The present disclosure relates to the field of materials and optoelectronic functional devices, particularly relates to use of a quaternary molybdenum/tungsten tellurite crystal and a device of the same, and more particularly to use of the same for a high-performance acousto-optic device.
Acousto-optic effects were found as far back as the 1930s, in which most of the then used acousto-optic media were isotropic media such as water and glass, and this phenomenon is known as “ultrasonic grating”. However, the acousto-optic effects had not received enough attention prior to the advent of laser because changes in frequencies and directions of light caused by the acousto-optic effects are relatively insignificant. Development of acousto-optic devices was driven by the emergence of laser in the 1960s. Due to good monochromaticity and directionality and high brightness of laser, as well as due to its capability of focusing, with coherent light it has, all energy of a laser beam to a spot of a diffraction-limited size, etc., the frequency, direction, and intensity of the laser beam can be quickly and effectively controlled using acousto-optic interaction, which greatly expands the range of applications of the laser, further promoting the development of acousto-optic devices. From the mid-1960s to the mid-1970s, the performance of acousto-optic devices has been improved rapidly with the advent of a collection of new high-performance acousto-optic crystals, such as PbMoO4, TeO2 and LiNbO3. Moreover, irrespective of which aspect of characteristics of the laser beam is controlled, the working principles, structures and manufacturing processes of the acousto-optic devices in use are essentially the same, such that different needs (even multi-purposes for a same device) may be accommodated only by making certain adaptations in design, which cannot be achieved by other optoelectronic devices. Evolution of the optical waveguide and the surface acoustic wave technologies further advances the development of surface wave acousto-optic devices. Because the surface acoustic wave and the optical guide wave are concentrated in a thin layer with the medium surface thickness being an order of magnitude of wavelength, the energy is very concentrated, such that only a very small drive power is needed for the surface wave acousto-optic device. Meanwhile, the surface wave acousto-optic device is fabricated using a planar process which is relatively simple and flexible, so that it is easy to fabricate a transducer with a complex structure, and a bandwidth larger than a bulk wave device can be obtained. In recent years, the acousto-optic devices play an important role in the fields of optical fiber communication, laser addressing, laser marking, laser pulse, laser frequency stabilization, laser power stabilization, laser facsimile, laser printing, etc.
Typical acousto-optic materials are classified into three kinds: liquid, glass and single crystal. In liquid materials, water is considered as a better acousto-optic interaction medium; however, it has a larger acoustic attenuation and cannot maintain a stable optical performance as it is prone to be perturbed under the action of acoustic waves and heat, thereby having no significance of use. Glass (SiO2) is one of the most common acousto-optic medium materials, but has a large acoustic attenuation, and its light transmissive wave band can hardly cover a mid-infrared wave band; meanwhile, a transparent glass with a refractive index greater than 2.1 can hardly be obtained in a visible spectrum region; further, glass has a small photoelastic coefficient, such that it is only suitable for acousto-optic devices with an audio frequency below 100 MHz. The early used acousto-optic crystals include LiNbO3, LiTaO3, α-Al2O3, R3Al5O12 and the like. However, all of these crystals have a poor acousto-optic performance.
At present, the most widely used acousto-optic crystals mainly comprise TeO2 and PbMoO4. TeO2, which belongs to a tetragonal crystal system, is an acousto-optic material having a high quality factor, a high refractive index (ne=2.430 and no=2.074), a high transparency to visible light, and a large photoelastic coefficient. Its shear wave is propagated at a slow acoustic velocity (0.62×105 cm/s) in the [110] direction, and such slow shear wave has a high acousto-optic merit value (M2=793×10−18 s3/g), and the transverse wave propagated in the direction at an angle of 35.9° relative to the X axis in the (001) plane has a zero temperature coefficient and a high merit value (M2=200×10−18 s3/g). Therefore, TeO2 can be applied to anisotropic acousto-optic deflectors and filters that require a large bandwidth and a high resolution. However, the TeO2 crystal growth technology is complex with a high growth cost; and it is difficult to obtain a high-quality bulk single crystal. PbMoO4 also belongs to the tetragonal crystal system, which has a good optical property and a small acoustic attenuation coefficient. In addition, the c axis of PbMoO4 coincides with its Y axis, so that the acousto-optic diffraction efficiency is unrelated to the polarization of incident light. Thus, the PbMoO4 crystal is broadly applied to acousto-optic modulators and deflectors and may also be applied to high-resolution acousto-optic deflectors. However, this crystal contains a toxic element Pb and is difficult to be processed due to its smaller hardness (with the Mohs hardness about 3).
The Chinese patent CN1313517A (application No. 01112800.3) discloses an acousto-optic modulator fabricated by a lead tungstate crystal modified by rare earth ions. In this patent, by fabricating an acousto-optic modulator using La3+: PWO or Y3+: PWO instead of the PMO or TeO2 crystal, the performance of the modulator is improved significantly without substantially changing the design and structure of the modulator; particularly, the working wave band of the modulator extends towards the near-ultraviolet region by 60-70 nm approximately and a good irradiation resistance is imparted. Although the performance of the PWO crystal acousto-optic device is improved in this patent, the problem that the crystal contains the toxic element Pb is not resolved yet.
The Chinese patent CN105068280A (application No. 201510425255.7) discloses uses of a potassium fluoroboratoberyllate (KBBF)-family crystal materials (including potassium fluoroboratoberyllate, rubidium fluoroboratoberyllate and cesium fluoroboratoberyllate) and an acousto-optic device. Uses of the KBBF-family crystal materials include: an acousto-optic medium in an acousto-optic device, wherein light incoming to the acousto-optic medium is ultraviolet light; the incoming direction of the acoustic wave generated by the acousto-optic device into the acousto-optic medium is c-axis direction of the KBBF-family crystals; and the incoming direction of the ultraviolet light into the acousto-optic medium is perpendicular to the c-axis direction. However, the KBBF-family crystals disclosed in this patent have certain difficulties in growing a large-size and high-quality single crystal. In addition, this kind of materials has a light transmissive wave band incapable of covering a mid-infrared wave band and has a poor acousto-optic effect, such that they can hardly be used in practice.
Development of laser technologies and lasers, particularly application of mid-infrared lasers, becomes highly demanding on comprehensive performance of the acousto-optic devices, particularly on the light transmissive wave band. High-performance acousto-optic materials are the basis of high-performance acousto-optic devices. Single-crystal materials are the preferred choice for the development of acousto-optic materials by virtue of their large quality factor M2, low acoustic attenuation, and good light transparency characteristics. A good acousto-optic material not only requires a high acousto-optic interaction performance, but also a good optical and acoustic performance. In general, the acousto-optic interaction performance of a material is measured by its acousto-optic merit value (also referred to as the acousto-optic quality factor). Moreover, requirements of an acousto-optic device on the optical performance of a material are essentially the same as those of a common optical device, including: 1) high light transmittance and high refractive index within a light wavelength range in use; 2) high chemical stability, and long the mechanical life; 3) high photodamage threshold and ease of machining; 4) small temperature coefficients of respective physical constants; 5) having developed a crystal growth technology capable of obtaining a high-quality and large-size crystal, wherein the good acoustic properties of a material are expressed as low acoustic attenuation, small nonlinear acoustic coefficient, and small acoustic velocity temperature coefficient; and 6) containing heavy ions and high crystal density, etc.
In view of the above, under the existing acousto-optic principles, the characteristics of the acousto-optic materials determine the characteristics and range of applications of the acousto-optic devices. Therefore, it is a hot topic in current researches on materials and devices to explore the acousto-optic materials and devices thereof with excellent performance so as to meet the needs of scientific and technological development.
To overcome the drawbacks in the prior art, the present disclosure provides a use of a quaternary molybdenum/tungsten tellurite crystal and a device of the same.
The technical solution of the present disclosure is provided as follows:
Use of quaternary molybdenum/tungsten tellurite crystal as an acousto-optic material, wherein the quaternary molybdenum/tungsten tellurite is a tetraoxide comprising tellurium (Te) and tungsten (W), or tellurium (Te) and molybdenum (Mo).
According to the present disclosure, the quaternary molybdenum/tungsten tellurite is β-BaTeMo2O9, α-BaTeMo2O9, Cs2TeMo3O12, Cs2TeW3O12, Na2TeW2O9, CdTeMoO6, etc., but is not limited to the above-listed materials.
According to the present disclosure, the quaternary molybdenum/tungsten tellurite crystal is used as an acousto-optic medium to fabricate an acousto-optic device, such as an acousto-optic modulator, an acousto-optic deflector, and an acousto-optic filter, etc.
The acousto-optic device comprises an acousto-optic medium, a piezoelectric transducer and an impedance matching network. The quaternary molybdenum/tungsten tellurite crystal serves as the acousto-optic medium.
The working principle of the present disclosure is provided as follows: as shown in
According to the acousto-optic device provided by the present disclosure, choice of a light transmission direction of the acousto-optic medium is designed and optimized based on a photoelastic coefficient in crystal anisotropy and propagation characteristic of the light.
According to the acousto-optic device provided by the present disclosure, a direction of the piezoelectric transducer is arranged in consideration of the interaction between acoustic wave and the acousto-optic medium.
In the present disclosure, the quaternary molybdenum/tungsten tellurite crystal may be grown according to a conventional growth method in the art, and machined according to a conventional method such as cutting and polishing in the art after the growth is completed.
The acousto-optic device provided by the present disclosure may be assembled according to a conventional method in the art.
The present disclosure has the following advantageous effects.
In the present disclosure, a novel quaternary molybdenum/tungsten tellurium compound is used as the acousto-optic medium to fabricate a high-performance acousto-optic device. The material in use is non-toxic; and a high-quality and large-size single crystal can be obtained easily. The physical properties of the crystal almost meet all requirements of a high-quality acousto-optic material. Thus, the crystal has important potential application values. Noteworthily, the light transmissive wave band of this kind of materials can cover 3-5 μm wave bands. The abundant crystal structures of such material cover high, medium and low crystal systems, such that material selection can be made according to practical application requirements.
The present disclosure will be described in detail below in conjunction with the embodiments and the drawings, but is not limited thereto.
Crystals described in the embodiments are all prepared according to the prior art.
Particularly, α-BaTeMo2O9 crystal is prepared with reference to the Chinese patent CN102031563A; β-BaTeMo2O9 crystal is prepared with reference to the Chinese patent CN1958883A; Cs2TeMo3O12 crystal is prepared with reference to the Chinese patent CN102011189A; Cs2TeW3O12 crystal is prepared with reference to the Chinese patent CN104562204A; and Na2TeW2O9 crystal is prepared with reference to Cryst. Growth Des. 10 (9), 4091-4095, 2010.
The α-BaTeMo2O9 crystal belongs to a biaxial crystal, the orthorhombic system, and mm2 point group. The crystal has a light transmissive range of 0.38-5.53 μm and a transmittance of about 80%. The transmittance of the crystal after being coated is up to 99% above. The crystal displays a higher refractive index (nz=2.42@0.4 μm). The α-BaTeMo2O9 crystal has excellent physicochemical properties such as ease of growing large-size and high-quality single crystals; resistance to deliquescence and cleavage, moderate hardness (Mohs˜4.7), ease of machining, and larger optical damage threshold, etc.
The acousto-optic device comprises an acousto-optic medium, a piezoelectric transducer and an impedance matching network. The α-BaTeMo2O9 crystal is selected as the acousto-optic medium, and choice and optimization is based on the acousto-optic coefficient of the crystal and a light propagation characteristic in the crystal (in the present embodiment, the z-axis is selected as the direction for transmitting light and the x-axis is for applying the piezoelectric transducer). The crystal is polished in the light transmission direction and coated with an optical anti-reflection film @ 1064 nm. The acousto-optic device is encapsulated with an aluminum shell.
The driver comprises a signal generation and power amplification circuit. The working voltage is DC+24V. The “power output” end outputs a drive power and is connected to an optical modulator device via a high-frequency cable; and a modulation signal is input through an “input” end.
If the acousto-optic device in this embodiment is applied to laser Q switching, a Q switching optical path diagram of the acousto-optic device is shown in
The β-BaTeMo2O9 crystal belongs to a biaxial crystal, the monoclinic system, and the 2nd point group. The crystal has a light transmissive range of 0.5-5 μm with a transmittance of about 80%. The transmittance of the crystal after being coated is up to 99% above. The crystal displays a higher refractive index (nz=2.32@0.4 μm). Similarly, the β-BaTeMo2O9 crystal also has excellent physicochemical properties such as ease of growing large-size and high-quality single crystals; resistance to deliquescence and cleavage, moderate hardness (Mohs˜4.7), ease of machining, and larger optical damage threshold, etc.
The β-BaTeMo2O9 crystal acousto-optic device is similar to that in Embodiment 1, except that in this embodiment, the crystal orientation selects a crystal refractive index main axis, Z axis, as the light transmission direction of the acousto-optic device, and Y axis for applying the piezoelectric transducer. Likewise, as shown in
The Cs2TeMo3O12 crystal belongs to a uniaxial crystal, the hexagonal crystal system, and the 6th point group. The crystal has a light transmissive range of 0.43-5.38 μm with a transmittance of about 80%/a. The transmittance of the crystal after being coated is up to 99% above. The crystal displays a higher refractive index (ne=2.03@0.4 μm and no=2.23@0.48 μm). The Cs2TeMo3O12 crystal has excellent physicochemical properties such as ease of growing large-size and high-quality single crystals; resistance to deliquescence and cleavage, moderate hardness (Mohs˜4.7), ease of machining, and larger optical damage threshold, etc.
The acousto-optic device of the Cs2TeMo3O12 crystal is similar to that in Embodiment 1. In this embodiment, the crystal refractive index Z axis is selected as a light transmission direction of the crystal, and the refractive index X axis is for applying the transducer. Likewise, as shown in
The Cs2TeW3O12 crystal belongs to a uniaxial crystal, the hexagonal crystal system, and the 6th point group. The crystal has a light transmissive range of 0.41-5.31 μm with a transmittance of about 80%. The transmittance of the crystal after being coated is up to 99% above. The crystal has a higher refractive index (ne=1.98@0.4 μm and no=2.20@0.48 μm). The Cs2TeW3O12 crystal has excellent physicochemical properties such as ease of growing large-size and high-quality single crystals; resistance to deliquescence and cleavage, moderate hardness (Mohs˜4.5), ease of machining, and larger optical damage threshold, etc.
The structure and properties of the Cs2TeW3O12 crystal are similar to those of the Cs2TeMo3O12 crystal. In this embodiment, a light transmission direction of the crystal is identical with that of the Cs2TeMo3O12 crystal. Likewise, as shown in
The CdTeMoO6 crystal belongs to a uniaxial crystal, a tetragonal crystal, and −42 mth point group. The crystal has a light transmissive range of 0.345-5.40 μm with a transmittance of about 80%. The transmittance of the crystal after being coated is up to 99% above. The crystal has a higher refractive index. The CdTeMoO6 crystal has excellent physicochemical properties such as ease of growing large-size and high-quality single crystals; resistance to deliquescence and cleavage, moderate hardness, ease of machining, good thermal stability and chemical stability, and larger optical damage threshold, etc.
The acousto-optic device of the CdTeMoO6 crystal is similar to that in Embodiment 1. The crystal refractive index Z axis is selected as a light transmission direction of the crystal, and the refractive index X axis is for applying the transducer. Likewise, as shown in
The Na2TeW2O9 crystal belongs to biaxial crystal system, the monoclinic system, and the mth point group. The crystal has a light transmissive range of 0.45-5.0 μm with a transmittance of about 80%. The transmittance of the crystal after being coated is up to 99% above. The crystal has a higher refractive index, wherein nz=2.12@0.6 μm. The Na2TeW2O9 crystal has excellent physicochemical properties such as ease of growing large-size and high-quality single crystals; resistance to deliquescence and cleavage, moderate hardness, ease of machining, and larger optical damage threshold, etc.
The acousto-optic device of the Na2TeW2O9 crystal is similar to that in Embodiment 1. The crystal refractive index Z axis is selected as a light transmission direction of the crystal, and the refractive index X axis is for applying the transducer. Likewise, as shown in
Table 1 shows testing of the properties of the crystals in Embodiments 1-6, conventional fused silica and TeO2.
It can be seen from Table 1 that the basic physical characteristics of the crystals provided by the present disclosure are close to the basic physical characteristic of the TeO2 crystal, wherein the diffraction angle and the diffraction efficiency in the performance parameters of the α-BaTeMo2O9 crystal acousto-optic device are slightly higher than those of the TeO2 crystal acousto-optic device.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201611161381.7 | Dec 2016 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2017/104968 | 9/30/2017 | WO | 00 |