressor 14 be supplied to the cavity 170 or to the outer-facing surface 182 of the CMC seal segment 136. This air is supplied both to cool the CMC seal segment 136 and to prevent leakage from the flow path in a radial direction past the CMC seal segment 136. However, supplying discharge air from the compressor 14 creates a high pressure load across the CMC seal segment 136 in the radial direction. By allowing the pressurized air supplied to the cavity 170 to be at a lower pressure than the pressure of discharge air from the compressor 14, the disclosed embodiments of a shroud segment 120 with a mating region 174 or buffering region 207 reduce pressure loads in the radial direction across the arcuate flange 162 of the CMC seal segment 136 resulting in longer lifespans for components. While the pressurized air supplied to the cavity 170 may be at a higher pressure than the trailing-edge flow path pressure such that cooling or purge air will vent to the flowpath, this supplied air pressure may be sufficiently low to allow a negative pressure gradient over the forward portion of the CMC seal segment 136 where the flow path air pressure is highest. When the pressures are balanced correctly, the net load between the CMC seal segment 136 and carrier segment 134 can be shifted from tension to compression by using a lower air pressure supplied to the cavity 170 than that used by traditional sealing segments. Traditional sealing segments do not use perimeter seals and therefore require higher air pressures to prevent flowpath air leakage.
The disclosed embodiments further achieve a work savings, since diverting air from an intermediate stage of the compressor 14 requires less work by the gas turbine engine than diverting discharge air of the compressor 14. Air from an intermediate stage is at a lower pressure and a lower temperature than discharge air, so that supplying air to the cavity 170 from an intermediate stage also has a greater cooling effect on the CMC seal segment 136. Less air is required to achieve the same cooling effect when air from an intermediate stage is used in favor of discharge air.
The shroud segment 120 embodiments disclosed herein additionally provide an ease of handling, assembly, and installation not available in the prior art. For example, operations such as match fitting or shimming, which are conducted to set the clearance between blades 36 of turbine wheel assembly 26 and the CMC seal segment 136, can be performed by altering a metal alloy carrier segment 134 instead of a CMC seal segment 136. This advantage will reduce or eliminate the machining of the CMC seal segment 136, which reduces assembly and installation costs and avoids damaging the CMC structure which can reduce CMC seal segment lifespan.
In some embodiments, the carrier segment 134 includes a static seal cover 901, 903 on the forward and aft lateral flanges 171,172 proximate to the forward carrier bore 190 and aft carrier bore 191 as shown in
The inward and outward facing surfaces 179, 182 of the arcuate flange 162, the inward facing surface 173 of the lateral flange 171, and the radially outward facing surface 1003 of the carrier segment 134 are shown as having generally parallel curves. In some embodiments, one or more of these surfaces may be machined with straight and orthogonal or other surface shapes.
Inter-segment seals may be used between shroud segments 120 to prevent leakage of flow path air between shroud segments. Inter-segment seals comprise strip seals or other suitable sealing means and are arranged circumferentially between shroud segments 120. In some embodiments, strip seals are located in slots machined into the carrier segment 134. Placing the inter-segment seals between adjacent carrier segments 134 allows for metal-to-metal sealing and avoids machining the CMC seal segment 136 in addition to the thermal stresses which would result from the different thermal expansion rates between the CMC seal segment and any inter-segment sealing element.
The plurality of shroud segments 120 are illustratively assemblies that are arranged circumferentially adjacent to one another to form a ring around the turbine wheel assembly 26 as shown, for example, in
The circumferential seal 130 may be located by inserting the circumferential seal 130 (illustratively a strip seal) into the seal-locating features 143, 145 (illustratively seal-receiving slots) formed in the carrier segments 134. In some embodiments, the circumferential seal 130 may be a plurality of small strip seals that are each inserted into the seal-locating features 143, 145 formed in the lateral flanges 168, 169 of carrier segments 134.
In some embodiments, the shroud segments 120 has metal to metal chordal seals between the nozzle guide vanes (not shown) and the carrier segment 134. While multiple forms of sealing techniques may be used, the carrier segment 134 with lateral flange 171 allows sealing the leading edge of the shroud segment 120 without requiring machining the CMC segment 136.
In some embodiments, the trailing edge of the shroud segment 120 is sealed to the aft vane with “W” or an omega seal. Specifically, this seal is connected to the aft face of the aft lateral flange 172 of the carrier segment 134. Alternative forms of seals can be used in this location with is subjected to lower pressures and temperatures than the leading face of the forward lateral flange 171.
Axial loads from the nozzle guide vanes are transferred to the carrier segment 134. Gussets or angled surfaces inside the carrier segment 134 may be used to transfer this load to the carrier hangers, such as hanger 152. In this arrangement, the carrier segment 134 isolates the CMC seal segment 136 from the axial loads transferred through the mating components and fore and aft seals.
Another embodiment of the present disclosure is directed to a system and method for reducing stresses caused by attaching the CMC seal segment to a carrier segment by providing a CMC seal segment with elongate pin bores.
Similar to the CMC seal segment 136 presented in
A series of arcuate flanges 162 extends circumferentially around the blades 36 of the turbine wheel assembly 26 and blocks gasses from passing around the blades 36 without impinging on the blades 36. Accordingly, the arcuate flange 162 of each CMC seal segment 136 cooperate to define the outer edge of the flow path for air moving through the turbine 18.
Arcuate flange has a leading edge 192, which may also be referred to as the forward edge, and a trailing edge 195, which may also be referred to as the aft edge. In some embodiments, the forward edge 192 and aft edge 195 are substantially perpendicular to the turbine axis 20. Arcuate flange 162 further has a first axial edge 193 and second axial edge 194 which, in some embodiments, are substantially parallel to the turbine axis 20. Further, arcuate flange 162 has an inward-facing surface 179 which is a curved surface facing the turbine blades 36 and an outward-facing surface 182 facing away from the turbine blades 36.
The one or more pin bore flanges 180 each define an elongate segment bore 181 adapted to receive an elongated pin 210. Various geometries of the inner surface 211 of segment bore 181 are contemplated. In some embodiments, segment bore 181 has a lateral cross-section with a continuously curved outer edge, meaning the inner surface 211 of segment bore 181 is continuously curved. In some embodiments, segment bore 181 has a lateral cross-section with a circular outer edge, meaning the inner surface 211 of segment bore 181 is circular and defines a cylindrical bore.
Segment bore 181 is envisioned with a larger lateral cross-section dimension, labeled D on
In some embodiments, the lateral cross-sectional dimension D of segment bore 181 varies along the length L1 of the segment bore 181.
In
In
Pin bore flanges 180 are connected to outward-facing surface 182 of arcuate flange 162 by spacing flanges 183. Each spacing flange 183 extends radially outward from arcuate flange 162 to effect receipt of an elongated pin 210 within the segment bore 181. The height H1 of each spacing flange 183 is determined to ensure alignment with associated bores of a carrier segment 134 as described further below in reference to
In some embodiments, spacing flange 183 tapers from pin bore flange 180 to arcuate flange 162 such that the length L3 of spacing flange 183 is less than the length L1 of pin bore flange 180. In other embodiments, spacing flange 183 is flush with pin bore flange 180 such that the length L3 of spacing flange 183 is equal to the length L1 of pin bore flange 180. Further, in some embodiments the length L1 of the pin bore flange 180 is equal to the length L2 of the arcuate flange 162, whereas in other embodiments the length L1 of the pin bore flange 180 is less than the length L2 of the arcuate flange 162. In some embodiments the length L3 of the spacing flange 183 and the length L1 of the pin bore flange is equal to the length of the arcuate flange 162.
The CMC seal segment 136 illustrated in
Similar to the shroud segment 120 presented in
CMC seal segment 136 is positioned in cavity 170 such that segment bore 181 aligns with forward cantilevered bore 215 and aft cantilevered bore 216. Thus an elongated pin 210 can be passed through forward cantilevered bore 215, segment bore 181, and aft cantilevered bore 216 to connect CMC seal segment 136 to carrier segment 134. A mating region 174 is defined proximate the entire perimeter of outward-facing surface 182 of the arcuate flange 162 of CMC seal segment 136.
CMC seal segment 136 is positioned in cavity 170 such that segment bore 181 aligns with forward through-thickness bore 217 and aft through-thickness bore 218. Thus an elongated pin 210 can be passed through forward through-thickness bore 217, segment bore 181, and aft through-thickness bore 218 to connect CMC seal segment 136 to carrier segment 134. A mating region 174 is defined proximate the entire perimeter of outward-facing surface 182 of the arcuate flange 162 of CMC seal segment 136.
In another embodiment, CMC seal segment 136 comprises an arcuate flange 162 and one or more segmented pin bore flanges 214.
A carrier segment 134 is illustrated in
CMC seal segment 136 is positioned in cavity 170 such that forward segment bore 220 and aft segment bore 221 align with forward through-thickness bore 217, aft through-thickness bore 218, and central carrier bore 224. Thus an elongated pin 210 can be passed through forward through-thickness bore 217, forward segment bore 220, central carrier bore 224, aft segment bore 221, and aft through-thickness bore 218 to connect CMC seal segment 136 to carrier segment 134. A mating region 174 is defined proximate the entire perimeter of outward-facing surface 182 of the arcuate flange 162 of CMC seal segment 136.
A variety of elongated pins 210 are contemplated for use with the disclosed CMC seal segment 136.
First elongated pin P1 comprises a solid pin. In some embodiments, first elongated pin P1 has a continuously curved or circular lateral cross-section. The illustrated first elongated pin P1 comprises a uniform outer lateral cross-sectional dimension D1. In some embodiments, first elongated pin P1 has an outer lateral cross-sectional dimension D1 of at least three-eighths inches, one half inch, five-eighths inches, or greater.
Second elongated pin P2 comprises a hollow pin. The illustrated second elongated pin P2 comprises a uniform inner lateral cross-sectional dimension D2 and uniform outer lateral cross-sectional dimension D1. In some embodiments, second elongated pin P2 has at least one continuously curved cross section D1 or D2. In some embodiments, inner lateral cross-sectional dimension D2 and outer lateral cross-sectional dimension D1 vary along the length of second elongated pin P2. In some embodiments, second elongated pin P2 has an outer lateral cross-sectional dimension D1 of at least three-eighths inches, one half inch, five-eighths inches, or greater. Hollow pins are advantageous for use in a pinned CMC seal segment as they allow for passing a bolt or similar attachment mechanism through the pin in order to secure a cover plate, cover seal, or static seal to a carrier segment. Hollow pins additionally provide lower radial stiffness which results in a wider contact region between pin and segment bore, and therefore results in lower contact stress. Further, a hollow pin has a lower weight than solid pins, which can be a concern in gas turbine engines.
Third elongated pin P3 comprises a split pin. A split pin comprises a hollow pin having a gap of width W. The illustrated third elongated pin P3 comprises a uniform inner lateral cross-sectional dimension D2 and uniform outer lateral cross-sectional dimension D1. In some embodiments, inner lateral cross-sectional dimension D2 and outer lateral cross-sectional dimension D1 vary along the length of third elongated pin P3. In some embodiments, third elongated pin P3 has an outer lateral cross-sectional dimension D1 of at least three-eighths inches, one half inch, five-eighths inches, or greater. Split pins are advantageous for use in a pinned CMC seal segment as they provide a reduced circumferential stress when compared to solid pins.
Fourth elongated pin P4 comprises a spiral rolled pin. A spiral rolled pin is formed from a sheet of material, typically metal alloy material, which is rolled into a cylinder. In some embodiments, a spiral rolled pin has several layers. The angle between a first end of the rolled material and a second end of the rolled material is measured as 0. In some embodiments, 0 is between 45 degrees and 135 degrees. The illustrated fourth elongated pin P4 comprises a constantly increased radii from a minimum inner lateral cross-sectional dimension D2 to a maximum outer lateral cross-sectional dimension D1. In some embodiments, inner lateral cross-sectional dimension D2 and outer lateral cross-sectional dimension D1 vary along the length of fourth elongated pin P4. In some embodiments, fourth elongated pin P4 has an outer lateral cross-sectional dimension D1 of at least three-eighths inches, one half inch, five-eighths inches, or greater. Spiral rolled pins are advantageous for use in a pinned CMC seal segment as they provide high radial compliance, reduced tensile and contact stresses, and have a high shear strength.
In still further embodiments, the lateral cross-sectional dimension of elongated pin 210 varies along the length of elongated pin 210. For example, fifth elongated pin P5 comprises a barreled pin having a greater lateral cross-sectional dimension at the longitudinal center than at either of opposing ends of the pin P5. Conversely, sixth elongated pin P6 comprises a crowned pin having a greater lateral cross-sectional dimension at either of opposing ends than at the longitudinal center of the pin P6. In still further embodiments, an elongated pin 210 has a minimum lateral cross-sectional dimension at a proximate end and a maximum lateral cross-sectional dimension at a distal end of the elongated pin 210. In some embodiments, pins such as elongated pins P5 and P6 improve the distribution of contact stresses between the elongated pin 210 and the segment bore 181 and or carrier bores, and also reduce edge loading. In some embodiments, elongated pins P5 and P6 are hollow as illustrated in
Elongated pins 210 with varying lateral cross-sectional dimensions are adapted to account for deflections of the pin and bore during operation such that a uniform load distribution occurs along the length of the segment bore 181. These types of pin profiles additionally tend to pull the pin surface away from the bore at the pin ends to avoid concentrated edge loading in the segment bore 181. In some embodiments such as illustrated in
In some embodiments, an elongated pin 210 used in the assembly of shroud segment 120 is formed from a high temperature nickel alloy or cobalt alloy. In some embodiments, an elongated pin 120 is formed from a metal alloy. In other embodiments, an elongated pin 120 is formed from ceramic material.
In some embodiments, an elongated pin 210 used in the assembly of shroud segment 120 is coated with an aluminide compound. An aluminide coating prevents or slows corrosion caused by silica-based CMC material interacting with a metal pin at the high operating temperatures typical for a gas turbine engine.
Additional embodiments are disclosed with variations in the number or design of pin bore flanges 180.
In some embodiments of the disclosed CMC seal segment 136, bushings 228 or bore liners are disposed within segment bore 181 to improve pin load distribution along the length of segment bore 181, to act as a thermal and/or diffusion barrier between the segment bore 181 and elongate pin 210, and to minimize wear caused by relative movement between the segment bore 181 and elongated pin 210 caused by thermal expansion differences.
In some embodiments, bushing 228 is formed from monolithic ceramic material, silicon-mononitride, silicon-nitride, or other suitable bushing material which may be bonded, welded, use a bimetallic clip, or attached to the segment bore 181 via another suitable mechanism. In other embodiments, bushing 228 is formed from a metal alloy such as a high temperature nickel alloy or cobalt alloy. The bushing 228 may also be manufactured using a cylindrical sleeve weave in order to ensure the bushing carries hoop stresses.
A further embodiment is provided wherein a CMC seal segment 136 includes a segment bore 181 with a retention feature 226.
Relative dimensions are disclosed of advantageous embodiments of a CMC seal segment 136.
Another comparison is provided between length L10 and the length L12 of first axial edge 193 of the arcuate flange 162 of CMC seal segment 136. In some embodiments, length L10 is at least 85% of length L12. In other embodiments, length L10 is at least 75% of length L12.
Similarly, in some embodiments length L10 is between 50% and 90% of the length L13 in the axial direction of carrier segment 134. In some embodiments, length L10 is between 60% and 70% of length L13. In further embodiments, length L10 is at least 70% of length L13.
In some embodiments, the height H2 of the radial member is greater than the thickness T2 of the arcuate flange 162. The height H2 may be twice or more than the thickness T2 of the arcuate flange 162. Spacing the segment bore 181 radially away from the flow path allows for the use of larger pins and other advantages as discussed below.
Finally, in some embodiments length L10 is greater than the thickness T1 of CMC seal segment 136. In some embodiments length L10 is greater than the thickness T2 of arcuate flange 162.
The above disclosed CMC seal segment 136 embodiments provide numerous advantages over the prior art. First, an elongate pin 210 is passed through a segment bore 181 and is supported on both ends by carrier bores. This design is advantageous over the prior art of cantilevered pins passed through through-thickness bores because it provides additional structural support for the pin and reduces pin deflection. Reduced pin deflection in turn results in reduced edge loading since such edge loading is typically caused by pin deflection against a stiff CMC segment bore. An elongate pin supported on both ends by carrier bores also improves load distribution across the pin.
Second, segment bores 181 are elongate, and in some embodiments are greater than one half inch. Elongated segment bores 181 are an improvement over through-thickness bores in that they provide additional structural support for the pin and allow for other carrier bore design features such as chamfers and surface profiling. Chamfering is possible in elongated segment bores 181 and helps prevent spalling of coating on surrounding surfaces by avoiding contact or by reducing edge loading between the pin and the coating. A shallower angle is better for minimizing edge loading, with the particular angle also being affected by any profiling to the pin and bore. Additionally, in cantilevered carrier bores as the length of the cantilevered member increases the vertical (radial) stress of the elongated pin on the carrier bore is reduced.
Third, segment bores 181 with a larger lateral cross-sectional dimension than those found in the prior art provides a greater bearing area, reduced peak contact stress, minimized pin bending and deflection, and avoidance of interference fit at operating temperatures. In some embodiments the segment bores 181 lateral cross-sectional dimension is greater than three-eighths of an inch. This greater lateral cross-sectional dimension is possible with the use of the spacing flange 183.
Fourth, the spacing flange 183 further distances the carrier and CMC segment bores 190, 181 and the elongated pins from the high temperature flow path and allows cooling air to flow around these components within the cavity 170. This results in drastically lower temperatures which minimizes the thermal stresses caused by differing thermal expansion rates of these components. As one example, the operating temperature of the flow path can reach 2800-2900 degrees F. with the inner- and outward-facing surfaces 179, 182 of the arcuate surface 162 reaching temperatures of 2150-2300 degrees F., and 1800 degrees F., respectively. By spacing the segment bore 181 with the spacing flange 183, the temperature proximate the elongated pin, segment bore 181, and carrier bore 190 may be reduced to as little as 1400 degrees F., or lower.
Another embodiment of the present disclosure is directed to a system and method of reducing stresses caused by varying rates of thermal expansion between unlike material components by providing flexible mounting of a CMC seal segment to a carrier segment. CMC materials have low thermal conductivity and low thermal expansion, leading to differential thermal expansion relative to non-CMC components such as elongated pins and carrier segments. These differential thermal expansions cause high stress in mating areas where CMC and non-CMC components are in close proximity. Such stresses are of particular concern given the low allowable stress of CMC materials such as a CMC seal segment.
In an embodiment of providing flexible mounting of a CMC seal segment 136 to carrier segment 134, the carrier segment 134 has a carrier bore bushing 301 disposed in each of a plurality of cantilevered carrier bores. An exemplary embodiment is provided in
As illustrated in
An elongate pin 210, exemplary of the solid pin type P1 described above, is disposed within each of the pair of carrier bore bushings 301. The location of a CMC shroud segment 136 having a pair of pin bore flanges 180 is illustrated in dotted lines in
The elongate pin 210 is further passed through a segment bore 181, as illustrated in
Forward lateral flange 171 includes a member 177 extending aft axially from the forward lateral flange 171 to define a carrier bore 303 which is cantilevered, having a length L20 greater than the axial dimension of the forward lateral flange 171, represented as length L21. Aft lateral flange 172 includes a member 178 extending axially forward from the aft lateral flange 172 to define a carrier bore 303 which is cantilevered, having a length L20 greater than the axial dimension of the aft lateral flange 172, represented as length L21. Axial flange 150, forward lateral flange 171, aft lateral flange 172, and arcuate flange 162 together define a cavity 170.
CMC seal segment 136 is positioned in cavity 170 such that segment bore 181 aligns with the carrier bore 303 defined by forward lateral flange 171 and the carrier bore 303 defined by aft lateral flange 172. A carrier bore bushing 301 is disposed within each carrier bore 303, and a segment bore bushing 228 is disposed within segment bore 181. Thus an elongated pin 210 can be passed through a forward carrier bore bushing 301, segment bore bushing 228, and an aft carrier bore bushing 301 to connect CMC seal segment 136 to carrier segment 134. The elongated pin 210 is illustrated as a solid pin.
In some embodiments, a compressible mating element 304 or plurality of compressible mating elements are arranged along the perimeter of the outer surface 182 of arcuate flange 162 of CMC seal segment 136 as suggested in
In some embodiments, a groove 305 is defined in the inward-facing surface 173 of one or more lateral flanges 171, 172 and compressible mating element 304 is disposed within the groove 305. In some embodiments, compressible mating element 304 is arranged along only a portion of the perimeter of the outer surface 182 of arcuate flange 162 of CMC seal segment 136. For example, in some embodiments compressible mating element 304 is not arranged along the trailing edge of arcuate flange 162 to allow for venting of cavity 170 into the flow path.
In some embodiments, carrier bore bushings 301 can be of the design disclosed above as radially compliant bushing 229. In some embodiments, segment bore bushing 228 can be replaced with radially compliant bushing 229.
In some embodiments, member 177 (and/or 178) has a length L20 sufficient to effect radial flexion between the member 177 (178) and the elongate pin 210 disposed within the carrier bore 303 defined by the member 177 (178). For example, in some embodiments member 177 (178) has a length L20 which is at least 120% the axial dimension L21 of the one or more lateral flanges 171, 172.
In some embodiments, a carrier bore 303 is defined having a continuously curved lateral cross-section. In some embodiments a carrier bore 303 is defined having a circular lateral cross-section. Further, in some embodiments carrier bore 303 has a lateral cross-sectional dimension of at least three-eighths inches, one half inch, five-eighths inches, or greater.
Carrier bore 303 includes a chamfered forward end 307. In some embodiments, carrier bore 303 has opposing chamfered ends.
In an exemplary embodiment, carrier bore retention feature 306 comprises a groove disposed circumferentially within carrier bore 303. An elongated pin 210 having a corresponding member for engaging retention feature 306 is inserted into carrier bore 303 and, upon engaging retention feature 306, provides reduced axial movement of the elongated pin 210 within the carrier bore 303. In embodiments having a carrier bore bushing 301 disposed within the carrier bore 303, the carrier bore bushing 301 may have a corresponding member for engaging retention feature 306 and be inserted into carrier bore 303 and, upon engaging retention feature 306, provide reduced axial movement of the carrier bore bushing 301 within the carrier bore 303. The disclosed member can take many forms, such as a full circumferential rib, an interrupted or segmented circumferential rib, a square or rectangular lateral cross-section, or a tapered outer diameter.
Although the embodiment described above with respect to
In further embodiments, a carrier segment 134 includes a mount bushing 310 connected to axial flange 150 by a flexible member 311.
In some embodiments, axial flange 150 is generally planar. In other embodiments, such as the embodiment illustrated in
Mount bushing 310 is connected to axial flange 150 by flexible member 311. Flexible member 311 provides a degree of flexibility to the mounting to allow for slight relative motion between the carrier segment 134 and the CMC seal segment 136 when assembled as shroud segment 120. In some embodiments, flexible member 311 is formed from a metal alloy. In some embodiments, flexible member 311 is formed from sheet metal.
Based on shape, size, and materials selected for construction, flexible member 311 is designed to achieve a desired degree of radial, lateral, and/or axial flexion during gas turbine operations. In some embodiments, flexible member 311 has a radial stiffness greater than the lateral stiffness. In other embodiments, flexible member 311 has a lateral stiffness greater than the radial stiffness.
As shown in
In other embodiments, a pair of mount bushings 310 may be disposed on both the forward and aft sides of segment bore 181, with an elongated pin 210 passing through a forward and aft mount bushing bores 314 and the segment bore 181 to connect each of the pair of mount bushings 310 to CMC seal segment 136. In such embodiments, mount bushings 310 may be referred to as mounting rings.
In some embodiments, carrier segment 134 further defines one or more carrier bores 303 in the one or more lateral flange 171 extending radially inward from axial flange 150. In such embodiments, carrier bores 303, mount bushing bores 314, and segment bores 181 are all in alignment with each other when carrier segment 134 and CMC seal segment 136 are assembled.
In some embodiments, a segment bore bushing 228 or radially compliant bushing 229 is disposed within segment bore 181. In some embodiments, mount bushing 310 is shaped as radially compliant bushing 229.
Additional exemplary embodiments for connecting a mount bushing 310 to carrier segment 134 are illustrated in
In
In
Although the exemplary embodiments of
In
In some embodiments, flexible member 311 is a helical or other spring connected between carrier segment 134 and mount bushing 310.
In a further embodiment, flexible mounting is provided by a carrier segment 134 having one or more lateral flanges 171,172 which define one or more carrier bores 303 and one or more apertures 320 adapted to effect radial flexion and positioned proximate one or more carrier bores 303.
Each aperture 320 is adapted to effect radial, lateral, or axial flexion between the carrier bore 320 and an elongate pin 210 disposed therein. In some embodiments, apertures 320 have a uniform thickness. In other embodiments, apertures 320 have a varying thickness, for example as illustrated in
Apertures 320 can be of any number and any configuration or shape. One advantage of the thin line apertures 320 presented in
In some embodiments, carrier segment 134 is formed from a metal alloy and apertures 320 are machined into the one or more lateral flanges.
In some embodiments, a static seal cover such as that disclosed above is disposed over apertures 320 to ensure a sealed cavity 170 within the carrier segment 134.
The above-disclosed embodiments of flexibly mounting a CMC seal segment 136 to a carrier segment 134 provide numerous advantages over the prior art. For example, flexibly mounting a CMC seal segment 136 to a carrier segment 134 significantly reduces contact stresses and wear caused by disparate rates of thermal expansion between unlike material components. Reducing such stresses and wear can result in substantially longer component lifespans. Relative motion is permitted between the CMC seal segment 136 and carrier segment 134, but cavity sealing is still possible using compressible mating element 304, mating region 174, or buffering region 207 disclosed above.
Flexible mounting is also advantageous as it allows more than two elongated pins to be used to mount the CMC seal segment 136 to carrier segment 134. The previous limiting factor for CMC seal segment 136 length in the circumferential direction was the length between segment bores due to CMC seal segment flattening. CMC seal segments where thus required to be relatively short in circumferential length, requiring numerous inter-segment seals to maintain adequate sealing of the turbine shroud. With flexible mounting, additional pins are permitted and longer circumferential lengths of CMC seal segments are possible. Additional length results in fewer CMC seal segments required to complete the turbine shroud, and thus fewer inter-segment seals. In some embodiments, the flexible member 311 supporting each mount bushing 310 may comprise at least one element which is individually tuned to provide a different radial and circumferential spring rate dependent on the location of the pin bore flange 180 which will account for the flattening of the arc flange 182. Individually tuned flexible members 311 may be required to account for different loading stresses which would otherwise be present if the flexible member 311 did not allow for more compliant mounting. These individually tuned spring rates may be designed to account for both the loading stress on the CMC segment 136 as well as blade tip clearance. In some embodiments, the spring rate in the radial direction is greater than 25,000 lbs./in., and, in designs in which more than two pins are used, the minimum radial spring rates is up to 60% less than the maximum radial spring rate.
In some embodiments, the CMC seal segments 136 described herein are manufactured using a two dimensional weave of SiC fibers and covered with additional SiC material. In other embodiments, additional materials known in the manufacture of CMC products, such as high nickelon fibers or high nicon Type S nippon carbon are used. In some embodiments, a three dimensional weave of fibers is used, or in some embodiment a combination of two dimensional weaves and three dimensional weaves are used.
Although examples are illustrated and described herein, embodiments are nevertheless not limited to the details shown, since various modifications and structural changes may be made therein by those of ordinary skill within the scope and range of equivalents of the claims.
The present application is a divisional of and claims priority to U.S. patent application Ser. No. 14/721,651, filed May 26, 2015, first named inventor: Daniel Kent Vetters, the entirety of which is hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14721651 | May 2015 | US |
| Child | 16189648 | US |