Patent Application
20210394126
Natural gas reforming remains the global method of choice for hydrogen production, with no significant changes expected in the near future. In hydrogen production processes, syngas, which is typically formed as an intermediate step, reacts with water vapors via the water gas shift reaction to produce “raw” hydrogen (60-80% H2, 20-40% CO2, and small amounts of impurities). It is difficult for the “raw” H2 product to meet the demands for high purity (e.g., for fuel cell technology which demands purity levels of 99.9%)). Accordingly, hydrogen purification is essential for obtaining high quality hydrogen fuel.
Membrane technology exhibits inherent advantages over existing separation technologies. Among different type of membranes, reverse selective or “CO2 selective” membranes, in which larger gas (CO2) permeates faster than smaller gas (H2), are more desirable for obtaining fuel cell quality hydrogen, since these membranes can more easily meet requirements for high purity as compared to H2-selective membranes. While strong progress has been made in H2-selective MOF membranes, reports of CO2-selective membranes are scarce. To the best of Applicant's knowledge, only two MOFs have been reported for potential use in hydrogen purification via membrane separation: a single crystal [Cu2(bza)4(pyz)]n membrane and a zeolite-like MOF membrane, anionic sod-ZMOF, which was developed by Applicant and exhibited preferential permeation of CO2 over H2 in a mixture. However, reported performances of MOF membranes remain lower than the performance of benchmark materials. Thus, MOFs are not considered to be potential materials for CO2/H2 separation applications.
Conventional separation of butane isomers via cryogenic distillation is environmentally damaging and energy intensive. Membrane-based separation, in turn, is an order of magnitude more energy efficient. However, for now, such separation is challenging and cannot meet requirements for practical applications due to limitations in material performance and material integration Mainly two classes of materials have been studied for such applications: polymers and zeolites. Rubbery polymers have generally low selectivity and high butane and isobutane permeability due to the high solubility of this molecules. The solubility, however, decreases as the polymer is plasticized, making them economically unattractive. Glassy polymers similarly are not applicable due to low butane permeability. While well-defined structure of zeolites offer control over diffusion and sorption of isobutane isomers, processability of zeolites as membranes remains an issue. Similarly to zeolites, MOF has a great potential to be used as a membranes for butane isomer separation. However, only ZIF-90 pure membrane has been reported in the literature for this application.
Methods of fabricating thin film membranes based on zeolite-like metal-organic frameworks with an ana topology (ana-ZMOF), methods of separating chemical species from fluid compositions using said membranes, and the like are disclosed herein. It has been discovered that, through the addition of polyvinylpyrrolidone to the reaction mixture, the challenges associated with pure crystal intergrowth can be overcome and zeolite-like metal-organic frameworks with an ana topology can be formed as continuous defect-free thin film membranes. The fabrication methods include a two-step procedure, the steps involving (1) in-situ modification of a support with ana-ZMOF crystal precursors and (2) subsequent crystal intergrowth to form a continuous defect-free ana-ZMOF thin film intergrown on the modified support. The resulting membranes have unique intrinsic properties suitable for use in a wide variety of separation processes, including, but not limited to, those involving carbon dioxide and hydrogen, butane isomers separation, and the like.
Accordingly, embodiments of the present disclosure describe methods of fabricating an ana-ZMOF thin film membrane comprising (1) modifying a substrate with ana-ZMOF crystal precursors in the presence of polyvinylpyrrolidone, and (2) intergrowing the ana-ZMOF crystal precursors in the presence of polyvinylpyrrolidone to form a continuous defect-free ana-ZMOF thin film intergrown on the substrate.
In certain embodiments, the method of fabricating a membrane with a thin film of a zeolite-like metal-organic framework with an ana topology can comprise one or more of the following steps: adding polyvinylpyrrolidone to a solution containing ana-ZMOF precursors and optionally one or more solvents to prepare a first precursor solution; immersing a substrate in the first precursor solution and heating the first precursor solution while the substrate is immersed therein to a first temperature to obtain a modified substrate; optionally drying the modified substrate; adding polyvinylpyrrolidone to a solution containing ana-ZMOF precursors and optionally one or more solvents to prepare a second precursor solution; immersing the dried modified substrate in the second precursor solution and heating the second precursor solution while the dried modified substrate is immersed therein to a second temperature to form an ana-ZMOF thin film membrane.
In an embodiment, the first precursor solution is sonicated prior to immersing the substrate in the first precursor solution. In an embodiment, the second precursor solution is sonicated and heated prior to immersing the dried modified substrate in the second precursor solution. In an embodiment, the ana-ZMOF precursors and one or more solvents are the same in the first precursor solution and the second precursor solution. In an embodiment, a concentration of each of the ana-ZMOF precursors in the first solution is less than their concentration in the second solution. In an embodiment, the ana-ZMOF precursors include a rare earth metal precursor, a ligand precursor, and an alkali metal precursor or an alkaline metal precursor. In an embodiment, the rare-earth metal precursors include a rare earth element selected form the group consisting of cerium, dysprosium, erbium, europium, gadolinium, holmium, lanthanum, lutetium, neodymium, praseodymium, promethium, samarium, scandium, terbium, thulium, ytterbium, yttrium, and any combination thereof. In an embodiment, the ligand precursor is selected from the group consisting of 4,5-imidazole dicarboxylic acid (ImDC); 1H-Imidazole-2-carboxylic acid; 2,7-diaza-antracene-1,8-dicarboxylic acid; pyrimidine-4,6-dicarboxcylic acid; pyridine-2,5-dicarboxylic acid; 2,7-diaza-anthracene-3,6-dicarboxylic acid; benzene-1,2,4,5,tetracarboxylic acid; naphthalene-2,3,6,7-tetracarboxylic acid; anthracene-2,3,6,7-tetracarboxylic acid; and any combination thereof. In an embodiment, the alkali metal precursor includes an alkali metal selected from the group consisting of lithium, sodium, potassium, rubidium, cesium, francium, and any combination thereof. In an embodiment, the alkaline metal precursor includes an alkaline metal selected from the group consisting of beryllium, magnesium, calcium, strontium, barium, radium, and any combination thereof. In an embodiment, the one or more solvents are selected form the group consisting of water; N,N-dimethyl formamide (DMF); ethanol; 4,4;-trimethylene-dipiperidine; 1,2-diaminocyclohexane; and any combination thereof. In an embodiment, the modified substrate is a substrate that has been modified with ana-ZMOF crystal precursors. In an embodiment, the second temperature is less than the first temperature. In an embodiment, the continuous ana-ZMOF thin film membrane comprises a continuous thin film of ana-ZMOF inter-grown on the modified substrate. In an embodiment, the method further comprises activating the ana-ZMOF thin film membrane by exchanging solvent present in the ana-ZMOF thin film membrane with another solvent and/or subjecting the ana-ZMOF thin film membrane to a vacuum to activate the ana-ZMOF thin film membrane.
Embodiments of the present disclosure also describe a membrane comprising a thin film of a continuous zeolite-like metal-organic framework having an ana topology (ana-ZMOF) intergrown on a modified substrate, wherein the ana-ZMOF thin film membrane has a pore window size of about 4.1 Å and exhibits a selectivity for CO2 over H2 and/or n-butane over iso-butane.
Embodiments of the present disclosure further describe a method of separating chemical species comprising contacting an ana-ZMOF thin film membrane with a fluid composition containing at least CO2 and H2; and separating CO2 from H2. In an embodiment, the H2 is substantially excluded from the ana-ZMOF thin film membrane.
Embodiments of the present disclosure further describe a method of separating chemical species comprising contacting an ana-ZMOF thin film membrane with a fluid composition containing at least n-butane and iso-butane; and separating n-butane from iso-butane. In an embodiment, the iso-butane is substantially excluded from the ana-ZMOF thin film membrane.
The details of one or more examples are set forth in the description below. Other features, objects, and advantages will be apparent from the description and from the claims.
This written disclosure describes illustrative embodiments that are non-limiting and non-exhaustive. In the drawings, which are not necessarily drawn to scale, like numerals describe substantially similar components throughout the several views. Like numerals having different letter suffixes represent different instances of substantially similar components. The drawings illustrate generally, by way of example, but not by way of limitation, various embodiments discussed in the present document.
Reference is made to illustrative embodiments that are depicted in the figures, in which:
Embodiments of the present disclosure describe methods of fabricating thin film membranes comprising a continuous, defect-free thin film of a zeolite-like metal-organic framework with an ana topology (ana-ZMOF(s)) supported on a modified substrate. The methods described herein reflect an optimization of reaction conditions and proceed in two stages: (1) in the first stage the substrate is modified in-situ with an ana-ZMOF crystal precursors and (2) in the second stage a continuous, a defect-free ana-ZMOF thin film is intergrown on the modified substrate. Each of the first stage and the second stage typically proceed in the presence of polyvinylpyrrolidone. Surprisingly, the fabrication of thin film membranes in this way not only overcame the challenges associated with scale-up and pure crystal intergrowth, but also produced continuous, defect-free thin films of ana-ZMOFs, with intrinsic properties suitable for achieving highly challenging separations.
Accordingly, embodiments of the present disclosure further describe methods of hydrogen purification and butane isomers separations. For example, in one embodiment, the ana-ZMOF thin film membranes can be used in sorption-driven CO2/H2 separations. In another embodiment, the ana-ZMOF thin film membranes can be used in size-driven n-butane/iso-butane separations. The ana-ZMOF thin film membranes' preferential permeation of CO2 over H2 and of C4 over i-C4 outperform conventional microporous inorganic and polymer membranes. The ana-ZMOF thin film membranes are also among the most selective membranes for CO2/H2 and C4/i-C4 separations, with a CO2/H2 selectivity and C4/i-C4 selectivity of greater than 88 and 80, respectively.
At step 201, polyvinylpyrrolidone can be added to a solution containing ana-ZMOF precursors and optionally one or more solvents to prepare or form a first precursor solution. The first precursor solution can contain one or more of ana-ZMOF precursors, polyvinylpyrrolidone, and one or more solvents. To prepare the first precursor solution, one or more of the ana-ZMOF precursors, polyvinylpyrrolidone, and one or more solvents can be contacted (e.g., combined or placed) in, or added to, a reaction vessel. Upon being contacted or during the contacting, the ana-ZMOF precursors, polyvinylpyrrolidone, and/or one or more solvents can be dispersed or mixed by any suitable means. For example, in an embodiment, the first precursor solution can be sonicated to disperse the ana-ZMOF precursors or polyvinylpyrrolidone, or both, in the one or more solvents of the first precursor solution. Among other things, the sonicating can be used to prevent the formation of aggregates or agglomerates, or both, in the first precursor solution. While sonicating is a suitable technique for the methods described herein, other techniques can be used herein for dispersing, such as agitating, mixing, stirring, etc.
The ana-ZMOF precursors can include rare earth metal precursors. The rare earth metal precursors can include a rare earth element. For example, the rare earth metal precursors can include a rare earth element selected from the group consisting of cerium, dysprosium, erbium, europium, gadolinium, holmium, lanthanum, lutetium, neodymium, praseodymium, promethium, samarium, scandium, terbium, thulium, ytterbium, yttrium, and any combination thereof. The rare earth metal precursors can be present as salts of the rare earth elements. For example, the rare earth metal precursors can include trivalent cations of rare earth elements paired with trivalent anions. The rare earth metal precursors are typically hydrated, but they can also be anhydrides or anhydrous. The rare earth metal precursors are not particularly limited. Other forms and types of rare earth metal precursors will be readily appreciated by a skilled person.
The ana-ZMOF precursors can further include ligand precursors. The ligand precursors can include heterofunctional polytopic ligands. For example, the ligand precursors can ditopic or tetratopic ligands including carboxylate moieties and optionally one or more nitrogen heteroatoms. Examples of suitable ligand precursors include, but are not limited to, 4,5-imidazole dicarboxylic acid (ImDC); 1H-Imidazole-2-carboxylic acid; 2,7-diaza-antracene-1,8-dicarboxylic acid; pyrimidine-4,6-dicarboxcylic acid; pyridine-2,5-dicarboxylic acid; 2,7-diaza-anthracene-3,6-dicarboxylic acid; benzene-1,2,4,5,tetracarboxylic acid; naphthalene-2,3,6,7-tetracarboxylic acid; anthracene-2,3,6,7-tetracarboxylic acid; or any combination thereof.
The ana-ZMOF precursors can further optionally comprise alkali metal precursors or alkaline metal precursors, or both alkali and alkaline metal precursors. The alkali metal precursors can be selected from the group consisting of lithium, sodium, potassium, rubidium, cesium, francium, and any combination thereof. The alkaline metal precursors can be selected form the group consisting of beryllium, magnesium, calcium, strontium, barium, radium, and any combination thereof.
The one or more solvents can be selected form the group consisting of water; N,N-dimethyl formamide (DMF); ethanol; 4,4;-trimethylene-dipiperidine; 1,2-diaminocyclohexane; and any combination thereof.
The in-situ modification of a substrate can be performed in one or both of the steps 202 and 203, among others. In those steps, a substrate can be immersed in the first precursor solution, and the first precursor solution can be heated while the substrate is immersed therein to a first temperature to obtain a modified substrate, or a substrate modified with ana-ZMOF crystal precursors. The substrate is typically completely immersed in the first precursor solution, although it can be partially immersed without departing from the scope of the invention of the present disclosure. One example of a suitable substrate that can be used herein is an alumina substrate, such as an α-Al2O3 substrate. Other substrates known in the art can be used herein. The heating can proceed to the first temperature or it can proceed at the first temperature, optionally while stirring the first precursor solution. The first temperature and duration of the heating are typically selected to promote the formation of ana-ZMOF crystal precursors on the substrate.
In an embodiment, the first temperature can range from about 80° C. to about 180° C., or any range there within. For example, the first temperature can be about 80° C., about 85° C., about 90° C., about 95° C., about 100° C., about 105° C., about 110° C., about 115° C., about 120° C., about 125° C., about 130° C., about 135° C., about 140° C., about 145° C., about 150° C., about 155° C., about 160° C., about 165° C., about 170° C., or about 180° C. In an embodiment, the duration of the heating can range from about 30 min to about 5 h, or any range there within. For example, the duration of the heating can be about 30 min, about 1 h, about 1.5 h, about 2 h, about 2.5 h, about 3 h, about 3.5 h, about 4 h, about 4.5 h, or about 5. In one embodiment, the first precursor solution can be heated in an oil bath with stirring, while the substrate is immersed therein, to about 140° C. for about 1 hour.
The modified substrate is optionally dried in step 204. For example, the modified substrate can be removed from the first precursor solution and allowed to dry. The manner in which the modified substrate is allowed to dry is not particularly limited. Any technique suitable for drying the modified substrate may be used herein. In an embodiment, the modified substrate can be dried by removing it from the first precursor solution and allowing the modified substrate to dry in air.
At step 205, polyvinylpyrrolidone can be added to a solution containing ana-ZMOF precursors and optionally one or more solvents to prepare or form a second precursor solution. The second precursor solution can contain one or more of the ana-ZMOF precursors, polyvinylpyrrolidone, and one or more solvents. For example, in some embodiments, the step 205 includes adding polyvinylpyrrolidone to a second precursor solution containing ana-ZMOF precursors. To prepare the second precursor solution, one or more of the ana-ZMOF precursors, polyvinylpyrrolidone, and one or more solvents can be contacted (e.g., combined or placed) in, or added to, a reaction vessel. Upon being contacted or during the contacting, the ana-ZMOF precursors, polyvinylpyrrolidone, and/or one or more solvents can be dispersed or mixed by any suitable means. For example, in an embodiment, the second precursor solution can be sonicated to disperse the ana-ZMOF precursors or polyvinylpyrrolidone, or both, in the one or more solvents of the second precursor solution. After the dispersing or mixing, the second precursor solution can be heated, while optionally stirring, to or at a third temperature. The third temperature can be the same as the first temperature or it can be a different temperature. The heating typically proceeds until the second precursor solution is visibly clear or until the ana-ZMOF precursors and polyvinylpyrrolidone are dissolved in the one or more solvents.
In an embodiment, the third temperature can range from about 80° C. to about 180° C., or any range there within. For example, the third temperature can be about 80° C., about 85° C., about 90° C., about 95° C., about 100° C., about 105° C., about 110° C., about 115° C., about 120° C., about 125° C., about 130° C., about 135° C., about 140° C., about 145° C., about 150° C., about 155° C., about 160° C., about 165° C., about 170° C., or about 180° C. In an embodiment, the duration of the heating can range from about 30 min to about 5 h, or any range there within. For example, the duration of the heating can be about 30 min, about 1 h, about 1.5 h, about 2 h, about 2.5 h, about 3 h, about 3.5 h, about 4 h, about 4.5 h, or about 5. In one embodiment, the second precursor solution can be heated with stirring to about 140° C. for about 1 hour.
In one or more aspects of the invention, the first precursor solution and the second precursor solution each include the same precursor species, wherein the precursor species are selected from the group consisting of the ana-ZMOF precursors, polyvinylpyrrolidone, solvents, and combinations thereof. For example, in an embodiment, the first precursor solution and the second precursor solution each include the same precursor species, wherein the precursors species are selected from the group consisting of rare earth metal precursors, ligand precursors, alkali metal precursors, alkaline metal precursors, solvents, and combinations thereof. In another aspect of the invention, the first precursor solution and the second precursor solution include at least one different precursor species, wherein the precursor species are selected from the group consisting of the ana-ZMOF precursors, polyvinylpyrrolidone, solvents, and combinations thereof. For example, in an embodiment, the first precursor solution and the second precursor solution include at least one different precursor species selected from the group consisting of rare earth metal precursors, ligand precursors, alkali metal precursors, alkaline metal precursors, solvents, and combinations thereof.
In one or more aspects of the invention, the concentration or amount (e.g., mass, volume, etc.) of the precursor species in the first precursor solution and the second precursor solution are different. For example, in an embodiment, the concentration or amount of one or more of the rare earth metal precursors, ligand precursors, alkali metal precursors, alkaline metal precursors, and solvents in the first precursor solution is different from the second precursor solution. The second precursor solution can typically include a greater concentration or amount of precursor species than the first precursor solution, but other variations can be used without departing from the scope of the invention of the present disclosure. In another aspect of the invention, the concentration or amount of the precursor species in the first precursor solution and the second precursor solution are the same. For example, in an embodiment, the concentration or amount of the rare earth metal precursors, ligand precursors, alkali metal precursors, alkaline metal precursors, and solvents in the first precursor solution and the second precursor solution are the same.
The ana-ZMOF thin film membrane can be formed in one or both of the steps 206 and 207, among others. In those steps, the dried modified substrate can be immersed in the second precursor solution, and the second precursor solution can be heated while the dried modified substrate is immersed therein to a second temperature. The dried modified substrate is typically completely immersed in the second precursor solution, although it can be partially immersed without departing from the scope of the invention of the present disclosure. The heating can proceed to the second temperature or it can proceed at the second temperature, usually without stirring, but optionally with stirring. The second temperature and duration of the heating should be sufficient to achieve growth or intergrowth of the ana-ZMOF thin film on the substrate. Following the heating, the reaction vessel containing the second precursor solution and thin film membrane can be allowed to cool to about room temperature. The thin film membrane can then be washed one or more times with, for example, DMF or ethanol, or both DMF and ethanol.
In an embodiment, the second temperature can range from about 50° C. to about 150° C., or any range there within. For example, the third temperature can be about 50° C., about 55° C., about 60° C., about 65° C., about 70° C., about 75° C., about 80° C., about 85° C., about 90° C., about 95° C., about 100° C., about 105° C., about 110° C., about 115° C., about 120° C., about 125° C., about 130° C., about 135° C., about 140° C., about 145° C., or about 150° C. In an embodiment, the duration of the heating can range from about 1 day to about 10 days, or any range therewith. For example, the duration of the heating can be about 1 day, about 2 days, about 3 days, about 4 days, about 5 days, about 6 days, about 7 days, about 8 days, about 9 days, or about 10 days. In one embodiment, the second precursor solution can be heated in an oven while the dried modified substrate is immersed therein to about 130° C. for about 3 days.
The ana-ZMOF thin film membrane can optionally be activated in step 208 (not shown). For example, in an embodiment, the ana-ZMOF thin film membrane can be activated by solvent exchange, drying the solvent-exchanged membrane, subjecting the dried solvent-exchanged membrane to vacuum or inert flow (e.g., helium), or any combination thereof. The solvent for solvent exchange can depend on the solvents used for the fabrication of the ana-ZMOF thin film membrane. A skilled person can readily select solvents suitable for solvent exchange, as well as inert gases suitable for activating the ana-ZMOF thin film membrane.
In an embodiment, the method of fabricating an ana-ZMOF thin film membrane comprises preparing a first solution containing Y(NO3)3.6H2O, 4,5-imidazoledicarboxylic acid, and KCl in water and DMF; immersing an alumina substrate in the first precursor solution and heating the first precursor solution while the alumina substrate is immersed therein to about 140° C. to obtain a modified substrate; drying the modified substrate; preparing a second precursor solution containing Y(NO3)3.6H2O, 4,5-imidazoledicarboxylic acid, and KCl in water and DMF; and immersed the dried modified substrate in the second precursor solution and heating the second precursor solution while the dried modified substrate is immersed therein to about 130° C. to form an ana-ZMOF thin film membrane.
Embodiments of the present disclosure further describe ana-ZMOF thin film membranes, such as the ana-ZMOF thin film membranes fabricated according to the methods of the present disclosure. The ana-ZMOF thin film membranes can comprise a continuous, defect-free thin film of an ana-ZMOF intergrown or supported on a substrate or a modified substrate. In an embodiment, the ana-ZMOF thin films exhibit a pore window size of about 4.1 Å. In an embodiment, the ana-ZMOF thin films exhibit a CO2/H2 selectivity of 88 or greater. In an embodiment, the ana-ZMOF thin films exhibit a C4/i-C4 selectivity of 80 or greater. In an embodiment, the ana-ZMOF thin film membranes exhibit a heat of adsorption for CO2 of about 40 kJ/mol. The ana-ZMOF thin film membranes can be used for sorption-driven CO2/H2 separations and/or for size-driven n-butane/iso-butane separations.
The ana-ZMOF thin film membrane is contacted with a fluid composition in step 301. The contacting can proceed by bringing the ana-ZMOF thin film membrane and fluid composition into physical contact, or immediate or close proximity. The contacting can proceed under any of a variety of conditions, depending on, for example, the source of the fluid composition. For example, in an embodiment, the contacting can proceed at a temperature ranging from about 20° C. to about 35° C. The fluid composition can be provided in any phase, such as a gas/vapor phase, liquid phase, or a combination thereof. The fluid composition typically includes at least CO2 and H2, but it can optionally include other species and impurities. For example, in an embodiment, the fluid composition can include hydrogen, carbon dioxide, and impurities and/or byproducts resulting from a water gas shift reaction between syngas and water vapor.
The CO2 is separated from H2 in step 302. The separation can proceed as a sorption-driven separation using the ana-ZMOF thin film membrane as a reverse-selective membrane in which the CO2 sorbs onto the membrane or its pores and/or permeates through the membrane to the exclusion or substantial exclusion of H2. The hydrogen recovered from the separation can be highly purified. For example, in an embodiment, the hydrogen can be recovered at 99.9% purity or greater, such as about 99.9% purity, 99.95% purity, 99.97% purity, 99.995% purity, 99.999% purity, or greater. Lower purity levels of hydrogen can also be achieved, such as 80% purity or greater, without departing from the scope of the invention of the present disclosure.
The ana-ZMOF thin film membrane is contacted with the fluid composition in step 401. The contacting can proceed by bringing the ana-ZMOF thin film membrane and fluid composition into physical contact, or immediate or close proximity. The contacting can proceed under any of a variety of conditions, depending on, for example, the source of the fluid composition. For example, in an embodiment, the contacting can proceed at a temperature ranging from about 20° C. to about 200° C. The fluid composition can be provided in any phase, such as a gas/vapor phase, liquid phase, or a combination thereof. The fluid composition typically includes a mixture of butane isomers, such as n-butane and iso-butane, but it can optionally include other species and impurities.
The n-butane is separated from iso-butane in step 402. The separation can proceed as a size-drive separation using the ana-ZMOF thin film membrane as a molecular sieve in which the n-butane permeates through the membrane to the exclusion or substantial exclusion of iso-butane. In other words, the ana-ZMOF thin film membrane can kinetically separate the n-butane from the iso-butane based on size. The butane recovered from the separation can be highly purified. For example, the butane can be recovered at 99% purity or greater, such as about 99.9% purity, 99.95% purity, 99.97% purity, 99.995% purity, 99.999% purity, or greater.
The following Examples are intended to illustrate the above invention and should not be construed as to narrow its scope. One skilled in the art will readily recognize that the Examiners suggest many other ways in which the invention could be practiced. It should be understand that numerous variations and modifications may be made while remaining within the scope of the invention.
The present Example describes a novel methodology for fabricating a continuous, defect-free ana-ZMOF membrane with unique intrinsic properties suitable for achieving highly challenging separations, such as CO2/H2 separations and separations of butane isomers, such as n-C4/i-C4 separations, among others. The ana-ZMOF membranes favorably exhibited a high affinity for CO2 and a small aperture size. The pore window size of the ana-ZMOF was one to three times bigger than a CO2 molecule and thus limited the diffusion of hydrogen. In particular, the pore window size estimated from the crystallography to be around 4.1 Å (
The ana-ZMOF membranes described herein address the problem of advancing materials for membranes used in CO2/H2 and C4/i-C4 separations. The unique property of ana-ZMOF sorption-driven CO2/H2 separation and size-driven C4/i-C4 separation reduced the surface modules of the membrane by using a highly CO2 selective membrane and butane selective membrane. The addition of polyvinylpyrrolidone in the fabrication of the ana-ZMOF membranes was a breakthrough that addressed the problems of membrane scale-up, among other things. The measured CO2/H2 and nC4/iC4 selectivity for this pure ana-ZMOF membrane was over 88 and 80, respectively, which makes the ana-ZMOF membranes one of the most selective membranes for CO2/H2 and butane isomers separation. Therefore the nC4/iC4 selectivity observed in these fabricated ana-ZMOF membrane was much higher than the reported polymeric membranes and other mixed-matrix materials (MMMs). These MOF membranes combine easy-fabrication with high-performance for practical applications of CO2/H2 and butane isomers separations.
The methodology described herein overcame numerous challenges associated with pure crystal intergrowth and conventional fabrication techniques. As described herein, pure crystal intergrowth was achieved by the addition of polyvinylpyrrolidone to the reaction mixture and a novel two-step synthetic procedure was optimized. The ana-ZMOF was fabricated as a thin film on alumina support using this newly developed two-step procedure. In the first step, the fabrication proceeded with the in-situ modification of the support with the ana-ZMOF crystal precursors. In a typical procedure, a stirrer bar and 20 mm in diameter α-Al2O3 substrate were placed on a bottom of a 60 mL scintillation vial (without contact), then a well-dispersed by sonication reaction mixture containing Y(NO3)3.6H2O (about 0.05 mmol, about 19.2 mg), 4,5-imidazoledicarboxylic acid (about 0.1 mmol, about 15.6 mg), KCl (about 0.05 mmol, about 3.7 mg), Polyvinylpyrrolidone (about 0.5 mL 20 wt % solution in DMF), water (about 0.1 mL), DMF (about 6 mL) was added. The vial was sealed with aluminium foil and cup. The vial was then placed in an oil bath and heated with stirring to about 140° C. for about 1 hour. After one-hour, the hot vial was opened and substrate was quickly removed and dried in air under the fume hood. In the second step, the well-dispersed by sonication reaction mixture containing Y(NO3)3.6H2O (about 0.2 mmol, about 76.8 mg), 4,5-imidazoledicarboxylic acid (about 0.4 mmol, about 62.4 mg), KCl (about 0.2 mmol, about 14.8 mg), Polyvinylpyrrolidone (about 0.5 mL 20 wt % solution in DMF), water (about 0.2 mL), and DMF (about 7 mL) was placed in an oil bath and heated with stirring to about 140° C. until the solution became clear. After about 20 min, when all reagents had dissolved, the stirrer bar was removed and the dried modified α-Al2O3 substrate from the first step was placed inside the vial, which was then sealed with aluminium foil and cap. The reaction mixture was placed in about 130° C. oven. After 5 days, the vial was allowed to cool down to about room temperature and the substrate was removed and washed with DMF and ethanol. For membrane activation, the remaining DMF in membrane was exchanged with ethanol, by placing the membrane in fresh solvent 2-3 times a day for 3 days. The solvent-exchanged membrane was dried in air at room temperature, and further activation was carried out in a permeation cell with vacuum or helium flow. The SEM images of a typical ana-ZMOF membrane are depicted in
The separation performance of the prepared ana-ZMOF membrane was assessed by permeations of pure and mixture gases of CO2, H2 and n-butane and iso-butane under about 1.4 bar at about 35° C.
Other embodiments of the present disclosure are possible. Although the description above contains much specificity, these should not be construed as limiting the scope of the disclosure, but as merely providing illustrations of some of the presently preferred embodiments of this disclosure. It is also contemplated that various combinations or sub-combinations of the specific features and aspects of the embodiments may be made and still fall within the scope of this disclosure. It should be understood that various features and aspects of the disclosed embodiments can be combined with or substituted for one another in order to form various embodiments. Thus, it is intended that the scope of at least some of the present disclosure should not be limited by the particular disclosed embodiments described above.
Thus the scope of this disclosure should be determined by the appended claims and their legal equivalents. Therefore, it will be appreciated that the scope of the present disclosure fully encompasses other embodiments which may become obvious to those skilled in the art, and that the scope of the present disclosure is accordingly to be limited by nothing other than the appended claims, in which reference to an element in the singular is not intended to mean “one and only one” unless explicitly so stated, but rather “one or more.” All structural, chemical, and functional equivalents to the elements of the above-described preferred embodiment that are known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the present claims. Moreover, it is not necessary for a device or method to address each and every problem sought to be solved by the present disclosure, for it to be encompassed by the present claims. Furthermore, no element, component, or method step in the present disclosure is intended to be dedicated to the public regardless of whether the element, component, or method step is explicitly recited in the claims.
The foregoing description of various preferred embodiments of the disclosure have been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the disclosure to the precise embodiments, and obviously many modifications and variations are possible in light of the above teaching. The example embodiments, as described above, were chosen and described in order to best explain the principles of the disclosure and its practical application to thereby enable others skilled in the art to best utilize the disclosure in various embodiments and with various modifications as are suited to the particular use contemplated. It is intended that the scope of the disclosure be defined by the claims appended hereto
Various examples have been described. These and other examples are within the scope of the following claims.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2019/058297 | 9/30/2019 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62739423 | Oct 2018 | US | |
| 62905976 | Sep 2019 | US |