Electrical energy storage cells are widely used to provide power to electronic, electromechanical, electrochemical, and other useful devices. An electric double layer ultracapacitor, for instance, generally employs a pair of polarizable electrodes that contain carbon particles (e.g., activated carbon) impregnated with a liquid electrolyte. Due to the effective surface area of the particles and the small spacing between the electrodes, large capacitance values may be achieved. Nevertheless, problems remain. For instance, it is often desirable to attach capacitors to a circuit board using a “solder reflow” process during which a solder paste is used to temporarily attach the capacitor and then heated to a relatively high peak temperature (e.g., about 150° C. or more) to melt the solder paste and connect the capacitor to the board. Unfortunately, however, most conventional ultracapacitors are highly sensitive to temperature and thus cannot be readily employed in solder reflow processes.
As such, a need currently exists for an improved ultracapacitor that can operate at high temperatures and still maintain stable electrical properties.
In accordance with one embodiment of the present invention, an ultracapacitor is disclosed that comprises a housing having sidewalls extending in a direction generally perpendicular to a base to define an upper end. An interior cavity is defined between an inner surface of the base and the sidewalls. First and second conductive members are disposed on the inner surface of the base, and first and second external terminations are disposed on an outer surface of the base and electrically connected to the first and second conductive members, respectively. An electrode assembly is positioned within the interior cavity that contains first and second leads extending outwardly therefrom. The first and second leads are electrically connected to the first and second conductive members, respectively. A nonaqueous electrolyte is in ionic contact with the electrode assembly, and a lid is disposed on the upper end of the sidewalls to seal the electrode assembly and the electrolyte within the housing.
Other features and aspects of the present invention are set forth in greater detail below.
A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art, is set forth more particularly in the remainder of the specification, which makes reference to the appended figure in which:
Repeat use of reference characters in the present specification and drawing is intended to represent same or analogous features or elements of the invention.
It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention, which broader aspects are embodied in the exemplary construction.
Generally speaking, the present invention is directed an ultracapacitor that is capable of exhibiting good properties even after being subjected to high temperatures, such as experienced during solder reflow. The ultracapacitor contains a housing having sidewalls that extend in a direction generally perpendicular to a base. An interior cavity is defined between an inner surface of the base and the sidewalls within which an electrode assembly can be positioned. The ultracapacitor also contains a lid that is disposed on an upper end of the sidewalls to seal the electrode assembly within the housing. To attach the electrode assembly to the housing, first and second conductive members are disposed on the inner surface of the base. The electrode assembly likewise contains first and second leads that extend outwardly therefrom and are electrically connected to the first and second conductive members, respectively. The first and second conductive members are, in turn, electrically connected to first and second external terminations, respectively, which are provided on an outer surface of the base. By selectively controlling the manner in which the electrode assembly is attached and retained within the housing, the present inventors have discovered that a variety of beneficial properties may be achieved. That is, the resulting ultracapacitor may exhibit excellent electrical properties even when exposed to high temperatures, such as about 150° C. or more, in some embodiments about 200° C. or more, and in some embodiments, from about 200° C. to about 350° C. For example, the ultracapacitor may be subjected to a “solder reflow” process in which it is placed into contact with a solder paste and then heated to a peak temperature of from about 150° C. or more, in some embodiments about 200° C. or more, and in some embodiments, from about 200° C. to about 350° C. to melt the paste and connect the ultracapacitor to a circuit board (e.g., printed circuit board).
Even after being exposed to such a high temperature, the ultracapacitor may remain dimensionally stable and may also retain good electrical properties. For example, the capacitor may be about 6 Farads per cubic centimeter (“F/cm3”) or more, in some embodiments about 8 F/cm3 or more, in some embodiments from about 9 to about 100 F/cm3, and in some embodiments, from about 10 to about 80 F/cm3, measured at a frequency of 120 Hz and without an applied voltage. The capacitance may be measured using a Keithley 3330 Precision LCZ meter with a DC bias of 0.0 volts, 1.1 volts, or 2.1 volts (0.5 volt peak to peak sinusoidal signal). The operating frequency is 120 Hz. A variety of temperature and relative humidity levels may be tested. For example, the temperature may be 200° C. and the relative humidity may be 25% or 85%. The capacitance can remain stable at such temperatures for a substantial period of time, such as for about 100 hours or more, in some embodiments from about 300 hours to about 5000 hours, and in some embodiments, from about 600 hours to about 4500 hours (e.g., 168, 336, 504, 672, 840, 1008, 1512, 2040, 3024, or 4032 hours). The ultracapacitor may also have a low equivalence series resistance (“ESR”), such as about 150 mohms or less, in some embodiments less than about 125 mohms, in some embodiments from about 0.01 to about 100 mohms, and in some embodiments, from about 0.05 to about 70 mohms, determined at a frequency of 1 kHz and without an applied voltage. The ESR can also remain stable at such temperatures for a substantial period of time, such as noted above. Equivalence series resistance may be measured using a Keithley 3330 Precision LCZ meter with a DC bias of 0.0 volts, 1.1 volts, or 2.1 volts (0.5 volt peak to peak sinusoidal signal). The operating frequency is 1 kHz. A variety of temperature and relative humidity levels may be tested. For example, the temperature may be 200° C. and the relative humidity may be 25% or 85%.
Various embodiments of the present invention will now be described in more detail.
As indicated above, the ultracapacitor of the present invention employs a housing within which an electrode assembly is retained and sealed. Referring to
As indicated above, first and second conductive members are also employed within the interior cavity of the housing to facilitate the connection of the electrode assembly in a mechanically stable manner. For example, referring again to
As shown in
In any event, attachment of the electrode assembly 60 to the conductive members may generally be accomplished using any of a variety of known techniques, such as welding, laser welding, conductive adhesives, etc. In one particular embodiment, for example, the leads 62 and 64 are connected to the conductive members 42 and 44, respectively, with a conductive adhesive. The conductive adhesive may be formed from conductive metal particles contained with a resin composition. The metal particles may be silver, copper, gold, platinum, nickel, zinc, bismuth, etc. The resin composition may include a thermoset resin (e.g., epoxy resin), curing agent (e.g., acid anhydride), and coupling agent (e.g., silane coupling agents). Suitable conductive adhesives are described in U.S. Patent Application Publication No. 2006/0038304 to Osako, et al.
The first and second conductive members 42 and 44 are electrically connected to first and second external terminations 52 and 54 (
Regardless of the manner in which they are formed, the first and second external terminations 52 and 54 are electrically connected to the first and second conductive members 42 and 44, respectively, to provide the desired connection with the electrode assembly. In one embodiment, for instance, the conductive members 42 and 44 may simply extend through the base 37 to form the external terminations 52 and 54. Alternatively, a separate conductive trace (not shown) may be attached to the first conductive member 42 that extends through the base 37 and either forms the first external termination 52 or is connected to an additional conductive member that serves as the external termination 52. Similarly, the second conductive member 44 may extend through the base 37 to form the external termination 54, or a separate conductive trace (not shown) may be attached to the second conductive member 44 that extends through the base 37 and either forms the termination 54 or is connected to an additional conductive member that serves as the termination 54. When traces are employed, a via (not shown) may be formed within the base 37 to accommodate the trace.
The manner in which they conductive members and external terminations are electrically connected may vary as is known in the art. In certain embodiments, for example, welding techniques may be employed, such as ultrasonic welding, laser welding, resistance welding, etc. In yet other embodiments, a conductive adhesive may be employed to connect the conductive members to respective terminations.
When employed, the conductive adhesive typically contains a plurality of particles that are formed from an electrically conductive material (e.g., metal). Examples of suitable conductive materials include, for instance, metals, such as nickel, copper, gold, silver, silver coated copper, silver coated nickel, etc., carbon materials, such as graphite, nickel coated carbon, etc.; and so forth. The conductive adhesive also generally contains a resinous material within which the conductive particles are dispersed. Although any resinous material may be employed, it is generally desired to use a resin that is a curable thermosetting resin, such as an epoxy resin, melamine resin, maleimide resin, polyimide resin, phenolic resin, etc. Epoxy resins are particularly suitable. Examples of suitable epoxy resins include, for instance, glycidyl ether type epoxy resins, such as bisphenol A type epoxy resins, bisphenol F type epoxy resins, phenol novolac type epoxy resins, orthocresol novolac type epoxy resins, brominated epoxy resins and biphenyl type epoxy resins, cyclic aliphatic epoxy resins, glycidyl ester type epoxy resins, glycidylamine type epoxy resins, cresol novolac type epoxy resins, naphthalene type epoxy resins, phenol aralkyl type epoxy resins, cyclopentadiene type epoxy resins, heterocyclic epoxy resins, etc. Still other suitable conductive adhesive resins may also be described in U.S. Patent Application Publication No. 2006/0038304 to Osako, et al. and U.S. Pat. No. 7,554,793 to Chacko. Typically, the resinous material constitutes from about 0.5 wt. % to about 50 wt. %, in some embodiments from about 1 wt. % to about 25 wt. %, and in some embodiments, from about 2 wt. % to about 20 wt. % of the dry weight of the adhesive. Likewise, the conductive particles typically constitute from about 50 wt. % to about 99.5 wt. %, in some embodiments from about 75 wt. % to about 99 wt. %, and in some embodiments, from about 80 wt. % to about 98 wt. % of the adhesive, on a dry basis. The adhesive may be applied using known techniques, such as screen-printing, dipping, electrophoretic coating, electron beam deposition, spraying, roller pressing, brushing, doctor blade casting, vacuum deposition, coating, etc. Regardless, once applied, the conductive adhesive may be cured as using any of a variety of known techniques, such as heat curing, actinic radiation curing (e.g., ultraviolet radiation, e-beam radiation, infrared radiation, etc.), and so forth.
Once connected in the desired manner, the electrode assembly may then be sealed within the housing. Referring again to
As indicated above, the electrode assembly contains first and second leads that are electrically connected to first and second electrodes, respectively. The first electrode typically includes a first electrode containing a first carbonaceous coating (e.g., activated carbon particles) electrically coupled to a first current collector, and a second electrode containing a second carbonaceous coating (e.g., activated carbon particles) electrically coupled to a second current collector. A separator may also be positioned between the first electrode and the second electrode. Various embodiments of such an assembly are described in more detail below.
A. Electrodes
As indicated above, the first and second electrodes typically contain first and second current collectors, respectively. It should be understood that additional current collectors may also be employed if desired, particularly if the ultracapacitor includes multiple energy storage cells. The current collectors may be formed from the same or different materials. Regardless, each collector is typically formed from a substrate that includes a conductive metal, such as aluminum, stainless steel, nickel, silver, palladium, etc., as well as alloys thereof. Aluminum and aluminum alloys are particularly suitable for use in the present invention. The substrate may be in the form of a foil, sheet, plate, mesh, etc. The substrate may also have a relatively small thickness, such as about 200 micrometers or less, in some embodiments from about 1 to about 100 micrometers, in some embodiments from about 5 to about 80 micrometers, and in some embodiments, from about 10 to about 50 micrometers. Although by no means required, the surface of the substrate may be optionally roughened, such as by washing, etching, blasting, etc.
In certain embodiments, at least one of the first and second current collectors, and preferably both, also contain a plurality of fiber-like whiskers that project outwardly from the substrate. Without intending to be limited by theory, it is believed that these whiskers can effectively increase the surface area of the current collector and also improve the adhesion of the current collector to the corresponding electrode. This can allow for the use of a relatively low binder content in the first electrode and/or second electrode, which can improve charge transfer and reduce interfacial resistance and consequently result in very low ESR values. The whiskers are typically formed from a material that contains carbon and/or a reaction product of carbon and the conductive metal. In one embodiment, for example, the material may contain a carbide of the conductive metal, such as aluminum carbide (Al4C3). Referring to
The manner in which such whiskers are formed on the substrate may vary as desired. In one embodiment, for instance, the conductive metal of the substrate is reacted with a hydrocarbon compound. Examples of such hydrocarbon compounds may include, for instance, paraffin hydrocarbon compounds, such as methane, ethane, propane, n-butane, isobutane, pentane, etc.; olefin hydrocarbon compounds, such as ethylene, propylene, butene, butadiene, etc.; acetylene hydrocarbon compounds, such as acetylene; as well as derivatives or combinations of any of the foregoing. It is generally desired that the hydrocarbon compounds are in a gaseous form during the reaction. Thus, it may be desired to employ hydrocarbon compounds, such as methane, ethane, and propane, which are in a gaseous form when heated. Although not necessarily required, the hydrocarbon compounds are typically employed in a range of from about 0.1 parts to about 50 parts by weight, and in some embodiments, from about 0.5 parts by weight to about 30 parts by weight, based on 100 parts by weight of the substrate. To initiate the reaction with the hydrocarbon and conductive metal, the substrate is generally heated in an atmosphere that is at a temperature of about 300° C. or more, in some embodiments about 400° C. or more, and in some embodiments, from about 500° C. to about 650° C. The time of heating depends on the exact temperature selected, but typically ranges from about 1 hour to about 100 hours. The atmosphere typically contains a relatively low amount of oxygen to minimize the formation of a dielectric film on the surface of the substrate. For example, the oxygen content of the atmosphere may be about 1% by volume or less.
The ultracapacitor may also contain first and second carbonaceous coatings that are electrically coupled to the first and second current collectors, respectively. While they may be formed from the same or different types of materials and may contain one or multiple layers, each of the carbonaceous coatings generally contains at least one layer that includes activated particles. In certain embodiments, for instance, the activated carbon layer may be directly positioned over the current collector and may optionally be the only layer of the carbonaceous coating. Referring to
In certain embodiments, it may be desired to selectively control certain aspects of the activated carbon particles, such as their particle size distribution, surface area, and pore size distribution to help improve ion mobility for certain types of electrolytes after being subjected to one or more charge-discharge cycles. For example, at least 50% by volume of the particles (D50 size) may have a size in the range of from about 0.01 to about 30 micrometers, in some embodiments from about 0.1 to about 20 micrometers, and in some embodiments, from about 0.5 to about 10 micrometers. At least 90% by volume of the particles (D90 size) may likewise have a size in the range of from about 2 to about 40 micrometers, in some embodiments from about 5 to about 30 micrometers, and in some embodiments, from about 6 to about 15 micrometers. The BET surface may also range from about 900 m2/g to about 3,000 m2/g, in some embodiments from about 1,000 m2/g to about 2,500 m2/g, and in some embodiments, from about 1,100 m2/g to about 1,800 m2/g.
In addition to having a certain size and surface area, the activated carbon particles may also contain pores having a certain size distribution. For example, the amount of pores less than about 2 nanometers in size (i.e., “micropores”) may provide a pore volume of about 50 vol. % or less, in some embodiments about 30 vol. % or less, and in some embodiments, from 0.1 vol. % to 15 vol. % of the total pore volume. The amount of pores between about 2 nanometers and about 50 nanometers in size (i.e., “mesopores”) may likewise be from about 20 vol. % to about 80 vol. %, in some embodiments from about 25 vol. % to about 75 vol. %, and in some embodiments, from about 35 vol. % to about 65 vol. %. Finally, the amount of pores greater than about 50 nanometers in size (i.e., “macropores”) may be from about 1 vol. % to about 50 vol. %, in some embodiments from about 5 vol. % to about 40 vol. %, and in some embodiments, from about 10 vol. % to about 35 vol. %. The total pore volume of the carbon particles may be in the range of from about 0.2 cm3/g to about 1.5 cm3/g, and in some embodiments, from about 0.4 cm3/g to about 1.0 cm3/g, and the median pore width may be about 8 nanometers or less, in some embodiments from about 1 to about 5 nanometers, and in some embodiments, from about 2 to about 4 nanometers. The pore sizes and total pore volume may be measured using nitrogen adsorption and analyzed by the Barrett-Joyner-Halenda (“BJH”) technique as is well known in the art.
As discussed above, one unique aspect of the present invention is that the electrodes need not contain a substantial amount of binders conventionally employed in ultracapacitor electrodes. That is, binders may be present in an amount of about 60 parts or less, in some embodiments 40 parts or less, and in some embodiments, from about 1 to about 25 parts per 100 parts of carbon in the first and/or second carbonaceous coatings. Binders may, for example, constitute about 15 wt. % or less, in some embodiments about 10 wt. % or less, and in some embodiments, from about 0.5 wt. % to about 5 wt. % of the total weight of a carbonaceous coating. Nevertheless, when employed, any of a variety of suitable binders can be used in the electrodes. For instance, water-insoluble organic binders may be employed in certain embodiments, such as styrene-butadiene copolymers, polyvinyl acetate homopolymers, vinyl-acetate ethylene copolymers, vinyl-acetate acrylic copolymers, ethylene-vinyl chloride copolymers, ethylene-vinyl chloride-vinyl acetate terpolymers, acrylic polyvinyl chloride polymers, acrylic polymers, nitrile polymers, fluoropolymers such as polytetrafluoroethylene or polyvinylidene fluoride, polyolefins, etc., as well as mixtures thereof. Water-soluble organic binders may also be employed, such as polysaccharides and derivatives thereof. In one particular embodiment, the polysaccharide may be a nonionic cellulosic ether, such as alkyl cellulose ethers (e.g., methyl cellulose and ethyl cellulose); hydroxyalkyl cellulose ethers (e.g., hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropyl hydroxybutyl cellulose, hydroxyethyl hydroxypropyl cellulose, hydroxyethyl hydroxybutyl cellulose, hydroxyethyl hydroxypropyl hydroxybutyl cellulose, etc.); alkyl hydroxyalkyl cellulose ethers (e.g., methyl hydroxyethyl cellulose, methyl hydroxypropyl cellulose, ethyl hydroxyethyl cellulose, ethyl hydroxypropyl cellulose, methyl ethyl hydroxyethyl cellulose and methyl ethyl hydroxypropyl cellulose); carboxyalkyl cellulose ethers (e.g., carboxymethyl cellulose); and so forth, as well as protonated salts of any of the foregoing, such as sodium carboxymethyl cellulose.
If desired, other materials may also be employed within an activated carbon layer of the first and/or second carbonaceous coatings and/or within other layers of the first and/or second carbonaceous coatings. For example, in certain embodiments, a conductivity promoter may be employed to further increase electrical conductivity. Exemplary conductivity promoters may include, for instance, carbon black, graphite (natural or artificial), graphite, carbon nanotubes, nanowires or nanotubes, metal fibers, graphenes, etc., as well as mixtures thereof. Carbon black is particularly suitable. When employed, conductivity promoters typically constitute about 60 parts or less, in some embodiments 40 parts or less, and in some embodiments, from about 1 to about 25 parts per 100 parts of the activated carbon particles in a carbonaceous coating. Conductivity promotes may, for example, constitute about 15 wt. % or less, in some embodiments about 10 wt. % or less, and in some embodiments, from about 0.5 wt. % to about 5 wt. % of the total weight of a carbonaceous coating. Activated carbon particles likewise typically constitute 85 wt. % or more, in some embodiments about 90 wt. % or more, and in some embodiments, from about 95 wt. % to about 99.5 wt. % of a carbonaceous coating.
The particular manner in which a carbonaceous coating is applied to a current collector may vary as is well known to those skilled in the art, such as printing (e.g., rotogravure), spraying, slot-die coating, drop-coating, dip-coating, etc. Regardless of the manner in which it is applied, the resulting electrode is typically dried to remove moisture from the coating, such as at a temperature of about 100° C. or more, in some embodiments about 200° C. or more, and in some embodiments, from about 300° C. to about 500° C. The electrode may also be compressed (e.g., calendered) to optimize the volumetric efficiency of the ultracapacitor. After any optional compression, the thickness of each carbonaceous coating may generally vary based on the desired electrical performance and operating range of the ultracapacitor. Typically, however, the thickness of a coating is from about 20 to about 200 micrometers, 30 to about 150 micrometers, and in some embodiments, from about 40 to about 100 micrometers. Coatings may be present on one or both sides of a current collector. Regardless, the thickness of the overall electrode (including the current collector and the carbonaceous coating(s) after optional compression) is typically within a range of from about 20 to about 350 micrometers, in some embodiments from about 30 to about 300 micrometers, and in some embodiments, from about 50 to about 250 micrometers.
B. Separator
The electrode assembly may also contain a separator that is positioned between the first and second electrodes. If desired, other separators may also be employed in the ultracapacitor of the present invention. For example, one or more separators may be positioned over the first electrode, the second electrode, or both. The separators enable electrical isolation of one electrode from another to help prevent an electrical short, but still allow transport of ions between the two electrodes. In certain embodiments, for example, a separator may be employed that includes a cellulosic fibrous material (e.g., airlaid paper web, wet-laid paper web, etc.), nonwoven fibrous material (e.g., polyolefin nonwoven webs), woven fabrics, film (e.g., polyolefin film), etc. Cellulosic fibrous materials are particularly suitable for use in the ultracapacitor, such as those containing natural fibers, synthetic fibers, etc. Specific examples of suitable cellulosic fibers for use in the separator may include, for instance, hardwood pulp fibers, softwood pulp fibers, rayon fibers, regenerated cellulosic fibers, etc. Regardless of the particular materials employed, the separator typically has a thickness of from about 5 to about 150 micrometers, in some embodiments from about 10 to about 100 micrometers, and in some embodiments, from about 20 to about 80 micrometers.
The manner in which these components are assembled into an electrode assembly may vary as is known in the art. For example, the electrodes and separator may be initially folded, wound, or otherwise contacted together to form an electrode assembly. In one particular embodiment, the electrodes are separator may be folded into an electrode assembly having a “jelly-roll” configuration. Referring to
To form an electrochemical cell, the ultracapacitor of the present invention also contains an electrolyte that is ionic contact with the electrode assembly. The electrolyte may be placed into contact with the electrode assembly in a variety of ways as is known in the art. In certain embodiments, for instance, the electrolyte may be placed into contact (e.g., immersed, coated, etc.) with the electrode assembly prior to its incorporation into the housing. In addition to or in lieu of pre-contact with the electrode assembly, the electrolyte may also be supplied to the interior cavity of the housing after the electrode assembly is provided therein. Regardless, the application of the electrolyte typically occurs before the lid is attached to the upper end of the sidewalls as discussed above.
The electrolyte is generally nonaqueous in nature and thus typically contains at least one nonaqueous solvent. To help extend the operating temperature range of the ultracapacitor, it is typically desired that the nonaqueous solvent have a relatively high boiling temperature, such as about 150° C. or more, in some embodiments about 200° C. or more, and in some embodiments, from about 220° C. to about 300° C. Particularly suitable high boiling point solvents may include, for instance, cyclic carbonate solvents, such as ethylene carbonate, propylene carbonate, butylene carbonate, vinylene carbonate, etc. Propylene carbonate is particularly suitable due to its high electric conductivity and decomposition voltage, as well as its ability to be used over a wide range of temperatures. Of course, other nonaqueous solvents may also be employed, either alone or in combination with a cyclic carbonate solvent. Examples of such solvents may include, for instance, open-chain carbonates (e.g., dimethyl carbonate, ethyl methyl carbonate, diethyl carbonate, etc.), aliphatic monocarboxylates (e.g., methyl acetate, methyl propionate, etc.), lactone solvents (e.g., butyrolactone valerolactone, etc.), nitriles (e.g., acetonitrile, glutaronitrile, adiponitrile, methoxyacetonitrile, 3-methoxypropionitrile, etc.), amides (e.g., N,N-dimethylformamide, N,N-diethylacetamide, N-methylpyrrolidinone), alkanes (e.g., nitromethane, nitroethane, etc.), sulfur compounds (e.g., sulfolane, dimethyl sulfoxide, etc.); and so forth.
The electrolyte may also contain at least one ionic liquid, which is dissolved in the nonaqueous solvent. While the concentration of the ionic liquid can vary, it is typically desired that the ionic liquid is present at a relatively high concentration. For example, the ionic liquid may be present in an amount of about 0.8 moles per liter (M) of the electrolyte or more, in some embodiments about 1.0 M or more, in some embodiments about 1.2 M or more, and in some embodiments, from about 1.3 to about 1.8 M.
The ionic liquid is generally a salt having a relatively low melting temperature, such as about 400° C. or less, in some embodiments about 350° C. or less, in some embodiments from about 1° C. to about 100° C., and in some embodiments, from about 5° C. to about 50° C. The salt contains a cationic species and counterion. The cationic species contains a compound having at least one heteroatom (e.g., nitrogen or phosphorous) as a “cationic center.” Examples of such heteroatomic compounds include, for instance, unsubstituted or substituted organoquaternary ammonium compounds, such as ammonium (e.g., trimethylammonium, tetraethylammonium, etc.), pyridinium, pyridazinium, pyramidinium, pyrazinium, imidazolium, pyrazolium, oxazolium, triazolium, thiazolium, quinolinium, piperidinium, pyrrolidinium, quaternary ammonium spiro compounds in which two or more rings are connected together by a spiro atom (e.g., carbon, heteroatom, etc.), quaternary ammonium fused ring structures (e.g., quinolinium, isoquinolinium, etc.), and so forth. In one particular embodiment, for example, the cationic species may be an N-spirobicyclic compound, such as symmetrical or asymmetrical N-spirobicyclic compounds having cyclic rings. One example of such a compound has the following structure:
wherein m and n are independently a number from 3 to 7, and in some embodiments, from 4 to 5 (e.g., pyrrolidinium or piperidinium).
Suitable counterions for the cationic species may likewise include halogens (e.g., chloride, bromide, iodide, etc.); sulfates or sulfonates (e.g., methyl sulfate, ethyl sulfate, butyl sulfate, hexyl sulfate, octyl sulfate, hydrogen sulfate, methane sulfonate, dodecylbenzene sulfonate, dodecylsulfate, trifluoromethane sulfonate, heptadecafluorooctanesulfonate, sodium dodecylethoxysulfate, etc.); sulfosuccinates; amides (e.g., dicyanamide); imides (e.g., bis(pentafluoroethyl-sulfonyl)imide, bis(trifluoromethylsulfonyl)imide, bis(trifluoromethyl)imide, etc.); borates (e.g., tetrafluoroborate, tetracyanoborate, bis[oxalato]borate, bis[salicylato]borate, etc.); phosphates or phosphinates (e.g., hexafluorophosphate, diethylphosphate, bis(pentafluoroethyl)phosphinate, tris(pentafluoroethyl)-trifluorophosphate, tris(nonafluorobutyl)trifluorophosphate, etc.); antimonates (e.g., hexafluoroantimonate); aluminates (e.g., tetrachloroaluminate); fatty acid carboxylates (e.g., oleate, isostearate, pentadecafluorooctanoate, etc.); cyanates; acetates; and so forth, as well as combinations of any of the foregoing.
Several examples of suitable ionic liquids may include, for instance, spiro-(1,1′)-bipyrrolidinium tetrafluoroborate, triethylmethyl ammonium tetrafluoroborate, tetraethyl ammonium tetrafluoroborate, spiro-(1,1′)-bipyrrolidinium iodide, triethylmethyl ammonium iodide, tetraethyl ammonium iodide, methyltriethylammonium tetrafluoroborate, tetrabutylammonium tetrafluoroborate, tetraethylammonium hexafluorophosphate, etc.
These and other modifications and variations of the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.
The present application claims filing benefit of U.S. Provisional Patent Application Ser. No. 62/425,636 having a filing date of Nov. 23, 2016, and which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62425636 | Nov 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15810498 | Nov 2017 | US |
| Child | 18182441 | US |