Patent Grant
7498369
The invention is directed to ultrahigh molecular weight polyethylene (UHMWPE) articles and their manufacture.
UHMWPE is difficult to process because the resin does not flow when melted. Berins, M. L., ed., Plastics Engineering Handbook of the Society of the Plastic Industry, Chapman & Hall, New York City, N.Y. (1991), p. 52. Consequently, UHMWPE is processed by sintering, compression molding, ram extrusion, or gel processing. Sintering is a process where resins are agglomerated by solid-state diffusion. Heat and pressure are usually essential. Compression molding is a process where resins are shaped between the faces of a mold by heat and pressure. Ram extrusion is a process where resins are shaped by forcing it through a die. The force is provided by a ram. U.S. Pat. Nos. 5,234,652 and 5,399,308 disclose a dry extrusion process for a mixture consisting of resins and lubricant. Gel processing is a process where resins are formed into gels for subsequent processing. The gel is a dilute solution or suspension of resin in a solvent, e.g., an extractable solvent (or oil or plasticizer).
UHMWPE is gel spun into fibers. In gel spinning, the primary mechanism of solidification is the gelling of the polymer solution by cooling to form a gel filament consisting of precipitated polymer and solvent. Solvent removal is accomplished following solidification by washing in a liquid bath. This process is also used to form microporous films. See U.S. Pat. Nos. 4,588,633 and 5,248,461. In U.S. Pat. No. 4,588,633, the gel solution consists of 2-4% by weight of UHMWPE. See Examples 1-12. In U.S. Pat. No. 5,248,461, the gel solution consists of up to 20% by weight of UHMWPE. See Examples 1-20. These membranes are useful as, among other things, separators for electrochemical cells. See U.S. Pat. No. 4,588,633, column 4, lines 30-36 and U.S. Pat. No. 5,248,461, column 4, lines 57-60.
Another variant of gel processing is gel processing with a filler. For example, see U.S. Pat. Nos. 3,351,495, 4,833,172, and 5,948,557. Generally, UHMWPE, a processing oil (or plasticizer), and a filler are mixed in an extruder and subsequently made into microporous sheets. In U.S. Pat. No. 3,351,495, the solution consisted of up to 20% by volume of UHMWPE. See Examples 6, 8, 18, 19, 20, and 21. The microporous membranes formed were used as separators for batteries. See column 1, lines 24-33. In U.S. Pat. Nos. 4,833,172 and 5,948,557, a calcium/zinc stearate lubricant, PETRAC® CZ-81, is added to the solution. See Tables 1 and 2, respectively. The microporous membranes formed were used as labels, diffusion membranes, and separators. See U.S. Pat. No. 5,948,557, column 1, lines 27-41.
There is a need to improve the processability of UHMWPE.
An article of manufacture comprises an ultrahigh molecular weight polyethylene (UHMWPE) mixed with a processing oil and a lubricant selected from the group consisting of fatty acid esters, ethoxylated fatty acid esters, glycol esters, PEG esters, glycerol esters, ethoxylated esters, sorbitol esters, ethoxylated sorbitol esters, aromatic ethoxylates, alcohol ethoxylates, mercaptan ethoxylates, modified ethoxylates, amide surfactants, phosphate esters, phosphonate esters, phosphite esters, alkyl sulfates, fatty acid ethers, alkyl ether sulfates, alkylaryl ether sulfates, sulfonates, naphthalene sulfonates, sulfosuccinates, sulfonated esters, sulfonated amides, alkyl ether carboxylates, alkylaryl ether carboxylates, quaternary amines, amino quaternary amines, ethoxylated amines, imidazoline derivatives, betaines, sultaines, aminopropionates, catechol derivatives, saturated fatty acids, unsaturated fatty acids, and combinations thereof. The method for making those articles is also disclosed.
An article of manufacture is any shaped article. For example, articles of manufacture may include, but is not limited to, films, fibers, sheets, plates, slabs, bars, rods, billets, and blocks. Preferably, these articles are made by an extrusion process. These articles also may be microporous, for example, microporous sheets and films.
Ultrahigh molecular weight polyethylene (UHMWPE) is a polyethylene polymer having a weight average molecular weight greater than 5×105. The polymer is either a homopolymer of ethylene or a copolymer of ethylene, with at most 10 mol % of one or more alpha-olefins. The polymer may be a blend with UHMWPE comprising at least 50% by weight of the blend and the balance being other polymers, such as, for example, polyolefins and synthetic and natural rubbers. The preferred weight average molecular weight is greater than 2×106. The most preferred UHMWPE has a weight average molecular weight greater than 5×106. UHMWPE resins are commercially available as GUR from Ticona LLC of Summit, N.J., STAMYLAN from DSM of Geleen, Netherland, UTEC from Polyailden of Camacari, Brazil, and HI-ZEX Million, LUBMER, and MIPELON, each from Mitsui Chemical of Tokyo, Japan. GUR 4130 (molecular weight about 4-5 million) and GUR 4170 (molecular weight about 8-9 million) are preferred.
Processing oil (or processing plasticizer) have little solvating effect on the UHMWPE at lower temperatures (e.g. 60° C.), but have a significant solvating effect at elevated temperatures (e.g. 200°). Such oils include paraffinic oils, naphthalenic oils, and aromatic oils, as well as other materials including the phthalate ester plasticizers such as dibutyl phthalate, bis(2-ethylene)phthalate, diisodecyl phthalate, dicyclohexyl phthalate, butyl benzyl phthalate, and ditridecyl phthalate. Additional oils, plasticizers, and/or solvents are mentioned in U.S. Pat. Nos. 3,351,495; 4,588,633; 4,833,172; 5,248,461; and 5,948,557 are incorporated herein by reference.
The filler includes any particulate filler as is well known in the art. For example, see U.S. Pat. Nos. 3,351,495; 4,833,172; and 5,948,557 each is incorporated herein by reference. Preferably, the filler is a silica. Such fillers are commercially available under the tradename HiSil® from PPG Industries, Inc. of Pittsburgh, Pa., SIPERANT from Degussa AG of Wesseling, Germany, ZEOSIL from Rhodia, Inc. of Cranberry, N.J. or KETJENSIL from Akzo Chemie of Compiegne, France.
Minor amounts of auxiliary components may be added. Such auxiliary components include: carbon black, stabilizers, and antioxidants. The compounds are conventional and known in the art.
Lubricants are compounds that, when added to an UHMWPE mixture, improve the processability of the UHMWPE mixture. Improved processability refers to a reduction in fusion time (the time it takes the polymeric system to melt (or dissolve) into a flowable solution). Improved processability is also seen as a reduction in energy consumption by the motor and as a reduction in mixture temperature when comparing systems with and without the lubricants. The results arising from this phenomenon include, but are not limited to, decreasing energy consumption, decreased thermal and mechanical degradation of the polymer, increased polymer strength, decreased machine wear, and increased polymer throughputs.
Such lubricants are selected from the material classes consisting of: fatty acid esters, ethoxylated fatty acid esters, glycol esters, PEG esters, glycerol esters, ethoxylated esters, sorbitol esters, ethoxylated sorbitol esters, aromatic ethoxylates, alcohol ethoxylates, mercaptan ethoxylates, modified ethoxylates, amide surfactants, phosphate esters, phosphonate esters, phosphite esters, alkyl sulfates, fatty acid ethers, alkyl ether sulfates, alkylaryl ether sulfates, sulfonates, naphthalene sulfonates, sulfosuccinates, sulfonated esters, sulfonated amides, alkyl ether carboxylates, alkylaryl ether carboxylates, quaternary amines, amino quaternary amines, ethoxylated amines, imidazoline derivatives, betaines, sultaines, aminopropionate, catechol derivatives, saturated fatty acids, unsaturated fatty acids, and combinations thereof. Preferably, the lubricants are selected from the material classes consisting of: fatty acid esters, ethoxylated fatty acid esters, PEG esters, ethoxylated esters, sorbitol esters, ethoxylated sorbitol esters, aromatic ethoxylates, alcohol ethoxylates, phosphate esters, phosphonate esters, phosphite esters and combinations thereof. Most preferred are sorbitol esters, ethoxylated sorbitol esters, and aromatic ethoxylates.
Such lubricants are commercially available. An exemplary list is set out in the Table below. Such lubricants specifically exclude the metallic salts of stearic acid (e.g., Zn stearate and Ca stearate) and lubricants containing same.
The components, UHMWPE, filler (optional), processing oil, and lubricant, are mixed. In formulations with filler, the weight ratio of polymer to filler may range from 1:1 to 1:5, 1:3 being preferred. The ratio of UHMWPE and filler to oil may range from 1:1 to 1:2, 1:1.5 being preferred. The lubricant may comprise up to 15 weight % of the formulation, with 0.2 to 8% being preferred. In formulation without filler, the polymer may comprise up to 80% by weight of the mixture, preferably in the range of 20-65% by weight. The ratio of oil to lubricant may range from 3:1 to 1:3, with the range of 2:1 to 1:2 being preferred. The components are preferably mixed in a continuous fashion, for example, in a twin screw extruder or a Brabender extruder or a screw extruder with a blown film die.
After mixing, the mixture is shaped. Shaping will depend upon the particular article desired, as is known in the art. For example, if a film or sheet is desired, then the appropriate die may be added to the extruder. After shaping, the articles are most often subjected to a step to remove the processing oil or solvent from the article (gel), (e.g., an extraction (or washing or leaching) step to remove processing oil and lubricant). This step is conventional. For example, see U.S. Pat. Nos. 3,351,495; 4,588,633; 4,833,172; 5,248,461; and 5,948,557 each is incorporated herein by reference. In formulations with filler, the extruded sheets are preferably subjected to an extraction step to remove processing oil. After extraction, these sheets may have about 0.5% (nominally 0%) to 30% by weight oil remaining, preferably 5-25%, and most preferably 10-20%. It is understood that it is impossible to remove all of the processing oil and lubricant from any of the mixtures, so at least a trace amount will remain in the final articles. In formulations without fillers, the extruded sheets are preferably subjected to an extraction step. After extraction, these sheets may have only residual amounts of oil and lubricant. Articles may be subjected to stretching or tentering before, during, or after extraction.
Preferably, these articles are formed into microporous sheets or films. Such microporous sheets and films may be used as labels, diffusion membranes, and separators in electrochemical devices (e.g., batteries, capacitors, and fuel cells). A battery is an electrochemical device having an anode, a cathode, an electrolyte, and a separator sandwiched between the anode and the cathode and impregnated with the electrolyte. Formulation with filler are used preferably in lead acid batteries. Formulations without filler are used preferably in lithium batteries.
In the following examples, set out in Tables 1-8, ultrahigh molecular weight polyethylene (GUR 4130 and GUR 4170 from Ticona LLC of Summit, N.J.), filler (specifically silica, HiSil from PPG of Pittsburgh, Pa.), processing oil (naphthalenic oil from Calumet Co. of Princeton, La.), and lubricant (as identified in the tables) were blended together and extruded from a twin screw extruder. The extruded product, a sheet, was subjected to an extraction step for the removal of processing oil. During extrusion, torque (% Kw) and melt temperature were measured for comparison to control (examples without additive) and indicates the amount of energy needed to mix the components. After extraction, the amount of oil remaining in the article of manufacture (final oil %) was determined by a extraction technique in which: a dried, 1.33 inch (3.38 cm)×6 inch (15.24 cm) piece of sheet was weighed (W1) and then immersed in 200 ml of fresh, room temperature hexane in a ultrasonic bath for at least 15 minutes; then the sample is dried and reweighed (W2). The % oil is [(W1-W2)/W1]*100. Two samples are averaged. Additionally, basis weight was measured in conventional fashion, and thickness (web) by ASTM D 374, MD tensile by ASTM D 638, porosity by Battery Council International (BCI) TM-3.207, and ER by BCI TM-3.218 using a conventional tester from Palico Instrument Limited of Circle Pines, Minn. Puncture strength generally follows ASTM D3763 except as noted below: The instrument used was a Chatillon digital force guage DFIS 10 on a motorized test stand TCM 201. Chatillon/Ametek is located in Largo, Fla. The puncture tip is slightly rounded and 1.930 mm in diameter, and the platform hole is 6.5 mm in diameter. The travel speed is set at 300 mm/min, and at least 10 measurements are averaged across a representative area of the sample. This method is generally independent of sample size, and representative area of the sample refers to across the width and length of a reasonably sized sample. The peak force needed to puncture the sample is recorded in units of N or lbs.
In Tables 1-5, ingredients were mixed at the throat of the extruder, and in Tables 6-8, the lubricant was injected through the extruder's barrel.
In the following examples, set out in Table 9, ultrahigh molecular weight polyethylene (GUR 4130 from Ticona LLC of Summit, N.J.), processing oil (naphthalenic oil from Calumet Co. of Princeton, La.), and lubricant (as identified in the table) were blended together and extruded from a twin screw extruder. The extruded product was observed as it exited the extruder die and categorized by appearance scale 1-10. A rating of 10 meant a smooth product that appeared well mixed, and a rating of 1 meant a very grainy and rough appearance.
In the following examples, set out in Table 10, ultrahigh molecular weight polyethylene (GUR 4170 from Ticona LLC, Summit, N.J.), filler (silica, HiSil from PPG of Pittsburgh, Pa.), processing oil (naphthelenic oil from Calumet Co. of Pamaton, La.), and lubricant (as identified in the table) were mixed together and extruded from a Brabender extruder (BW Brabender Co. of South Hackensack, N.J.). In the control, 5.42 grams of UHMWPE was mixed with 14.65 g filler and 30.56 g oil. In the other examples, 5.42 grams of UHMWPE was mixed with 14.65 filler, 29.06 g oil and 1.50 g lubricant. This procedure is used to predict the lubricant's efficacy by observing fusion time and terminal torque. The fusion time is a measure of when the polymer dissolves in the oil (phase inversion of the polymer). The fusion time is typically the second peak on a plot of torque as a function of time. The fusion time typically occurs after a first peak which indicates wetting of the polymer by the oil. The terminal torque is measured after 10 minutes of mixing.
The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicated the scope of the invention.
This Application is a Divisional Application from application Ser. No. 10/121,278 filed Apr. 12, 2002, now U.S. Pat. No. 7,238,744.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3346547 | Cohen | Oct 1967 | A |
| 3351495 | Larsen et al. | Nov 1967 | A |
| 4588633 | Kono et al. | May 1986 | A |
| 4699857 | Giovannoni et al. | Oct 1987 | A |
| 4833172 | Schwarz et al. | May 1989 | A |
| 4861644 | Young et al. | Aug 1989 | A |
| 4892779 | Leatherman et al. | Jan 1990 | A |
| 5230843 | Howard et al. | Jul 1993 | A |
| 5234652 | Woodhams et al. | Aug 1993 | A |
| 5246798 | Yaacoub | Sep 1993 | A |
| 5248461 | Pluyter et al. | Sep 1993 | A |
| 5281491 | Rein et al. | Jan 1994 | A |
| 5318866 | Degen et al. | Jun 1994 | A |
| 5326391 | Anderson et al. | Jul 1994 | A |
| 5336573 | Zuckerbrod et al. | Aug 1994 | A |
| 5399308 | Woodhams et al. | Mar 1995 | A |
| 5422061 | Takahashi et al. | Jun 1995 | A |
| 5479952 | Zachariades et al. | Jan 1996 | A |
| 5583171 | Schwarz et al. | Dec 1996 | A |
| 5618642 | Samii et al. | Apr 1997 | A |
| 5641565 | Sogo | Jun 1997 | A |
| 5665488 | Young et al. | Sep 1997 | A |
| 5683634 | Fujii et al. | Nov 1997 | A |
| 5863466 | Mor | Jan 1999 | A |
| 5922492 | Takita et al. | Jul 1999 | A |
| 5948557 | Ondeck et al. | Sep 1999 | A |
| 6124059 | Bohnstedt et al. | Sep 2000 | A |
| 6242127 | Paik et al. | Jun 2001 | B1 |
| 6372379 | Samii et al. | Apr 2002 | B1 |
| 6403264 | Bunsch et al. | Jun 2002 | B1 |
| 6485867 | Navarrete et al. | Nov 2002 | B1 |
| 6524742 | Emanuel et al. | Feb 2003 | B1 |
| 6559195 | Yamamoto et al. | May 2003 | B1 |
| 6566012 | Takita et al. | May 2003 | B1 |
| 6586138 | Pekala et al. | Jul 2003 | B2 |
| 6666969 | Funaoka et al. | Dec 2003 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20050245653 A1 | Nov 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10121278 | Apr 2002 | US |
| Child | 11070511 | US |