Urethane foam for use in impregnating cosmetic composition

Abstract

Provided is a polyether-based urethane foam for impregnating a cosmetic composition. The polyether-based urethane foam has excellent touch feel, portability and stability.

Description

FIELD

This disclosure relates to urethane foam for use in impregnating cosmetic composition and a cosmetic including urethane foam.

BACKGROUND

In the old days, cosmetic compositions were used mainly indoors. However, as leisure activities have been generalized recently and modern life styles have been changed correspondingly, cosmetic compositions have been frequently used outdoors. Particularly, in the old days, UV protecting cosmetic compositions were used mostly in summer seasons. However, as modern people enjoy outdoor activities and recognize hazard of UV rays more and more, there is a tendency for UV protecting cosmetic compositions to be used frequently throughout all the seasons besides summer seasons. Therefore, there is an increasing need for cosmetic compositions convenient to use and easy to carry.

Polyester-based urethane foam was developed accidentally by a German technical specialist in the late 1940's during which development of plastics was in the midst. Since such urethane foam is based on polyester, it is also called ester foam. Producing such urethane foam requires no advanced technology. Thus, polyester-based urethane foam has been produced generally and used in various industrial fields, particularly those requiring strong tensile force.

However, polyester-based urethane foam tends to be broken easily under a wet environment. In addition, it has a microcellular structure and low air permeability, and thus shows low cushiony feel, softness and flexibility. As a result, polyester-based urethane foam is not suitable for use in impregnating a cosmetic composition, particularly a liquid cosmetic composition. Under these circumstances, there is an imminent need for developing urethane foam suitable for use in impregnating a cosmetic composition.

Polyester-based urethane foam tends to be brittle under wet environment and has a small cell structure and low air permeability. Thus, polyester-based urethane foam shows low cushioning property, softness and flexibility, so that it is not suitable for impregnation with a cosmetic composition, particularly a liquid cosmetic composition. Therefore, there has been a need for developing urethane foam suitable for impregnation with a cosmetic composition.

SUMMARY OF THE INVENTION

This disclosure is directed to providing urethane foam for use in impregnating a cosmetic composition, the urethane foam being capable of maintaining high stability of the cosmetic composition to be impregnated therein and high post-impregnation stability.

In one general aspect, there is provided polyether-based urethane foam for use in impregnating a cosmetic composition, a cosmetic composition-impregnated polyether-based urethane foam, and a cosmetic including polyether-based urethane foam impregnated with a cosmetic composition. The polyether-based urethane foam disclosed herein maintains high stability even after it is impregnated with a cosmetic composition, shows high durability and excellent filling ability and dischargeability when it is impregnated with a cosmetic composition, and thus is suitable for impregnation with a cosmetic composition. The polyether-based urethane foam disclosed herein enhances the portability and feeling in use of a cosmetic composition.

The polyether-based urethane foam disclosed herein maintains high stability even after carrying out impregnation with a cosmetic composition, and improves portability and touch feel of a cosmetic composition.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a microscopic view of wet polyether-based urethane foam;

FIG. 2 shows a packed make-up product in which a urethane foam impregnated with a W/O type emulsion make-up composition is enclosed;

FIG. 3 is a microscopic view of the urethane foams listed in Table 2, each magnified at 10×0.3;

FIG. 4 is a microscopic view of the urethane foams listed in Table 3, each magnified at 10×0.3; and

FIG. 5 shows photographs of Example 1, Comparative Example 1 and Comparative Example 2 after storing them at 50° C. for 2 hours.

FIGS. 6A-J show ten types of materials each of which is impregnated with 15 g of a cosmetic composition and then stored at 55° C. for 7 days (6A: NBR, 6B: SBR, 6C: NR, 6D: PU-ether, 6E: PU-ester, 6F: flocking, 6G: PE, 6H: EVA, 6I: PO, 6J: PVA);

FIG. 7 is a graph illustrating the time required for impregnation of 15 g of the same cosmetic composition in each of the ten types of materials;

FIG. 8 is a graph illustrating the amount (g) of cosmetic composition discharged when taking the cosmetic composition from each of the ten types of materials impregnated with the same cosmetic composition;

FIG. 9 shows a pact with a built-in urethane foam impregnated with a W/O type emulsified make-up cosmetic composition; and

FIG. 10 is a 3D view illustrating a reticulated structure of a polyether-based urethane foam.

DETAILED DESCRIPTION

In one aspect, there is provided polyether-based urethane foam for use in impregnating a cosmetic composition. In another aspect, the polyether-based urethane foam may function as a carrier in which a cosmetic composition is supported and retained.

As used herein, the term ‘urethane foam’ means a foamed and solidified polyurethane resin, and is also referred to as ‘foamed urethane’.

As used herein, “durability” means a degree of any material to maintain as it is without melting, tearing or swelling when the material is impregnated with a cosmetic composition and stored at a predetermined temperature for a predetermined time. As used herein, “filling ability” means ability of any material to fill a cosmetic composition therein, and may be represented as time required for filling a predetermined amount of cosmetic composition. As used herein. “dischargeability” means an amount of cosmetic composition discharged when taking the cosmetic composition from any material impregnated therewith. When taking the cosmetic composition, the cosmetic composition is required to be discharged in an adequate amount, not too much, but not too little.

According to an embodiment, the urethane foam, particularly polyether-based urethane foam disclosed herein maintains high durability even after it is impregnated with a cosmetic composition, allows easy filling of a cosmetic composition, an discharges an adequate amount of cosmetic composition, as compared to other materials, including acrylonitrile-butadiene rubber (NBR), styrene-butadiene rubber (SBR), natural rubber (NR), PU-PE flocking, polyethylene (PE), ethylene vinyl acetate (EVA), polyolefin (PO) and polyvinyl alcohol (PVA). Thus, the urethane foam disclosed herein is suitable for impregnation with a cosmetic composition.

In one aspect, urethane foam, particularly polyether-based urethane foam is more resistant against humidity as compared to polyester-based urethane foam, and thus shows low brittleness and high stability even under a high-humidity condition and is not broken easily under a high-humidity condition and shows high stability. Particularly, polyether-based urethane foam shows higher durability after being impregnated with a cosmetic composition, as compared to polyester-based urethane foam, and thus is suitable for impregnation with a cosmetic composition. In addition, the polyether-based urethane foam has a larger cellular structure than polyester-based urethane foam, and thus has improved air permeability, cushiony feel/cushioning property, softness and flexibility. Further, the polyether-based urethane foam requires reduced cost for production, and thus has higher cost-efficiency than polyester-based urethane foam.

In one aspect, urethane foam may include dry urethane foam or wet urethane foam. Particularly, wet polyether-based urethane foam has the properties as shown in the following Table 1.

	TABLE 1
	Item
	Pore size	200	μm
	Surface Properties	Hydrophilic
	ASKER DUROMETER HARDNESS	90
	Type C hardness
	Tensile strength	15	kgf/cm2
	Elongation	260%
	Apparent specific gravity (g/cm3)	0.21
	Moisture holding ratio	420%

In general, wet polyether-based urethane foam has a smaller pore size and more dense structure than dry polyether-based urethane foam. While dry polyether-based urethane foam has oleophilic surface properties, wet polyether-based urethane foam has hydrophilic surface properties as a result of wet foaming. Wet polyether-based urethane foam is continuous microporous urethane foam having uniform and high porosity, shows high water/oil absorbability, and produces no particles spontaneously. FIG. 1 is a microscopic view of wet polyether-based urethane foam.

In one aspect, urethane foam may have a quenched or reticulated structure. In another aspect, urethane foam may have a reticulated structure that allows uniform and easy impregnation with a cosmetic composition and provides a high impregnation ratio.

According to still another embodiment, the polyether-based urethane foam is impregnated with cosmetic composition, which is different as compared to a conventional cosmetic applicator (puff or cosmetic sponge). The cosmetic applicator is used when a user applies a cosmetic composition on a skin. Specifically, it is used when a cosmetic is applied to a skin in such a way to touch an applicator with a cosmetic composition on a skin. The cosmetic applicator itself does not contain any cosmetic composition, whereas the impregnation material for cosmetic composition impregnates and stores a cosmetic composition before a user actually uses it (durability and filling property are necessary). When the user actually uses it, a proper amount of cosmetic composition is applied to a cosmetic applicator (discharging property is necessary). The impregnation material for a cosmetic composition of the present invention does not directly contact with a skin, but contains a cosmetic composition, so a certain applicator is necessary. In case of a cosmetic applicator, specifically, a puff, when a cosmetic composition penetrates deep into the inner side of a sponge, the cosmetic composition is not easy to be applied to a user's skin when in use, so the cosmetics should not easily penetrate into the deep portion of the sponge. The cosmetic composition-impregnated foam according to the present invention itself is an impregnation material of a cosmetic composition which has an impregnation function, so it is definitely different from a cosmetic applicator (puff).

FIG. 9 is a view illustrating a product containing an impregnation material for a cosmetic composition with which a cosmetic composition of the present invention is impregnated.

According to still another embodiment, urethane form may have a reticulated structure. In the case of a reticulated structure, it is easy to carry out homogeneous impregnation of urethane foam with a cosmetic composition, thereby providing a higher impregnation ratio.

The reticulated structure urethane foam according to the present invention is formed by an additional process. The reticulated structure is also called a 3D network structure. The reticulated structure is made in a network shape as the balloon-shaped membranes (walls) are reticulated. The reticulated structure has features in that air can penetrate, and liquid can be absorbed and discharged. The “reticulation” is a kind of process for changing to a reticulated structure depending on its application after a foamed structure is made. In case of a sponge foam, the membranes of each pore is broken and reticulated. The reticulation process is shown in FIG. 10. The reticulated structure of the present invention is different from a conventional foamed structure in which cosmetic composition cannot penetrate deep into the inner side having a 3D membrane structure in a sponge. The present invention is also different from the top of the urethane foam support covered by cloth, net, non-woven fabric, etc.

According to still another embodiment, urethane foam may have an open cell structure.

The urethane foam made through a foaming and concreting process has a closed cell or semi-open cell structure. When urethane foam has a closed cell structure, air bubbles may be trapped in urethane so that the urethane foam may not be impregnated with a low-viscosity emulsified cosmetic composition easily. The present invention can provide a complete open cell structure in which only frames remain after the cell surfaces of the foams are reticulated through the reticulation process.

In one aspect, urethane foam may have a density of 1 to 3 pounds per cubic feet (pcf), particularly 1 to 2 pcf. When urethane foam has a density less than 1 pcf, a cosmetic composition may be liberated excessively and thus is not convenient to use. When urethane foam has a density higher than 3 pcf, it is not possible to provide a sufficient number of pores through which a cosmetic composition is impregnated, thereby making it difficult to impregnate a cosmetic composition effectively.

Herein, density may be determined, for example, based on ASTM D3547.

In one aspect, urethane foam may have a pore number of 70 to 120 pores per inch (ppi), particularly 75 to 95 ppi. When urethane foam has a pore number less than 70 ppi, it has low elasticity, provides no comfort in use and has difficulty controlling the flowability of a cosmetic composition. When urethane foam has a pore number greater than 120 ppi, it provides low durability and poor touch feel of a cosmetic composition during use.

As used herein, ‘ppi’ (pore per inch) is a unit expressing the size of a pore, and refers to the number of pores per inch, i.e., pore number shown on a1-inch line in the section of a foam material. As a ppi number increases, pore size decreases. Since such a pore number is determined by visual inspection, recognition of pores depends on condition of pores, approved in different manners by different countries. For example, Visual Counting Methods (ppi check) of Japan, USA and Europe are shown in the following Table 2.

TABLE 2
Visual Counting Methods (ppi check)
Determination
of ppi	Japan	USA	Europe
Method	Count only full cells	Count full cells	Count all cells (all
	(completely shaped	(completely shaped	cells observed
	cells)	cells within the	within the
	corresponding to	designated line and	designated line and
	the designated line	on the boundary)	on the boundary,
	as observed by a	observed by a	regardless of cell
	microscope	microscope; 1.8	shapes) observed
		times of the value	by a microscope; 2
		determined in	times of the value
		Japan	determined in
			Japan

Herein, Visual Counting Method of USA is used to determine ppi. Therefore, the ppi of urethane foam according to an aspect is different by about 30 ppi from the ppi thereof determined by using Visual Counting Method of Japan.

The cell size of the present invention is an average value measured using an optical microscope (NIKON ECLIPSE 80i).

In one aspect, urethane foam before a cosmetic composition is impregnated may have an ASKER hardness of 10 to 70, particularly 20 to 60, particularly 35-55, and more particularly 30 to 50 as measured by DUROMETER HARDNESS TESTER (Type F) available from ASKER. When urethane has a hardness less than 10 and is too soft, a cosmetic composition impregnated in the urethane foam may be discharged in an excessively large amount, when taking it with cosmetic tools/utensils used for a make-up composition enclosed in a packed container, for example by nitrile butadiene rubber (NBR) puff, or hands. When urethane foam has a hardness larger than 70 and is too hard, it is difficult to discharge a cosmetic composition from the urethane foam.

In one aspect, urethane foam may have an open cell structure. When urethane foam has a closed cell structure, air bubbles are kept in urethane so that a low-viscosity emulsion type cosmetic composition may not be impregnated therein easily. Thus, urethane foam having an open cell structure may be used specifically.

In one aspect, the cosmetic composition to be impregnated in urethane foam includes a liquid cosmetic composition, particularly an emulsion type cosmetic composition, and more particularly a water in oil (W/O) type or oil in water (O/W) type emulsion cosmetic composition.

According to an embodiment, the cosmetic composition applicable to the urethane foam for impregnation may be a liquid cosmetic composition, particularly an emulsified cosmetic composition, and more particularly a water in oil (W/O) type or oil in water (O/W) type emulsified cosmetic composition.

In one aspect, the emulsion cosmetic composition may have a low viscosity, particularly of 5,000 to 15,000 centipoise (cps), and more particularly of 6,000 to 10,000 cps. When the emulsion cosmetic composition has a viscosity less than 5,000 cps, oil phase/aqueous phase separation occurs right after preparing the emulsified cosmetic composition. As a result, it is difficult to impregnate urethane foam with such a composition. When an emulsified cosmetic composition has a viscosity higher than 15,000 cps, it provides an undesirable tacky and heavy touch feel during skin application.

According to still another embodiment, the viscosity may be determined by a viscometer. The measured values may include LVDV II+PRO or RVDV III ULTRA, spindle No. 63 or spindle No. 64, speed RPM or 12RM, the values of which are not limited thereto. The viscosity value may vary with systems used for measurement, spindle number, rpm, or the like.

In one aspect, the cosmetic composition includes both a skin care composition and a make-up composition. Particular non-limiting examples of the cosmetic composition may include make-up primer, make-up base, foundation, powder, twin cake, lipstick, lip gloss, eye shadow, eyebrow, concealer, lip liner, blusher, UV protecting agent/UV protector, lotion, cream or essence. More particularly, the cosmetic composition may be formulated into make-up primer, make-up base, liquid or solid foundation, powder, twin cake, lipstick, lip gloss, eye shadow, eyebrow, concealer or blusher, but is not limited thereto.

In one aspect, there is provided a cosmetic product in which polyether-based urethane foam impregnated with a cosmetic composition is enclosed. The cosmetic product includes a cosmetic composition applied to the polyether-based urethane foam disclosed herein, and thus allows high-quality packing of the cosmetic composition. Therefore, the cosmetic allows good packing of a cosmetic composition, supports a cosmetic composition homogeneously for a long time, enables an adequate amount of cosmetic composition to be discharged therefrom when taking the cosmetic composition, and maintains high durability and stability for a long time. In still another aspect, the cosmetic may be provided as a cosmetic container generally called ‘pact’ in brief and including a container that has a bottom portion in which the polyether-based urethane foam is received, and a top portion as a lid to which a mirror or the like may be attached. Such polyether-based urethane foam provided in a pact container is shown in FIG. 2.

The examples, comparative examples, preparation examples and test examples will now be described to describe the construction and effects of the present disclosure in more detail. The following examples, comparative examples, preparation examples and test examples are for illustrative purposes only and not intended to limit the scope of the present disclosure.

[Test Example 1] Investigation of Characteristics of Materials

To select urethane foam suitable for impregnation with a W/O type or O/W type low-viscosity emulsion cosmetic composition, various types of urethane foam are determined for their properties. The following Tables 3 and 4 show each type of urethane foam and the corresponding properties. In addition, FIG. 3 and FIG. 4 are microscopic views of each type of urethane foam magnified at 10×0.3.

	TABLE 3
	Polyester-based
	urethane foam 1	Polyester-based	Polyester-based
	(conventional	urethane foam 2	urethane foam 3
	urethane foam)	(Q100UT)	(QS100EB)
Pore per	80 ppi	85 ppi	85 ppi
inch (ppi)
Density		1.7	1.7-2.0
(pcf)
Available	Germany	Foamtec(Thailand)	Foamtec(Thailand)
from
Remarks	Flexible	Polyester-	Polyester-
	polyurethane	Polyurethane,	Polyurethane,
	foam	Quenched foam	Reticulated foam
Hardness	45	48

	TABLE 4
	Polyether-based	Polyester-based	Polyester-based
	urethane foam 1	urethane foam 4	urethane foam 5
	(EZ93N)	(ZH100KT)	(ZH100LG)
Pore per	88-100 ppi	90 ppi	90 ppi
inch (ppi)
Density	1.8-2.0	5.4-6.60	5.4-6.60
(pcf)
Available	Foamtec	Foamtec	Foamtec
from	(Thailand)	(Thailand)	(Thailand)
Remarks	Polyether-	Polyester-	Polyester-
	Polyurethane,	Polyurethane,	Polyurethane,
	Reticulated foam	Reticulated foam	Reticulated foam
Hardness	45

In Table 4, Polyether-based urethane foam 1 is dry polyether-based urethane foam.

To select a material suitable for impregnation of a cosmetic composition, the following ten types of materials are provided: acrylonitrile-butadiene rubber (NBR), styrene-butadiene rubber (SBR), natural rubber (NR), polyether-based urethane (PU-ether), polyester-based urethane (PU-ester), PU-PE flocking (flocking), polyethylene (PE), ethylene vinyl acetate (EVA), polyolefin (PO) and polyvinyl alcohol (PVA). Each material has the characteristics as shown in the following Tables 5 and 6.

	TABLE 5
				PU-	PU-
	NBR	SBR	NR	ether	ester
Charac-	Con-	Con-	Con-	Variable	Variable
teristics	trollable	trollable	trollable	pore size	pore size
	pore size,	pore size,	pore size,
	elastic	soft and	soft and
		elastic	elastic
Pore size	70-100 ppi	70-100 ppi	70-100 ppi	88-100 ppi	88-100 ppi

	TABLE 6
	flocking	PE	EVA	PO	PVA
Characteristics	Used for	Moisture-	Light	Open	Uniform and
	cosmetic	resistant,	and soft	cell	continuous open
	puff	highly		structure,	cell structure,
		heat		soft	excellent water-
		insulating			retaining, water-
					absorbing and dust-
					absorbing properties
Pore size	70-90 ppi	80-100 ppi	80-100 ppi	90-110 ppi	70-100 ppi

[Test Example 2] Evaluation of Formulation Stability

Among the different kinds of urethane foam listed in Tables 3 and 4, Polyether-based urethane foam 1 (Example 1), Polyester-based urethane foam 2 (Comparative Example 1) and Polyester-based urethane foam 3 (Comparative Example 2) are selected and subjected to impregnation with a W/0 type emulsion make-up composition. Then, their stabilities are evaluated as a function of storage temperature and time. The results are shown in the following Table 7 and FIG. 5. FIG. 5 shows photographs of Example 1, Comparative Example 1 and Comparative Example 2 after storing them at 50° C. for 2 hours.

	TABLE 7
		45° C.→30° C.→frozen
	55° C.,	at −10° C. (each for 8	30° C.,
	after 7 days	hours), after 5 days	after 7 days
Example 1	Stable	Stable	Stable
Comparative	Urethane foam	Urethane foam	Stable
Example 1	broken	broken
Comparative	Urethane foam	Urethane foam	Stable
Example 2	broken	broken

As can be seen from the above results, when each foam is impregnated with a W/O type emulsion make-up composition, each urethane foam according to Comparative Examples 1 and 2 is broken, causes separation of the make-up composition and generates air bubbles with time under a high temperature or severe change in temperature, and thus is shown to be very unstable. On the contrary, Example 1 substantially maintains its original state and shows high stability.

Therefore, it can be seen that polyether-urethane foam shows higher stability than polyester-based urethane foam upon impregnation with a cosmetic composition, and thus is more suitable for impregnating a cosmetic composition.

The ten types of materials as described in Test Example 1 are selected and classified into two groups having a similar pore size, and are evaluated for durability. The test method will be described in detail hereinafter.

Each material is formed into a circular shape having a size of diameter 48 mm×thickness 10 mm, and is impregnated with 15 g of the same cosmetic composition having a viscosity of 10,000 cps. Then, each material is stored at 55° C. for 7 days and checked for its condition. The results are shown in the following Tables 8 and 9.

TABLE 8
NBR	SBR	NR	PU-ether	PU-ester
Inappropriate,	Easily	Easily	Appropriate,	Melted,
swelled with	torn when	torn when	maintaining	cracked when
cosmetic	pressed	pressed	shape and	pressed
composition	with	with	volume	with
	finger	finger		finger

TABLE 9
flocking	PE	EVA	PO	PVA
Melted,	Good,	Good,	Melted,	Good,
stuck on	maintaining	maintaining	stuck on	maintaining
bottom of	shape and	shape and	bottom of	shape and
container	volume	volume	container	volume

FIGS. 6A-6J show each of the materials after each is impregnated with a cosmetic composition and stored for 7 days (6A: NBR, 6B: SBR, 6C: NR, 6D: PU-ether, 6E: PU-ester, 6F: flocking, 6G: PE, 6H: EVA, 6I: PO, 6J: PVA).

As can be seen from FIGS. 6A-6J, polyether-based urethane foam maintains its shape and volume even after being impregnated with a cosmetic composition, and thus shows the highest durability.

[Test Example 3] Evaluation of Filling Ability

The ten types of materials as described in Test Example 1 are selected and classified into two groups having a similar pore size, and are evaluated for filling ability. Particularly, each material is formed into a circular shape having a size of diameter 48 mm×thickness 10 mm. Then, measured is the time required for each material to be impregnated with 15 g of the same cosmetic composition having a viscosity of 10,000 cps. The results are shown in the following Table 10 and FIG. 7.

TABLE 10
Filling time (sec)
NBR      40
SBR      20
NR       15
PU-ether 5
PU-ester 5
flocking 7
PE       45
EVA      35
PO       40
PVA      30

As can be seen from the above results, polyether-based urethane foam and polyester-based urethane foam have the smallest filling time. This suggests that polyether-based urethane foam and polyester-based urethane foam have the highest cosmetic composition filling ability.

[Test Example 4] Evaluation of Dischargeability

(1) Investigation of Optimum Discharge Amount

First, to investigate the amount of a cosmetic composition suitable as a unit discharge amount, 50 persons are allowed to apply different amounts of cosmetic composition and to evaluate each of the following items from which the optimum amount may be derived by rating it as grade 1 to grade 9 (higher grade represents better quality). The results are shown in the following Table 11. “Applicability” refers to a degree of goodness of skin application amount, “cosmetic effect” refers whether or not the cosmetic composition shows excellent coverage on skin without agglomeration and allows uniform make-up within an adequate time, “comfort” refers to a degree of comfort in use of cosmetic composition without take-up many times while allowing easy control of application amount, and ‘satisfaction” refers to a degree of overall satisfaction.

TABLE 11
Unit
application		Cosmetic
amount (g)	Applicability	effect	Comfort	Satisfaction
0.05	1	1	1	1
0.1	1	1	1	1
0.3	7	5	5	5
0.5	9	9	9	9
0.7	5	5	3	3
0.9	1	3	1	1
1.1	1	1	1	1
1.3	1	1	1	1
1.5	1	1	1	1

As can be seen from the above results, when the unit application amount of a cosmetic composition is 0.3-0.5 g, particularly is about 0.5 g, a high cosmetic effect, comfort and satisfaction are obtained. Therefore, it can be seen that when a cosmetic composition is taken once, 0.3-0.5 g, particularly about 0.5 g is adequate as a unit application amount.

(2) Evaluation of Dischargeability

The ten types of materials as described in Test Example 1 are selected and classified into two groups having a similar pore size, and are evaluated for dischargeability. Particularly, each material is impregnated with 15 g of the same cosmetic composition having a viscosity of 10,000 cps, and the amount (g) of cosmetic composition discharged when taking the cosmetic composition once by using puff. In addition, 50 persons are allowed to apply a cosmetic composition by using the ten types of materials, and to evaluate each of applicability, cosmetic effect, comfort and satisfaction by rating it as grade 1 to grade 9 (higher grade represents better quality). The results are shown in the following Table 12 and FIG. 8.

	TABLE 12
	Discharge		Cosmetic
	amount	Applicability	effect	Comfort	Satisfaction
	(g)	(grade)	(grade)	(grade)	(grade)
NBR	0.83	1	3	1	1
SBR	0.3	5	7	5	5
NR	0.25	3	7	3	3
PU-ether	0.5	9	9	9	9
PU-ester	0.5	9	9	9	9
Flocking	1.2	1	1	1	9
PE	0.2	3	5	3	3
EVA	0.18	3	3	1	3
PO	0.05	1	1	1	1
PVA	0.15	1	1	1	1

[Preparation Examples 1 and 2] Preparation of UV Protecting Cosmetic Composition

In Preparation Examples 1 and 2, W/0 type emulsion UV protecting cosmetic compositions are prepared according to the formulation of the following Table 13.

Particularly, a UV protecting agent is introduced to oily ingredients and dissolved and emulsified therein. Next, the oily ingredients are mixed with a surfactant and heated to and agitated at 80° C. so that the mixture is homogenized. Then, a pigment is further added thereto, followed by agitation and homogenization, to provide an oily part. In a separate mixer, aqueous ingredients are mixed and heated to and agitated at 80° C. to provide a completely dissolved aqueous part. The prepared aqueous part is introduced gradually to the oily part and subjected to emulsification by using a homogenizer mixer. After cooling to 50° C., skin protecting ingredients and fragrances are introduced thereto, followed by cooling, to provide a low-viscosity W/0 type emulsion UV protecting cosmetic composition.

	TABLE 13
		Prep.	Prep.
	Ingredients (wt %)	Ex. 1	Ex. 2
Oily	Oily	Ozokerite	0.1	1.0
Part	Ingredients	Dicaprylyl carbonate	10.00	10.00
	Preservative	Methyl paraben	0.100	0.100
	UV	Octylmethoxy cinnamate	7.000	7.000
	protecting	Isoamyl p-methoxy	2.000	2.000
	agents	cinnamate
	Pigment	Disteardimonium hectorite	0.20	1.50
	Oily	Decamethylcyclopentasilxane	16.00	16.00
	Ingredients
	Emulsifiers	Sorbitan sesquioleate	2.000	2.000
		Lauryl PEG/PPG-18/18	1.500	1.500
		methicon
	Pigments	Polymethyl methacrylate	5.00	5.00
		Titanium dioxide/Aluminum	7.00	7.00
		hydroxide/Stearic acid
Aq.		Water	To 100	To 100
Part	Moisturizer	Glycerin	8.000	8.000
	Emulsion	Sodium chloride	1.00	1.00
	stabilizer
		Fragrance	0.400	0.400
Total	100	100

In Table 13, disteardimonium hectorite functions as a thickening agent, polymethyl methacrylate serves as a pure body pigment, and titanium dioxide/aluminum hydroxide/stearic acid serves as an inorganic UV protecting agent.

[Test Example 3] Evaluation of Preference Depending on Hardness of Urethane Foam

Different types of polyether-based urethane foam having a different value of hardness are impregnated with Preparation Examples 1 and 2, and user preference of each case is determined. Particularly, 50 females are divided into two groups (each group having 25 persons). They are allowed to apply each of Preparation Example 1 and Preparation Example 2 impregnated in polyether-based urethane foam having a different value of hardness to their skin with NBR puff for 2 days. Then, overall user preference including touch feel and coating quality is evaluated in each case. The results are shown in the following Tables 14 and 15.

	TABLE 14
		Hardness of
		urethane foam
	Cosmetic composition	(ASKER hardness,
	used for impregnation	Type F)	Preference (%)
Example 2	Preparation Example 1	5	5
Example 3	Preparation Example 1	80	10
Example 4	Preparation Example 1	40	85

	TABLE 15
		Hardness of
		urethane foam
	Cosmetic composition	(ASKER hardness,
	used for impregnation	Type F)	Preference (%)
Example 5	Preparation Example 2	5	5
Example 6	Preparation Example 2	80	5
Example 7	Preparation Example 2	40	90

As can be seen from the above results, the highest preference is available when polyether-based urethane foam used for impregnation with both compositions according to Preparation Examples 1 and 2 has Asker hardness value of 40.

As can be seen from the above results, polyether-based urethane foam and polyester-based urethane foam show the most adequate discharge amount. In addition, polyether-based urethane foam and polyester-based urethane foam provide excellent applicability, cosmetic effect, comfort and satisfaction. This means that polyether-based urethane foam and polyester-based urethane foam shows the highest cosmetic composition dischargeability.

As can be seen from the foregoing, polyether-based urethane foam having excellent durability, filling ability and dischargeability of a cosmetic composition is suitable for use in impregnation with a cosmetic composition.

Those skilled in the art will appreciate that the conceptions and specific embodiments disclosed in the foregoing description may be readily utilized as a basis for modifying or designing other embodiments for carrying out the same purposes of the present disclosure. Those skilled in the art will also appreciate that such equivalent embodiments do not depart from the spirit and scope of the disclosure as set forth in the appended claims.

Claims

1. A cosmetic product comprising: a polyether-based urethane foam impregnated with a liquid cosmetic composition having a viscosity of 5000 to 15,000 centipoise; anda container in which the polyether-based urethane foam impregnated with the liquid cosmetic composition is stored,wherein the polyether-based urethane foam is configured to release the liquid cosmetic composition to a cosmetic tool that is separate from the polyether-based urethane foam and that tool is for applying the released cosmetic composition to skin,wherein the polyether-based urethane foam has a pore number of 70 to 120 pores per inch, andwherein the polyether-based urethane foam has a density of 1-3 pounds per cubic foot (pcf) as determined by ASTM D3547 before the liquid cosmetic composition is impregnated.

2. The cosmetic product of claim 1, wherein the polyether-based urethane foam has a reticulated structure.

3. The cosmetic product of claim 1, wherein the polyether-based urethane foam has a pore number of 75 to 95 pores per inch.

4. The cosmetic product of claim 1, wherein the polyether-based urethane foam has a hardness of 10-70 as determined by a durometer before the cosmetic composition is impregnated.

5. The cosmetic product of claim 1, wherein the liquid cosmetic composition is a water in oil (W/O) emulsion or an oil in water (O/W) emulsion.

6. The cosmetic product of claim 1, wherein the liquid cosmetic composition is a UV-protecting cosmetic composition.

7. The cosmetic product of claim 1, wherein the cosmetic tool is disposed in the container separately from the polyether-based urethane foam impregnated with the liquid cosmetic composition.

8. The cosmetic product of claim 1, wherein the liquid cosmetic composition is make-up primer, make-up base, foundation, powder, twin cake, lipstick, lip gloss, eye shadow, eye brow, concealer, or blusher.

9. The cosmetic product of claim 1, wherein the polyether-based urethane foam is not broken when the polyether-based urethane foam impregnated with a W/O type liquid cosmetic composition is stored at 55° C. for 7 days.

10. The cosmetic product according to claim 1, wherein the density of the polyether-based urethane foam is 2-3 pcf as determined by ASTM D3547 before the cosmetic composition is impregnated.

11. The cosmetic product according to claim 1, wherein the density of the polyether-based urethane foam is 1-2 pcf as determined by ASTM D3547 before the cosmetic composition is impregnated.

12. The cosmetic product of claim 1, wherein the polyether-based urethane foam has a hardness of 35-55 as determined by a durometer before the cosmetic composition is impregnated.

13. The cosmetic product of claim 1, wherein the polyether-based urethane foam is configured to release 0.3 g to 0.5 g of the liquid cosmetic composition to the cosmetic tool.

14. A method of making the cosmetic product of claim 1 comprising: impregnating a polyether-based urethane foam with a liquid cosmetic composition to form an impregnated polyether-based urethane foam; andstoring the impregnated polyether-based urethane foam in a container separately from a cosmetic tool that is for applying the liquid cosmetic composition released from the impregnated polyether-based urethane foam to skin.

15. A method of applying the liquid cosmetic composition of claim 1 to skin comprising: releasing a liquid cosmetic composition that is impregnated in a polyether-based urethane foam onto a cosmetic tool that is for applying the liquid cosmetic composition released from the impregnated polyether-based urethane foam to skin; andapplying the released liquid cosmetic composition to skin using the cosmetic tool.

16. A cosmetic container comprising: a bottom portion receiving a polyether-based urethane foam impregnated with a liquid cosmetic composition having a viscosity of 5000 to 15,000 centipoise;a cosmetic tool that is separate from the polyether-based urethane foam and is for applying the released cosmetic composition to skin; anda lid portion,wherein the polyether-based urethane foam is configured to release the liquid cosmetic composition to the cosmetic tool,wherein the polyether-based urethane foam has a pore number of 70 to 120 pores per inch, andwherein the polyether-based urethane foam has a density of 1-3 pounds per cubic foot (pcf) as determined by ASTM D3547 before the liquid cosmetic composition is impregnated.

17. The cosmetic container of claim 16, wherein the lid portion comprises a mirror.

18. The cosmetic container of claim 16, wherein the polyether-based urethane foam has a pore number of 75 to 95 pores per inch.

19. The cosmetic container of claim 16, wherein the polyether-based urethane foam has a hardness of 10-70 as determined by a durometer before the cosmetic composition is impregnated.

20. The cosmetic container of claim 16, wherein the polyether-based urethane foam is not broken when the polyether-based urethane foam impregnated with a liquid cosmetic composition is stored at 55° C. for 7 days.

21. The cosmetic container of claim 16, wherein the polyether-based urethane foam has a hardness of 35-55 as determined by a durometer before the cosmetic composition is impregnated.

22. The cosmetic container of claim 16, wherein the polyether-based urethane foam is configured to release 0.3 g to 0.5 g of the liquid cosmetic composition to the cosmetic tool.