Two-stage process for preparing aromatic polyamide fiber

The present invention relates to a process for preparing aromatic polyamide fibers, and particularly to the preparation of aromatic polyamide fibers by a two-stage process.
TECHNICAL BACKGROUND AND PRIOR ART
In the fields of aircraft and aerospace industries, the development of new materials which are very light and yet strong has been requested recently.
Therefore, high strength and high modulus inorganic fibers have been developed using ceramic, graphite or boron and these have been utilized. However, on the other hand, they have not been widely applied because they were very expensive and difficult to handle.
But, it was found that aromatic polyamide fibers had high strength, high durability to friction and high modulus, and thus the development of them has progressed actively.
Also, they have been used as reinforcing materials for plastics in various fields of industry such as the aircraft industry, etc., especially, resin composites reinforced with glass fibers have been used as building materials.
But, there were many problems with the foregoing fibers and films. In an effort to solve the prior problems, West Germany patent laid open No. 1,810,426 to Kwoleck discloses a method for increasing the tensile strength and modulus of the fiber.
The method comprises wet-spinning using aromatic polyamide dope having an optically anisotropic property, and heating the fiber while applying tension.
Thus, aromatic polyamide dope was prepared according to the above method, and spun to obtain fibers and films therefrom. In particular, pulp-like short fibers by the above method were expected to be very widely employed as insulating materials, adiabators, and friction resistant materials in place of asbestos.
As mentioned above, aromatic polyamide fibers, especially pulp-like short fibers having many advantages have been studied and many improvements in their properties made, consequently the following methods have been invented.
That is, according to U.S. Pat. Nos. 3,869,429 and 3,869,430, high molecular weight polymer is obtained by dissolving inorganic salts and aromatic diamines in amide solvents, polymerizing with aromatic diacid chloride at a low temperature to make the polymer of the acid crumb form, washing to remove the polymerization solvents and inorganic salts, and continuously drying. Liquid crystalline dope is obtained by redissolving the above polymer in 20% by weight sulfuric acid, chlorosulfuric acid or flourosulfuric acid.
This dope is then spun through a spinning hole to water, neutralized, washed, dried and treated by mechanical processes to prepare the object aromatic polyamide fibers and film. In the application of the prior art, there are many disadvantages in that the process is complicated, and therefore, costly.
The manufacturing apparatus is easily corroded by sulfuric acid, and also the process is somewhat dangerous. Because the polymer decomposes in dope, the property of fibers may be reduced.
Moreover, not only is it difficult to handle calcium sulfate (CaSO.sub.4), a by-product, but also the color of fibers changes with time due to residual sulfuric acid.
The compression strength of the fiber of this method is much weaker than the theoretical value, due to a defect layer in the fiber itself, and its chemical resistance is also poor because a crystal defect layer is formed in the fiber.
In Japan patent Publication Ser. No. 59-47694, aromatic polyamides of low molecular weight according to interfacial polymerization are dissolved in an amide solvent, and the resulting solution is mixed with a precipitator and stirred to produce pulp-like particles. In this method, this polymer is precipitated and stirred in water or alcohol, the inherent viscosity of the fiber is about 2 to 3.5 at most, therefore the property is decreased and high quality aromatic polyamide short fibers can not be easily prepared.
Also, recent art U.S. Pat. No. 4,511,623 discloses a novel method for preparing highly oriented and high strength aromatic polyamide short fibers having an inherent viscosity of 5 to 7. These fibers are prepared by adding tertiary amines like pyridine prior to the polymerization reaction and applying a high mechanical shear rate (160 cm.sup.-1) at the moment gelation is achieved, hence, rapidly increasing the rate of polymerization and producing a high degree of orientation and a high degree of polymerization.
But in that case, because the amide solvent and excess tertiary amines are added simultaneously, the viscosity is suddenly increased while polymerization occurs by means of adding terephtaloyl chloride. Therefore, polymerization is rapidly terminated within 10 seconds, and then control of the process is very difficult. It is impossible to continuously produce fibers.
U.S. Pat. Nos. 3,672,143 and 3,817,941 disclose art analogous to the present invention. Those are the methods where the polymerization media as a dope (This dope is In situ polymer dope and is different from Isolated polymer dope.) is spun or ejected by extrusion into a precipitator, and then the object fibers are obtained by said simple process. On the other hand, they have some disadvantages in that it is difficult to increase the molecular weight due to the use of a chain terminator during polymerization and water as a precipitator. Moreover, it is impossible to obtain high quality fibers with an improved molecular weight.
The prior method for preparing aromatic polyamide fibers comprises polymerizing, washing, preparing 20% by weight dope of high molecular weight PPTA (poly-(p-phenylene terephthalamide)) and concentrated sulfuric acid, and spinning into water through an air gap to produce fibers. For instance, this method is based on the principle that the orientation of the molecular chain of the high molecular weight polymer is achieved by drawing during spinning using the foregoing concentrated (20%) solution. And though the molecular chain of the aromatic polyamide is rigid and the polymer forms liquid crystals, the complete orientation of the molecular chain can not be achieved due to the high viscosity of more than 1,000 poise at 80.degree. C.
The resulting aromatic polyamide fibers have microscopic structure of skin (exterior) and core (interior) portions as shown in FIGS. 6(a) and (b). The core portion has crystal defect layers every 250 nm perpendicular to the fiber axis and a radially arranged pleated sheet structure, while the skin portion has a compact and well-oriented structure. (Ref. Journal of Polymer Science; Polymer Physics Edition, Vol. 21, 1955-1969 (1983)). The fiber strength is considerably lower in comparison with the theoretical strength because of the crystal defect layers perpendicular to the fiber axis of the core portion.
A report in the Journal of Polymer Science; Polymer Physics Edition 21, 1757 (1983) discloses a case of spinning after preparing sulfuric acid dope. But in that case, the chain ends of the polymer are ionized to -NH.sub.3.sup.+ HSO.sub.4.sup.- and form clusters which comprise the defect layers to the fiber axis. When a force is applied, weak crystal defect layer is formed, hence, chemical strength and durability decrease. In said paper, it is stated that the strength can be increased by preventing cluster formation, however, it is impossible to attain this by prior art methods.
In the case of polyethylene (PE), the strength of existing fibers is less than 5 g/d, however, if the molecular chains are extended by a specific spinning known as gel spinning, the strength is increased to at least 20 g/d. And, though the chemical structure of two compounds is the same, their properties are remarkably different from each other because of their crystalline structures.
Therefore, the present inventors have concentrated on the foregoing point and have sought to improve the property of aromatic polyamides for a long time. Hence the present invention.
An object of the present invention is to provide aromatic polyamide fiber and film having high strength and a high degree of orientation by means of separating the "liquid crystalline pre-polymer dope" (LCPD) formation process from the "molecular orientation polymerization" process, permitting the final polymerization and the molecular chain orientation to occur simultaneously in order to overcome the prior disadvantages, including the economic disadvantages of a multistep process, the difficulty of process control due to a sudden increase in the degree of polymerization, the low degree of polymerization, etc.
Another object is to provide a process for the preparation of aromatic polyamide fibers and film in which the manufacturing cost is inexpensive and process control is easy, and the fiber can be produced successively and obtained directly at the same time as polyermization.
Another object is to provide aromatic polyamide fibers and film with an inherent viscosity of higher than 3.0, with random distributions of the molecular chain's end, where a crystal defect layer is not formed perpendicular but parallel to the fiber axis, and also the color is not changed by aging.

BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic diagram of the manufacturing process according to the first embodiment example of the invention.
FIG. 2 is an enlarged cross-sectional view of the nozzle jet in FIG. 1.
FIG. 3 is a schematic diagram of the process according to the second embodiment example of the invention.
FIG. 4 is a schematic diagram of the process according to the third embodiment example of the invention.
FIG. 5 is an enlarged cross-sectional view of the extrusion apparatus in FIG. 4.
FIG. 6(a) is a partial cross-sectional drawing depicting the structure of the aromatic polyamide fiber according to the prior method.
FIG. 6(b) is an enlarged drawing of the core portion having a pleated sheet structure in the aromatic polyamide fiber according to the prior method.
FIG. 7 is cross-sectional drawing depicting the structure of the aromatic polyamide fiber by the present invention.
FIG. 8(a) is an enlarged picture of the aromatic polaymide fiber according to the prior method, taken with a scanning electron microscope (in this picture, the defect layers can easily be seen).
FIG. 8(b) is an enlarged picture of the aromatic polyamide fiber according to the present invention, taken with a scanning electron microscope (in this picture, the defect layers can not be seen).
FIG. 9(a) is a picture of the aromatic polaymide fiber of the prior method taken with a polarizing microscope (in this picture, the skin-core and defect layers can be seen).
FIG. 9(b) is a picture of the aromatic polyamide fiber (PPD-T) according to the present invention, taken with a polarizing microscope (in this picture, the skin-core and defect layers can't be seen).
FIG. 10(a) is a picture of the prior aromatic polyamide fiber etched with NaOH and taken with a scanning electron microscope (in this picture, the defect layers are etched preferentially by NaOH).
FIG. 10(b) is a picture of the aromatic polyamide fiber according to the present invention, etched with NaOH and taken with a scanning electron microscope (in this picture, the fibers were etched homogeneously by NaOH).
FIG. 11(a) is a picture of prior aromatic polyamide fiber, taken with a transmission electron microscope (this picture shows defect bands perpendicular to the fiber axis)
FIG. 11(b) is a picture of the aromatic polyamide fiber according to the present invention, taken with transmission electron microscope (this picture shows no defect bands perpendicular to the fiber axis)

DETAILED DESCRIPTION OF THE INVENTION
In the present invention, aromatic polyamide in the form of fiber and film are prepared by the following process;
A polymerization solution mixture is prepared by adding equivalent moles of an aromatic diamine and an aromatic diacidchloride reactant to a first amide polyermization solvent containing an inorganic salt and optionally containing a small amount of tertiary amine, and dissolving diamine and diacidchloride in the first solvent. Liquid crystalline prepolymer dope (LCPD) is prepared before the polymerization is completely terminated, that is, just before gelation and after stir opalesence occurs during polymerization in the form of a co-polymer or a homo-polymer and contains repeating units of one of the following structures (I) or (II), and has an inherent viscosity of 1.0 to 4.0. The above LCPD is spun continuously into a second polymerization accelerating-precipitation solvent composed of a tertiary amine solvent, a mixture of the tertiary amine and a amide or a mixture of both of the above and an inorganic salt, and wound successively under a spin-stretch factor of 1 to 4, at a temperature of -40.degree. C. to 50.degree. C. ##STR1## wherein, R.sub.1, R.sub.2 and R.sub.3 are selected from the group consisting of the following radicals and wherein R.sub.1 and R.sub.2 are the same or different from each other and both are present in substantially equivalent moles; ##STR2##
Also, in the present invention, the LCPD having repeating units of one of the above structure (I) or (II) is prepared by the foregoing method. The resulting LCPD is ejected by extrusion with the polymerization accelerating-precipitation solvent. Thus they are simultaneously contacted with each other and the LCPD is subjected to at least a shear rate of 20 sec.sup.-1 by the above solvent. Therefore, the aromatic polyamide fiber is successively obtained as a pulp-like short fiber.
The microscopic structure of the obtained fiber is a fully extended chain structure as a result of sufficient molecular orientating polymerization. It has random distributions of molecular chain's end in the direction of the fiber axis. Thus, the fibers and film of this invention are free of crystal defect layers such as defect zones caused by -NH.sub.3.sup.+ HSO.sub.4.sup.- ionic clusters. The product has a unique structure characterized as having a high inherent viscosity of at least 3.0 and a high strength of at least 15 g/d.
In this invention, the LCPD is the partially polymerized solution and it is formed by dissolving aromatic diamine in the first amide solvent containing the inorganic salts, and optionally containing a small amount of tertiary amine, cooling in the presence of nitrogen, and effecting the solution polymerization with the aromatic diacid chloride at a temperature of less than 40.degree. C. At this time, with a view to obtaining the LCPD of the optional molecular weight to use in the process for the final polymerization, the monomer and solvent should be as pure as possible and the polymerization should occur substantially.
The first solvent, for example, a mixture of organic solvents such as amide or urea and inorganic salts, optionally containing a small amount of tertiary amine may be primarily used. The amide or urea solvents used in the invention include, for example, N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide (DMAc), hexamethyl phosphoramide (HMPA), N,N-dimethylformamide (DMF), N,N-dimethylsulfoxide (DMSO), and N,N,N',N'-tetramethylurea (TMU), besides, N-methylpiperidone, N-methylcaprolactam, N-acetylpyrrolidine, N-ethylpyrrolidine, N,N-dimethylpropionamide and N,N-dimethyl isobutylamide.
The amount of tertiary amine in the polymerization solvent is preferably about 0.01 to 2% by weight of the polymerization solvent. Examples of the tertiary amine are pyridine, quinoline, triethylamine, t-butylamine, picoline, pyrimidine, pyrazine, and quinoxaline.
If the amount of tertiary amine in the polymerization solvent is less than 0.01% by weight, the desired effect of tertiary amine addition, namely an increased polymerization rate, is not achieved. In the case of adding more than 2% by weight, control of the reaction rate becomes difficult, and then process control is not easy.
Inorganic salts are used in order to increase the solubility of the polymer. Preferred inorganic salts include metal halides such as LiCl, CaCl.sub.2, KCl, KBr, and LiBr. The amount is preferably 0.5 to 15% by (weight of salt/volume of amide solvent) of the polymerization solvent.
Aromatic diamine such as p-phenylenediamine and aromatic diacid chloride such as terephthaloylchloride are added to the amide solvent containing inorganic salt and optionally a small amount of tertiary amine, and then the resulting mixture is stirred. Consequently poly (p-phenylenetere phthalamide), represented by the following structure (III), is obtained as the LCPD before gelation: ##STR3##
The above LCPD is different from the prior art dope in the form of the isolated polymer dissolved in sulfuric acid in which the isolated polymer dope was prepared by separating the polymer after polymerization, and dissolving it in a solvent such as concentrated sulfuric acid.
The above LCPD in accordance with the present invention has an amount of polymer of 4 to 20% by weight of the LCPD. When the amount is greater than 20% by weight, LCPD is not suitable for use as dope because the reaction rate increases suddenly and consequently process control becomes difficult. On the other hand, in the case of less than 4% by weight, the inherent viscosity of the final polymer decreases remarkably, and the process suffers a loss of cost effectiveness.
In this invention, a suitable inherent viscosity of the polymer of the LCPD ranges from 1.0 to 4.0, preferably from 1.5 to 3.5.
When the amount of polymer or the inherent viscosity are higher than the above suitable ranges, it is difficult to use and to spin or extrude through a nozzle in this invention.
The obtained LCPD according to this invention is transferred to a temperature-controlled cylinder equipped with orifices, and spun into the polymerization accelerating-precipitation solvent, which consists mainly of tertiary amine containing less than 5,000 ppm moisture. Then the final polymerization occurs by means of a molecular orientating polymerization method, and the degree of polymerization is abruptly increased by the tertiary amine solvent. The spun polymer is wound so as to increase the degree of molecular orientation, continuously washed and dried, and then the object polyamide fiber and film may be obtained finally.
In the polymerization system of this invention, all monomers and solvents should contain minimum impurity (moisture), and the quantities should preferably meet the conditions of weight balance. Moreover, it is preferred that the temperature of the tertiary amine solvent or the solvent mixture composed of tertiary amine and amide be maintained at low level.
The diameter of the nozzle through which the LCPD is spun is preferably 50 .mu.m to 10,000 .mu.m, and the ratio of tube length to nozzle diameter (L/D) in the spinning-nozzle jet is preferred to be 0.5 to 10. But, the use of a small nozzle promotes penetration by the tertiary amine solvent and thus tends to increase the resultant inherent viscosity (.eta.inh, I.V.) and the degree of molecular orientation can be easily improved. And also in accordance with adjusting the speed of winding, the molecular orientation of the polymer can be controlled.
The longer the contact time between the LCPD and the polymerization accelerating-precipitation solvent the better, but too long may be impracticable. Therefore, it is preferred that the contact time is within the range of 0.1 to 1,000 sec.
Also, the spinning speed (`JV`, the average velocity of LCPD in the tube of the spinning nozzle calculated from the cross sectional area of the orifice and the volume of LCPD passing through the orifice) is 1 m/min to 300 m/min, preferably 50 to 100 m/min, and the spin-stretch factor (SSF) refers to the ratio of fiber winding speed to the ejecting speed, and is preferably in the range of 1 to 4.
The spin process of this invention is usually carried out at a temperature of -40.degree. to 50.degree. C.
In the case where the temperature is lower than -40.degree. C., additional equipment would be required to maintain the temperature, and this causes an increase in manufacturing costs. On the other hand, the case where the temperature is higher than 50.degree. C. results in less molecular orientation.
The spin process is carried out at a temperature of -10.degree. to 45.degree. C. preferably, and more preferably at 0.degree. to 25.degree. C. When the fiber and film obtained by the foregoing process is treated with heat under tension, its various properties are improved; for example, the modulus increases 30 to 200% and elongation decreases 30 to 200% of the virgin fiber.
And, the present invention includes the preparation of pulp-like short fibers from fibers in the form of a filament before drying them by means of a known method. Namely the obtained filament fiber or film is transferred to a grinding attachment through a feed roll, and chopped and ground by mechanical treatment, and then the pulp-like short fibers according to the invention are obtained.
The invention also includes a process for directly preparing the pulp-like short fiber by ejection or by contact with the above LCPD having optical anisotropy and the second polymerization accelerating-precipitation solvent under a shear rate of at least 20 sec.sup.-1.
Therefore, the above process for directly preparing the aromatic polyamide pulp-like short fibers is illustrated as follows by the enclosed figures.
FIG. 1 is a schematic diagram of the manufacturing process according to the first embodiment of the invention, that is, under the condition that the reaction vessel (1) containing the LCPD as stated above and the storage (2) for storing the polymerization accelerating-precipitation solvent are set up separately. The LCPD in reaction vessel (1) is fed through a transfer line (3) by gear pump (4) to a nozzle jet (7), and simultaneously the solvent in storage (2) is fed through a transfer line (6) by the circulatory pump (5) to a nozzle jet (7). Subsequently the LCPD and the second solvent flow into the nozzle jet (7) and contact each other by ejecting at the same time. As a result molecular orientation and polymerization occur in the ejection tube (8). Then the flow velocity in the transfer line (6) should be such that it is possible to orient the LCPD flowing the nozzle jet (7), therefore, the flow velocity ratio of the LCPD and the second solvent is preferably 1:50 to 1:0.1, more preferably 1:15 to 1:0.2 to remarkably improve process control and various properties of the pulp-like short fibers.
The diameter of transfer line (3) transferring the LCPD can be 1/16", 1/8", 1/4" or 1/2" and the ejection speed of the LCPD from transfer line (3) is preferably higher than 5 m/min. The diameter of the nozzle in the nozzle (27) jet (7) shown in FIG. 2 is preferably 0.006 to 1 mm, more preferably 0.01 to 0.7 mm, and the number of nozzles (27) ranges from 5 to 500.
And, the above diameter or the number of nozzles are proposed mainly to control the velocity and flow rate in the transfer lines (3 and 6) as well as to improve the degree of orientation or the size of the pulp-like short fiber. Moreover, the nozzles are preferably circular, however, the nozzles are not limited to this shape.
The length of the ejection tube (8) is chosen to allow sufficient time for the molecular orientation of the LCPD by the second solvent. Then pulp-like short fibers of the aromatic polyamide are obtained.
FIG. 3 is the process schematic diagram of the second embodiment of the invention, the LCPD is held in the storage tank (21) maintained at a temperature of less than 30.degree. C. by the circulation of a brine introduced through inlet (22). The exhausted brine is discharged through outlet (23).
A nitrogen pressure of 2 to 20 kg/cm.sup.2 is a applied to the LCPD in storage tank (21) through inlet (24). The LCPD passes through a stainless steel ejection tube (25) 1/8" in diameter and is fed to the impeller (30). The end of the tube (25) provided with a nozzle (27), that has a diameter less than the diameter of the tube (25). The nozzle (27) has a diameter less than 1/8". The LCPD is ejected into the second polymerization accelerating-precipitation solvent (28), and is sheared with impeller (30) that is rotated by operating motor (29). The distance between the impeller (30) and the nozzle (27) is preferably less than 2.54 mm in order to increase the shear force and to cause sufficient molecular orientation, as the result of a shear rate of about 20 sec.sup.-1.
After carrying out the foregoing, the LCPD in a stirrer (26) is polymerized and oriented by the molecular orientation polymerization method while being stirred and contacted with the second polymerization accelerating-precipitation solvent. It is transferred along the transfer line (31) to the filter (32), and the filter (32) separates the object polymer and the second polymerization accelerating-precipitation solvent. The recovered solvent is returned to the stirrer (26) through a circulating tube (34). At this moment, a pump (25) is operated within the compass capable of preventing a backward flow of the second solvent.
The resulting object polymer is obtained as a pulp-like short fiber of the aromatic polyamide by the washing and drying process. The inherent viscosity of the obtained fiber is higher than 3.0.
FIG. 4 represents the process of a third embodiment of the invention. The solution completely dissolving the aromatic diamine to the amide solvent containing inorganic salt and optionally containing tertiary amine is in the reaction vessel (41) filled with nitrogen as the first embodiment. The above solution is added to the mixer (43), and the aromatic diacid chloride is simultaneously added to the mixer (43) quantitatively from tank (42).
When the LCPD as in the first embodiment is obtained by the reaction of the above two components in the mixer (43), it is transferred to the ejector (46) at a flow rate controlled by the gear pump (45), just after the removal of gases by a vacuum pump (44).
And the LCPD is contacted in the ejector (46) with the second polymerization accelerating-precipitation solvent provided through feed line (47) from storage (57).
The second polymerization accelerating-precipitation solvent flows toward the LCPD provided through the introduction opening (48) at a contact angle (49) as shown in FIG. 5. And they are simultaneously contacted by ejecting through the conflux ejection orifice (50) with a shear rate of at least 20 sec.sup.-1 as in the first embodiment.
The shape of the conflux ejection orifice (50) is preferably circular. The diameter of the orifice (50) is 0.005 mm to 50 mm. The L/D (the ratio of length to diameter of orifice) of the orifice (50) is preferably in the range of 1 to 10.
The contact angle (49) is preferably in the range of 20.degree. to 80.degree. C. If it is less than 20.degree., the effect of molecular orientation increases, but the pulverizing effect decreases. On the other hand, if it is more than 80.degree. C., the effect of molecular orientation decreases and the pulverizing effect increases. Therefore, the above two cases are not suitable. A more preferable range is 40.degree. to 50.degree..
It is suitable that the ejection speed is 1 m/min to 300 m/min, and the most preferable length of conflux ejection orifice (50) is 100 mm to 1,000 mm in order to allow the LCPD and the polymerization accelerating-precipitation solvent to make good contact.
The ejected LCPD and polymerization accelerating-precipitation solvent are separated into a solid phase and a liquid phase by the filter conveyor (51), transferred to a roller (52), and the pulp-like short fibers are recovered in the recovery vessel (54) by scrubber (53). At this time, the polymerization accelerating-precipitation solvent is returned to storage (57) of the polymerization accelerating-precipitation solvent tank along recovery line (56) using a pump (55).
In the above process, the polymerization accelerating-precipitation solvent contributes to improvement in the degree of polymerization and the molecular orientation. For instance, the shear force of the solvent may promote formation of hydrogen bonds between the amide bonds. In this invention, the second solvent is preferably a tertiary amine or a mixture of a tertiary amine and an amide or a mixture of either of the above and an inorganic salt. The suitable amount of amide solvent is 10 to 90% by volume of the tertiary amine solvent.
The tertiary amine is present in an amount more than equivalent to the HCl produced by the reaction of diacid chloride and diamine.
The tertiary amine used in the second solvent of the invention includes, for example, pyridine, t-butylamine, quinoline, picoline, quinuclidine, triethylamine, dimethylethylamine, pyrazine, quinoxaline and pyrimidine. Especially pyridine is an effective solvent to improve the inherent viscosity and the degree of orientation of the fibers. Also, suitable amide solvents for the invention include, for example, N-methyl-2-pyrrolidone (NMP), hexamethylphosphoramide (HMPA), N,N-dimethylacetamide (DMAc), N,N-dimethylformamide (DMF), dimethylsulfoxide (DMSO), and N,N,N',N'-tetramethylurea (TMU), N-methylpiperidone, N-methylcaprolactam, N-acetylpyrrolidine, N-ethylpyrrolidine, N,N-dimethylpropinamide and N,N-dimethylisobutylamide, etc. The inorganic salt includes, for example, LiCl, CaCl.sub.2, KCl, KBr and LiBr. It is desirable that the amount of inorganic salt is 0.01 to 10% by weight of the polymerization accelerating-precipitation solvent.
The process of contacting the LCPD and polymerization accelerating-precipitation solvent is usually carried out at a temperature of less than 50.degree. C., preferably -40.degree. to 50.degree. C. The lower the temperature, the better is the molecular orientation effect. However, in the case of a temperature lower than -40.degree. C., additional equipment would be required to maintain the temperature and this causes an increase in manufacturing costs. Moreover, in the case of a temperature of higher than 50.degree. C., the molecular orientation becomes unnecessarily reduced, and, therefore, is not suitable for use in this invention. Therefore, the contact process is preferably carried out at -10.degree. C., to 40.degree. C., and more preferably at 0.degree. C. to 25.degree. C., e.g., room temperature.
Of the pulp-like short fibers obtained by the foregoing processes and by heat-treatment, these various properties are improved. For example, the modulus increases 30 to 300% and the elongation decreases 30 to 200%.
The properties of the fiber according to the invention may be evaluated in terms of their inherent viscosity (I.V.) calculated from the equation: ##EQU1## wherein .eta.rel represents relative viscosity; and C represents a concentration of 0.5 grams of polymer in 100 ml of sulfuric acid.
The relative viscosity, .eta.rel is the flow time ratio between sulfuric acid and a solution of the polymer. Flow times are determined at 30.degree. C. by an Ostward capillary viscometer, using mainly concentrated sulfuric acid (95 to 98%) as a solvent.
The present invention remarkably differs from prior art processes as follows:
First, the LCPD (the phase just before gelation and after stir opalescence occurs during polymerization) is spun into a polymerization accelerating-precipitation solvent under a spin stretch factor of 1 to 4 or it is contacted by ejection with the second solvent, under a shear rate of more than 20 sec.sup.-1, and then the desired aromatic polyamide fiber and film having a high strength and a high degree of orientation is obtained by the molecular orientating polymerization method.
Second, in the invention there are two separate process, namely one for making LCPD and the other for preparing a polymer having a high degree of polymerization with the proper molecular orientation, especially the following conditions of processing can be freely controlled, for example, the polymer content in the polymerization solvent, the temperature of polymerization, the temperature of contacting the LCPD and the polymerization accelerating-precipitation solvent, etc. Therefore, the polymer of LCPD can maintain an inherent viscosity of 1.0 to 4.0 for 30 minutes and so process control becomes easy.
Third, the inherent viscosity of fiber and film is improved to more than 3.0 by the molecular orientation polymerization method using a tertiary amine solvent or a mixture of a tertiary amine and amide or a mixture of either of the above and inorganic salt, as the polymerization accelerating-precipitation solvent. Moreover, the fiber and film, having a high degree of orientation and an extended molecular chain, can be prepared easily because it is possible to accelerate the polymerization rate and the orientation of the molecular chains according to the polymerization accelerating-precipitation solvent by using a low viscosity LCPD.
Fourth, the object fibers and film can directly be prepared during the polymerization process, without the accompanying processes as follows; separating polymer from the resulting solution, washing, preparing sulfuric acid dope, and spinning. So, the whole process becomes simple and economical, and the fiber does not decolorize, as prior fibers were due to residual sulfuric acid.
Fifth, the size (length and diameter), shape, and inherent viscosity of the fiber and film can be easily controlled by changing the extrusion pressure, the spin-stretch factor, the length of the transfer line, the diameter of nozzle, etc.
Sixth, there is an additional advantage that the polymerization accelerating-precipitation solvent can be reused provided it has not become contaminated with impurities that affect the degree of polymerization.
As the result of the foregoing differences in process, the fibers produced to the present invention are considerably superior to prior fibers, as follows.
When a prior aromatic polyamide having a pleated sheet structure like FIG. 6 is examined under a polarizing microscope, transverse bands perpendicular to the axis of fiber are observed at intervals of about 500 to 600 nm, as shown by FIG. 9(a). As a result of the above structural features, the prior fiber has a low strength and modulus, especially has a significantly low compression strength, and then there are many restrictions on its use not only as a substitute material for asbestos or glass fibers but also as reinforcing material for plastics and rubbers.
Moreover, the molecular chains of prior fibers cannot be fully oriented and have crystal joints, so the fibers are easily dissolved by strong acids succh as sulfuric acid, chlorosulfuric acid and flourosulfuric acid, and also they are easily hydrolyzed by acids or alkalies.
FIG. 10(a) is a picture of a prior aromatic polyamide fiber taken with a SEM after being etched by NaOH or HCl. One can observe that a layer 20.ANG. in thickness is caused by crystal defect layers which exist along the axis of fiber at regular intervals.
The prior fibers have structure of skin-core portions resulting from an insufficient orientation due to a high viscosity of more than 1,000 poise. Also, they are spun as H.sub.2 SO.sub.4 PPD-T(about 20%) dope. Therefore, they cannot have sufficient properties as fibers.
On the other hand, in the present invention provides aromatic polyamide fibers and film (PPD-T), in which the preferred molecular orientation is easily achieved because of a low molecular weight of LCPD in spinning stage and the crystal defect layers are uniformly distributed. The fiber does not have crystal defect layers as shown by FIG. 8(b) and transverse bands as shown by FIG. 9(b).
Besides, it does not have the skin-core structure but has a unique structure similar to the skin portion (0.1 .mu.m) of the prior fiber, as shown by FIG. 10(b), and the crystal defect layers do not exist with perpendicular to the fiber axis, as shown by FIG. 11(b).
As a result, the fully extended aromatic polyamide fibers and film can have excellent properties such as strength, modulus and compression strength, as compared with prior fibers.
The properties of the fiber (PPD-T) according to this invention are compared to those of the prior fiber, as the following Table:
TABLE______________________________________ Prior fiber PPD-T(present invention)______________________________________.eta.inh 5.3 1.5 2.0 3.0 5.3 6.2Tenacity 22 4.5 15.2 20 26 31Elongation (%) 3-4 6 6 2.1 2.1 1.0Modulus (g/d) 480 440 510 760 460 520______________________________________
This invention is illustrated by the following Examples, but should not be construed to be limited thereto.
EXAMPLE 1
After a 4-neck flask of 5 1 is sufficiently purged with nitrogen gas and then the moisture in the flask is removed as much as possible, 1,200 ml of NMP is introduced into the above flask.
The temperature is raised to 100.degree. C., 27.0 g of CACl.sub.2 is added and completely dissolved into the solution and also 24.5 g of PPD is dissolved sufficiently in the above solution.
45.95 g of TPC is added while cooling the resulting mixture using an ice bath, and stirring well for 15 minutes with a stir speed of 3,000 rpm in order to produce the LCPD.
The resultant obtained the LCPD is transferred to a cylinder equipped with an orifice having 0.5 of L/D and 0.7 mm of diameter. The LCPD is spun into pyridine, and is simultaneously wound at 20 m/min of the wind rate. The wound fiber is washed with water and dried to obtain the object aromatic polyamide fiber having an inherent viscosity (I.V.) of 5.0 and D/E/T/Mi of 3/7/21/476.
EXAMPLE 2
The processes for preparing aromatic polyamide fiber are carried out as described in Example 1 except that polymerization solvent inorganic salt, polymerization accelerating-precipitation solvent and polymerization time are replaced as shown by Table 1.
The resulting I.V. and D/E/T/Mi of the fibers are listed in following Table 1.
TABLE 1__________________________________________________________________________ Polymer- Poly.Exp. ization Inorga- Precipitation timeNo. solvent nic salt solvent (min) I.V. D/E/T/Mi__________________________________________________________________________1 NMP CaCl.sub.2 Pyridine(2 L) 6 4.8 1.5/3/22/5502 " " Pyridine (1.5 L)/ NMP(0.5 L)/CaCl.sub.2 8 5.2 2/5/20/450 (0.01% by weight)3 " " Py/CaCl.sub.2 11 6.1 2.5/4/19/518 (5% by weight)4 DMAc LiCl Pyridine (2 L) 7 4.9 3/3.5/23/5605 " " Pyridine (1.5 L)/ 7 5.0 2/4.5/21/530 DMAc6 " " Pyridine/NMP 9 6.1 1.5/4.6/20/485 (1.7 L/0.7 L)7 " " Py/acetone 8 6.7 2.5/6.0/22/478 (1.5 L/0.5 L)__________________________________________________________________________
EXAMPLE 3
The processes as described in Example 1 are carried out, except that polymerization solvent and inorganic salt are changed in accordance with Table 2 and pyridine is used as the polymerization accelerating-precipitation solvent.
The results are shown in Table 2.
EXAMPLE 4
The aromatic polyamide fibers are prepared by the same process as in Example 1 except that the polymerization solvent and polymerization accelerating-precipitation solvent are replaced and the L/D and spin stretch factor (SSF) are adjusted in accordance with Table 3.
The results are shown in Table 3.
TABLE 2______________________________________Exp. Polymerization InorganicNo. solvent salt I.V. D/E/T/Mi______________________________________1 NMP/Pyridine CaCl.sub.2 5.3 1.5/3/20/530 (0.5% by weight)2 NMP/Pyridine " 5.7 1.5/4.5/23/510 (1% by weight)3 NMP/Pyridine " 6.1 2/4/10/519 (1% by weight)4 NMP/Pyridine " 6.2 2.5/3.5/31/525 (2.5% by weight)5 DMAc/Pyridine LiCl 5.5 2/3.5/23/490 (1% by weight)6 DMAc/Pyridine " 5.9 2.5/3/21/515 (2% by weight)7 NMP (108 ml)/ HMPA(120 ml)/Py CaCl.sub.2 6.0 3/3.0/24/540 (1% by weight)8 NMP(1080 ml)/ DMAc(120 ml)/Py LiCl 5.8 3/4/20/515 (1% by weight)______________________________________
TABLE 3__________________________________________________________________________ Polymeri-Exp. zation Precipitation *I.V.'No. solvent solvent L/D SSF I.V. (into water)__________________________________________________________________________1 NMP Pyridine (2.5 L) 0.5 2.5 6.8 2.52 " Py/NMP(2.2 L/0.3 L) " " 6.1 2.33 " Py/NMP(2.0 L/0.5 L) 1.0 2.0 5.0 2.14 " Py/CaCl.sub.2 " 4.5 1.8 (7% by weight)5 DMAc Pyridine(2.0 L) 0.5 2.5 5.4 2.06 " Py/DMAc " " 6.1 2.2 (1.8 L/0.2 L)7 " Py/DMAc 1.0 " 5.1 2.1 (1.5 L/0.5 L)8 " Py/LiCl " " 4.8 1.9 (7% by weight)__________________________________________________________________________ *I.V.' is defined as when the LCPD is spun into water instead of the polymerization accelerating precipitation solvent.
EXAMPLE 5
150 ml of NMP and 50 ml of DMAc are introduced into a dry 1 l4-neck flask. After dissolving the mixture, 5.4 g of CaCl.sub.2 and 4.0 g of PPD are added and completely dissolved. 9.19 g of TPC is added while stirring. The temperature during the polymerization is controlled by circulating cooling water, and is maintained at 40.degree. C.
After the resulting solution is stirred for approximately 20 minutes, the LCPD is spun into pyridine through an orifice having a diameter of 0.6 mm and L/D of 0.8, and is wound with a winding speed of 40 m/min. The resultant fiber is washed with water and dried.
The I.V. of the fiber was 4.0 and D/E/T/Mi of 3/12/21/450.
EXAMPLE 6
The aromatic polyamide fibers are prepared by the same process as in Example 5, except that the polyermization solvent is replaced and SSF and L/D are adjusted in accordance with Table 4.
The results are shown in Table 4.
TABLE 4__________________________________________________________________________ Polymeri-Exp. zation PrecipitationNo. solvent SSF L/D solvent I.V. D/E/T/Mi__________________________________________________________________________1 NMP(180 ml)/ 2.0 0.8 Pyridine 5.2 5/11/18/382 DMAc(20 ml)2 NMP(100 ml)/ " 1.0 Pyridine 4.8 10/15/14/350 DMAc(100 ml)3 NMP(50 ml)/ " 1.0 " 6.0 3/13/21/451 DMAc(150 ml)4 NMP(180 ml)/ 2.5 0.5 " 7.1 7/9/17/400 HMPA(20 ml)5 NMP(150 ml)/ " " " 4.7 4/10/21/340 HMPA(50 ml)6 NMP(100 ml)/ " 1.0 " 5.4 2/13/23/500 HMPA(100 ml)7 NMP(50 ml)/ " " " 4.8 5/16/17/350 HMPA(150 ml)__________________________________________________________________________
EXAMPLE 7
The aromatic polyamide fibers are prepared by the same process as in Example 5, except that the polymerization solvent, L/D, SSF and polymerization accelerating-precipitation solvent are substituted as in accordance with Table 5.
The results are shown in Table 5.
TABLE 5______________________________________ Polymeri- Precipi-Exp. zation tation I.V.'No. solvent L/D SSF solvent I.V. (into water)______________________________________1 NMP 0.5 2.0 Pyridine 4.9 2.3 (10 ml)/ (250 ml) DMAc (50 ml)2 NMP " " Pyridine 4.6 2.0 (100 ml)/ (200 ml)/ DMAc NMP (100 ml) (50 ml)3 NMP " 3.0 Pyridine 5.0 2.1 (80 ml)/ (300 ml) HMPA (70 ml)4 NMP " 5.0 Pyridine 5.4 2.1 (50 ml)/ (282 ml)/ HMPA NMP (100 ml)5 DMAc " " Pyridine 5.4 2.2 (100 ml)/ (300 ml) HMPA (50 ml)6 DMAc " " Pyridine 5.2 2.3 (30 ml)/ (200 ml)/ HMPA DMAc (120 ml) (100 ml)______________________________________
EXAMPLE 8
After 6.3 g of CaCl.sub.2 is added and dissolved in the mixed solvent of 130 ml of NMP and 20 ml of DMAc, 4.0 g of PPD is dissolved in the mixture, and 9.19 g of TPC is added and allowed to polymerize, while stirring. The temperature is controlled at 40.degree. C. by cooling water.
After polymerizing for 10 minutes, the resulting LCPD is spun into pyridine through an orifice having a width of 0.7 mm and L/D of 2, and simultaneously wound with a winding speed of 30 m/min.
The resulting film is washed with water and dried. And, the polyamide film is prepared.
The results were as follows: I.V.=5.1
EXAMPLE 9
After 5.4 g of CaCl.sub.2 is dissolved in 200 ml of DMAc, 4.9 g of PPD is added and stirred for about 5 minutes. 9.19 g of TPC is added and allowed to polymerize. At that time, the temperature is maintained at 10.degree. C. by cooling water while stirring for 10 minutes. The resulting LCPD is spun into pyridine through an orifice having a diameter of 0.7 mm and an L/D of 2, wound at with a winding speed of 30 m/min.
The resultant fiber is washed with water and dried.
The fiber has an I.V. of 4.0 and D/E/T/Mi of 31/1.5/22/450.
EXAMPLE 10
AFter 3.82 g of LiCl is added and dissolved in 200 ml of DMAc, 4.1 g of PPD is dissolved in the mixture while stirring. 7.66 g of TPC is added and allowed to polymerize. The polymerization reaction is carried out at a temperature of 40.degree. C. which is controlled with cooling water.
The above LCPD is allowed to react for 20 minutes and is then introduced into a cylinder equipped with an orifice having diameter of 0.5 mm and L/D of 0.5, and is spun into pyridine.
The spun fiber is wound with a winding speed of 30 m/min, and the fiber is washed with water and dried. The fiber has an I.V. of 4.3 and D/E/T/Mi of 5/11/19/450.
EXAMPLE 11
The fibers are prepared as the same process as in Example 10 except that a number of conditions including the polymerization solvent, L/D, SSF and polymerization accelerating-precipitation solvent are changed in accordance with Table 6.
The results are shown in Table 6.
TABLE 6______________________________________ Polymeri- Precipi-Exp. zation tationNo. solvent L/D SSF solvent I.V. D/E/T/Mi______________________________________1 NMP(250 ml) 0.5 2.0 Pyridine 4.3 3/13/21/ (300 ml) 4732 " " 3.0 Pyridine 4.8 10/15/ (250 ml)/ 17/350 NMP (50 ml)3 NMP(150 ml)/ " 1.0 Pyridine 5.1 2/12/20/ (300 ml)/ 470 DMAc(50 ml) CaCl.sub.2 (1% by weight)4 " " " Pyridine 4.9 4/10/19/ (200 ml) 410 DMAc (100 ml)5 NMP(170 ml)/ 1.0 3.0 Pyridine 5.7 2/20/19/ (300 ml) 395 HMPA(30 ml)6 NMP(100 ml)/ 1.0 3.0 Pyridine 4.9 5/13/20/ (250 ml) 441 HMPA(100 ml) NMP (50 ml)7 DMAc(150 ml) " 2.0 Pyridine 5.2 7/18/16/ (300 ml) 400 HMPA (50 ml)8 DMAc(50 ml)/ 1.0 3.0 Pyridine 5.1 6/11/20/ (230 ml)/ 370 HMPA(150 ml) HMPA (70 ml)______________________________________
COMPARATIVE EXAMPLE 1
The fibers are prepared by the same process as in Example 11 except that the resultant LCPD is spun into water.
The I.V. of resulting fibers were compared with those of fibers according to Example 11, and the results are shown in Table 7.
TABLE 7______________________________________Exp. No. I.V.(Pyridine/amide solvent) I.V. (Water)______________________________________1 4.3 1.72 4.8 1.83 5.1 2.34 4.0 2.15 5.7 2.76 4.9 2.27 5.2 2.48 5.1 2.3______________________________________
EXAMPLE 12
After 2.16 g of PPD and 5.05 g of 3,4-diaminodiphenylether re dissolved in a solution of 5.4 g of CaCl.sub.2 dissolved in 200 ml of NMP, 9.19 g of TPC is added and polymerized for 10 minutes, at a low temperature.
The resulting LCPD are spun into pyridine through an orifice having a diameter of 0.3 mm and L/D of at a winding speed of 50 m/min. The resultant fibers were washed with water and dried.
The fiber has an I.V. of 5.6
EXAMPLE 13
After 5.4 g of CaCl.sub.2 and 4.90 g of PPD are dissolved in a mixed solvent of 100 ml NMP and 100 ml HMPA, 9.14 g of TPC is added and cooled while stirring. After stirring for 30 minutes, the resulting LCPD is spun into a mixed solvent of pyridine/HMPA (80 parts by weight/20 parts by weight) through an orifice under the same conditions as in Example 12. The spun fiber is wound, washed with water and dried.
The fiber has an I.V. of 4.6 and T/E/Mi/Den of 7/10/400/3.
EXAMPLE 14
This example is the first embodiment describing the process for directly preparing aromatic polyamide pulp-like short fibers by means of extrusion-ejection.
The reaction vessel is sufficiently purged with nitrogen gas and moisture in the vessel is removed completely. 250 ml of NMP, the amide solvent, is introduced into the vessel and the temperature is increased to 80.degree. C. After that, 10.0 g of CaCl.sub.2 is also added and stirred for 30 minutes in order to dissolve it.
After preparation of the amide polymerization solvent containing inorganic salt according to the foregoing process, 10.38 g of PPD is added and dissolved while stirring for 10 minutes, and 19.55 g of TPC is also added and simultaneously stirred vigorously while maintaining a temperature of 30.degree. C.
After stirring for 8 minutes, the resulting LCPD is transferred to the nozzle jet apparatus through a transfer line having a diameter of 1/8 inch by the operating gear pump. Then, the diameter of nozzle is 0.3 mm, there are 15 nozzles and the gear pump is operated at pressure of 3 Kg/cm.sup.2.
Just after the above LCPD begin to be extruded into the nozzle jet, pridine (water content is less than 1,000 ppm) in storage of the polymerization accelerating-precipitation solvent is extruded through transfer line of 1/4 inch diameter into the nozzle jet by the operating transfer pump which provides a pressure of 0.3 Kg/cm.sup.2.
In the nozzle jet, the LCPD come into contact with pyridine at 20.degree. C. and then they are simultaneously ejected by extrusion through an ejection tube that is 1/4 inch in diameter and 4 m in length.
The resulting pulp-like particles are pyridine solvent are separated by filtration. Then, the pyridine filterate is recirculated, and the resultant fibers are dried for 5 hours in a vacuum drier maintained at 110.degree. C.
The inherent viscosity of the pulp-like short fibers is 4.03.
EXAMPLE 15
The process is the same as in Example 14, but the I.V. of the polymer of the LCPD is changed according to Table 8.
The altered I.V.'s of the resultant pulp-like short fibers are shown in Table 8.
TABLE 8______________________________________Exp. I.V. of the polymer I.V. of resultant pulp-likeNo. of the LCPD short fiber______________________________________1 2.37 4.532 2.74 5.343 3.04 6.014 3.27 5.745 3.65 5.216 3.47 5.50______________________________________
EXAMPLE 16
In this example, the object fibers are prepared by the same process as in Example 14 except that the mixed solvents, pyridine and amides, shown in Table 9, are used as polymerization accelerating-precipitation solvent and the transfer pressure is adjusted to 0.5 Kg/cm.sup.2.
The I.V. of the polymer of the LCPD and the resultant pulp-like short fibers are shown in Table 9.
TABLE 9______________________________________ I.V. I.V. of resul-Exp. Precipitation of the polymer tant pulp-No. solvent of the LCPD like short fibers______________________________________1 pyridine 90 parts/ 2.37 5.84 NMP 10 parts2 pyridine 70 parts/ 2.63 5.31 NMP 30 parts3 pyridine 50 parts/ 2.45 5.12 NMP 50 parts4 pyridine 30 parts/ 3.04 6.30 NMP 70 party/CaCl.sub.2 8% by weight5 pyridine 6 parts/ 3.71 4.80 NMP 94 parts6 pyridine 50 parts/ 2.46 5.31 DMAc 50 parts7 pyridine 70 parts/ 2.95 5.59 HMPA 30 parts8 pyridine 50 parts/ 3.43 6.13 HMPA 50 parts______________________________________
EXAMPLE 17
The object pulp-like short fibers are prepared by the same process as in Example 14 except that a tertiary amine is used as shown in Table 10.
In this case, the I.V.'s of the polymer of the LCPD is 2.71.
TABLE 10______________________________________ Precipitation I.V. of resultant pulp-likeExp. No. solvent short fibers______________________________________1 triethylamine 4.32 t-butylamine 5.473 dimethylethylamine 4.1______________________________________
EXAMPLE 18
In this example, the process having the same reaction conditions as in Example 14 is carried out, but the extrusion speeds of the LCPD and pyridine are changed as shown by Table 11.
According to this example, the I.V.'s of the polymer of the LCPD are resultant pulp-like short fibers are seen in Table 11.
The diameter of the nozzle is 0.5 mm.
TABLE 11______________________________________ Speed of Speed of I.V. of the I.V. of resultantExp. LCPD pyridine polymer of the pulp-likeNo. (m/min) (m/min) LCPD short fiber______________________________________1 2 10 2.73 4.702 2 12 2.73 4.803 2 20 2.73 5.814 4 20 2.59 5.535 4 50 2.54 4.766 10 50 3.12 6.347 10 30 3.12 6.918 15 35 2.45 6.079 15 50 2.45 5.9110 20 50 3.46 6.6311 25 70 3.46 5.7412 30 70 3.46 6.4113 40 100 3.77 7.1414 50 130 3.77 6.91______________________________________
EXAMPLE 19
The pressure of the gear pump is adjusted to 5 Kg/cm.sup.2 and the pressure of circulatory pump is adjusted to 0.7 Kg/cm.sup.2. Also the I.V. of the polymer of the LCPD, diameter and number of nozzles are changed as described in Table 12.
Except for these mentioned above all of the reaction conditions are the same as those in Example 14.
The I.V. of the object pulp-like short fibers are as listed in Table 12.
EXAMPLE 20
In this example, the processes are carried out as in Example 14 except that the I.V. of the polymer of the LCPD and the length of ejection tube are altered as shown in Table 13. At that time, the diameter and number of nozzles are 0.5 mm and 15, the pressure applied to the LCPD is 5 Kg/cm.sup.2, and the pressure of pyridine is 0.7 Kg/cm.sup.2.
The I.V.'s of the resultant pulp-like short fibers are shown in Table 13.
TABLE 12______________________________________ Diameter Number I.V. of the I.V. ofExp. of nozzle of polymer of the pulp-likeNo. (mm) nozzles LCPD short fiber______________________________________1 0.1 10 3.17 5.732 0.3 5 2.74 5.033 0.3 20 2.69 4.854 0.5 10 3.25 5.975 0.5 20 3.47 6.346 0.5 30 3.36 6.597 0.5 40 2.94 6.048 0.7 5 2.61 5.839 0.7 15 3.54 6.1410 0.7 25 3.04 6.3611 0.7 35 2.70 5.8312 1.0 5 2.91 6.0913 1.0 10 3.20 6.3114 1.0 20 3.08 6.25______________________________________
TABLE 13______________________________________ Length I.V. of the I.V. of resultantExp. of ejection polymer of pulp-likeNo. tube (m) the LCPD short fiber______________________________________1 5 2.07 5.092 7 3.28 6.733 10 2.73 5.134 20 2.01 6.275 30 3.15 6.476 40 2.36 6.437 50 2.38 6.27______________________________________
EXAMPLE 21
The proccesses are carried out under the same conditions as in Example 14, except that a mixture of NMP and HMPA or DMAc alone or a mixture of DMAc and HMPA are used instead of NMP. When the solvent is a mixture of NMP and HMPA, 10.0 g of CaCl.sub.2 is used as inorganic salt, as in Example 14. When the solvent is DMAc alone or a mixture of DMAc and HMPA, 10.0 g of LiCl is used.
The obtained LCPD and the resultant pulp-like short fibers, according to this example, have I.V.'s as the following Table 14.
In this example, the condition of nozzles and the pressures of the LCPD and pyridine are equal to the foregoing Example 20.
TABLE 14______________________________________ I.V. of the I.V. ofExp. Polymerization polymer of pulp-likeNo. solvent the LCPD short fiber______________________________________1 NMP(175 ml) + HMPA(75 ml) 2.14 5.412 NMP(125 ml) + HMPA(125 ml) 1.96 4.973 DMAc(250 ml) 2.21 5.584 DMAc(175 ml) + 2.18 4.01 HMPA(75 ml)5 DMAc(125 ml) + 2.09 4.78 HMPA(125 ml)______________________________________
EXAMPLE 22
The processes are carried out under the same conditions as in Example 14, except that the monomers (aromatic diamine and aromatic diacid chloride) are replaced according to Table 15. When using 3,4'-diaminodiphenylether as a monomer, the monomers are preferably 25 mole % p-phenylenediamine, 50 mole % terephtaloylchloride, and 25 mole % 3,4'-diaminodiphenylether.
At that time, the diameter and number of nozzles are 0.7 mm and 15, and the pressures of the LCPD and pyridine are 4 Kg/cm.sup.2 and 0.5 Kg/cm.sup.2.
As a result, the I.V. of the polymer of the LCPD and the resultant pulp-like short fibers is listed in Table 15.
TABLE 15______________________________________ I.V. of the I.V. of resultantExp. polymer of pulp-likeNo. Monomer the LCPD short fiber______________________________________1 chloro-p-phenylene 1.93 4.46 diamine/terephtha- loylchloride (TPC)2 4,4'-diaminodiphen- 2.19 4.80 yl methane/TPC3 PPD/2,6-naphthalene 1.86 4.83 dicarboxylic acid chloride4 4,4'-diaminodiphen- 2.04 5.03 yl sulfone/TPC5 PPD/3,4'-diaminodi- 1.97 4.68 phenylether______________________________________
EXAMPLE 23
The processes are carried out under the same conditions as in Example 14, except that amide solvent containing a small amount of amine (namely, pyridine) are used as polymerization solvents. At that time, the composition of the polymerization solvent and the inorganic salts are changed as shown in Table 16.
The results are listed in Table 16.
COMPARATIVE EXAMPLE 2
In this comparative example, water is used instead of polymerization accelerating-precipitation solvent, as in the prior arts.
The I.V.'s of the polymer of the LCPD and the resultant pulp-like short fibers are shown in Table 17.
TABLE 16______________________________________ I.V. of the I.V. of resultantExp. Polymerization Inorganic polymer of pulp-likeNo. solvent salt the LCPD short fiber______________________________________1 NMP/Pyridine CaCl.sub.2 2.24 5.73 (0.5% by weight)2 NMP/Pyridine " 2.36 5.79 (1% by weight)3 NMP/Pyridine " 2.51 6.02 (2% by weight)4 NMP/Pyridine " 2.53 6.24 (2.5% by weight)5 DMAc/Pyridine LiCl 2.37 5.93 (0.5% by weight)6 DMAc/Pyridine " 2.43 5.94 (1% by weight)7 DMAc/Pyridine " 2.49 6.03 (2% by weight)8 NMP(70%)/ CaCl.sub.2 HMPA(30%) Pyridine 2.35 5.84 (1% by weight)______________________________________
TABLE 17______________________________________I.V. of the polymer of I.V. of resultantthe LCPD pulp-like short fiber______________________________________2.1 2.132.37 2.293.04 3.163.65 3.833.97 3.95______________________________________
EXAMPLE 24 (COMPARATIVE EXAMPLE 3)
This example is the second embodiment describing the process for directly preparing aromatic polyamide pulp-like short fibers.
Preparation of the LCPD is according to the process of Example 14 but using 240 ml of NMP, 7.2 g of CaCl.sub.2, 6.53 g of PPD and 12.26 g of TPC. The resultant LCPD are transferred into dope storage, maintained at a low temperature by cooling water, and ejected through 1/8 inch stainless steel tube into pyridine at 0.degree. C. and 3 Kg/cm.sup.2 nitrogen pressure, while stirring. The impeller has a width of 1.2 cm a diameter of 6.5 cm and revolves at a rate of 1,500 rpm. The distance between the impeller and the end of ejection tube is approximately 1.0 mm.
In order to examine the effect of pyridine, the LCPD are also ejected into both water and a 6% NaHCO.sub.3 aqueous solution.
After that, the above resultant polymers are washed with water and dried under vacuum, at 110.degree. C. for 6 hours.
The resultant polymers had I.V.'s as listed in Table 18.
TABLE 18______________________________________Precipitation solvent I.V.______________________________________water 2.366% NaHCO.sub.3 2.37Pyridine 5.62______________________________________
EXAMPLE 25 (COMPARATIVE EXAMPLE 4)
In this example, the same process as in the foregoing Example 24, is carried out, but the polymerization time after adding TPC, the size and shape of the ejection tube, the stir rate during extrusion, and the polymerization accelerating-precipitation solvent are changed as shown in Table 19.
Simultaneously, another process using water as the precipitation solvent is carried out also.
The measured I.V.s of the resultant pulp-like short fibers are listed in Table 19.
EXAMPLE 26 (COMPARATIVE EXAMPLE 5)
The pulp-like short fiber is prepared by the same process as in Example 24 except that polymerization time, stir rate, and polymerization accelerating-precipitation solvent are replaced as shown in Table 20.
The mixture of amide solvent and pyridine is used as the polymerization accelerating-precipitation solvent. As a Comparative example, water is also used as precipitation solvent, in place of the above mixture.
Consequently, the resultant short fibers had I.V. as shown in Table 20.
TABLE 19______________________________________ Polymeri- Size and StirringExp. zation shape of rate PrecipitationNo. time (min) discharge (rpm) solvent I.V.______________________________________1 15 1/8 inch 1500 water 1.90 (1 hole) pyridine 4.332 17 1/8 inch 3000 water 3.20 (1 hole) pyridine 5.813 10 1/8inch 1750 water 1.95 (1 hole) pyridine 5.584 13 0.1 mm 3000 water 1.85 (3 hole) pyridine 6.48 /CaCl.sub.2 (7% by weight)5 13 0.1 mm 3000 water 2.29 (3 hole) pyridine 7.106 12 0.1 mm 3000 water 3.43 (3 hole) pyridine 6.01______________________________________
TABLE 20______________________________________ StirringExp. Polymerization rate PrecipitationNo. time (min) (rpm) solvent I.V.______________________________________1 15 3000 NMP/Pyridine(1/5) 5.64 water 1.902 7 3000 NMP/Pyridine(1/3) 4.96 water 2.373 12.5 3000 NMP/Pyridine(1/1) 5.04 water 2.254 12 3000 NMP/Pyridine(2/1) 8.56 water 2.43______________________________________
EXAMPLE 27 (COMPARATIVE EXAMPLE 6)
A process having the same reaction conditions as in Example 24 is carried out, but using DMAc as an amide solvent, and LiCl instead of CaCl.sub.2. The polymerization time after adding TPC, the diameter and shape of the ejection tube are changed as shown in Table 21. The I.V.'s of the resultant pulp-like short fibers are as listed in Table 21.
The, I.V.'s of the resultant pulp-like short fibers in the case where water or ethanol is used as the precipitation solvent shown as a comparison in Table 21. The stir rate was 3,000 rpm.
TABLE 21______________________________________ Polymeriz- Diameter andExp. zation shape ofNo. time (min) ejection tube precipitation solvent I.V.______________________________________1 8 1/8inch water 2.23 (1 hole) Pyridine 4.652 16 1/8inch water 2.53 (1 hole) Pyridine 4.92 DMAc/Pyridine(1/3) 6.013 13 1/16 inch water 2.40 (1 hole) Pyridine 5.72 DMAc/Pyridine(1/2) 3.65 acetone/Pyridine(1/5) 3.33 ethanol 2.45______________________________________
EXAMPLE 28
The conditions of this example are the same as in Example 24 except that the composition of the polymerization solvent and the inorganic salt are changed as described in Table 22.
The measured I.V.'s of the resultant pulp-like short fiber are listed in Table 22.
TABLE 22______________________________________ I.V. of I.V. of the resultantExp. Polymerization Inorganic polymer of pulp-likeNo. solvent salt the LCPD short fiber______________________________________1 NMP/Pyridine CaCl.sub.2 2.45 6.21 (1% by weight)2 NMP/triethylamine CaCl.sub.2 2.39 5.94 (0.5% by weight)3 DMAc/triethyline LiCl 2.41 5.91 (1% by weight)4 NMP(70%)/HMPA CaCl.sub.2 2.33 5.83 (30%) /pyridine (0.5% by weight)______________________________________
EXAMPLE 20
This example is the third embodiment of the invention. In this example, the LCPD are prepared by the same process as in Example 14, and transferred to the mixer. Simultaneously the LCPD and the pyridine from the storage cylinder are transferred to the ejector.
After that, the LCPD and pyridine are ejected at the same time. The temperature is -6.degree. C., the diameter of the ejection orifice is 0.3 mm, the length of that is 3 m, and the ejection speed of the LCPD is 1 m/min, while the ejection speed of pyridine is 30 m/min.
The I.V. of the resultant pulp-like short fiber is 6.5.
EXAMPLE 30
The pulp-like short fiber is prepared under the same reaction conditions as in Example 29 except that the conditions are as described in Table 23.
The I.V. of the resultant pulp-like short fibers are as listed in Table 23.
TABLE 23______________________________________ I.V. of I.V. of Polymeri- Inor- Precipi- the poly- resultantExp. zation ganic tation mer of pulp-likeNo. solvent salt solvent the LCPD short fiber______________________________________1 NMP CaCl.sub.2 Pyridine 2.1 4.02 " LiCl " 2.35 6.523 " CaCl.sub.2 Pyridine/ 2.35 6.52 CaCl.sub.2 (5% by weight4 DMAc LiCl Pyridine 2.21 5.875 " CaCl.sub.2 " 2.48 7.686 " LiCl Pyridine/ 2.39 4.01 Acetone______________________________________
EXAMPLE 31
The conditions of this example are the same as in Example 29 with the exception of the I.V. of the polymer of the LCPD and the ejection speed (m/min.) which are changed as shown in Table 24.
The I.V.'s of the resultant pulp-like short fibers re listed in Table 24.
TABLE 24______________________________________ Ejection I.V. of the I.V. of resultantExp. speed polymer of the pulp-likeNo. (m/mm) LCPD short fiber______________________________________1 10 2.18 4.532 20 2.53 4.813 50 2.41 5.844 100 2.05 6.405 500 2.23 5.906 1000 2.30 7.70______________________________________
EXAMPLE 32
The pulp-like short fiber is prepared under the same conditions as in Example 29. I.V.'s of the polymer of the LCPD and the resultant pulp-like fibers are measured as the content of the polymer (weight) to polymerization solvent (volume) and changed according to Table 25.
The results are shown in Table 25.
TABLE 25______________________________________Exp. Content I.V. of the poly- I.V. of resultant pulp-No. (%) mer of the LCPD like short fiber______________________________________1 4.5 1.90 5.612 6 2.34 5.813 8 2.15 6.044 10 2.41 5.735 12 2.05 6.416 14 2.23 7.00______________________________________
COMPARATIVE EXAMPLE 7
In this commparative example, the pulp-like short fiber is prepared under the same conditions as in Example 29 except that the precipitation solvent is changed as shown in Table 26.
TABLE 26______________________________________ I.V. ofExp. Precipitation I.V. of the poly- resultant pulp-No. solvent mer of the LCPD like short fiber______________________________________1 H.sub.2 O 1.85 2.452 NMP/H.sub.2 O)(1:1) 2.07 2.583 methylalcohol 2.14 2.77______________________________________

Number	Date	Country
86-3826	May 1986	KRX
86-3827	May 1986	KRX
86-5983	Jul 1986	KRX
86-5984	Jul 1986	KRX

Two-stage process for preparing aromatic polyamide fiber

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (4)

US Referenced Citations (1)

Foreign Referenced Citations (1)

Non-Patent Literature Citations (2)