Claims
- 1. A process of preparing a polyaminopolymer which contains functionality comprising the steps of (a) contacting a polyfunctional amine with an ethylenically unsaturated alkylating agent under reaction conditions to form an amine/ethylenically unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound under reaction conditions to form a polyaminopolymer (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality; and crosslinking the polyaminopolymer by either or both: (h), after step (b) and before step (c), contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups under reaction conditions to form a crosslinked polyaminopolymer; or (d), after step (c) raising the pH of the polyaminopolymer having halohyrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight.
- 2. The process of claim 1 wherein the polyaminopolymer is soluble in water.
- 3. The process of claim 2 wherein step (b) additionally comprises contacting the adduct and polyfunctional compound with a saturated polyamine.
- 4. The process of claim 3 wherein the mole ratio of adduct to saturated polyamine is from about 100:0 to about 70:30.
- 5. The process of claim 4 wherein in step (a) the mole ratio of polyfunctional amine to alkylating agent is from about 10:1 to about 1:10.
- 6. The process of claim 2 wherein the alkylating agent is an organic chloride.
- 7. The process of claim 5 wherein the alkylating agent is allyl chloride, allyl bromide, allyl iodide, 1-chloro-3-butene, 2-chloro-3-butene, 1-chloro-4-pentene, 2-chloro-4-pentene, 3-chloro-4-pentene, 1-chloro-2-butene, 1-chloro-2-pentene, 1-chloro-3-pentene, 3,3-dichloropropene, 3,3,3-trichloropropene, 1,3-dichloropropene, 1,2,3-trichloropropene or 1,1,3-trichloropropene.
- 8. The process of claim 2 wherein the polyfunctional amine is an alkanolamine, polyethylene polyamine, polypropylene polyamine, polybutylene polyamine, or hexamethylenediamine.
- 9. The process of claim 8 wherein the polyfunctional amine is diethylenetriamine, bis-2-hydroxyethyl ethylenediamine, triethylenetetraamine, tetraethylenepentamine, pentaethylenehexamine, hexaethyleneheptamine, aminoethylpiperazine, hydroxyethylpiperazine, aminoethylethanolamine, bis(3-aminopropyl)ethylenediamine, bis(3-aminoethyl)-1,3-diaminopropane, n,n-dimethyldiethylenetriamine, tris(2-aminoethyl)amine, polyethyleneimine, branched, a cyclic isomer or congener, of said amines or a polyethylene polyamine having an average molecular wight of from about 200 to about 500.
- 10. The process of claim 9 wherein the polyfunctional amine is diethylenetriamine and the alkylating agent is allyl chloride.
- 11. The process of claim 2 wherein the polyfunctional amine has more than one amine group, independently selected form primary of secondary amine groups, or amine groups which differ in their pK.sub.b 's by at least about 2 units, and at least one amine group is blocked under reaction conditions to form a selective reaction product of the ethylenically unsaturated alkylating agent and an amine group.
- 12. The process of claim 11 wherein the pH is adjusted to from about 4 to about 9 such that the ethylenically unsaturated alkylating agent reacts selectively agent and an amine group.
- 13. The process of claim 11 wherein the preselected amine group is a secondary amine group.
- 14. The process of claim 2 wherein in step (b) the mole ratio of adduct to polyfunctional compound is from about 0.6 to about 1.4.
- 15. The process of claim 14 wherein in step (b) the polyfunctional compound has at least 2 reactive groups which are independently carboxylic acid, carboxylic ester, acyl halide, a, .beta.-ethylenically unsaturated acid, or a,.beta.-ethylenically unsaturated ester groups.
- 16. The process of claim 15 wherein the polyfunctional compound is diglycolic acid or a saturated aliphatic dicarboxylic acid having from about 3 to about 8 carbon atoms.
- 17. The process of claim 15 wherein the polyfunctional compound is adipic acid, succinic acid, oxalic acid, glutaric acid, pimelic acid, suberic acid, azelaic acid, sebacic acid.
- 18. The process of claim 2 wherein in step (c) the equivalents of halogen, hypohalous acid or precursor thereof is from about 90 to about 110 percent of the equivalents of polyaminopolymer.
- 19. The process of claim 17 wherein step (c) comprises contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof at a pH of less than about 3 under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality.
- 20. The process of claim 2 wherein in step (d) the pH is raised to from about 5 to about 8.
- 21. The process of claim 2 comprising an additional step (e) between steps (b) and (c) of lowering the pH of the solution of polyaminopolymer having halohydrin or dihalo functionality to a pH of from about 1 to about 3.
- 22. The process of claim 21 wherein step (e) comprises adding an acid selected from the group consisting of hydrochloric, nitric, sulfuric, formic and perchloric.
- 23. The process of claim 22 wherein the acid is hydrochloric.
- 24. The process of claim 2 comprising an additional step (f) after step (b) of reacting the polyaminopolymer with an alkylating agent under reaction conditions to form quaternary amine groups.
- 25. The process of claim 24 wherein the alkylating agent is methyl iodide, dimethyl carbonate, trimethyloxonium tetrafluoroborate, triethyloxonium tetrafluoroborate, methyltosylate, ethyl tosylate, dimethyl sulfate, diethyl sulfate, ethyl iodide, methyl bromide, ethyl bromide or a mixture thereof.
- 26. The process of claim 2 comprising an additional step (g) after step (b) of reacting the polyaminopolymer with a compound having a quaternary amine group and a group reactive with the polyaminopolymer under reaction conditions to introduce quaternary amine groups onto the polyaminopolymer.
- 27. The process of claim 26 wherein the compound is glycidyltrimethylammonium chloride, (2-bromoethyl)trimethylammonium chloride or bromide, (2-chloroethyl)trimethylammonium chloride.
- 28. The process of claim 1 wherein after step (a) the amine/unsaturated alkylating agent adduct is purified to remove unreacted alkylating agent.
- 29. The process of claim 1 wherein in step (h) the crosslinking agent is an alkyl compound having from 2 to about 6 carbon atoms and at least 2 halogen atoms selected from bromine or chlorine or mixtures thereof.
- 30. The process of claim 29 wherein the crosslinking agent is selected from 1,2-dichloroethane, succinyl chloride, malonyl chloride, 1,3-dichloropropane or 1,3-dibromopropane, 1,3-dibromopropane; 1,2-dibromoethane, succinyl bromide, malonyl bromide, or mixtures thereof.
- 31. The process of claim 29 wherein the crosslinking agent is contacted in an amount sufficient to produce from about 3 to about 18 percent crosslinking based on secondary amine groups in the polymer.
- 32. The process of claim 2 additionally comprising a step (j) drying the resulting polyaminopolymer to less than about 20 percent by weight water.
- 33. The process of claim 32 wherein step (j) comprises heating the polyaminopolymer to about 10 percent by weight water.
- 34. The process of claim 32 additionally comprising a step (k) dissolving the polyaminopolymer in water.
- 35. A water soluble polyaminopolymer prepared by a process comprising the steps of (a) contacting a polyfunctional amine with an ethylenically unsaturated alkylating agent under reaction conditions to form an amine/ethylenically unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound under reaction conditions to form a polyaminopolymer; (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality; and crosslinking the polyaminopolymer by either or both of: (h) after step (b) and before step (c), contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups therefor having at least two functional groups reactive with amine (d), after step (c), raising the pH of the polyaminopolymer having halohydrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight.
- 36. The polyaminopolymer of claim 35 wherein the adduct prepared in step (a) is purified before step (b).
- 37. The polyaminopolymer of claim 36 wherein, in step (b), contacting of the adduct and polyfunctional compound is additionally with a saturated polyamine.
- 38. The polyaminopolymer of claim 35 wherein the alkylating agent is allyl chloride, allyl bromide, allyl iodide, 1-chloro-3-butene, 2-chloro-3-butene, 1-chloro-4-pentene, 2-chloro-4-pentene, 3-chloro-4-pentene, 1-chloro-2-butene, 1-chloro-2-pentene, 1-chloro-3-pentene, 3,3-dichloropropene, 3,3,3-trichloropropene, 1,3-dichloropropene, 1,2,3-tirchloropropene or 1,1,3-trichloropropene and the polyfunctional amine is diethylenetriamine, bis-2-hydroxyethyl ethylenediamine, triethylenetetraamine, tetraethylenepentamine, pentaethylenehexamine, hexaethyleneheptamine, aminoethylpiperazine, hydroxyethylpiperazine, aminoethylethanolamine, bis(3-aminopropyl)ethylenediamine, bis(3-aminoethyl)-1,3-diaminopropane, n,n-dimethyldiethylenetriamine, tris-(2-aminoethyl)amine, polyethyleneimine, a branched or cyclic isomer or congener of said amines, or a polyethylene polyamine having an average molecular weight of from about 200 to about 500.
- 39. The polyaminopolmyer of claim 35 wherein the polyaminopolymer is contacted with hypochlorus acid, and in step (c) contacting is at a pH of less than about 3.
- 40. The polyaminopolymer of claim 39 wherein step (b) additionally comprises contacting the adduct and polyfunctional compound with a saturated polyamine.
- 41. The polyaminopolymer of claim 40 wherein the mole ratio of adduct to saturated polyamine is from about 100:0 to about 70:30.
- 42. The polyaminopolymer of claim 35 wherein the polyfunctional amine has more than one amine group, selected from primary and secondary amine groups and amine groups which differ in their pK.sub.b 's by at least about 2 units, and at least one amine group is blocked under reaction conditions to form a selective reaction product of the ethylenically unsaturated alkylating agent a preselected amine group.
- 43. The polyaminopolymer of claim 35 prepared by a process additionally comprising a step (f) after step (b) of reacting the polyaminopolymer with an alkylating agent under reaction conditions to form quaternary amine groups.
- 44. The polyaminopolymer of claim 43 wherein the alkylating agent is methyl iodide, dimethyl carbonate, trimethyloxonium tetrafluoroborate, triethyloxonium tetrafluoroborate, methyltosylate, ethyl tosylate, diethyl sulfate, dimethyl sulfate, ethyl iodide, methyl bromide, ethyl bromide or mixtures thereof.
- 45. The polyaminopolymer of claim 35 prepared by a process comprising an additional step (g) after step (b) of reacting the polyaminopolymer with a compound having a quaternary amine group and a group reactive with the polyaminopolymer under reaction conditions to introduce quaternary amine groups onto the polyaminopolymer.
- 46. The polyaminopolymer of claim 45 wherein the compound is glycidyltrimethylammonium chloride, (2-bromoethyl)trimethylammonium chloride or bromide, (2-chloroethyl)trimethylammonium chloride.
- 47. The polyaminopolymer of claim 35 prepared by a process additionally comprising a step (j) drying the resulting polyaminopolymer to less than about 20 percent by weight water.
- 48. The polyaminopolymer of claim 47 prepared by a process additionally comprising a step (k) dissolving the polyaminopolymer in water.
CROSS REFERENCE TO A RELATED APPLICATION
This application is a continuation-in-part of application Ser. No. 07/751,035 filed Aug. 28, 1991 which is a continuation-in-part of application Ser. No. 07/568,917 filed Aug. 17, 1990, both abandoned, both of which are incorporated herein in their entirities.
US Referenced Citations (22)
Foreign Referenced Citations (1)
Number |
Date |
Country |
2092150 |
Aug 1982 |
GBX |
Non-Patent Literature Citations (4)
Entry |
Geo. Clifford White, The Handbook of Chlorination, 2nd Edition, p. 152, (1986). |
N. H. Agnew et al., J. Chem. Soc. (London), Sect. C, pp. 203-208 (1966). |
Chemical Abstract 97:56043M (1982). |
S. Hedge, et al., J. Org. Chem. pp. 3148-3150, (1982). |
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
751035 |
Aug 1991 |
|
Parent |
568917 |
Aug 1990 |
|