ULTRA-LOW-LOSS COUPLED-CORE MULTICORE OPTICAL FIBERS

Abstract

A coupled-core multicore optical fiber has a plurality of cores that are doped with alkali metals or chlorine to achieve low attenuation and a large effective area. The cores may be embedded in a common cladding region that may be fluorine doped. The cores may also be doped with chlorine, either with the alkali metals described above or without the alkali metals.

Description

BACKGROUND

Field

The present disclosure pertains to optical fibers. More particularly, the present disclosure relates to coupled-core multicore optical fibers having a plurality of cores that are doped with alkali metals and/or chlorine to achieve low attenuation and a large effective area.

Technical Background

The transmission capacity through single-mode optical fiber has theoretically reached its fundamental limit of around 100 Tb/s/fiber. Transmitting even 80 Tb/s in a single-mode optical fiber over transoceanic distance has proven challenging in the absence of an improved optical signal-to-noise ratio (OSNR). The actual capacity limit over about 10,000 km of a submarine single-mode optical fiber system used in a transoceanic transmission system is only about 50 Tb/s, even with advanced ultra-low-loss and low-nonlinearity optical fibers.

Spatial division multiplexing (SDM) technologies are being studied intensively to overcome this capacity limit. Transmission capacity may be increased by increasing the fiber pair count in the cable, increasing the capacity of each fiber, or increasing both. However, in submarine cables, higher fiber counts have limited practicality because a thicker and heavier cable significantly increases the cable installation cost due to the limited loading capacities of the ships that deploy the cables.

Multicore fiber (MCF) may exhibit less transmission loss when used in transoceanic applications. However, for practical use in ultra-long-haul submarine systems, the MCF should have ultra-low loss (i.e., low attenuation) to produce a high OSNR, have high spatial-mode density to increase the spatial channel count, and enable low differential group delay (DGD) between spatial modes to decrease the digital signal processing complexity. Also, the standard cladding diameter of 125 µm should be maintained so that no major modifications are needed for installation of the cable.

SUMMARY

Thus, there is a need for new optical fibers that solve the problems described above while having satisfactory attenuation and an increased transmission capacity.

In a first aspect, either alone or in combination with any other aspect, a coupled-core multicore optical fiber includes an outer common cladding comprising a relative refractive index Δ_OCC relative to pure silica; and a plurality of cores disposed in the outer common cladding, each of the plurality of cores comprising a relative refractive index Δ_Ci relative to pure silica and a maximum relative refractive index A_CLi relative to pure silica. For the coupled-core multicore optical fiber A_CLi > Δ_Ci > Δ_OCC. Each of the plurality of cores has an effective area at 1550 nm of greater than or equal to 120 micrometers² (µm²) and less than or equal to 160 µm². A coupling coefficient K between adjacent cores of the plurality of cores is greater than or equal to 1 × 10^-3 /m.

In a second aspect, either alone or in combination with any other aspect, a coupled-core multicore optical fiber includes an outer common cladding comprising a relative refractive index Δ_OCC relative to pure silica; and a plurality of cores disposed in the outer common cladding, each of the plurality of cores comprising an inner core portion comprising a relative refractive index Δ_Ci relative to pure silica and a maximum relative refractive index A_CLi relative to pure silica. For the coupled-core multicore optical fiber A_CLi > Δ_Ci > Δ_OCC. Each of the inner core portions comprises greater than or equal to 0.02 wt.% and less than or equal to 0.15 wt.% fluorine. A distance between centers of an adjacent two of the plurality of cores is greater than or equal to 20 micrometers (µm) and less than or equal to 40 µm. A coupling coefficient K between adjacent cores in the plurality of cores is greater than or equal to 1 × 10^-3 /m.

In a third aspect, either alone or in combination with any other aspect, a distance between centers of an adjacent two of the plurality of cores is greater than or equal to 45 µm and less than or equal to 65 µm.

In a fourth aspect, either alone or in combination with the third aspect, a crosstalk between the plurality of cores is greater than or equal to -50 decibels (dB) per kilometer.

In a fifth aspect, either alone or in combination with any other aspect, the coupled-core multicore optical fiber includes greater than or equal to 2 and less than or equal to 6 of the cores.

In a sixth aspect, either alone or in combination with the fifth aspect, the coupled-core multicore optical fiber includes 3 sets of 3 of the cores.

In a seventh aspect, either alone or in combination with any other aspect, a cable cutoff wavelength of each of the plurality of cores of the optical fiber is greater than or equal to 1200 nanometers (nm) and less than or equal to 1520 nm.

In an eighth aspect, either alone or in combination with the seventh aspect, an average bend loss of the plurality of cores of the optical fiber at a wavelength of 1550 nm measured on a mandrel having a diameter of 20 millimeters (mm) is greater than or equal to 0.01 decibels per turn (dB/turn) and less than or equal to 1 dB/turn.

In a ninth aspect, either alone or in combination with any other aspect, an average bend loss of the plurality of cores of the optical fiber at a wavelength of 1550 nm measured on a mandrel having a diameter of 30 mm is greater than or equal to 0.001 decibels per turn (dB/turn) and less than or equal to 0.03 dB/turn.

In a tenth aspect, either alone or in combination with any other aspect, a minimum distance between a center of one of the plurality of cores to an adjacent edge of the optical fiber along a line formed by a centerpoint of the optical fiber, the center of the one of the plurality of cores, and the adjacent edge in a plane perpendicular to a long axis of the coupled-core multicore optical fiber is greater than or equal to 30 µm and less than or equal to 50 µm.

In an eleventh aspect, either alone or in combination with any other aspect, each of the plurality of cores comprises an inner core portion surrounded by an inner cladding portion.

In a twelfth aspect, either alone or in combination with any other aspect, each inner cladding portion comprises a relative refractive index Δ_ICi, the inner core portion comprises the A_CLi, and Δ_CLi > A_Ci > Δ_ICi > Δ_OCC.

In a thirteenth aspect, either alone or in combination with any other aspect, each of the plurality of cores comprises an inner cladding portion and an inner core portion corresponding to the inner cladding portion, each inner cladding portion surrounding the corresponding inner core portion.

It is to be understood that both the foregoing general description and the following detailed description are merely exemplary and are intended to provide an overview or framework to understand the nature and character of the claims. Additional features and advantages will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from the description or recognized by practicing the embodiments as described in the written description and claims hereof, as well as the appended drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding, and are incorporated in and constitute a part of this specification. The drawings are illustrative of selected aspects of the present disclosure, and together with the description serve to explain principles and operation of methods, products, and compositions embraced by the present disclosure, in which:

FIG. 1 schematically depicts an optical system including a signal source, a multicore optical fiber, and a photodetector, according to one or more embodiments shown and described herein;

FIG. 2 schematically depicts a multicore optical fiber, according to one or more embodiments shown and described herein;

FIG. 3 schematically depicts an X-Y cross-section of the multicore optical fiber of FIG. 2 taken along the line 3-3, according to one or more embodiments shown and described herein;

FIG. 4 schematically depicts an X-Y cross-section of an exemplary core and inner cladding of a multicore optical fiber, according to one or more embodiments shown and described herein;

FIG. 5A schematically depicts an X-Y cross-section of an alternative multicore optical fiber of FIG. 2 along section 3-3 having four cores, a common inner cladding, and a common outer cladding according to one or more embodiments shown and described herein;

FIG. 5B schematically depicts an X-Y cross-section of an alternative multicore optical fiber of FIG. 2 along section 3-3 having four cores, four inner claddings, and a common outer cladding according to one or more embodiments shown and described herein;

FIG. 6A schematically depicts an X-Y cross-section of an alternative multicore optical fiber of FIG. 2 along section 3-3 having three cores, according to one or more embodiments shown and described herein;

FIG. 6B schematically depicts an X-Y cross-section of an alternative multicore optical fiber of FIG. 2 along section 3-3 having three cores, according to one or more embodiments shown and described herein;

FIG. 6C schematically depicts an X-Y cross-section of an alternative multicore optical fiber of FIG. 2 along section 3-3 having six cores, according to one or more embodiments shown and described herein;

FIG. 6D schematically depicts an X-Y cross-section of an alternative multicore optical fiber of FIG. 2 along section 3-3 having three clusters of three cores, according to one or more embodiments shown and described herein;

FIG. 7A graphically depicts a relative refractive index profile of a single core, inner common cladding, and outer common cladding of an optical fiber preform from which a coupled-core multicore fiber may be drawn, according to one or more embodiments shown and described herein;

FIG. 7B graphically depicts a relative refractive index profile of a single core, inner cladding, and outer common cladding of an optical fiber preform from which a coupled-core multicore fiber may be drawn, according to one or more embodiments shown and described herein;

FIG. 8 graphically depicts a relative refractive index profile of a single core, inner cladding, inner common cladding, and outer common cladding of the coupled-core multicore fiber of Example 1, according to one or more embodiments shown and described herein;

FIG. 9 graphically depicts a relative refractive index profile of a single core, inner common cladding, and outer common cladding of the coupled-core multicore fiber of Example 2, according to one or more embodiments shown and described herein;

FIG. 10 graphically depicts a relative refractive index profile of a single core, inner common cladding, and outer common cladding of the coupled-core multicore fiber of Example 3, according to one or more embodiments shown and described herein;

FIG. 11 graphically depicts a relative refractive index profile of a single core, inner common cladding, and outer common cladding of the coupled-core multicore fiber of Example 4, according to one or more embodiments shown and described herein;

FIG. 12 graphically depicts a relative refractive index profile of a single core, inner common cladding, and outer common cladding of the coupled-core multicore fiber of Example 5, according to one or more embodiments shown and described herein; and

FIG. 13 graphically depicts a relative refractive index profile of a single core, inner common cladding, and outer common cladding of the coupled-core multicore fiber of Example 6, according to one or more embodiments shown and described herein.

DETAILED DESCRIPTION

In this specification and in the claims which follow, reference will be made to a number of terms which shall be defined to have the following meanings:

As used herein, the term “about” means that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but may be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. When the term “about” is used in describing a value or an end-point of a range, the disclosure should be understood to include the specific value or end-point referred to. Whether or not a numerical value or end-point of a range in the specification recites “about,” the numerical value or end-point of a range is intended to include two embodiments: one modified by “about,” and one not modified by “about.” It will be further understood that the end-points of each of the ranges are significant both in relation to the other end-point, and independently of the other end-point.

A multicore optical fiber, also referred to as a multicore fiber or “MCF”, is considered for the purposes of the present disclosure to include two or more core fibers disposed within a cladding matrix. Each core fiber can be considered as having a higher index core surrounded by a lower index cladding matrix defining a common cladding. Optionally, each core fiber can include a higher index core surrounded by one or more lower index inner claddings disposed between each core and the cladding matrix of the common cladding. As used herein, the term “inner core portion” refers to the higher index core. That is, a core fiber may include an inner core portion and optionally one or more lower index inner claddings.

“Radial position” and/or “radial distance,” when used in reference to the radial coordinate “r” refers to radial position relative to the centerline (r = 0) of each individual core in a multicore optical fiber. “Radial position” and/or “radial distance,” when used in reference to the radial coordinate “R” refers to radial position relative to the centerline (R = 0, central fiber axis) of the multicore optical fiber. The length dimension “micrometer” may be referred to herein as micron (or microns) or µm.

The “refractive index profile” is the relationship between refractive index or relative refractive index and radial distance r from the core’s centerline for each core fiber of the multicore optical fiber. For relative refractive index profiles depicted herein as having step boundaries between adjacent core and cladding regions, normal variations in processing conditions may result in step boundaries at the interface of adjacent regions that are not sharp. It is to be understood that although boundaries of refractive index profiles may be depicted herein as step changes in refractive index, the boundaries in practice may be rounded or otherwise deviate from perfect step function characteristics. It is further understood that the value of the relative refractive index may vary with radial position within the core region and/or any of the cladding regions. When relative refractive index varies with radial position in a particular region of the fiber (core region and/or any of the cladding regions), it may be expressed in terms of its actual or approximate functional dependence or in terms of an average value applicable to the region. Unless otherwise specified, if the relative refractive index of a region (core region and/or any of the inner and/or common cladding regions) is expressed as a single value, it is understood that the relative refractive index in the region is constant, or approximately constant, and corresponds to the single value or that the single value represents an average value of a non-constant relative refractive index dependence with radial position in the region. Whether by design or a consequence of normal manufacturing variability, the dependence of relative refractive index on radial position may be sloped, curved, or otherwise non-constant.

The “relative refractive index” or “relative refractive index percent” as used herein with respect to multicore optical fibers and fiber cores of multicore optical fibers is defined according to equation (1):

$\begin{array}{cc}\Delta \%=100\frac{n^2\left(r\right)-n_c^2}{2n^2\left(r\right)}& \text{­­­(1)}\end{array}$

where n(r) is the refractive index at the radial distance r from the core’s centerline at a wavelength of 1550 nm, unless otherwise specified, and n_c is 1.444, which is the refractive index of undoped silica glass at a wavelength of 1550 nm. As used herein, the relative refractive index is represented by Δ (or “delta”) or Δ% (or “delta %) and its values are given in units of “%” or “%Δ”, unless otherwise specified. Relative refractive index may also be expressed as Δ(r) or Δ(r)%. When the refractive index of a region is less than the reference index n_c, the relative refractive index is negative and can be referred to as a trench. When the refractive index of a region is greater than the reference index n_c, the relative refractive index is positive and the region can be said to be raised or to have a positive index.

The average relative refractive index of a region of the multicore optical fiber can be defined according to equation (2):

$\begin{array}{cc}\Delta \%\text{=}\frac{{\displaystyle {\int }_{r_{inner}}^{r_{outer}}\Delta \left(r\right)dr}}{\left(r_{outer}\text{-}{r}_{inner}\right)}& \text{­­­(2)}\end{array}$

where r_inner is the inner radius of the region, r_outer is the outer radius of the region, and Δ(r) is the relative refractive index of the region.

The term “α-profile” (also referred to as an “alpha profile”) refers to a relative refractive index profile Δ(r) that has the following functional form (3):

$\begin{array}{cc}\Delta \left(r\right)=\Delta \left(r_0\right)\left\{1-{\left[\frac{\left|r-r_0\right|}{\left(r_1-r_0\right)}\right]}^{\alpha }\right\}& \text{­­­(3)}\end{array}$

where r_o is the point at which Δ(r) is maximum, r₁ is the point at which Δ(r) is zero, and r is in the range r_i ≤ r ≤ r_f, where r_i is the initial point of the α-profile, r_f is the final point of the α-profile, and α is a real number. In some embodiments, examples shown herein can have a core alpha of 1 ≤ α ≤ 100. In practice, an actual optical fiber, even when the target profile is an alpha profile, some level of deviation from the ideal configuration can occur. Therefore, the alpha parameter for an optical fiber may be obtained from a best fit of the measured index profile, as is known in the art.

The term “graded-index profile” refers to an α-profile, where α< 10. The term “step-index profile” refers to an α-profile, where α ≥ 10.

The “effective area” can be defined as (4):

$\begin{array}{cc}{A}_{eff}=\frac{2\pi {\left[{\displaystyle {\int }_0^{\infty }{\left(f\left(r\right)\right)}^{2}rdr}\right]}^2}{{\displaystyle {\int }_0^{\infty }{\left(f\left(r\right)\right)}^{4}rdr}}& \text{­­­(4)}\end{array}$

where f(r) is the transverse component of the electric field of the guided optical signal and r is radial position in the fiber. “Effective area” or “A_eff” depends on the wavelength of the optical signal. Specific indication of the wavelength will be made when referring to “Effective area” or “A_eff” herein. Effective area is expressed herein in units of “µm²”, “square micrometers”, “square microns” or the like.

Unless otherwise noted herein, optical properties (such as dispersion, dispersion slope, etc.) are reported for the LP01 mode.

“Chromatic dispersion,” herein referred to as “dispersion” unless otherwise noted, of an optical fiber is the sum of the material dispersion, the waveguide dispersion, and the intermodal dispersion. “Material dispersion” refers to the manner in which the refractive index of the material used for the optical core affects the velocity at which different optical wavelengths propagate within the core. “Waveguide dispersion” refers to dispersion caused by the different refractive indices of the core and cladding of the optical fiber. In the case of single mode waveguide fibers, the inter-modal dispersion is zero. Dispersion values in a two-mode regime assume intermodal dispersion is zero. The zero-dispersion wavelength (λ_o) is the wavelength at which the dispersion has a value of zero. Dispersion slope is the rate of change of dispersion with respect to wavelength. Dispersion and dispersion slope are reported herein at a wavelength of 1310 nm or 1550 nm, as noted, and are expressed in units of ps/nm/km and ps/nm²/km, respectively. Chromatic dispersion is measured as specified by the IEC 60793-1-42:2013 standard, “Optical fibres - Part 1-42: Measurement methods and test procedures - Chromatic dispersion.”

The cutoff wavelength of an optical fiber is the minimum wavelength at which the optical fiber will support only one propagating mode. For wavelengths below the cutoff wavelength, multimode transmission may occur and an additional source of dispersion may arise to limit the fiber’s information carrying capacity. Cutoff wavelength will be reported herein as a cable cutoff wavelength. The cable cutoff wavelength is based on a 22-meter cabled fiber length as specified in TIA-455-80: FOTP-80 IEC-60793-1-44 Optical Fibres — Part 1-44: Measurement Methods and Test Procedures — Cut—off Wavelength (21 May 2003), by Telecommunications Industry Association (TIA).

The “theoretical cutoff wavelength”, or “theoretical fiber cutoff”, or “theoretical cutoff”, for a given higher-order mode, is the wavelength above which guided light cannot propagate in that higher-order mode. According to an aspect of the present disclosure, the cutoff wavelength refers to the cutoff wavelength of the LP11 mode. A mathematical definition can be found in Single Mode Fiber Optics, Jeunhomme, pp. 39-44, Marcel Dekker, New York, 1990, wherein the theoretical fiber cutoff is described as the wavelength at which the mode propagation constant becomes equal to the plane wave propagation constant in the common cladding. This theoretical wavelength is appropriate for an infinitely long, perfectly straight fiber that has no diameter variations.

The bend resistance of an optical fiber, expressed as “bend loss” herein, can be gauged by induced attenuation under prescribed test conditions as specified by the IEC-60793-1-47:2017 standard, “Optical fibres - Part 1-47: Measurement methods and test procedures -Macrobending loss.” For example, the test condition can entail deploying or wrapping the fiber one or more turns around a mandrel of a prescribed diameter, e.g., by wrapping 1 turn around either a 15 mm, 20 mm, or 30 mm or similar diameter mandrel (e.g. “1×15 mm diameter bend loss” or the “1×20 mm diameter bend loss” or the “1×30 mm diameter bend loss”) and measuring the increase in attenuation per turn.

The term “attenuation,” as used herein, is the loss of optical power as the signal travels along the optical fiber. Attenuation is measured as specified by the IEC 60793-1-40:2019 standard entitled “Optical fibres - Part 1-40: Attenuation measurement methods.”

As used herein, the multicore optical fiber can include a plurality of cores, wherein each core can be defined as an i^th core (i.e., 1^st, 2^nd, 3^rd, 4^th, etc). Each i^th core can have an outer radius r_Ci, an average relative refractive index Δ_Ci, and a maximum relative refractive index A_CiMAX. Each i^th core is disposed within a cladding matrix of the multicore optical fiber, which defines an outer common cladding of the multicore optical fiber. The outer common cladding includes a relative refractive index Δ_OCC and an outer radius Rocc. Optionally, an inner common cladding may be disposed within the outer common cladding of the multicore optical fiber. The inner common cladding includes a relative refractive index Δ_ICC and an outer radius R_ICC. In embodiments in which the inner common cladding is not present, the refractive index of the outer common cladding is typically referred to as Δ_CC and the outer radius of the common cladding is typically referred to as Rec.

Optionally, each i^th core includes a corresponding i^th centerline region that includes an outer radius r_CLi and maximum relative refractive index Δ_CLi. Thus, i=1 refers to a first core having an outer radius r_C1 and relative refractive index Δ_Cl and a centerline region having an outer radius r_CL1 and maximum relative refractive index Δ_CL1. When i=2, the core is referred to as a second core having an outer radius r_C2 and relative refractive index Δ_C2. When the second core includes a corresponding i^th centerline region, where i=2, it is referred to as the second centerline region and includes an outer radius r_CL2 and maximum relative refractive index Δ_CL2. Each additional i^th core and optional i^th inner cladding is referred to as a third core and optional centerline region (i=3), a fourth core and optional fourth centerline region (i=4), etc... The number assigned to each i^th core is used to distinguish one core from another for the purposes of discussion and does not necessarily imply any particular ordering of the cores.

Optionally, each i^th core is surrounded by a corresponding i^th inner cladding having a width δr_ICi and a relative refractive index Δ_ICi. Thus, i=1 refers to a first core having an outer radius r_C1 and relative refractive index Δ_C1. When the first core is surrounded by a corresponding i^th inner cladding, where i=1, it is referred to as the first inner cladding and has a width δr_ICl and a relative refractive index Δ_IC1. When i=2, the core is referred to as a second core having an outer radius r_C2 and relative refractive index Δ_C2. When the second core is surrounded by a corresponding i^th inner cladding, where i=2, it is referred to as the second inner cladding and includes a width δr_IC2 and a relative refractive index Δ_IC2. Each additional i^th core and optional i^th inner cladding is referred to as a third core and optional third inner cladding (i=3), a fourth core and optional fourth inner cladding (i=4), etc... The number assigned to each i^th core is used to distinguish one core from another for the purposes of discussion and does not necessarily imply any particular ordering of the cores.

According to one aspect of the present disclosure, the core forms the central portion of each core fiber within the multicore optical fiber and is substantially cylindrical in shape. In addition, when present, the surrounding inner cladding region is substantially annular in shape. Annular regions may be characterized in terms of an inner radius and an outer radius. Radial positions r refer herein to the outermost radii of the region (e.g., the core, the centerline region, the inner cladding region, etc...). When two regions are directly adjacent to each other, the outer radius of the inner of the two regions coincides with the inner radius of the outer of the two regions. For example, in embodiments in which an inner cladding region surrounds and is directly adjacent to a core region, the outer radius of the core region coincides with the inner radius of the inner cladding region and the outer radius of the inner cladding region is separated from the inner radius of the inner cladding region by the width δr_IC.

An “up-dopant” is herein considered to be a substance added to the glass of the component being studied that has a propensity to raise the refractive index relative to pure undoped silica. A “down-dopant” is herein considered to be a substance added to the glass of the component being studied that has a propensity to lower the refractive index relative to pure undoped silica. Examples of up-dopants include GeO₂ (germania), Al₂O₃, P₂O₅, TiO₂, Cl, Br, and alkali metal oxides, such as K₂O, Na₂O, Li₂O, C_S2O, Rb₂O, and mixtures thereof. Examples of down-dopants include fluorine and boron.

The term “crosstalk” in a multi-core fiber is a measure of how much power leaks from one core to another, adjacent core. As used herein, the term “adjacent core” refers to the core that is nearest to the reference core. In embodiments, all cores may be equally spaced from one another, meaning that all cores are adjacent one another. In other embodiments, the cores may not be equally spaced from one another, meaning that some cores will be spaced further from the reference core than adjacent cores are spaced from the reference core. The crosstalk can be determined based on the coupling coefficient, which depends on the refractive index profile design of the core, the distance between the two adjacent cores, the structure of the cladding surrounding the two adjacent cores, and Δβ, which depends on a difference in propagation constant β values between the two adjacent cores. For two adjacent cores with power P₁ launched into the first core, then the power P₂ coupled from the first core to the second core can be determined from coupled mode theory using the following equation (5):

$\begin{array}{cc}{P}_2=\frac{L}{L_c}〈{\left(\frac{\kappa }{g}\right)}^{2}si{n}^2\left(g\Delta L\right)〉P_1& \text{­­­(5)}\end{array}$

where < > denotes the average, L is fiber length, K is the coupling coefficient between the electric fields of the two cores, ΔL is the length of the fiber, L_c is the correlation length, and g is given by the following equation (6):

$\begin{array}{cc}{g}^2={\kappa }^2+{\frac{\left(\Delta \beta \right)}{2}}^2& \text{­­­(6)}\end{array}$

where Δβ is the mismatch in propagation constants between the LP01 modes in the two adjacent cores when they are isolated. The crosstalk (in dB) is then determined using the following equation (7):

$\begin{array}{cc}X=10log\left(\frac{P_2}{P_1}\right)=10log\left(\frac{L}{L_c}〈{\left(\frac{\kappa }{g}\right)}^{2}si{n}^2\left(g\Delta L\right)〉\right)& \text{­­­(7)}\end{array}$

The crosstalk between the two adjacent cores increases linearly with fiber length in the linear scale (equation (5)) but does not increase linearly with fiber length in the dB scale (equation (7)). As used herein, crosstalk performance is referenced to a 1 km length L of optical fiber. However, crosstalk performance can also be represented with respect to alternative optical fiber lengths, with appropriate scaling. For optical fiber lengths other than 1 km, the crosstalk between cores can be determined using the following equation (8):

$\begin{array}{cc}X\left(L\right)=X\left(100\right)+10log\left(L\right)& \text{­­­(8)}\end{array}$

For example, for a 10 km length of optical fiber, the crosstalk can be determined by adding “10 dB” to the crosstalk value for a 1 km length optical fiber. For a 100 km length of optical fiber, the crosstalk can be determined by adding “20 dB” to the crosstalk value for a 1 km length of optical fiber. For long-haul transmission in an uncoupled-core multicore fiber, the crosstalk should be less than or equal to -50 dB, less than or equal to -60 dB, or even less than or equal to -70 dB. For long-haul transmission in a coupled-core multicore fiber, the crosstalk is greater than or equal to -40 dB, greater than or equal to -30 dB, greater than or equal to -20 dB, or even greater than or equal to -10 dB. If the coupling coefficient is large enough, the power can couple back and forth periodically between two cores along the fiber. In this case, the crosstalk does not scale with the fiber length, but changes periodically. The crosstalk could even reach 100%, or zero dB.

Techniques for determining crosstalk between cores in a multicore optical fiber can be found in M. Li, et al., “Coupled Mode Analysis of Crosstalk in Multicore Fiber with Random Perturbations,” in Optical Fiber Communication Conference, OSA Technical Digest (online), Optical Society of America, 2015, paper W2A.35, and Shoichiro Matsuo, et al., “Crosstalk behavior of cores in multi-core fiber under bent condition,” IEICE Electronics Express, Vol. 8, No. 6, p. 385-390, published Mar. 25, 2011 and Lukasz Szostkiewicz, et al., “Cross talk analysis in multicore optical fibers by supermode theory,” Optics Letters, Vol. 41, No. 16, p. 3759-3762, published Aug. 15, 2016, the contents of which are all incorporated herein by reference in their entirety.

The phrase “coupling coefficient” K, as used herein, is related to the overlap of electric fields when the two cores are close to each other. The square of the coupling coefficient, K², is related to the average power in core m as influenced by the power in other cores in the multicore optical fiber. The “coupling coefficient” can be estimated using the coupled power theory, with the methods disclosed in M. Koshiba, K. Saitoh, K. Takenaga, and S. Matsuo, “Analytical Expression of Average Power-Coupling Coefficients for Estimating Intercore Crosstalk in Multicore Fibers,” IEEE Photonics J., 4(5), 1987-95 (2012); and T. Hayashi, T. Sasaki, E. Sasaoka, K. Saitoh, and M. Koshiba, “Physical Interpretation of Intercore Crosstalk in Multicore Fiber: Effects of Macrobend, Structure Fluctuation, and Microbend,” Optics Express, 21(5), 5401-12 (2013), the contents of which are incorporated by reference herein in their entirety.

Directional terms as used herein - for example up, down, right, left, front, back, top, bottom - are made only with reference to the figures as drawn and are not intended to imply absolute orientation.

Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order, nor that with any apparatus specific orientations be required. Accordingly, where a method claim does not actually recite an order to be followed by its steps, or that any apparatus claim does not actually recite an order or orientation to individual components, or it is not otherwise specifically stated in the claims or description that the steps are to be limited to a specific order, or that a specific order or orientation to components of an apparatus is not recited, it is in no way intended that an order or orientation be inferred, in any respect. This holds for any possible non-express basis for interpretation, including: matters of logic with respect to arrangement of steps, operational flow, order of components, or orientation of components; plain meaning derived from grammatical organization or punctuation, and; the number or type of embodiments described in the specification.

As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a” component includes aspects having two or more such components, unless the context clearly indicates otherwise.

The present description provides a coupled-core multicore optical fiber having a plurality of cores that are doped with alkali metals or chlorine to achieve low attenuation and a large effective area. The cores may be embedded in an inner (or common inner) cladding region that may be fluorine doped, which may be surrounded by an outer (or common outer) cladding, which may also be fluorine doped, with a total diameter of 125 µm or greater, such as for example about 200 µm. For instance, the total diameter may be greater than or equal to 125 µm and less than or equal to 180 µm. In other embodiments, the cores may be doped with chlorine, either with the alkali metals described above or without the alkali metals.

Coupled-core multicore optical fiber is distinct from uncoupled-core multicore optical fiber. In the uncoupled variety, the cores are meant to be spatially isolated from one another to limit crosstalk between the cores. Coupled-core multicore optical fibers, however, take advantage of crosstalk between the cores. As a result, the distance between cores (i.e., the “core pitch”) can be much smaller in coupled-core multicore optical fibers than in uncoupled-core multicore optical fibers, allowing for more cores per unit area of the cross section of the multicore optical fiber.

Referring now to FIG. 1, an optical system 100 comprising a coupled-core multicore optical fiber 110 with a plurality of cores C₁, C₂ (FIG. 2), a signal source 180, and a photon detector 190 is schematically depicted. The signal source 180 may produce multiple modulated signals, S₁ and S₂, such as those produced by a distributed feedback lasers (DFB) or vertical-cavity surface-emitting lasers (VCSEL). The coupled-core multicore optical fiber 110 comprises an input end 112 optically coupled to the signal source 180 and an output end 114 optically coupled to the photodetector 190 and an outer surface 116. In operation, the signal source 180 may selectively direct photons from one laser into an individual core of the plurality of cores. For example, the signal source 180, the input end 112 of the coupled-core multicore optical fiber 110, or both, may be coupled to a multicore fan-in device, which is configured to align the signal source 180 with any individual core of the plurality of cores. For example, the signal S₁ from signal source 180 may be aligned with the core C₁ (FIG. 2) of the coupled-core multicore optical fiber 110 and may direct a plurality of photons into the core C₁, and the signal S₂ from signal source 180 may be aligned with the core C₂ (FIG. 2) of the coupled-core multicore optical fiber 110 and may direct a plurality of photons into the core C₂.

FIGS. 2 and 3 illustrate an isometric view of a section of a coupled-core multicore optical fiber 110 and a cross-sectional view of the coupled-core multicore optical fiber 110 along section 3-3 of FIG. 2, respectively. The coupled-core multicore optical fiber 110 includes a central fiber axis 12 (the centerline of the coupled-core multicore optical fiber 110, which defines radial position R = 0) and a cladding matrix 14 defining a common cladding 19. The common cladding 19 can have an outer radius R_CC, which in the illustrated embodiment of FIGS. 2 and 3 corresponds to the outer radius of the coupled-core multicore optical fiber 110. A plurality of cores C_i (individually denoted C₁ and C₂ in the example of FIGS. 2 and 3 and collectively referred to as cores “C”) are disposed within the cladding matrix 14, with each core C_iforming a core fiber CF_i that generally extends through a length of the coupled-core multicore optical fiber 110 parallel to the central fiber axis 12. With reference to FIG. 3, each core C₁ and C₂ includes a central axis or centerline CL₁ and CL₂ (which define radial position r = 0 for each core) and an outer radius r_C1 and r_C2, respectively. A position of each of the centerlines CL₁ and CL₂ within the coupled-core multicore optical fiber 110 can be defined using Cartesian coordinates with the central fiber axis 12 defining the origin (0,0) of an x-y coordinate system coincident with the coordinate system defined by the radial coordinate R. The position of centerline CL₁ can be defined as (x₁,y₁) and the position of centerline CL₂ can be defined as (x₂,y₂). A distance D_C1-C2 between the centerlines CL₁ and CL₂ can then be defined as √[(x₂- x₁)² + (y₂ - y₁)²], and may be referred to herein as “core pitch.” Thus, for a given core C_ihaving a centerline CL_i and an adjacent core C_j having a centerline CL_j, a distance D_Ci-Cj is defined as √[(x_j - x_i)² + (y_j - y_i)²]. The plurality of cores C_imay also be spaced apart from the central fiber axis 12 by a predetermined distance D_12-Ci as measured from the central fiber axis 12 to the centers CL_i of each of the plurality of cores C_i. The plurality of cores C_imay also be spaced apart from the outer surface 116 of the coupled-core multicore optical fiber 110 by a predetermined distance D_CEi-116 as measured from the edge CE_i of each of the plurality of cores C_ito the outer surface 116. The D_CEi-116 may be composed of a range of values depending on the symmetry of the arrangement of each of the plurality of cores Ci within the coupled-core multicore optical fiber 110. For instance, the distance between CE₁ and point A on outer surface 116 of coupled-core multicore optical fiber 110 of FIG. 3 is much smaller than the distance between CE₁ and point B. Without intending to be bound by any particular theory, it is believed that the extent of signal loss due to tunneling is dependent upon the minimum value for D_CEi-116.

In embodiments, the multicore optical fiber can have a circular cross-section shape with seven cores, wherein six of the cores are at the vertices of a hexagon and the seventh core is at the center of the circular cross-section. In some embodiments, the multicore optical fiber of the present disclosure can have a circular cross-section and the cores can be arranged in a 2 × 2 configuration. In still other embodiments, the multicore optical fiber of the present disclosure can have a circular cross-section and the number of cores can be between 10 and 20. The coupled-core multicore optical fiber 110 can have N number of total cores C_i, wherein i=1 ... N and N is at least 2. According to one aspect of the present disclosure, the total number N of cores C_i in the multicore optical fiber 10 is from 2 to 20, 2 to 18, 2 to 16, 2 to 12, 2 to 10, 2 to 8, 2 to 6, 2 to 4, 2 to 3, 4 to 20, 4 to 18, 4 to 16, 4 to 12, 4 to 10, 4 to 8, 4 to 6, 6 to 20, 6 to 18, 6 to 16, 6 to 12, 6 to 10, 6 to 8, 8 to 20, 8 to 18, 8 to 16, 8 to 12, 8 to 10, 10 to 20, 10 to 18, 10 to 16, 10 to 12, 12 to 20, 12 to 18, or 12 to 16. For example, the total number N of cores C_i in the multicore optical fiber 10 can be 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, or any total number N of cores C_i between any of these values. The total number N of cores C_i can be even or odd and can be arranged in any pattern within the cladding matrix 14, non-limiting examples of which include a 2 × 2 pattern (or multiples thereof; see, e.g., FIGS. 5A and 5B, discussed below), a square pattern, a rectangular pattern, a circular pattern, and a hexagonal lattice pattern. For example, the multicore optical fiber 10 can have N=7 cores C_i arranged in a hexagonal lattice pattern. In another example, the multicore optical fiber 10 can have N=12 cores C_i arranged in a circular pattern. In one example, the coupled-core multicore optical fiber 110 can have a core C_i positioned such that the core centerline CL_i aligns with the central fiber axis 12. In another example, the coupled-core multicore optical fiber 110 can have a core C_i pattern such that the cores C_i are spaced around the central fiber axis 12.

Referring now to FIG. 4, according to embodiments, one or more of the plurality of cores C_i of the coupled-core multicore optical fiber 110 can optionally be surrounded by an inner cladding IC_i. The inner cladding, when included, may help increase coupling and crosstalk between adjacent cores. Each inner cladding IC_i has an outer radius r_ICi and an inner radius that corresponds to the outer radius rC_i of the core C_i. The inner cladding IC_i has a width δr_ICi defined by the outer radius rC_i of the core C_iand the outer radius r_ICi of the inner cladding IC_i. The core C_i can include a diameter d_i corresponding to 2*r_Ci and the inner cladding IC_i can include a diameter d_ICi corresponding to 2*r_ICi. The diameter d_ICi also corresponds to the diameter of core fiber CF_i.

Referring now to FIG. 5A, which depicts an X-Y cross-section of an embodiment of the coupled-core multicore optical fiber 110 in which coupled-core multicore optical fiber 110 comprises four cores C₁, C₂, C₃, C₄ disposed in a common cladding. In this embodiment, the common cladding is an inner common cladding 20 having an outer radius R_ICC. The inner common cladding 20 surrounds each core of the plurality of cores (i.e., cores C₁, C₂, C₃, C₄), each core having a radius r_C1, r_C2, r_C3, r_C4, respectively. The inner common cladding 20 is in turn disposed in an outer common cladding 21 having an outer radius R_OOC; the outer radius Rocc also represents the outer radius of the entire glass portion of the coupled-core multicore optical fiber 110. Accordingly, it should be understood that the outer radius R_ICC of the inner common cladding 20 is less than the radius Rocc of the outer common cladding 21. It should be understood that what is depicted in the figures is the “glass portion” of the optical fiber. One or more coatings may be disposed around the glass portion (i.e., around the outer common cladding 21). The coating(s) may be used to protect the glass of the coupled-core multicore optical fiber 110. Further, the coating(s) may also be used to enhance the optical properties of the coupled-core multicore optical fiber 110. Outer common cladding 21 may have a radial thickness t_ROCC that extends from the outer surface 127 of the inner common cladding 20 to the outer surface 116 of the coupled-core multicore optical fiber 110. The cores C₁, C₂, C₃, C₄ are distributed within the inner common cladding 20 so as to have a core pitch D_Ci-Cj. The term “core pitch”, as used herein, refers to the distance between the centers CL_i, CL_j of two adjacent cores C_i, C_j (i.e., the center-to-center spacing between two adjacent cores). The cores C₁, C₂, C₃, C₄ may also be spaced apart from the central fiber axis 12 by a predetermined distance D_12-Ci, where each D_12-Ci is measured from the central fiber axis 12 to the centers CL₁, CL₂, CL₃, CL₄ of each of the cores C₁, C₂, C₃, C₄, respectively.

In embodiments, the radius R_ICC of the inner common cladding 20 may be greater than or equal to 20 µm and less than or equal to 45 µm or greater than or equal to 25 µm and less than or equal to 40 µm or greater than or equal to 20 µm and less than or equal to 30 µm or greater than or equal to 30 µm and less than or equal to 35 µm or even greater than or equal to 35 µm and less than or equal to 45 µm. It should be understood that the radius R_ICC may be within a range formed from any one of the lower bounds for the radius R_ICC and any one of the upper bounds of the radius R_ICC described herein.

In the same or alternative embodiments, the radius rC_i of each core C_imay be greater than or equal to 3 µm and less than or equal to 10 µm or greater than or equal to 4 µm and less than or equal to 9 µm or greater than or equal to 4 µm and less than or equal to 8 µm or greater than or equal to 4 µm and less than or equal to 7 µm or greater than or equal to 4 µm and less than or equal to 6 µm or greater than or equal to 4 µm and less than or equal to 5 µm or greater than or equal to 5 µm and less than or equal to 7 µm or even greater than or equal to 6 µm and less than or equal to 7 µm. It should be understood that the radius rC_i may be within a range formed from any one of the lower bounds for the radius rC_i and any one of the upper bounds of the radius rC_i described herein.

Still referring to FIG. 5A, in embodiments, R_ICX may be defined as R_ICC - D_12-Ci-rC_i and is the distance between the edge of core C_i and the edge of the inner common cladding 20 as defined by the radius R_ICC along a line formed from the center CL_i of the core and the central fiber axis 12. In embodiments, R_ICX may be greater than or equal to 15 µm and less than or equal to 30 µm or greater than or equal to 16 µm and less than or equal to 29 µm or greater than or equal to 17 µm and less than or equal to 28 µm or greater than or equal to 18 µm and less than or equal to 27 µm or greater than or equal to 19 µm and less than or equal to 26 µm or greater than or equal to 20 µm and less than or equal to 25 µm or greater than or equal to 21 µm and less than or equal to 24 µm or even greater than or equal to 22 µm and less than or equal to 23 µm. It should be understood that R_ICX may be within a range formed from any one of the lower bounds for the radius R_ICX and any one of the upper bounds of the radius R_ICX described herein.

Referring now to FIG. 5B, which depicts an X-Y cross-section of an embodiment of the coupled-core multicore optical fiber 110 in which coupled-core multicore optical fiber 110 comprises four cores C₁, C₂, C₃, C₄, each surrounded by an individual inner cladding IC_i and disposed in an outer common cladding 21. Each core of the plurality of cores (i.e., cores C₁, C₂, C₃, C₄) has radius r_C1, r_C2, r_C3, r_C4, respectively, and each inner cladding of the plurality of inner claddings has radius r_ICI, r_IC2, r_IC3, r_IC4, respectively. Each of the plurality of cores is disposed in an outer common cladding 21 having an outer radius R_OOC; the outer radius Rocc also represents the outer radius of the entire glass portion of the coupled-core multicore optical fiber 110. It should be understood that what is depicted in the figures is the “glass portion” of the optical fiber. One or more coatings may be disposed around the glass portion (i.e., around the outer common cladding 21). The coating(s) may be used to protect the glass of the coupled-core multicore optical fiber 110. Further, the coating(s) may also be used to enhance the optical properties of the coupled-core multicore optical fiber 110. The cores C₁, C₂, C₃, C₄ are distributed within the common cladding 21 so as to have a core pitch D_Ci-Cj. The term “core pitch”, as used herein, refers to the distance between the centers CL_i, CL_j of two adjacent cores C_i, C_j (i.e., the center-to-center spacing between two adjacent cores). The cores C₁, C₂, C₃, C₄ may also be spaced apart from the central fiber axis 12 by a predetermined distance D_12-Ci, where each D_12-Ci is measured from the central fiber axis 12 to the centers CL₁, CL₂, CL₃, CL₄ of each of the cores C₁, C₂, C₃, C₄, respectively.

In the same or alternative embodiments, the radius r_ICi of each inner cladding IC_i (depicted in FIG. 4) may be greater than or equal to 8 µm and less than or equal to 16 µm or greater than or equal to 9 µm and less than or equal to 15 µm or greater than or equal to 10 µm and less than or equal to 14 µm or even greater than or equal to 11 µm and less than or equal to 13 µm. It should be understood that the radius r_ICi may be within a range formed from any one of the lower bounds for the radius r_ICi and any one of the upper bounds of the radius r_ICi described herein.

While FIGS. 5A and 5B depicts a coupled-core multicore optical fiber 110 having four cores CL₁, CL₂, CL₃, CL₄, it should be understood that other arrangements are contemplated and possible. For example and without limitation, FIGS. 6A-6D show alternative embodiments of coupled-core multicore optical fiber 110 core layouts with each of the plurality of cores CL_i distributed in the common cladding 21. In particular, FIG. 6A shows a coupled-core multicore optical fiber 110a having three cores C₁, C₂, C₃. In this embodiment, the coupled-core multicore optical fiber 110a may have a core pitch D_Ci-Cj of, for example and without limitation, 38 micrometers (µm). FIG. 6B shows a coupled-core multicore optical fiber 110b having three cores C₁, C₂, C₃. In this embodiment, the coupled core multicore optical fiber 110b may have a core pitch D_Ci-Cj of, for example and without limitation, 29 µm. FIG. 6C shows a coupled-core multicore optical fiber 110c having six cores C₁, C₂, C₃, C₄, C₅, C₆ arranged in a hexagonal configuration. Hybrid designs with clusters of two or more closely-coupled cores C_i, C_j distributed in the common cladding 21 are also contemplated and possible. For example, FIG. 6D shows a coupled-core multicore optical fiber 110d having three clusters of three cores C₁, C₂, C₃, C₄, C₅, C₆, C₇, C₈, C₉ with each cluster of cores arranged in a triangular configuration. The embodiment shown in FIG. 6D also includes a tenth marker core, C_M, which does not transmit data but can facilitate optical alignment of the MCF during splicing and connectorization. It should be understood that the foregoing examples are intended to be illustrative, not limiting, and many other arrangements of the cores of the coupled-core multicore optical fibers are contemplated and possible.

In embodiments, the core C_i may include alkali-doped silica glass, with the inner cladding IC_i doped with fluorine to provide an index differential between the core and the common cladding layer. The alkali-doped silica glass of the core Ci may include for example, concentrations of alkali metal oxide from 20 ppm to 1000 ppm, from 50 ppm to 600 ppm, or even from 110 ppm to 200 ppm. The alkali may include, for example, oxides of sodium, potassium, rubidium, lithium, cesium, or a combination of two or more of these. In some embodiments, the core comprises more than one alkali doped in the core.

In embodiments, the silica-based glass of each of the plurality of cores C_i may comprise silica-based glass doped with one or more alkali metal oxides selected from K₂O, Na₂O, Li20, Cs₂O, Rb₂O, and mixtures thereof. Without intending to be bound by any particular theory, it is believed that including alkali metal oxides as dopants in each of the plurality of cores C_i may reduce the viscosity of the glass at elevated temperatures which, in turn, aids relaxation by mitigating the development of stress in the glass during drawing. The mitigation of stress in the glass decreases the attenuation of the glass. However, if the glass is doped with too much alkali, the concentration fluctuation contribution to Rayleigh scattering may be increased, leading to an increased observed attenuation. Further, in embodiments in which the silica-based glass is co-doped with both alkali metal oxides and germania, undesirable crystallization may occur.

In embodiments including the alkali metal oxide, the concentration of the alkali metal oxide in each of the plurality of cores C_i may be greater than or equal to 20 ppm and less than or equal to 1000 ppm by weight (0.1 wt.%) of each of the plurality of cores C_i. For example, the concentration of alkali metal oxide may be greater than or equal to 50 ppm (0.005 wt.%) and less than or equal to 950 ppm (0.095 wt.%) or greater than or equal to 100 ppm (0.01 wt.%) and less than or equal to 900 ppm (0.09 wt.%) or greater than or equal to 150 ppm (0.015 wt.%) and less than or equal to 850 ppm (0.085 wt.%) or greater than or equal to 200 ppm (0.02 wt.%) and less than or equal to 800 ppm (0.08 wt.%) or greater than or equal to 250 ppm (0.025 wt.%) and less than or equal to 750 ppm (0.075 wt.%) or greater than or equal to 300 ppm (0.03 wt.%) and less than or equal to 700 ppm (0.07 wt.%) or greater than or equal to 350 ppm (0.035 wt.%) and less than or equal to 650 ppm (0.065 wt.%) or greater than or equal to 400 ppm (0.04 wt.%) and less than or equal to 600 ppm (0.06 wt.%) or even greater than or equal to 450 ppm (0.045 wt.%) and less than or equal to 550 ppm (0.055 wt.%). It should be understood that the amount of alkali metal oxide in the silica-based glass may be within a range formed from any one of the lower bounds for alkali metal oxide and any one of the upper bounds of alkali metal oxide described herein.

In the same or different embodiments, the silica-based glass of each of the plurality of cores C_i may comprise silica-based glass doped with fluorine. Fluorine is a down-dopant that reduces the index of refraction of each of the plurality of cores C_i relative to undoped silica. In some embodiments, the concentration of fluorine in each of the plurality of cores C_i is greater than or equal to 0.02 wt.% and less than or equal to 0.15 wt.% by weight of the fully formed core C_i. For example, the concentration of fluorine in each of the plurality of cores C_i may be greater than or equal to 0.04 wt.% and less than or equal to 0.13 wt.%, greater than or equal to 0.06 wt.% and less than or equal to 0.11 wt.%, or even greater than or equal to 0.08 wt.% and less than or equal to 0.09 wt.%. It should be understood that the amount of fluorine in the compositions may be within a range formed from any one of the lower bounds for fluorine and any one of the upper bounds of fluorine described herein.

In embodiments, the silica-based glass of each of the plurality of cores C_i may comprise silica-based glass doped with chlorine. Chlorine is an up-dopant that increases the index of refraction of each of the plurality of cores C_i relative to undoped silica. In some embodiments, the concentration of the chlorine in each of the plurality of cores C_i is greater than or equal to 1 wt.% and less than or equal to 7 wt.% by weight of each of the plurality of cores C_i. For example, the concentration of chlorine may be greater than or equal to 1.5 wt.% and less than or equal to 7 wt.%, greater than or equal to 2 wt.% and less than or equal to 6.5 wt.%, greater than or equal to 2.5 wt.% and less than or equal to 6 wt.%, greater than or equal to 3 wt.% and less than or equal to 5.5 wt.%, greater than or equal to 3.5 wt.% and less than or equal to 5 wt.%, or even greater than or equal to 4 wt.% and less than or equal to 4.5 wt.%. It should be understood that the amount of chlorine in the compositions may be within a range formed from any one of the lower bounds for chlorine and any one of the upper bounds of chlorine described herein.

In embodiments, the silica-based glass of each of the plurality of cores C_i may comprise silica-based glass doped with phosphorus. Phosphorus is an up-dopant that increases the index of refraction of each of the plurality of cores C_i relative to undoped silica. In embodiments in which the phosphorus is present, the concentration of phosphorus in each of the plurality of cores C_i is greater than 0 wt.% and less than or equal to 2 wt.% or greater than or equal to 0.2 wt.% and less than or equal to 1.8 wt.% or greater than or equal to 0.4 wt.% and less than or equal to 1.6 wt.% or greater than or equal to 0.6 wt.% and less than or equal to 1.4 wt.% or greater than or equal to 0.8 wt.% and less than or equal to 1.2 wt.% or even greater than or equal to 1 wt.% and less than or equal to 1.1 wt.%. It should be understood that the amount of phosphorus in the compositions may be within a range formed from any one of the lower bounds for phosphorus and any one of the upper bounds of phosphorus described herein.

In embodiments, the silica-based glass of each of the plurality of cores C_i may comprise silica-based glass doped with phosphorus and one or more alkali metal oxides. In embodiments, the silica-based glass of each of the plurality of cores C_i may comprise silica-based glass doped with phosphorus and chlorine. In embodiments in which both phosphorus and chlorine are present, the concentration of chlorine may be greater than or equal to 1 wt.% to less than or equal to 6.5 wt.%, and the concentration of phosphorus may be greater than or equal to 0.5 wt.% and less than or equal to 2 wt.%. For example, the concentration of chlorine may be greater than or equal to 1.5 wt.% and less than or equal to 6 wt.% or greater than or equal to 2 wt.% and less than or equal to 5.5 wt.% or greater than or equal to 2.5 wt.% and less than or equal to 5 wt.% or greater than or equal to 3 wt.% and less than or equal to 4.5 wt.% or even greater than or equal to 3.5 wt.% and less than or equal to 4 wt.%. It should be understood that the amount of chlorine in the compositions may be within a range formed from any one of the lower bounds for chlorine and any one of the upper bounds of chlorine described herein. Further, the concentration of phosphorus may be greater than or equal to 0.6 wt.% and less than or equal to 1.9 wt.% or greater than or equal to 0.7 wt.% and less than or equal to 1.8 wt.% or greater than or equal to 0.8 wt.% and less than or equal to 1.7 wt.% or greater than or equal to 0.9 wt.% and less than or equal to 1.6 wt.% or greater than or equal to 1 wt.% and less than or equal to 1.5 wt.% or greater than or equal to 1.1 wt.% and less than or equal to 1.4 wt.% or even greater than or equal to 1.2 wt.% and less than or equal to 1.3 wt.%. It should be understood that the amount of phosphorus in the compositions may be within a range formed from any one of the lower bounds for phosphorus and any one of the upper bounds of phosphorus described herein.

When present, the inner common cladding 20 may comprise silica-based glass. In embodiments, the inner common cladding 20 may consist of, or consist essentially of, silica-based glass. In embodiments, the silica-based glass of the inner common cladding 20 may comprise a down-dopant such that the inner common cladding 20 has an index of refraction lower than that of each of the plurality of cores Ci. In embodiments, the down-dopant is fluorine.

In some embodiments, inner common cladding 20, when present, may include fluorine in a concentration greater than or equal to 0.5 wt.% and less than or equal to 1.8 wt.%. For example, the inner common cladding 20 may include fluorine in a concentration greater than or equal to 0.6 wt.% and less than or equal to 1.7 wt.% or greater than or equal to 0.7 wt.% and less than or equal to 1.6 wt.% or greater than or equal to 0.8 wt.% and less than or equal to 1.5 wt.% or greater than or equal to 0.9 wt.% and less than or equal to 1.4 wt.% or greater than or equal to 1 wt.% and less than or equal to 1.3 wt. % or even greater than or equal to 1.1 wt. % and less than or equal to 1.2 wt.% It should be understood that the amount of fluorine in the compositions may be within a range formed from any one of the lower bounds for fluorine and any one of the upper bounds of fluorine described herein.

The outer common cladding 21 may comprise silica-based glass. In embodiments, the outer common cladding 21 may consist of, or consist essentially of, silica-based glass. In embodiments, the silica-based glass of the outer common cladding 21 may comprise a down-dopant, such as fluorine, which reduces the index of refraction such that the outer common cladding 21 has an index of refraction lower than that of each of the plurality of cores C₁ and higher than that of the inner common cladding 20. In other embodiments, each of the plurality of cores C₁ may be undoped, the inner common cladding 20 may include a down-dopant, and the outer common cladding may include an up-dopant. Exemplary up-dopants include, but are not limited to, chlorine, germania, and titania.

In some embodiments, the concentration of fluorine in the silica-based glass of the outer common cladding 21 is greater than or equal to 0.3 wt.% and less than or equal to 1.6 wt.% of the fully formed outer common cladding 21. For example, the concentration of fluorine may be greater than or equal to 0.4 wt.% and less than or equal to 1.5 wt.% or greater than or equal to 0.7 wt.% and less than or equal to 1.4 wt.% or greater than or equal to 0.8 wt.% and less than or equal to 1.3 wt.% or greater than or equal to 0.9 wt.% and less than or equal to 1.2 wt.% or even greater than or equal to 1 wt.% and less than or equal to 1.1 wt.%. It should be understood that the amount of fluorine in the compositions may be within a range formed from any one of the lower bounds for fluorine and any one of the upper bounds of fluorine described herein.

Still referring to FIGS. 5A-5B and 6A-6D, to facilitate coupling between each of the plurality of cores C₁ of the coupled-core multicore optical fiber 110, the core pitch D_Ci-cj may be greater than or equal to 20 µm and less than or equal to 40 µm. For example, the core pitch D_Ci-Cj may be greater than or equal to 20 µm and less than or equal to 35 µm, greater than or equal to 22 µm and less than or equal to 32 µm, greater than or equal to 24 µm and less than or equal to 30 µm, greater than or equal to 25 µm and less than or equal to 30 µm, greater than or equal to 20 µm and less than or equal to 28 µm, greater than or equal to 20 µm and less than or equal to 26 µm, greater than or equal to 30 µm and less than or equal to 40 µm, or even greater than or equal to 32 µm and less than or equal to 38 µm. It should be understood that the core pitch D_ci-cj may be within a range formed from any one of the lower bounds for core pitch D_Ci-Cj and any one of the upper bounds of core pitch D_Ci-Cj described herein.

To minimize radiation or tunneling loss, the minimum distance D_Ci-116 from the centers CL_i of each of the plurality of cores C_i to the outer surface 116 of the coupled-core multicore optical fiber 110 may be greater than or equal to 30 µm in a plane perpendicular to the long axis of the coupled-core multicore optical fiber (i.e., the X-Y plane of the coordinate axes depicted in the figures), such as greater than or equal to 30 µm and less than or equal to 50 µm. For example, the distance D_Ci-116 may be greater than or equal to 32 µm and less than or equal to 48 µm, greater than or equal to 34 µm and less than or equal to 46 µm, greater than or equal to 34 µm and less than or equal to 44 µm, greater than or equal to 36 µm and less than or equal to 42 µm, greater than or equal to 30 µm and less than or equal to 40 µm, greater than or equal to 32 µm and less than or equal to 38 µm, greater than or equal to 34 µm and less than or equal to 36 µm, greater than or equal to 40 µm and less than or equal to 50 µm, greater than or equal to 42 µm and less than or equal to 48 µm, or even greater than or equal to 44 µm and less than or equal to 46 µm. It should be understood that the distance D_Ci-116 may be within a range formed from any one of the lower bounds for this distance D_Ci-116 and any one of the upper bounds of this distance D_Ci-116 described herein.

Referring to FIGS. 7A, 7B, and 8, various properties of the inner common cladding 20, the outer common cladding 21, and each of the plurality of cores C_i and inner claddings IC_i will be described in more detail. Some properties are discussed with reference to an “individual core,” C_i, and are applicable to any of the plurality of cores C_i. Other properties characterize a relationship between at least two cores C_i and C_j. For ease of explanation and understanding, the first core C₁ and the second core C₂ are used in these descriptions. However, it should be understood that these properties may apply to any two cores of the plurality of cores C_i.

FIG. 7A shows a relative refractive index profile of a portion of an optical fiber preform from which a coupled-core multicore optical fiber may be drawn, such as the coupled-core multicore optical fiber depicted in FIG. 5A, according to embodiments. The relative refractive index profile of FIG. 7A is presented herein to illustrate the relative positioning of portions of a single core of the coupled-core multicore optical fiber as well as the relative refractive index of a single core of the coupled-core optical fiber. The dimensions of the Y axis and the X axis have been omitted and the variables (such as r_CL1, r_C1, R_ICX, etc.) are superimposed on the ordinates for purposes of illustration only. The horizontal axis of FIG. 7A generally corresponds to the coupled-core multicore optical fiber along a path from a center line CL_i of a core C_i through inner common cladding 20, and across outer common cladding 21, with center line CL₁ representing the r = 0 value of the horizontal axis and Radius referring to radial coordinate r. The vertical axis corresponds to the relative refractive index Δ% (Delta%) as a function of the dimension of the coupled-core multicore optical fiber along the path. At center line CL₁, the core has a relative refractive index Δ_CLI, relative to pure silica, and the centerline region extends to radius r_CL1. The core C₁ surrounds the centerline region and has a radius r_Cl with average relative refractive index Δ_CI, relative to pure silica. Between the edge (r_C1) of the core C_l and the edge of the inner common cladding ICC of the coupled-core multicore optical fiber 110, designated as R_ICX, the inner common cladding ICC has an average relative refractive index Δ_ICC, relative to pure silica. In the embodiment shown in FIG. 7A, the inner common cladding ICC is surrounded by outer common cladding OCC, which has an average relative refractive index Δ_OCC, relative to pure silica. In embodiments, Δ_CLI > Δ_Cl > Δ_ICC. In embodiments, Δ_CLI > Δ_Cl > Δ_occ > Δ_ICC. In embodiments, without the optional higher index inner core segment, Δ_Cl > Δ_ICC. In some of these embodiments, Δ_Cl > Δ_OCC > Δ_ICC. The dopants may be used, as described in the preceding paragraphs, to achieve the desired differences in A_CL1, Δ_CI, and Δ_ICC.

FIG. 7B shows a relative refractive index profile of a portion of an optical fiber preform from which a coupled-core multicore optical fiber may be drawn, such as the coupled-core multicore optical fiber depicted in FIG. 5B, according to embodiments. The relative refractive index profile of FIG. 7B is presented herein to illustrate the relative positioning of portions of a single core of the coupled-core multicore optical fiber as well as the relative refractive index of a single core of the coupled-core optical fiber. The dimensions of the Y axis and the X axis have been omitted and the variables (such as r_CL1, r_C1, R_ICI, etc.) are superimposed on the ordinates for purposes of illustration only. The horizontal axis of FIG. 7B generally corresponds to the coupled-core multicore optical fiber along a path from a center line CL_i of a core C_i through inner cladding IC, and across outer common cladding 21, with center line CL₁ representing the r = 0 value of the horizontal axis and Radius referring to radial coordinate r. The vertical axis corresponds to the relative refractive index Δ% (Delta%) as a function of the dimension of the coupled-core multicore optical fiber along the path. At center line CL₁, the core has a relative refractive index Δ_CLI, relative to pure silica, and the centerline region extends to radius r_CL1. The core C₁ surrounds the centerline region and has a radius r_Cl with average relative refractive index Δ_CI, relative to pure silica. Between the edge (r_C1) of the core C_i and the edge of the inner cladding IC_i of the coupled-core multicore optical fiber 110, designated as R_ICI, the inner cladding IC_i has an average relative refractive index Δ_ICI, relative to pure silica. In the embodiment shown in FIG. 7B, the inner cladding IC_i is surrounded by outer common cladding OCC, which has an average relative refractive index ΔOCC, relative to pure silica. In embodiments, Δ_CLI > Δ_Cl > Δ_ICI. In embodiments, Δ_CLI > Δ_Cl > Δ_OCC > Δ_ICI. In embodiments, without the optional higher index inner core segment, Δ_Cl > Δ_ICI. In some of these embodiments, Δ_C1 > Δ_OCC > Δ_IC1. The dopants may be used, as described in the preceding paragraphs, to achieve the desired differences in Δ_CL1, Δ_C1, and Δ_IC1.

In embodiments, Δ_CLI is greater than or equal to -0.1 Δ% and less than or equal to 0.3 Δ%. For example, Δ_CLI may be greater than or equal to -0.05 Δ% and less than or equal to 0.25 Δ% or greater than or equal to -0.03 Δ% and less than or equal to 0.2 Δ% or even greater than or equal to -0.03 Δ% and less than or equal to 0.15 Δ%. It should be understood Δ_CLI may be within a range formed from any one of the lower bounds for Δ_CL1 and any one of the upper bounds of Δ_CL1 described herein.

In embodiments, Δ_Cl is greater than or equal to -0.1 Δ% and less than or equal to 0.2 Δ%. For example, Δ_Cl may be greater than or equal to -0.05 Δ% and less than or equal to 0.15 Δ% or even greater than or equal to 0 Δ% and less than or equal to 0.1 Δ%. It should be understood Δ_Cl may be within a range formed from any one of the lower bounds for Δ_Cl and any one of the upper bounds of Δ_Cl described herein.

In embodiments with an inner common cladding as depicted in FIG. 5A, Δ_ICC is greater than or equal to -0.4 Δ% and less than or equal to -0.2 Δ%. For example, Δ_ICC may be greater than or equal to -0.35 Δ% and less than or equal to -0.25 Δ%. It should be understood Δ_ICC may be within a range formed from any one of the lower bounds for Δ_ICC and any one of the upper bounds of Δ_ICC described herein.

In embodiments in which each of the plurality of the cores is surrounded by an individual inner cladding as depicted in FIG. 5B, Δ_ICI is greater than or equal to -0.4 Δ% and less than or equal to -0.2 Δ%. For example, Δ_ICI may be greater than or equal to -0.35 Δ% and less than or equal to -0.25 Δ%. It should be understood Δ_IC1 may be within a range formed from any one of the lower bounds for Δ_ICI and any one of the upper bounds of Δ_ICI described herein.

In embodiments, Δ_OCC is greater than or equal to -0.4 Δ% and less than or equal to -0.2 Δ%. For example, Δ_OCC may be greater than or equal to -0.35 Δ% and less than or equal to -0.25 Δ%. It should be understood Δ_OCC may be within a range formed from any one of the lower bounds for Δ_OCC and any one of the upper bounds of Δ_OCC described herein.

While not intending to be limited by theory, the electro-magnetic fields of the waves (e.g., light waves) propagating in the coupled-core multicore optical fiber 110 may be coupled, for example, selectively coupled, when certain conditions are met. For example, each of the plurality of cores C_i of the coupled-core multicore optical fiber 110 may be characterized by a plurality of coupling coefficients (i.e., various coupling coefficients for coupling from one individual core, such as the first core C₁, to another individual core, such as the second core C₂). Coupling coefficients measure the amount of overlay between the modal fields of two cores of the plurality of cores C₁, such as the first core C₁ and the second core C₂. Modal fields of the cores depend on various parameters, such as the radius of the core r_Ci, the refractive index of the core, the material of the core, the material of the cladding, and the wavelength of operation (λ) (i.e., the wavelength of light propagating in the core).

The coupling coefficient κ between two adjacent cores C_1, C₂ depend upon the core pitch between adjacent cores, which may also be referred to as the core spacing. Larger coupling coefficients are expected as the distance between cores decreases. For instance, at very small core spacing, e.g. 15 µm, the coupling coefficient may be greater than or equal to 100 (linear units) per meter and less than or equal to 600 per meter, or greater than or equal to 150 per meter and less than or equal to 550 per meter, or even greater than or equal to 300 per meter and less than or equal to 400 per meter. However, at very large core spacing, e.g. 60 µm, the coupling coefficient may be greater than or equal to 8 × 10^-6 per meter and less than or equal to 4 × 10^-4 per meter.

In embodiments, the coupling coefficient may be greater than or equal to 1 × 10^-3 /m. For instance, the power coupling coefficient may be greater than or equal to 1 × 10^-3 /m and less than or equal to 5 × 10^-3 /m or greater than or equal to 1.5 × 10^-3 /m and less than or equal to 4.5 × 10^-3 /m or greater than or equal to 2 × 10^-3 /m and less than or equal to 4 × 10^-3 /m or even greater than or equal to 2.5 × 10^-3 /m and less than or equal to 3.5 × 10^-3 /m.

Another parameter affecting the transmission of information using the fibers described herein is crosstalk. In various embodiments, the crosstalk between two adjacent cores 120a, 120b is greater than or equal to -30 dB for 1 km fiber length and less than or equal to 0 dB for 1 km fiber length. For example, the crosstalk may be greater than or equal to -25 dB for 1 km fiber length and less than or equal to -1 dB for 1 km fiber length, greater than or equal to -20 dB for 1 km fiber length and less than or equal to -2 dB for 1 km fiber length, greater than or equal to -15 dB for 1 km fiber length and less than or equal to -3 dB for 1 km fiber length, or even greater than or equal to -10 dB for 1 km fiber length and less than or equal to -4 dB for 1 km fiber length. It should be understood crosstalk may be within a range formed from any one of the lower bounds for crosstalk and any one of the upper bounds of crosstalk described herein.

In embodiments, each core of the coupled-core multicore optical fiber 110 may have an effective area A_eff of greater than 100 µm² at a wavelength of 1550 nm. The effective area is determined individually for each core of the coupled-core multicore optical fiber without consideration of the effects of crosstalk between the cores of the coupled-core multicore optical fiber. For instance, the effective area or each core may be greater than or equal to 110 µm² and less than or equal to 160 µm², greater than or equal to 120 µm² and less than or equal to 158 µm², greater than or equal to 124 µm² and less than or equal to 156 µm², greater than or equal to 126 µm² and less than or equal to 154 µm², greater than or equal to 128 µm² and less than or equal to 152 µm², greater than or equal to 130 µm² and less than or equal to 150 µm², greater than or equal to 132 µm² and less than or equal to 148 µm², greater than or equal to 134 µm² and less than or equal to 146 µm², greater than or equal to 136 µm² and less than or equal to 144 µm², or even greater than or equal to 138 µm² and less than or equal to 142 µm². In other embodiments, each core of the coupled-core multicore optical fiber 110 may have an effective area of greater than or equal to 70 µm² and less than or equal to 85 µm² at a wavelength of 1550 nm. For instance, the effective area of each core may be greater than or equal to 71 µm² and less than or equal to 84 µm², greater than or equal to 72 µm² and less than or equal to 83 µm², greater than or equal to 73 µm² and less than or equal to 82 µm², greater than or equal to 74 µm² and less than or equal to 81 µm², greater than or equal to 75 µm² and less than or equal to 80 µm², greater than or equal to 76 µm² and less than or equal to 79 µm², or even greater than or equal to 77 µm² and less than or equal to 78 µm². It should be understood that the A_eff of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for A_eff and any one of the upper bounds of A_eff described herein.

The average attenuation of the coupled-core multicore optical fiber is determined by measuring the attenuation for each core of the coupled-core multicore optical fiber at a wavelength of 1510 nm and then calculating an average attenuation for the entire coupled-core multicore optical fiber based on the individual attenuation measurements of each core. In embodiments, the average attenuation of the coupled-core multicore optical fiber 110 is less than or equal to 0.18 dB/km, less than or equal to 0.175 dB/km, less than or equal to 0.17 dB/km, or even less than or equal to 0.165 dB/km. In embodiments, the attenuation of the optical fiber at a wavelength of 1550 nm may be greater than or equal to 0.16 dB/km and less than or equal to 0.18 dB/km, greater than or equal to 0.165 dB/km and less than or equal to 0.175 dB/km, greater than or equal to 0.16 dB/km and less than or equal to 0.175 dB/km, or even greater than or equal to 0.165 dB/km and less than or equal to 0.18 dB/km. It should be understood that the attenuation of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for attenuation and any one of the upper bounds of attenuation described herein.

In various embodiments, the cable cutoff of each core of the coupled-core multicore optical fiber 110 is greater than or equal to 1200 nm and less than or equal to 1530 nm. For example, the cable cutoff of each core of each core of the coupled-core multicore optical fiber 110 may be greater than or equal to 1220 nm and less than or equal to 1530 nm, greater than or equal to 1240 nm and less than or equal to 1530 nm, greater than or equal to 1260 nm and less than or equal to 1530 nm, greater than or equal to 1280 nm and less than or equal to 1530 nm, greater than or equal to 1300 nm and less than or equal to 1500 nm, greater than or equal to 1320 nm and less than or equal to 1480 nm, greater than or equal to 1340 nm and less than or equal to 1460 nm, greater than or equal to 1360 nm and less than or equal to 1440 nm, greater than or equal to 1380 nm and less than or equal to 1420 nm, greater than or equal to 1390 nm and less than or equal to 1400 nm, greater than or equal to 1300 and less than or equal to 1500 nm, or even greater than or equal to 1320 and less than or equal to 1480 nm. It should be understood that the cable cutoff of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for cable cutoff and any one of the upper bounds of cable cutoff described herein.

The average 15 mm bend loss of the coupled-core multicore optical fiber is determined by measuring the 15 mm bend loss for each core of the coupled-core multicore optical fiber at a wavelength of 1510 nm and then calculating an average 15 mm bend loss for the entire coupled-core multicore optical fiber based on the individual 15 mm bend loss measurements of each core. In various embodiments, the average bend loss of the coupled-core multicore optical fiber 110 measured at a wavelength of 1550 nm using a mandrel with a 15 mm diameter (“1 × 15 mm diameter bend loss”) is greater than or equal to 0.1 dB/turn and less than or equal to 10 dB/turn. For example, the 1 × 15 mm diameter bend loss at 15 mm is less than or equal to 5 dB/turn, less than or equal to 4 dB/turn, less than or equal to 3 dB/turn, less than or equal to 2 dB/turn, or even less than or equal to 1 dB/turn.

The average 20 mm bend loss of the coupled-core multicore optical fiber is determined by measuring the 20 mm bend loss for each core of the coupled-core multicore optical fiber at a wavelength of 1510 nm and then calculating an average 20 mm bend loss for the entire coupled-core multicore optical fiber based on the individual 20 mm bend loss measurements of each core. In various embodiments, the average bend loss of the coupled-core multicore optical fiber 110 at a wavelength of 1550 nm using a mandrel with a 20 mm diameter (“1 × 20 bend loss”) is greater than or equal to 0.01 dB/turn and less than or equal to 1 dB/turn. For example, the 1 x 20 bend loss is less than or equal to 0.8 dB/turn, less than or equal to 0.6 dB/turn, less than or equal to 0.5 dB/turn, less than or equal to 0.4 dB/turn, less than or equal to 0.3 dB/turn, or even less than or equal to 0.2 dB/turn.

The average 30 mm bend loss of the coupled-core multicore optical fiber is determined by measuring the 30 mm bend loss for each core of the coupled-core multicore optical fiber at a wavelength of 1510 nm and then calculating an average 30 mm bend loss for the entire coupled-core multicore optical fiber based on the individual 30 mm bend loss measurements of each core. In various embodiments, the average bend loss at 1550 nm of the coupled-core multicore optical fiber 110 at a wavelength of 1550 nm using a mandrel with a 30 mm diameter (“1 × 30 bend loss”) is greater than or equal to 0.001 dB/turn and less than or equal to 0.03 dB/turn. For example, the 1 × 30 bend loss is greater than or equal to 0.001 dB/turn and less than or equal to 0.025 dB/turn or even greater than or equal to 0.001 dB/turn and less than or equal to 0.02 dB/turn. It should be understood that the 1 × 30 bend loss mm of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for 1 × 30 bend loss and any one of the upper bounds of 1 × 30 bend loss described herein.

In various embodiments, the zero-dispersion wavelength of each core of the coupled-core multicore optical fiber 110 is greater than or equal to 1200 nm and less than or equal to 1350 nm. For example, the zero-dispersion wavelength of each core of the coupled-core multicore optical fiber 110 may be greater than or equal to 1225 nm and less than or equal to 1325 nm or even greater than or equal to 1250 nm and less than or equal to 1300 nm. It should be understood that the zero-dispersion wavelength of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for zero-dispersion wavelength and any one of the upper bounds of zero-dispersion wavelength described herein.

In various embodiments, dispersion at 1310 nm of each core of the coupled-core multicore optical fiber 110 is greater than or equal to 0.2 ps/nm/km and less than or equal to 3.5 ps/nm/km. For example, the dispersion at 1310 of each core of the coupled-core multicore optical fiber 110 may be greater than or equal to 0.5 ps/nm/km and less than or equal to 3 ps/nm/km, greater than or equal to 1 ps/nm/km and less than or equal to 2.5 ps/nm/km, or even greater than or equal to 1.5 ps/nm/km and less than or equal to 2 ps/nm/km. It should be understood that the dispersion at 1310 nm of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for dispersion at 1310 nm and any one of the upper bounds of dispersion at 1310 nm described herein.

In various embodiments, the dispersion slope at 1310 nm of each core of the coupled-core multicore optical fiber 110 is greater than or equal to 0.08 ps/nm²/km and less than or equal to 0.095 ps/nm²/km. For example, the dispersion slope at 1310 nm of each core of the coupled-core multicore optical fiber 110 may be greater than or equal to 0.081 ps/nm²/km and less than or equal to 0.094 ps/nm²/km, greater than or equal to 0.082 ps/nm²/km and less than or equal to 0.093 ps/nm²/km, greater than or equal to 0.083 ps/nm²/km and less than or equal to 0.092 ps/nm²/km, greater than or equal to 0.084 ps/nm²/km and less than or equal to 0.091 ps/nm²/km, greater than or equal to 0.085 ps/nm²/km and less than or equal to 0.09 ps/nm²/km, greater than or equal to 0.086 ps/nm²/km and less than or equal to 0.089 ps/nm²/km, or even greater than or equal to 0.087 ps/nm²/km and less than or equal to 0.088 ps/nm²/km. It should be understood that the dispersion slope at 1310 nm of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for dispersion slope at 1310 nm and any one of the upper bounds of dispersion slope at 1310 nm described herein.

In various embodiments, dispersion at 1550 nm of each core of the coupled-core multicore optical fiber 110 is greater than or equal to 15 ps/nm/km and less than or equal to 25 ps/nm/km. For example, dispersion at 1550 of each core of the coupled-core multicore optical fiber 110 may be greater than or equal to 16 ps/nm/km and less than or equal to 24 ps/nm/km, greater than or equal to 17 ps/nm/km and less than or equal to 23 ps/nm/km, greater than or equal to 18 ps/nm/km and less than or equal to 22 ps/nm/km, or even greater than or equal to 19 ps/nm/km and less than or equal to 21 ps/nm/km. It should be understood that the dispersion at 1550 nm of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for dispersion at 1550 nm and any one of the upper bounds of dispersion at 1550 nm described herein.

In various embodiments, the dispersion slope at 1550 nm of each core of the coupled-core multicore optical fiber 110 is greater than or equal to 0.05 ps/nm²/km and less than or equal to 0.065 ps/nm²/km. For example, the dispersion slope at 1550 nm of each core of the coupled-core multicore optical fiber 110 may be greater than or equal to 0.051 ps/nm²/km and less than or equal to 0.064 ps/nm²/km, greater than or equal to 0.052 ps/nm²/km and less than or equal to 0.063 ps/nm²/km, greater than or equal to 0.053 ps/nm²/km and less than or equal to 0.062 ps/nm²/km, greater than or equal to 0.054 ps/nm²/km and less than or equal to 0.061 ps/nm²/km, greater than or equal to 0.055 ps/nm²/km and less than or equal to 0.06 ps/nm²/km, greater than or equal to 0.056 ps/nm²/km and less than or equal to 0.059 ps/nm²/km, or even greater than or equal to 0.057 ps/nm²/km and less than or equal to 0.058 ps/nm²/km. It should be understood that the dispersion slope at 1550 nm of each core of the coupled-core multicore optical fiber 110 may be within a range formed from any one of the lower bounds for dispersion slope at 1550 nm and any one of the upper bounds of dispersion slope at 1550 nm described herein.

The coupled-core multicore optical fiber 110 of the present disclosure can be made using any suitable method for forming a multicore optical fiber. See, for example, U.S. Pat. No. 9,120,693 and U.S. Published Pat. Application No. 20150284286, the disclosures of which are incorporated herein by reference in their entirety. For example, the coupled-core multicore optical fiber 110 can be formed by drawing a multicore preform made using conventional optical-fiber techniques, such as glass drilling or stacking. The glass drilling method can be used to form a multicore preform by drilling holes in a silica glass cylinder (pure, undoped silica or doped silica). The locations and dimensions of the holes are based on the multicore optical fiber design. Core canes having the desired refractive index profile and a diameter that is slightly smaller than the pre-drilled holes are then inserted into the pre-drilled holes to form the multicore preform. The multicore preform is then heated to a temperature sufficient to melt the silica glass forming the pre-drilled holes such that the pre-drilled holes collapse around the core canes. The multicore preform is then drawn into a fiber. The core canes can be made using any suitable conventional preform manufacturing technique, such as outside vapor deposition (OVD), modified chemical vapor deposition (MCVD), or plasma activated chemical vapor deposition (PCVD).

Suitable precursors for silica include SiCl₄ and organosilicon compounds. Organosilicon compounds are silicon compounds that include carbon, and optionally oxygen and/or hydrogen. Examples of suitable organosilicon compounds include octamethylcyclotetrasiloxane (OMCTS), silicon alkoxides (Si(OR)₄), organosilanes (SiR₄), and Si(OR)_xR_4-x, where R is a carbon-containing organic group or hydrogen and where R may be the same or different at each occurrence, and wherein at least one R is a carbon-containing organic group. Suitable precursors for chlorine doping include Cl₂, SiCl₄, Si₂Cl₆, Si₂OCl₆, SiCl₃H, and CCl₄. Suitable precursors for fluorine doping include F₂, CF₄, and SiF₄. Regions of constant refractive index may be formed by not doping or by doping at a uniform concentration over the thickness of the region. Regions of variable refractive index are formed through non-uniform spatial distributions of dopants over the thickness of a region and/or through incorporation of different dopants in different regions. The OVD, MCVD, PCVD and other techniques for generating silica soot permit fine control of dopant concentration through layer-by-layer deposition with variable flow rate delivery of dopant precursors.

One exemplary method that can be used to form the multicore optical fibers of the present disclosure is a method that utilizes a cane-based optical fiber preform and then draws the optical fiber from the cane-based glass preform. An exemplary cane-based glass preform method is disclosed in Applicant’s co-pending U.S. Pat. Application Serial No. 62/811,842 (Attorney Docket No. SP19-067PZ), entitled “Vacuum-Based Methods of Forming a Cane-Based Optical Fiber Preform and Methods of Forming an Optical Fiber Using Same,” which was filed on Feb. 28, 2019, the contents of which are incorporated herein by reference in their entirety.

Briefly, a cane-based glass preform method for forming the multicore optical fibers 10 can include utilizing one or more glass cladding sections each having one or more precision axial holes formed therein and a top end with a recess defined by a perimeter lip. When using multiple glass cladding sections, the sections can be stacked so that the axial holes are aligned. A core cane can then be added to each axial hole to define a cane-cladding assembly. Top and bottom caps, respectively, can be added to the top and bottom of the cane-cladding assembly to define a preform assembly. The top cap closes off the recess at the top of the glass-cladding section. The bottom cap can have its own raised lip and recess that becomes closed off when the bottom cap is interfaced with the bottom end of the cane-cladding assembly. The closed-off recesses and gaps formed by the canes within the axial holes define a substantially sealed internal chamber. The preform assembly can then be dried and purified by drawing a select cleaning gas (e.g., chlorine) through a small passage in the bottom cap that leads to the internal chamber. A vacuum can be applied through the top cap to create a pressure differential between the internal chamber and the ambient environment. The pressure differential facilitates maintaining the components of the preform assembly together, and can be referred to as a vacuum-held preform assembly. The vacuum-held preform assembly can then be consolidated by heating in a furnace to just above the glass softening temperature so that the glass cladding section(s), the core canes, and the top and bottom caps, which are all made of glass, seal to one another. In addition, the glass flow can remove the internal chamber. The result is a solid glass preform that is ready to be drawn, especially if the furnace used for the consolidation is a draw furnace used for drawing optical fiber.

Additionally, if an outer common cladding is to be included, the material that will become the outer common cladding may be added to the outer surface of the preform containing the cores. For instance, soot may be applied to the preform via organic vapor deposition and then consolidated with the desired dopant. After the cores, inner common cladding material, and outer common cladding material are assembled as above, the coupled-core multicore optical fibers may then be drawn to the desired fiber diameter, as described above.

The coupled-core multicore optical fibers described herein will now be further described with reference to the following examples.

EXAMPLES

Fabrication of Coupled-core Multicore Optical Fibers

The coupled-core multicore optical fiber shown in FIG. 2 was fabricated as follows. A core cane was drawn to an outer diameter of 5 mm and a length of 120 mm. In general, the core cane was composed of potassium-doped silica in which the potassium concentration was from 150 ppm to 250 ppm. The core cane was cut into four sections having a length of 30 cm. Separately, an inner common cladding preform with a target outer diameter of 28 mm was fabricated and doped with 1.11 wt.% fluorine during consolidation such that the refractive index delta (i.e., Δ_ICC%) was -0.34% relative to pure silica. Four 5 mm holes were drilled into the fluorine-doped preform. The centers of the holes were symmetrically located 5.9 mm away from the central axis of the preform. The core cane sections were inserted into the holes drilled into the inner common cladding preform, and a 35 mm lead and tail section of a dummy preform were added to create a 1 m preform with an outer diameter of 28 mm. Soot was applied to the inner common cladding preform via outside vapor deposition, and doped with 0.95 wt.% fluorine during consolidation to create a fluorine-doped outer common cladding with an outer diameter of 53 mm and a relative refractive index delta of -0.29% relative to pure silica around the inner cladding preform. Optical fiber was then drawn from the preform with a cladding diameter of 125 µm. The diameters of the cores and common inner cladding in the drawn fiber had the same 125 µm/53 mm scaling ratio and are 11.8 µm and 66 µm, respectively.

Characterization of Exemplary Coupled-core Multicore Optical Fibers

Six coupled-core multicore optical fibers were fabricated as detailed above in a 2 × 2 core (“four core”) arrangement as depicted in FIG. 5A. The four cores were symmetrically disposed about the central fiber axis 12. These example coupled-core multicore optical fibers were characterized by obtaining their refractive index profiles to obtain Δ_CLI, Δ_CI, Δ_ICC, and Δ_OCC, all in %, as well as r_CL1, r_C1, and R_ICC, all in µm. The results are presented in Table 1. The geometric parameters, including overall fiber diameter in µm, and the core-to-core distance (“core pitch”) in µm were also determined. Physical characteristics, including the effective area (A_eff) of the cores in µm², the average attenuation in dB/km, the cable cutoff in nm of each core, average 1 × 15 mm diameter bend loss at 1550 nm in dB/turn, average 1×20 mm diameter bend loss at 1550 nm in dB/turn, average 1×30 mm diameter bend loss at 1550 nm in dB/turn, zero-dispersion wavelength in nm of each core, the dispersion at 1310 nm in ps/nm/km of each core, dispersion slope at 1310 nm in ps/nm²/km of each core, the dispersion at 1550 nm in ps/nm/km of each core, and the dispersion slope at 1550 nm in ps/nm²/km of each core, were also determined. Additionally, the concentration of fluorine in the respective claddings in wt.% was determined. The characterization data are tabulated in Table 1. The refractive index profile of Example 1 prior to being drawn and scaled to the dimensions anticipated in the optical fiber is shown in FIG. 8. The refractive index profile of Example 2 after being drawn is shown in FIG. 9. The refractive index profile of Example 3 after being drawn is shown in FIG. 10. The refractive index profile of Example 4 prior to being drawn and scaled to the dimensions anticipated in the optical fiber is shown in FIG. 11. The refractive index profile of Example 5 prior to being drawn is shown in FIG. 12. The refractive index profile of Example 6 prior to being drawn and scaled to the dimensions anticipated in the optical fiber is shown in FIG. 13. The radii and percent delta values of the index profiles shown in FIGS. 8-13 are labeled similarly to those of FIG. 7A.

Example	1	2	3	4	5	6
ΔCL1 (%)	0.114	0	0	0.114	0.085	0.134
rCL1 (µm)	1.15	2.22	2.22	1.409	2.13	2.69
ΔC1 (%)	-0.068	-0.039	-0.039	-0.071	-0.071	-0.073
rC1 (µm)	4.41	6.845	8.14	5.752	6.12	7.27
ΔICC(%)
RICCX (µm)	15.5	17.57	19.43	21.26	22.64	26.57
ΔOCC (%)	-0.44	-0.273	-0.253	-0.308	-0.305	-0.287
F wt % core and inner cladding portions	1.47	1.04	0.83	1.18	-1.06	1.08
Max F wt% inner common cladding portion	1.63	1.24	1.01	1.18	1.06	1.08
F wt% in outer common cladding	1.47	0.91	0.84	1.03	1.02	0.96
Fiber Diameter ROCC (µm)	125	125	125	125	125	125
Core-to-core minimum distance (core pitch) (µm)	31	35.14	38.84	42.51	45.28	53.14
Core-to-core maximum distance (core pitch between diagonally adjacent cores) (µm)	63.63	63.63	63.63	63.63	63.63	63.63
Aeff at 1550 nm (µm2) of each core	73.54	115	150	111	122.8	136
Average Attenuation at 1550 nm (dB/km)	0.165	0.165	0.165	0.165	0.165	0.165
Cable cutoff (nm) of each core	1219	1393	1528	1353	1364	1528
Average 1×15 mm diameter bend loss (dB/turn)	0.529	1.23	1.38	1.9	3.84	0.859
Average 1×20 mm diameter bend loss (dB/turn)	0.103	0.306	0.308	0.46	0.923	0.202
Average 1×30 mm diameter bend loss (dB/turn)	0.0017	0.018	0.008	0.02	0.029	0.01
Zero-dispersion wavelength (nm) of each core	1313	1285	1284	1290	1291	1285
Dispersion at 1310 nm (ps/nm/km) of each core	0.388	3	3.07	2.5	2.4	3
Dispersion slope at 1310 nm (ps/nm2/km) of each core	0.0867	0.09	0.091	0.088	0.0889	0.092
Dispersion at 1550 nm (ps/nm/km) of each core	17.17	20.66	21.03	19.97	19.96	20.94
Dispersion slope at 1550 nm (ps/nm2/km) of each core	0.058	0.06	0.062	0.06	0.061	0.063

Examples 1, 3, 5, 6 were also examined to determine the coupling coefficient and the crosstalk between adjacent cores in dB with various core-to-core spacing. The coupling coefficients were determined by calculating the overlap integral between the electric fields of the LP01 modes in two neighboring cores. The crosstalk was calculated based on Equation (7). The results are summarized in Table 2 (coupling coefficients) and Table 3 (crosstalk). From the two tables, it is possible to choose the core spacing for a profile design to achieve a desired coupling coefficient and crosstalk. For coupled core multicore optical fibers, the core spacing can provide a coupling coefficient greater than or equal to 3.4 × 10^-4 /m, greater than or equal to 1.1 × 10^-3 /m, or even greater than or equal to 2.5 × 10^-3 /m. The crosstalk is greater than or equal to -20 dB, greater than or equal to -10 dB, or even equal to 0 dB.

	Coupling coefficients (per meter)
Core spacing (µm)	Example 1	Example 3	Example 5	Example 6
15	158.7685	509.718	333.266	380.7536
20	24.62562	101.1711	71.81051	77.00593
25	3.819529	20.08087	15.47338	15.57415
30	0.592424	3.985739	3.334127	3.149811
35	0.091887	0.791107	0.718421	0.637037
40	0.014252	0.157022	0.154802	0.128838
45	0.002211	0.031166	0.033356	0.026057
50	0.000343	0.006186	0.007187	0.00527
55	5.32E-05	0.001228	0.001549	0.001066
60	8.25E-06	0.000244	0.000334	0.000216

	Crosstalk (dB)
Core spacing (µm) =	Example 1	Example 3	Example 5	Example 6
15	0	0	0	0
20	0	0	0	0
25	0	0	0	0
30	0	0	0	0
35	-10.7	0	0	0
40	-26.9	-6.1	-6.2	-7.8
45	-43.1	-20.1	-19.5	-21.7
50	-59.3	-34.2	-32.9	-35.6
55	-75.5	-48.2	-46.2	-49.4
60	-91.7	-62.3	-59.5	-63.3

As shown in Examples 2-6, the optical fibers described herein are capable of achieving an effective area A_eff for each core of greater than 100 µm² at 1550 nm. And in some instances, the A_eff of each core may be much greater, such as with Example 3, which has an A_eff for each core of 150 µm². However, the average attenuation remained relatively low in all the examples, i.e., 0.165 dB/km. The attenuation would be expected to be higher if there were significant levels of crosstalk present, but this undesirable phenomenon is suppressed through optimization of the refractive indices and dimensions of the cores and claddings and the spacing between the cores.

It will be apparent to those skilled in the art that various modifications and variations can be made to the embodiments described herein without departing from the spirit and scope of the claimed subject matter. Thus it is intended that the specification cover the modifications and variations of the various embodiments described herein provided such modification and variations come within the scope of the appended claims and their equivalents.

Claims

1. A coupled-core multicore optical fiber comprising: an outer common cladding comprising a relative refractive index ΔOCC relative to pure silica; anda plurality of cores disposed in the outer common cladding, each of the plurality of cores comprising an inner core portion comprising a relative refractive index ACi relative to pure silica and a maximum relative refractive index ΔCLi relative to pure silica; wherein: ΔCLi > ΔCi > ΔICC;each of the inner core portions comprises greater than or equal to 0.02 wt.% and less than or equal to 0.15 wt.% fluorine;a distance between centers of an adjacent two of the plurality of cores is greater than or equal to 20 micrometers (µm) and less than or equal to 40 µm; anda coupling coefficient κ between adjacent cores in the plurality of cores is greater than or equal to 1 × 10-3 /m.

2. The coupled-core multicore optical fiber of claim 1, wherein a distance between centers of an adjacent two of the plurality of cores is greater than or equal to 45 µm and less than or equal to 65 µm.

3. The coupled-core multicore optical fiber of claim 1, wherein a crosstalk between the plurality of cores is greater than or equal to -50 decibels (dB) per kilometer.

4. The coupled-core multicore optical fiber of claim 1, comprising greater than or equal to 2 and less than or equal to 6 of the cores.

5. The coupled-core multicore optical fiber of claim 1, comprising 3 sets of 3 of the cores.

6. The coupled-core multicore optical fiber of claim 1, wherein a cable cutoff wavelength of each of the plurality of cores of the optical fiber is greater than or equal to 1200 nanometers (nm) and less than or equal to 1520 nm.

7. The coupled-core multicore optical fiber of claim 1, wherein an average bend loss of the plurality of cores of the optical fiber at a wavelength of 1550 nm measured on a mandrel having a diameter of 20 millimeters (mm) is greater than or equal to 0.01 decibels per turn (dB/turn) and less than or equal to 1 dB/turn.

8. The coupled-core multicore optical fiber of claim 1, wherein an average bend loss of the plurality of cores of the optical fiber at a wavelength of 1550 nm measured on a mandrel having a diameter of 30 mm is greater than or equal to 0.001 decibels per turn (dB/turn) and less than or equal to 0.03 dB/turn.

9. The coupled-core multicore optical fiber of claim 1, wherein a minimum distance between a center of one of the plurality of cores to an adjacent edge of the optical fiber along a line formed by a centerpoint of the optical fiber, the center of the one of the plurality of cores, and the adjacent edge in a plane perpendicular to a long axis of the coupled-core multicore optical fiber is greater than or equal to 30 µm and less than or equal to 50 µm.

10. The coupled-core multicore optical fiber of claim 1, wherein each of the plurality of cores comprises an inner cladding portion and an inner core portion corresponding to the inner cladding portion, each inner cladding portion surrounding the corresponding inner core portion.

11. The coupled-core multicore optical fiber of claim 10, wherein each inner cladding portion comprises a relative refractive index ΔICi, the inner core portion comprises the ΔCLi, and ΔCLi > ΔCi > ΔICi > ΔOCC.