Two component coating compositions and coatings produced therefrom

FIELD OF INVENTION

[0002] This invention generally relates to curable coating compositions used in automotive refinish and Original Equipment Manufacturing (OEM) applications and it particularly relates to two component coating compositions that cure under ambient conditions and more particularly to those compositions having low VOC (volatile organic content).

BACKGROUND OF THE INVENTION

[0003] A number of clear and pigmented coating compositions are utilized in various coatings, such as, for example, basecoats and clearcoats used in automotive refinish coatings, which are generally solvent based.

[0004] In repairing damage, such as dents to auto bodies, the original coating in and around the damaged area is typically sanded or ground out by mechanical means. Some times the original coating is stripped off from a portion or off the entire auto body to expose the bare metal underneath. After repairing the damage, the repaired surface is coated, preferably with low VOC coating compositions, typically in portable or permanent low cost painting enclosures vented to atmosphere to remove the organic solvents from the freshly applied paint coatings in a safe manner from the standpoint of operator health and explosion hazard. Typically, the drying and curing of the freshly applied paint takes place within these enclosures. Furthermore, the foregoing drying and curing steps take place within the enclosure to also prevent the wet paint from collecting dirt in the air or other contaminants.

[0005] As these paint enclosures take up significant floor space of typical small auto body paint repair shops, these shops prefer to dry and cure these paints as fast as possible. More expensive enclosures are frequently provided with heat sources, such as conventional heat lamps located inside the enclosure to cure the freshly applied paint at accelerated rates. Therefore, to provide more cost effective utilization of shop floor space and to minimize fire hazards resulting from wet coatings from solvent based coating compositions, there exists a continuing need for fast curing coating formulations which cure under ambient conditions while still providing outstanding performance characteristics particularly chip resistance, mar-resistance, durability and appearance.

[0006] In the past, several approaches have been used to improve the productivity of isocyanate crosslinked coatings. One approach was based on using higher Tg acrylic polymers (U.S. Pat. No. 5,279,862 and No. 5,314,953) and another on the use of reactive oligomers (U.S. Pat. No. 6,221,494 B1). Due to the high Mw and high Tg of such acrylic polymers, the fast dry was achievable, but the film vitrified and the faster cure was not achievable. The viscosity of these types of acrylic polymers was also comparatively high and thus that approach resulted in higher VOC. The reactive oligomer approach improved the appearance and the rate of cure of the coating at lower VOC, however these oligomers are difficult to make at high enough Tg needed to reduce the dry time. Moreover, the higher the amount of these oligomers in the coating compositions, the lower was the hardness of the resultant coatings.

[0007] Thus, a continuing need still exists for a coating composition that cures under ambient conditions, more particularly those compositions having low VOC.

STATEMENT OF THE INVENTION

[0008] The present invention is directed to a coating composition comprising crosslinkable and crosslinking components, wherein said crosslinkable component comprises:

[0009] a copolymer having on an average 2 to 25 crosslinkable groups selected from the group consisting of hydroxyl, acetoacetoxy, carboxyl, primary amine, secondary amine, epoxy and a combination thereof; a weight average molecular weight ranging from about 1000 to 4500; a polydispersity ranging from about 1.05 to 2.5; wherein said copolymer is polymerized from a monomer mixture comprising one or more non-functional acrylate monomers and one or more functional methacrylate monomers provided with said functional groups, and

[0010] wherein said crosslinking component for said crosslinkable groups is selected from the group consisting of polyisocyanate, polyamine, ketimine, melamine, epoxy, polyacid and a combination thereof.

[0011] The present invention is further directed to a process for producing a coating on a substrate, said process comprises:

[0012] a) mixing a crosslinkable and crosslinking components of a coating composition to form a potmix, wherein said crosslinkable component comprises:

[0013] a copolymer having on an average 2 to 25 crosslinkable groups selected from the group consisting of hydroxyl, acetoacetoxy, carboxyl, primary amine, secondary amine, epoxy and a combination thereof; a weight average molecular weight ranging from about 1000 to 4500; a polydispersity ranging from about 1.05 to 2.5; wherein said copolymer is polymerized from a monomer mixture comprising one or more non-functional acrylate monomers and one or more functional methacrylate monomers provided with said functional groups, and

[0014] wherein said crosslinking component for said crosslinkable groups is selected from the group consisting of polyisocyanate, polyamine, ketimine, melamine, epoxy, polyacid and a combination thereof;

[0015] b) applying a layer of said potmix on said substrate;

[0016] c) curing said layer into said coating on said substrate.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0017] As used herein:

[0018] “Two-pack coating composition” means a thermoset coating composition having two components stored in separate containers. The containers containing the two components are typically sealed to increase the shelf life of the components of the coating composition. The components are mixed just prior to use to form a pot mix, which has a limited pot life, typically ranging from a few minutes (15 minutes to 45 minutes) to a few hours (4 hours to 8 hours). The pot mix is applied as a layer of a desired thickness on a substrate surface, such as an auto body. After application, the layer dries and cures at ambient or elevated temperatures to form a coating on the substrate surface having desired coating properties, such as, high gloss, mar-resistance and resistance to environmental etching.

[0019] “Low VOC coating composition” means a coating composition that includes the range of from 0.1 kilograms (1.0 pounds per gallon) to 0.72 kilograms (6.0 pounds per gallon), preferably 0.3 kilograms (2.6 pounds per gallon) to 0.6 kilograms (5.0 pounds per gallon) and more preferably 0.34 kilograms (2.8 pounds per gallon) to 0.53 kilograms (4.4 pounds per gallon) of the solvent per liter of the coating composition. All VOC's determined under the procedure provided in ASTM D3960.

[0020] “High solids composition” means a coating composition having solid component of above 30 percent, preferably in the range of from 35 to 90 percent and more preferably in the range of from 40 to 80 percent, all in weight percentages based on the total weight of the composition.

[0021] “GPC weight average molecular weight” means a weight average molecular weight measured by utilizing gel permeation chromatography. A high performance liquid chromatograph (HPLC) supplied by Hewlett-Packard, Palo Alto, Calif. was used. Unless stated otherwise, the liquid phase used was tetrahydrofuran and the standard was polymethyl methacrylate or polystyrene.

[0022] “Tg” (glass transition temperature) measured in ° C. determined by DSC (Differential Scanning Calorimetry).

[0023] “Polydispersity” means GPC weight average molecular weight divided by GPC number average molecular weight. The lower the polydispersity (closer to 1), the narrower will be the molecular weight distribution, which is desired.

[0024] “(Meth)acrylate” means acrylate and methacrylate.

[0025] “Polymer solids” or “Binder solids” means a polymer or binder in its dry state.

[0026] “Crosslinkable component” means a component that includes a compound, polymer or copolymer having functional crosslinkable groups positioned in the backbone of the polymer, pendant from the backbone of the polymer, terminally positioned on the backbone of the polymer, or a combination thereof. One of ordinary skill in the art would recognize that certain crosslinkable group combinations would be excluded from the crosslinkable component of the present invention, since, if present, these combinations would crosslink among themselves (self-crosslink), thereby destroying their ability to crosslink with the crosslinking groups in the crosslinking components defined below.

[0027] “Crosslinking component” is a component that includes a compound, polymer or copolymer having crosslinking groups positioned in the backbone of the polymer, pendant from the backbone of the polymer, terminally positioned on the backbone of the polymer, or a combination thereof, wherein these groups are capable of crosslinking with the crosslinkable groups on the crosslinkable component (during the curing step) to produce a coating in the form of crosslinked structures. One of ordinary skill in the art would recognize that certain crosslinking group/crosslinkable group combinations would be excluded from the present invention, since they would fail to crosslink and produce the film forming crosslinked structures.

[0028] In coating application, especially the automotive refinish application, a key driver is productivity, i.e., the ability of a layer of a coating composition to dry rapidly to a tack free state and then cure sufficiently rapidly to a buffable state. However, the productivity is adversely impacted by the increasingly stricter environmental considerations, which require coating compositions to have lower VOCs. The present invention addresses the forgoing issues by utilizing crosslinking technology. Thus, the present coating composition includes a crosslinkable and crosslinking component.

[0029] The crosslinkable component includes a copolymer having on an average 2 to 25, preferably 3 to 15, more preferably 4 to 12 crosslinkable groups selected from the group consisting of hydroxyl, acetoacetoxy, carboxyl, primary amine, secondary amine, epoxy, and a combination thereof. The hydroxyl, acetoacetoxy and secondary amine functional groups are preferred and hydroxyl is more preferred. It would be clear to one ordinary skill in the art that certain combinations would be excluded from the foregoing as they tend to self-crosslink. Therefore, a combination of carboxyl, primary or secondary amine and epoxy as crosslinkable groups would be excluded from the forgoing combinations. The weight average molecular weight of the copolymer ranges from about 1000 to 4500, preferably from 1250 to 3700 and more preferably from 1500 to 3500, a polydispersity ranging from about 1.05 to 2.5, preferably ranging from 1.1 to 2.0 and more preferably ranging from 1.1 to 1.7. The Tg of the copolymer can range from about −10° C. to 80° C., preferably from about 0° C. to 65° C. and more preferably from about 10° C. to 60° C.

[0030] The copolymer is polymerized from a monomer mixture of one or more non-functional acrylate monomers and one or more functional methacrylate monomers. The ratio of the non-functional acrylate monomers to the functional methacrylate monomers in the monomer mixture ranges from about 90:10 ::10:90, preferably from about 25:75::75:25. Generally, the monomer mixture includes 100% to 60%, preferably 100% to 80% of the total amount of the non-functional acrylate monomers and functional methacrylate monomers, all percentages being in weight percent based on the weight of the monomer mixture.

[0031] The use of non-functional acrylate monomers and functional methacrylate monomers in the monomer mixture by the polymerization process described below ensures functionality on almost every copolymer chain, with low levels of non-functional chains of preferably less than 1% and mono-functional polymer chains of preferably less than 5%, even at these low molecular weights, the percentages being based on of the total number of chains. By contrast, using commonly practiced random polymerization techniques; the conventional copolymers at these low molecular weights would typically have unacceptable functionality distribution and contain high levels of undesirable non-functional and mono-functional polymer chains. Generally, the presence of non-functional and mono-functional polymer chains in coating compositions reduces the crosslinking of the crosslinkable functionalities with the crosslinking functionalities and results in poor coating properties, such as low crosslink density, high soluble fraction, low hardness, poor adhesion; and poor chip and humidity resistance.

[0032] More particularly, when the copolymers of the present invention have a Tg of greater than 10° C. by using suitably appropriate monomers, the resulting coating composition has desirable application viscosity, reactivity and functionality in almost every polymer chain. As a result, a coating from such a composition has improved cure time and desirable coating properties, such as coating hardness. Since the presence of the copolymer in coating compositions provides a desirable balance of coating properties, much higher levels of these copolymers can be included in the coating compositions. As a result, the VOC of the resulting composition, as compared to those containing conventional reactive oligomers, can be lowered without affecting coating properties.

[0033] The non-functional acrylate monomer can be provided with one or more groups selected from the group consisting of linear C1 to C20 alkyl, branched C3 to C20 alkyl, cyclic C3 to C20 alkyl, bicyclic or polycyclic C5 to C20 alkyl, aromatic with 2 to 3 rings, phenyl, C1 to C20 fluorocarbon and a combination thereof The functional methacrylate monomer is provided with one or more groups selected from the group consisting of hydroxyl, carboxyl, acetoacetoxy, primary and secondary amine, epoxy and a combination thereof

[0034] Some of the one or more non-functional acrylate monomers in the monomer mixture include methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, pentyl acrylate, hexyl acrylate, octyl acrylate, nonyl acrylate, isodecyl acrylate, and lauryl acrylate; branched alkyl monomers, such as isobutyl acrylate, t-butyl acrylate and 2-ethylhexyl acrylate; and cyclic alkyl monomers, such as cyclohexyl acrylate, methylcyclohexyl acrylate, trimethylcyclohexyl acrylate, tertiarybutylcyclohexyl acrylate and isobornyl acrylate. Isobornyl acrylate and butyl acrylate are preferred.

[0035] Some of the specific functional methacrylate monomers in the monomer mixture can include hydroxyalkyl methacrylates, such as hydroxyethyl methacrylate, hydroxy propyl methacrylate, hydroxyisopropyl methacrylate, hydroxybutyl methacrylate; aminoalkyl methacrylates, such as tertiarybutylaminoethyl methacrylate and N-methylaminoethyl methacrylate; glycidyl methacrylate, methacrylic acid and acetoacetoxyethyl methacrylate. Hydroxyethyl methacrylate and hydroxybutyl methacrylate are preferred.

[0036] The monomer mixture can also further include small amounts, typically ranging from 0.01% to 10% by weight of functional acrylate monomers provided enough functional methacrylate monomers are present in the monomer mixture to ensure the presence of aforedescribed functionalities on each polymer chain. All percentages based on the total weight of the monomer mixture.

[0037] The monomer mixture can also further include small amounts, typically ranging from 0.01% to 10% by weight of non-functional methacrylate monomers, for example butyl methacrylate, provided enough functional methacrylate monomers are present in the monomer mixture to ensure the presence of a functionality on each polymer chain.

[0038] The monomer mixture can also include one or more of other monomers for the purpose of achieving the desired properties, such as hardness, appearance and mar resistance. Some of the other such monomers include, for example, styrene, α-methyl styrene, acrylonitrile and methacrylonitrile. When included, preferably, the monomer mixture includes such monomers in the range of 5% to 30%, all percentages being in weight percent based on the total weight of the monomer mixture. Styrene is preferred.

[0039] If desired one or more silane functionalities can be incorporated into the copolymers of the present invention preferably by post reacting hydroxyl functionalities on the copolymer with isocyanatopropyl trimethoxy silane. The reaction is conducted on an equivalent basis with equivalents of isocyanate, from the isocyanatopropyl trimethoxy silane, to hydroxyl groups, on the copolymer, ranging from 0.01 to 1.0.

[0040] One of the processes of producing the copolymer of the present invention includes free radically solution polymerizing the aforedescribed monomer mixture at a polymerization temperature ranging from 120° C. to 300° C., preferably ranging from 150° C. to 200° C. and more preferably ranging from 160° C. to 200° C. Typically the reactor gage pressure ranges from 0.1 to 2.86 MPa (0 to 400 psig), preferably from 0.1 to 0.71 MPa (0 to 100 psig). It is understood that the higher the polymerization temperature, the higher will be the reactor pressure for a given composition of monomers and solvent. Typically, the monomer mixture is solvated in a polymerization medium, which typically includes one or more organic solvents, such as methylamyl ketone, Aromatic 100 from ExxonMobil Chemical, Houston, Tex. and butyl acetate. Thus, the higher the boiling point of the polymerization medium, the higher can be the polymerization temperature. Typical reaction time ranges from about 1 hour to 6 hours, generally from about 2 hours to 4 hours.

[0041] The polymerization of the monomer mixture can be initiated by preferably simultaneously adding conventional thermal initiators, such as azos exemplified by Vazo® 64 azobis(isobutyronitrile) supplied by DuPont Company, Wilmington, Del.; and peroxides, such as t-butyl peroxy acetate. By adjusting the amount of initiator used and the reaction temperature, the molecular weight of the resulting copolymer of the present invention can be adjusted. Thus, to attain the same molecular weight, the lower the polymerization temperature, the more will be the amount of the initiator needed. Typically, to attain the claimed molecular weight range, at high polymerization temperatures (higher than 150° C.) about 0.1% to about 6% of initiator is used, all percentages being in weight percent based on the weight of the monomer mixture. Conversely, at low polymerization temperatures (lower than 150° C.) about 4% to about 12% of initiator is used, all percentages being in weight percent based on the weight of the monomer mixture. Another approach to lowering the molecular weight of the copolymer includes polymerizing the monomer mixture under very dilute conditions. Thus, using the same amount of the initiator, a copolymer made at 70 weight percent solids will have higher molecular weight than a copolymer made at 10 to 20 weight percent solids.

[0042] One of the processes for incorporating acetoacetoxy functionalities in the copolymer can be to post react some or all of the hydroxyl functionalities on the copolymer with tertiary butyl acetoacetate.

[0043] The crosslinking component of the present invention suitable for crosslinking with the crosslinkable groups present in the copolymer in the crosslinkable component is selected from the group consisting of polyisocyanate, polyamine, ketimine, melamine, epoxy, polyacid and a combination thereof It would be clear to one ordinary skill in the art that generally certain combinations of crosslinking groups from crosslinking components crosslink with crosslinkable groups from the crosslinkable components. Some of those paired combinations include:

[0044] 1. Ketimine crosslinking component generally crosslinks with acetoacetoxy crosslinkable groups.

[0045] 2. Polyisocyanate and melamine crosslinking components generally crosslink with hydroxyl, primary and secondary amine crosslinkable groups.

[0046] 3. Epoxy crosslinking component generally crosslinks with carboxyl, primary and secondary amine crosslinkable groups.

[0047] 4. Polyamine crosslinking component generally crosslinks with acetoacetoxy crosslinkable groups.

[0048] 5. Polyacid crosslinking component generally crosslinks with epoxy crosslinkable groups.

[0049] However, it should be noted that combinations of the foregoing paired combinations could also be used.

[0050] Typically, the polyisocyanate is provided with in the range of 2 to 10, preferably 2.5 to 8, more preferably 3 to 5 crosslinking isocyanate functionalities. Generally, the ratio of equivalents of isocyanate functionalities on the polyisocyanate per equivalent of the functional group of the copolymer ranges from 0.5/1 to 3.0/1, preferably from 0.7/1 to 1.8/1, more preferably from 0.8/1 to 1.3/1. Some suitable polyisocyanates include aromatic, aliphatic, or cycloaliphatic polyisocyanates, trifunctional polyisocyanates and isocyanate functional adducts of a polyol and difunctional isocyanates. Some of the particular polyisocyanates include diisocyanates, such as 1,6-hexamethylene diisocyanate, isophorone diisocyanate, 4,4′-biphenylene diisocyanate, toluene diisocyanate, biscyclohexyl diisocyanate, tetramethyl-m-xylylene diisocyanate, ethyl ethylene diisocyanate, 1-methyltrimethylene diisocyanate, 1,3-phenylene diisocyanate, 1,5-napthalene diisocyanate, bis-(4-isocyanatocyclohexyl)-methane and 4,4′-diisocyanatodiphenyl ether.

[0051] Some of the suitable trifunctional polyisocyanates include triphenylmethane triisocyanate, 1,3,5-benzene triisocyanate, and 2,4,6-toluene triisocyanate. Trimers of diisocyanate, such as the trimer of hexamethylene diisocyante sold under the trademark Desmodur®N-3390 by Bayer Corporation of Pittsburgh, Pa. and the trimer of isophorone diisocyanate are also suitable. Furthermore, trifunctional adducts of triols and diisocyanates are also suitable. Trimers of diisocyanates are preferred and trimers of isophorone and hexamethylene diisocyantes are more preferred.

[0052] Some of the suitable melamines include monomeric melamine, polymeric melamine-formaldehyde resin or a combination thereof. The coating composition can include in the range of from 0.1 percent to 40%, preferably in the range of from 15% to 35%, and most preferably in the range of 20 percent to 30 percent of the melamine, the percentages being in weight percentages based on the total weight of composition solids. The monomeric melamines include low molecular weight melamines which contain, on an average, three or more methylol groups etherized with a C1 to C5 monohydric alcohol such as methanol, n-butanol, or isobutanol per triazine nucleus, and have an average degree of condensation up to about 2 and preferably in the range of about 1.1 to about 1.8, and have a proportion of mononuclear species not less than about 50 percent by weight. By contrast the polymeric melamines have an average degree of condensation of more than 1.9. Some such suitable monomeric melamines include alkylated melamines, such as methylated, butylated, isobutylated melamines and mixtures thereof. Many of these suitable monomeric melamines are supplied commercially. For example, Cytec Industries Inc., West Patterson, N.J. supplies Cymel® 301 (degree of polymerization of 1.5,95% methyl and 5% methylol), Cymel® 350 (degree of polymerization of 1.6,84% methyl and 16% methylol), 303, 325, 327 and 370, which are all monomeric melamines. Suitable polymeric melamines include high imino (partially alkylated, —N, —H) melamine known as Resimene® BMP5503 (molecular weight 690, polydispersity of 1.98, 56% butyl, 44% imino), which is supplied by Solutia Inc., St. Louis, Mo., or Cymel®1158 provided by Cytec Industries Inc., West Patterson, N.J. Cytec Industries Inc. also supplies Cymel® 1130 @ 80 percent solids (degree of polymerization of 2.5), Cymel® 1133 (48% methyl, 4% methylol and 48% butyl), both of which are polymeric melamines.

[0053] Ketimines useful in the present invention are typically prepared by the reaction of ketones with amines. Representative ketones, which may be used to form the ketimine, include acetone, methyl ethyl ketone, methyl isopropyl ketone, methyl isobutyl ketone, diethyl ketone, benzyl methylketone, diisopropyl ketone, cyclopentanone, and cyclohexanone. Representative amines which may be used to form the ketimine include ethylene diamine, ethylene triamine, propylene diamine, tetramethylene diamine, 1,6-hexamethylene diamine, bis(6-aminohexyl)ether, tricyclodecane diamine, N,N′- dimethyldiethyltriamine, cyclohexyl-1,2,4-triamine, cyclohexyl-1,2,4,5-tetraamine, 3,4,5-triaminopyran, 3,4-diaminofuran, and cycloaliphatic diamines. Preparation and other suitable imines are shown in U.S. Pat. No. 6,297,320, herein incorporated by reference. It should be noted that when the copolymer contains only acetoacetoxy functional groups, then ketimine is typically as a crosslinking component.

[0054] Suitable polyamines include primary and secondary amines, such as, ethylenediamine, propylenediamine, butylenediamine, pentamethylenediamine, hexamethylenediamine, decamethylenediamine, 4,7-dioxadecane-1,10-diamine, dodecamethylenediamine, 4,9-dioxadodecane- 1,12-diamine, 7-methyl-4, 10-dioxatridecane-1,13-diamine, 1,2-diaminocyclohexane, 1,4-diaminocyclohexane, 4,4′-diminodicyclohexyl methane, isophorone diamine, bis(3-methyl-4-aminocyclohexyl)methane, 2,2-bis(4-aminocyclohexyl)propane, nitrile tris(ethane amine), bis(3-aminopropyl)methylamine, 3-amino-1-(methylamino)propane, 3-amino-1-(cyclohexylamino)propane, and N-(2-hydroxyethyl)ethylene diamine. Ethylenediamine, propylenediamine, butylenediamine and 1,2-diaminocyclohexane are preferred.

[0055] Suitable epoxy crosslinking components contain at least two glycidyl groups and can be an oligomer or a polymer, such as sorbitol polyglycidyl ether, mannitol polyglycidyl ether, pentaerythritol polyglycidol ether, glycerol polyglycidyl ether, low molecular weight epoxy resins, such as epoxy resins of epichlorohydrin and bisphenol A., di- and polyglycidyl esters of acids, polyglycidyl ethers of isocyanurates, such as Denacol® EX301 from Nagase. Sorbitol polyglycidyl ether, such as Araldite XYGY-358® from Ciba-Geigy, and di- and polyglycidyl esters of acids, such as Araldite CY-184® from Ciba-Geigy, are preferred since they form high quality finishes.

[0056] Suitable polyacid crosslinking components include aliphatic acids, such as succinic, maleic, fumaric, glutaric, adipic, azeleic, and sebacic acids; cycloaliphatic polycarboxylic acids, such as tetrahydrophthalic acid, hexahydrophthalic acid, 1,2-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, 4-methylhexahydrophthalic acid, tricyclodecanedicarboxylic acid, cyclohexanetetracarboxylic acid and cyclobutanetetracarboxylic acid; aromatic polycarboxylic acids, such as phthalic acid, isophthalic acid, terephthalic acid, halogenophthalic acids, such as, tetrachloro- or tetrabromophthalic acid, trimellitic acid, and pyromellitic acid. It should be noted that aromatic acid crosslinkers tend to be less durable in clearcoats than aliphatic and cycloaliphatic acid crosslinkers.

[0057] The coating composition preferably includes a catalytic amount of a catalyst for accelerating the curing process. Generally, in the range of about 0.001 percent to about 5 percent, preferably in the range of from 0.005 percent to 2 percent, more preferably in the range of from 0.01 percent to 1 percent of the catalyst is utilized, all in weight percent based on the total weight of crosslinkable and crosslinking component solids. A wide variety of catalysts can be used, such as, tin compounds, including dibutyl tin dilaurate and dibutyl tin diacetate; tertiary amines, such as, triethylenediamine. These catalysts can be used alone or in conjunction with carboxylic acids, such as, acetic acid. One of the commercially available catalysts, sold under the trademark, Fastcat® 4202 dibutyl tin dilaurate by Elf-Atochem North America, Inc. Philadelphia, Pa., is particularly suitable.

[0058] When the crosslinking component includes melamine, it also preferably includes one or more acid catalysts to further enhance the crosslinking of the components on curing. Generally, the coating composition includes in the range of from 0.1 percent to 5 percent, preferably in the range of from 0.1 to 2 percent, more preferably in the range of from 0.5 percent to 2 percent and most preferably in the range of from 0.5 percent to 1.2 percent of the catalyst, the percentages being in weight percentage based on the total weight of composition solids. Some suitable catalysts include the conventional acid catalysts, such as aromatic sulfonic acids, for example dodecylbenzene sulfonic acid, para-toluenesulfonic acid and dinonylnaphthalene sulfonic acid, all of which are either unblocked or blocked with an amine, such as dimethyl oxazolidine and 2-amino-2-methyl-1-propanol, n,n-dimethylethanolamine or a combination thereof. Other acid catalysts that can be used are strong acids, such as phosphoric acids, more particularly phenyl acid phosphate, which may be unblocked or blocked with an amine.

[0059] The crosslinkable component of the present invention can further include in the range of from 0.1 percent to 95 percent, preferably in the range of from 10 percent to 90 percent, more preferably in the range of from 20 percent to 80 percent and most preferably in the range of 30 percent to 70 percent, all based on the total weight of the crosslinkable component of an additional acrylic polymer, a polyester or a combination thereof. Applicants have discovered that by adding one or more the foregoing polymers to the crosslinkable component, the coating composition resulting therefrom provides coating with improved sag resistance, and flow and leveling properties.

[0060] The additional acrylic polymer suitable for use in the present invention can have a GPC weight average molecular weight exceeding 5000, preferably in the range of from 5000 to 20,000, more preferably in the range of 6000 to 20,000, and most preferably in the range of 8000 to 12,000. The Tg of the acrylic polymer varies in the range of from 0° C. to 100° C., preferably in the range of from 30° C. to 80° C.

[0061] The additional acrylic polymer suitable for use in the present invention can be conventionally polymerized from typical monomers, such as alkyl (meth)acrylates having alkyl carbon atoms in the range of from 1 to 18, preferably in the range of from 1 to 12 and styrene and functional monomers, such as, hydroxyethyl acrylate and hydroxyethyl methacrylate.

[0062] The polyester suitable for use in the present invention can have a GPC weight average molecular weight exceeding 1500, preferably in the range of from 1500 to 100,000, more preferably in the range of 2000 to 50,000, still more preferably in the range of 2000 to 8000 and most preferably in the range of from 2000 to 5000. The Tg of the polyester varies in the range of from −50° C. to +100° C., preferably in the range of from −20° C. to +50° C.

[0063] The polyester suitable for use in the present invention can be conventionally polymerized from suitable polyacids, including cycloaliphatic polycarboxylic acids, and suitable polyols, which include polyhydric alcohols. Examples of suitable cycloaliphatic polycarboxylic acids are tetrahydrophthalic acid, hexahydrophthalic acid, 1,2-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, 4-methylhexahydrophthalic acid, endomethylenetetrahydrophthalic acid, tricyclodecanedicarboxylic acid, endoethylenehexahydrophthalic acid, camphoric acid, cyclohexanetetracarboxylic acid and cyclobutanetetracarboxylic acid. The cycloaliphatic polycarboxylic acids can be used not only in their cis but also in their trans form and as a mixture of both forms. Examples of suitable polycarboxylic acids, which, if desired, can be used together with the cycloaliphatic polycarboxylic acids, are aromatic and aliphatic polycarboxylic acids, such as, for example, phthalic acid, isophthalic acid, terephthalic acid, halogenophthalic acids, such as, tetrachloro- or tetrabromophthalic acid, adipic acid, glutaric acid, azelaic acid, sebacic acid, fumaric acid, maleic acid, trimellitic acid, and pyromellitic acid.

[0064] Suitable polyhydric alcohols include ethylene glycol, propanediols, butanediols, hexanediols, neopentylglycol, diethylene glycol, cyclohexanediol, cyclohexanedimethanol, trimethylpentanediol, ethylbutylpropanediol, ditrimethylolpropane, trimethylolethane, trimethylolpropane, glycerol, pentaerythritol, dipentaerythritol, tris(hydroxyethyl) isocyanate, polyethylene glycol and polypropylene glycol. If desired, monohydric alcohols, such as, for example, butanol, octanol, lauryl alcohol, ethoxylated or propoxylated phenols may also be included along with polyhydric alcohols. The details of polyester suitable for use in the present invention are further provided in the U.S. Pat. No. 5,326,820, which is incorporated herein by reference. One commercially available polyester, which is particularly preferred, is SCD®-1040 polyester, which is supplied by Etna Product Inc., Chagrin Falls, Ohio.

[0065] The crosslinkable component of the present invention can be blended with reactive oligomers covered in U.S. Pat. No. 6,221,494, which is incorporated herein by reference, and non-alicyclic (linear or aromatic) oligomers, if desired. Such non-alicyclic-oligomers can be made by using non-alicyclic anhydrides, such as succinic or phthalic anhydrides, or mixtures thereof. Caprolactone oligomers described in U.S. Pat. No. 5,286,782 incorporated herein by reference can also be used.

[0066] The coating composition of the present invention can optionally contain, in the range of from 0.1 percent to 50 percent, a modifying resin, such as non-aqueous dispersion (NAD), all percentages being based on the total weight of composition solids. The weight average molecular weight of the modifying resin generally varies in the range of from 20,000 to 100,000, preferably in the range of from 25,000 to 80,000 and more preferably in the range from 30,000 to 50,000.

[0067] The non-aqueous dispersion-type polymer is prepared by dispersion polymerizing at least one vinyl monomer in the presence of a polymer dispersion stabilizer and an organic solvent. The polymer dispersion stabilizer may be any of the known stabilizers used commonly in the field of non-aqueous dispersions.

[0068] The coating composition can optionally include in the range of from 0.1 percent to 30 percent, preferably in the range of from 5 percent to 25 percent, more preferably in the range of from 10 percent to 20 percent, all in weight percentages based on the total weight of components solids, additional crosslinkers, such as aldimine and polyaspartic esters. Aldimines useful in the present invention may be prepared from aldehydes such as acetaldehyde, formaldehyde, propionaldehyde, isobutyraldehyde, n-butyraldehyde, heptaldehyde and cyclohexyl aldehydes, and aldehydes, such as acetaldehyde, formaldehyde, propionaldehyde, isobutyraldehyde, n-butyraldehyde, heptaldehyde and cyclohexyl aldehyde by reaction with amine. Representative amines which may be used to form the aldimine include ethylene diamine, ethylene triamine, propylene diamine, tetramethylene diamine, 1,6-hexamethylene diamine, bis(6-aminohexyl)ether, tricyclodecane diamine, N,N′-dimethyldiethyltriamine, cyclohexyl-1,2,4-triamine, cyclohexyl-1,2,4,5-tetraamine, 3,4,5-triaminopyran, 3,4-diaminofuran, and cycloaliphatic diamines.

[0069] Polyaspartic esters useful in the present invention are typically prepared by the reaction of diamines, such as, isophorone diamine with dialkyl maleates, such as, diethyl maleate.

[0070] The foregoing polyaspartic ester and selected aldimines are supplied commercially under the trademark Desmophen® amine co-reactants by Bayer Corporation, Pittsburgh, Pa. Suitable catalyst for the crosslink reaction of aldimine and aspartic ester with acetoxy functionality is sold under the trademark Amicure® TEDA from Air Products & Chemicals, Allentown, Pa.

[0071] The crosslinkable or crosslinking component of coating composition of the present invention, typically contains at least one organic solvent which is typically selected from the group consisting of aromatic hydrocarbons, such as, petroleum naphtha or xylenes; ketones, such as, methyl amyl ketone, methyl isobutyl ketone, methyl ethyl ketone or acetone; esters, such as, butyl acetate or hexyl acetate; and glycol ether esters, such as propylene glycol monomethyl ether acetate. The amount of organic solvent added depends upon the desired solids level as well as the desired amount of VOC of the composition. If desired, the organic solvent may be added to both components of the binder. High solids and low VOC coating composition is preferred.

[0072] The coating composition of the present invention can also contain conventional additives, such as, pigments, metallic flakes, hollow glass beads, UV absorbers, stabilizers, rheology control agents, flow agents, reinforcing fibers, toughening agents and fillers. Such additional additives will, of course, depend upon the intended use of the coating composition. Fillers, pigments, and other additives that would adversely affect the clarity of the cured coating are typically not included if the composition is intended as a clear coating. It is understood that one or more of these conventional additives, such as pigments, can be added before, during or at the end of the agitating step.

[0073] To improve weatherability of a coating from the coating composition, about 0.1 to 5% by weight, based on the weight of the composition solids, of an ultraviolet light stabilizer or a combination of ultraviolet light stabilizers and absorbers may be added. These stabilizers include ultraviolet light absorbers, screeners, quenchers and specific hindered amine light stabilizers. Also, about 0.1 to 5% by weight, based on the weight of the composition solids, of an antioxidant can be added. Most of the foregoing stabilizers are supplied by Ciba Specialty Chemicals, Tarrytown, N.Y.

[0074] The coating composition of the present invention can be formulated in the form of a clear coating composition, pigmented composition, metallized coating composition, basecoat composition, monocoat composition or a primer. The present formulations are particularly useful as a clear coating for outdoor articles, such as automobile and other vehicle body parts. The substrate is generally prepared with a primer and or a color coat or other surface preparation prior to coating with the present compositions.

[0075] The present invention is also directed to a method of producing a coating on a substrate. The coating composition of the present invention can be supplied in the form of a two-pack coating composition. Generally, the crosslinkable component and the crosslinking component are mixed; typically just prior to application to form a pot mix. The mixing can take place though a conventional mixing nozzle or separately in a container. A layer of the pot mix generally having a thickness in the range of 15 micrometers to 200 micrometers is applied over a substrate, such as an automotive body or an automotive body that has precoated layers, such as electrocoat primer. The foregoing application step can be conventionally accomplished by spraying, electrostatic spraying, roller coating, dipping or brushing the pot mix over the substrate. The layer after application is typically dried to reduce the solvent content from the layer and then cured at temperature ranging from ambient to 204° C. Under typical automotive OEM applications, the dried layer of the composition can be typically cured at elevated temperatures ranging from 60° C. to 160° C. in about 10 to 60 minutes. Preferably, for automotive refinish applications curing can take place at about ambient to 60° C., and for heavy-duty truck body applications it can take place at about 60° C. to 80° C. The cure under ambient conditions occurs in about 30 minutes to 24 hours, generally in about 30 minutes to 4 hours to form a coating on the substrate having the desired coating properties. It is further understood that the actual curing time can depend upon the thickness of the applied layer, the cure temperature, humidity and on any additional mechanical aids, such as fans, that assist in continuously flowing air over the coated substrate to accelerate the cure rate. It is understood that actual curing temperature would vary depending upon the catalyst and the amount thereof, thickness of the layer being cured and the amount of the crosslinking component utilized.

[0076] The suitable substrates for applying the coating composition of the present invention include automobile bodies, any and all items manufactured and painted by automobile sub-suppliers, frame rails, commercial trucks and truck bodies, including but not limited to beverage bodies, utility bodies, ready mix concrete delivery vehicle bodies, waste hauling vehicle bodies, and fire and emergency vehicle bodies, as well as any potential attachments or components to such truck bodies, buses, farm and construction equipment, truck caps and covers, commercial trailers, consumer trailers, recreational vehicles, including but not limited to, motor homes, campers, conversion vans, vans, pleasure vehicles, pleasure craft snow mobiles, all terrain vehicles, personal watercraft, bicycles, motorcycles, boats, and aircraft. The substrate further includes industrial and commercial new construction and maintenance thereof; cement and wood floors; walls of commercial and residential structures, such office buildings and homes; amusement park equipment; concrete surfaces, such as parking lots and drive ways; asphalt and concrete road surface, wood substrates, marine surfaces; outdoor structures, such as bridges, towers; coil coating; railroad cars; printed circuit boards; machinery; OEM tools; signage; fiberglass structures; sporting goods; and sporting equipment.

EXAMPLES

Test Procedures

[0077] Swell Ratio

[0078] The swell ratio of a free film (removed from a sheet of TPO—thermoplastic olefin) was determined by swelling the film in methylene chloride. The free film was placed between two layers of aluminum foil and using a LADD punch, a disc of about 3.5 mm in diameter was punched out of the film and the foil was removed from the film. The diameter of the unswollen film (Do) was measured using a microscope with a 10× magnification and a filar lens. Four drops of methylene chloride were added to the film and the film was allowed to swell for a few seconds and then a glass slide was placed over the film and the swollen film diameter (Ds) was measured. The swell ratio was then calculated as follow:

Swell ratio=(Ds)2/(Do)2

[0079] The lower the swell ratio, the higher is the crosslink density.

[0080] Persoz Hardness Test

[0081] The change in film hardness of the coating was measured with respect to time by using a Persoz hardness tester Model No. 5854 (ASTM D4366), supplied by Byk-Mallinckrodt, Wallingford, Conn. The numbers of oscillations (referred to as Persoz number) were recorded.

[0082] Hardness (Fischer)

[0083] Hardness was measured using a Fischerscope® hardness tester (the measurement is in Newtons per square millimeter).

[0084] Cotton Tack Free Time

[0085] Allow coated panel to dry for set period of time (e.g. 30 minutes). Drop a cotton ball from a height of 1 inch onto the surface of the panel and leave the cotton ball on the surface for a set time interval and invert panel. Repeat above until the time the cotton ball drops off the panel on inversion and note that as the cotton tack free time.

[0086] BK Dry Time

[0087] Surface drying times of coated panels measured according to ASTM D5895.

[0088] Gel Fraction

[0089] Measured according to the procedure set forth in U.S. Pat. No. 6,221,494 col. 8, line 56 to col. 9 line 2 which procedure is hereby incorporated by reference.

[0090] MEK Rubs

[0091] A coated panel is rubbed (100 times) with an MEK (methyl ethyl ketone) soaked cloth using a rubbing machine and any excess MEK is wiped off. The panel is rated from 1-10. Rating of 10 means no visible damage to the coating, 9 means 1 to 3 distinct scratches, 8 means 4 to 6 distinct scratches, 7 means 7 to 10 distinct scratches, 6 means 10 to 15 distinct scratches with slight pitting or slight loss of color, 5 means 15 to 20 distinct scratches with slight to moderate pitting or moderate loss of color, 4 means scratches start to blend into one another, 3 means only a few undamaged areas between blended scratches, 2 means no visible signs of undamaged paint, 1 means complete failure i.e., bare spots are shown. The final rating is obtained by multiplying the number of rubs by the rating.

[0092] Water Spot Test

[0093] Water spot rating is a measure of how well the film is crosslinked early in the curing of the film. If water spot damage is formed on the film, this is an indication that the cure is not complete and further curing of the film is needed before the film can be wet sanded or buffed or moved from the spray both. The water spot rating is determined in the following manner.

[0094] Coated panels are laid on a flat surface and deionized water was applied with a pipette at 1 hour-timed intervals. A drop about ½ inch in diameter was placed on the panel and allowed to evaporate. The spot on the panel was checked for deformation and discoloration. The panel was wiped lightly with cheesecloth wetted with deionized water, which was followed by lightly wiping the panel dry with the cloth. The panel was then rated on a scale of 1 to 10. Rating of 10 best—no evidence of spotting or distortion of discoloration, rating 9—barely detectable, rating 8—slight ring, rating 7—very slight discoloration or slight distortion, rating 6—slight loss of gloss or slight discoloration, rating 5—definite loss of gloss or discoloration, rating of 4—slight etching or definite distortion, rating of 3—light lifting, bad etching or discoloration, rating of 2—definite lifting and rating of 1—dissolving of the film.

Copolymer 1

[0095] To a five-liter flask with heating mantle, stirrer, condenser with 50 ml moisture receiver, nitrogen blanket, monomer and initiator feed lines, enough solvent (Aromatic 100 from ExxonMobil Chemicals of Houston, Tex.) was added to completely fill the receiver. Then, 450 g of solvent (Aromatic 100) were added to the reaction flask and the flask heated to reflux. To this flask, a monomer mixture (AAEM/IBOA//37/63) consisting of 832.5 g of acetoacetoxyethyl methacrylate (AAEM from Eastman Chemical, Kingsport, Tenn.) and 1417.5 g of isobornyl acrylate (Sipomer® HP from Rhodia Inc., Cranbury, N.J.) was added over a period of 240 minutes. Simultaneously with the monomer feed, a mixture consisting of 67.5 g of tert-butylperoxy acetate (Luperox® 7M75 from Atofina, Philadelphia, Pa.) and 375 g of Aromatic 100 was added over a period of 270 minutes. Reflux at polymerization temperature of 169° C. was maintained over the entire reaction time. After completion of the initiator feed, the system was cooled to 150° C. and 375 g of methyl amyl ketone were added. The flask was further cooled to less than 80° C. and the contents poured out.

[0096] The product resin was @ 67.6% solids with a GPC Mn of 1521 and GPC Mw of 2438. The copolymer had an average number of 2.4 functional groups of acetoacetoxyethyl methacrylate per polymer chain. The Tg of the polymer was 6° C.

Copolymer 2

[0097] In a two reactor set, the first being operated at {fraction (1/10)}th the volume of the second, and connected to the second via a transfer line, Part 1 (listed below) was added and heated to 190° C. at 2.5 bar pressure. Part 2 (listed below) followed by Part 3 (listed below) were then charged to separate feed tanks, mixed and then fed to the first reactor over 280 minutes. Once the feeds increase the level in the first reactor to 90% of its normal operating volume, the reaction product from the first reactor was transferred to the second reactor so as to maintain a constant level in the first reactor. After 40 minutes of transfer from the first reactor to the second reactor, the second reactor was heated to reflux and Part 4 (listed below) was fed to the second reactor over 270 minutes. Once Part 2 and 3 feeds were completed, the entire contents of the first reactor were dumped into the second reactor. The second reactor was held at reflux for 1 hour at 157° C., cooled and emptied. All parts in the table below are by weight.

1Part 1Methyl amyl ketone6.8Part 2Hydroxyethyl methacrylate22.2Isobornyl acrylate37.8Methyl amyl ketone1.6Part 3Methylamyl ketone20.4t-butyl peroxy acetate1.8Part 4Methyl amyl ketone7.6t-butyl peroxy acetate1.8

[0098] The resulting copolymer had GPC Mn of 1704, GPC Mw of 3380 and Mw/Mn of 1.98 with near complete conversion of the monomer. The average number of functionalities (hydroxyl) is 4.8 per polymer chain. The Tg of the copolymer was 57.3° C.

Copolymer 3

[0099] To a five-liter flask fitted with heating mantle, stirrer, condenser with 50 ml moisture receiver, nitrogen blanket, monomer and initiator feed lines, enough solvent (Aromatic 100 from ExxonMobil Chemical, Houston, Tex.) was added to completely fill the receiver. Then 300.6 g of solvent (Aromatic 100) was added to the reaction flask and the flask was heated to reflux, followed by the addition of a monomer mixture consisting of 450.4 g of hydroxyethyl methacrylate (Rocryl® 400 monomer from Rohm and Haas Company, Philadelphia, Pa.) and 1050.4 g isobornyl acrylate (Sipomer® HP from Rhodia Inc., Cranbury, N.J.) over a period of 240 minutes to the flask. Simultaneously with the monomer feed, an initiator feed consisting of 45.1 g of tert-butylperoxy acetate (Luperox® 7M75 from Atofina, Philadelphia, Pa.) and 250 g of Aromatic 100 was added over a period of 270 minutes. Reflux at a temperature of approximately 169° C. was maintained over the entire reaction time. After completion of the initiator feed, the flask was cooled to 150° C. and 250 g of methyl N-amyl ketone (PM133 from Eastman Chemical, Kingsport, Tenn.) was added. The flask was further cooled to <80° C. and the contents poured out. The resulting copolymer (HEMA/IBOA//30/70) was at 70% solids with a GPC Mn of 1684 and GPC Mw of 2893 using polystyrene as the standard. The average number of functionalities (hydroxyl) is 3.9 per polymer chain. The Tg of the copolymer was 43.36° C.

Copolymer 4

[0100] To a five-liter flask fitted with heating mantle, stirrer, condenser with 50 ml moisture receiver, nitrogen blanket, monomer and initiator feed lines, enough solvent (Aromatic 100 from ExxonMobil Chemical, Houston, Tex.) was added to completely fill the receiver. Then, 300.1 g of solvent (Aromatic 100) was added to the reaction flask and the flask was heated to reflux, followed by the addition of a monomer mixture consisting of 551.1 g of hydroxyethylmethacrylate (Rocryl® 400 monomer from Rohm and Haas Company, Philadelphia, Pa.) and 945 g isobornyl acrylate (Sipomer® HP from Rhodia Inc., Cranbury, N.J.) over a period of 240 minutes to the flask. Simultaneously with the monomer feed, an initiator feed consisting of 45 g of tertiarybutylperoxy acetate (Luperox® 7M75 from Atofina, Pa.) and 250.1g of Aromatic 100 was added over a period of 270 minutes. Reflux at a temperature of approximately 169° C. was maintained over the entire reaction time. After completion of the initiator feed, the flask was cooled to 150° C. and 250.2 g of methyl N-amyl ketone (PM133 from Eastman Chemical, Kingsport, Tenn.) was added. The flask was further cooled to <80° C. and the contents poured out. The resulting copolymer (HEMA/IBOA//37/63) was at 70% solids, with a GPC Mn of 1637, and GPC Mw of 2978 using polystyrene as the standard. The average number of functionalities (hydroxyl) is 4.6 per polymer chain. The Tg of the copolymer was 41.05° C.

Copolymer 5

[0101] To a five-liter flask fitted with heating mantle, stirrer, condenser with 50 ml moisture receiver, nitrogen blanket, monomer and initiator feed lines, enough solvent (Aromatic 100 from ExxonMobil Chemical, Houston, Tex.) was added to completely fill the receiver. Then 300 g of solvent (Aromatic 100) was added to the reaction flask and the flask was heated to reflux, followed by the addition of a monomer mixture consisting of 630.1 g of hydroxyethylmethacrylate (Rocryl® 400 monomer from Rohm and Haas Company, Philadelphia, Pa.) and 870.1 g isobornyl acrylate (Sipomer® HP from Rhodia Inc., Cranbury, N.J.) over a period of 240 minutes to the flask. Simultaneously with the monomer feed, an initiator feed consisting of 45 g of tert-butylperoxy acetate (Luperox® 7M75 from Atofina, Philadelphia, Pa.) and 250 g of Aromatic 100 was added over a period of 270 minutes. Reflux at a temperature of approximately 169° C. was maintained over the entire reaction time. After completion of the initiator feed, the flask was cooled to 150° C. and 250 g of methyl amyl ketone was added. The flask was further cooled to <80° C. and the contents poured out. The resulting copolymer (HEMA/IBOA//42/58) was at 70% solids, with a GPC Mn of 1678, and GPC Mw of 2997 using polystyrene as the standard. The average number of functionalities (hydroxyl) is 5.4 per polymer chain. The Tg of the copolymer was 38.57° C.

Compound 1

[0102] The following monomer mixture (all in parts by weight) was charged to a reactor equipped with stirrer, condenser and nitrogen blanket:

2methylamyl ketone200pentaerythritol136Sanko ® HCA*5.46tetraethylammonium bromide4.19methylhexahydrophthalic anhydride457.9hexahydrophthalic anhydride196.2*Supplied by International Resources, Columbia, Maryland.

[0103] The reaction mixture was heated to 140° C. and then held at 140° C. for 3 hours. Then, 302.4 parts by weight of butyleneoxide was added to the reactor over a period of 4 hours while maintaining the reaction temperature at 140° C. After completion of the feed, the reaction temperature was continued to be held at 140° C. until acid number of less than 5 was attained. The reactor was re-equipped with a vigreaux column, condenser, and purged with nitrogen followed by the addition of 632 parts by weight of tertiary butylacetoacetate. The reaction temperature was raised to 130° C. followed by nitrogen purge and removal 296 parts by weight of tertiary butylalcohol. The resulting compound had a solids content of 84.38% and a Gardner-Holdt viscosity of Y+1/2 and molecular weight of 1415. The equivalent weight was 354 and the compound had 4 functional groups of acetoacetoxy per molecule.

Crosslinking Component 1

[0104] The following ingredients were charged to a reactor equipped with a stirrer, condenser and nitrogen blanket and the charge was heated 120° C. and held for 3 hours.

3Epoxy resin*187.2 gKetimine**356.0 g*DER 331 Epoxy resin from Dow Chemical, Midland, Michigan **Amicure ® kt-22 ketimine from Air Products, Allentown, Pennsylvania

[0105] The resulting crosslinking agent had a solids percentage of 83.6, a Gardner-Holdt viscosity of X-¼, and the equivalent weight of 225 grams of solids per equivalent.

Comparative Hydroxy-Functional Acrylic Copolymer

[0106] To a 2-liter flask fitted with an agitator, water condenser, thermocouple, nitrogen inlet, heating mantle, and addition pumps and ports was added 305.3 g of xylene, which was agitated and heated to reflux temperature (137 to 142° C.). A monomer mixture comprising of 106.1 grams styrene, 141.4 grams methyl methacrylate, 318.3 grams isobutyl methacrylate, 141.4 grams hydroxyethyl methacrylate and 10.4 g xylene was then added to the flask via the addition pumps and ports simultaneously with an initiator mixture comprising 17.0 grams t-butyl peracetate and 85.2 g xylene. The monomer mixture was added over 180 minutes and the addition time for the initiator mixture was also 180 minutes. The batch was held at reflux (137° C. to 142° C.) throughout the polymerization process. An initiator mixture comprising of 4.3 g t-butyl peracetate and 57.8 g of methyl ethyl ketone was then immediately added to the reaction mixture over 60 minutes and the batch was subsequently held at reflux for 60 minutes. The batch was then cooled to below 90° C. and 13.0 g of methyl ethyl ketone were added. The resulting polymer solution has weight solids of 60% and viscosity of 14,400 cps. The number average molecular weight of the acrylic polymer was 5,000 and weight average molecular weight was 11,000, as determined by gel permeation chromatography (polystyrene standard).

[0107] Clear coating composition of the invention (Examples 1 through 3 and Comparative Example) were prepared by adding the components listed in Table 1 below (all in parts by weight):

4TABLE 1Comp.Composition ComponentsEx. 1Ex. 2Ex. 3Ex.Crosslinkable ComponentCopolymer 346.48Copolymer 437.74Copolymer 533.11Comp. Copolymer*22.39Solvent (butyl Acetate)8.448.098.0911.39Flow Additive**0.470.470.470.32Catalyst***2.342.031.871.62Crosslinking ComponentTolonate ® HDT-LV (Isocyanurate14.2714.2714.2714.27Trimer of Hexamethylene Di-isocyanate)*****Comp. Copolymer (Reactive oligomer based on procedure #2 in U.S. Pat. No. 6,221,494 B1) @ 80% weight solids in Methyl Amyl Ketone. **10% BYK ® 301 Flow Additive from BYK-Chemie, Wallingford, Connecticut in propylene glycol monomethyl ether acetate. ***1% Di Butyl Tin Dilaurate in Methyl Ethyl Ketone. ****Supplied by Rhodia Chemicals, Inc., Cranbury, New Jersey.

[0108] The crosslinkable and crosslinking components listed in Table 1 above were mixed to form pot mixes, which were applied with a doctor blade over a separate phosphated cold roll steel panels primed with a layer of PowerCron® Primer supplied by PPG, Pittsburgh, Pa. to a dry coating thickness of 50 micrometers and air dried at ambient temperature conditions. Then the panels were tested using the tests set forth in following Table 2, which also includes the test results:

5TABLE 2Comp.Ex.Ex. 1Ex. 2Ex. 3PE/MH/IBOA/IBOA/IBOA/EOHEMAHEMAHEMAProperties & Tests(1/4/4)(70/30)(63/37)(58/42)GPC Mn964168416371678GPC Mw1054289329782997Tg4.643.3641.0538.57Viscosity* @ 60% theo. Solids6082.5107102(cps)Equivalent Weight242433351309.5Pot Life in minutes55956550BK3 Time in minutes385231194111Cotton Tack Free Time in minutes255235215125Persoz Hardness (pz)4 hours @ Room Temp.164134321 day @ Room Temp.123178160147Visual AppearanceGoodGoodGoodGoodFischer Hardness (FI)1 day15.818.724.13030 day5917214112230 day @ 3 mil.58828190Water Spot Test - 4 hours @7888Room Temp.Swell Ratio1 day1.991.831.861.8430 day1.611.631.551.54Gel Fraction - 30 day @ Room99.994.3895.4597.69Temp.*The viscosity of copolymers.

[0109] The results in Table 2 show significant improvement in cure time for coating compositions containing the copolymers of the present invention versus the one containing Comparative Copolymer.

[0110] 1. BK 3 dry times ranging from 111-231 minutes versus 385 minutes for the Comparative Copolymer.

[0111] 2. One day swells ranging from 1.83-1.86 versus 1.99 for the Comparative Copolymer.

[0112] 3. Some improvement in water spot resistance rating (Rating 8 versus 7 for the Comparative Copolymer).

[0113] Improved Early and Final Coating Hardness:

[0114] 1. Persoz reading ranging from 32-41 versus 16 for the Comparative Copolymer in 4 hours at Room temperature.

[0115] 2. Persoz reading ranging from 147-178 versus 123 for the Comparative Copolymer in 1 day at room temperature.

[0116] 3. Fischer hardness reading ranging from 122-172 at 30 days versus 59 for the Comparative Copolymer.

[0117] In some instances (coating compositions of Examples 1 and 2) improved pot life ranging from 65-95 minutes versus 55 minutes for the coating composition containing Comparative Copolymer was also noted.

[0118] Increased coating hardness and reduced coating cure time provided by the coating compositions of the present invention as compared to those for coatings using conventional coating compositions will permit refinish body shops to sand and buff the clearcoats much earlier, thereby improving the body shop productivity. Moreover, these improved properties also allow a refinish formulator to include higher amounts of these copolymers in refinish coating compositions, thereby reducing the VOC in the resulting coating compositions without adversely affecting the coating properties.

Viscosity Test Comparison

[0119] Copolymers 3, 4, 5 and Comparative Copolymer from procedure #2, U.S. Pat. No. 6,221,494 B1 were reduced to 60% weight solids with a solvent blend of 80% Methyl amyl Ketone and 20% Methyl ethyl ketone. The results, shown in the Table 2, indicate that the viscosities of Copolymers 3, 4 and 5 are remarkably low. They are comparable to Comparative Copolymer from procedure # 2 of U.S. Pat. No. 6,221,494 B1. These low viscosities will allow the use of these copolymers in low VOC coating compositions without adversely affecting application spray viscosity and film hardness of the resultant coatings. By contrast, a standard acrylic copolymer, such as Comparative Hydroxy-Functional Acrylic Copolymer has a viscosity at 60% solids of 14,400 cps.

[0120] Thus, it is clearly seen from the property and viscosity data of the copolymers of the present invention and the coating compositions made therefrom that these types of copolymers offer a significant advantage in lowering VOC as compared to conventional acrylic copolymers. Furthermore, the copolymers of the present invention also provide favorable film forming properties (early and final) when compared against the oligomers such as those described in U.S. Pat. No. 6,221,494 B1.

Example 4

[0121] In a glass jar, 41.39 grams of Crosslinking Component 1 was mixed with 0.65 g of Byk® 329 flow additive supplied by Byk-Chemie, Wallingford, Conn., 37.38 grams of isobutanol, and 0.34 grams of benzoic acid to form a crosslinkable component. Then 51.19 grams of Compound 1 and 39.05 grams of Copolymer 1 were added to the crosslinking component to produce pot mix @ 60% solids with an AcAc/ketimine equivalent ratio of 1.024/1. The pot mix was stirred and a layer of the pot mix was drawn down to give coatings of ˜75 micrometers (3 mils) in thickness. After 2 hours, the coating had a Persoz Pendulum hardness of 20 and after one day it had a swell ratio of 1.82. The coating had BK3 and BK4 times of 31 and 59 minutes respectively. The viscosity of the potmix was 42 seconds when measured with a Zahn 2 paint cup.

Example 5

[0122] The following components were used to prepares the composition of Example 5:

6TABLE 3Composition ComponentsParts by weightCrosslinkable ComponentCopolymer 4175.95Catalyst14.80methyl ethyl ketone22.89methyl amyl ketone69.45xylene17.12Catalyst21.15Flow additive37.55Acetic acid0.58Crosslinking ComponentFirst polyisocyanate462.83Second polyisocyanate515.84butyl acetate5.56Exxate 600 Solvent616.2812% dibutyl tin dilaurate in ethyl acetate available as Fascat ® 4202 from Atofina Chemicals, Inc., Philadelphia, Pennsylvania. 210% AMICURE ® TEDA in xylene from Air Products & Chemicals, Allentown, Pennsylvania. 332% Byk ® 306 in xylene supplied by Byk-Chemie, Wallingford, Connecticut. 4Desmodur ® N-3300 BA from Bayer Corporation, Pittsburgh, Pennsylvania. 5Desmodur ® Z 4470 BA from Bayer Corporation Pittsburgh, Pennsylvania. 6ExxonMobil Chemical Company, Houston, Texas.

[0123] Example 5 had a solids content of 48% by weight percent based on the total weight of the composition. A layer having a dry film thickness of 52.4 micrometers (2.09 mils) of the coating composition of Example 5 was applied to Powercron® 0 590 electrocoat supplied by PPG Industries, Pittsburgh, Pa. and thermoplastic olefin panels by spraying. The coated panels were dried under ambient conditions for 14 days and then subjected to an elevated temperature of 140° C. for thirty minutes. The table below shows the results of various tests performed on the coatings:

7TABLE 4Test ConductedResultsZahn #2 ViscosityInitial17.03After 60 minutes17.80BK Dry Time in minutesBK 271BK 3139BK 4>720Persoz hardness in secondsAfter 4 hours of drying at room temperature20After 24 hours of drying at room temperature141AppearanceAcceptableFischer hardness in (N/m2)After 1 day of drying at room temperature27After 14 days of drying at room temperature113After 14 days of drying at room temperature followed by155exposure to 140° C. (285° F.) for 30 minutesWater Spot (water sensitivity on a rating of 1 to 10,where is 10 best)After 1 hour of drying at room temperature6After 2 hours of drying at room temperature8After 3 hours of drying at room temperature8MEK rubs testAfter 24 hours of drying at room temperature800Swell ratioAfter 1 day of drying at room temperature1.67After 14 days of drying at room temperature1.53After 14 days of drying at room temperature followed by1.53exposure to 140° C. (285° F.) for 30 minutes

Two component coating compositions and coatings produced therefrom

Information

Publication Number

Date Filed

Date Published

Inventors

CPC

US Classifications

International Classifications

Abstract

Description

Claims

CROSS-REFERENCE TO RELATED APPLICATION

Provisional Applications (1)