Patent Application
20160052927
The present invention relates to the use of organic oxyimides as flame retardant for plastic materials. According to the present invention, a flame-retardant plastic material composition is likewise indicated, which includes an oxyimide as flame retardant. In addition, moulded parts, produced from a flame-retardant polymer composition according to the invention, are indicated.
Most plastic materials, such as e.g. plastic materials based on polyolefins, polystyrene, polyamides, polyurethanes or polyesters, are combustible and comparatively easily inflammable. In order to reduce or exclude the risk of fire of plastic materials in specific applications, it is therefore absolutely necessary to reduce the flammability and to use flameproof or flame-retardant plastic material compositions. For this purpose, generally flame retardants are added to the plastic material with the aim of preventing ignition for a specific time or significantly reducing the spread of fire. Traditional flame retardants are based on chlorine- and bromine-containing compounds (generally in combination with antimony trioxide), on phosphorus-containing, on nitrogen-containing compounds and/or on inorganic hydroxides. In modern times, halogen-free flame-retardant solutions are preferred for environmental reasons and/or from the point of view of toxicology.
For the production of flame-retardant plastic materials, there is a large number of flame retardants which are used generally specifically for substrates for a specific polymer and a specific field of use, corresponding to the standards which form the basis thereof. Flame-retardant plastic materials are used for example in electrical and electronic applications, in the transport/automobile field and in construction. A very effective flame-retardant class, developed in the last few years, on a nitrogen basis, preferably for polyolefins, is based on alkoxyamines (WO 99/00450, WO 2008101845, WO 2011086114). Due to cleavage of the alkoxyamines, radicals are produced in the case of fire, which radicals become involved in the decomposition process of the polymer and hence cause the flame-retardant effect (C. R. Wilen, R. Pfaendner, J. Appl. Pol. Sci. 2013, R. Pfaendner, C. R. Chemistry 9 (2006), 1338-1344). The alkoxyamines can also be used advantageously in synergistic combinations with other flame retardants (WO 02/074847, WO 03/016388, WO 2010026230, WO 2009080554, WO 2011003773, WO 2011117266). Furthermore, it was found that hydroxylamine stabilisers also can effect a synergistic improvement in the effect of bromine-containing, phosphorus-containing and inorganic flame retardants (WO 02/074847).
The previously mentioned flame retardants known from the state of the art do not however fulfil all requirements placed on these nowadays. Thus these must still be used for example in a relatively high concentration with respect to the plastic material composition to be protected, which can lead for example to impairment in the mechanical properties of the plastic material. Further criteria are for example the thermal stability, discolouration, formation of toxic gases in the case of fire, easy availability on an industrial scale inter alia.
It was the object of the present invention to make available new flame retardants and synergistic flame retardant components which are effective in low concentrations and comparatively readily available.
This object is achieved, with respect to the use of organic oxyimides as flame retardant for plastic materials, according to the features of patent claim 1, with respect to a flame-retardant plastic material composition, by the features of patent claim 12, with respect to a method for the production of this plastic material composition, by the features of patent claim 15 and also, with respect to a moulded part, a paint or a coating which is producible from a flame-retardant polymer composition, by the features of patent claim 16. The respectively dependent patent claims thereby represent advantageous developments.
According to the invention, the use of organic oxyimides, comprising at least one structural element of the subsequently illustrated formula I
is indicated as flame retardant for plastic materials.
Formula I should thereby be understood such that the illustrated structural element is contained in the organic oxyimide. The oxyimides used according to the invention should not thereby be equated with isocyanurates or compounds or compound classes derived herefrom. The oxyimide used according to the invention is thereby halogen-free, i.e. the corresponding compound includes no halogen atoms.
It was able to be shown that the organic oxyimides used according to the invention have good effectiveness, as described above, for making plastic materials flame-retardant.
Hence new flame retardants and flame-retardant compositions for polymers are proposed, which, from the point of view of effect and price/performance ratio, represent an attractive alternative to compositions known and used today.
According to a preferred embodiment of the present invention, oxyimides, comprising at least one structural element of the subsequent formula II,
R1 standing for hydrogen or a possibly substituted alkyl-, cycloalkyl-, aryl-, heteroaryl- or acyl radical, are used as flame retardant.
Alternatively or in combination with the previously mentioned preferred variant, bridged oxyimides, comprising at least one structural element of the subsequent formula III,
R2 standing for a possibly substituted akylene-, cycloalkylene-, arylene-, heteroarylene- or bridging acyl radical, can likewise be used.
According to a preferred variant, R2 is selected from radicals of the group consisting of —(CH2)n— with n=1 to 18, —CH(CH3)—, —C(CH3)2, —O—, —S—, —SO2—, —NHCO—, —CO— and also the subsequently illustrated groups,
the cycloaliphatic or aromatic ring systems contained in the previously illustrated groups being unsubstituted or substituted by one or more alkyl- and/or alkoxy groups,
For particular preference, the radicals R2 are thereby reproduced by the subsequently illustrated structural elements, Q having the above-indicated meaning:
In particular, the radicals R2 can thereby be given by the subsequent structural elements:
According to a particularly preferred embodiment, the organic oxyimide has one of the subsequent structural formulae:
respectively R1 and R2 having the above-indicated meaning.
A particularly preferred radical R1 is thereby hydrogen or an acyl radical.
The subsequently illustrated compounds with R1═H are particularly suitable for the purposes of the present invention,
R2 having the above-indicated meaning.
Also the subsequently illustrated compounds with R1=acyl are suitable in particular for the purposes of the present invention.
The above-indicated compounds with R1═H are for example available by the reaction of commercially obtainable di- or tetracarboxylic anhydrides with hydroxylamine in the form of the hydrochloride or then with R1═H or R2=acyl by the subsequent esterification of the obtained hydroxylamines with for example an acid chloride or by reesterification from the corresponding acid esters with e.g. readily volatile alcohols, such as e.g. methyl esters.
Furthermore, these hydroxylamine derivatives can also be present in the form of linear oligomers or polymers by, for example, difunctional hydroxylamines (R1═H) being converted, e.g. with difunctional acid chlorides and then the corresponding polyesters being obtained. Analogously, the corresponding linear polyurethanes can be produced from the difunctional hydroxylamines (R1═H) and diisocyanates. The syntheses of these polymers is described in more detail for example in H. Imajo et al., J. Pol. Sci.: Pol. Chem. 18, 2189-2196 (1980) or in H. Imajo et al., J. Pol. Sci.: Pol. Chem. 19, 1855-1861 (1981).
If desired, these polymers can also be synthesised in the form of branched or crosslinked structures by a difunctional component being replaced partially or completely by a tri-, tetra- or higher-functionalised compound, e.g. a trifunctional acid component or a trifunctional hydroxylamine.
Furthermore, it is possible and obvious to the person skilled in the art that copolymers can be synthesised according to the invention by e.g. a difunctional hydroxylimide being replaced partially by a diol compound, such as e.g. ethylene glycol, butanediol-1-4, hexanediol-1,6, hydroquinone, 4,4′-dihydroxybiphenyl. Correspondingly, e.g. copolyesters or copolyurethanes are available. Furthermore, by means of partial exchange of the difunctional hydroxylimides with difunctional compounds structures other than diols such as e.g. diamines, copolymers of mixed structures, such as e.g. polyester amides, are obtainable.
According to the present invention, the organic oxyimides which are used according to the invention can be used for the following illustrated plastic materials, particularly preferred in thermoplastic, elastomeric or duroplastic plastic materials, in particular thermoplastic polymers:
Provided that the polymers indicated under a) to o) concern copolymers, these can be present in the form of stochastic (“random”), block- or “tapered” structures.
Provided that the polymers indicated under a) to o) concern stereo-regular polymers, these can be present in the form of isotactic, stereotactic, but also in atactic forms.
Furthermore, the polymers indicated under a) to o) can have both amorphous and (partially) crystalline morphologies.
Possibly, the polyolefins mentioned under a) can also be present in crosslinked form, e.g. crosslinked polyethylene which is then termed X-PE. The polyolefins mentioned under a) can also have any stereo structures, i.e. be present isotactically, syndiotactically or atactically or in stereo block structures.
For very particular preference, the organic oxyimides used according to the invention are used for polyolefins, in particular for the polyolefins mentioned under a).
Furthermore, the present flame retardants can be used in the following duromeric, non-thermoplastic, plastic materials:
The flame retardants according to the invention are used for very particular preference in the case of polyolefins, preferably polypropylene and/or polyethylene and the copolymers and blends thereof.
Furthermore, the oxyimide which is used according to the invention can be used in combination with at least one further flame retardant, as a result of which synergistic effects are produced. The at least one further flame retardant is thereby preferably selected from the group consisting of
The halogen-containing flame retardants mentioned under b) frequently concern commercial products which are commercially available, e.g. from the companies Albemarle, Chemtura/Great Lakes or ICL.
In particular in the case of combinations of the oxyimide used according to the invention with at least one radical former as further flame retardant, synergistic effects result.
Radical formers in the sense of the present invention are compounds which can produce radicals by means of thermal and light-induced cleavage. Suitable radical formers for the applications present here are those which have sufficient thermal stability for the plastic material- or coating-processing processes, i.e. during processing, still form no or only very small quantities of radicals and produce radicals spontaneously only at higher temperatures, as occur only in the case of fire. The respective processing processes and temperatures for coatings and plastic material processing processes are known to the person skilled in the art. Plastic material processing processes and associated temperatures can however also be obtained from the expert literature, such as e.g. H. Domininghaus, P. Elsner, P. Eyerer, T. Hirth, Plastic materials, 8th edition, Springer 2012.
The radical former is thereby selected preferably from the group consisting of N-alkoxyamines, —C—C— radical formers, radical formers with azo groups (—N═N—), radical formers with hydrazine groups (—NH—HN—), radical formers with hydrazone groups (>C═N—NH—), radical formers with azine groups (>C═N—N═C<), radical formers with triazene groups (—N═N—N<), radical formers with disulphide- or polysulphide groups (—S—S), radical formers with thiol groups (—S—H), thiuram sulphide, dithiocarbamates, mercaptobenzothiazole and sulphene amides.
The radical former is thereby selected for particular preference from the group consisting of
Typical examples of the previously mentioned N-alkoxyamines of the indicated structure are thereby:
1-cyclohexyloxy-2,2,6,6-tetramethyl-4-octadecylaminopiperidine; bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate; 2,4-bis[(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-6-(2-hydroxyethylamino-S-triazine; bis(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl) adipate; 2,4-bis[(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-6-chloro-S-triazine; 1-(2-hydroxy-2-methylpropoxy)-4-hydroxy-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-oxo-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine; bis(1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl) sebacate; bis(1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl) adipate; 2,4-bis{N-[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]-N-butylamino}-6-(2-hydroxyethylamino)-S-triazine); 4-piperidinol, 2,2,6,6-tetramethyl-1-(undecyloxy)-,4,4′-carbonate; the reaction product of 2,4-bis[(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-6-chloro-S-triazine with N,N′-bis(3-aminopropylethylenediamine); the oligomer compound, which is the condensation product of 4,4′-hexamethylene-bis(amino-2,2,6,6-tetramethylpiperidine) and 2,4-dichloro-6-[(1-cyclohexyloxy-2,2,6,6-tetramethyl-4-yl)butylamino]-S-triazine, closed at the ends with 2-chloro-4,6-bis(dibutylamino)-S-triazine; aliphatic hydroxylamine, such as e.g. distearyl hydroxylamine; and also compounds of the formula
in which n=1-15.
The above-mentioned compounds are partially commercial products and are sold under the following trade names: FLAMESTAB NOR 116®, TINUVIN NOR 371® IRGATEC CR 76® of BASF SE, Hostavin NOW® of Clariant or ADK Stab LA 81® of Adeka. Dicumyl and polycumyl are commercial products which are obtainable for example from United Initiators.
The at least one further flame retardant can be in particular also a phosphorus-containing flame retardant. Preferred phosphorus-containing flame retardants are thereby phosphinates of the following structures:
R1 and R2 preferably being identical or different and being selected from linear or branched C1-C6 alkyl and/or aryl; M being selected from the group consisting of Mg, Ca, Al, Sb, Sn, Ge, Ti, Fe, Zr, Ce, Bi, Sr, Mn, Li, Na, K, Zn and/or a protonated nitrogen base, preferably calcium ions, magnesium ions, aluminium ions and/or zinc ions; and m=1-4, preferably 2 or 3; n=1-4, preferably 1 or 3; x=1-4, preferably 1 or 2. In a particularly preferred embodiment, R1=alkyl, R2=alkyl and M=Al or Zn.
A particularly preferred example of a phosphinate according to the invention is the commercially available products Exolit OP® of Clariant SE.
Further preferred phosphorus-containing flame retardants are metal salts of hypophosphorous acid with a structure according to the formula
Met being a metal, selected from groups I, II, III and IV of the periodic table of elements, and n being a number from 1 to 4 which corresponds to the charge of the corresponding metal ion Met. Met is for example Na+, Ca2+, Mg2+, Zn2+, Ti4+ or Al3+, wherein Ca2+, Zn2+ and Al3+ are particularly preferred.
The above-mentioned salts of hypophosphorous acid are partially commercially available, e.g. with the title Phoslite® of Italmatch Chemicals.
A further preferred group of phosphorus-containing flame retardants are phosphonates or phosphonic acid diaryl esters of a structure according to the following formula:
R8 and R10═H, alkyl, preferably C1-C4 alkyl, R9═C1-C4 alkyl, u=1-5 and v=1-5.
Corresponding structures can also be present in the form of phosphonate oligomers, polymers and co-polymers. Linear or branched phosphonate oligomers and polymers are known from the state of the art. For branched phosphonate oligomers and polymers, reference is made to the US patents U.S. Pat. No. 2,716,101, U.S. Pat. No. 3,326,852, U.S. Pat. No. 4,328,174, U.S. Pat. No. 4,331,614, U.S. Pat. No. 4,374,971, U.S. Pat. No. 4,415,719, U.S. Pat. No. 5,216,113, U.S. Pat. No. 5,334,692, U.S. Pat. No. 3,442,854, U.S. Pat. No. 6,291,630 B1, U.S. Pat. No. 6,861,499 B2 and U.S. Pat. No. 7,816,486 B2. For phosphonate oligomers, reference is made to the US patent applications US 2005/0020800 A1, US 2007/0219295 A1 and US 2008/0045673 A1. With respect to linear phosphonate oligomers and polymers, reference is made to the US patent documents U.S. Pat. No. 3,946,093, U.S. Pat. No. 3,919,363, U.S. Pat. No. 6,288,210 B1, U.S. Pat. No. 2,682,522 and U.S. Pat. No. 2,891,915.
Phosphonates are available for example under the trade name Nofia® of FRX Polymers.
A further preferred group of phosphorus-containing flame retardants are compounds based on oxaphosphorine oxide and derivatives thereof with for example the following structures:
M being a metal, selected from the second, third, twelfth or thirteenth group of the periodic table of the elements, x=2 or 3, n≧10, m=0-25, R═H, halogen or an aliphatic or aromatic radical with 1-32 C atoms and R1═H, C1-C6 alkyl.
Products based on oxaphosphorine oxide are marketed for example under the trade name Ukanol® of Schill and Seilacher GmbH. Further compounds can be produced for example according to the patent specifications WO 2013020696, WO 2010135398, WO 03070736, WO 2006084488, WO 2006084489, WO 2011000019, WO 2013068437, WO 2013072295.
Further synergistic phosphorus-containing flame retardants are cyclic phosphonates of a structure according to one of the following formulae:
A1 and A2, independently of each other, representing a substituted or unsubstituted, straight-chain or branched alkyl group with 1 to 4 carbon atoms, substituted or unsubstituted benzyl, substituted or unsubstituted phenyl, substituted or unsubstituted naphthyl, and A3 and A4, independently of each other, being methyl or ethyl and A5 being a straight-chain or branched alkyl group with 1 to 4 carbon atoms or a phenyl- or benzyl group which can have respectively up to 3 methyl groups.
Cyclic phosphonates are marketed for example by the company Thor GmbH under the trade name Aflammit® or can be produced according to EP 2450401.
The at least one further flame retardant can be in particular also a nitrogen-containing flame retardant. Preferred nitrogen-containing flame retardants are melamine polyphosphate, melamine cyanurate, melamine-metal phosphates, poly-[2,4-(piperazin-1,4-yl)-6-(morpholin-4-yl)-1,3,5-triazine] and ammonium polyphosphate. These compounds are commercial products and obtainable under the trade names Melapur® of BASF SE, Budit® of Budenheim Chemische Fabrik, Exolit® of Clariant, Safire® of Floridienne or MCA PPM triazine of MCA Technologies GmbH.
In the case of a combined use of the oxyimide used according to the invention with at least one further flame retardant, it is preferred if the previously mentioned compounds are used in a weight ratio (oxyimide:flame retardant) of 99:1 to 1:99, preferably of 5:95 to 50:50, particularly preferred of 10:90 to 30:70.
Furthermore, it is advantageous if the organic oxyimides, relative to the plastic materials, are used at 0.01 to 30% by weight, preferably at 0.1 to 20% by weight, particularly preferred at 1 to 10% by weight.
In addition, the present invention relates to a flame-retardant plastic material composition, comprising or consisting of
According to a preferred embodiment, the flame-retardant plastic material composition can comprise in addition
In addition, additives can be used, selected from the group consisting of UV absorbers, light stabilisers, stabilisers, hydroxylamines, benzofuranones, metal deactivators, filler deactivators, nucleation agents, impact strength enhancers, plasticisers, lubricants, rheology modifiers, processing aids, pigments, colourants, optical brighteners, antimicrobial active substances, antistatic agents, slip agents, antiblocking agents, coupling means, dispersants, compatibilisers, oxygen collectors, acid collectors, marking means or anti-fogging means. In a preferred embodiment, the compositions comprise in particular acid collectors, e.g. based on salts of long-chain acids, such as e.g. calcium stearate, magnesium stearate, zinc stearate, calcium lactate or hydrotalcites and/or stabilisers from the group of phenolic antioxidants and phosphites/phosphonites and/or light stabilisers from the group of hindered amines (HALS) and/or dispersants.
Suitable light stabilisers are for example compounds based on 2-(2′-hydroxyphenyl)benzotriazoles, 2-hydroxybenzophenones, esters of benzoic acids, acrylates, oxamides and 2-(2-hydroxyphenyl)-1,3,5-triazines.
Suitable 2-(2″-hydroxyphenyl)benzotriazoles are for example 2-(2′-hydroxy-5′-methylphenyl)benzotriazole, 2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)benzotriazole, 2-(5′-tert-butyl-2′-hydroxy-phenyl)benzotriazole, 2-(2′-hydroxy-5′-(1,1,3,3-tetramethylbutyl)phenyl)benzotriazole, 2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-methylphenyl-5-chlorobenzotriazole, 2-(3′-sec-butyl-5′-tert-butyl-2′-hydroxyphenyl)benzotriazole, 2-(2′-hydroxy-4′-octyloxyphenyl)benzotriazole, 2-(3′,5′-di-tert-amyl-2′-hydroxyphenyl)benzotriazole, 2-(3′,5′-bis(α,α-dimethylbenzyl)-2′-hydroxyphenyl)benzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyloxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)carbonylethyl]-2′-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′12-methoxycarbonylethyl)phenyl)benzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′12-octyloxycarbonylethyl)phenyl)benzotriazole, 2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)carbonylethyl]-2′-hydroxyphenyl)benzotriazole, 2-(3′-dodecyl-2′-hydroxy-5′-methylphenyl)benzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-isooctyloxycarbonylethyl)phenylbenzotriazole, 2,2′-methylenebis[4-(1,1,3,3-tetramethylbutyl)-6-benzotriazol-2-ylphenol]; the product of reesterification of 2-[3′-tert-butyl-5′-(2-methoxycarbonylethyl)-2′-hydroxyphenyl]-2H-benzotriazole with polyethylene glycol 300; [R—CH2CH2—COO—CH2CH2-2, with R=3′-tert-butyl-4′-hydroxy-5′-2H-benzotriazol-2-ylphenyl, 2-[2′-hydroxy-3′-(α,α-dimethylbenzyl)-5′-(1,1,3,3-tetramethylbutyl)phenyl]benzotriazole, 2-[2′-hydroxy-3′-(1,1,3,3-tetramethylbutyl)-5′-(α,α-dimethylbenzyl)phenyl]benzotriazole.
Suitable 2-hydroxybenzophenones are for example 4-hydroxy-, 4-methoxy-, 4-octyloxy-, 4-decyloxy-4-dodecyloxy, 4-benzyloxy, 4,2′,4′-trihydroxy- and 2′-hydroxy-4,4′-dimethyoxy derivatives of 2-hydroxybenzophenones.
Suitable acrylates are for example ethyl-α-cyano-β,β-diphenylacrylate, isooctyl-α-cyano-β,β-diphenylacrylate, methyl-α-carbomethoxycinnamate, methyl-α-cyano-β-methyl-β-methoxycinnamate, butyl-α-cyano-β-methyl-p-methoxycinnamate, methyl-α-carbomethoxy-p-methoxycinnamate and N-(β-carbomethoxy-β-cyanoyinyl)-2-methylindoline.
Suitable esters of benzoic acids are for example 4-tert-butylphenylsalicylate, phenylsalicylate, octylphenylsalicylate, dibenzoylresorcinol, bis(4-tert-butylbenzoyl)resorcinol, benzoylresorcinol, 2,4-di-tert-butylphenyl-3, 5-di-tert-butyl-4-hydroxybenzoate, hexadecyl-3, 5-di-tert-butyl-4-hydroxybenzoate, octadecyl-3, 5-di-tert-butyl-4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl-3, 5-di-tert-butyl-4-hydroxybenzoate.
Suitable oxamides are for example 4,4′-dioctyloxyoxanilide, 2,2′-diethoxyoxanilide, 2,2′-dioctyloxy-5, 5′-di-tert-butoxanilide, 2,2′-didodecyloxy-5, 5′-di-tert-butoxanilide, 2-ethoxy-2′-ethyloxanilide, N,N′-bis(3-dimethylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2′-ethoxanilide and the mixtures thereof with 2-ethoxy-2′-ethyl-5,4′-di-tert-butoxanilide, mixtures of o- and p-methoxy-disubstituted oxanilides and mixtures of o- and p-ethoxy-disubstituted oxanilides.
Suitable 2-(2-hydroxyphenyl)-1,3,5-triazines are for example 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2,4-bis(2-hydroxy-4-propyloxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl-1,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-butyloxypropoxy)-phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-octyloxypropyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[4-(dodecyloxy/tridecyloxy-2-hydroxypropoxy)-2-hydroxyphenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxypropoxy)phenyl]-4,6-bis(2,4-dimethylphenyl-1,3,5-triazine, 2-(2-hydroxy-4-hexyloxy)phenyl-4,6-diphenyl-1,3,5-triazine, 2-(2-hydroxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine, 2,4,6-tris[2-hydroxy-4-(3-butoxy-2-hydroxypropoxy)phenyl]-1,3,5-triazine, 2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)-6-phenyl-1,3,5-triazine, 2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]phenyl}-4,6-bis(2,4-dimethylphenyl-1,3,5-triazine.
Suitable metal deactivators are for example N,N′-diphenyloxamide, N-salicylal-N′-salicyloylhydrazine, N,N′-bis(salicyloyl)hydrazine, N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine, 3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalyldihydrazide, oxanilide, isophthaloyldihydrazide, sebacoylbisphenylhydrazide, N,N′-diacetyladipoyldihydrazide, N,N′-bis(salicyloyl)oxylyldihydrazide, N,N′-bis(salicyloyl)thiopropionyldihydrazide.
In particular, the following structures are suitable as metal deactivators:
Suitable phenolic antioxidants are for example:
alkylated monophenols, such as e.g. 2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-dimethylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dimethylphenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol, 2,6-di-tert-butyl-4-methoxymethylphenol, linear or branched nonylphenols, such as e.g. 2,6-dinonyl-4-methylphenol, 2,4-dimethyl-6-(1′-methylundec-1′-yl)phenol, 2,4-dimethyl-6-(1′-methylheptadec-1′-yl)phenol, 2,4-dimethyl-6-(1′-methyltridec-1′-yl)phenol and mixtures hereof;
alkylthiomethylphenols, such as e.g. 2,4-dioctylthiomethyl-6-tert-butylphenol, 2,4-dioctylthiomethyl-6-methylphenol, 2,4-dioctylthiomethyl-6-ethylphenol, 2,6-didodecylthiomethyl-4-nonylphenol;
hydroquinones and alkylated hydroquinones, such as e.g. 2,6-di-tert-butyl-4-methyoxyphenol, 2, 5-di-tert-butylhydroquinone, 2, 5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyloxyphenol, 2,6-di-tert-butylhydroquinone, 2, 5-di-tert-butyl-4-hydroxyanisole, 3, 5-di-tert-butyl-4-hydroxyanisole, 3, 5-di-tert-butyl-4-hydroxyphenylstearate, bis(3, 5-di-tert-butyl-4-hydroxylphenyl)adipate;
tocopherols, such as e.g. α-, β-, γ-, δ-tocopherol and mixtures of these (vitamin E);
hydroxylated thiodiphenylethers, such as e.g. 2,2′-thiobis(6-tert-butyl-4-methylphenol), 2,2′-thiobis(4-octylphenol), 4,4′-thiobis(6-tert-butyl-3-methylphenol), 4,4′-thiobis(6-tert-butyl-2-methylphenol), 4,4′-thiobis(3,6-di-sec-amylphenol), 4,4′-bis(2,6-dimethyl-4-hydroxyphenyl)disulphide;
alkylidenebisphenols, such as e.g. 2,2′-methylenebis(6-tert-butyl-4-methylphenol), 2,2′-methylenebis(6-tert-butyl-4-ethylphenol), 2,2′-methylenebis[4-methyl-6-(α-methylcyclohexyl)phenol], 2,2′-methylenebis(4-methyl-6-cyclhexylphenol), 2,2′-methylenebis(6-nonyl-4-methylphenol), 2,2′-methylenebis(4,6-di-tert-butylphenol), 2,2′-ethylidenebis(4,6-di-tert-butylphenol), 2,2′-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2′-methylenebis[6-(α-methylbenzyl)-4-nonylphenol], 2,2′-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol], 4,4′-methylenebis(2,6-di-tert-butylphenol, 4,4′-methylenebis(6-tert-butyl-2-methylphenol), 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane, ethyleneglycol-bis[3,3-bis(3′-tert-butyl-4′-hydroxyphenyl)butyrate], bis(3-tert-butyl-4-hydroxy-5-methylphenyl)dicyclopentadiene, bis[2-(3′-tert-butyl-2′-hydroxy-5′-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate, 1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis(3, 5-di-tert-butyl-4-hydroxyphenyl)propane, 2,2-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-4-n-dodecylmercaptobutane, 1,1, 5, 5-tetra(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane;
O-, N- and S-benzyl compounds, such as e.g. 3,5,3′,5′-tetra-tert-butyl-4,4′-dihydroxydibenzylether, octadecyl-4-hydroxy-3,5-dimethylbenzylmercaptoacetate, tridecyl-4-hydroxy-3, 5-di-tert-butylbenzylmercaptoacetate, tris(3, 5-di-tert-butyl-4-hydroxybenzyl)amine, bis(4-tert-butyl-3-hydroxy-2, 6-dimethylbenzyl)dithioterephthalate, bis(3,5-di-tert-butyl-4-hydroxybenzyl) sulphide, isooctyl-3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate;
hydroxybenzylated malonates, such as e.g. dioctadecyl-2,2-bis(3,5-di-tert-butyl-2-hydroxybenzyl)malonate, dioctadecyl-2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)malonate, didodecylmercaptoethyl-2,2-bis(3, 5-di-tert-butyl-4-hydroxybenzyl)malonate, bis[4-(1,1,3,3-tetramethylbutyl)phenyl]-2,2-bis(3, 5-di-tert-butyl-4-hydroxybenzyl)malonate;
aromatic hydroxybenzyl compounds, such as e.g. 1,3,5-tris(3, 5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene, 1,4-bis(3, 5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene, 2,4,6-tris(3, 5-di-tert-butyl-4-hydroxybenzyl)phenol;
triazine compounds, such as e.g. 2,4-bis(octylmercapto)-6-(3, 5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3, 5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3, 5-di-tert-butyl-4-hydroxyphenoxy)-1,3,5-triazine, 2,4,6-tris(3, 5-di-tert-butyl-4-hydroxyphenoxy)-1,2,3-triazine, 1,3,5-tris(3, 5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 1,3,5-tris(4-tert-butyl-3-hydroxy-2, 6-dimethylbenzyl)isocyanurate, 2,4,6-tris(3, 5-di-tert-butyl-4-hydroxphenylethyl)-1,3,5-triazine, 1,3,5-tris(3, 5-di-tert-butyl-4-hydroyphenylpropionyl)hexahydro-1,3,5-triazine, 1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl)isocyanurate;
benzylphosphonates, such as e.g. dimethyl-2, 5-di-tert-butyl-4-hydroxybenzylphosphonate, diethyl-3, 5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl-3, 5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl-5-tert-butyl-4-hydroxy-3-methylbenzylphosphonate, the calcium salt of the monoethylester of 3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid;
acylaminophenols, such as e.g. 4-hydroxylauranilide, 4-hydroxystearanilide, octyl-N-(3, 5-di-tert-butyl-4-hydroxyphenyl)carbamate;
esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with mono- or multivalent alcohols, e.g. methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethyleneglycol, 1,2-propanediol, neopentylglycol, thiodiethyleneglycol, diethyleneglycol, triethyleneglycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane,
esters of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with mono- or multivalent alcohols, e.g. methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethyleneglycol, 1,2-propanediol, neopentylglycol, thiodiethyleneglycol, diethyleneglycol, triethylenerglycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6, 7-trioxabicyclo[2.2.2]octane, 3,9-bis[2-{3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy}-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane;
esters of β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with mono- or multivalent alcohols, e.g. methanol, ethanol, octanol, octadecaneol, 1,6-hexanediol, 1,9-nonanediol, ethyleneglycol, 1,2-propanediol, neopentylglycol, thiodiethyleneglycol, diethyleneglycol, triethyleneglycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane;
esters of 3,5-di-tert-butyl-4-hydroxyphenyl)acetic acid with mono- or multivalent alcohols, e.g. methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethyleneglycol, 1,2-propanediol, neopentylglycol, thiodiethyleneglycol, diethyleneglycol, triethyleneglycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane;
amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, such as e.g. N,N′-bis(3, 5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N′-bis(3, 5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazide, N,N′-bis[2-(3-[3, 5-di-tert-butyl-4-hydroxyphenyl]propionyloxy) ethyl]oxamide (Naugard®XL-1, marketed by Uniroyal);
ascorbic acid (vitamin C).
Particularly preferred phenolic antioxidants are:
octadecyl-3-(3, 5-di-tert-butyl-4-hydroxyphenyl)propionate, pentaerythritol-tetrakis[3-(3, 5-di-tert-butyl-4-hydroxyphenyl)propionate, tris(3, 5-di-tert-butyl-4-hydroxyphenyl)isocyanurate, 1,3,5-trimethyl-2,4,6-tris(3, 5-di-tert-butyl-4-hydroxyphenyl)isocyanurate, 1,3,5-trimethyl-2,4,6-tris(3, 5-di-tert-butyl-4-hydroxybenzyl)benzene, triethyleneglycol-bis[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionate, N,N′-hexan-1, 6-diyl-bis[3-(3, 5-di-tert-butyl-4-hydroxyphenyl)propionic acid amide.
Suitable phosphites/phosphonites are for example:
triphenylphosphite, diphenylalkylphosphites, phenyldialkylphosphites, tri(nonylphenyl)phosphite, trilaurylphosphites, trioctadecylphosphite, distearylpentaerythritoldiphosphite, tris-(2,4-di-tert-butylphenyl)phosphite, diisodecylpentaerythritoldiphosphite, bis(2,4-di-tert-butylphenyl)pentaerythritoldiphosphite, bis(2,4-di-cumylphenyl)pentaerythritoldiphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritoldiphosphite, diisodecyloxypentaerythritoldiphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritoldiphosphite, bis(2,4,6-tris(tert-butylphenyl)pentaerythritoldiphosphite, tristearylsorbitoltriphosphite, tetrakis(2,4-di-tert-butylphenyl)-4,4-biphenylenediphosphonite, 6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenzo[d,g]-1, 3,2-dioxaphosphocine, bis(2,4-di-tert-butyl-6-methylphenyl)methylphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)ethylphosphite, 6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-dibenzo[d, g]-1,3,2-dioxaphosphocine, 2,2′2″-nitrilo[triethyltris(3,3″,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite], 2-ethylhexyl(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl))phosphite, 5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane.
Particularly preferred phosphites/phosphonites are:
Further suitable stabilisators are amine antioxidants. Suitable amine antioxidants are for example:
N,N′-di-isopropyl-p-phenylenediamine, N,N′-di-sec-butyl-p-phenylenediamine, N,N′-bis(1,4-dimethylpentyl)-p-phenylenediamine, N,N′-bis(1-ethyl-3-methylpentyl)-p-phenylenediamine, N,N′-bis(1-methylheptyl)-p-phenylenediamine, N,N′-dicyclohexyl-p-phenylenediamine, N,N′-diphenyl-p-phenylenediamine, N,N′-bis(2-naphthyl)-p-phenylenediamine, N-isopropyl-N′-phenyl-p-phenylenediamine, N-(1,3-dimethylbutyl)-N,N′-phenyl-p-phenylenediamine, N-(1-methylheptyl)-N,N′-phenyl-p-phenylenediamine, N-cyclohexyl-N′-phenyl-p-phenylenediamine, 4-(p-toluenesulfamoyl)diphenylamine, N,N ‘-dimethyl-N,N’-di-sec-butyl-p-phenylenediamine, diphenylamine, N-allyldiphenylamine, 4-isopropoxydiphenylamine, N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine, N-phenyl-2-naphthylamine, octylated diphenylamine, e.g. p,p′-di-tert-octyldiphenylamine, 4-n-butylaminophenol, 4-butyrylaminophenol, 4-nonanoylaminophenol, 4-dodecanoylaminophenol, 4-octadecanoylaminophenol, bis(4-methoxyphenyl)amine, 2,6-di-tert-butyl-4-dimethylaminomethylphenol, 2,4′-diaminodiphenylmethane, 4,4′-diaminodiphenylmethane, N,N,N′,N′-tetramethyl-4,4′-diaminodiphenylmethane, 1,2-bis[(2-methylphenyl)amino]ethane, 1,2-bis(phenylamino)propane, (o-tolyl)biguanide, bis[4-(1′,3′-dimethylbutyl)phenyl]amine, tert-octylated N-phenyl-1-naphthylamine, a mixture of mono- and dialkylated tert-butyl/tert-octyldiphenylamines, a mixture of mono- and dialkylated nonyldiphenylamines, a mixture of mono- and dialkylated dodecyldiphenylamines, a mixture of mono- and dialkylated isopropyl/isohexyldiphenylamines, a mixture of mono- and dialkylated tert-butyldiphenylamines, 2,3-dihydro-3,3-dimethyl-4H-1,4-benzothiazine, phenothiazine, a mixture of mono- and dialkylated tert-butyl/tert-octylphenothiazines, a mixture of mono- and dialkylated tert-octylphenothiazines, N-allylphenothiazine, N,N,N′,N′-tetraphenyl-1,4-diaminobut-2-ene and also mixtures or combinations hereof.
Further suitable amine antioxidants are hydroxylamines, or N-oxides (nitrons), such as e.g. N,N-dialkylhydroxylamines, N,N-dibenzylhydroxylamine, N,N-dilaurylhydroxylamine, N,N-distearylhydroxylamine, N-benzyl-α-phenylnitron, N-octadecyl-α-hexadecylnitron, and also Genox EP (Chemtura) according to the formula:
Further suitable stabilisers are thiosynergists. Suitable thiosynergists are for example, distearylthiodipropionate, dilauryldipropionate or the compound according to the following formula:
Further suitable stabilisers, in particular for polyamides, are copper salts, such as e.g. copper(I)iodide, copper(I)bromide or copper complexes, such as e.g. triphenylphosphine-copper(I) complexes.
Suitable hindered amines are for example 1,1-bis(2,2,6,6-tetramethyl-4-piperidyl)succinate, bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate, bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidyl)sebacate, bis(1,2,2,6,6-pentamethyl-4-piperidyl)-n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine und succinic acid, linear or cyclic condensation products of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-tert-octylamino-2,6-di-chloro-1,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl)nitrilotriacetate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylate, 1,1′-(1,2-ethandiyl)-bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, linear or cyclic condensation products of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-morpholino-2,6-dichloro-1,3,5-triazine, the reaction product of 7,7,9,9-tetramethyl-2-cycloundecyl-1-oxa-3,8-diaza-4-oxospiro-[4,5]decane und epichlorhydrin.
Suitable dispersants are for example:
polyacrylates, e.g. copolyers with long-chain side groups, polyacrylate block copolymers, alkylamides: e.g. N,N′-1,2-ethandiylbisoctadecaneamide sorbitan ester, e.g. monostearyl sorbitan ester, titanates und zirconates, reactive copolymers with functional groups, e.g. polypropylene-co-acrylic acid, polypropylene-co-maleic anhydride, polyethylene-co-glycidylmethacrylate, polystyrene-alt-maleic anhydride-polysiloxanes: e.g. dimethylsilanediol-ethylene oxide copolymer, polyphenylsiloxane copolymer, amphiphilic copolymers: e.g. polyethylene-block-polyethylenoxide, dendrimers, e.g. hydroxyl group-containing dendrimers.
Suitable nucleation agents are for example talc, alkali or alkaline earth salts of mono- and polyfunctional carboxylic acids, such as e.g. benzoic acid, succinic acid, adipic acid, e.g. sodium benzoate, zinc glycerolate, aluminium hydroxy-bis(4-tert-butyl)benzoate, benzylidenesorbitols, such as e.g. 1,3:2,4-bis(benzylidene)sorbitol or 1,3:2,4-bis(4-methylbenzylidene)sorbitol, 2,2″-methylene-bis-(4,6-di-tert-butylphenyl)phosphate, and also trisamides, such as e.g according to the following structures
Suitable fillers and reinforcing materials are for example synthetic or natural materials, such as e.g. calcium carbonate, silicates, glass fibres, glass balls (solid or hollow), talc, mica, kaolin, barium sulphate, metal oxides and metal hydroxides, carbon black, graphite, carbon nanotubes, graphene, sawdust or fibres from natural products, such as e.g. cellulose, or synthetic fibres. Further suitable fillers are hydrotalcites or zeolites or layer silicates, such as e.g. montmorrillonite, bentonite, beidelite, mica, hectorite, saponite, vermiculite, ledikit, magadite, illite, kaolinite, wollastonite, attapulgite.
Suitable pigments can be of an inorganic or organic nature. Suitable inorganic pigments are for example titanium dioxide, zinc oxide, zinc sulphide, iron oxide, ultramarine, carbon black. Suitable organic pigments are for example anthraquinones, anthanthrones, benzimidazolones, quinacridones, diketopyrrolopyrroles, dioxazines, indanthrones, isoindolinones, azo compounds, perylenes, phthalocyanines or pyranthrones. Further suitable pigments are effect pigments on a metal base or pearlescent pigments on a metal oxide base.
Optical brighteners are for example bisbenzoxazoles, phenylcumarines or bis(styryl)biphenyls and in particular optical brighteners of the formulae:
Suitable filler deactivators are for example epoxides, such as e.g. bisphenol-A-diglycidyl ethers, polysiloxanes, polyacrylates, in particular block copolymers such as polymethacrylic acid-polyalkylene oxide.
Suitable antistatic agents are for example ethoxylated alkylamines, fatty acid esters, alkyl sulphonates and polymers such as e.g. polyether amides.
Furthermore, the present invention relates to a moulding compound, a moulded part, a paint or a coating producible from a previously described flame-retardant plastic material composition, in particular in the form of injection moulded parts, foils or films, coatings or paints, foams, fibres, cables and pipes, profiles, strips, membranes, such as e.g. geomembranes, adhesives, which are produced by extrusion, injection moulding, blow-moulding, calendering, pressing processes, spinning processes or brushing and coating processes, e.g. for the electrical and electronic industry, construction industry, transport industry (car, aircraft, ship, train), for medical applications, for household and electrical appliances, vehicle parts, consumer articles, furniture, textiles. A further field of use is varnishes, paints and coatings.
For example, the compositions according to the invention can be used for marine applications (pontoons, planks, boats), auto applications (bumpers, batteries, trim parts, petrol tanks, cables, wires etc.), aircraft parts, railway parts, bicycle and motor cycle parts, space applications, such as e.g. satellite parts, housing parts for electrical appliances, such as computers, telephones, printers, audio and video systems, plugs, printed circuits, switches, lamp shades, refrigerators, coffee machines, vacuum cleaners, rotor blades for energy production, ventilators, foils for roof constructions, building foils, pipes, such as e.g. waste water pipes and gas pipes, connection parts, drainage systems, profiles, such as e.g. window profiles or cable channels, wood composites, furniture, flooring, covering plates, artificial grass, stadium seating, carpets, nets, ropes, furniture parts, mats, garden seats, outdoor boxes, containers and barrels.
The invention relates likewise to a method for the production of a previously described plastic material composition according to the invention in which the at least one organic oxyimide is incorporated before, after or at the same time as the at least one further flame retardant in the at least one plastic material, preferably the at least one thermoplastic polymer.
Incorporation of the above-described flame retardants and the additional additives in the plastic material is effected by normal processing methods, the polymer being melted and mixed with the flame retardants and additives, preferably by mixers, kneaders and extruders. As processing machines, extruders, such as e.g. single-screw extruders, twin-screw extruders, planet roller extruders, ring extruders, co-kneaders are preferred, which are preferably equipped with vacuum degassing. The processing can thereby be effected under air or possibly under inert gas conditions. Different flame retardants and additives can be added thereby separately or as a mixture, in the form of liquids, powders, granulates or compacted products or likewise in the form of master batches or concentrates which comprise for example 50-80% of the compositions according to the invention.
The invention likewise relates to a flame-retardant composition consisting of an organic oxyimide, comprising at least one structural element of the subsequently illustrated formula I,
and a further flame retardant, the organic oxyimide being halogen-free.
The present invention is explained in more detail with reference to the subsequent embodiments without restricting the invention to the special parameters illustrated there.
12.3 g (0.1773 mol, 2.2 eq.) hydroxylamine hydrochloride is dissolved in 100 ml of pyridine. 17.6 g (0.0807 mol, 1 eq.) of pyromellitic dianhydride is added to the solution. The reaction mixture is agitated for 2 h at 90° C. and subsequently for a further 12 h at room temperature. The precipitated residue is filtered off and washed with 5% hydrochloric acid and also with water. 12 g (60%) of a white product is obtained.
1H-NMR (DMSO, 300 MHz) δ [ppm]=8.13 (s, 2H, CH), 11.15 (s, 2H, OH).
4.9 g (0.0705 mol, 1.5 eq.) of hydroxylamine hydrochloride is dissolved in 60 ml of pyridine. 9.3 g (0.0469 mol, 1 eq.) of 1,8-naphthalic anhydride is added to the solution. The reaction mixture is agitated for 20 h at room temperature. The precipitated residue is filtered off and washed with 5% hydrochloric acid and also with water. 8 g (80%) of a white product is obtained.
1H-NMR (DMSO, 300 MHz) δ [ppm]=7.87 (t, 2H, CH), 8.49 (dd, 4H, CH), 10.73 (s, 1H, OH).
91 g of N-hydroxyphthalimide (0.5578 mol, 3 eq.) is dissolved in 200 ml of pyridine under a protective gas atmosphere. 38 g (0.1870 mol, 1 eq.) of terephthalic dichloride is added to the solution. The mixture is agitated for 2 h at 60° C. and subsequently for 12 h at room temperature. The white solid material is filtered off and washed with 5% hydrochloric acid and also with water. 76 g (89%) of white crystals is obtained.
1H-NMR (DMSO, 300 MHz) δ [ppm]=8.05 (m, 8H, CH), 8.44 (s, 4H, CH).
30 g (0.1840 mol, 3 eq.) of N-hydroxyphthalimide is dissolved in 180 ml of dry pyridine under a protective gas atmosphere. 6.75 ml (0.0613 mol, 1 eq.) of succinic dichloride is added in drops to the solution. The reaction mixture is agitated for 24 h at room temperature. The precipitated solid material is filtered off and washed with 5% hydrochloric acid and also with water. The purification is effected by recrystallisation in dichloromethane. 15 g (60%) of white crystals is obtained.
1H-NMR (DMSO, 300 MHz) δ [ppm]=3.21 (s, 4H, CH2), 7.96 (m, 8H, CH).
2.82 (0.0139 mol. 1 eq.) of terephthalic acid dichloride is suspended in a heated Schlenk flask under a nitrogen stream in 60 ml of dry pyridine. A second solution of 4.79 g (0.0417 mol, 3 eq.) of N-hydroxysuccinimide in 60 ml dry pyridine is added in drops to the suspension under a protective gas atmosphere and the reaction mixture is agitated for 24 h at room temperature. The precipitated residue is filtered off and washed with 5% hydrochloric acid (3×15 ml) and also with water. The obtained solid material is dried in a vacuum. 3.379 g (68%) of a white product is obtained.
1H-NMR (DMSO, 300 MHz) δ [ppm]=2.92 (s, 8H, CH3), 8.34 (s, 4H, CH).
3.80 g (0.0232 mol, 3 eq.) of N-hydroxyphthalimide is dissolved with 2.1 ml (0.026 mol, 3.4 eq.) of pyridine in a heated Schlenk flask in the nitrogen stream in 83 ml of dry acetone and then cooled to 5° C. With agitation, a solution of 1.4 ml (0.0077 mol, 1 eq.) of trimesyltrichloride in 19 ml distilled acetone is added in drops with agitation. After completion of the addition, the mixture is agitated for 1 h at 5° C., subsequently the reaction mixture is agitated for 12 h at room temperature. The precipitated, white solid material is filtered off and washed with 5% hydrochloric acid and also with water. 3.9 g (78%) of a white product is obtained.
1H-NMR (DMSO, 300 MHz) δ [ppm]=8.04 (m, 12H, CH), 9.09 (s, 3H, CH).
6.18 g (0.0290 mol, 2.5 eq.) of N-hydroxynaphthalimide is dissolved in a heated Schlenk flask in the nitrogen stream in 180 ml of dry pyridine at 45° C. Under a protective gas atmosphere, 2.3 g (0.0113 mol, 1 eq.) of terephthalic acid dichloride is added to the solution. The reaction mixture is agitated for 1 h at 45° C. and subsequently for a further 20 h at room temperature. The precipitated residue is filtered off and washed with 5% hydrochloric acid and also with water. 4.8 g (76%) of a white product is obtained.
1H-NMR (ODCB, 300 MHz) δ [ppm]=7.41 (t, 4H, CH), 7.83 (d, 4H, CH), 8.12 (s, 4H, CH), 8.34 (d, 4H, CH).
The extrusions of the polypropylene samples (DOW 766-03) are effected at a temperature of 190° C. and a screw speed of rotation of 150 rpm on a DSM Micro 5cc, twin-screw extruder. The dwell time of the mixture in the bypass operation is 60 s. The desired mixture of polymer and additives (see subsequent table 1) is firstly mixed manually in a beaker glass and supplied in small portions to the microextruder. If the volume of the appliance is filled with melt, the material remains for another 60 s (dwell time) in the appliance and then is released.
The obtained plastic material strands are granulated (Pell-Tec SD 50 pure).
Test pieces for the fire test are produced from the granulate at a temperature of 220° C. and a pressure of 2 t using a hydraulic 10 t press (Werner & Pfleiderer). For this purpose, the granulate is filled into the compression mould and this is transferred into the already preheated press. At a pressure of 0.5 t, the granulate is firstly melted for 60 s. After expiry of the melt time, the pressure is increased to 2 t and kept constant for a further 3 min. Whilst maintaining the compression pressure, the mould is cooled to 60° C. and thereafter the test pieces are removed. The test pieces have, according to the standard, the following dimensions: 125×12.5×1.5 mm.
The examples according to the invention and comparative examples contained in Table 1 were tested according to DIN EN 60695-11-10 and the burning times and classification according to the standard were obtained.
Surprisingly, the examples according to the invention have significantly curtailed burning times relative to the comparative examples at the same concentration.
Analogously to examples 1-35 according to the invention, a thermoplastic polyurethane (Elastollan 1185A of the company BASF SE) was processed with 8% diethylaluminium phosphinate and 4% of compound 3 at 190° C. and compressed at 200° C. to form test pieces. The classification V-2 with a total burning duration (4 test pieces) of 1.3 seconds was obtained.
Analogously to examples 1-35, films made of polypropylene (Sabic 575 P) were produced and tested by means of the standard DIN 4102 B2, the results compiled in table 3 are obtained:
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2013 005 307.2 | Mar 2013 | DE | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2014/055847 | 3/24/2014 | WO | 00 |