Ultrasonic degassing of molten metals

Information

  • Patent Grant
  • 9617617
  • Patent Number
    9,617,617
  • Date Filed
    Thursday, September 12, 2013
    11 years ago
  • Date Issued
    Tuesday, April 11, 2017
    7 years ago
Abstract
Methods for degassing and for removing impurities from molten metals are disclosed. These methods can include operating an ultrasonic device in a molten metal bath, and adding a purging gas into the molten metal bath in close proximity to the ultrasonic device.
Description
COPYRIGHTS

All rights, including copyrights, in the material included herein are vested in and the property of the Applicants. The Applicants retain and reserve all rights in the material included herein, and grant permission to reproduce the material only in connection with reproduction of the granted patent and for no other purpose.


BACKGROUND

The processing or casting of certain metal articles may require a bath containing a molten metal, and this bath of molten metal may be maintained at a temperature in a range of 700° C. to 1200° C., or more, depending upon the particular metal. Many instruments or devices may be used in the molten metal bath for the production or casting of the desired metal article. There is a need for these instruments or devices to better withstand the elevated temperatures encountered in the molten metal bath, beneficially having a longer lifetime and limited to no reactivity with the particular molten metal.


Moreover, molten metals may have one or more gasses dissolved in them and/or impurities present in them, and these gasses and/or impurities may negatively impact the final production and casting of the desired metal article, and/or the resulting physical properties of the metal article itself. Attempts to reduce the amounts of dissolved gasses or impurities present in molten metal baths have not been completely successful. Accordingly, there is a need for improved methods to remove gasses and/or impurities from molten metals.


SUMMARY

This summary is provided to introduce a selection of concepts in a simplified form that are further described below in the detailed description. This summary is not intended to identify required or essential features of the claimed subject matter. Nor is this summary intended to be used to limit the scope of the claimed subject matter.


The present invention is directed to methods for reducing the amount of a dissolved gas (and/or various impurities) in a molten metal bath (e.g., ultrasonic degassing). In one embodiment, the method may comprise operating an ultrasonic device in the molten metal bath, and introducing a purging gas into the molten metal bath in close proximity to the ultrasonic device. For example, the dissolved gas may comprise hydrogen, the molten metal bath may comprise aluminum or copper (including alloys thereof), and the purging gas may comprise argon and/or nitrogen. The purging gas may be added to the molten metal bath within about 50 cm (or 25 cm, or 15 cm, or 5 cm, or 2 cm) of the ultrasonic device.


The present invention also discloses ultrasonic devices, and these ultrasonic devices may be used in many different applications, including ultrasonic degassing. As an example, the ultrasonic device may comprise an ultrasonic transducer; an elongated probe comprising a first end and a second end, the first end attached to the ultrasonic transducer and the second end comprising a tip; and a purging gas delivery system, wherein the purging gas delivery system may comprise a purging gas inlet and a purging gas outlet. In some embodiments, the purging gas outlet may be within about 10 cm (or 5 cm, or 1 cm) of the tip of the elongated probe, while in other embodiments, the purging gas outlet may be at the tip of the elongated probe. In addition, the ultrasonic device may comprise multiple probe assemblies and/or multiple probes per ultrasonic transducer.


Both the foregoing summary and the following detailed description provide examples and are explanatory only. Accordingly, the foregoing summary and the following detailed description should not be considered to be restrictive. Further, features or variations may be provided in addition to those set forth herein. For example, certain embodiments may be directed to various feature combinations and sub-combinations described in the detailed description.





BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and constitute a part of this disclosure, illustrate various embodiments of the present invention. In the drawings:



FIG. 1 shows a partial cross-sectional view of an ultrasonic device in an embodiment of the present invention.



FIG. 2 shows a partial cross-sectional view of an ultrasonic device in another embodiment of the present invention.



FIG. 3 shows a partial cross-sectional view of an ultrasonic device in yet another embodiment of the present invention.



FIG. 4 is a bar graph illustrating the percentage difference in density for each of Examples 1-4 as compared to the theoretical density of aluminum.



FIG. 5 is a bar graph illustrating the hydrogen content in ppm of each of Examples 1-4.



FIG. 6 is a plot of hydrogen concentration as a function of time for Examples 5-8.





DETAILED DESCRIPTION

The following detailed description refers to the accompanying drawings. Wherever possible, the same or similar reference numbers are used in the drawings and the following description to refer to the same or similar elements. While embodiments of the invention may be described, modifications, adaptations, and other implementations are possible. For example, substitutions, additions, or modifications may be made to the elements illustrated in the drawings, and the methods described herein may be modified by substituting, reordering, or adding stages to the disclosed methods. Accordingly, the following detailed description does not limit the scope of the invention.


The terms “a,” “an,” and “the” are intended to include plural alternatives, e.g., at least one. For instance, the disclosure of “an ultrasonic device,” “an elongated probe,” “a purging gas,” etc., is meant to encompass one, or combinations of more than one, ultrasonic device, elongated probe, purging gas, etc., unless otherwise specified.


All publications and patents mentioned herein are incorporated herein by reference for the purpose of describing and disclosing, for example, the constructs and methodologies that are described in the publications, which might be used in connection with the presently described invention. The publications discussed throughout the text are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the inventors are not entitled to antedate such disclosure by virtue of prior invention.


Applicants disclose several types of ranges in the present invention. When Applicants disclose or claim a range of any type, Applicants' intent is to disclose or claim individually each possible number that such a range could reasonably encompass, including end points of the range as well as any sub-ranges and combinations of sub-ranges encompassed therein. For example, in an embodiment of the invention, the purging gas may be added to the molten metal bath at a rate in a range from about 1 to about 50 L/min. By a disclosure that the flow rate is in a range from about 1 to about 50 L/min, Applicants intend to recite that the flow rate may be about 1, about 2, about 3, about 4, about 5, about 6, about 7, about 8, about 9, about 10, about 11, about 12, about 13, about 14, about 15, about 16, about 17, about 18, about 19, about 20, about 21, about 22, about 23, about 24, about 25, about 26, about 27, about 28, about 29, about 30, about 31, about 32, about 33, about 34, about 35, about 36, about 37, about 38, about 39, about 40, about 41, about 42, about 43, about 44, about 45, about 46, about 47, about 48, about 49, or about 50 L/min. Additionally, the flow rate may be within any range from about 1 to about 50 L/min (for example, the rate is in a range from about 2 to about 20 L/min), and this also includes any combination of ranges between about 1 and about 50 L/min. Likewise, all other ranges disclosed herein should be interpreted in a similar manner.


Embodiments of the present invention may provide systems, methods, and/or devices for the ultrasonic degassing of molten metals. Such molten metals may include, but are not limited to, aluminum, copper, steel, zinc, magnesium, and the like, or combinations of these and other metals (e.g., alloys). Accordingly, the present invention is not limited to any particular metal or metal alloy. The processing or casting of articles from a molten metal may require a bath containing the molten metal, and this bath of the molten metal may be maintained at elevated temperatures. For instance, molten copper may be maintained at temperatures of around 1100° C., while molten aluminum may be maintained at temperatures of around 750° C.


As used herein, the terms “bath,” “molten metal bath,” and the like are meant to encompass any container that might contain a molten metal, inclusive of vessel, crucible, trough, launder, and so forth. The bath and molten metal bath terms are used to encompass batch, continuous, semi-continuous, etc., operations and, for instance, where the molten metal is generally static (e.g., often associated with a crucible) and where the molten metal is generally in motion (e.g., often associated with a launder).


Many instruments or devices may be used to monitor, to test, or to modify the conditions of the molten metal in the bath, as well as for the final production or casting of the desired metal article. There is a need for these instruments or devices to better withstand the elevated temperatures encountered in molten metal baths, beneficially having a longer lifetime and limited to no reactivity with the molten metal, whether the metal is (or the metal comprises) aluminum, or copper, or steel, or zinc, or magnesium, and so forth.


Furthermore, molten metals may have one or more gasses dissolved in them, and these gasses may negatively impact the final production and casting of the desired metal article, and/or the resulting physical properties of the metal article itself. For instance, the gas dissolved in the molten metal may comprise hydrogen, oxygen, nitrogen, sulfur dioxide, and the like, or combinations thereof. In some circumstances, it may be advantageous to remove the gas, or to reduce the amount of the gas in the molten metal. As an example, dissolved hydrogen may be detrimental in the casting of aluminum (or copper, or other metal or alloy) and, therefore, the properties of finished articles produced from aluminum (or copper, or other metal or alloy) may be improved by reducing the amount of entrained hydrogen in the molten bath of aluminum (or copper, or other metal or alloy). Dissolved hydrogen over 3-5 ppm, on a mass basis, may have detrimental effects on the casting rates and the quality of resulting aluminum (or copper, or other metal or alloy) rods and other articles. Hydrogen may enter the molten aluminum (or copper, or other metal or alloy) bath by its presence in the atmosphere above the bath containing the molten aluminum (or copper, or other metal or alloy), or it may be present in aluminum (or copper, or other metal or alloy) feedstock starting material used in the molten aluminum (or copper, or other metal or alloy) bath.


Attempts to reduce the amounts of dissolved gasses in molten metal baths have not been completely successful. Often, these processes involve additional and expensive equipment, as well as potentially hazardous materials. For instance, a process used in the metal casting industry to reduce the dissolved gas content of a molten metal may consist of rotors made of a material such as graphite, and these rotors may be placed within the molten metal bath. Chlorine gas additionally may be added to the molten metal bath at positions adjacent to the rotors within the molten metal bath. This process will be referred to as the “conventional” process throughout this disclosure, and is often referred to in the industry as rotary gas purging. While the conventional process may be successful in reducing, for example, the amount of dissolved hydrogen in a molten metal bath in some situations, this conventional process has noticeable drawbacks, not the least of which are cost, complexity, and the use of potentially hazardous and potentially environmentally harmful chlorine gas.


Additionally, molten metals may have impurities present in them, and these impurities may negatively impact the final production and casting of the desired metal article, and/or the resulting physical properties of the metal article itself. For instance, the impurity in the molten metal may comprise an alkali metal or other metal that is neither required nor desired to be present in the molten metal. As one of skill in the art would recognize, small percentages of certain metals are present in various metal alloys, and such metals would not be considered to be impurities. As non-limiting examples, impurities may comprise lithium, sodium, potassium, lead, and the like, or combinations thereof. Various impurities may enter a molten metal bath (aluminum, copper, or other metal or alloy) by their presence in the incoming metal feedstock starting material used in the molten metal bath.


Embodiments of this invention may provide methods for reducing an amount of a dissolved gas in a molten metal bath or, in alternative language, methods for degassing molten metals. One such method may comprise operating an ultrasonic device in the molten metal bath, and introducing a purging gas into the molten metal bath in close proximity to the ultrasonic device. The dissolved gas may be or may comprise oxygen, hydrogen, sulfur dioxide, and the like, or combinations thereof. For example, the dissolved gas may be or may comprise hydrogen. The molten metal bath may comprise aluminum, copper, zinc, steel, magnesium, and the like, or mixtures and/or combinations thereof (e.g., including various alloys of aluminum, copper, zinc, steel, magnesium, etc.). In some embodiments, the molten metal bath may comprise aluminum, while in other embodiments, the molten metal bath may comprise copper. Accordingly, the molten metal in the bath may be aluminum or, alternatively, the molten metal may be copper.


Moreover, embodiments of this invention may provide methods for reducing an amount of an impurity present in a molten metal bath or, in alternative language, methods for removing impurities. One such method may comprise operating an ultrasonic device in the molten metal bath, and introducing a purging gas into the molten metal bath in close proximity to the ultrasonic device. The impurity may be or may comprise lithium, sodium, potassium, lead, and the like, or combinations thereof. For example, the impurity may be or may comprise lithium or, alternatively, sodium. The molten metal bath may comprise aluminum, copper, zinc, steel, magnesium, and the like, or mixtures and/or combinations thereof (e.g., including various alloys of aluminum, copper, zinc, steel, magnesium, etc.). In some embodiments, the molten metal bath may comprise aluminum, while in other embodiments, the molten metal bath may comprise copper. Accordingly, the molten metal in the bath may be aluminum or, alternatively, the molten metal may be copper.


The purging gas employed in the methods of degassing and/or methods of removing impurities disclosed herein may comprise one or more of nitrogen, helium, neon, argon, krypton, and/or xenon, but is not limited thereto. It is contemplated that any suitable gas may be used as a purging gas, provided that the gas does not appreciably react with, or dissolve in, the specific metal(s) in the molten metal bath. Additionally, mixtures or combinations of gases may be employed. According to some embodiments disclosed herein, the purging gas may be or may comprise an inert gas; alternatively, the purging gas may be or may comprise a noble gas; alternatively, the purging gas may be or may comprise helium, neon, argon, or combinations thereof; alternatively, the purging gas may be or may comprise helium; alternatively, the purging gas may be or may comprise neon; or alternatively, the purging gas may be or may comprise argon. Additionally, Applicants contemplate that, in some embodiments, the conventional degassing technique can be used in conjunction with ultrasonic degassing processes disclosed herein. Accordingly, the purging gas may further comprise chlorine gas in some embodiments.


However, in other embodiments of this invention, methods for degassing or for reducing an amount of a dissolved gas in a molten metal bath may be conducted in the substantial absence of chlorine gas, or with no chlorine gas present. As used herein, a substantial absence means that no more than 5% chlorine gas by weight may be used, based on the amount of purging gas used. In some embodiments, the methods disclosed herein may comprise introducing a purging gas, and this purging gas may be selected from the group consisting of nitrogen, helium, neon, argon, krypton, xenon, and combinations thereof.


The amount of the purging gas introduced into the bath of molten metal may vary depending on a number of factors. Often, the amount of the purging gas introduced in a method of degassing molten metals (and/or in a method of removing impurities from molten metals) in accordance with embodiments of this invention may fall within a range from about 0.1 to about 150 standard liters/min (L/min). In some embodiments, the amount of the purging gas introduced may be in a range from about 0.5 to about 100 L/min, from about 1 to about 100 L/min, from about 1 to about 50 L/min, from about 1 to about 35 L/min, from about 1 to about 25 L/min, from about 1.5 to about 20 L/min, from about 2 to about 15 L/min, or from about 2 to about 10 L/min. These volumetric flow rates are in standard liters per minute, i.e., at a standard temperature (21.1° C.) and pressure (101 kPa).


In continuous or semi-continuous molten metal operations, the amount of the purging gas introduced into the bath of molten metal may vary based on the molten metal output or production rate. Accordingly, the amount of the purging gas introduced in a method of degassing molten metals (and/or in a method of removing impurities from molten metals) in accordance with such embodiments may fall within a range from about 10 to about 500 mL/hr of purging gas per kg/hr of molten metal (mL purging gas/kg molten metal). In some embodiments, the ratio of the volumetric flow rate of the purging gas to the output rate of the molten metal may be in a range from about 10 to about 400 mL/kg; alternatively, from about 15 to about 300 mL/kg; alternatively, from about 20 to about 250 mL/kg; alternatively, from about 30 to about 200 mL/kg; alternatively, from about 40 to about 150 mL/kg; or alternatively, from about 50 to about 125 mL/kg. As above, the volumetric flow rate of the purging gas is at a standard temperature (21.1° C.) and pressure (101 kPa).


Methods for degassing molten metals consistent with embodiments of this invention may be effective in removing greater than about 10 weight percent of the dissolved gas present in the molten metal bath, i.e., the amount of dissolved gas in the molten metal bath may be reduced by greater than about 10 weight percent from the amount of dissolved gas present before the degassing process was employed. In some embodiments, the amount of dissolved gas present may be reduced by greater than about 15 weight percent, greater than about 20 weight percent, greater than about 25 weight percent, greater than about 35 weight percent, greater than about 50 weight percent, greater than about 75 weight percent, or greater than about 80 weight percent, from the amount of dissolved gas present before the degassing method was employed. For instance, if the dissolved gas is hydrogen, levels of hydrogen in a molten bath containing aluminum or copper greater than about 3 ppm or 4 ppm or 5 ppm (on a mass basis) may be detrimental and, often, the hydrogen content in the molten metal may be about 4 ppm, about 5 ppm, about 6 ppm, about 7 ppm, about 8 ppm, about 9 ppm, about 10 ppm, about 15 ppm, about 20 ppm, or greater than 20 ppm. It is contemplated that employing the methods disclosed in embodiments of this invention may reduce the amount of the dissolved gas in the molten metal bath to less than about 4 ppm; alternatively, to less than about 3 ppm; alternatively, to less than about 2 ppm; alternatively, to within a range from about 1 to about 4 ppm; alternatively, to within a range from about 1 to about 3 ppm; or alternatively, to within a range from about 2 to about 3 ppm. In these and other embodiments, the dissolved gas may be or may comprise hydrogen, and the molten metal bath may be or may comprise aluminum and/or copper.


Embodiments of this invention directed to methods of degassing (e.g., reducing the amount of a dissolved gas in bath comprising a molten metal) or to methods of removing impurities may comprise operating an ultrasonic device in the molten metal bath. The ultrasonic device may comprise an ultrasonic transducer and an elongated probe, and the probe may comprise a first end and a second end. The first end may be attached to the ultrasonic transducer and the second end may comprise a tip, and the tip of the elongated probe may comprise niobium. Specifics on illustrative and non-limiting examples of ultrasonic devices that may be employed in the processes and methods disclosed herein will be discussed further below. As it pertains to an ultrasonic degassing process or to a process for removing impurities, the purging gas may be introduced into the molten metal bath, for instance, at a location near the ultrasonic device. Often, the purging gas may be introduced into the molten metal bath at a location near the tip of the ultrasonic device. It is contemplated that the purging gas may be introduced into the molten metal bath within about 1 meter of the tip of the ultrasonic device, such as, for example, within about 100 cm, within about 50 cm, within about 40 cm, within about 30 cm, within about 25 cm, or within about 20 cm, of the tip of the ultrasonic device. In some embodiments, the purging gas may be introduced into the molten metal bath within about 15 cm of the tip of the ultrasonic device; alternatively, within about 10 cm; alternatively, within about 8 cm; alternatively, within about 5 cm; alternatively, within about 3 cm; alternatively, within about 2 cm; or alternatively, within about 1 cm. In a particular embodiment, the purging gas may be introduced into the molten metal bath adjacent to or through the tip of the ultrasonic device.


While not intending to be bound by this theory, Applicants believe that a synergistic effect may exist between the use of an ultrasonic device and the incorporation of a purging gas in close proximity, resulting in a dramatic reduction in the amount of a dissolved gas in a bath containing molten metal. Applicants believe that the ultrasonic energy produced by the ultrasonic device may create cavitation bubbles in the melt, into which the dissolved gas may diffuse. However, Applicants believe that, in the absence of the purging gas, many of the cavitation bubbles may collapse prior to reaching the surface of the bath of molten metal. Applicants believe that the purging gas may lessen the amount of cavitation bubbles that collapse before reaching the surface, and/or may increase the size of the bubbles containing the dissolved gas, and/or may increase the number of bubbles in the molten metal bath, and/or may increase the rate of transport of bubbles containing dissolved gas to the surface of the molten metal bath. Regardless of the actual mechanism, Applicants believe that the use of an ultrasonic device in combination with a source of a purging gas in close proximity may provide a synergistic improvement in the removal of the dissolved gas from the molten metal bath, and a synergistic reduction in the amount of dissolved gas in the molten metal. Again, while not wishing to be bound by theory, Applicants believe that the ultrasonic device may create cavitation bubbles within close proximity to the tip of the ultrasonic device. For instance, for an ultrasonic device having a tip with a diameter of about 2 to 5 cm, the cavitation bubbles may be within about 15 cm, about 10 cm, about 5 cm, about 2 cm, or about 1 cm of the tip of the ultrasonic device before collapsing. If the purging gas is added at a distance that is too far from the tip of the ultrasonic device, the purging gas may not be able to diffuse into the cavitation bubbles. Hence, while not being bound by theory, Applicants believe that it may be beneficial for the purging gas to be introduced into the molten metal bath within about 25 cm or about 20 cm of the tip of the ultrasonic device, and more beneficially, within about 15 cm, within about 10 cm, within about 5 cm, within about 2 cm, or within about 1 cm, of the tip of the ultrasonic device.


Ultrasonic devices in accordance with embodiments of this invention may be in contact with molten metals such as aluminum or copper, for example, as disclosed in U.S. Patent Publication No. 2009/0224443, which is incorporated herein by reference in its entirety. In an ultrasonic device for reducing dissolved gas content (e.g., hydrogen) in a molten metal, niobium or an alloy thereof may be used as a protective barrier for the device when it is exposed to the molten metal, or as a component of the device with direct exposure to the molten metal.


Embodiments of the present invention may provide systems and methods for increasing the life of components directly in contact with molten metals. For example, embodiments of the invention may use niobium to reduce degradation of materials in contact with molten metals, resulting in significant quality improvements in end products. In other words, embodiments of the invention may increase the life of or preserve materials or components in contact with molten metals by using niobium as a protective barrier. Niobium may have properties, for example its high melting point, that may help provide the aforementioned embodiments of the invention. In addition, niobium also may form a protective oxide barrier when exposed to temperatures of about 200° C. and above.


Moreover, embodiments of the invention may provide systems and methods for increasing the life of components directly in contact or interfacing with molten metals. Because niobium has low reactivity with certain molten metals, using niobium may prevent a substrate material from degrading. Consequently, embodiments of the invention may use niobium to reduce degradation of substrate materials resulting in significant quality improvements in end products. Accordingly, niobium in association with molten metals may combine niobium's high melting point and its low reactivity with molten metals, such as aluminum and/or copper.


In some embodiments, niobium or an alloy thereof may be used in an ultrasonic device comprising an ultrasonic transducer and an elongated probe. The elongated probe may comprise a first end and a second end, wherein the first end may be attached to the ultrasonic transducer and the second end may comprise a tip. In accordance with this embodiment, the tip of the elongated probe may comprise niobium (e.g., niobium or an alloy thereof). The ultrasonic device may be used in an ultrasonic degassing process, as discussed above. The ultrasonic transducer may generate ultrasonic waves, and the probe attached to the transducer may transmit the ultrasonic waves into a bath comprising a molten metal, such as aluminum, copper, zinc, steel, magnesium, and the like, or mixtures and/or combinations thereof (e.g., including various alloys of aluminum, copper, zinc, steel, magnesium, etc.).



FIG. 1 illustrates using niobium and other materials in an ultrasonic device 300, which may be used to reduce dissolved gas content in a molten metal. The ultrasonic device 300 may include an ultrasonic transducer 360, a booster 350 for increased output, and an ultrasonic probe assembly 302 attached to the transducer 360. The ultrasonic probe assembly 302 may comprise an elongated ultrasonic probe 304 and an ultrasonic medium 312. The ultrasonic device 300 and ultrasonic probe 304 may be generally cylindrical in shape, but this is not a requirement. The ultrasonic probe 304 may comprise a first end and a second end, wherein the first end comprises an ultrasonic probe shaft 306 which is attached to the ultrasonic transducer 360. The ultrasonic probe 304 and the ultrasonic probe shaft 306 may be constructed of various materials. Exemplary materials may include, but are not limited to, stainless steel, titanium, niobium, a ceramic (e.g., Sialon) and the like, or combinations thereof. The second end of the ultrasonic probe 304 may comprise an ultrasonic probe tip 310. The ultrasonic probe tip 310 may comprise niobium. Alternatively, the tip 310 may consistent essentially of, or consist of, niobium. Niobium may be alloyed with one or more other metals, or niobium may be a layer that is plated or coated onto a base layer of another material. For instance, the tip 310 may comprise an inner layer and an outer layer, wherein the inner layer may comprise a ceramic or a metal material (e.g., titanium) and the outer layer may comprise niobium. In this embodiment, the thickness of the outer layer comprising niobium may be less than about 25 microns, or less than about 10 microns, or alternatively, within a range from about 2 to about 8 microns. For example, the thickness of the outer layer comprising niobium may be in range from about 3 to about 6 microns.


The ultrasonic probe shaft 306 and the ultrasonic probe tip 310 may be joined by a connector 308. The connector 308 may represent a means for attaching the shaft 306 and the tip 310. For example the shaft 306 and the tip 310 may be bolted or soldered together. In one embodiment, the connector 308 may represent that the shaft 306 contains recessed threading and the tip 310 may be screwed into the shaft 306. It is contemplated that the ultrasonic probe shaft 306 and the ultrasonic probe tip 310 may comprise different materials. For instance, the ultrasonic probe shaft 306 may be or may comprise titanium and/or niobium, while the ultrasonic probe tip 310 may be or may comprise niobium. Alternatively, the ultrasonic probe shaft 306 may be or may comprise titanium and/or a ceramic (e.g., Sialon), while the ultrasonic probe tip 310 may be or may comprise a ceramic (e.g., Sialon).


In other embodiments, the ultrasonic probe 304 may be a single piece, e.g., the ultrasonic probe shaft 306 and the ultrasonic probe tip 310 are a unitary part having the same construction. In such instances, the ultrasonic probe may comprise, for instance, niobium or an alloy thereof, a ceramic (e.g., Sialon), or other suitable material.


Referring again to FIG. 1, the ultrasonic device 300 may comprise an inner tube 328, a center tube 324, an outer tube 320, and a protection tube 340. These tubes or channels may surround at least a portion of the ultrasonic probe 304 and generally may be constructed of any suitable metal or ceramic material. It may be expected that the ultrasonic probe tip 310 will be placed into the bath of molten metal; however, it is contemplated that a portion of the protection tube 340 also may be immersed in molten metal. Accordingly, the protection tube 340 may be or may comprise titanium, niobium, silicon carbide, a ceramic, or a combination of more than one of these materials. Contained within the tubes 328, 324, 320, and 340 may be fluids 322, 326, and 342, as illustrated in FIG. 1. The fluid may be a liquid or a gas (e.g., argon), the purpose of which may be to provide cooling to the ultrasonic device 300 and, in particular, to the ultrasonic probe tip 310 and the protection tube 340.


The ultrasonic device 300 may comprise an end cap 344. The end cap may bridge the gap between the protection tube 340 and the probe tip 310 and may reduce or prevent molten metal from entering the ultrasonic device 300. Similar to the protection tube 340, the end cap 344 may be or may comprise, for example, titanium, niobium, silicon carbide, a ceramic, or a combination of more than one of these materials.


The ultrasonic probe tip 310, the protection tube 340, or the end cap 344, or all three, may comprise niobium. Niobium alone may be used, niobium may be alloyed with one or more other metals, or niobium may be a layer that is plated or coated onto a base layer of another material. For instance, the ultrasonic probe tip 310, the protection tube 340, or the end cap 344, or all three, may comprise an inner layer and an outer layer, wherein the inner layer may comprise a ceramic or a metal material and the outer layer may comprise niobium. It may be expected that the presence of niobium on parts of the ultrasonic device may improve the life of the device, may provide low or no chemical reactivity when in contact with molten metals, may provide strength at the melting temperature of the molten metal, and may have the capability to propagate ultrasonic waves. In accordance with some embodiments of this invention, when the tip 310 of the ultrasonic device does not comprise niobium, the tip may show erosion or degradation after only about 15-30 minutes in a molten metal bath (e.g., of aluminum or copper). In contrast, when the tip of the ultrasonic device comprises niobium, the tip may show no or minimal erosion or degradation after at least 1 hour or more, for instance, no erosion or degradation after at least 2 hours, after at least 3 hours, after at least 4 hours, after at least 5 hours, after at least 6 hours, after at least 12 hours, after at least 24 hours, after at least 48 hours, or after at least 72 hours.


In another embodiment, the ultrasonic probe tip 310, the protection tube 340, or the end cap 344, or all three, may comprise a ceramic, such as Sialon. Further, the ultrasonic probe shaft 306 may comprise a ceramic, or alternatively, titanium.



FIG. 2 illustrates another ultrasonic device 400 that may comprise niobium, a ceramic such as Sialon, or other suitable material. The ultrasonic device 400 may include an ultrasonic transducer 460, a booster 450 for increased output, and an ultrasonic probe assembly 402 attached to the transducer 460. The booster 450 may permit increased output at boost levels greater than about 1:1, for instance, from about 1.2:1 to about 10:1, or from about 1.4:1 to about 5:1. A booster clamp assembly 451 having a height H may be employed, where the height H may vary as needed to accommodate different length ultrasonic probes. The ultrasonic probe assembly 402 may comprise an elongated ultrasonic probe as depicted in FIG. 1 and an ultrasonic probe tip 410. The ultrasonic probe and tip may be constructed of various materials, as previously discussed, including, but not limited to, stainless steel, titanium, niobium, ceramics, and the like, or combinations thereof, inclusive of mixtures thereof, alloys thereof, and coatings thereof.


The ultrasonic device 400 may comprise a means for introducing a purging gas (e.g., into a molten metal bath) at a location near the ultrasonic device 400. It is contemplated that an external purging gas injection system (not shown) may be positioned in the molten metal bath, and the injection site may be near the ultrasonic device of FIG. 1 and/or FIG. 2. Alternatively, the ultrasonic device may comprise a purging gas outlet, such that the purging gas may be expelled near or at the tip of the ultrasonic device. For instance, the purging gas may be expelled through the end cap of the ultrasonic device and/or through the probe of the ultrasonic device. Referring again to FIG. 2, the ultrasonic device may comprise a purging gas inlet port 424 and injection chamber 425, connected to a purging gas delivery channel 413. The purging gas may be delivered to, and expelled through, a purging gas delivery space 414 located near or at the tip 410 of the ultrasonic device 400. It is contemplated that the purging gas delivery space 414, or purging gas outlet, may be within about 10 cm of the tip 410 of the ultrasonic device 400, such as, for example, within about 5 cm, within about 3 cm, within about 2 cm, within about 1.5 cm, within about 1 cm, or within about 0.5 cm, of the tip of the ultrasonic device.


Additionally, the ultrasonic device 400 may comprise an ultrasonic cooler system 429, which may be designed to keep the ultrasonic tip and/or the ultrasonic probe and/or the ultrasonic probe assembly at a temperature closer to room temperature (e.g., the temperature may be in a range from about 15° C. to about 75° C., or from about 20° C. to about 35° C.), as opposed to the elevated temperatures of molten metal experienced by the outer surface of the tip 410 of the ultrasonic device. It is contemplated that an ultrasonic cooler system may not be required if the ultrasonic probe and assembly comprise niobium, a ceramic such as Sialon, or other suitable material. The ultrasonic cooler system 429 of FIG. 2 may be similar to that system depicted in FIG. 1 including, for instance, an inner tube 328, a center tube 324, an outer tube 320, a protection tube 340, and fluids 322, 326, and 342, designed to provide cooling and/or temperature control to the ultrasonic device. The fluid may be a liquid or a gas, and it is contemplated that the fluid may be the same material as the purging gas.



FIG. 3 illustrates yet another ultrasonic device 500 that may comprise niobium, a ceramic such as Sialon, or other suitable material. The ultrasonic device 500 may include an ultrasonic transducer 560, a booster 550 for increased output, and an ultrasonic probe assembly 510 attached to the transducer 560. The booster 550 may permit increased output at boost levels greater than about 1:1, for instance, from about 1.2:1 to about 10:1, or from about 1.4:1 to about 5:1. The ultrasonic probe 510 may be a single piece, or the ultrasonic probe 510 may comprise an ultrasonic probe shaft and an optional (and replaceable) ultrasonic probe tip 511, similar to that depicted in FIG. 1. The ultrasonic probe and tip may be constructed of various materials, as previously discussed, including, but not limited to, stainless steel, titanium, niobium, ceramics, and the like, or combinations thereof, inclusive of mixtures thereof, alloys thereof, and coatings thereof.


The ultrasonic device 500 may comprise a means for introducing a purging gas (e.g., into a molten metal bath) at a location near the ultrasonic device 500 and/or near the ultrasonic probe tip 511. As above, It is contemplated that an external purging gas injection system (not shown) may be positioned in the molten metal bath, and the injection site may be near the ultrasonic device of FIG. 3. Alternatively, the ultrasonic device may comprise a purging gas outlet, such that the purging gas may be expelled near or at the tip of the ultrasonic device. For instance, the purging gas may be expelled through the probe/tip of the ultrasonic device. Referring again to FIG. 3, the ultrasonic device may comprise a purging gas inlet port 522 in a chamber with the booster 550, an upper housing 520, lower support housing 521, and a lower support housing cover 523. The upper housing 520 may be gas tight and/or leak proof. The purging gas inlet port 522 may be connected to a purging gas delivery channel 524, which may be contained within the ultrasonic probe 510. The purging gas may be delivered to, and expelled through, a purging gas injection point 525 located at the tip 511 of the ultrasonic device 500. Accordingly, in this embodiment, the ultrasonic device 500 may comprise an ultrasonic probe 510 comprising a purging gas injection system with a purging gas injection point at the tip of the ultrasonic probe.


Optionally, the ultrasonic device 500 may comprise an ultrasonic cooler system, such as described above relative to FIG. 1 and/or FIG. 2, but this is not a requirement.


While certain embodiments of the invention have been described, other embodiments may exist. Further, any disclosed methods' stages may be modified in any manner, including by reordering stages and/or inserting or deleting stages, without departing from the invention. While the specification includes examples, the invention's scope is indicated by the following claims. Furthermore, while the specification has been described in language specific to structural features and/or methodological acts, the claims are not limited to the features or acts described above. Rather, the specific features and acts described above are disclosed as illustrative embodiments of the invention.


EXAMPLES
Examples 1-4

In Examples 1-4, a series of tests were conducted to demonstrate the reduction in the amount of dissolved hydrogen in a molten bath of aluminum that may be achieved by the disclosed methods. A control sample of the aluminum was taken and tested prior to the use of any degassing technique (Example 1). The molten metal bath of aluminum was operating at a temperature of about 1350° F. (732° C.). A conventional degassing technique, rotary gas purging, was then employed to determine the effectiveness of conventional methods of hydrogen removal (Example 2). Example 3 utilized an ultrasonic degassing process as disclosed herein, namely, an ultrasonic device in combination with the introduction of a purging gas. In Example 3, the ultrasonic device contained a niobium tip, and the tip of the ultrasonic device was placed into the aluminum bath. The ultrasonic device was operated at 20,000 Hz (frequency) in the molten bath of aluminum. Concurrently with the operation of the ultrasonic device, the purging gas argon was introduced into the molten metal bath at a rate of about 4.7 standard liters per minute (L/min). The argon was injected along the tip of the ultrasonic device (the distance between the injection point and the tip was less than about 2 cm). Example 4 utilized both the ultrasonic degassing process in combination with the conventional degassing technique.


Aluminum samples of Example 1 (no degassing), Example 2 (after conventional degassing), Example 3 (after ultrasonic degassing), and Example 4 (after ultrasonic and conventional degassing) were allowed to cool and solidify under vacuum. Then, one cubic centimeter (1 cc=1 mL) cubes from each example were measured to determine the mass and, accordingly, the density of the aluminum of each example. Aluminum has a theoretical density of 2.7 g/cc, and the presence of hydrogen gas in aluminum will reduce this density. FIG. 4 shows the percentage difference in density for each of Examples 1-4 as compared to the theoretical density of aluminum. In FIG. 4, the closer to the theoretical density of aluminum that each sample is (i.e., the lower the percentage below the density of aluminum), the more effective the degassing procedure. As demonstrated in FIG. 4, the ultrasonic procedure (Example 3) was as effective as the conventional technique (Example 2), and the use of both in combination (Example 4) may offer a slight additional improvement.


Aluminum samples of Examples 1-4 were also evaluated for the ppm hydrogen content (on a mass basis). Cast samples that were cooled and solidified under vacuum were analyzed for hydrogen content. The hydrogen content analyses are summarized in FIG. 5. In FIG. 5, the lower the hydrogen content in ppm, the more effective the degassing procedure. As demonstrated in FIG. 5, the ultrasonic procedure (Example 3) was more effective in removing hydrogen than the conventional technique (Example 2), and the use of both in combination (Example 4) did not appear to offer any additional benefit. The data of FIG. 5 are no longer relied upon. Applicants believe there was an analytical error in the determination of the listed ppm hydrogen content.


Examples 5-8

In Examples 5-8, a series of tests were conducted to determine the relative speed at which dissolved hydrogen in a molten bath of aluminum can be degassed in accordance with the disclosed methods. First, a small amount of aluminum was melted in a metal bath, and then maintained, at a temperature of about 1350° F. (732° C.). An Alspek unit was used to determine a baseline reading of hydrogen content, in units of mL/100 g. The Alspek unit uses the principle of partial pressures in an electrolytic half cell to determine the amount of dissolved hydrogen in molten aluminum. The tip of an ultrasonic device was placed into the aluminum bath, and the purging gas argon was added to the molten metal bath at a rate of about 1 standard liter per minute (L/min). For Examples 5-7, the ultrasonic device was operated with a 3:1 booster and at 20,000 Hz, although up to and including 40,000 Hz, or more, could be used. For Example 5, a baseline ultrasonic vibration amplitude was used, and a baseline power level for the ultrasonic power supply (watts); for Example 6, the ultrasonic vibration amplitude was 2 times the baseline, and the power level of the ultrasonic power supply was 1.9 times the baseline; and for Example 7, the ultrasonic vibration amplitude was 3 times the baseline, and the power level of the ultrasonic power supply was 3.6 times the baseline. For Example 8, the ultrasonic device was not used, only addition of the argon purging gas. The level of hydrogen was monitored over time using the Alspek unit, and recorded. Between each experiment, hydrogen was added into the aluminum bath, and the baseline before the addition of the argon gas was determined.


An ultrasonic device similar to that illustrated in FIG. 3 was used in Examples 5-8. The ultrasonic device did not have a cooling assembly, and the purging gas was injected thru the tip of the ultrasonic probe. The ultrasonic probe was 1″ (2.5 cm) in diameter, and both the probe and tip (as a single part) were constructed of a niobium alloy containing hafnium and titanium.



FIG. 6 illustrates a plot of hydrogen concentration in mL of hydrogen per 100 g of the aluminum alloy as a function of time after the addition of the argon purging gas (and the activation of the ultrasonic device, if used). FIG. 6 demonstrates the each of Examples 5-7 degassed hydrogen from aluminum significantly faster (using a purging gas and an ultrasonic device) than that of Example 8, which only used a purging gas, but no ultrasonic device. Examples 6-7 performed slightly better than Example 5, which used a lower ultrasonic vibration amplitude and a lower baseline power level for the ultrasonic power supply.


Examples 9-10

Examples 9-10 were large scale trials to determine the effectiveness of using a purging gas and an ultrasonic device to remove hydrogen and lithium/sodium impurities in a continuous casting experiment using aluminum alloy 5154 (containing magnesium). The temperature of the metal bath was maintained at a temperature of about 1350° F. (732° C.).


Sodium and lithium concentrations in weight percent were determined using a spectrometer, and hydrogen concentrations were determined using an Alscan hydrogen analyzer for molten aluminum. Example 9 was a control experiment, and the prevailing sodium and lithium concentrations in the molten aluminum alloy of Example 9 were 0.00083% (8.3 ppm) and 0.00036% (3.6 ppm), respectively. The hydrogen concentration in Example 9 was 0.41 mL/100 g.


The ultrasonic device of Examples 5-8 was used in Example 10 and operated at 20,000 Hz. In conjunction with the operation of the ultrasonic device, in Example 10, argon gas was added to the molten metal bath at a volumetric flow rate of about 80-85 mL/hr per kg/hr of molten metal output (i.e., 80-85 mL purging gas/kg molten metal). After the use of the ultrasonic device and the argon purging gas, the sodium concentration in the molten aluminum alloy was below the minimum detection limit of 0.0001% (1 ppm), and the lithium concentration in the molten aluminum alloy was 0.0003% (3 ppm). The hydrogen concentration in Example 10 was 0.35 mL/100 g, a reduction of about 15%.

Claims
  • 1. An ultrasonic device comprising: an ultrasonic transducer,an elongated probe comprising a first end and a second end, the first end attached to the ultrasonic transducer and the second end comprising a tip, wherein the elongated probe comprises a ceramic;a purging gas delivery system, wherein the purging gas delivery system comprises a purging gas inlet and a purging gas outlet, wherein the purging gas outlet is at the tip of the elongated probe; anda booster between the ultrasonic transducer and the elongated probe, wherein the purging gas inlet is in the booster.
  • 2. The ultrasonic device of claim 1, wherein the ceramic is a Sialon.
  • 3. The ultrasonic device of claim 2, wherein the elongated probe is a unitary part.
  • 4. The ultrasonic device of claim 1, wherein the ceramic is silicon carbide.
  • 5. The ultrasonic device of claim 4, wherein the elongated probe is a unitary part.
  • 6. The ultrasonic device of claim 1, wherein the tip of the elongated probe comprises a ceramic.
  • 7. The ultrasonic device of claim 6, wherein the ceramic is a Sialon.
  • 8. The ultrasonic device of claim 1, wherein the ultrasonic device comprises two or more elongated probes.
  • 9. The ultrasonic device of claim 1, wherein the elongated probe is generally cylindrical and the ceramic is silicon carbide.
  • 10. The ultrasonic device of claim 1, wherein the elongated probe is a unitary part.
  • 11. The ultrasonic device of claim 1, wherein the purging gas delivery system is capable of a volumetric flow rate in a range from about 0.1 to about 150 L/min.
  • 12. The ultrasonic device of claim 1, wherein the purging gas delivery system comprises a purging gas delivery channel in the elongated probe.
  • 13. The ultrasonic device of claim 1, further comprising a cooling system surrounding at least a portion of the elongated probe.
  • 14. The ultrasonic device of claim 13, wherein the cooling system comprises channels for a cooling fluid.
  • 15. An ultrasonic device comprising: an ultrasonic transducer,a unitary, generally cylindrical, elongated probe comprising a first end and a second end, the first end attached to the ultrasonic transducer and the second end comprising a tip, wherein the elongated probe comprises a Sialon;a purging gas delivery system, wherein the purging gas delivery system comprises a purging gas inlet and a purging gas outlet, wherein the purging gas outlet is at the tip of the elongated probe; anda booster between the ultrasonic transducer and the elongated probe, wherein the purging gas inlet is in the booster.
  • 16. The ultrasonic device of claim 15, wherein the purging gas delivery system comprises a purging gas delivery channel in the elongated probe.
  • 17. The ultrasonic device of claim 15, wherein the purging gas delivery system is capable of a volumetric flow rate in a range from about 0.1 to about 150 L/min.
REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. patent application Ser. No. 13/082,437, filed on Apr. 8, 2011, now U.S. Pat. No. 8,574,336, which claims the benefit of U.S. Provisional Application Ser. No. 61/322,324, filed on Apr. 9, 2010, the disclosures of which are incorporated herein by reference in their entirety.

US Referenced Citations (120)
Number Name Date Kind
2820263 Fruengel Jan 1958 A
3177084 Amstein Apr 1961 A
3162908 De Luca Dec 1964 A
3193889 Lane et al. Jul 1965 A
3270376 Thalmann Sep 1966 A
3276082 Thomas Oct 1966 A
3286312 Davis et al. Nov 1966 A
3434823 Adamec Mar 1969 A
3459255 Kolle Aug 1969 A
3495104 Burgo et al. Feb 1970 A
3521849 Voss et al. Jul 1970 A
3633898 Josefsson et al. Jan 1972 A
3709722 Corrigan et al. Jan 1973 A
3734480 Zanis et al. May 1973 A
3794102 Binder Feb 1974 A
3848847 Komatsu et al. Nov 1974 A
3858640 Sifferlen Jan 1975 A
3872913 Lohikoski Mar 1975 A
3900947 Diepers et al. Aug 1975 A
3973750 Rabinovitch et al. Aug 1976 A
3990498 Dompas et al. Nov 1976 A
4074152 Asai et al. Feb 1978 A
4175609 El Gammal et al. Nov 1979 A
4287755 Mansfield Sep 1981 A
4316734 Spinosa et al. Feb 1982 A
4426244 Wang Jan 1984 A
4485179 Brennan et al. Nov 1984 A
4564059 Dobatkin et al. Jan 1986 A
4573521 Artz et al. Mar 1986 A
4582117 Kushnick Apr 1986 A
4589468 Misera et al. May 1986 A
4662427 Larrecq et al. May 1987 A
4662431 Lowry et al. May 1987 A
4699636 Bofinger et al. Oct 1987 A
4770699 Mountford Sep 1988 A
4802436 Wilson et al. Feb 1989 A
5186236 Gabathuler et al. Feb 1993 A
5198187 Lu et al. Mar 1993 A
5281251 Kenny et al. Jan 1994 A
5333844 Holcombe et al. Aug 1994 A
5334236 Sang et al. Aug 1994 A
5340379 Tremblay et al. Aug 1994 A
5355935 Nogues Oct 1994 A
5372634 Monahan Dec 1994 A
5443892 Holcombe et al. Aug 1995 A
5527381 Waite et al. Jun 1996 A
5604301 Mountford et al. Feb 1997 A
5626179 Choudhury et al. May 1997 A
5656236 Waite et al. Aug 1997 A
5660614 Waite et al. Aug 1997 A
5803948 Sizov et al. Sep 1998 A
5810037 Sasaki et al. Sep 1998 A
5934900 Billings Aug 1999 A
5950706 Choudhury et al. Sep 1999 A
5983978 Vining et al. Nov 1999 A
6095957 Ichino et al. Aug 2000 A
6132532 Shepelev et al. Oct 2000 A
6177755 Hur Jan 2001 B1
6253831 Genma et al. Jul 2001 B1
6277224 Muesch et al. Aug 2001 B1
6336495 McCullough et al. Jan 2002 B1
6604941 Billings Aug 2003 B2
6629557 Blucher et al. Oct 2003 B2
6676381 Subramanian et al. Jan 2004 B2
6705385 Ray et al. Mar 2004 B2
6776214 Ray et al. Aug 2004 B2
6799626 Ray et al. Oct 2004 B2
6811602 Beppu et al. Nov 2004 B2
7036556 Caputo et al. May 2006 B2
7131308 McCullough et al. Nov 2006 B2
7164096 Gordon et al. Jan 2007 B1
7297238 Nayar et al. Nov 2007 B2
7485198 Michaluk Feb 2009 B2
7540995 Furst et al. Jun 2009 B2
7582133 Kelly et al. Sep 2009 B2
7651731 Miranda Jan 2010 B2
7682556 Han et al. Mar 2010 B2
7731823 Nayar et al. Jun 2010 B2
7744729 Nayar et al. Jun 2010 B2
7790101 Kelly et al. Sep 2010 B2
7802613 Bullied et al. Sep 2010 B2
7820249 Nayar et al. Oct 2010 B2
7837811 Motegi et al. Nov 2010 B2
8236231 Ferguson et al. Aug 2012 B2
8574336 Rundquist et al. Nov 2013 B2
8652397 Rundquist Feb 2014 B2
8844897 Rundquist et al. Sep 2014 B2
9327347 Rundquist et al. May 2016 B2
9382598 Rundquist et al. Jul 2016 B2
20020083740 Pandelisev Jul 2002 A1
20030234173 Minter Dec 2003 A1
20040055735 Hong et al. Mar 2004 A1
20040190733 Nayar et al. Sep 2004 A1
20040211540 Hong et al. Oct 2004 A1
20060024490 Werner et al. Feb 2006 A1
20060127577 Miranda et al. Jun 2006 A1
20060180293 Maehara Aug 2006 A1
20070235159 Han et al. Oct 2007 A1
20080011442 Pankl Jan 2008 A1
20080156147 Kelly et al. Jul 2008 A1
20080156453 Kelly et al. Jul 2008 A1
20080196550 Abe et al. Aug 2008 A1
20080250863 Moore Oct 2008 A1
20090068434 Michaluk Mar 2009 A1
20090224443 Rundquist et al. Sep 2009 A1
20090314390 Gigliotti, Jr. et al. Dec 2009 A1
20100264095 Hadfield et al. Oct 2010 A1
20110030914 Farina Feb 2011 A1
20110036467 Stebbing Feb 2011 A1
20110247456 Rundquist et al. Oct 2011 A1
20110303866 Li et al. Dec 2011 A1
20120042751 Rundquist et al. Feb 2012 A1
20120168040 Furukawa et al. Jul 2012 A1
20120237395 Jarry Sep 2012 A1
20130098208 Li et al. Apr 2013 A1
20130156637 Park et al. Jun 2013 A1
20140008848 Rundquist Jan 2014 A1
20140123812 Rundquist May 2014 A1
20140352908 Rundquist et al. Dec 2014 A1
20150135901 Rundquist May 2015 A1
Foreign Referenced Citations (65)
Number Date Country
101435064 May 2009 CN
101722288 Jun 2010 CN
101775518 Jul 2010 CN
101829777 Sep 2010 CN
201702337 Jan 2011 CN
2104843 Aug 1972 DE
3905829 Apr 1990 DE
0 583 124 Feb 1994 EP
0 931 607 Jul 1999 EP
1 050 347 Nov 2000 EP
1 060 798 Dec 2000 EP
1 250 972 Oct 2002 EP
1 405 679 Apr 2004 EP
2 257 390 Jan 2012 EP
2 452 763 May 2012 EP
1 373 768 Oct 1964 FR
2 323 988 Aug 1997 FR
1 515 933 Jun 1978 GB
61-46368 Mar 1986 JP
S6186058 May 1986 JP
S62259644 Nov 1987 JP
S62270252 Nov 1987 JP
S63140744 Jun 1988 JP
S63160752 Jul 1988 JP
S63295061 Dec 1988 JP
1-127624 May 1989 JP
2-250745 Oct 1990 JP
H0381047 Apr 1991 JP
H062056 Jan 1994 JP
H0741876 Feb 1995 JP
H0797681 Nov 1995 JP
4-110057 Apr 1996 JP
8-107899 Apr 1996 JP
1997-9-508441 Aug 1997 JP
H1192514 Apr 1999 JP
1-1254095 Sep 1999 JP
05-318034 Dec 1999 JP
2000-342597 Dec 2000 JP
00-77486 Sep 2001 JP
03-181378 Jul 2003 JP
03-266378 Sep 2003 JP
2003-326356 Nov 2003 JP
3 555 485 May 2004 JP
2004-209487 Jul 2004 JP
2005-103552 Apr 2005 JP
2005-199253 Jul 2005 JP
2006-102807 Apr 2006 JP
2006-522562 Sep 2006 JP
2006-320945 Nov 2006 JP
4 594 336 Jul 2008 JP
4 551 995 Jul 2010 JP
2010-247179 Nov 2010 JP
4 984 049 May 2012 JP
5 051 636 Aug 2012 JP
100660223 Dec 2006 KR
20110138897 Dec 2011 KR
WO 8606749 Nov 1986 WO
WO 9727005 Jan 1997 WO
WO 0044959 Aug 2000 WO
WO 0136695 May 2001 WO
WO 2005052207 Jun 2005 WO
WO 2009111536 Sep 2009 WO
WO 2011127402 Oct 2011 WO
WO 2012054478 Apr 2012 WO
WO 2013007891 Jan 2013 WO
Non-Patent Literature Citations (35)
Entry
U.S. Office Action dated Mar. 27, 2014 cited in U.S. Appl. No. 12/397,534. 14 pgs.
Notice of Allowance dated Jun. 5, 2014 cited in U.S. Appl. No. 12/397,534.
Chinese Office Action dated May 6, 2014 in Chinese Application Serial No. 2014043001007870, 3 pages.
Chinese Office Action dated Sep. 13, 2013 in Chinese Application Serial No. 201180028126.4 2 pages.
U.S. Office Action dated Dec. 5, 2013 cited in U.S. Appl. No. 12/397,534. 20 pages.
Chinese Office Action dated May 26, 2014 in Chinese Application Serial No. 201180028126.4, 7 pages.
Chinese Rejection Decision Action dated Dec. 3, 2014 in Chinese Application Serial No. 201180028126.4, 21 pages.
Chinese Second Office Action dated Jan. 14, 2015 in Chinese Application Serial No. 20131003696.9, 8 pages.
Notice of Allowance dated Oct. 15, 2013 cited in U.S. Appl. No. 13/270,401, 12 pages.
U.S. Office Action dated Aug. 10, 2010 cited in U.S. Appl. No. 12/397,534.
U.S. Final Office Action dated Mar. 14, 2011 cited in U.S. Appl. No. 12/397,534.
U.S. Office Action dated Oct. 7, 2011 cited in U.S. Appl. No. 12/397,534.
U.S. Office Action dated Apr. 5, 2012 cited in U.S. Appl. No. 12/397,534.
U.S. Office Action dated Aug. 2, 2012 cited in U.S. Appl. No. 12/397,534.
U.S Office (Advisory) Action dated Oct. 9, 2012 in U.S. Appl. No. 12/397,534, 4 pages.
U.S. Office Action dated Jun. 27, 2013 cited in U.S. Appl. No. 13/270,401, 28 pages.
European Search Report dated Apr. 13, 2012 cited in Application No. 11195036.6-2212.
International Search Report dated Aug. 17, 2011 cited in Application No. PCT/US2011/031781.
European Communication dated Feb. 9, 2011 cited in Application No. 09 718 430.3-2213, 5 pages.
International Search Report and Written Opinion dated Sep. 24, 2009 cited in Application No. PCT/US2009/035983, 16 pages.
Metals Handbook, American Society of Metals, Sep. 1992, pp. 1.44-1.53.
Conduction: The Physics Hypertext book, http://physics.infor/conduction, 1998, pp. 1-3.
Partial International Search Report dated Jul. 8, 2009 cited in Application No. PCT/US2009/035983, 6 pages.
Shimada et al., Article entitled “A Kinetic Study on Oxidation of Niobium Carbide,” published in the 1993 Elsevier Science Publishers B.V., Solid State Ionics 63-65 (1993) pp. 312-317.
Ohsawa, et al., Article entitled “Effects of Ultrasonic Vibration on Solidification Structures of Cast Iron” (1995) pp. 325-330.
Osawa et al., Paper entitled “Refining of Graphite Particles in Cast Irons by Applying Ultrasonic Vibration to Their Melts,” National Research Institute for Metal, Japan, Processing and Fabrication of Advanced Materials VI, The Institute of Materials 1998, pp. 15-22.
Abramov, O. V., entitled “Ultrasound in Liquid and Solid Metals,” Ultrasonics Research and Development, The Institute of General and Inorganic Chemistry, Russian Academy of Sciences, Moscow, Russia (1994), cover, index and pp. 30-34.
Notification for the Grant of Inventor Patent Right and the Notification for Completion of Formalities for Registration dated Nov. 5, 2012, 4 pages.
Shimada et al, entitled “A Kinetic Study on Oxidation of Niobium Carbide,” 1993 Elsevier Science Publishers B.V., Solid State Ionics 63-65 (1993) pp. 312-317.
U.S. Office Action dated Feb. 28, 2013 cited in U.S. Appl. No. 13/082,437, 27 pages.
Notice of Allowance dated Jun. 13, 2013 cited in U.S. Appl. No. 13/082,437, 7 pages.
International Search Report dated Aug. 30, 2013 cited in Application No. PCT/US2012/059529, 14 pages.
Partial International Search Report dated Mar. 2, 2015, cited in Application No. PCT/US2014/065912.
International Search Report dated Jun. 16, 2015 in Application No. PCT/US2014/065912, 13 pages.
Bao, Sarina, “Filtration of Aluminum—Experiments, Wetting, and Modelling”; Trondheim, Oct. 2011, Norwegian University of Science and Technology; NTNU—Trondheim; 218 pages.
Related Publications (1)
Number Date Country
20140008848 A1 Jan 2014 US
Provisional Applications (1)
Number Date Country
61322324 Apr 2010 US
Divisions (1)
Number Date Country
Parent 13082437 Apr 2011 US
Child 14024932 US