The present invention relates to particle coating and in particular to devices and methods for ultraviolet coating of particles.
Conventional liquid spray particle coating processes are commonly known to be prone to agglomeration due to the prolonged period of time needed to convert coated liquid to a tack free solid, even when the uncoated particles can be well separated in the suspension stage. In addition, the common use of a solvent or nonsolvent in conventional particle coating processes poses environmental, health and cost concerns. Thus there is a need for a particle coating process that reduces or eliminates agglomeration. It would also be beneficial to the environment, cost effective and reduce health risks to provide a particle coating process that is solvent-free.
Novel particle coating processes and systems in accordance with the present invention take advantages of the ability of UV-curable materials to form tack-free surfaces rapidly. By applying UV curable compositions on well suspended particles the present inventors have found that the UV particle coating technology enables a scalable process of coating fine particles at desirable coating thicknesses with a wide spectrum of obtainable properties. Processes in accordance with the present invention completely decouple the particle suspension and film formation steps, enabling ample time to first deliver evenly the coating materials to the particle surfaces, followed by rapid polymerization/curing reaction induced by the UV light to rapidly create tack-free surfaces, thus preventing particles agglomeration while achieving uniform and thin-layer coating. Solventless UV coating processes in accordance with the present invention are considered to be an environmental friendly process since they typically operate at room temperature with very high transfer efficiency. Unlike conventional coating technologies, no heating is required to either evaporate a carrier solvent or cross-link a coating. This is a significant advantage in the coating of heat-sensitive substrates. Final coating performance, such as barrier properties, solubility, permeability, flexibility, chemical resistance, hardness, and sensitivity to stimuli can also be readily tuned to appropriate needs by adjusting the UV chemistry and UV radiation exposure. This technology is readily adoptable to provide functional coatings in various applications including munitions constituents, chemicals, food, pharmaceutical and agricultural industrial sectors.
In accordance with at least one aspect of the present invention a process of coating particles is provided comprising essentially the steps of introducing a UV curable liquid onto a suspended particle, followed by UV curing. Essentially, after a selected amount of UV-curable liquid is coated on the particle surfaces, the coated UV liquid is converted to solid coatings when exposed to a UV source.
In at least one embodiment a process in accordance with the present invention is free or essentially free of solvent.
In accordance with at least one aspect a particle suspension step can be achieved by conventional dry particle coating devices such as but not limited to fluidized coaters, drum coaters, or tumbling coaters equipped with liquid spray capabilities. In one embodiment a system in accordance with the present invention employs vacuum applied in a closed system coater such as a drum or tumbling coater.
According to at least one aspect suspension media, depending on a specific application, include but are not limited to air, nitrogen, carbon dioxide or any other gases or combination thereof known to be appropriate to those having skill in the art. In one embodiment, non-oxygen containing media is preferred due to the potential of oxygen to inhibit UV polymerization reactions and safety considerations.
UV-curable materials contemplated by the present invention include but are not limited to free radical systems or ionic systems. UV liquids in accordance with the present invention typically consist of oligomers, photoinitiators, reactive diluents, and fillers or additives. In free radical systems the curable materials polymerize and cure only when exposed to UV radiation. Suitable UV curable monomers include aliphatic urethane acrylate, aromatic urethane acrylate, polyester acrylate, epoxy acrylate, ether acrylate and amine modified ether acrylate. Reactive diluents in accordance with the present invention include mono or multi-functional acrylates. Acceptable photo initiators include α-hydroxylketone, α-aminoketone, mono acyl phosphine and bis acyl phosphine.
In ionic systems, once initiated, polymerization and curing will advance even without exposure to UV radiation. Suitable cationic curable materials include monocycloaliphatic epoxides and biscycloaliphatic epoxides. Examples of suitable co-monomers are vinyl ethers. Suitable photo initiators include diaryliodonium salts and triarylsulfonium salts.
The wavelength of UV light employed is in the range of about 200 to about 400 nm.
It is an object of the present invention to provide novel particle coating techniques employing a UV curing step.
It is a further object of the present invention to permit the coating of particles without the use of solvents.
It is another object of the present invention to provide a process for particle coating that reduces agglomeration.
It is a further object of the present invention to provide novel, versatile and cost effective processes for coating components with UV curable polymeric materials.
It is still a further object of the present invention to provide devices capable of coating particles in accordance with processes disclosed herein.
Other aspects, features, advantages, etc. will become apparent to one skilled in the art when the description of the preferred embodiments of the invention herein is taken in conjunction with the accompanying drawings.
For the purposes of illustrating the various aspects of the invention, there are shown in the drawings forms that are presently preferred, it being understood, however, that the invention is not limited to the precise arrangements and instrumentalities shown.
In the following description, for purposes of explanation, specific numbers, materials and configurations are set forth in order to provide a thorough understanding of the invention. It will be apparent, however, to one having ordinary skill in the art that the invention may be practiced without these specific details. In some instances, well-known features may be omitted or simplified so as not to obscure the present invention. Furthermore, reference in the specification to phrases such as “one embodiment” or “an embodiment” means that a particular feature, structure or characteristic described in connection with the embodiment is included in at least one embodiment of the invention. The appearances of phrases such as “in one embodiment” in various places in the specification are not necessarily all referring to the same embodiment.
Now referring to
In an alternate embodiment, a second air flow (not shown) is introduced into the fluidization bed in order to clean the glass window during the coating process.
It will be apparent to those skilled in the art the UV light source 20 may be internal in the coater 10, externally attached to the coater 10 or not connected to the coater 10. In one embodiment as indicated by the arrow in
A process in accordance with the present invention includes suspending particles in a coater 10, feeding a UV curable liquid into the coater 10 and exposing the UV curable liquid to a UV light source for a selected period of time. Now referring to
Alternatively, materials to be coated such as, but not limited to, RDX powders are premixed with UV curable powder in any conventional blender. The mixture is introduced into a coater and exposed to a UV light source. In a preferred embodiment, the blender is heated to about 100° C. to achieve uniform coating.
UV-Curing
UV curable materials employed in the novel processes may be selected from free radical systems or ionic systems. In free radical systems the UV-curable materials polymerize and cure only when exposed to UV radiation. In ionic systems, once initiated, polymerization and curing will advance even without exposure to UV radiation.
Monomers
As will be apparent to those having skill in the art when selecting monomers for a particular system important characteristics to consider include curing speed and viscosity. Optimally, curing speed is high and viscosity low. In addition, as will be apparent to those having skill in the art, properties of importance are adhesion which optimally is excellent, elasticity which should be at least good, hardness which should be fair to good, general barrier properties which should be excellent, and flexibility which should be good to excellent. Acceptable monomers include acrylates with multi functionalities (double bonds), i.e., more than 2 and preferably between 4-6. Suitable UV curable monomers in free radical systems include but are not limited to suitable acrylates such as aliphatic urethane acrylate, aromatic urethane acrylate, polyester acrylate, epoxy acrylate, ether acrylate and amine modified ether acrylate. Suitable commercially available monomers include Laromer® (BASF), Actilane® (Akzo Nobel); aromatic urethane acrylates including Actilane® 130, Actilane® 196, and Laromer® UA 9031V; aliphatic urethane acrylates including Actilane® 251 (Akzo Nobel), Laromer® LR 8987, Laromer® UA 9029V; epoxy acrylates including Actilane®300HV, Actilane® 340, Laromer® LR 9019 & LR 9023; polyester acrylates including Actilane® 500 series, Laromer® LR 8981, Laromer® PE 56F; and amine acrylates including Actilane® 765, Laromer® LR 8812, Laromer® LR 8889 and Laromer® LR 8869.
In addition to the monomers mentioned above, the following monomers can be polymerized by an ionic based photocatalyst: multi-functional vinyl ethers, multi-functional epoxides, hybrids of vinyl ether and epoxide ans cyclic monomers such as cyclic sulfides, cyclic ethers, cyclic amines and trioxane.
Photocatalysts (Liquids or Solids)
As will be apparent to the skilled artisan characteristics under consideration when selecting an appropriate photocatalyst or photoinitiator include solubility (preferably high), catalytic efficiency (preferably high), tendency toward poisoning by oxygen (preferably none to low), thermal stability (preferably high), toxicity (preferably low) and quantum yield (preferably high).
Examples of free radical based photocatalysts include α-hydroxyl ketone, monoacyl phosphine (MAPO), bis acyl phosphine (BAPO), and mixtures of α-hydroxyl ketone/BAPO, preferably in proportions ranging from about 5:95 to about 20:80 by weight. Suitable commercially available free radical based photocatalysts include Irgacure® 2959, Irgacure® 819, Irgacure® 2005 & 2010 & 2020 (Ciba), Lucirin® LR 8953, Lucirin® LR TPO (BASF), Darocure® 1173 and SR 1129 (Sartomer). Preferably, free radical based photocatalysts comprise less than about 10 parts, preferably between 1-3 parts by weight of a UV curable composition.
Examples of ionic based photocatalysts include iodonium salts such as diphenyliodium salts; sulfonium salts bearing at least one aromatic or other resonance stabilizing chromophore, such as triphenylsulfonium salts, trialkylsulfonium salts and dialkyophenacylsulfonium salts; and ferrocenium salts. Preferably, ionic based photocatalysts comprise less than about 10 parts, preferably between 1-3 parts by weight of a UV curable composition.
Reactive Diluents
As will be apparent to the skilled artisan characteristics under consideration when selecting an appropriate reactive diluent include viscosity (preferably low), reactivity (preferably medium to high) and performance enhancement (preferably high). The performance considerations are the same as those for monomers, i.e., adhesion which optimally is excellent, elasticity which should be at least good, hardness which should be fair to good, general barrier properties which should be excellent, and flexibility which should be good to excellent. Suitable commercially available reactive diluents include mono or multi-functional acrylates such as compositions of the Actilane® 400 series. Preferably, reactive diluents comprise less than about 30 parts, preferably less than about 10 parts by weight of a UV curable composition.
Preferably, the surface tack free time in either free radical or ionic systems ranges from a fraction of a second to minutes, most preferably less than about 10 seconds. Complete through cure time can range from a fraction of a second to minutes, most preferably less than 30 seconds. The coating thickness ranges from 1 to 1000 microns, preferably less than 5 microns. Optimum curing temperature ranges from about 20° C. to about 80° C., preferably about 20° C. Appropriate acceptable gas media include air, CO2 and N2, preferably CO2. Coatings made in accordance with the present invention exhibit good adhesion, cost-effectiveness, and a wide range of attainable properties.
The wavelength of UV light employed in both free radical and ionic systems in accordance with the present invention is preferably in the range of from about 200 nm to about 400 nm.
The UV particle coating methods of the present invention permit at least one thin layer of polymeric materials to be evenly coated onto selected particles, while particle agglomeration is kept at a minimum or entirely eliminated. The processes disclosed herein allow the tailoring of coating structures and thickness, which can be achieved by controlling numbers of spray/curing cycles of the same or different UV curable liquids.
The teachings of the present invention are applicable in a broad range of particle sizes. It will be apparent to those skilled in the art that particles ranging in size from about 200 nm to about 500 microns and larger can be coated in accordance with the teachings of the present invention. In one embodiment, methods employed in accordance with the present invention employ particles in the range of from about 10 microns to about 300 microns.
Those skilled in the art will appreciate variables in UV coating processes employing a fluidization bed can be grouped into three categories: fluidization parameters, spraying variables and curing variables. Table 1 summarizes these variables.
*The secondary air flow rate is only a standard operating parameter in a fluidization bed employing a secondary air flow.
Those skilled in the art will also recognize coating processing also depends on the properties of particulates, UV chemicals, and the interaction between them, as listed in Table 2.
Over-deposition of UV-curable materials on a particle surface tends to raise the adhesive force between particles, which has the potential for instabilities in the fluidization process, namely defluidization or quenching, and some degree of agglomeration. In accordance with one embodiment, a multi-step feeding/spraying/curing method of coating particles employing UV-curable material as depicted in
Experiments
A series of particle coating experiments employing a fluidized bed coater equipped with a UV light source were conducted. The equipment used in Experiments I-III was a Mini-Glatt, commercially available from Glatt Air Technology, equipped with a bottom spray modified to include a UV light source and a secondary air flow. Experiments IV and V employed a Glatt Microkit product vessel, which has a smaller diameter than the Mini-Glatt and a round corner at the air entrance, and equipped with a bottom spray, with a UV light source and secondary air flow. The particles employed in each experiment were potassium chloride (KCL) with an average diameter around 284 μm. Experiments were performed under nitrogen.
UV curable liquids available from Jodan Technology, Yorktown Heights, N.Y. were tested for various parameters as set forth in Table 3. Table 4 lists the description of each formulation. UV Intensity employed was 418 mW/cm2.
*Product Number from Jordan Technology
In the experiments that follow, Formulation E98C and E98C-L were selected, considering the viscosity, curing time, and sensitivity to moisture. Experiments I-III used Formulation E98C, and Experiments IV-V used E98C-L.
Experiment I
Table 5 shows the operating conditions in the coater wherein the curing ratio of Formulation E98C was tested in a coating process. Table 6 lists the sampling procedure. The samples were tested at concentration of UV chemicals at 0.93% and 1.64% vol. Thermo-Gravimetric Analysis (TGA) was employed in the sample analysis. As seen in Table 7 it was observed at about half of the UV chemicals were cured, and elongation in curing time helps to increase the ratio of cured materials
Experiment II
Table 8 lists the operating conditions in the process. Table 9 shows the sampling procedure. The UV chemical was Formulation E98C. The air screen was modified with a paper filter, in order to adjust the fluidization behavior.
Now referring to
Experiment III
Table 10 lists the operating conditions and Table 11 lists the sampling procedure. The air temperature was raised to 50° C. in this experiment, instead of 25° C. in Experiment II. The UV chemical amount per shot and the UV exposure time were also adjusted in order to shorten the total processing time.
Confocal Raman Spectroscopy was used to check the curing of UV chemicals, as shown in
Experiment IV
A Microkit product vessel was employed. Table 12 shows operating conditions and Table 13 the sampling procedure. Formulation E98C-L was employed as the UV curable liquid.
Experiment V
The operating conditions were the same as those in Experiment IV except that the fluidization air pressure was increased gradually as coating proceeded in order to achieve stable fluidization, i.e., to counter the effect of any UV chemicals remaining uncured on the particle surface. Table 14 shows operating conditions and Table 15 the sampling procedure. Formulation E98C-L was employed as the UV curable liquid.
Although the invention herein has been described with reference to particular embodiments, it is to be understood that these embodiments are merely illustrative of the principles and applications of the present invention. It is therefore to be understood that numerous modifications may be made to the illustrative embodiments and that other arrangements may be devised without departing from the spirit and scope of the present invention as defined by the appended claims.
This application claims the benefit of U.S. Provisional Patent Application Ser. No. 60/557,479, entitled “ULTRAVIOLET PARTICLE COATING PROCESSES,” filed Mar. 30, 2004, the entire disclosure of which is incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
60557479 | Mar 2004 | US |