This application claims benefit, under U.S.C. §119 or §365 of French Application Number FR 05.05575, filed Jun. 1, 2005; and PCT/FR2006/001233 filed May 31, 2006.
The present invention relates to the use of a composition comprising the combination of a thermosetting resin and a particular polymer for producing composite materials by filament winding.
The present invention also relates to a process for producing parts by filament winding from said composition.
The general field of the invention is therefore that of composite materials.
The composite materials result from the close combination of:
The two components (reinforcement and matrix) have qualities which combine together synergistically.
By varying the nature of the reinforcement and of the matrix, it is thus possible to attain materials having a very great diversity of mechanical and chemical properties.
This is the reason why composite materials find a very large number of applications in numerous fields, such as the aeronautics industry, the automotive industry, the naval industry and the construction industry.
In order to produce composite parts, dozens of techniques are currently known, among which mention may be made, amongst others, of: contact molding, spray-up molding, lay-up molding, low-pressure molding, etc.
In a certain number of cases, especially when it is desired to obtain large hollow parts, it may be advantageous to work directly with wound fibers. These fibers may be used in prepreg form. However, these fibers are expensive and have a limited shelf life, considering the difficulty of keeping these fibers without curing of the resin occurring. This is why it may be advantageous, for producing hollow parts, to use the filament winding technique, which uses, at the outset, dry fibers.
More specifically, the filament winding technique consists in firstly making dry fibers pass into a bath comprising a resin then secondly in winding them onto a mandrel having a shape suitable for the part to be produced. The part thus obtained by winding is cured during a subsequent step, for example by heating.
The difficulty of this technique lies in the step of impregnating the dry fibers. This is because for a satisfactory impregnation, it is necessary that the composition be sufficiently liquid to correctly impregnate the fiber without however causing runs when the fiber exits the bath.
The compositions used to date do not make it possible to avoid this running phenomenon. This phenomenon is responsible for a sizeable loss of composition, inhomogeneous depositions at the surface of the fibers and soiling of the equipment.
There is therefore a real need for compositions that do not have the following drawbacks.
The inventors have surprisingly discovered that by incorporating, into a composition comprising a resin formulation, a polymer having particular rheological characteristics, it was possible to overcome the drawbacks of the compositions of the prior art used to produce parts by filament winding.
Thus, the invention relates, according to a first subject, to the use of a composition for producing parts by filament winding, said composition comprising:
It should be pointed out that, according to the invention, the shear rate C1 results from the traveling speed of the fiber to be impregnated into the bath comprising the composition whereas the high-temperature state corresponds to the temperature in the bath, this temperature generally ranging from 40 to 150° C., for example from 80 to 100° C.
It should be pointed out that the shear rate C2 results from the residual sliding of the composition deposited on the fiber, outside of the composition bath, this rate consequently being much lower than C1, whereas the “low-temperature” state represents the temperature outside of the bath when the fiber is conveyed from the bath to the mandrel.
Due to a large difference in viscosity between the high-temperature state and the low-temperature state of the composition, the run phenomena on exiting the bath with fibers coated with this composition are significantly reduced, as is soiling on the various components of the process. The deposition thus remains uniform over the fibers. This results, after winding of the fibers onto a mandrel and curing, in a uniform distribution of the mechanical and physical properties of the resulting composite material.
Furthermore, due to the fact that the compositions of the invention have a Newtonian character in the “high-temperature” state, that is to say that their viscosity does not vary substantially with the strain rate of the mixture, it is possible to obtain fibers coated in an equivalent manner (that is to say, with an approximately identical amount of composition and a uniform distribution of the composition) regardless of the traveling speed of the fiber in the bath comprising the composition.
Finally, due to the fact that the abovementioned rheological characteristics (viscosity, Newtonian character) are mainly induced by the addition into the solution of the rheology control agent as defined above, this makes it possible to have greater freedom as to the choice of the resin formulation.
Advantageously, the rheology control agent induces a difference in viscosity between the high-temperature state and the low-temperature state of a factor of at least 500, and that does not generally exceed 105, for example for a temperature difference between the high-temperature state and the low-temperature state of at least 60° C.
By way of example, the abovementioned compositions have a viscosity below 1 Pa·s at 100° C. (temperature of the bath of composition) and a viscosity of around 1000 Pa·s at ambient temperature (the ambient temperature corresponding to the temperature of the part onto which the filament winding process takes place).
The rheology control agents may be polymers, for example linear or branched polymers.
In particular, the rheology control agents may be block copolymers, of which at least one of the blocks is incompatible with said resin formulation.
According to one particular embodiment of the invention, the polymers conferring the compositions with the aforementioned rheological characteristics may be block copolymers comprising:
The M block is a polymer miscible with the resin formulation.
M may be a methyl methacrylate homopolymer.
M may also a methyl methacrylate copolymer.
For example, M may be a copolymer of methyl methacrylate and at least one water-soluble monomer.
This copolymer may comprise at least 20 wt % of methyl methacrylate, preferably at least 50 wt % of methyl methacrylate and a water-soluble monomer.
By way of example of water-soluble monomers, mention may be made of acrylic or methacrylic acid, amides derived from these acids such as for example dimethyl-acrylamide, 2-methoxyethyl(meth)acrylate, optionally quaternized 2-aminoethyl(meth)acrylates, polyethylene glycol (PEG) (meth)acrylates, water-soluble vinyl monomers such as N-vinylpyrrolidone or any other monomer that is soluble in water.
Advantageously, the polyethylene glycol group of the polyethylene glycol (meth)acrylates has a mass ranging from 400 g/mol to 10000 g/mol.
Preferably, the water-soluble monomer is dimethyl-acrylamide.
The molar proportion of methyl methacrylate may be from 10 to 95%, preferably from 60 to 90%, per 90 to 5%, preferably per 40 to 10%, of water-soluble monomer.
Moreover, the M block may comprise other monomers, such as reactive or unreactive acrylic or non-acrylic monomers. The expression “reactive monomer” is understood to mean a chemical group capable of reacting with the oxirane functional groups of the epoxy molecules or with the chemical groups of the curing agent.
By way of nonlimiting examples of reactive functional groups mention may be made of: oxirane functional groups, amine functional groups and carboxy functional groups. The reactive monomer may be (meth)acrylic acid or any other hydrolyzable monomer leading to these acids. Among the other monomers which may constitute the M block, mention may be made by way of nonlimiting examples of glycidyl methacrylate or tert-butyl methacrylate and n-butyl acrylate.
The B block is a polymer incompatible with the resin formulation and with the M block. Advantageously, the Tg of B is below 0° C. and preferably below −40° C. The monomer used to synthesize the B block may be a diene chosen from butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 2-phenyl-1,3-butadiene. B is advantageously chosen from polydienes especially polybutadiene, polyisoprene and random copolymers thereof or else from partially or completely hydrogenated polydienes. Among the polybutadienes, those whose Tg is lowest, for example poly(1,4-butadiene) having a Tg (about −90° C.) below that of poly(1,2-butadiene) (about 0° C.), are advantageously used. The B blocks may also be hydrogenated. This hydrogenation is carried out according to standard techniques. The monomer used to synthesize the B block may also be an alkyl (meth)acrylate (in other words, the B block may be a poly(alkyl(meth)acrylate) such as ethyl acrylate (Tg=−24° C.), n-butyl acrylate (Tg=−45° C.), 2-ethylhexyl acrylate (Tg=−60° C.), n-octyl acrylate (Tg=−62° C.), hydroxyethyl acrylate (Tg=−15° C.) and 2-ethylhexyl methacrylate (Tg=−10° C.). Advantageously n-butyl acrylate is used. The acrylates are different than those of the M block in order to respect the condition of B and M being incompatible. Preferably, the B blocks are mainly composed of poly(1,4-butadiene). B is incompatible with the thermosetting resin and with the M block.
According to one particular embodiment, the rheology control agent is an M-B-M triblock copolymer, B and M being blocks such as defined above.
The two M blocks of the M-B-M triblock copolymer may be identical or different. When they are different, they may be different by the nature of the monomers constituting them or different by their molecular weight but composed of the same monomers.
The M-B-M triblock copolymer has a number-average molecular weight which may be between 10 000 g/mol and 500 000 g/mol, preferably between 20 000 and 200 000 g/mol. Advantageously, the M-B-M triblock has the following compositions of M and B, expressed as weight fractions, the total being 100%:
M: between 10% and 80%, preferably between 15 and 70%; and
B: between 90 and 20%, preferably between 85% and 30%.
One particularly suitable M-B-M triblock copolymer is a copolymer in which:
Another particularly suitable M-B-M triblock copolymer is a copolymer in which:
The copolymers used as a rheology control agent may comprise, besides the B and M blocks, an S block incompatible with said resin formulation and the B block.
S is incompatible with the thermosetting resin and with the B block. The Tg or the Tm of S is advantageously above the Tg of B and above 23° C. and preferably above 50° C. By way of examples of S blocks, mention may be made of those which derive from vinylaromatic compounds such as styrene, α-methylstyrene, vinyltoluene, and those which derive from alkyl esters of acrylic and/or methacrylic acids having from 1 to 18 carbon atoms in the alkyl chain.
Preferably, the S block is a polystyrene.
According to one particular embodiment of the invention, the rheology control agent is an S-B-M triblock copolymer, S, B and M being blocks such as defined above.
The S-B-M triblock copolymer has a number-average molecular weight which may be between 10 000 g/mol and 500 000 g/mol, preferably between 20 000 and 200 000 g/mol. Advantageously, the S-B-M triblock copolymer has the following compositions of S, M and B, expressed as a weight fraction, the total being 100%:
M: between 10% and 80%, preferably between 15 and 70%;
B: between 2 and 80% and preferably between 5% and 70%; and
S: between 10 and 88% and preferably between 15 and 85%.
According to the invention, one part of S-B-M may be replaced by an S-B diblock. This part may represent up to 70 wt % of the copolymer.
One particularly suitable S-B-M triblock copolymer is a copolymer comprising:
According to another embodiment of the invention, the polymers that can be used as a rheology control agent and that confer on the compositions containing them the aforementioned rheological characteristics, may be block copolymers comprising:
The S and B blocks may be such as defined above.
In particular, these copolymers may be S-B diblock copolymers, in which:
The compositions used according to the invention comprise a resin formulation consisting of at least one thermosetting resin.
Advantageous thermosetting resins are epoxy resins.
Epoxy resin, denoted hereinafter by E, is understood to mean any organic compound having at least two oxirane-type functional groups, polymerizable by ring opening. The term “epoxy resins” denotes all common epoxy resins that are liquid at ambient temperature (23° C.) or at a higher temperature. These epoxy resins may be monomeric or polymeric on the one hand, aliphatic, cycloaliphatic, heterocyclic or aromatic on the other hand. As examples of such epoxy resins, mention may be of resorcinol diglycidyl ether, bisphenol A diglycidyl ether, triglycidyl p-aminophenol, bromobisphenol F diglycidyl ether, m-aminophenol triglycidyl ether, tetraglycidyl methylene dianiline, (trihydroxy-phenyl)methane triglycidyl ether, phenol-formaldehyde novolac polyglycidyl ethers, ortho-cresol novolac polyglycidyl ethers and tetraphenylethane tetraglycidyl ethers. Mixtures of at least two of these resins may also be used.
Epoxy resins having at least 1.5 oxirane functional groups per molecule and more particularly epoxy resins containing between 2 and 4 oxirane functional groups per molecule are preferred. Epoxy resins having at least one aromatic ring, such as bisphenol A diglycidyl ethers, are also preferred.
The resin formulation generally comprises a curing agent.
Regarding the curing agent, mention may be made of:
It would not be outside the scope of the invention to add some customary additives to the composition, for instance thermoplastics such as polyethersulfones, polysulfones, polyetherimides, polyphenylene ethers, liquid elastomers or core-shell impact modifiers.
The composition of the invention may be prepared by mixing the resin formulation and the rheology control agent by any conventional mixing technique. It is possible to use any thermoplastic technique that makes it possible to produce homogeneous mixing between the two parts of the thermosetting resin and the control agent, such as extrusion.
Regarding the proportion of the resin formulation and of the rheology control agent, the proportion of the agent advantageously ranges from 5 to 20 wt % per 95 to 80 wt % of the resin formulation. Preferably, the content of the agent advantageously ranges from 5 to 15 wt % per 95 to 85 wt % of the resin formulation.
As mentioned above, the compositions described are used for producing parts by filament winding.
Thus, the invention relates, according to a second subject, to a process for producing a part by filament winding that successively comprises:
The rheology control agent is such as defined above.
Thus, according to one particular embodiment of the invention, the rheology control agent may be a block copolymer comprising:
The M and B blocks are such as defined above.
According to another embodiment, the rheology control agent may be a block copolymer comprising:
The B and S blocks are such as defined above.
The fibers intended to constitute the reinforcement of the part may be glass fibers, carbon fibers or else aramid fibers.
Firstly, these fibers are conveyed from an unwinding creel towards an impregnation bath, where they are coated with the composition described above.
Secondly, they are conveyed by a guiding system towards the aforementioned mandrel then deposited on it.
Once the deposition operation is finished, the coated fibers are subjected to a curing step which may take place:
The curing step will especially depend on the nature of the curing agent introduced into the composition.
The composition used according to the invention may be applied for manufacturing parts in a large number of fields. Thus, the invention relates to parts obtained by the aforementioned process, said parts possibly being intended for the aeronautics industry, the naval industry, the construction industry, the manufacture of wind turbines, the manufacture of pipes for the transport of fluids, for example in factories of the chemical industry or for the transport of hydrocarbons.
Finally, the invention relates to a composition for manufacturing parts by filament winding, the composition being such as defined above.
Thus, according to one particular embodiment of the invention, the rheology control agent may be a block copolymer comprising:
The M and B blocks are such as defined above.
According to another embodiment, the rheology control agent may be a block copolymer comprising:
The B and S blocks are such as defined above.
The invention will now be described with respect to the following examples given by way of illustration and nonlimitingly.
In this example, the copolymer used was an SBM triblock copolymer in which:
More precisely, this copolymer had the molecular characteristics:
This copolymer was present in the composition in an amount of 15 wt % relative to the total weight of the composition.
The composition tested comprises, in addition:
The protocol for producing the composition was the following:
This composition was perfectly suitable to be used according to the filament winding process, as illustrated in
Thus, the composition showed a viscosity of 1.5 Pa·s at 80° C. and of 0.4 Pa·s at 100° C. This viscosity range, in this temperature window, was perfectly suitable for coating a carbon or glass fiber according to the filament winding process.
Furthermore, in this temperature window, the mixture had a Newtonian character, that is to say that its viscosity did not vary with the strain rate of the mixture, as illustrated in
This behavior constitutes a significant advantage as, at any traveling speed of the fiber into the bath of product, an equivalent coating will be produced.
Advantageously, this composition also shows a very large change in viscosity with temperature, contrary to the compositions of the prior art which retain a relatively low viscosity on exiting the bath.
It follows that, when the coated fiber exits the bath, run phenomena may occur, which will be the cause of change in the amount of product deposited on the fiber and also possible soiling on the various components of the process.
In the case of the composition of this example, these types of problems will not occur since the viscosity of the composition increases considerably when the temperature drops.
Very advantageously, the rheological behavior of the composition also changes when the temperature drops, having a pseudoplastic character at low temperature. The pseudoplastic character of the composition is expressed by a marked increase in the viscosity, when the shear rate decreases, which is the case for the fiber coated with the composition on exiting the bath, insofar as the shear rate is only due to the actual weight of the composition.
Thus, at 20° C., the composition of this example has a viscosity of more than 1000 Pa·s at a shear stress frequency of 6.28 rad/s.
In this example, the copolymer used was an M-B-M copolymer in which:
More precisely, this copolymer comprised the following molecular characteristics:
This copolymer was present in the composition in an amount of 5 wt % relative to the total weight of the composition.
The composition used comprised, in addition:
The protocol for producing the composition was the following:
This composition was perfectly suitable to be used according to the filament winding process, as illustrated in
Thus, the composition showed a viscosity of 1.8 Pa·s at 80° C. and of 0.6 Pa·s at 100° C. This viscosity range, in this temperature window, was perfectly suitable for coating a carbon or glass fiber according to the filament winding process.
Furthermore, in this temperature window, the mixture had a Newtonian character, that is to say that its viscosity did not vary with the strain rate of the mixture, as illustrated in
This behavior constitutes a significant advantage as, at any traveling speed of the fiber into the bath of product, an equivalent coating will be produced.
Very advantageously, this composition also shows a very large change in viscosity with temperature, contrary to the compositions of the prior art which retain a relatively low viscosity on exiting the bath.
It follows that, when the coated fiber exits the bath, run phenomena may occur, which will be the cause of change in the amount of product deposited on the fiber and also possible soiling on the various components of the process.
In the case of the composition of this example, these types of problems will not occur since the viscosity of the composition increases considerably when the temperature drops and when the rheological behavior of the composition changes, having a pseudoplastic character at low temperature.
The pseudoplastic character of the composition is expressed by a marked increase in the viscosity, when the shear rate decreases, which is precisely the case for the fiber coated with the composition on exiting the bath, insofar as the shear rate is only due to the actual weight of the composition.
At 20° C., the composition of this example has a viscosity of more than 1000 Pa·s at a shear stress frequency of 6.28 rad/s.
In this example, the copolymer used was an M-B-M copolymer in which:
More precisely, this copolymer comprised the following molecular characteristics:
This copolymer was present in the composition in an amount of 10 wt % relative to the total weight of the composition.
The composition used comprised, in addition:
The protocol for producing the composition was the following:
This composition was perfectly suitable to be used according to the filament winding process, as illustrated in
Thus, the composition showed a viscosity of 2.3 Pa·s at 90° C. and of 0.8 Pa·s at 110° C. This viscosity range, in this temperature window, was perfectly suitable for coating a carbon or glass fiber according to the filament winding process.
Furthermore, in this temperature window, the mixture had a Newtonian character, that is to say that its viscosity did not vary with the strain rate of the mixture, as illustrated in
This behavior constitutes a significant advantage as, at any traveling speed of the fiber into the bath of product, an equivalent coating will be produced.
Very advantageously, this composition also shows a very large change in viscosity with temperature, contrary to the compositions of the prior art which retain a relatively low viscosity on exiting the bath.
It follows that, when the coated fiber exits the bath, run phenomena may occur, which will be the cause of change in the amount of product deposited on the fiber and also possible soiling on the various components of the process.
In the case of the composition of this example, these types of problems will not occur since the viscosity of the composition increases considerably when the temperature drops and when the rheological behavior of the composition changes, having a pseudoplastic character at low temperature. The pseudoplastic character of the composition is expressed by a marked increase in the viscosity, when the shear rate decreases, which is the case for the fiber coated with the composition on exiting the bath, insofar as the shear rate is only due to the actual weight of the composition.
At 30° C., the composition of this example has a viscosity of more than 1000 Pa·s at a shear stress frequency of 6.28 rad/s.
Number | Date | Country | Kind |
---|---|---|---|
0505575 | Jun 2005 | FR | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/FR06/01233 | 5/31/2006 | WO | 00 | 5/29/2008 |