Patent Application
20220017419
The invention is generally in the field of cementitious compositions, hydraulic cements, blended cements, supplementary cementitious materials, mineral fines, performance-enhancing particulate pre-mixes, and methods of manufacture.
The cement and concrete industry continuously searches for new ways to substitute Ordinary Portland Cement (OPC) with alternative materials that are cost-effective and have lower carbon footprint. The manufacture of OPC generates enormous quantities of CO2, representing an estimated 5-7% of manmade CO2. In general, manufacturing a ton of OPC releases almost a ton of CO2 into the atmosphere. With worldwide cement production being about 4.2 billion tons per year, the manufacture of cement creates approximately 4 billion tons of CO2 per year. Cement is also the most costly component in concrete (based on unit cost and quantity added). Reducing clinker content and other cementitious binders is desirable because it reduces production of CO2 and cost.
Ground granulated blast furnace slag (GGBFS), fly ash, natural pozzolans, silica fume, and other mineral substitutes (“supplementary cementitious materials” or “SCMs”) have been used as components of blended cement and/or as partial cement substitutes in concrete. When used in blended cement, SCMs are often interground with clinker. To offset strength loss, interground blended cements are typically ground more finely than OPC, which makes them more reactive but can detrimentally increase water demand and concrete durability. There is also an upper limit to how much clinker can be substituted with SCMs before there is serious loss in strength, especially early strength. While SCMs are widely used, a substantial portion of known SCMs, including much of the fly ash produced, are not used but discarded into the environment or otherwise remain undeveloped. In spite of known environmental and economic benefits in reducing clinker content through increased use of SCM, SCM utilization remains suboptimal because of substantial technical hurdles.
Limestone has been interground with cement clinker to make Portland-limestone cement. Limestone is softer and more easily ground than cement clinker and forms predominantly in the ultrafine fraction. Because limestone has no cementitious or pozzolanic properties, only limited quantities of limestone can be interground with cement without seriously affecting strength, durability and other performance criteria. Until recently, ASTM C-150 did not permit any limestone addition to Types I-V cement. In 2003, Hawkins et al. of the Portland Cement Association published a paper entitled “The Use of Limestone in Portland Cement: A State-of-the-Art Review”, which advocated a change in ASTM C-150 to permit up to 5% limestone addition in OPC. In 2004, ASTM C-150 was amended to permit limestone additions of up to 5% in Types I-V cement. In 2012, ASTM approved a proposal to amend ASTM C-595 (blended cements) to permit inclusion of 5-15% limestone. These standards indicate that the use of limestone as a substitute for cement clinker is limited compared to SCMs such as GGBFS and fly ash, which are commonly used in amounts greater than 15% and which can contribute to long-term strength development (although they commonly reduce early strength). Because interground Portland-limestone cement must be ground more finely to avoid serious strength loss, there is little or no economic benefit compared to OPC. The main benefit appears to be to cement companies, which have an abundant supply of limestone and can use it as a filler to stretch clinker and increase production capacity. Little or no cost benefit is passed on to customers even though such cement is typically of lower quality. Blended cements typically can cost the same or more than OPC, making them less attractive than OPC because of performance loss. For example, intergrinding clinker, natural pozzolan, and limestone in Mexico yields blend cements with pour performance. From a technical standpoint, a major drawback is the inability to control the respective particle size distributions (PSDs) of the cement and limestone particles when interground. This creates variability and uncertainty in performance.
Researchers have used separately processed very fine or ultrafine limestone (sometimes called “nano-limestone”) to replace cement clinker, including to augment strength in high volume fly ash (HVFA) mortars. Ultrafine limestone has also been used in ultra-high performance concrete (UHPC) as an ultrafine mineral filler similar to silica fume to decrease pore size and increase paste density. In ultrafine limestone, most or all of the particles are less than about 8 μm in size). Though found to enhance strength, ultrafine limestone is typically as expensive or more expensive than OPC and is therefore not economically feasible for general purpose cements and concrete.
A promising source of low cost limestone or other mineral fines is leftover quarry fines (sometimes called “rock dust” or “quarry by-products”) from aggregate manufacture. Aggregates are typically limestone or igneous rock of volcanic origin. By way of background, processing of crushed stone for use as construction aggregate consists of blasting, primary and secondary crushing, washing, screening, and stockpiling operations. Quarry by-products are produced during crushing and washing operations. According to a publication by the Federal Highway Association (FHWA-RD-97-1480) (last modified Mar. 8, 2016), there are generally three types of quarry by-products resulting from these operations: screenings, pond fines, and baghouse fines.
“Screenings” refers to the finer fraction of crushed stone that accumulates after primary and secondary crushing and separation on a 4.75 mm (No. 4) sieve. The size distribution, particle shape, and other physical properties can be somewhat different from one quarry location to another, depending on the geological source of the rock quarried, the crushing equipment used, and the method used for coarse aggregate separation. Screenings contain freshly fractured faces, have a fairly uniform gradation, and do not usually contain large quantities of plastic fines. Screenings are a uniformly sized, fine, sandy material with some silt particles. Screenings commonly range in particle size from 3.2 mm (⅛ inch) down to finer than 75 μm (No. 200 sieve). Normally, the percentage of particle sizes finer than 75 μm is 10% or less by weight. Stockpiles of screenings may contain some particles up to 4.75 mm (No. 4 sieve) ( 3/16 inch) in size, which is usually the screen size used for separation of fine and coarse aggregates. Some weathered rock or overburden material may be present in the screenings from certain processing operations
“Settling pond fines” refers to the fines obtained from washing crushed stone aggregate. During production, the coarser size range (greater than No. 30 sieve, or 0.60 mm) from washing may be recovered by means of a sand screw classifier. The remainder of the fines in the overflow is discharged to a series of sequential settling ponds or basins, where they settle by gravity, sometimes with the help of flocculating polymers. “Pond clay” is usually used to describe waste fines derived from the washing of natural sands and gravels. Pond fines, when initially recovered from the pond, consist of low solids content, fine-grained slurry, usually with 90-95% of the particles finer than 150 μm (No. 100 sieve) and 80% or more finer than 75 μm (No. 200 sieve).
“Baghouse fines” are produced in quarries that operate as dry plants because of dry climatic conditions or a lack of market for washed aggregate products. Dry plant operation requires the use of dust collection systems, such as cyclones and baghouses, to capture dusts generated during crushing operations. These dusts are referred to as baghouse fines. Although particle sizing may vary somewhat with fines from different types of stone, the range in particle size is from 75 μm (No. 200 sieve) down to 1 μm or finer. Baghouse fines can be a source of “nano-limestone” when milled or classified to average particle size of about 1-8 μm.
It is estimated that in the U.S. alone at least 159 million metric tons (175 million tons) of quarry by-products are generated each year, mostly from crushed stone production operations. As much as 3.6 billion metric tons (4 billion tons) of quarry by-products may have accumulated in the U.S. According to FHWA-RD-97-1480, it is assumed that very little of the 159 million metric tons (175 million tons) produced annually are used, especially pond fines. In a recent survey, three states (Arizona, Illinois, and Missouri) indicated that quarry by-products have been used as an embankment material, and three other states (Florida, Georgia, and Vermont) indicated some use of quarry by-products in base or subbase applications. Use has been made of limestone screenings as agricultural limestone, and baghouse fines from quarry sources have been used as mineral filler in asphalt paving. Limited quantities of baghouse fines have been provided and/or milled and/or classified to provide nano-limestone for laboratory testing; however, there has been no consistent use of these or other quarry fines in concrete.
Quarry fines can be used in coal mines as “mine safety dust”. Combustible coal dust that is emitted into the air and settles on objects in a coal mine creates a dangerous risk of mine explosions. Coal dust also causes “black lung” in miners. Dusting of coal mines with mine safety dust reduces the danger of explosions by diluting the combustible dust in the mine with a noncombustible dust, sometimes by misting with water to wash particulates out of the air. The fineness desired for safety mine dust is 100% passing a No. 20 sieve (0.85 mm) and at least 50% passing a No. 200 sieve (0.075 mm). Because silica-based dust is harmful if inhaled, limestone-based quarry fines (or rock dust) are considered to be a safer option for mine safety dust because they have low silica content. An example of limestone-based mine safety dust is produced and sold as Coal Mine Rock Dust by Staker Parson, headquartered in Ogden, Utah (“Staker”), a division of Oldcastle and CRH. Staker owns and operates an aggregate quarry that produces limestone and dolomitic limestone aggregates for many of Staker's ready-mix concrete facilities in Utah. Leftover quarry fines are collected, further milled, and sold to coal mine operators. Similar products are manufactured by other companies, such as Graymont, Blue Mountain Minerals, E. Dillon & Company, Carmeuse, and Omya. Quarry fines are not commonly used by concrete companies in the manufacture of concrete notwithstanding this material is made by concrete companies or aggregate producers, are readily available in the same locations as aggregates used in concrete, are a low cost by-product (e.g., retailing at about $2 to $8 per ton in bulk), and are produced in great abundance.
The reported reason that the cement and concrete industries have tried but failed to effectively use quarry fines in concrete is that they negatively and unpredictably increase water demand and negatively and unpredictably affect rheology (flow and workability properties). Jeknavorian et al., of W.R. Grace, published a paper in 2010 entitled “Use of Chemical Admixtures to Modify the Rheological Behavior of Cementitious Systems Containing Manufactured Aggregates,” 2010 Concrete Sustainability Conference, National Ready Mixed Concrete Association (“Grace Article”). The Grace Article detailed the negative and unpredictable effects of quarry fines on rheology and other properties of concrete and noted that the most effective way to offset the negative effects of using manufactured sand containing large amounts of quarry fines is by increasing cement and/or SCM content. The Grace Article also stated that the main reason for using quarry fines is to produce sustainable concrete with locally produced materials notwithstanding the negative effects of quarry fines on concrete. However, using more cement makes concrete less sustainable. The Grace Article also explored the undesired interaction between polycarboxylate-based superplasticizers and clay-bearing aggregates containing high quantities of quarry fines. To address this issue, the Grace Article evaluated the interaction of both natural and manufactured sands with a bio-polymer type viscosity-modifying agent (VMA), a class of admixture used with angular-shaped fine aggregates. An admixture company attempting to find an admixture for quarry fines reportedly abandoned the project due to failure or lack of interest from the concrete industry.
Another reason why quarry fines are difficult to use is they do not fit within any specified category of materials used in concrete. The only two options explored by concrete companies and researchers has been to treat quarry fines either as an SCM, used to replace or augment OPC, or as an aggregate. Because quarry fines do not behave like typical SCMs and are even finer than fine aggregates, their effect on strength and rheology is unpredictable and usually negative. The following question was asked at an academic cement conference in November 2017: “What is limestone powder? Cementitious binder or aggregate?” An expert replied: “Neither.” To which the follow-on question was asked: “What ASTM standard specifies how limestone powder is to be used in concrete?” The expert replied: “There isn't one.” This blind spot in ASTM standards, common practice, and among experts in the field highlights why it has heretofore been difficult, if not impossible, to intelligently utilize quarry fines and/or limestone powder to manufacture concrete having predictable strength and rheology.
Other mineral materials discarded in vast quantities include bottom ash from coal combustion, metallurgical slags (e.g., steel slag produced by scrap reprocessing), stone dust (e.g., marble dust) from stone cutting operations, mine tailings, discarded shale from oil shale extraction, discarded sand from tar sands extraction, washout fines from concrete and/or mortar manufacture (wet or dried), and ground recycled concrete. Such materials are often similar in minerology to aggregates used in concrete, are therefore also “quarry fines” or “mineral fines” and are rarely if ever used as aggregates or fillers.
Attempts have also been made to utilize concrete washout fines in concrete. Concrete washout fines are formed by washing out a concrete truck or other concrete mixer with water to remove unused fresh concrete as a slurry and removing coarse aggregate particles, such as rock and pea gravel. Washout fines typically include Portland cement, such as hydrated Portland cement, partially hydrated Portland cement, and/or unhydrated Portland cement, fine aggregate particles, water, and optionally supplementary cementitious materials and/or chemical admixtures. Washout fines can be dewatered and placed in piles for disposal and/or used as road base or fill material. Both wet and dried washout fines typically have high alkalinity and can have a pH of 10 or higher. The effects on water demand and set time are highly unpredictable such that widespread use of concrete washout fines has not been technically feasible
The inability of the concrete industry to effectively utilize quarry fines and other waste mineral fines is not surprising since anything that creates unpredictability, increased water demand, and/or performance loss is rejected by the concrete industry, which requires predictable and reproducible results when producing concrete guaranteed to satisfy prescribed standards set by building codes and engineers. Accordingly, there exists a long-felt but unsatisfied need to find a way to beneficially utilize quarry fines and other waste mineral fines in concrete, with predictable strength and rheology, in order to produce more sustainable concrete. The failure of cement, concrete, and admixture companies to develop a systematic, reliable, and easily followed approach to utilize quarry fines, other waste mineral fines, or limestone powder in concrete, notwithstanding their great abundance, low cost, and the tremendous efforts the past two decades to make more sustainable concrete, highlights the problem, the lack of any viable solution to the problem, and the acuteness of the long-felt but unsatisfied need.
Disclosed herein are compositions and methods for manufacturing cementitious compositions that contain quarry fines, limestone powder, mine tailings, ground recycled concrete, concrete washout fines (wet or dried), and/or other waste minerals (collectively “mineral fines”) with predictable water demand, predictable rheology, predictable strength, predictable admixture requirements, and other performance benefits. An example method comprises mixing together hydraulic cement, mineral fines, an aggregate fraction, and water so that the cementitious composition has a “defined water-to-cementitious binder ratio” (“defined w/cm”) (or “design w/cm”), and wherein a first portion of the mineral fines is defined and apportioned as forming part of the cementitious binder so as to contribute to the defined w/cm and a second portion of the mineral fines is defined and apportioned as forming part of the aggregate fraction so as to not contribute to the defined w/cm. Replacing both a portion of cementitious binder and aggregate with mineral fines can significantly reduce both clinker content and cost while maintaining desired and predictable strength, water demand, rheology, durability, admixture requirement, and other performance properties.
An example cementitious composition comprises hydraulic cement, mineral fines (e.g., having a D90 between about 30 μm and about 500 μm, about 40 μm and about 300 μm, or about 50 μm and about 150 μm), an aggregate fraction, and water so that the cementitious composition has a defined w/cm, and wherein a first portion of the mineral fines is defined and apportioned as forming to part of the cementitious binder so as to contribute to the defined w/cm and a second portion of the mineral fines is defined and apportioned as forming part of the aggregate fraction so as to not contribute to the defined w/cm. Attributing a portion of the mineral fines as “cementitious binder” can reduce clinker content and account for the effect of the mineral fines on water demand without substantially overstating or understating it. Attributing a portion of the mineral fines to the aggregate fraction (e.g., as an “ultrafine aggregate”, some or all of which is dispersed within the cement paste) provides a strength-enhancing filler effect by increasing total powder in the cement paste without substantially overstating or understating its effect on strength. The mineral fines can beneficially increase particle packing density of the cement binder particles and yield a denser cement paste. They can also reduce autogenous, plastic, and drying shrinkages.
To bridge the size gap between cementitious binder and fine aggregate (sand), the mineral fines are substantially finer than the fine aggregate, with a D90 as defined herein, and coarser than the cementitious binder, which also follows from the D90 defined herein. The Blaine fineness of the mineral fines is advantageously less than about 375 m2/kg, or less than about 350 m2/kg, or less than about 325 m2/kg, or less than about 300 m2/kg, or less than about 275 m2/kg, or less than about 250 m2/kg, or less than about 225 m2/kg, or less than about 200 m2/kg, or less than about 175 m2/kg, or less than about 150 m2/kg, or less than about 125 m2/kg, or less than about 100 m2/kg, or less than about 75 m2/kg, or less than about 50 m2/kg, or less than about 25 m2/kg. The minimum Blaine fineness can be at least about 15 m2/kg, or at least about 25 m2/kg, or at least about 35 m2/kg, or at least about 50 m2/kg.
There is test data suggesting that cement paste made with mineral fines can bind more strongly to coarse aggregates, leading to the hypothesis that proper use of mineral fines can densify cement paste in the interfacial transition zone (ITZ) between the bulk paste and coarse aggregate surfaces where paste strength is usually at a minimum due to a gradient of increasing w/cm in the direction from the bulk paste toward the coarse aggregate surface. It is further hypothesized that cement particles shrink when hydrating, causing higher plastic shrinkage of paste in the ITZ, which can form micro-fissures that can decrease paste-aggregate bond strength and/or create pores that provide a pathway for ion transport, which can negatively affect durability and increase the chance of chemical attack of the cement paste and/or alkali-silica reaction (ASR) at the aggregate surface. Mineral fines are non-shrinking and are believed to provide nucleation sites for cement crystal growth. Both of these effects may substantially increase paste density and reduce paste shrinkage in the ITZ, yielding higher paste-aggregate bond strength and/or improved resistance to chemical attack.
In some embodiments, it can be advantageous to identify a cutoff particle size between fine and coarse mineral fines particles, which can be used to define the particles as either “cement” (or “cementitious binder”) or “aggregate” (or “non-cementitious filler”) depending on whether they are smaller or larger than the cutoff particle size. By way of example and not limitation, if the cutoff particle size were defined as 45 μm, mineral fines at or smaller than 45 μm can be apportioned or designated as “cement” or “cementitious binder” that contribute to (are accounted for in) the defined w/cm, and particles larger than 45 μm can be apportioned or designated as “aggregate” that does not contribute to (and is not accounted for in) the defined w/cm, for purposes of designing concrete or other cementitious compositions having predictable water demand, rheology, and/or strength. The cutoff particle size can be empirically determined or it may be arbitrarily set or approximated based on experience. In general, the cutoff particle size can be any reasonable value that works in accordance with the disclosed methods. For example, it can be between about 15 μm and about 75 μm, or between about 20 μm and about 65 μm, or between about 25 μm and about 55 μm, or between about 30 μm and about 50 μm.
Defining or attributing a portion of mineral fines as “cementitious binder” that contribute to the “defined w/cm” during design and manufacture of concrete can perhaps be understood as fictitious or arbitrary because they are not ordinarily considered to be “cementitious binders.” The term “defined w/cm” as used herein for purposes of designing and manufacturing concrete (which can also be called a “design w/cm”) can be different than the “actual w/cm” (or simply “w/cm” in ordinary parlance) as defined by ASTM, AASHTO, EN, engineers, concrete companies, or other established standards. Using conventional design methods or definitions, the actual w/cm (or w/cm) will usually exclude mineral fines as not being a cementitious binder, or they may consider all of the mineral fines as “cementitious binder.” As such, the defined w/cm used to design concrete having predictable strength and rheology will typically lie between a “higher actual w/cm” when none of the mineral fines are counted as forming part of the cementitious binder and a “lower actual w/cm” when all of the mineral fines are counted as forming part of the cementitious binder. Though perhaps fictitious or arbitrary, it has now been discovered that using a defined w/cm (or design w/cm) by defining one portion of mineral fines as “cementitious binder” and another portion as “aggregate” is much more accurate and predictive of the rheology and strength of the concrete. When none of the mineral fines are defined as cementitious binder, but no adjustment is made to account for water that is absorbed into the mineral fines (e.g., to make a saturated surface dry (SSD) aggregate), a higher actual w/cm is assumed, which underestimates both water demand and strength. Conversely, when all of the mineral fines are defined as cementitious binder, even though mineral fines do not typically react with water, a lower actual w/cm is assumed, which overestimates both water demand and strength. Using a design w/cm through proper apportionment of mineral fines between cementitious binder and aggregate is a powerful new tool because it more accurately and reproducibly predicts actual water demand and strength of the concrete mix. This, in turn, reduces or substantially eliminates uncertainty and lack of reproducibility, which are typically encountered when assuming either a higher or lower w/cm than the defined w/cm (or design w/cm) as used herein.
The hydraulic cement binder may comprise ordinary Portland cement (OPC) as defined by ASTM C-150 or blended cement under ASTM 595 or ASTM 1157. Blended cement can be made by intergrinding and/or separate processing and blending. Ordinary Portland cement (OPC) and blended cements typically have a D90 between about 35 μm and about 45 μm. Alternatively, the cement binder may comprises a narrow PSD cement having a lower D90 and/or higher D10 compared to OPC, which reduces the amount of coarse particles not able to fully hydrate and/or the amount of ultrafine particles that increase water demand without providing a corresponding strength benefit. The cement binder can also include calcium sulfoaluminate (CSA) cement, supersulfated cements, oil well cements, geopolymer cements, and other hydraulic cements known in the art.
Supplementary cementitious materials (SCMs) having pozzolanic and/or cementitious activity can be used and beneficially provide a substantial portion of fine and/or ultrafine particles of the overall cementitious binder system. Substituting at least a portion of the ultrafine cement particles (e.g., below about 3 μm) with ultrafine SCM particles substantially reduces water demand because ultrafine SCM particles do not significantly react with and consume water in the early stages during mixing and placement of concrete. SCMs are also less likely to flocculate like ultrafine cement particles during early stages of mixing and placement. Ultrafine SCMs are much more pozzolanically reactive than less fine SCM particles, greatly enhancing their strength contribution to the cementitious binder system. Mineral fines can provide a substantial portion of coarse particles in the cement paste. A coarse SCM may be included to provide particles that are coarser than the cement particles. In a well-optimized cementitious binder system, a substantial portion (e.g., ≥30%, ≥40%, ≥50%, or majority) of the ultrafine particles less than 3 μm may comprise SCM particles, a substantial portion (e.g., majority) of medium sized particles between 3-30 μm may comprise hydraulic cement particles, and a substantial portion (e.g., ≥30%, ≥40%, ≥50%, or majority) of coarse particles between 30-150 μm may comprise mineral fines, optionally in combination with coarse SCM particles between 30-150 μm. Strength and durability can be increased by increasing the overall powder content in the cement paste through the use of mineral fines that provide a substantial portion (e.g., ≥30%, ≥40%, ≥50%, or majority) of particles between 30-150 μm. It will be appreciated that mineral fines are not required to have particles as large as 150 μm or be devoid of particles larger than 150 μm.
It has also been found that using a relatively small quantity of supplemental lime (e.g., 0.2-4.8% of hydrated lime by weight of cementitious binder) can improve rheology and enhance both early and late age strengths. It is believed that supplemental lime accelerates and is consumed in the pozzolanic reaction when a pozzolanic SCM is used. Hydrated lime adds calcium ions to the system while only adding hydroxyl ions. This feature helps restore proper ion balance in the event that the SCM consumes excessive calcium ions required for proper hydration of hydraulic cement. It also raises the pH of the system and may increase the rate of the pozzolanic reaction. It has been found that a relatively small quantity of supplemental lime usually works better than a large quantity. Using more supplemental lime than can be consumed in the pozzolanic reaction decreases strength by forming weak voids or pockets of soft filler particles. The ability of supplemental lime to react pozzolanically is limited by its low water solubility such the proper amount of supplemental lime is more closely related to the amount of water in the system than the stoichiometric amount that might theoretically react with the pozzolan.
It has also been found that using a relatively small quantity of supplemental sulfate (e.g., 0.2-2.5% of plaster of Paris by weight of the cementitious binder) to help maintain proper sulfate balance can help maintain normal set time, which can extend workability, and enhance early and late age strengths. A sulfate deficiency may occur when a substantial quantity of sulfate-carrying OPC is reduced and replaced with SCMs containing aluminates, which can compete for sulfate provided by the OPC. The tendency of mineral fines to accelerate cement hydration may also cause sulfate deficiency. The use of superplasticizers and other admixtures to deflocculate fine cement particles can increase the surface area of cement particles exposed to water, which can cause sulfate deficiency. Where a large amount of cement is replaced with other materials so that the water-to-cement ratio (w/c) is substantially higher than the water-to-cementitious binder ratio (w/cm), the excess water bathing the cement particles can increase cement hydration and cause sulfate deficiency.
In another aspect of the disclosed technology, a cementitious composition comprises ground Portland cement clinker and sulfate to control setting, a supplementary cementitious material (SCM) having pozzolanic properties, mineral fines comprising particles less than 50 μm in size, and at least one accelerator selected from the group consisting of lime, quicklime, hydrated lime, and Type S lime and that is included in an amount in a range of 0.1% to 4.8% by combined weight of hydraulic cement, SCM, and mineral fines having a particle size less than 60 μm, or less than 50 μm. Such composition may or may not include mineral fines having a particle size greater than 50 μm, or greater than 60 μm. Such composition may optionally include supplemental sulfate (e.g., 0.2-2.5% of plaster of Paris by weight of the cementitious binder).
Mineral fines can be blended with one or more performance-enhancing additives to yield a performance-enhancing particulate pre-mix that can be added to concrete or other cementitious mixture to substitute for a portion of the cement and/or aggregate components normally used in accordance with a given mix design. Performance-enhancing additives may include one or more of supplemental lime, supplemental sulfate, alkanolamines, water-reducing admixtures, superplasticizers, accelerators, retardants, and the like. Because mineral fines are non-reactive, additives containing water (e.g., calcium sulfate slurry or paste scrubber biproducts) can be blended with mineral fines without premature hydration, as would occur if added to a hydraulic cement binder prior to being used to make a fresh cementitious mixture.
The performance-enhancing particulate premix can be used to replace a portion of cementitious binder, including OPC, but especially blended cements comprising OPC and at least one SCM selected from slag, fly ash, bottom ash, natural pozzolan, ground glass, metakaolin, silica fume, and the like. Because of its low cost, which is less than, similar to, or only marginally more than the cost of aggregate, the premix may also be used to replace a portion of sand or other aggregate. Because water demand of the performance-enhancing particulate premix is typically less than cement, but more than aggregate, using it to replace both a portion of the cementitious binder and aggregate portions strikes an optimal balance that enhances performance without significantly increasing, and in some cases reducing, water demand. Mineral fines reduce bleeding and segregation, thereby reducing the need for expensive viscosity modifying agents (VMAs) in the case of high strength concrete that includes substantial quantities of superplasticizers. Reducing or eliminating VMAs can yield high strength concrete that is less sticky and less thixotropic.
Concrete washout fines, whether wet or dried, typically have high alkalinity and may include a substantial quantity of free lime. In such cases, it may be desirable to passivate and neutralize possible detrimental effects of high alkaline values by blending carbon dioxide with concrete washout fines before or during mixing of concrete. At least some of the added carbon dioxide can beneficially react with free lime and form nano-sized mineral particles (e.g., calcium carbonate) in situ within the fresh concrete or other cementitious mix (e.g., having a D90 less than 0.5 μm). Nano-sized mineral particles can be formed in situ using any known process. An economical way to form nano-sized mineral particles in situ is by introducing carbon dioxide (CO2) gas into a fresh cementitious mix, which reacts with calcium ions to form nano-sized calcium carbonate (CaCO3) particles. The CO2 can also react in situ with other metal ions to form other nano-sized mineral particles, such as magnesium carbonate (MgCO3) particles. The nano-sized mineral particles are typically smaller than even the smallest cementitious binder particles and therefore fill interstitial spaces between the cement particles. This increases the particle packing density of particles in the cementitious paste. The nano-sized mineral particles can also provide nucleation sites that promote formation of cementitious binder crystals, such as calcium silicate hydrates, calcium aluminate hydrates, other aluminosilicate hydrates, and the like. Formation of nano-sized mineral particles can densify cement paste and increase concrete strength.
These and other advantages and features of the invention will become more fully apparent from the following description and appended claims, or may be learned by the practice of the invention as set forth hereinafter.
To further clarify the above and other advantages and features of the present invention, a more particular description of the invention will be rendered by reference to specific embodiments thereof, which are illustrated in the appended drawings. It is appreciated that these drawings depict only illustrated embodiments of the invention and are therefore not to be considered limiting of its scope. The invention will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:
Disclosed herein are compositions and methods for effectively using quarry fines, limestone powder, mine tailings, ground recycled concrete, concrete washout fines (wet or dried), and/or other waste minerals (collectively “mineral fines”) in concrete with predictable performance, such as predictable water demand, rheology, and admixture requirement, similar or higher strength and durability, and reduced shrinkage. The compositions and methods disclosed herein can be used to reduce clinker content in concrete. They can enhance effectiveness of SCMs used to replace a portion of Portland cement clinker.
In some embodiments, a method of designing and manufacturing concrete to beneficially utilize mineral fines involves selecting materials having both fine and coarse particles and apportioning them between cementitious binder and aggregate. For example, it can be beneficial to define and apportion a first portion of mineral fines as “cementitious binder” for purposes of designing and manufacturing concrete having a defined water-to-cementitious binder ratio (defined w/cm) and define and apportion a second portion of mineral fines as “aggregate” (e.g., “ultrafine aggregate”) that does not factor into the defined w/cm.
In some embodiments, a concrete composition includes mineral fines apportioned between cementitious binder and aggregate. A first portion of mineral fines is defined and apportioned as “cementitious binder” for purposes of defining the w/cm of the concrete, and a second portion of mineral fines is defined and apportioned as “aggregate” (e.g., “ultrafine aggregate”) that does not factor into the defined w/cm. Surprisingly and unexpectedly, when a first portion of mineral fines is apportioned or defined as forming part of the “cementitious binder” so as to contribute or factor in to the defined w/cm and a second portion is apportioned or defined as forming part of the “aggregate” so as to not contribute or factor in to the defined w/cm, concrete can be designed and manufactured with predictable properties, including predictable water demand, rheology, strength, and other performance criteria.
Without being bound to theory, and by way of example and not limitation, it has been found that mineral fines having a D90 in a range of about 50 μm to about 150 μm and a D10 in a range of about 1 μm to about 30 μm, and which contain particles that are both larger and smaller than the largest cement particles found in OPC (e.g., which are typically between about 35-50 μm), include a first fraction of particles that can be defined as forming part of the cementitious binder and a second fraction of particles that can be defined as forming part of the aggregate fraction. To be certain, mineral fines, such as coarse limestone, dolomitic limestone, granite powder, stone dust, marble dust, mine safety rock dust, mine tailings, and at least coarse particles in shale flue dust, are generally non-cementitious and non-pozzolanic and are not actually a “cementitious binder”. They absorb but do not chemically consume water, are essentially a non-reactive filler, and generally have lower water demand compared to similarly sized cement particles. Nevertheless, mineral fines have a surface area with particle surfaces that must be wetted and therefore “consume” some amount of water by absorption and adsorption. In general, mineral fines consume or absorb less water than cement but more water than sand or other fine aggregate. Designing and manufacturing concrete so that a first portion of mineral fines is defined and apportioned as forming part of the cementitious binder that contributes or factors into the defined w/cm and a second portion is defined and apportioned as forming part of the aggregate that does not contribute or factor into the defined w/cm, facilitates reliable and predictable design and manufacture of concrete having desired rheology, strength, admixture requirements, and other performance criteria.
By way of illustration, one can envision that the portion of mineral fines smaller than a specified particle size (e.g., below 20 μm, 25 μm, 30 μm, 35 μm, 40 μm, or 45 μm) are “cement” or “cementitious binder” and that the portion of particles above the specified particle size are “aggregate.” In practice, this distinction may be arbitrary but is a good way to envision how or why mineral fines can be apportioned between cementitious binder and aggregate when designing and manufacturing concrete and other cementitious compositions. It may also be useful in determining what percentage of mineral fines is defined as “cementitious binder” and what percentage is defined as “aggregate.” In addition, while mineral fines that are coarser than cement particles are hardly “ultrafine” from the standpoint of cement particle size, they can be thought of as providing or comprising an “ultrafine aggregate” when compared to larger particles in typical fine aggregate (or sand) in concrete or mortar.
In practical terms, concrete designed and manufactured using the foregoing criteria of apportioning or defining mineral fines between cementitious binder and aggregate can have both reduced clinker content and reduced fine aggregate content. The mineral fines can in essence straddle the line between the cementitious binder and fine aggregate fractions, replacing a portion of each. Because mineral fines usually cost substantially less than OPC, they reduce cost by reducing clinker content. Even if mineral fines are more expensive than fine aggregate, as long as the cost of mineral fines is less than the combined cost of the hydraulic cement and aggregate they replace, the net result is reduced cost, all other things being equal.
Moreover, the design and manufacture of concrete using mineral fines in the foregoing manner permits further reductions in clinker content when used together with one or more supplementary cementitious materials (SCMs) having pozzolanic properties. SCMs such as fly ash, GGBFS, and natural pozzolans are slow reacting and typically reduce early strength and/or retard setting. On the other hand, at least some mineral fines (e.g., containing limestone and/or dolomitic limestone) can act as an accelerator to offset early strength reduction and/or set retardation when using SCMs. Because SCMs and mineral fines typically have lower water demand than OPC, overall apportioned cementitious binder content can be increased and/or the defined w/cm reduced, both of which increase concrete strength and durability. In addition, when mineral fines are apportioned between cementitious binder and aggregate, the effective water-to-powder ratio (w p) is lower than both the defined w/cm and actual w/cm, which can further increase strength due to the “filler effect.” The w/p will usually be lower than the w/cm of a conventional cementitious composition used as a reference or starting point when designing a new cementitious composition. In summary, the defined w/cm arrived at by, or used when, apportioning mineral fines between “cementitious binder” and “aggregate” has been found to be a powerful new tool for designing and manufacturing concrete having predictable rheology, admixture requirements, and strength.
All four of the water-to-cement ratio (w/c), defined or design w/cm, actual w/cm, and w/p can be useful when designing and manufacturing concrete having a desired strength (e.g., compressive strength) and rheology (e.g., slump). The w/c is useful in understanding and predicting the nature and extent of hydration of Portland cement. The design w/cm, actual w/cm, and w/p are useful in understanding and predicting the combined strength and rheological attributes provided by the Portland cement, SCM, and mineral fines fractions.
The foregoing design and manufacturing criteria were initially discovered when designing concrete and mortar using limestone powder (e.g., having a D90 in a range of about 50 μm to about 200 μm and a D10 in a range of about 1 to about 30 μm). It was determined that limestone powder (e.g., Marble White 80 of Specialty Minerals), which is used as a fine white aggregate in precast concrete and glass fiber reinforced concrete (GFRC), can be apportioned between the cementitious binder and aggregate portions when designing precast concrete and GFRC having reduced clinker content. In example embodiments, the amount of Portland cement (e.g., white cement) was reduced by about 50-60%, with a portion of the “removed” white cement being “replaced” with a white-colored GGBFS and another portion being “replaced” by simply increasing the amount of Marble White 80 previously used only as “aggregate.” In such mixes, a portion of limestone powder was deemed “cement” for purposes of defining the cementitious binder content and another portion was deemed “aggregate” to arrive at proper volume. The resulting compositions had similar or higher strength than commercial compositions made using only white cement as cementitious binder. Examples of cementitious compositions made using a ternary blend of white cement, white-colored GGBFS, and limestone powder are disclosed in U.S. Pat. No. 9,957,196, the disclosure of which is incorporated herein in its entirety.
In particle size optimized compositions, the cement, SCM, and mineral fines fractions can have complementary PSDs that yield a cementitious binder system having a broadened PSD compared to the individual particulate components. The mineral fines are generally coarser than and have a particle size distribution (PSD) that complements rather than entirely matches and overlaps the PSD of the hydraulic cement. Using a fine or ultrafine SCM that is finer than hydraulic cement can also complement rather than match the PSD of the hydraulic cement. An example is fine fly ash (FFA) or ultrafine fly ash (UFFA) formed by grinding or classifying fly ash to remove or comminute coarse particles so as to have a D90 of less than about 25 μm, 20 μm, 17.5 μm, 15 μm, 12.5 μm, 10 μm, or 8 μm. Another example is silica fume. Another example is fine GGBFS having a D90 of less than about 30 μm, 25 μm, 22.5 μm, or 20 μm. Another is ultrafine natural pozzolan (e.g., ultrafine pumice, volcanic ash, calcined shale, or metakaolin formed by ultragrinding) having a D90 of less than about 25 μm, 20 μm, 17.5 μm, 15 μm, 12.5 μm, 10 μm, or 8 μm. Together, fine or ultrafine SCM, medium size hydraulic cement (e.g., OPC or narrow PSD cement), and relatively “coarse” mineral fines having a D90 between about 30 μm, 40 μm, or 50 μm to about 80 μm, 100 μm, 150 μm, 200 μm, or 300 μm, yield a ternary blend with an overall PSD that is substantially broader than the respective PSDs of the individual components. This approach reduces water demand, increases particle packing density of cementitious and SCM particles, increases paste density, increases SCM reactivity, and permits mineral fines to provide a powerful filler effect. In this way, mineral fines can increase strength due to the filler effect without providing too many fine or ultrafine particles (as occurs when using ultrafine or nano-limestone) that would otherwise compete with the cement and SCM particles when filling the fine and ultrafine regions of the overall PSD of the powder (cementitious binder plus mineral fines).
Fine SCMs are highly reactive and can impart substantially higher early and/or late strength compared to SCMs of normal PSD. Fine and ultrafine SCMs typically begin reacting after the cement fraction initially sets to form a rigid or semi-rigid structure. Nonetheless, during initial mixing and placement, fine SCMs, even ultrafine fly ash (UFFA), are at least temporarily “unreactive,” do not consume water other than by surface wetting, and therefore can greatly reduce water demand. Using less water to achieve the same rheology can substantially increase both short and long-term strengths. Therefore, using a fine or ultrafine SCM in place of at least some of the fine or ultrafine cement particles can substantially improve flow and strength. It may also be beneficial in some cases to include a coarse SCM, such as dedusted fly ash having a D90 in a range of about 75 μm to about 125 μm and a D10 in a range of about 10 μm to about 30 μm, to augment the coarse particles provided by mineral fines. The coarse SCM can provide additional strength by additional filler effect, later age pozzolanic reactions, and/or denser paste.
It was also determined that replacing a portion of hydraulic cement with mineral fines and one or more SCMs having pozzolanic properties can alter the balance of calcium, silicate, aluminate, and sulfate ions in the mixture, which can have a moderate to profound effect on the hydration mechanism. Substantially altering the ion balance in the aqueous solution during initial mixing and/or in the pore solution after setting, can create problems, such as reduced early strength, reduced late-age strength, and loss of workability. It was determined that such problems can be addressed and at least partially offset by adding minor quantities of one or more common and relatively inexpensive additives.
For example, it was discovered that adding a relatively small amount of lime, such as quicklime or hydrated lime (e.g., Type S lime used in mortar), can significantly increase early and late age strengths. Without being bound to theory, it is hypothesized that using SCMs having pozzolanic activity consumes calcium ions pozzolanically and lowers the pH to below what is required for proper setting, early strength development, and/or late age strength development. Adding a small but significant amount of quicklime or hydrated lime, which is only slightly soluble in water, up to and somewhat exceeding the amount required to form a saturated calcium hydroxide solution, may increase the pH and restore proper calcium ion concentration during early hydration and setting and also provide calcium ions and higher pH to increase later pozzolanic reactions. However, using too much lime can be detrimental because amounts that cannot ultimately dissolve or otherwise be consumed in the pozzolanic reaction may decrease mortar strength (e.g., because hydrated lime particles that form part of the cement paste are very soft and can act as a weak filler). Quicklime, if not fully hydrated to form hydrated lime in situ before final set, can be deleteriously expansive. It may be preferable to use hydrated lime, which is already hydrated and therefore not expansive, when it is desired to add more lime than what can readily dissolve. Nevertheless, quicklime can be desirable due to its higher solubility than hydrated lime if added in amounts that can quickly dissolve or otherwise be consumed during early stages of mixing, setting, and hardening.
In addition, the use of SCMs having pozzolanic activity and mineral fines may negatively affect sulfate balance, leading to loss of workability, set retardation, delayed strength development, and lower ultimate strength. For example, when SCMs and mineral fines replace Portland cement, the quantity of sulfate carried by the Portland cement is reduced by the same percentage as the percent reduction in Portland cement. However, the increased w/c resulting when maintaining the same or even lower w/cm can change how Portland cement hydrates and alter proper sulfate balance. In theory, a higher w/c may mean faster consumption of sulfate and hydration of the aluminate and aluminoferrite minerals in cement clinker. For example, it was observed by researchers at Calmetrix, Inc. that using a superplasticizer to deflocculate cement particles exposes more of the cement particle surfaces to hydration, resulting in faster consumption of sulfate and higher sulfate requirement. A similar phenomenon may occur when the w/c is increased by replacing OPC with SCMs and mineral fines, which do not react with and consume significant water apart from adsorption during initial mixing. That means more water is available to wet the cement particles and a greater surface area of the cement grains may be exposed to water, resulting in faster consumption of sulfate and higher sulfate requirement.
Another cause of sulfate deficiency is the presence of aluminates in SCMs such as fly ash, GGBFS, and natural pozzolans, which can consume sulfate ions required for proper hydration of Portland cement. This can result in loss of workability, set retardation, delayed strength development, and long-term strength reduction. Some mineral fines may also include aluminates that can cause sulfate deficiency. While limestone may theoretically partially offset the effects of insufficient sulfate through formation of calcium carboaluminates, this reaction and its interplay with ettringite formation and later depletion of ettringite (AFt) to form monosulfoaluminates (AFm) are not well understood. It may be safer to assume that limestone powder cannot completely offset negative effects of insufficient sulfate, particularly because limestone powder has very low solubility, while uncontrolled hydration of aluminates can occur in minutes. Limestone powder may provide positive effects later on, but during early stages of hydration and set control it is better to ensure there is sufficient sulfate to control hydration of aluminates in the cement and SCM fractions. In addition, there is some evidence that added sulfate helps SCMs to more quickly and completely react pozzolanically over time, which increases ultimate strength.
Whether or not there is a sulfate deficiency can be determined using calorimetry, such as calorimeters provided or operated by Calmetrix, and measuring heat release as a function of time when a cement blend is subjected to hydration conditions. A properly sulfate-balanced cement binder system will usually have a signature heat release curve. Too little sulfate results in insufficient formation of ettringite and/or premature depletion of ettringite to monosulfate, which permit aluminates to hydrate uncontrollably with water to form calcium aluminate hydrates. Rapid formation of calcium aluminate hydrates causes loss of workability and delayed setting (e.g., by coating tricalcium silicate crystals and inhibiting their proper hydration). It has been found that adding supplemental sulfate, such as plaster of Paris, gypsum, anhydrite, or alkali metal sulfate, can improve rheology, avoid loss of workability, reduce or eliminate delayed setting, and provide higher early and ultimate strengths. As with supplemental lime, the amount of supplemental plaster of Paris, gypsum, or anhydrite should not substantially exceed the ability of it or its hydration products to dissolve and be consumed by aluminates since calcium sulfate dihydrate has low solubility and will act as a weak filler if it remains unreacted within cement paste over time. In addition, unhydrated plaster of Paris that persists after setting can cause delayed ettringite formation and long-term expansion.
In summary, use of the disclosed design criteria for using mineral fines, coupled with use of one or more SCMs, sometimes with addition of supplemental lime and/or sulfate, has yielded mortar and concrete of acceptable or superior strength at greatly reduced clinker content. In some cases, mortar and concrete with low clinker content have the same or higher strength compared to control mixes made with high clinker content.
In the case where wet or dried concrete washout fines are used as part or all of the mineral fines, they can be passivated by mixing with CO2 either before or during manufacture of freshly mixed concrete. Due to the formation of nano-sized mineral particles in situ (e.g. CaCO3 and/or MgCO3), the resulting composition may include at least two different size categories of mineral particles that can complement the particle size distribution of the hydraulic cement binder: (1) nano-sized mineral particles formed in situ within the fresh cementitious mix (e.g., having a D90 less than 0.5 μm) and (2) macro-sized mineral fines of larger size (e.g., having a D90 of 50-300 μm) processed separately from the cementitious binder. The result is a ternary blend of complementary-sized particles that synergistically interact to form a cementitious paste of high strength per unit weight of cementitious binder. If a fine or ultrafine SCM is used, a quaternary blend is formed comprising in situ formed nano-sized mineral particles, fine or ultrafine SCM, hydraulic cement, and mineral fines.
Information regarding hydraulic cement, supplementary cementitious materials (SCMs), binary, ternary, and quaternary cement-SCM blends, and cementitious compositions that can be made using such materials are disclosed in U.S. Pat. Nos. 7,799,128, 7,972,432, 8,323,399, 8,377,201, 8,414,700, 8,551,245, 8,845,940, 8,974,593, 9,067,824, 9,102,567, 9,108,883, 9,376,345, 9,388,072, 9,492,945, 9,738,562, 9,758,437, 9,790,131, 9,957,196, 10131575, 10246379, and 10350787, the disclosures of which are incorporated herein in their entirety.
The term “Dx”, where x is a numeric value between 0 and 100 and Dx is a designated particle size, means the percentage of particles in a distribution of particles that is at or below the designated particle size. For example, a particulate material with a “D90” of 75 μm means that 90% of the particles are 75 μm or smaller (i.e., are 90% passing at 75 μm, or No. 200 sieve) and 10% of the particles are larger than 75 μm. Similarly, a particulate material with a D10 of 20 μm means that 10% of the particles are 20 μm or smaller (i.e., are 90% passing at 20 μm) and 90% of the particles are larger than 20 μm. A particulate material with a D50 of 45 μm means that 50% of the particles are 45 μm or smaller (i.e., are 50% passing at 45 μm) and 50% of the particles are larger than 45 μm.
The terms “water-to-cement ratio” and “w/c refer to the ratio of water to hydraulic cement (e.g., Portland cement) and is typically expressed as a weight ratio. For example, a cementitious composition comprising 300 pounds of water and 400 pounds of hydraulic cement would have a water-to-cement ratio (w/c) of 0.75. The term “w/c” as used herein typically disregards and does not consider supplementary cementitious materials (SCMs) and mineral fines. The w/c does consider sulfate added to control setting of hydraulic cement and may also consider the amount of additives, such as supplemental lime and supplemental sulfate, that provide calcium and sulfate ions and which augment the calcium and sulfate ions provided by the hydraulic cement.
The terms “water-to-cementitious binder ratio” and “w/cm” are typically understood to refer to the ratio of water to total cementitious binder, including hydraulic cement and supplementary cementitious material(s) (SCM), but excluding unreactive mineral fines, and is typically expressed as a weight ratio. For example, a cementitious composition comprising 300 pounds of water and 600 pounds of combined hydraulic cement and SCM(s) would have an actual water-to-cementitious binder ratio (w/cm) of 0.5. The “actual w/cm” as used herein is generally synonymous with the common meaning of the term “w/cm” as used by ASTM, AASHTO, EN, engineers, concrete companies, or other established standards.
The terms “defined water-to-cementitious binder ratio,” “defined w/cm” and “design w/cm” differ from the w/c and (actual) w/cm because the former also include or account for mineral fines defined or apportioned as “cementitious binder” in addition to the hydraulic cement and SCM(s). The defined w/cm is typically expressed as a weight ratio. For example, a cementitious composition comprising 300 pounds of water and 600 pounds of combined hydraulic cement, SCM, and apportioned mineral fines would have a defined w/cm (or design w/cm) of 0.5. The defined w/cm typically disregards and does not consider the portion of mineral fines defined or apportioned as “aggregate”, which can be thought of as simply a non-reactive filler or ultrafine aggregate within or that augments the cement paste.
The terms “water-to-powder ratio” and “w/p” refer to the ratio of water to total cementitious binder and powder, including hydraulic cement, supplementary cementitious materials (SCMs), and some or the entirety of mineral fines. The “w/p” is typically expressed as a weight ratio. For example, a cementitious composition comprising 300 pounds of water and 750 pounds of combined hydraulic cement, SCM, and total mineral fines that are not true aggregate has a water-to-powder ratio (w/p) of 0.4. The w/p as used is different than the defined w/cm because it also accounts for the portion of mineral fines apportioned to the aggregate.
The “cement factor” relates to the amount of cementitious binder and/or cement paste relative to the amount of aggregate. In general and within limits, increasing the cement factor typically increases strength at a given w/cm. An increased cement factor can reduce the tendency of the cementitious composition to experience bleeding or segregation, improving workability, cohesiveness, finishability, and overall performance. However, it can also increase the propensity for plastic shrinkage, drying shrinkage, and/or autogenous shrinkage. One skilled in the art can select an appropriate cement factor in combination with the actual w/cm, defined w/cm and/or w/p to yield concrete having desired performance attributes.
The terms “hydraulic cement” and “cement” include Portland cement, cements defined by ASTM C150 (Types I-V), blended cements defined by ASTM C595 and C1157, and similar materials that contain one or more of the four clinker minerals: C3S (tricalcium silicate), C2S (dicalcium silicate), C3A (tricalcium aluminate), and C4AF (tetracalcium aluminoferrite). Other examples of hydraulic cement include white cement, calcium aluminate cement, high-alumina cement, magnesium silicate cement, magnesium oxychloride cement, oil well cements (e.g., Type VI, VII and VIII), magnesite cements, calcium sulfoaluminate (CSA) cement, supersulfated cements, geopolymer cement, and combinations of these. Ground granulated blast-furnace slag (GGBFS) and other slags that include one or more clinker minerals may also function as hydraulic cement. They also qualify as SCMs. Some highly reactive class C fly ashes have self-cementing properties and can be defined, if desired, to provide a portion of the “hydraulic cement.”
Consistent with defining GGBFS, slags, and reactive fly ashes as “hydraulic cement,” alkali-activated cements (e.g., alkali-activated class C fly ash, alkali-activated GGBFS, and the like) sometimes known as “geopolymer cements,” are also examples of “hydraulic cements.” Geopolymer cements can benefit from the use of mineral fines as defined herein that are coarser than the particles used to make geopolymer cement. In the case of geopolymer cements or other cements that may be deficient in calcium ions, a source of calcium and/or magnesium ions may be added to react with the CO2 to form nano-sized mineral particles.
The terms “supplementary cementitious material” and “SCM” include materials commonly used in the industry as partial replacements for Portland cement in concrete, mortar, and other cementitious materials, either in blended cements or by self-blending by end users. Examples include moderate to highly reactive materials with both cementitious and pozzolanic properties (e.g., GGBFS, Class C fly ash, and steel slag), moderate to highly reactive pozzolanic materials (e.g., silica fume and activated metakaolin), and low to moderately reactive pozzolanic materials (e.g., Class F fly ash, volcanic ash, natural pozzolans, trass, calcined shale, calcined clay, and ground glass). Through alkali activation, it is possible for some SCMs to become hydraulically reactive. In a sense, the pozzolanic reaction is a form of alkali activation, albeit by less basic and/or lower soluble calcium ions as compared to more basic and/or higher soluble sodium or potassium ions as in typical geopolymer cements.
The term “mineral fines” refers to waste mineral fines produced during the manufacture of crushed rock, such as the manufacture of aggregates used in concrete. Crushed rock and sand is typically graded using wire meshes or screens with holes or passages of a specified size. Coarse aggregates are typically separated from finer materials by collecting the larger rock pieces and particles that are mostly or entirely retained on a screen having a given mesh size, typically a No. 4 sieve (4.75 mm). Medium aggregates (e.g., pea gravel) and fine aggregates (e.g., sand) are similarly those materials retained on a screen having an appropriate mesh size. Sand (fine aggregate) that is manufactured by milling and/or that passes through a No. 4 sieve (4.75 mm) is commonly screened using a 100 mesh screen, which retains particles of about 150 μm and larger. Particles that fall through the screens are quarry fines. In addition, coarse, medium and fine aggregates can be washed to remove fines adhered to the surface. This material is also quarry fines. In some cases quarry fines are discarded in the state in which they are made. In other cases they are put through a mill to generate a finer particulate material (i.e., mine or agricultural rock dust). For example, rock dust can be milled to 100 mesh (approximately 150 μm) and smaller, such as 200 mesh (approximately 75 μm) and smaller. Quarry fines are advantageously sized so as to have a D90 in a range of about 50-150 μm, or about 55-125 μm, or about 60-100 μm, or about 70-90 μm.
The term “mineral fines” refers to fines of any mineral, including but not limited to, waste aggregate particles or fines, waste or manufactured limestone fines, quarry fines, shale flue dust from manufacturing lightweight calcined shale aggregates, granite fines, stone dust, rock dust, marble dust, mine tailings, pulverized bottom ashes, pulverized metallurgical slags, waste or pulverized shale from shale oil extraction, and waste or pulverized sand from tar sand extraction, ground recycled concrete, and concrete washout fines (wet or dried). Mineral fines many contain basaltic minerals, other siliceous minerals, and igneous minerals. Virtually any particulate mineral material can used as and/or processed or pulverized to be mineral fines. Unless otherwise specified, the terms “mineral fines” and “quarry fines” are understood to include “limestone powder” (e.g., ground limestone powder).
In some embodiments, quarry fines are advantageously produced as a byproduct of the production of limestone aggregates and will comprise primarily limestone (e.g., calcite and/or dolomite). Calcite is a mineral having the chemical formula CaCO3. Dolomite contains a mixture of CaCO3 and MgCO3 and may thought of as having the chemical formula CaMg(CO3)2. Dolomite found in nature does not necessarily have a 1:1 ratio of CaCO3 and MgCO3. Quarry fines many also contain basaltic and other siliceous minerals but advantageously contains at least 50%, 60%, 70%, 80%, 85%, 90%, 95% or 98% calcite and/or dolomite. Some amount of aluminosilicate clay or mica are permissible so long as they are not unduly expansive and/or do not adversely affect rheology to an impermissible degree.
The term “limestone powder” refers to ground minerals containing mostly calcite and/or dolomite. Limestone powder is typically manufactured for use as limestone and will generally be a more pure form of the mineral with less contaminants than quarry fines or rock dust. Nevertheless, many limestone powders are produced by aggregate manufacturers that also produce quarry fines and may even be quarry fines, albeit a more pure form. Thus, limestone powder, quarry fines, and/or rock dust may be synonymous in some cases. In some cases, limestone powders are made from white limestone powders that have high brightness so that they can be used in decorative precast concrete compositions. In other cases, they can be off-white or grey. Limestone powders that are particularly advantageous for use in the disclosed compositions and methods can have a D90 in a range of about 50-150 μm, or 55-125 μm, or 60-100 μm, or 70-90 μm.
Mineral fines may also comprise a wider range of particles and have a more gritty or sandy consistency. In such cases, a smaller proportion of mineral fines may be defined as “cementitious binder” and larger proportion defined as “aggregate.” Mineral fines of any size range can be analyzed to determine particle size distribution and apportioned between cementitious binder and aggregate using the principles disclosed herein. In general, mineral fines that are coarser and less processed are lower cost and can substitute for a relatively larger portion of aggregate to further reduce cost of the cementitious composition. Depending on the effect of coarse mineral fines on rheology and/or strength, the cutoff particle size between “cementitious binder” and “aggregate” can be higher or lower to account for such rheological and/or strength differences.
The term “coarse aggregate” generally refers to aggregate particles that are mostly or entirely retained on a No. 4 sieve, and are generally at least 4.75 mm ( 3/16 inch) in size, up to about 5 inches, 4 inches, 3 inches, 2 inches, 1.5 inch, 1 inch, ¾ inch, or ½ inch. The term “medium aggregate” generally refers to a subset of coarse aggregate, but of smaller average size (e.g., pea gravel, which can include particles ¼ to ½ inch in size and/or ⅛ to ¼ inch in size). Coarse aggregates can be made from any appropriate mineral, such as limestone, granite, basalt, other geological materials, and metallurgical slags. Hence, quarry fines may include any leftover fines from making coarse aggregate.
The term “fine aggregate” (e.g., sand) generally refers to aggregate particles that mostly or entirely pass through a No. 4 sieve, and are generally less than 4.75 mm ( 3/16 inch) in size and retained on a screen having an appropriate mesh size. Sand (fine aggregate) can be manufactured by milling and/or removed from coarse aggregate by screening. To control consistency, fine aggregate is commonly screened using a No. 100 sieve, which retains particles of about 150 μm and larger, or a No. 140 sieve, which retains particles of about 105 μm and larger, or a No. 200 sieve, which retains particles of about 75 μm and larger. Particles that fall through the screen(s) are collected and discarded as quarry fines. Fine aggregates can be made from any appropriate mineral, such as limestone, granite, basalt, other geological materials, and metallurgical slags. Hence, mineral fines may include any leftover fines from making fine aggregate.
According to one embodiment, the PSD of the hydraulic cement, blended cement, supplementary cementitious material (SCM), mineral fines, and in-situ formed mineral particles can be defined by their respective D10, D50 and D90, with the D10 approximating the lower PSD endpoint (“LEP”), the D90 approximating the upper PSD endpoint (“UEP”), and the D50 approximating the mean particle size (“MPS”) of the PSD. In other embodiments, the D1, D5, D15, d20 or intermediate value can be used as the approximate LEP, the D80, D85, D95, D99, or intermediate value as the approximate UEP, and the D40, D45, D55, D60 or intermediate value as the approximate MPS.
It can be useful to select cementitious binder materials and mineral fines having complementary rather than completely overlapping PSDs as defined by their respective D90s, D50s and D10s. This includes, for example, selecting a hydraulic cement of intermediate fineness, an SCM finer than the hydraulic cement, and mineral fines coarser than the cement, and optionally a coarse SCM coarser than the cement.
The PSD of a particulate material or blend of particles can be determined according to accepted methods for determining particle sizes of ground or otherwise non spherical materials. Particle size can be measured using any acceptable method and/or methods yet to be developed. Examples include sieving, optical or electron microscope analysis, laser diffraction, x-ray diffraction, sedimentation, hydrometer analysis, elutriation, microscope counting, Coulter counter, and Dynamic Light Scattering.
A. Hydraulic Cement
A common and useful hydraulic cement that can advantageously be used in the disclosed compositions and methods is ordinary Portland cement (OPC), as defined by ASTM C-150 and which include Types I-V cement and their variants. Types I, II, and V cements typically have a Blaine fineness between about 350-450 m2/kg (3500-4500 cm2/g). Type III cement typically has a Blaine fineness between about 450-600 m2/kg (4500-6000 cm2/g). Type 1L, 1P, and C-595 cements can also be used.
Other types of hydraulic cement include aluminate cements, super-sulfated cements, alkali-activated cements, geopolymer cements, and the like.
Alternatively, narrow PSD cements can be used, which have different PSDs than Types I-V cement. Narrow PSD cements are characterized as having a spread (e.g., UEP-LEP) and endpoint ratio (e.g., UEP/LEP) that are lower than the spread and endpoint ratio, respectively, of ordinary Portland cement (OPC), often substantially lower. Lowering the UEP may advantageously reduce the volume of unhydrated cement, which increases hydration efficiency. Raising the LEP reduces water demand. In one embodiment, a narrow PSD cement fraction can have a LEP that is substantially higher, and a UEP that is substantially lower, than the respective LEP and UEP of OPC (e.g., for both Fuller and Tsivilis distributions).
Nevertheless, OPC can be used in connection with the compositions and methods disclosed herein and may be a primary source of hydraulic cement to the extent it is readily available and less expensive than narrow PSD cement. However, implementing the present invention using OPC may in time open the door for the use of narrow PSD cements once manufacturers realize the power and predictability of using carefully selected particle sizes for the various cement binder components. The same is true for fine and ultrafine SCMs, which may become more valuable and widely used in making ternary blends once the power and simplicity of the disclosed methodologies are better understood by cement, concrete, and admixture companies.
The upper endpoint (UEP) of hydraulic cement can be selected to provide desired reactivity and/or fineness in conjunction with or independent of the lower endpoint (LEP) and/or a desired particle packing density in conjunction with coarser and mineral fines. The UEP (e.g., D85, D90, D95 or D99) can be equal to or less than about 45 μm, 42.5 μm, 40 μm, 37.5 μm, 35 μm, 32.5 μm, 30 μm, 27.5 μm, 25 μm, 22.5 μm, 20 μm, 18 μm, 16.5 μm, 15 μm, 13.5 μm, 12 μm, or 11 μm. The lower UEP range limit can be about 8 μm, 9 μm, 10 μm, 11 m, 12 μm, 13 μm, 14 μm or 15 μm.
The lower endpoint (LEP) can be selected to provide desired water demand and/or fineness in conjunction with or independent of the upper endpoint (UEP) and/or desired particle packing density in conjunction with one or more finer SCMs. The LEP (e.g., D1, D5, D10 or D15) can be equal to or greater than about 0.8 μm, 1.0 μm, 1.25 μm, 1.5 μm, 1.75 μm, 2 μm, 2.5 μm, 3 μm, 4 μm, 5 μm, 6 μm, 7 μm, or 8 μm. The upper LEP limit can be about 6 μm, 8 m, 10 μm, 12 μm or 15 μm.
The UEP and LEP can also define the spread (UPE-LEP) of the hydraulic cement. For example, and depending on the UEP and LEP of the cement and ability or limitations of processing equipment to produce narrow PDS cements, the spread can be less than about 40 m, 35 μm, 30 μm, 25 μm, 22.5 μm, 20 μm, 17.5 μm, 15 μm, 13 μm, 11.5 μm, 10 μm, 9 μm, 8 m, 7 μm, 6 μm, 5 μm, or 4 μm.
In some cases, the ratio UEP/LEP can define a narrow PSD cement having desired reactivity, fineness and/or particle packing density in conjunction with and mineral fines and one or more SCMs. The UEP/LEP (e.g., D90/D10) of narrow PSD cements can be less than the ratio of Types I-V cements as defined by ASTM C-150. According to several embodiments, the UEP/LEP can be less than or equal to about 30, 27.5, 25, 22.5, 20, 17.5, 15, 12.5, 10, 8, 6, 5, 4.5, 4, 3.5, 3, 2.5 or 2.
It will be appreciated that defining the PSD of a narrow PSD cement by ratio UEP/LEP is not limited by a particular UEP or LEP or range of particle sizes. For example, a first hypothetical narrow PSD cement having a D90 of 15 μm and a D10 of 3 μm has a UEP/LEP (i.e., D90/D10) of 5 and spread (D90-D10) of 12 μm. By comparison, a second hypothetical narrow PSD cement having a D90 of 28 μm and a D10 of 7 μm has a UEP/LEP (i.e., D90/D10) of 4 and a spread (D90-D10) of 21 μm. While the spread of the second hypothetical narrow PSD cement is greater the UEP/LEP (i.e., D90/D10) is smaller than those of the first hypothetical narrow PSD cement. Thus, the second hypothetical cement has a narrower PSD compared to the first hypothetical cement as defined by UEP/LEP (i.e., D90/D10) even though the spread is greater.
B. Mineral Fines
Mineral fines, such as quarry fines, limestone powder, rock dust, safety mine dust, mine tailings, marble dust, stone dust, shale dust, granite fines, ground bottom ash, ground metallurgical slags, waste or pulverized shale from shale oil extraction, waste or pulverized sand from tar sand extraction, ground recycled concrete, concrete washout fines (wet or dried), and other waste or manufactured minerals can be blended with hydraulic cement, such as OPC or narrow PSD cement, to provide particles that are larger than the coarsest cement particles. Mineral fines can replace some of the cement particles, optionally some of the SCM particles, optionally some of the aggregate, provide a “paste aggregate” or filler to complement or augment the total quantity of cementitious binder particles in the cement paste, increase particle packing density and paste density, provide a filler effect using a less expensive component, lower the w/p and/or w/cm, increase fluidity, increase strength, and reduce shrinkage and creep.
When defining mineral fines as “powder” for purposes of determining the w/p, the UEP (e.g., D85, D90, D95 or D99) of the mineral fines can be less than about 500 μm, about 400 μm, about 300 μm, 250 μm, 200 μm, 175 μm, 150 μm, 125 μm, 110 μm, 100 μm, 90 μm, 85 μm, 80 μm, 75 μm, 70 μm, 65 μm, or 60 μm, with a lower UEP range limit of about 30 μm, 40 μm, 50 μm, or 60 μm. In some embodiments, the mineral fines have a D90 in a range of about 50 μm to about 150 μm, preferably about 55 μm to about 125 μm, more preferably about 60 μm to about 100 μm, even more preferably about 70 μm to about 90 μm. Sandier, coarser mineral fines can have particles up to about 5 mm, 4 mm, 3 mm, 2 mm, 1 mm, or 0.5 mm (500 m). In such cases, the quantity of mineral fines apportioned as “aggregate” will typically be substantially greater than the amount apportioned as “cementitious binder” (as illustrated in
The LEP (e.g., D1, D5, D10 or D15) of the mineral fines can be equal to or greater than about 2 μm, 2.5 μm, 5 μm, 7.5 μm, 10 μm, 12.5 μm, 15 μm, 17.5 μm, 20 μm, 25 μm, 30 μm, 35 μm, 40 μm, 45 μm, or 50 μm, or be within a range defined by any two of the foregoing values.
Example mineral fines that can be used in the disclosed compositions and methods can be obtained from Staker Parson of Ogden, Utah. They are manufactured at the Keigley quarry located in Genola, Utah, further milled to about 200 mesh minus (75 μm and smaller), and sold primarily as mine safety dust (or Coal Mine Rock Dust) and secondarily as a limestone-based soil amendment by Oldcastle (parent company of Staker Parson). A particle size analysis of the Coal Mine Rock Dust was performed using a Microtrac-X100 particle size analyzer and determined to have a very broad, flat PSD curve, with particles as large as about 135 μm, a small proportion (3%) smaller than 1 μm, a D90 of about 70 μm, a D50 of about 17 μm, and a D10 of about 2.5 μm. Assuming the particle size cutoff were 30 μm, which is roughly the d70, one can design and manufacture a cementitious composition in which about 70% of the rock dust is defined as “cementitious binder” and about 30% as “aggregate,” and that has reasonably predictable rheology (e.g., slump, yield stress and/or viscosity) and strength. Alternatively, assuming the particle size cutoff were 22 μm, which is roughly the D60, one can design and manufacture a cementitious composition in which about 60% of the rock dust is defined as “cementitious binder” and about 40% as “aggregate,” and that has reasonably predictable rheology (e.g., slump, yield stress and/or viscosity) and strength.
An example limestone powder that can be used in the disclosed compositions and methods can be obtained from Specialty Minerals of Lucerne Valley, Calif. It is a ground calcium carbonate sold under the name Marble White 80. It has a D90 of about 150 μm. Marble White 80 can effectively be apportioned between cementitious binder and aggregate to reduce clinker content when used together with Portland cement (e.g., white cement) and one or more SCMs (e.g., GGBFS, ground volcanic ash, fly ash, and/or ground pumice). Another example is Blue Mountain Feed Flour, which has a D90 of about 100 μm and a D50 of about 43 μm and which is whiter than Coal Mine Rock Dust but less white than Marble 80.
C. Supplementary Cementitious Materials
The PSD of one or more SCM fractions can be defined by the D10, D50 and D90, with the D10 approximating the lower PSD endpoint (LEP), the D90 approximating the upper PSD endpoint (UEP), and the D50 approximating the mean particle size (“MPS”). In other embodiments, the D1, D5, D15, d20 or intermediate value can be used to approximate LEP, the D80, D85, D95, D99 or intermediate value to approximate UEP, and the D40, D45, D55, D60 or intermediate value to approximate MPS. In some cases, the PSD of a fine SCM fraction may be defined mainly or exclusively in terms of the MPS and/or the UEP, while the PSD of a coarse SCM fraction may be defined mainly or exclusively in terms of the MPS and/or the LEP.
Blending a fine or ultrafine SCM fraction with OPC or narrow PSD cement can “replace” at least a portion of fine or ultrafine cement particles, help disperse cement particles, fill fine pore spaces, increase fluidity, increase strength, increase particle packing density, and decrease permeability. The UEP (e.g., D85, D90, D95 or D99) of a fine or ultrafine SCM can be less than about 25 μm, 22.5 μm, 21 μm, 20 μm, 19 μm, 17.5 μm, 15 μm, 13 μm, 12 μm, 11 m 10 μm, 9 μm, 8 μm, 7 μm, 4.5 μm, 4 μm, 3.5 μm, or 3 μm or any range defined by two of the foregoing sizes. The lower UEP range limit can be about 1 μm, 2 μm, 3 μm, 4 μm, 6 μm, 8 μm, 10 μm, 12 μm, 15 μm, 17 μm, or 19 μm. The LEP (e.g., D1, D5, D10 or D15) can be equal to or greater than about 0.01 μm, 0.03 μm, 0.05 μm, 0.075 μm, 0.1 μm, 0.25 μm, 0.5 μm, 0.75 m, 1.0 μm, 1.25 μm, 1.5 μm, 1.75 μm, 2 μm, 2.5 μm, 3 μm, 4 μm, or 5 μm. The upper LEP range limit can be about 8 μm, 6 μm, 5 μm or 4 μm.
In some embodiments, it may be desirable to include a coarse SCM fraction that is as coarse or coarser than the mineral fines. Coarse SCMs can provide additional filler effect to increase strength, particle packing density, and paste density, reduce water demand, and provide late age pozzolanic activity. For example, using coarse fly and mineral fines can broaden the PSD of the overall cement blend but offer different benefits. Coarse fly ash can react pozzolanically over time but may not contribute significantly to early strength. Mineral fines do not react pozzolanically but can provide nucleation sites and/or form calcium carbonaluminates in order to accelerate early strength gain. Together, coarse fly ash and mineral fines can boost early and late strengths.
It should also be understood that ordinary SCMs can be used in the compositions and methods disclosed herein. For example, ordinary fly ash that has not been classified to form FFA or UFFA, or dedusted to form coarse fly ash (CFA), can be used to produce concrete of high strength when used in combination with mineral fines having a D90 in a range of about 50 μm to about 150 μm. GGBFS having a D90 between about 15-25 μm, 17-23 μm, 18-22 μm, or 19-21 μm has been found to be especially useful when combined with Portland cement of lower fineness (e.g., OPC), and mineral fines (e.g., limestone powder) coarser than the Portland cement.
D. In Situ Nano-Sized Mineral Particles
Optional nano-sized mineral particles formed by blending CO2 with concrete washout fines and/or in situ within a freshly mixed cementitious composition will typically have a D90 of less than 1 μm, 0.9 μm, 0.8 μm, 0.7 μm, 0.6 μm, 0.5 μm, 0.4 μm, 0.3 μm, 0.2 μm, 0.1 μm, 0.09 μm, 0.08 μm, 0.07 μm, 0.06 μm, 0.05 μm, 0.04 μm, 0.03 μm, 0.02 μm, or 0.01 μm.
A. Supplemental Lime
It can be beneficial to add supplemental lime to the cementitious compositions. Such lime is “supplemental” to lime released during hydration of hydraulic cements such as Portland cement. Supplemental lime can be added as quicklime (CaO), hydrated lime (Ca(OH)2) and/or Type S lime. Although quicklime is more soluble than hydrated lime, when exposed to water quicklime is converted into hydrated lime. Therefore, the solubility of hydrated lime, or calcium hydroxide, in water is generally a limiting factor for how much supplemental lime can be added before it becomes deleterious. The solubility of calcium hydroxide in water is reportedly 0.189 g/100 mL at 0° C., 0.173 g/100 mL at 20° C., and only 0.066 g/100 mL at 100° C. The temperature of concrete when hydrating is usually above 20° C. and below 100° C. Therefore, the solubility of hydrated lime is somewhere between 0.173 g/100 mL and 0.066 g/100 mL and decreases at increased temperature.
In general, hydrated lime (e.g., Type S lime) is readily available and easier and safer to handle than quicklime. Hydrated lime also does not consume water when mixed into a cementitious composition and therefore does not affect water demand as much as quicklime. It is also not expansive like quicklime, which expands when it hydrates. It has been found that hydrated lime typically works more predictably than quicklime, with similar or even superior results from the standpoint of early and late strength development.
In some embodiments, the amount of supplemental lime can be below, at, or above the amount required to achieve or maintain saturation in water. The amount of supplemental lime required to maintain a saturated pore solution is dependent on factors such as the amount of free lime released from the hydraulic cement during hydration, the amount of lime consumed during cement hydration and pozzolanic reactions, and the solubility of lime, which decreases with increased temperature. Increased temperature may accelerate consumption of lime, offsetting negative effects of decreased solubility. Using a more reactive pozzolan may deplete lime faster than a less reactive pozzolan. The ideal amount of supplemental lime is theoretically that amount that maintains a pore solution saturated with calcium ions over time in conjunction with lime released from the hydraulic cement and is consumed by pozzolanic reactions. A relatively small excess of supplemental lime can be added as a reservoir to provide additional lime as it is depleted.
In some embodiments, the amount of supplemental lime is 1-10 times, or 1.2-8 times, or 1.5-5 times the amount required to achieve saturation in the amount of added water. One purpose of adding supplemental lime is to maintain the pore solution at a pH similar to the pH when using OPC alone. Some SCMs, including fly ash and, in particular, ultrafine fly ash (UFFA), can rapidly deplete calcium ions and lower pH of the pore solution, which can interfere with normal cement hydration and/or retard pozzolanic reactions. Adding supplemental lime helps maintain a high pH characteristic of normal cement hydration and increase the rate of pozzolanic reactions. Because lime does not otherwise contribute to concrete strength but can actually weaken it, it has been found that using a relatively small amount of supplemental lime works better than using either no added lime or too much added lime. In some embodiments, the amount of supplemental lime based on the total weight of cementitious binder (cement, SCM and mineral fines apportioned to the cementitious binder) can be about 0.1% to about 10%, or about 0.125% to about 8%, or about 0.15% to about 6%, or about 0.2% to about 4.8%, or about 0.3% to about 4%, or about 0.4% to about 3%, or about 0.5% to about 2.5%, or about 0.6% to about 2%, or about 0.7 to about 1.8% (e.g., 0.8-1.6%).
B. Supplemental Sulfate
When there is insufficient sulfate to properly react with aluminates in the cementitious binder system, a supplemental sulfate source can be added, such as calcium sulfate hemihydrate (plaster of Paris), calcium sulfate dihydrate (gypsum), anhydrous calcium sulfate (anhydrite), and alkali metal sulfates (e.g., lithium sulfate). When used, the amount of supplemental sulfate based on the total weight of cementitious binder (cement, SCM and mineral fines apportioned to the cementitious binder) can be about 0.1% to about 6%, or about 0.15% to about 5%, or about 0.2% to about 4%, or about 0.3% to about 3%, or about 0.5% to about 2.5%, or about 0.6% to about 2%, or about 0.8% to about 1.6%.
Cementitious binder blends designed and manufactured as described herein can be used in place of OPC, site blends of OPC and SCM, interground blends, and other cements and blended cements known in the art. They can be used to make concrete, ready mix concrete, high performance concrete (HPC), ultrahigh performance concrete (UHPC), self-consolidating concrete (SCC) (also known as self-compacting concrete), bagged concrete, bagged cement, mortar, bagged mortar, grout, bagged grout, molding compositions, bagged molding compositions, or other fresh or dry cementitious compositions known in the art. Cementitious binder blends can be used to manufacture concrete and other cementitious compositions that include a hydraulic cement binder, water and aggregate, such as fine and coarse aggregates. Mortar typically includes cement, water, sand, and lime and is sufficiently stiff to support the weight of a brick or concrete block. Oil well cement refers to cementitious compositions continuously blended and pumped into a well bore. Grout is used to fill in spaces, such as cracks or crevices in concrete structures, spaces between structural objects, and spaces between tiles. Molding compositions are used to manufacture molded or cast objects, such as pots, troughs, posts, walls, floors, fountains, countertops, sinks, ornamental stone, building facades, and the like.
Water is both a reactant and rheology modifier that permits a fresh cementitious composition to flow or be molded into a desired configuration. Hydraulic cement reacts with water, binds the other solid components together, is most responsible for early strength development, and can contribute to later strength development. Blends with high packing density have reduced void space, which reduces water demand and increases workability for a given quantity of water.
Cementitious binder blends can be dry-blended or formed in situ when making a fresh cementitious composition containing water and aggregate. Cementitious binder blends include binary, ternary, quaternary, and other blends. In some embodiments, mineral fines and one or more SCMs are blended with hydraulic cement. In some embodiments, cementitious binder blends may include one or more chemical additives that affect the chemistry of the aqueous solution, such as accelerating, retarding, and/or water-reducing admixtures, supplemental lime, and supplemental sulfate.
Calcium carbonate in some mineral fines and/or formed in situ using CO2 can enhance strength development. While calcium carbonate has substantially lower solubility than lime (only 0.013 g/L at 25°), it can still contribute some quantity of calcium ions. It can also provide nucleation sites for the formation of cement hydration products, mainly calcium silicate hydrates, calcium sulfoaluminate hydrates, calcium carboaluminates, and calcium carboaluminoferrites, and the like.
The cementitious binder blend can be mixed with water and one or more aggregates to form concrete and other cementitious compositions (e.g., moldable compositions, precast concrete, GFRC, stucco, grout, mortar and the like). A blend of coarse and fine aggregates of standard size can be used in ready mixed concrete. Other cementitious compositions may exclude coarse aggregates and only include one or more grades of fine aggregate.
Admixtures known in the industry can be included in cementitious compositions. Examples include low-, medium- and/or high-range water reducers (e.g., lignosulfonates, sulfonated melamine formaldehyde condensate, sulfonated naphthalene formaldehyde condensate, polycarboxylate ethers), superplasticizers (e.g., polycarboxylate ethers), set controllers (e.g., sulfates), retardants (e.g., hydroxycarboxylic acids and carbohydrates), accelerators (e.g., alkali and alkaline earth metal salts), strength-enhancers (e.g., TEA, TIPA, THEED, other amines), corrosion inhibitors (e.g., nitrite salts), hydration stabilizers, and viscosity modifying agents (VMAs) (e.g., cellulosic ethers).
The water-to-cementitious binder ratio (w/cm) and water-to-powder ratio (w/p) can greatly affect rheology and strength. In general, lowering the amount of water increases strength but negatively affects flow, requiring a superplasticizer and/or water-reducing admixture to maintain proper flow. Thus, there is usually an inverse correlation and tradeoff between strength and rheology, all things being equal. Of course, poor rheology can also negatively affect strength if a fresh cementitious composition cannot be properly consolidated or compacted. In addition to w/cm and w/p, the “cement factor” can affect strength. The w/cm can be in any desired value in a range of about 0.2 to about 0.7. Concrete of low strength typically has a w/cm greater than about 0.55. Concrete of moderate strength can have a w/cm between about 0.45 and about 0.55. Concrete of moderately high to high strength can have a w/cm between about 0.33 and about 0.45. Concrete of high to very high strength can have a w/cm between about 0.22 and about 0.33. Ultrahigh performance concrete (UHPC) can have a w/cm between about 0.17 and about 0.25.
The design principals disclosed herein can provide reduced clinker and/or improved strength through a wide range of water-to-cementitious binder ratios and cement factors. Nevertheless, they have been shown to provide greater improvements in terms of reduced clinker and/or improved strength and/or reduced shrinkage at lower w/cm and/or higher cement factor compared to concrete made using OPC as sole binder or at higher concentrations relative to SCMs and other mineral additions.
Notwithstanding the principals disclosed herein relative to the beneficial use of mineral fines, concrete and mortar mixes have been made having reduced clinker at improved strength when using ultrafine fly ash (UFFA) and/or coarse calcined shale dust (e.g., flue dust) at moderate substitution levels and modestly high w/cm (i.e., between about 0.35 and about 0.485). This is attributed to the special qualities of such SCMs alone. For example, a UFFA having a D90 of about 8.5 or about 10.5 μm was found to provide the same or greater strength when substituted for cement in amounts of about 10-30%, or about 15-25% (e.g., 20%), compared to a control mix comprising 100% cement. In some cases, the UFFA was shown to provide a similar strength increase as silica fume at an OPC substitution level of 15% and a w/cm of 0.35. The UFFA was also shown to provide both greater strength and improved rheology at an OPC substitution level of 20% and a w/cm of 0.47 compared to a control mix comprising 100% cement. Calcined shale dust that was coarser than both OPC and fly ash was shown to provide greater strength and approximately the same rheology at an OPC substitution level of 15-25% (e.g., 20%) and a w/cm of 0.47 compared to a control mix comprising 100% cement.
Cementitious compositions can be made using any known method, while incorporating the materials disclosed herein. In some embodiments, a cementitious mix is manufactured by blending together a cementitious binder, mineral fines, aggregate, and water to form a fresh cementitious mixture. In some embodiments, CO2 can be added to the mixture, such as by sparging in CO2 gas, adding carbonated water, and/or adding crushed dry ice. A fine CO2 “snow” can be formed by expressing compressed CO2 from a nozzle and mixing the CO2 snow into the cementitious mixture using known means. An example mixing vessel is a central mixer or concrete mixing truck used to manufacture ready mixed concrete. Concrete washout fines can be passivated by reacting with CO2, such as before or while preparing a cementitious mix.
Freshly mixed concrete and other cementitious compositions are typically placed into a mold while in a plastic or flowable condition and then allowed to set up and harden within the mold. In some cases, the mold is a form, such as to make a footing, wall, pillar, piling, or other vertical structure. In the case of precast concrete, the mold can have the shape of a concrete barrier, structural concrete shape, decorative concrete, and the like. Forms for flatwork can hold concrete within a confined area with an exposed surface, which can be finished using a trowel, screed, float, polisher, and/or other known finishing device.
Reference is made to
Method 100 differs from a design or manufacturing method in which limestone powder (e.g., nano-limestone) is used as a filler to augment but not replace a portion of the cementitious binder, which may comprise Portland cement or a blend of Portland cement and one or more SCMs. In such case, there would be no beneficial reduction in cement clinker content but merely use of limestone powder as an additive or filler, effectively replacing a portion of the fine aggregate. While using limestone powder as an additive can increase the strength of concrete due to the filler effect, it comes at the cost of increased water demand, which requires the use of more water, thereby negating or reversing the strength benefit, and/or the use of expensive water reducing admixtures, which further increases cost. There is no environmental benefit from the standpoint of reducing the CO2 footprint of concrete when clinker content is not reduced. Because fine limestone powder can cost more than aggregate, replacing less expensive fine aggregate with more expensive limestone powder further increases cost.
Method 100 also differs from a design or manufacturing method in which limestone powder (e.g., nano-limestone) is used entirely as a partial substitute for Portland cement. In that case, there is a beneficial reduction in cement clinker content but also loss of strength and durability because the hydraulic cement particles are diluted with unreactive limestone particles. The only way to offset such strength loss would be to reduce the water to cement ratio (w/c), which reduces paste content, requiring either an increase in aggregate content, paste content or both, to maintain proper volume. Increasing aggregate content generally decreases strength and creates a harsher mix (i.e., more gritty and harder to finish). Increasing paste content merely adds back what was removed and typically requires several iterations to obtain the proper balance between paste content and w/c to obtain proper strength and rheology.
The tendency to use limestone powder as either an aggregate or cement substitute is based on conventional thinking and the standard practice of categorizing materials as either “cement” or “aggregate”. A major U.S. concrete company tried and failed to find a way to effectively use limestone powder in concrete: when they replaced a portion of the cementitious binder with limestone powder they obtained a beneficial cost reduction but suffered significant strength loss as well; when they added limestone powder in addition to the cementitious binder (i.e., as a filler or aggregate that replaced a portion of the fine aggregate) they obtained a beneficial increase in strength but at significantly increased cost because the limestone powder cost more than fine aggregate and more water reducing admixture was required. It did not occur to this company to split the difference and replace part of the cement with a first portion of the limestone powder and replace part of the fine aggregate with a second portion of the limestone powder (i.e., by defining or apportioning a first portion of limestone powder as “cement” or “cementitious binder” and a second portion as “aggregate” or “filler”), which unexpectedly can reduce cost while maintaining comparable strength, rheology, water demand, and admixture requirements. This inability to think outside the box is consistent with industry practices.
Simply stated, before the present invention, there was no known standard, guideline, or accepted industry practice for characterizing mineral fines as containing both “cementitious binder” and “aggregate” portions when designing and manufacturing concrete and other cementitious compositions. In fact, quarry fines, limestone powder, concrete washout fines, ground recycled concrete, mine tailings, and other mineral fines do not fit any definition of “cement” or standard definition of “aggregate” and are in fact neither. An expert in the field, when asked, stated that mineral fines such as quarry fines and/or limestone powder are neither cement nor aggregate and confirmed there currently is no ASTM standard for using these and other mineral fines in concrete or blended cement. Nor do most quarry fines and/or limestone powder fit the definition of a pozzolanic SCM. Therefore, treating mineral fines as any of “cement”, “SCM,” or “aggregate” is technically incorrect. Mineral fines fit no definitions other than “mineral addition” to cement. As such, the industry has haphazardly attempted to use mineral fines through trial and error testing but with no practical guidelines. The lack of understanding of how to knowledgeably and effectively categorize and utilize mineral fines explains why they are rarely if ever used in concrete but continue to pile up unused in enormous quantities.
The present invention seeks to overcome poor practices and confined thinking by defining or apportioning a first portion of mineral fines as “cement” (or “cementitious binder”) and a second portion as “aggregate” (or “filler”) for the purpose of designing and manufacturing concrete. When this simple, but heretofore unknown, practice is followed, it provides a simple yet highly effective way to design and manufacture concrete and other cementitious compositions having predictable rheology, admixture requirements, and strength. The inventive methods provide predictable rheology by factoring in a first portion of mineral fines into the determination of the defined w/cm to account for its contribution to water demand, but without overstating or understating it. The inventive method provides predictable strength and avoids overstating or understanding the effect on water demand by defining and using a second portion of the mineral fines as an ultrafine “aggregate” to provide a strength-enhancing “filler effect” by effectively reducing the water-to-powder ratio (w/p) of the cement paste.
Design and manufacturing method 100 is therefore a powerful new tool, technical breakthrough, and methodology that result in new cementitious compositions with different ratios of hydraulic cement, mineral fines, aggregate and water, but with predictable results from the standpoint of rheology, admixture requirements, and strength. It is an entirely new way of treating materials that have heretofore been characterized as being one, and only one, of cement, SCM, or aggregate, and which fit no actual definition other than “mineral addition” that can be interground with cement clinker in amounts up to 5% according to ASTM C-150 or between 5-15% according to ASTM C-595, or “filler” that can replace a portion of the fine aggregate.
In general, finer mineral fines may reasonably be considered to contain or approximate more “cementitious binder” particles and fewer “aggregate” particles, and coarser mineral fines may reasonably be considered to contain or approximate fewer “cementitious binder” particles and more “aggregate” particles. A few test batches can be used to determine a reasonable apportionment, mainly by testing rheology, which can be performed in a relatively short period of time, such as within 10-30 minutes after initially mixing the test batches. As a general rule, apportioning more of the mineral fines as “cementitious binder” will improve rheology, while apportioning more of the mineral fines as “aggregate” will improve strength. Striking a desirable balance between the two has been found to be remarkably simple compared to traditional trial and error testing, which demonstrates the robustness of the methodology.
In some embodiments a method of manufacturing improved or augmented concrete incorporating mineral fines, comprises:
The “reference concrete mix” is typically a commercial concrete mix produced and distributed by a concrete manufacturer, but which does not include added mineral fines. In the United States, concrete mix designs are typically expressed in amounts of each component per 1 cubic yard (yd3) of concrete. The components of the concrete mix designs expressed in amounts that when combined yield 1 cubic yard of concrete. To make 1 cubic yard of concrete, the components of the concrete mix design are combined in the stated amounts. If more or less concrete is desired, the mix design can be infinitely scaled up or down by multiplying the specified amounts of components in the mix design by the number of cubic yards required or specified. For example, if “x” cubic yards of concrete is/are desired or specified, the manufacturer can simply scale the mix design up or down by multiplying each component of the mix design by scaling factor “x” to obtain scaled amounts and combine them to produce “x” cubic yards of concrete. Outside the U.S., concrete mix designs are typically expressed in amounts of each component per 1 cubic meter (m3) of concrete and can be infinitely scaled up or down as needed by multiplying each component of the mix design by scaling factor “x” to obtain scaled amounts and combine them to produce “x” cubic meters of concrete.
The design and manufacturing methods of the disclosed invention can be applied to produce an augmented or improved concrete mix designs that includes added mineral fines. When this happens, a concrete company that previously produced or currently produces concrete mixes that do not contain added mineral fines can thereafter produce augmented concrete mixes that contain added mineral fines. Because concrete mix designs are typically specified for specific uses or purposes, the present invention can be used to redesign some or all of the concrete company's mix designs. In this way, the previously produced concrete mixes are “reference concrete mixes,” and the previous concrete mix designs are “reference concrete mix designs.” The inventiveness of the augmented concrete mixes and concrete mix designs can be shown by comparing them to the reference concrete mixes and reference concrete mix designs, respectively, previously made and used by the concrete manufacturer.
The methods disclosed herein can be used to systematically redesign some or all existing concrete mix designs of a concrete manufacturer and thereby replace some or all of the existing concrete mix designs with augmented concrete mix designs that can be used to produce augmented concrete mixes containing added mineral fines. The previous or existing concrete mix designs are reference concrete mix designs used for specific purposes, and the augmented concrete mix designs can be used to make augmented concrete mixes for the same specified purposes as the previous or existing concrete mixes (which are reference concrete mixes). Alternatively, a new concrete manufacturer entering the market can use the design methods to create augmented concrete mix designs based on previously known or existing reference concrete mixes.
In some embodiments, a method of manufacturing augmented concrete by a concrete manufacturer incorporating mineral fines comprises:
In some embodiments, the method comprises preparing or obtaining a plurality of augmented concrete mix designs to replace a plurality of corresponding reference concrete mix designs and manufacturing a plurality of corresponding augmented concrete mixes according to the plurality of augmented concrete mix designs.
In some embodiments, at least some of the following conditions are present:
In some embodiments, a method of manufacturing augmented concrete incorporating mineral fines comprises:
Mineral fines can be blended with one or more performance-enhancing additives to yield a performance-enhancing particulate pre-mix that can be added to concrete or other cementitious mixture to substitute for a portion of the cement and/or aggregate components normally used in accordance with a given mix design. Performance-enhancing additives may include one or more of supplemental lime (e.g., CaO, Ca(OH)2, hydrated lime, or Type S Lime), supplemental sulfate (e.g., calcium sulfate hemihydrate, plaster of Paris, calcium sulfate dihydrate, gypsum, anhydrous calcium sulfate, anhydrite, or alkali metal sulfate), alkanolamines (e.g., triethanolamine (TEA) or triisopropanolamine (TIPA)), amines (tetrahydroxylethylethylene diamine (THEED) or poly(hydroxyalkylated)ethylene diamine) (polyHEED), water-reducing admixtures, superplasticizers, accelerators, retardants, and the like. Because mineral fines are generally non-reactive, additives containing water or moisture can be blended with mineral fines without premature hydration, as would occur if added to a cementitious binder prior to being used to make a fresh cementitious mixture. The performance-enhancing particulate premix can be made using any known blending method, including intergrinding, planetary mixers, spraying, and the like.
In some embodiments, the performance-enhancing particulate pre-mix comprises less than 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 7%, 5%, 4%, 3%, 2%, or 1% of hydraulic cement and can be free of hydraulic cement altogether. In some embodiments, the performance-enhancing particulate pre-mix comprises less than 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, 7%, 5%, 4%, 3%, 2%, or 1% of combined hydraulic cement and supplemental cementitious material (SCM) and can be free of hydraulic cement and SCM altogether. In some embodiments, the performance-enhancing particulate pre-mix may comprise an interground mixture of mineral fines and volcanic ash, pumice, other natural pozzolan, fly ash, and/or GGBFS.
The performance-enhancing particulate premix can be used to replace a portion of cementitious binder, including OPC, but especially blended cements comprising OPC and at least one SCM selected from slag, fly ash, natural pozzolan, ground glass, and the like. Because of its low cost, which is less than, the same as, or only marginally more than the cost of aggregate, the premix may also be used to replace a portion of sand or other aggregate. Because water demand of the performance-enhancing particulate premix is typically less than cement, but more than aggregate, using it to replace both a portion of the cementitious binder and aggregate portions strikes an optimal balance that enhances performance without significantly increasing, and in some cases reducing, water demand.
Reference is made to
Concrete and other cementitious compositions made according to the disclosed invention will typically have readily observable attributes or signatures that set them apart from conventional concrete mix designs, particularly when the disclosed design methods are used to redesign an existing concrete mix design. For example, a commercial concrete mix design will typically have a specified cementitious binder content, specified water-to-cementitious binder ratio (w/cm) (i.e., weight of water divided by the combined weight of Portland cement and all SCMs), and specified aggregate(s) content. A new concrete mix design made according to the disclosed invention will typically have one or more of the following attributes or signatures:
Some examples below utilized mineral fines (i.e., quarry fines) purchased from the Keigley quarry located on Genola, Utah at a price substantially lower than the typical cost of OPC. A ton of the mineral fines was conveniently packaged in forty 50-pound sacks of coal mine rock dust stacked on a pallet. In this form, the product was still significantly less expensive than the bulk price of OPC. If purchased in bulk, the cost of mineral fines would be about ⅓ or less than the bulk price of OPC. This highlights the tremendous cost savings that can be realized by effectively using mineral fines. In the examples below, 25-50% of the OPC normally contained in concrete was replaced with various SCMs and mineral fines and provided similar or greater strength than control mixes containing 100% OPC or 80% OPC and 20% fly ash. A first particle size analysis of the coal mine rock dust performed using a Microtrac-X100 particle size analyzer showed a very broad, flat PSD curve, with particles as large as about 135 μm and a small proportion (3%) smaller than 1 μm, a D90 of about 70 μm, a D50 of about 17 μm, and a D10 of about 2.5 μm. A chemical analysis of the coal mine rock dust showed that it contained 87% calcite (CaCO3), 3% dolomite (CaMg(CO3)2), 3% quartz, 1% K-feldspar, 1% ankerite/Fe dolomite, and 5% illite-mica. A second particle size analysis obtained by hydrometer analysis showed a percent passing of 93% at 75 μm, 61% passing at 27 μm, 53% passing at 18 μm, 43% passing at 11 μm, 31% passing at 8 μm, 23% passing at 6 μm, 13% passing at 3 μm, and 6.2% passing at 1 μm. A third particle size analysis performed by a Malvern Mastersizer 2000 showed a D90 of about 91 μm, a D50 of about 17 μm, and a D10 of about 2.75 μm.
Some examples utilized Feed Flour limestone powder sold by Blue Mountain Minerals, Columbia, Calif. It reportedly contains about 90% CaCO3 and has a D90 of about 100 μm and a D50 of about 43 μm. It is off-white in color.
Some examples utilized Rock Dust—High Calcium Pulverized Limestone (nominal size 100 μm-0 μm (No. 140) from the Cricket Mountain Plant of Graymont, located in Delta, Utah. It reportedly contains 96.6% CaCO3 and has a percent passing of 80% (D80) of 75 μm and a D50 of about 43 μm. The D90 is estimated to be about 80 μm. It was off-white in color.
Some examples utilized limestone powder sold by Specialty Minerals in Lucerne Valley, Calif. It is a ground calcium carbonate sold under the name Marble White 80. It reportedly has a brightness of 92, specific gravity of 2.7, and contains 98% calcium carbonate, 1.2% magnesium carbonate, and less than 0.1% iron oxide. A sieve analysis was performed on a 1000 g sample, with 32.51 g (3.251%) retained on a #70 sieve (212 μm), 71.83% (7.183%) retained on a #100 sieve (150 μm), 170.18 g (17.018%) retained on a #140 sieve (106 μm), 246.52 (24.653%) retained on a #200 sieve (75 μm), and 478.95 g (47.895%) in the pan. The D90 is therefore about 150 μm and the D50 is about 75 μm.
Some examples utilized Class F fly ash produced at the Gaston, Ala. steam power plant and provided by Headwaters, Inc., previously headquartered in South Jordan, Utah, recently acquired by Boral. Various forms of this fly ash were used, including in its original form (FA) and after being classified into fine (FFA), ultrafine (UFFA), and coarse fractions (CFA). Classification was performed by RSG, Inc., located in Sylacauga, Ala. The PSD of each material was measured by RSG using a Microtrac-X100 particle size analyzer. The unprocessed fly ash (FA) had a D90 of about 80 μm, a D50 of about 20 μm, and a D10 of about 2.5 μm. The fine fly ash (FFA) after a first classification had a D90 of about 20 μm, a D50 of about 7.5 μm, and a D10 of about 1.5 μm. The coarse fly ash (CFA) after the first classification had a D90 of about 120 μm, a D50 of about 45 μm, and a D10 of about 20 μm. The FFA was classified again to yield a first ultrafine fly ash (UFFA) having a D90 of about 4.6 μm, a D50 of about 2.5 μm, and a D10 of about 1.16 μm, and a second UFFA having a D90 of about 8.5 μm, a D50 of about 4.6 μm, and a D10 of about 1.45 μm. Some examples utilized Class F fly ash produced at Four Corners, Fruitland, N. Mex., power plant, distributed by SRMG, and provided by Central Concrete, a division of U.S. Concrete (now Vulcan Materials). Some examples utilized fly ash from Jim Bridger power plant in Bridger, Wyo.
Some examples utilized ultrafine fly ash (UFFA) produced by classifying fly ash produced at three power plants owned by Pacificorp: Jim Bridger, located in Bridger, Wyo.; Hunter, located in Castle Dale, Utah; and Huntington, located in Huntington, Utah. The fly ashes were classified by RSG. The Bridger fly ash was apparently moist and agglomerated and was not able to be effectively classified or its PSD characterized. The Bridger “UFFA” was therefore the least effective even though it is the only one of these three fly ashes sold and used commercially in concrete on a consistent basis.
The Hunter and Huntington fly ashes are generally considered to be of substandard quality, are not generally used in concrete, are sometimes used in asphalt, and are typically landfilled (i.e., because of excessive carbon and/or a reactivity index below 75). They reportedly amount to about 750,000 to 1 million tons produced per year. This would be a substantial source of fly ash if it could be beneficiated into usable products of acceptable quality. The Hunter and Huntington fly ashes were classified to provide a 20% yield of UFFA product, which would amount to about 150,000 to about 200,000 tons per year of high quality UFFA between the two geographically similar situated power plants.
The PSD of the Hunter UFFA was measured by RSG using a Microtrac X100 particle size analyzer and reported to have a D90 of about 7.5 μm, a D50 of about 3.1 μm, and a D10 of about 1.1 μm. The PSD was bimodal with peaks at about 1.3 μm and about 4 μm. The specific gravity of the Hunter UFFA was determined to be 2.6375 and the LOI satisfied ASTM C-618. The Hunter UFFA was tested by Wyoming Analytical Laboratories and determined to contain 44.73% SiO2, 18.70% Al2O3, 13.53% CaO, 2.72% SO3, 5.78% Fe2O3 (total SAF=69.21); 5.29% MgO, 1.66% Na2O, 1.57% K2O, 0.99% TiO2, 1.26% P2O5, and 3.43% LOI. A calorimetry test indicated some degree of set retardation when used with OPC at 40%.
The PSD of the Huntington UFFA was measured by RSG using a Microtrac X100 particle size analyzer and reported to have a D90 of about 10.5 μm, a D50 of about 3.8 μm and a D10 of about 1.26 μm. The specific gravity of the Huntington UFFA was determined to be 2.534 and the LOI satisfied ASTM C-618 according to NIST analysis. The Huntington UFFA was tested by Wyoming Analytical Laboratories and determined to contain 44.94% SiO2, 19.30% Al2O3, 4.17% Fe2O3 (total SAF=69.11), 9.34% CaO, 2.17% SO3, 3.35% MgO, 2.87% Na2O, 1.85% K2O, 1.07% TiO2, 0.92 P2O5, and 9.02% LOI (making it non-conforming if accurate). A calorimetry test indicated some degree of set retardation when used with OPC at 40%.
Some examples utilized coarse calcined shale flue dust produced by Utelite Corporation, Coalville, Utah. The shale flue dust is collected in the baghouse and is a byproduct produced during the calcining of shale to make lightweight aggregates. The shale flue dust has not previously been used in concrete and, to the best of the knowledge of Utelite personnel that provided a sample, had never previously been tested in concrete or as a cement substitute. Instead, it is occasionally used as a filler in asphalt but typically landfilled. The PSD of the shale flue dust was measured by RSG using a Microtrac X100 particle size analyzer and reported to have a D90 of about 114 μm, a D50 of about 24 μm and a D10 of about 3.5 μm. The shale flue dust was determined by XRF to contain 56.6% SiO2, 14.2% Al2O3, 6.04% CaO, 2.25% MgO, 4.21% Fe2O3, 0.29% Na2O, 1.98% K2O, 0.54% TiO2, 0.21P2O5, 0.72% S, 0.02% MnO2, 0.06% BaO, <0.21% Cl−. The chemistry is therefore similar to a Class F fly ash except that shale flue dust has no combustible elemental carbon.
Some examples used Holcim Type II/V OPC manufactured at Devil's Slide cement plant, Morgan, Utah, and sold at Home Depot, Salt Lake City, Utah (sometimes labeled as Type I/II/V or I/II, previously assumed to be Type I/II, and now understood to be Type II/V according to general requirement for cement in Utah to be Type II/V according to ASTM C-150). Some examples used Lehigh Type II/V cement from Lehigh Hanson cement plant, Cupertino, Calif., and provided by Central Concrete. Some examples use Ash Grove Type II/V OPC manufactured at the Leamington, Utah, plant.
Some examples utilized Grade 120 ground granulated blast furnace slag (GGBFS) sold by Lehigh Heidelberg, Stockton, Calif., and provided by Central Concrete. The GGBFS was determined by XRD to be 97.2% amorphous and by XRF to contain 30.4% SiO2, 10.7% Al2O3, 43.4% CaO, 6.3% MgO, 0.6% Fe2O3, 0.1% Na2O, 0.3% K2O, 0.6% TiO2, 4.4% SO3, and 0.01% MnO2. The PSD of the GGBFS reportedly has D90 of about 20 μm, a D50 of about 7.5 μm and a D10 of about 1.6 μm.
Some examples utilized a fine clinker ground by Gebr. Pfeiffer at Kaiserslautern, Germany, to specifications provided by the inventor. Raw Type II/V clinker was provided by Drake Cement, located in Paulden, Ariz., and owned by Unacem, Peru. Some examples utilized an interground blend of volcanic ash provided by Staker Parson, Ogden, Utah, and limestone granules provided by Pfeiffer and ground by Pfeiffer to specifications provided by the inventor. The moisture content of the volcanic ash as received was 6.0%. Intergrinding the volcanic ash with limestone reduced the water content of the interground blend to less than 0.5%. Strength testing indicates the volcanic ash was pozzolanically activated by intergrinding with the limestone.
Some examples utilized concrete washout fines obtained from Ready Made Concrete, located in Salt Lake City, Utah. Such fines were removed from a settling pond, placed in a pile to dry, used as road base and fill, and are sold for about $20 a ton in bulk.
Some examples utilized wet concrete washout fines obtained from Delta Industries, located in Jackson, Miss. Such fines are typically land-filled and have negative value. The wet washout fines were oven dried to remove water before adding to mortar mixes.
Some examples utilized 1-inch aggregate and sand purchased from Staker Parson, North Salt Lake, Utah.
Concrete mixes tested herein were prepared using a 3.5 cubic feet rotary mixer and cast into 4×8 inch plastic cylinder molds, allowed to harden, transported to CMT Engineering, Inc., of West Valley City, Utah, demolded, placed into a curing chamber, and tested at designated intervals (e.g., 3, 7, 28, 91, and 182 days). Mortar mixes were prepared using a Hobart mixer and cast into 2×2 inch cube molds, allowed to harden, placed into a saturated limewater bath, transported to CMT Engineering, placed into a saturated limewater bath inside the curing chamber, and tested at designated intervals. A lignosulfonate water reducer and/or superplasticizer was/were employed as needed to maintain adequate rheology (e.g., approximate slump of about 3-6 inches, or 7.5-15 cm) and in commercially acceptable amounts.
Comparative Example 1 was prepared from a standard “6-bag” concrete mix containing 564 lbs. of OPC per cubic yard and having a design strength of 5200 psi (35.85 MPa) at 28 days. Comparative Example 2 was prepared from a standard 6-bag concrete mix in which 20% of the OPC is substituted with fly ash. Comparative Example 3 was a further modified standard 6-bag mix in which 30% of the OPC was substituted with fly ash and the sand reduced. Comparative Examples 1-3 are useful control mixes against which other concrete mixes can be compared. The compositions of Comparative Examples 1-3 are set forth in Table 1. Comparative Example 4 is identical to Comparative Example 2 except that 20% of the OPC was substituted with mineral fines instead of fly ash. Comparative Example 5 is identical to Comparative Example 3 except that 30% of the OPC was substituted with mineral fines instead of fly ash. Comparative Examples 4 and 5 do not include an additional quantity of mineral fines deemed as aggregate to replace a portion of the sand.
Comparative Examples 1-3 show the relative effects of using OPC compared with a blend of OPC and fly ash at 206 and 300 substitution. Comparative Examples 4 and 5 included OPC and mineral fines at 20% and 30% substitution. As expected, the mineral fines, being non-reactive, performed worse than fly ash when used simply as a partial cement substitute. But when used in ternary and quaternary blends as described in working examples below, they permitted substantially higher clinker reductions at similar to higher strength compared to Comparative Examples 1-5.
The following working examples were designed and manufactured by the inventor and are identified using their mix TD numbers assigned during testing. They were manufactured using the concrete mix designs set forth in the tables below. Strength values are also provided.
Compared to Comparative Examples 1-5, Mix 10 had lower clinker content, higher absolute water-to-cement ratio (w/c), and higher strength at 28, 91, and 182 days. Mixes 10, 11A, 11B and 12B all benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition. In addition, the inclusion of Type S lime in each of Mixes 10, 11A, 11B and 12B also appears to have provided a strength benefit. The inclusion of plaster of Paris is believed to have improved rheology and/or increased strength.
Mix 12A is unique because it included no mineral fines, Type S lime, or plaster of Paris addition but exhibited high strength owing to the use of Huntington UFFA having a D90=10.5 μm, a D50=3.8 μm, and a D10=1.26 μm. UFFA was easily dispersed and greatly increased flow compared to using silica fume.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
Mix 13B contained Huntington UFFA, and Mix 13C contained Hunter UFFA. Mixes 12C, 13B, 13C and 17C all appear to have benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition. In addition, Mixes 12C, 13C and 17C appear to have benefitted significantly by including Type S lime.
Mix 13A is unique because it included no mine rock dust, Type S lime, or plaster of Paris addition but exhibited higher strength than any of Comparative Examples 1-5 at all ages owing to the use of calcined shale flue dust having a D90=114 μm, D50=24 μm and D10=3.5 μm. This material is an industrial waste product that has not heretofore been used by any concrete company to make concrete or other cementitious composition. It may be considered to be a form of mineral fines because it is a biproduct of lightweight aggregate manufacture.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
Mixes 17D, 17E, 17F, 17G and 17H all appear to have benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition. Mixes 17E, 17F, 17G and 17H appear to have benefitted by including Type S lime.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
Mixes 17I, 17J, 15-30-10, 15-20-20, and 15-30-30 all appear to have benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition. Mixes 17I and 17J appear to have benefitted by including Type S lime.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
Mixes 14A, 14AF, 12CF, and 12CG all appear to have benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition. Mixes 14A, 14B, 14AF, 12CF, and 12CG appear to have benefitted by including Type S lime. Mixes 14AF, 12CF, and 12CG appear to have benefitted by including Fine clinker instead of OPC and UFFA instead of FA.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
Mixes 18A, 18B, 18C, 5A and 5B all appear to have benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition. Mixes 18A, 18B, 18C and 5B appear to have benefitted by including Type S lime, and Mixes 18A, 18C and 5B appear to have benefitted by including plaster of Paris. In fact, the only difference between Mixes 18B and 18C was the inclusion of a small amount of plaster of Paris, with a corresponding reduction in mineral fines—the effect on strength was dramatic and consistent at all ages, which indicates that the use of GGBFS in this mix caused a sulfate deficit and the plaster of Paris apparently corrected it.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
Mixes 19A, 19B, and 19C all appear to have benefited significantly from including mineral fines as both a partial cement replacement and a partial ultrafine aggregate addition and by including Type S lime. The use of plaster of Paris in Mix 19B does not seem to have made much difference, if any, and may have improved Mix 19C.
In 2017, Central Concrete asked the inventor to design concrete mixes for commercial production that incorporated ground limestone powder as a partial replacement for Portland Cement that could both meet specified the strength requirements and reduce cost (which Central Concrete admittedly could not do). Using techniques disclosed herein, the inventor designed several concrete mixes that reduced the Portland cement content far beyond reductions previously achieved by Central Concrete using GGBFS and fly ash while meeting the strength requirements and reducing cost.
The following examples were designed and manufactured according to the present invention and are improvements to a commercial mix of Central Concrete having a design strength of 5000 psi (34.5 MPa) at 28 days and total cementitious binder of 610 lbs/yd3. The compositions, strengths, and estimated cost savings are set forth below in Table 9. All mixes exceeded the design strength and had reduced cost compared to the commercial mix.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Central Concrete
2Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines, i.e., limestone powder (Blue Mountain Minerals Feed Flour) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix. Type S lime and plaster of Paris appear to have had a negative effect in these mixes, suggesting that at higher w/c they are not necessarily beneficial.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
The following examples were designed and manufactured according to the present invention and are improvements to a commercial mix of Central Concrete having a design strength of 8000 psi (55.2 MPa) at 28 days and total cementitious binder of 845 lbs/yd3. The compositions, strengths, and estimated cost savings are set forth below in Tables 10 and 11. All but one mix exceeded the design strength and all had reduced cost compared to the commercial mix.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Central Concrete
2Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
Mixes 2C-2F are virtually identical except for varying quantities of Type S lime and plaster of Paris. The best results were obtained when plaster of Paris was used. Type S lime appears to have provided no benefit by itself and a small benefit when used in combination with plaster of Paris. It appears that more Type S lime than could be consumed was added given the low w/cm of the mixes and low solubility of lime.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Central Concrete
2Assumes 0.83 ton of CO2 emitted per ton of cement manufactured pcy = per cubic yard
Mix 2F was tested for shrinkage by Central Concrete, which indicated less than 0.070% shrinkage at 28 days, and lower shrinkage at each of 7, 14, 21, and 28 days compared to the corresponding commercial mix of Central Concrete.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
The following examples were designed and manufactured according to the present invention and are improvements to a commercial mix of Central Concrete with a design strength of 4000 psi (27.6 MPa) at 3 days and total cement binder (100% OPC) of 687 lbs/yd3. The compositions, strengths, and estimated cost savings are set forth below in Table 12. All mixes equaled or exceeded the design strength and all had reduced cost compared to the commercial mix.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Central Concrete
2Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines (limestone powder) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to the commercial mix. Type S lime and plaster of Paris appear to provide a positive effect in these mixes, perhaps because they were appropriate for the w/c.
Mixes 18C-1, 3B, and 3C were tested for shrinkage by Central Concrete, which indicated less than 0.04000 shrinkage at 28 days for each mix, and lower shrinkage for each mix at each of 7, 14, 21, and 28 days compared to the corresponding commercial mix of Central Concrete.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
The following examples were designed and manufactured according to the present invention and are improvements to a commercial mix of Central Concrete with a design strength of 4000 psi (27.6 MPa) at 28 days and total cement binder of 551 lbs/yd3. The compositions, strengths, and estimated cost savings are set forth below in Table 13. All mixes equaled or exceeded the design strength and all had reduced cost compared to the commercial mix.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Central Concrete
2Assumes 0.83 ton of CO2 emitted per ton of cement maunfactured pcy = per cubic yard
The use of mineral fines (limestone powder) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix. Type S lime and plaster of Paris were not used.
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
In 2021, Geneva Rock, Utah, provided the inventor with concrete mix designs to determine whether they could be redesigned to incorporate ground limestone powder as a partial replacement for Portland Cement while meeting specified the strength requirements. Using techniques disclosed herein, the inventor designed several concrete mixes that reduced the Portland cement content far beyond any reductions previously achieved by Geneva Rock using fly ash while meeting the strength requirements and reducing cost.
Geneva Rock provided Ash Grove Type II/V cement, Jim Bridger fly ash, ¾ inch minus aggregates, pea gravel, and sand. Greymont provided ground limestone powder having 80% passing at 75 μm (estimated D90 of about 80 μm).
The following example was designed and manufactured according to the present invention and is improvement to a commercial mix of Geneva Rock having a design strength of 3500 psi (24.1 MPa) at 28 days and total cementitious binder of 517 lbs/yd3. The composition, strength, and estimated cost saving are set forth below in Table 14.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Geneva Rock
2Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines, i.e., limestone powder (Greymost) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix.
The following example was designed and manufactured according to the present invention and is improvement to a commercial mix of Geneva Rock having a design strength of 4000 psi (27.6 MPa) at 28 days and total cementitious binder of 564 lbs/yd3. The composition, strength, and estimated cost saving are set forth below in Table 15.
1OPC Reduction (%)
2CO2 reduction lb/yd3
1OPC reduction compared to OPC content in commercial mix of Geneva Rock
2Assumes 0.83 ton of CO2 emitted per ton of cement manufactured pcy = per cubic yard
The use of mineral fines, i.e., limestone powder (Greymost) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix.
The following example was designed and manufactured according to the present invention and is improvement to a commercial mix of Geneva Rock having a design strength of 4500 psi (31.0 MPa) at 28 days and total cementitious binder of 611 lbs/yd3. The composition, strength, and estimated cost saving are set forth below in Table 16.
1 OPC Reduction (%)
2 CO2 reduction lb/yd3
1 OPC reduction compared to OPC content in commercial mix of Geneva Rock
2 Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines, i.e., limestone powder (Greymost) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix.
The following examples were designed and manufactured according to the present invention and are an improvement to a commercial mix of Geneva Rock having a design strength of 5000 psi (34.5 MPa) at 28 days and total cementitious binder of 660 lbs/yd3. The composition, strength, and estimated cost saving are set forth below in Table 17.
1 OPC Reduction (%)
2 CO2 reduction lb/yd3
1 OPC reduction compared to OPC content in commercial mix of Geneva Rock
2 Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines, i.e., limestone powder (Greymost) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix.
The following examples were designed and manufactured according to the present invention and are an improvement to a commercial mix of Geneva Rock having a design strength of 6000 psi (41.4 MPa) at 28 days and total cementitious binder of 752 lbs/yd3. The composition, strength, and estimated cost saving are set forth below in Table 18.
1 OPC Reduction (%)
2 CO2 reduction lb/yd3
1 OPC reduction compared to OPC content in commercial mix of Geneva Rock
2 Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines, i.e., limestone powder (Greymost) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix.
The following example was designed and manufactured according to the present invention and is improvement to a commercial mix of Geneva Rock having a design strength of 8000 psi (55.2 MPa) at 28 days and total cementitious binder of 875 lbs/yd3. The composition, strength, and estimated cost saving are set forth below in Table 19.
1 OPC Reduction (%)
2 CO2 reduction lb/yd3
1 OPC reduction compared to OPC content in commercial mix of Geneva Rock
2 Assumes 0.83 ton of CO2 emitted per ton of cement manufactured
The use of mineral fines, i.e., limestone powder (Greymost) according to the invention permitted substantial clinker reduction, cost reduction, and comparable strength compared to commercial mix.
In cooperation with Ready Made Concrete in West Valley City, Utah, the inventor made 10 concrete mixes and had them delivered to a job site in standard ready mixed concrete trucks to confirm whether the concrete mixes disclosed herein can be readily scaled up, mixed, delivered, finished, and cured like conventional concrete. All mixes behaved adequately and produced quality concrete of acceptable slump, strength, finishability, and set time. The mixes were loosely designed to replace a standard concrete mix design containing OPC (553 lb/yd3) and fly ash (115 lb/yd3) cementitious binder, with a design strength of 4500 psi @ 28 days. A portion of concrete from the concrete mixer truck was taken off and cast into 4×8 inch cylinders for compressive strength testing by CMT Engineering.
The mix designs and properties are set forth below in Tables 20 and 21. While not all mixes had 28-day compressive strength of 4500 psi, the margin of cost savings was so great that they can easily be redesigned to have greater strength while still reducing cost.
1 Percent
2 CO2
3 Design
4 Actual
1 OPC reduction compared to commercial mix
2 Assuming 0.83 ton of CO2 emitted per ton of cement manufactured
3 Design w/cm assumes a portion of coal mine rock dust is “cementitious binder”
4 Actual w/cm excludes coal mine rock dust from the “cementitious binder”
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
1 Percent
2 CO2
3 Design
4 Actual
1 OPC reduction compared to commercial mix
2 Assuming 0.83 ton of CO2 emitted per ton of cement manufactured
3 Design w/cm assumes a portion of coal mine rock dust is “cementitious binder”
4 Actual w/cm excludes coal mine rock dust from the “cementitious binder”
The foregoing compositions have the following characteristics and prophetic or hypothetical modification range:
The purpose of the foregoing mixes was not to reduce cost per se but to test a variety of supplementary cementitious materials (SCMs) to see how concrete would behave in a concrete mixer truck. The first two mixes had substantially greater strength than 4500 psi with only minor cost increase compared to the 4500 psi control mix. The second two mixes used leftover SCMs in the inventor's possession. The last mix had very high substitution of OPC with shale flue dust. Given the high cost saving, it can easily be redesigned to have higher strength if required.
As of 2018, one of the most highly touted technologies for reducing the carbon footprint of concrete, measured as reduction of CO2 per cubic yard, involves injecting concentrated or pure CO2 into freshly mixed concrete. This is reported to reduce the CO2 footprint of concrete in two ways: (1) injected CO2 reacts with lime (CaO) to form insoluble calcium carbonate (CaCO3) and (2) the calcium carbonate marginally increases strength, permitting a small Portland cement reduction. According to numbers published in 2018 by CarbonCure, total reduction of CO2 is reportedly 11.44 pounds per cubic yard (lb/pcy). The net cost reduction using this process is reportedly $0.94 pcy. This is the current state of the art for CO2 reduction and cost savings.
By comparison, the CO2 reduction for concrete mixes based on the commercial mix having a design strength of 5000 psi (34.5 MPa) at 28 days and total cementitious binder of 610 lbs/yd3 (Examples 1A to 1E) was between 66.0 and 89.4 lb/pcy. These mixes provided 6 to 8 times more CO2 reduction than CO2 injection. The net cost saving for these mixes was between $1.91 and $3.17 pcy, about 2 to 3 times more than for CO2 injection.
By further comparison, the CO2 reduction for concrete mixes based on the commercial mix having a design strength of 8000 psi (55.2 MPa) at 28 days and total cementitious binder of 845 lbs/yd3 (Examples 2A to 2H-1) was between 104.2 and 127 lb/pcy. These examples provided 9 to 11 times more CO2 reduction than CO2 injection. The net cost saving for these mixes was between $2.41 and $9.56 pcy, about 2½ to 10 times more than for CO2 injection.
By further comparison, the CO2 reduction for concrete mixes based on the commercial mix having a design strength of 4000 psi (27.6 MPa) at 3 days and total cementitious binder of 687 lbs/yd3 (Examples 18C to 3C) was between 285.1 and 361.9 lb/pcy. These mixes provided 25 to 31 times greater CO2 reduction than CO2 injection. The net cost saving for these mixes was between $4.64 and $8.54 pcy, about 5 to 9 times more than for CO2 injection.
By further comparison, the CO2 reduction for concrete mixes based on the commercial mix having a design strength of 4000 psi (27.6 MPa) at 28 days and total cementitious binder of 551 lbs/yd3 (Examples 4A to 4F) was between 22.8 and 91.4 lb/pcy. These mixes provided 2 to 8 times greater CO2 reduction than CO2 injection. The net cost saving for these mixes was between $0.76 and $2.15 pcy, or up to twice the cost savings of CO2 injection.
Mortar mixes were made according to ASTM C109 using a Hobart mixer but were modified to include less water and more cement. Fresh mortar was cast into 2×2 inch cubes and tested by CMT Engineering in West Valley City, Utah. Portland cement was a Type I/II OPC manufactured by Holcim, Devil's Slide, Utah plant, and purchased at Home Depot, Salt Lake City. Ultrafine fly ash (UFFA) was made by classifying a fly ash from Huntington, Hunter, Jim Bridger, and Gaston power plants. The Bridger fly ash was moist, became agglomerated and did not form UFFA but either there was no separation or there was only poor separation. It will be designated as fine fly ash (FFA). The silica fume was condensed silica fume provided by Calmetrix. The calcined shale dust was obtained from Utelite, Coalville, Utah. Class F fly ash was a standard fly ash obtained from Gaston, Ala., steam power plant owned by Boral and provided by its predecessor Headwaters Inc., of South Jordan, Utah. Limestone powder was Marble White 80 from Specialty Minerals. The mineral fines containing about 90% limestone as calcite was coal mine rock dust purchased from Staker Parson and produced in Genola, Utah at Keigley limestone quarry. The sand was graded Unimin silica sand purchased at Home Depot. The components, their quantities, and compressive strengths of the mortar mixes are set forth in the Tables below. Lignosulfonate (Plastocrete 161) and/or polycarboxylate ether (Viscocrete 2100) were used in some cases to maintain flow between 100-120 on a flow table.
Mix 111 is a 100% OPC control mix. Mix 111A is an 85-15% OPC-fly ash control mix. Mix 111B is an 85-15% OPC-silica fume control mix. They are surrogates for how concrete and mortar are commonly manufactured. Mix 111 illustrates a high strength mortar that includes an elevated quantity of OPC and has a moderately low water to cement ratio (w/c=0.35). Mix 111A illustrates the negative effect on early strength of replacing 15% of the OPC with ordinary fly ash. Mix 111B illustrates the positive effect on strength of replacing 15% of the OPC with silica fume. The effect on strength of using different SCMs and optionally mineral fines and/or Type S lime, are illustrated by the other mortar mixes below.
Mixes 111A and 111E indicate that using unprocessed Gaston fly ash and poorly classified Bridger fly ash yielded mortar having substantially reduced strength compared to Mix 111. Mixes 111D and 111F indicate that Hunter and Huntington UFFA were substantially superior to Gaston and Bridger fly ashes. Huntington UFFA was comparable to silica fume in terms of strength development but required significantly less superplasticizer to yield mortar with proper flow.
Mixes 111G and 111H indicate that using lime as an additive to Bridger fly ash substantially improved strength at all ages. Mixes 111I-111L indicate that using mineral fines (limestone powder) improved the strength of mortars containing Bridger fly ash, Gaston UFFA or Gaston FFA.
Mixes 111M-111P show the effect on strength of using mineral fines (limestone powder) and/or lime on strength when using different types of fly ash. Mixes 111Q and 111R illustrate the effect of using or not using lime when using calcined shale dust. When lime is used, the mortar containing calcined shale dust exhibited much higher 3-day strength, similar 7-day strength, and slightly higher 28-day strength.
Mixes 111S-111U demonstrate the effect of substituting twice as much OPC (i.e., 300%) with Bridger fly ash and calcined shale dust, optionally with limestone powder. Mixes 111V-111X demonstrate the beneficial effect on strength of using finer mineral fines instead of coarser limestone powder. Mixes 111W and 111X compare the effect of excluding or including lime when using quarry dust and calcined shale or FFA.
Mixes 111Y and 111Z show the effect of using mineral fines and lime to assist the strength development of mortar made using either UFFA or ultrafine steel slag, which is an industrial waste product having few uses and that is not used effectively in mortar and concrete by the industry. Mix 111Z shows that even very inexpensive steel slag, when blended with mineral fines and lime, can produce mortar comparable in strength to mortars made using UFFA and silica fume.
Architectural cast stone mixes were made based on a commercial mix design that used Portland White Cement, three differently sized limestone aggregates (Specialty Minerals #9 coarse limestone sand, Vical 1600 medium limestone sand, and Marble White 80 fine limestone aggregate/coarse limestone powder), latex adhesive to bond to polystyrene foam, polyvinyl acetate (PVA) fibers to increase toughness, superplasticizer to maintain low water to cement ratio (e.g., w/c=0.36), and viscosity modifying agent (cellulosic either) to prevent segregation and assist fiber dispersion. Mix 104 was a mortar mix derived from a commercial cast stone mix, used white cement as sole cementitious binder, and is the control mix. Mixes 104A-104D were designed by the inventor to provide a similarly commercially acceptable cast stone mix but with substantially reduced cement clinker content and lower cost (i.e., about 10-20% less expensive in material cost compared to the commercial mix design).
White cement, aggregates, fiber, adhesive, superplasticizer, and viscosity modifying agent were provided by Tuscan Stoneworx, Lindon, Utah. GGBFS was white or off-white and purchased from Lehigh Cement, Stockton, Calif. Fine recycled glass was baghouse glass provided by Momentum Recycling in Salt Lake City, Utah. Type S lime was purchased from Home Depot, Salt Lake City, Utah. Fine limestone powder is an agricultural limestone purchased from Oldcastle.
As is readily apparent, by using GGBFS, limestone powder and/or Type S lime, all of which cost substantially less than white cement, cast stone mixes with clinker reductions of 55-6000 were made having adequate strength. Mixes 104A-104C had 60% clinker reduction and were comparable in strength (only slightly lower) compared to control Mix 104. Mix 104D had 5500 clinker reduction and substantially higher strength at each of 3 days, 7 days and 28 days compared to control Mix 104.
Mixes 104E-104I demonstrate that substituting between 54.7% and 61% of the white cement with GGBFS, an additional portion of Marble White 80, and Type S lime, all of which cost substantially less than white cement, yielded cast stone mixes with comparable to significantly higher strength, particularly at 7 and 28 days, compared to control Mix 104.
Glass fiber reinforced concrete (GFRC) mixes were made based on a commercial GFRC mix design that used Portland White Cement, three differently sized silica sand or coarse limestone powder aggregates (Wedron #530 medium silica sand, Scott #730 fine silica sand, and Marble White 80 fine limestone aggregate/coarse limestone powder), latex adhesive to bond to polystyrene foam, glass fibers to increase toughness, superplasticizer to maintain low water to cement ratio (i.e., w/c=0.27), and viscosity modifying agent (cellulosic either) to prevent segregation and clogging of a GFRC nozzle. Mix 110 was a mortar mix derived from the commercial GFRC mix, used white cement as sole cementitious binder, and is the control mix. Mixes 110A-110D were designed by the inventor to provide a similarly commercially acceptable GFRC mix but with substantially reduced cement clinker content and lower cost (i.e., about 10-20% less expensive in material cost compared to the commercial mix design).
White cement, aggregates, fiber, adhesive, superplasticizer, and viscosity modifying agent were provided by Tuscan Stoneworx, Lindon, Utah. GGBFS was white or off-white and purchased from Lehigh Cement, Stockton, Calif. A sample of fine pumice was provided by Hess Pumice, Malad, Id. Type S lime was purchased from Home Depot, Salt Lake City, Utah. Interground volcanic ash and limestone was prepared by intergrinding at Gebr. Pfieffer GmbH, Kaiserslautern, Germany a volcanic ash from a deposit in Stockton, Utah provided by Staker Parson, Ogden, Utah, with limestone granules provided by Pfeiffer.
Mixes 110A-110D show that clinker reductions of about 54-58% were possible by substituting part of the white cement with GGBFS and increasing the amount of Marble White 80 fine aggregate, which is a coarse limestone powder. Each of Mixes 110A-110D had comparable or greater strength compared to control Mix 110. At 28 days, Mixes 110A-110D all had significantly to substantially higher strength than Mix 110, but with less than half of the original amount of white cement. When initially cast, Mixes 110A-110D were less white than Mix 110. However, after curing and drying, they were almost indistinguishable in whiteness. If a pigment were used, the final color of Mixes 110A-110D would likely be virtually, if not entirely, indistinguishable from Mix 110.
Mixes 110E and 110F show that clinker reductions of about 35.600 were possible when using much less expensive calcined shale dust and quarry fines instead of GGBFS and Marble White 80. Color was more of a natural limestone color when using calcined shale dust and quarry fines. The molded cubes had a nice, natural look in the absence of added pigments. They also had strengths that were superior to those of Mix 110 and comparable to those of Mixes 110A-11D.
Mixes 110G-110H were made using Type I/II OPC, which costs about half as much as white cement, and also very inexpensive calcined shale dust and quarry fines. Cost savings were greater than 25% compared to Mix 110, although cement binder costs were reduced by more than 65%. Mixes 110G-110H had strengths comparable or superior to those of Mix 110.
Mortar mixes were prepared using concrete washout fines. A control mortar mix made was manufactured using a silica sand and Portland cement from Home Depot in Salt Lake City, Utah. The cement was manufactured by Ash Grove and appears to be poor quality as compared to previous Portland cements obtained from the same Home Depot in Salt Lake City, Utah but manufactured by Holcim. While the strength was lower than previous control mortars made using different Portland cement, it provided a baseline against which other mixes were compared. The mortar mixes were cast into 2 inch molds, cured, and tested by CMT Laboratories.
Concrete mixes were prepared using concrete washout fines and Portland cement from Home Depot in Salt Lake City, Utah. The mortar mixes were cast into 4×8 inch cylinder molds, cured, and tested by CMT Laboratories.
Any of the foregoing Examples is modified so that one more of the components is altered by ±20%, ±18%, ±16%, ±14%, ±12%, ±10%, 8%, ±6%, ±5%, ±4%, ±3%, ±2%, ±1.5%, ±1%, or 0.5%. The compositions have strengths and other properties comparable to the corresponding Examples modified.
Any of the foregoing Examples is modified so that one more of the ratios (w/c, w/cm, or w/p) is altered by ±20%, ±18%, ±16%, ±14%, ±12%, ±10%, 8%, ±6%, ±5%, ±4%, ±3%, ±2%, ±1.5%, ±1%, or 0.5%. The compositions have strengths and other properties comparable to the corresponding Examples modified.
Any of the foregoing Examples is modified by adding concentrated or pure carbon dioxide (CO2) to the freshly mixed cementitious mixture at a rate of about 0.5 to about 10 pounds of CO2 per cubic yard. This results in cementitious compositions having lower CO2 footprint and higher earlier strength. An example process for injecting concentrated or pure CO2 into concrete is provided by CarbonCure Technologies, Inc., headquartered in Dartmouth, Nova Scotia, Canada, such as disclosed in U.S. Pat. Nos. 8,845,940, 9,108,883, 9,376,345, 9,388,072, 9,492,945, 9,738,562, 9,758,437, 9,790,131, 10246379, and 10350787, which are incorporated herein by reference. Another example process for injecting concentrated or pure CO2 into concrete is disclosed in U.S. Patent Publication No. US 2017/0341988 to Welker et al., which is incorporated by reference.
An example process for mixing concentrated or pure CO2 with concrete wash water prior to mixing into fresh concrete is disclosed in US Pat. Pub. No. 2019/0168416 to Monkman et al., which is incorporated by reference. The process in Monkman et al. for mixing CO2 with concrete wash water can be modified to mix concentrated or pure CO2 with wet or dried concrete washout fines in order to passivate alkaline values. Dried concrete washout fines can be mixed with water prior to or while mixing with CO2 to facilitate the reaction.
Concentrated or pure CO2 can be added to the fresh cementitious mixture and/or premixed with concrete washout fines, by sparging in CO2 gas, adding carbonated water, and/or adding crushed dry ice. A fine CO2 “snow” can be formed by expressing compressed CO2 from a nozzle and mixing the CO2 snow into the cementitious mixture using known means. An example mixing vessel is a central mixer or concrete mixing truck used to manufacture ready mixed concrete. The concentrated or pure CO2 can be injected under pressure into a pressurized feed line for introducing one or more components into the mixing vessel. In the case where the cementitious mixture is made using concreate washout fines, highly alkaline values in the washout fines can be passivated by reacting them with CO2 (e.g., after, while, or before being introduced into the mixing vessel).
Any of the foregoing Examples is modified by adding one or more highly alkaline materials into a cementitious mixture that is or has been passivated by being exposed to and/or reacted with concentrated or pure CO2 before, during, or after being introduced into the mixing vessel. The one or more highly alkaline materials can be any industrial byproduct having a high quantity of alkaline values. Examples are class C fly ash, cement kiln dust (CKD), bottom ash, incinerator ash, biomass ash, and the like. Passivation of an alkaline material with CO2 can be used to sequester substantially greater quantities of CO2 (e.g., 2-20 times more) compared to simply injecting CO2 into freshly mixed concrete as currently done by CarbonCure.
The present invention may be embodied in other specific forms without departing from its spirit or essential characteristics. The described embodiments are to be considered in all respects only as illustrative and not restrictive. The scope of the invention is, therefore, indicated by the appended claims rather than by the foregoing description. All changes which come within the meaning and range of equivalency of the claims are to be embraced within their scope.
This application is a continuation-in-part of U.S. patent application Ser. No. 16/921,065, filed Jul. 6, 2020, which claims the benefit of U.S. Prov Pat App No. 62/879,705, filed Jul. 29, 2019 and U.S. Prov Pat App No. 62/874,178, filed Jul. 15, 2019, and is a continuation-in-part of U.S. patent application Ser. No. 16/180,323, filed Nov. 5, 2018, now U.S. Pat. No. 10,737,980, which is a continuation-in-part of U.S. patent application Ser. No. 16/028,398, filed Jul. 5, 2018, now U.S. Pat. No. 10,730,805, which is a continuation-in-part of Intl Pat App No PCT/US18/13097, filed Jan. 10, 2018, and a continuation-in-part of U.S. patent application Ser. No. 15/866,455, filed Jan. 9, 2018, now U.S. Pat. No. 10,131,575, which claims the benefit of U.S. Prov Pat App No. 62/522,274, filed Jun. 20, 2017, U.S. Prov Pat App No. 62/451,533, filed Jan. 27, 2017, U.S. Prov Pat App No. 62/451,484, filed Jan. 27, 2017, and U.S. Prov Pat App No. 62/444,736, filed Jan. 10, 2017. The foregoing applications and corresponding patents are incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62879705 | Jul 2019 | US | |
| 62874178 | Jul 2019 | US | |
| 62522274 | Jun 2017 | US | |
| 62451533 | Jan 2017 | US | |
| 62451484 | Jan 2017 | US | |
| 62444736 | Jan 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16921065 | Jul 2020 | US |
| Child | 17477199 | US | |
| Parent | 16180323 | Nov 2018 | US |
| Child | 16921065 | US | |
| Parent | 16028398 | Jul 2018 | US |
| Child | 16180323 | US | |
| Parent | PCT/US18/13097 | Jan 2018 | US |
| Child | 16028398 | US | |
| Parent | 15866455 | Jan 2018 | US |
| Child | PCT/US18/13097 | US |