The present invention refers to the underlay mat for floor coverings.
The prior art discloses such underlay mats in many embodiments.
They are usually laid on such a substrate as concrete floor or screed before laying the floor covering, e.g. in the form of wooden or plastic floor panels (e.g. laminate) .
By using such mats, it is possible to obtain, in particular, e.g. the levelling of possible substrate irregularities, reduction in sound above the floor cover in the room where the floor is installed and reduction in audible sounds in rooms below the one where the floor is installed.
The characteristic of commonly known underlay mats is that in order to ensure soundproofing, the mats are provided with a layer of less or more elastic, resilient material such as cork or plastics (most frequently foamed), for instance, polyolefins (PO), polyethylene (PE), polyurethane (PU), polystyrene (PS), ethylene vinyl acetate (EVA) etc.
Underlay mats may be used, e.g. as a loosely laid function layer of floor, i.e. without being fixed to the substrate or floor covering. In many cases, it is more preferable to use an underlay mat with gluing between the surface layer of the underlay mat and the bottom layer of the floor covering, which usually translates into an increase in the comfort of walking on the floor. This kind of gluing, however, constitutes a certain cost in the floor production.
Irrespective of the type of the used adhesive, the problem of damaging the flexible, resilient layer by substances evaporating from the adhesive may occur and may have a negative effect on the desirable properties of the mat over time. This type of a negative effect may also be caused by substances evaporating from the floor covering regardless of its material. Another risk for the durability of the floor may be a liquid spilled on the floor, which may, for instance, reach inside the underlay mat.
In order to reduce the problems described above, the prior art proposes underlay mats with a multi-layer design, which is often connected with high material and production costs, non-optimal utility properties and/or use of non-ecological materials.
The aim of this invention is to manufacture an underlay mat enabling the easy installation, which meets high requirements regarding utility properties and durability despite low costs of materials and production, as well as good tolerance by the natural environment.
According to the invention, this task is fulfilled by the underlay mat for floor coverings, which contains:
The underlay mat, which is the subject of the invention, is not expensive in production, and despite this, it guarantees good utility properties at simultaneous good tolerance by the natural environment, in particular, in view of the fact that polystyrene is well suited for recycling.
The mechanical properties of the underlay mat such as drum sound, impact sound, etc. and its thermal properties (e.g. thermal insulation and thermal capacity) are co-determined by the properties of the used foamed polystyrene layer. These properties can be, to a large extent adjusted in a very positive way, e.g. through a selection of process parameters during the production of the polystyrene layer.
In one of the embodiments, the polystyrene layer consists of extruded polystyrene. At the same time, it is preferred to use the closed-cell foam, in particular, the one which is relatively hard and which demonstrates high mechanical load capacity and high resistance to moisture. The high mechanical load capacity translates into the protection of the floor covering against damage resulting from the use of the floor.
In one of the embodiments, the specific weight of the polystyrene layer ranges between 30 and 200 kg/m3, in particular between 100 and 200 kg/m3.
The relatively high density of the polystyrene layer, for instance, higher than 50 kg/m3, and in particular, higher than 80 kg/m3 is the preferred embodiment in view of the mechanical load capacity and an increase in the walking comfort related thereto.
The most preferable thickness of the polystyrene layer is the thickness of at least 1.0 mm, in particular, at least 1.1 mm. In reference to the most frequent examples of application of the mat, the maximum thickness of around 2.0 mm, in particular, maximum 1.8 mm has been determined as the preferred thickness.
In one of the preferred embodiments, the thickness of the polystyrene layer ranges between 1.1 and 1.8 mm.
In one of the embodiments, the thickness of the polystyrene layer constitutes no less than 80%, in particular at least 90% of the total thickness of the underlay mat. On the other hand, it is most frequently preferred that the thickness of the polystyrene layer covers maximum 99% of the total thickness.
It is ideal, if the PET film is provided with the liquid or gas blocking function, so that the polystyrene layer is well protected, e.g. against penetration of harmful substances from the top. Furthermore, the PET film translates into better thermal insulation of the underlay mat, and functions successfully as the load-bearing layer for the applied layer of adhesive.
In one of the embodiments, the PET film was laminated directly from the top side of the polystyrene layer, in another one, it was applied by means of the heat-sealing process, and still in another one, the PET film was glued to the polystyrene layer.
In view of this type of a joint between the PET film and polystyrene, i.e. without further function layers between PET and polystyrene, it turned out to be particularly preferable in the production of a cheap and reliable joint.
In particular, it is possible to apply inexpensive adhesives here, which do not lead to the damage of the PET film or polystyrene layer, i.e. they do not affect the reduction in the durability of the underlay mat.
In the particularly preferred embodiment, the PET film was glued directly on the top side of the polystyrene layer, using the adhesive which was also used to manufacture the layer of adhesive applied onto the PET film.
There is a whole range of adhesives available, which are perfectly fit for gluing both the PET film and polystyrene as well as PET film and other popular materials from which floor coverings are produced.
In the case of the underlay mat, which is the subject of the invention, the layer of adhesive applied onto the PET film, in combination with the removable protective layer applied on the layer of adhesive, translates into an easy installation of the underlay mat. After laying the floor mat and removing the protective layer, the user can easily glue the floor covering (e.g. floor panels) through its application to the mat. Therefore, it is not necessary to use additional adhesive that is suitable for fixing the floor covering.
In the preferred embodiment, owing to the appropriate selection of the adhesive, the layer of the adhesive demonstrates low initial adhesion in relation to popular plastics from which floor coverings such as e.g. PVC (polyvinyl chloride) are manufactured. This allows the correction of the position of an element of the floor covering (e.g. a plastic floor panel) on the underlay mat by the user, after its first application. The performance of such adhesive, which initially holds rather weakly, is strengthened after some time, which ensures good adhesion of the finished floor covering to the underlay mat.
The underlay mat, which is the subject of the invention, is thus particularly well fit for application together with floor coverings, or elements of the covering made of plastics such PVC.
In one of the embodiments, the layer of adhesive is characterised by a mesh immersed in it, which is made from fibres. The mesh can, for instance, be a square mesh. Fibres may contain, in particular, fibres in the form of threads. The fibres may be natural and/or synthetic fibres.
In one of the embodiments, the removable protective layer includes the plastic film and/or layer of paper, e.g. a laminate made from these materials.
In one of the embodiments, the underlay mat has the surface specific weight ranging between 0.25 and 0.5 kg/m2.
The most preferable thickness of the underlay mat is the thickness of at least 1.0 mm, in particular, at least 1.1 mm. In reference to the most frequent examples of application of the mat, the maximum thickness of around 2.2 mm, in particular, maximum 2.0 mm has been determined as the preferred thickness.
In one of the preferred embodiments, the thickness of the underlay mat ranges between 0.8 and 3.0 mm.
Other advantages of the underlay mat, in many cases of applications, include the possibility of laying the polystyrene layer directly on the substrate (e.g. concrete, screed, etc.), even if such substrate demonstrates certain local or isolated irregularities. The multi-layer underlay mats disclosed by the prior art in the form of the layer located at the very bottom often have a special function layer to compensate for any unevenness, e.g. a non-woven layer or a similar one. The application of such layers located at the bottom of the underlay mat involves additional costs. In the case of the underlay mat, which is the subject of the invention, it turned out that the function of levelling out of any insignificant or isolated unevenness, in particular, is perfectly fulfilled by the polystyrene layer. Thus, the application of the special finishing layer from the underside of the underlay mat, e.g. the non-woven layer or similar one, is not necessary in the case of this invention.
In connection with the foregoing, in one of the specific embodiments, the polystyrene layer forms the lowest layer of the underlay mat.
The invention has been described below based on one embodiment in reference to the attached figure. The cross-section of the underlay mat has been presented in
In the presented example, the polystyrene layer (1) consists of extruded polystyrene, often referred to as “XPS”, with a specific weight of around 100 kg/m3 and thickness of around 1.4 mm.
The PET film (2) was laminated directly on the top side of the polystyrene layer by means of a relatively thin layer of adhesive (5) (e.g. acrylic adhesive) 1.
The layer of adhesive (3) applied on the PET film (2) is formed by the same adhesive which was used to generate the layer of adhesive (5).
In order to improve the mechanical load capacity of gluing (not presented in the figure) of the floor veneer by means of the layer of adhesive (3), the layer is characterised by the square fibre mesh immersed in it (3′).
After laying the underlay mat on the substrate, the user can successively remove the protective layer of paper/plastic material (4) from the top side of the underlay mat, lay the elements of the floor covering on it (such as e.g. PVC panels) and glue them at the same time. The top layer of the underlay mat is made from paper, thus it can bear any print without any problem.
| Number | Date | Country | Kind |
|---|---|---|---|
| P.424139 | Jan 2018 | PL | national |