Use of titania or zirconia in the preparation of tertiary butyl alcohol from tertiary butyl hydroperoxide

Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to the catalytic decomposition of tertiary butyl hydroperoxide (TBHP). More particularly, this invention relates to a method for the preparation of tertiary butyl alcohol (TBA) by the catalytic decomposition of tertiary butyl hydroperoxide. Still more particularly, this invention relates to a method wherein titania or zirconia is used to catalyze the substantially selective decomposition of tertiary butyl hydroperoxide to tertiary butyl alcohol.
2. Prior Art
It is known to react isobutane with oxygen, either thermally or catalytically, to form a peroxidation reaction product wherein the principal peroxide that is formed is tertiary butyl hydroperoxide. It is also known to thermally or catalytically decompose the tertiary butyl hydroperoxide to form tertiary butyl alcohol.
In the text entitled "Organic Peroxides" edited by Daniel Swern (Wiley Interscience, a Division of John Wiley & Sons, New York), in Vol. II on page 157 it is stated that the metal-ion-catalyzed decomposition of primary hydroperoxides yields mainly alcohols, aldehydes and carboxylic acids, citing as an example the decomposition of hydroxymethyl hydroperoxide with aqueous ferrous sulfate to provide formaldehyde, formic acid and water.
Quin U.S. Pat. No. 2,854,487 discloses the hydrogenation of hydrocarbon peroxides in the presence of hydrogen and palladium on activated alumina to provide carbinols.
In Massie U.S. Pat. No. 3,775,472 a process is disclosed wherein alkyl substituted aromatic hydrocarbons are oxidized to products such as aromatic alcohols, aldehydes and carboxylic acids in the presence of ruthenium compounds.
Grane U.S. Pat. No. 3,474,151 discloses that tertiary butyl alcohol starts to dehydrate at 450.degree. F. and to decompose at a "rapid rate" at temperatures above 475.degree. F. Grane discovered, however, that residual quantities of hydroperoxide contaminants present in tertiary butyl alcohol could be thermally decomposed by heating the contaminated tertiary butyl alcohol at a temperature of 375.degree. to 475.degree. F. for about 1 to 10 minutes.
Grane et al. U.S. Pat. No. 4,294,999 discloses a process wherein isobutane is oxidized in a pressured reactor in the presence of a solubilized molybdenum catalyst to provide a mixture of tertiary butyl alcohol, tertiary butyl hydroperoxide, methanol, acetone, and other oxygen-containing compounds. The tertiary butyl hydroperoxide is thermally decomposed under pressure at about 280.degree. F. to provide a tertiary butyl alcohol product containing only residual quantities of tertiary butyl hydroperoxide which are then decomposed in accordance with Grane U.S. Pat. No. 3,474,151 by heating the tertiary butyl alcohol at 375.degree. to 475.degree. for about 1 to 10 minutes. Heating tertiary butyl alcohol containing small amounts of peroxides at high temperatures for even short periods of time to remove the peroxides produces undesirable products such as isobutylene.
Grane et al. U.S. Pat. No. 4,296,262 discloses a related process wherein isobutane is reacted with oxygen in a reaction zone for a residence time of about 1 to 10 hours at a temperature of about 240.degree. to about 340.degree. F. and a pressure of about 100 to about 1000 psig. in the presence of a catalytically effective amount of a soluble molybdenum catalyst. A liquid stream comprising tertiary butyl alcohol is recovered from the reaction mixture and fed to a decomposition zone wherein the tertiary butyl hydroperoxide contained therein is decomposed by "hot aging" at 250.degree.-350.degree. F. at a pressure lower than the pressure in the oxidation zone. The tertiary butyl alcohol can be further subjected to a clean-up treatment at 375.degree.-475.degree. F. for 1 to 10 minutes. Worrell et al. in U.S. Pat. No. 4,296,263 disclose a related process wherein the feedstock is a mixture of normal butane with isobutane and wherein the oxidation catalyst is a soluble form of chromium, cobalt, nickel, manganese, molybdenum, or a mixture thereof.
In U.S. Pat. No. 3,505,360, Allison et al. disclose a method wherein an alkenyl hydroperoxide is decomposed in the presence of a catalyst based on a compound of a Group IV-A, V-A or VI-A metal. Taylor et al., in U.S. Pat. No. 4,508,923 disclose the use of a catalyst system comprising ruthenium and chromium for decomposing organic hydroperoxides. The use of a cobalt borate catalyst for the decomposition of hydroperoxides is disclosed in Sanderson et al. U.S. Pat. No. 4,547,598.
Taylor et al. U.S. Pat. No. 4,551,553 is directed to a process for the formation of alcohols such as tertiary butyl alcohol by the catalytic decomposition of an organic hydroperoxide such as tertiary butyl hydroperoxide using a binary catalyst composed of a mixture of a ruthenium compound with a chromium compound. It is stated that the use of the binary catalyst eliminates the need for stabilizing ligands.
Sanderson et al. disclose the use of a variety of catalysts for the decomposition of tertiary butyl hydroperoxide in a series of U.S. patents, including a catalyst composed of unsupported nickel, copper, chromia and iron (U.S. Pat. No. 4,704,482), a catalyst composed of iron, copper, chromia and cobalt (U.S. Pat. No. 4,705,903), a catalyst composed of a base treated hydrogenation catalyst from groups VIB or VIIIB of the Periodic Table (U.S. Pat. No. 4,742,179), a catalyst consisting essentially of nickel, copper, chromium and barium (U.S. Pat. No. 4,873,380), a catalyst composed of a metal phthalocyanine promoted with a rhenium compound (U.S. Pat. No. 4,910,349), a catalyst composed of a base promoted metal phthalocyanine compound (U.S. Pat. No. 4,912,269), a catalyst composed of a soluble ruthenium compound promoted with a bidentate ligand (U.S. Pat. No. 4,912,033), a catalyst composed of a metal porphine such as iron (III) or manganese (III) promoted with an alkyl thiol or an amine, a catalyst composed of an imidazole promoted metal phthalocyanine compound (U.S. Pat. No. 4,912,266), (U.S. Pat. No. 4,922,034), a catalyst composed of a metal phthalocyanine promoted with a thiol and a free radical inhibitor (U.S. Pat. No. 4,922,035), a catalyst composed of a borate promoted metal phthalocyanine (U.S. Pat. No. 4,922,036), or a catalyst composed of a soluble ruthenium compound and an iron compound such as an acetate, a borate, a bromide, a chloride, a 1,3-propanedionate, a 2-ethyl-hexanoate, an iodide, a nitrate, a 2,4-pentanedionate, a perchlorate or a sulfate (U.S. Pat. No. 5,025,113).
BACKGROUND INFORMATION
When isobutane is reacted with molecular oxygen, the principal products of the reaction are tertiary butyl alcohol and tertiary butyl hydroperoxide. However, minor amounts of other contaminants are also formed.
In addition, a minor amount of water will be formed, which will normally amount to about 0.5 to 1 wt. % of the reactor effluent. The amount of byproduct water that is produced is a function of the severity of the reaction conditions employed and will tend to increase as the severity of the reaction conditions is increased.
As indicated, tertiary butyl hydroperoxide is useful as a raw material for the manufacture of tertiary butyl alcohol. The tertiary butyl alcohol can be formed by catalytic decomposition of the tertiary butyl hydroperoxide. In the Williams et al. process disclosed in U.S. Pat. No. 3,472,876, an oxygen-containing gas was charged to a reactor containing isobutane and an oxidation catalyst to provide a reaction mixture comprising tertiary butyl alcohol, tertiary butyl hydroperoxide, acetone, and tertiary butyl ether. The reported results in the patent indicate that there was a comparatively low rate of conversion and a comparatively poor selectivity of the reaction to tertiary butyl alcohol.
SUMMARY OF THE INVENTION
Titanium dioxide (titania) and zirconium dioxide (zirconia) are rugged, stable compounds that are useful as supports for catalytically active metals. It has been surprisingly discovered in accordance with the present invention that titania and zirconia effectively and substantially selectively catalyze the decomposition of tertiary butyl hydroperoxide to tertiary butyl alcohol.
Thus, in accordance with the present invention, a solvent solution of a tertiary butyl hydroperoxide charge stock is brought into contact with a catalytically effective amount of titania or zirconia in a hydroperoxide decomposition reaction zone in liquid phase with agitation to convert the tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol. The hydroperoxide decomposition catalyst consists essentially of titania or zirconia. Tertiary butyl alcohol is recovered from the products of the hydroperoxide decomposition reaction.
The tertiary butyl alcohol will not be the only decomposition product that is formed. Minor amounts of other oxygen-containing materials such as those listed above will also be formed.
The tertiary butyl alcohol that is recovered from the decomposition reaction mixture will be contaminated with the oxygenated impurities.

DESCRIPTION OF THE PROCESS OF THE PRESENT INVENTION
The starting materials for the process of the present invention are a tertiary butyl hydroperoxide feedstock and titania or zirconia.
The Tertiary Butyl Hydroperoxide Feedstock
The tertiary butyl hydroperoxide charge stock may comprise an isobutane oxidation product wherein the tertiary butyl hydroperoxide is dissolved in a mixture of isobutane and tertiary butyl alcohol or may comprise an isobutane oxidation product enriched by the addition of tertiary butyl alcohol, such that the solution of tertiary butyl alcohol in the mixture of isobutane with tertiary butyl alcohol contains from about 5 to about 30 wt. % of tertiary butyl hydroperoxide. A surprising and unexpected increase in the yield of tertiary butyl alcohol is obtained with a feedstock comprising a mixture of isobutane with tertiary butyl alcohol.
Alternately, the isobutane reaction product may be charged to a distillation zone where unreacted isobutane is removed as a distillate fraction for recycle to thereby provide a solution of tertiary butyl hydroperoxide in tertiary butyl alcohol containing about 5 to about 30 wt. % of tertiary butyl hydroperoxide.
The Catalyst
The hydroperoxide decomposition catalyst to be used in accordance with the present invention consists essentially of titania, zirconia or a mixture thereof.
Catalytic Decomposition of Tertiary Butyl Hydroperoxide
The process of the present invention may be conducted batchwise in kettles or by continuously passing the reactants through a tubular reactor.
The catalytic decomposition of the tertiary butyl hydroperoxide is preferably conducted at a temperature within the range of about 20.degree. to about 160.degree. C. and, more preferably, at a temperature within the range of about 80.degree. to about 100.degree. C. The reaction is preferably conducted at a pressure sufficient to keep the reactants and the reaction products in liquid phase. A pressure of about 0 to about 10,000 psig. may be used, if desired.
Flow rates of the charge solution to the reaction zone should be adjusted in order to provide an appropriate contact time within the reactor. In a batch process, the holding time may suitably be from about 0.5 to about 10 hours, and more preferably about 1 to 3 hours.
In accordance with a preferred embodiment of the present invention, isobutane is reacted with oxygen in an oxidation zone under oxidation reaction conditions including a temperature of about 135.degree. to about 155.degree. C., a pressure of about 300 to about 800 psig., and a holding time of about 2 to about 6 hours to provide an initial oxidation reaction product comprising unreacted isobutane, tertiary butyl hydroperoxide, tertiary butyl alcohol, and oxygen-containing by-products. The initial oxidation reaction product is then used as the tertiary butyl hydroperoxide charge stock of the present invention. If the concentration of tertiary butyl hydroperoxide in the tertiary butyl hydroperoxide charge stock is more than about 30 wt. % of the initial oxidation reaction product, the initial oxidation reaction product can be diluted with an amount of tertiary butyl alcohol sufficient to lower the concentration of the tertiary butyl hydroperoxide to a desired percentage, to provide, for example, a tertiary butyl hydroperoxide charge stock containing from about 15 to about 25 wt. % of tertiary butyl hydroperoxide.
Alternately, the initial oxidation reaction product may be fractionated in any appropriate manner (e.g., by distillation in a distillation zone) to remove the isobutane therefrom for recycle and to provide a solution of tertiary butyl hydroperoxide and tertiary butyl alcohol which will normally contain from about 5 to about 30 wt. % of tertiary butyl hydroperoxide.
In a continuous process, the solution of tertiary butyl hydroperoxide in tertiary butyl alcohol is charged to a catalytic hydroperoxide decomposition zone where it is brought into contact with pelleted titania or zirconia to substantially selectively convert the tertiary butyl hydroperoxide to tertiary butyl alcohol with high yields and selectivities.
As indicated, the catalytic decomposition of the tertiary butyl hydroperoxide in the catalytic hydroperoxide decomposition reaction zone may suitably be conducted at a temperature within the range of about 20.degree. to about 160.degree. C., preferably from about 60.degree. to about 120.degree. C., and more preferably from about 80.degree. to 100.degree. C. at autogenous pressure or if desired at a superatmospheric pressure up to 10,000 psig. for a contact time within the range of about 0.5 to about 10 hours, and more preferably about 1 to 3 hours.
When the process of the present invention is practiced in a continuous manner by continuously charging the tertiary butyl hydroperoxide charge stock to a reactor containing a fixed bed of pelleted hydroperoxide decomposition catalyst, the space velocity is suitably in the range of about 0.5 to about 3 volumes of tertiary butyl hydroperoxide charge stock per volume of catalyst per hour. Preferably, the space velocity is within the range of about 1 to about 3 volumes of tertiary butyl hydroperoxide charge stock per volume of catalyst per hour.
The reaction product from the tertiary butyl hydroperoxide decomposition step may then be fractionated in any suitable manner, such as by distillation to recover the tertiary butyl alcohol.
SPECIFIC EXAMPLES
The invention will be further illustrated by the following specific examples which are given by way of illustration and not as limitations on the scope of this invention.
Procedure
The reactor was a stainless steel tube (0.51".times.15") which was electrically heated. Liquid feed was pumped into the bottom of the reactor. Pressure regulation was with a Skinner Uni-Flow valve and a Foxboro controller. The liquid feed was pumped with a Ruska dual drive pump.
20% TBHP was prepared from 55% isobutane peroxidation reactor effluent by diluting with commercial TBA.
Analysis of the reactor effluent was by GC. Details are given in the following tables:
Example 1
In this example, the catalyst consisted essentially of pelleted titania or zirconia.
TABLE 1__________________________________________________________________________CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDETO TERT-BUTYLALCOHOL Notebook Number 6844-10-A 6906-14-1 6906-14-2 6906-14-3 6906-14-4__________________________________________________________________________Catalyst Norton TiO.sub.2 Norton TiO.sub.2 Norton TiO.sub.2 Norton TiO.sub.2Catalyst (cc) 100 100 100 100Pressure (psig) 500 500 500 500Feed Rate (cc/Hr.) 50 50 50 50Temperature (.degree.C.) 80 100 120 140Time on Stream (Hr) 4 4 4 4Space Vel. (cc/cc) 0.5 0.5 0.5 0.5TBHP Conversion (mol. %) 22.5 72.0 92.7 98.5Selectivity IC4= (mol. %) 0.3 0.2 0.1 1.5Sel. Acetone (mol. %) 11.6 16.4 31.0 32.8Sel. Methanol (mol. %) 1.3 3.3 8.5 8.9Sel. TBA (mol. %) 80.5 79.3 66.4 66.1Sel. DTBP (mol. %) 7.9 4.3 2.5 1.1Remarks H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free BasisComposition, wt %IC4= 0.001 0.009 0.014 0.008 0.172MEOH/MF 0.016 0.036 0.178 0.553 0.614Acetone 0.008 0.329 1.465 3.559 3.994TEA 79.968 83.753 91.494 93.449 93.754DTBP 0.055 0.330 0.531 0.419 0.230TBHP 19.146 14.843 5.356 1.395 0.288__________________________________________________________________________
TABLE 2__________________________________________________________________________CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDETO TERT-BUTYLALCOHOL Notebook Number 6844-10-A 6906-15-1 6906-15-2 6906-15-3 6906-15-4__________________________________________________________________________Catalyst Norton TiO.sub.2 Norton TiO.sub.2 Norton TiO.sub.2 Norton TiO.sub.2Catalyst (cc) 100 100 100 100Pressure (psig) 500 500 500 500Feed Rate (cc/Hr.) 100 100 100 100Temperature (.degree.C.) 80 100 120 140Time on Stream (Hr) 4 4 4 4Space Vel. (cc/cc) 1.0 1.0 1.0 1.0TBHP Conversion (mol. %) 8.3 35.8 89.2 99.5Selectivity IC4= (mol. %) 0.0 0.2 0.7 2.1Sel. Acetone (mol. %) 0.0 13.0 27.5 40.6Sel. Methanol (mol. %) 0.0 2.6 8.1 10.5Sel. TBA (mol. %) 0.0 82.2 70.4 59.3Sel. DTBP (mol. %) 0.0 4.8 2.1 0.2Remarks H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free BasisComposition, wt %IC4= 0.001 0.006 0.009 0.077 0.245MEOH/MF 0.016 0.032 0.080 0.507 0.726Acetone 0.008 0.196 0.583 3.037 4.993TBA 79.968 81.060 85.597 93.102 92.353DTBP 0.055 0.150 0.322 0.342 0.079TBHP 19.146 17.562 12.289 2.067 0.091__________________________________________________________________________
TABLE 3__________________________________________________________________________CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDETO TERT-BUTYLALCOHOL Notebook Number 6844-10-A 6906-16-1 6906-16-2 6906-16-3 6906-16-4__________________________________________________________________________Catalyst Norton TiO.sub.2 Norton TiO.sub.2 Norton TiO.sub.2 Norton TiO.sub.2Catalyst (cc) 100 100 100 100Pressure (psig) 500 500 500 500Feed Rate (cc/Hr.) 200 200 200 200Temperature (.degree.C.) 80 100 120 140Time on Stream (Hr) 4 4 4 4Space Vel. (cc/cc) 2.0 2.0 2.0 2.0TBHP Conversion (mol. %) 3.4 16.4 55.1 89.0Selectivity IC4= (mol. %) 0.0 0.4 0.4 2.4Sel. Acetone (mol. %) 0.0 14.1 20.0 36.2Sel. Methanol (mol. %) 0.0 2.3 3.5 11.7Sel. TBA (mol. %) 0.0 80.7 76.9 62.8Sel. DTBP (mol. %) 0.0 5.2 3.0 1.0Remarks H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free BasisComposition, wt %IC4= 0.001 0.002 0.008 0.027 0.252MEOH/MF 0.016 0.016 0.042 0.146 0.723Acetone 0.008 0.095 0.293 1.370 3.984TBA 79.968 80.247 82.401 88.264 91.443DTBP 0.055 0.113 0.188 0.314 0.190TBHP 19.146 18.490 16.000 8.597 2.114__________________________________________________________________________
TABLE 4__________________________________________________________________________CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDETO TERT-BUTYLALCOHOL Notebook Number 6844-10-A 6906-17-1 6906-17-2 6906-17-3 6906-17-4__________________________________________________________________________Catalyst Norton ZrO.sub.2 Norton ZrO.sub.2 Norton ZrO.sub.2 Norton ZrO.sub.2Catalyst (cc) 100 100 100 100Pressure (psig) 500 500 500 500Feed Rate (cc/Hr.) 50 50 50 50Temperature (.degree.C.) 80 100 120 140Time on Stream (Hr) 4 4 4 4Space Vel. (cc/cc) 0.5 0.5 0.5 0.5TBHP Conversion (mol. %) 19.7 77.5 100.0 100.0Selectivity IC4= (mol. %) 0.0 0.0 0.1 0.1Sel. Acetone (mol. %) 10.8 15.8 30.2 32.5Sel. Methanol (mol. %) 1.3 3.8 7.8 7.3Sel. TBA (mol. %) 81.1 79.2 67.5 66.4Sel. DTBP (mol. %) 8.2 5.0 2.3 1.1Remarks H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free BasisComposition, wt %IC4= 0.001 0.001 0.004 0.008 0.013MEOH/MF 0.016 0.034 0.216 0.545 0.511Acetone 0.008 0.270 1.523 3.733 4.018TBA 79.968 83.121 92.713 94.030 94.347DTBP 0.055 0.305 0.656 0.417 0.220TBHP 19.146 15.373 4.302 0.000 0.000__________________________________________________________________________
TABLE 5__________________________________________________________________________CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDETO TERT-BUTYLALCOHOL Notebook Number 6844-10-A 6906-18-1 6906-18-2 6906-18-3 6906-18-4__________________________________________________________________________Catalyst Norton ZrO.sub.2 Norton ZrO.sub.2 Norton ZrO.sub.2 Norton ZrO.sub.2Catalyst (cc) 100 100 100 100Pressure (psig) 500 500 500 500Feed Rate (cc/Hr.) 100 100 100 100Temperature (.degree.C.) 80 100 120 140Time on Stream (Hr) 4 4 4 4Space vel. (cc/cc) 1.0 1.0 1.0 1.0TBHP Conversion (mol. %) 7.1 53.9 95.9 96.9Selectivity IC4= (mol. %) 0.0 0.0 0.5 0.2Sel. Acetone (mol. %) 0.0 13.7 26.8 35.6Sel. Methanol (mol. %) 0.0 3.3 6.8 8.2Sel. TBA (mol. %) 0.0 80.8 70.9 63.6Sel. DTBP (mol. %) 0.0 5.6 2.3 0.8Remarks H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free BasisComposition, wt %IC4= 0.001 0.001 0.002 0.057 0.022MEOH/MF 0.016 0.024 0.138 0.459 0.558Acetone 0.008 0.162 0.916 3.183 4.258TBA 79.968 80.948 88.872 94.379 93.539DTBP 0.055 0.196 0.522 0.401 0.177TBHP 19.146 17.793 8.827 0.781 0.602__________________________________________________________________________
TABLE 6__________________________________________________________________________CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDETO TERT-BUTYLALCOHOL Notebook Number 6844-10-A 6906-19-1 6906-19-2 6906-19-3 6906-19-4__________________________________________________________________________Catalyst Norton ZrO.sub.2 Norton ZrO.sub.2 Norton ZrO.sub.2 Norton ZrO.sub.2Catalyst (cc) 100 100 100 100Pressure (psig) 500 500 500 500Feed Rate (cc/Hr.) 200 200 200 200Temperature (.degree.C.) 80 100 120 140Time on Stream (Hr) 4 4 4 4Space Vel. (cc/cc) 2.0 2.0 2.0 2.0TBHP Conversion (mol. %) 4.5 28.9 83.0 94.9Selectivity IC4= (mol. %) 0.0 0.0 -0.0 0.1Sel. Acetone (mol. %) 0.0 13.4 11.6 34.0Sel. Methanol (mol. %) 0.0 3.1 7.0 8.6Sel. TBA (mol. %) 0.0 80.4 85.8 65.3Sel. DTBP (mol. %) 0.0 6.2 2.6 0.7Remarks H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free Basis H.sub.2 O Free BasisComposition, wt %IC4= 0.001 0.001 0.002 0.000 0.011MEOH/MF 0.016 0.021 0.076 0.410 0.575Acetone 0.008 0.102 0.486 1.201 3.992TBA 79.968 80.470 84.554 94.037 93.362DTBP 0.055 0.151 0.331 0.386 0.159TBHP 19.146 18.287 13.615 3.252 0.967__________________________________________________________________________
Example 2
A 19.1% solution of TBHP in TBA decomposed over a heterogeneous zirconium or titanium catalyst gave good yields of TBA. For example, using a 50 cc up-flow reactor at 100.degree. C. and a space velocity of 0.5, a commercial titanium oxide catalyst gave 72.0% TBHP conversion and a selectivity to TBA of 79.3%. The selectivity to acetone was 16.4%, methanol 3.3% and DTBP 4.3%. Under the same conditions a commercial zirconium oxide catalyst gave 77.5% TBHP conversion and a selectivity to TBA of 79.2%. The selectivity to acetone was 15.8%, methanol 3.8% and DTBP 5.0%. Minor products including carboxylic acids were also formed.

Claims

1. In a method wherein a solvent solution of a tertiary butyl hydroperoxide charge stock is brought into contact with a catalytically effective amount of a hydroperoxide decomposition catalyst in a hydroperoxide decomposition reaction zone in liquid phase to convert said tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol, the improvement which comprises:
a) using titania or zirconia or a mixture thereof as said hydroperoxide decomposition catalyst, and
b) recovering tertiary butyl alcohol from the products of said hydroperoxide decomposition reaction.
2. A method as in claim 1 wherein the solvent comprises tertiary butyl alcohol.
3. A method as in claim 1 wherein the solvent comprises a mixture of isobutane with tertiary butyl alcohol.
4. A method as in claim 1 wherein the catalyst consists essentially of titania.
5. A method as in claim 1 wherein the catalyst consists essentially of zirconia.
6. In a method wherein a solution of a tertiary butyl hydroperoxide charge stock in tertiary butyl alcohol that contains from about 5 to about 30 wt. % of tertiary butyl hydroperoxide is brought into contact with a catalytically effective amount of a hydroperoxide decomposition catalyst in a hydroperoxide decomposition reaction zone in liquid phase under hydroperoxide conversion conditions including a temperature within the range of about 25.degree. to about 250.degree. C. and a pressure of about 0 to about 1,000 psig to convert said tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol, the improvement which comprises:
a) using titania or zirconia or a mixture thereof as said hydroperoxide decomposition catalyst, and
b) recovering tertiary butyl alcohol from the products of said hydroperoxide decomposition reaction.
7. A method as in claim 6 wherein the temperature is in the range of about 40.degree. to about 150.degree. C. and the pressure is about 0 psig.
8. A method as in claim 6 wherein the catalyst consists essentially of titania.
9. A method as in claim 6 wherein the catalyst consists essentially of zirconia.
10. In a method wherein a solution of a tertiary butyl hydroperoxide charge stock in a mixture of isobutane with tertiary butyl alcohol that contains from about 5 to about 30 wt. % of tertiary butyl hydroperoxide is continuously brought into contact with a catalytically effective amount of a hydroperoxide decomposition catalyst in a hydroperoxide decomposition reaction zone in liquid phase under hydroperoxide conversion conditions including a temperature within the range of about 25.degree. to about 250.degree. C. and a pressure of about 0 to about 1,000 psig to convert said tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol, the improvement which comprises:
a) using pelleted titania or pelleted zirconia as said hydroperoxide decomposition catalyst, and
b) recovering tertiary butyl alcohol from the products of said hydroperoxide decomposition reaction.
11. A method as in claim 10 wherein the temperature is in the range of about 40.degree. to about 150.degree. C., and the pressure is about 0 psig.
12. A method as in claim 11 wherein the catalyst consists essentially of pelleted titania.
13. A method as in claim 11 wherein the catalyst consists essentially of zirconia.

Use of titania or zirconia in the preparation of tertiary butyl alcohol from tertiary butyl hydroperoxide

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims