Use of water-insoluble polyoxyalkylene-polysiloxane block copolymers for defoaming aqueous media

Information

  • Patent Grant
  • 6686320
  • Patent Number
    6,686,320
  • Date Filed
    Monday, March 18, 2002
    22 years ago
  • Date Issued
    Tuesday, February 3, 2004
    20 years ago
Abstract
The invention relates to the use of water-insoluble polyoxyalkylene-polysiloxane block copolymers of the general average formula wherein the variables and indices are described herein as defoaming agents for aqueous media. This invention also provides for defoaming compositions comprising said water-insoluble polyoxyalkylene-polysiloxane block copolymers as well as coating materials, printing inks and cooling lubricants containing the inventive defoaming compositions.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The invention relates to the use of water-insoluble polyoxyalkylene-polysiloxane block copolymers for defoaming aqueous media.




In numerous industrial processes, aqueous formulations use surface-active substances in order, for example, to emulsify water-insoluble substances or to reduce the interfacial tension and so achieve better wetting characteristics. An unwanted accompanying effect of these surface-active substances, however, is that air introduced during the preparation and processing of such water-based formulations is stabilized as foam. Examples of processes in which such problems occur include papermaking, wastewater treatment, emulsion polymerization, and the manufacture and application of water-dilutable coating systems.




Foam of this kind, produced in the course of stirring or dispersing operations during manufacture or filling, prolongs production times and reduces the effective capacity of the production plant Foam is disruptive to the application of coating materials since it leads to unwanted surface defects. As a result, the use of antifoams or defoamers in virtually all water-based systems is widespread and often indispensable.




In the past, a large number of formulations have been described which envisage the use of, for example, silicone oils, organo modified siloxanes, hydrophobic polyoxyalkylenes, mineral oils, natural oils and other hydrophobic liquids as defoaming substances. Frequently, the above-mentioned substances are used in combination with hydrophobic solids, such as silicas, metal stearates or fatty acid amides, for example, which often intensify the foam inhibiting or defoaming effect.




In accordance with the present state of knowledge, it is critical to the defoaming action of a defoamer that it is able to penetrate into the foam lamellae and so to weaken them until they collapse (cf. K. Koezo, J. K. Koezone, D. T. Wasan, J. Colloid Interface Sci. 166, 225-238 (1994)). To achieve this requires a controlled incompatibility (hydrophobicity) with the aqueous phase to be defoamed: if a defoamer is too compatible (hydrophilic), it will not be able to be very effective since it does not penetrate preferentially into the foam lamella. If the degree of incompatibility is too great, then defoaming is generally very good but there are frequently the unwanted side effects of surface defects, deterioration in wetting characteristics, and separation phenomena.




Consequently, the search for a suitable defoamer is always a search for the correct incompatibility/compatibility balance for the system to be defoamed, with the aim of getting as close as possible to the target hydropbobicity/hydrophilicity equilibrium




2. Description of the Related Art




In the past, polyoxyalkylene-polysiloxane block copolymers have proven suitable for allowing this equilibrium to be established in a particularly variable manner, as is described, inter alia, in U.S. Pat. No. 3,763,021.




When polyoxyalkylene-polysiloxane block copolymers are used, advantage is taken of the fact that the polysiloxane blocks can be modified in a targeted manner with polyoxyalkylene units which, by virtue of their composition from hydrophilic and hydrophobic polyoxyalkylene units, can be adapted, in interplay with the polysiloxane block, to the abovementioned desired hydrophobicity/hydrophilicity equilibrium.




The prior art, an example of which that may be mentioned here is DE-C-1 012 602, includes polyoxyalkylene-polysiloxane block copolymers in which the polyoxyalkylene block is defined as (C


n


H


2n


O)


x


. The index n is an integer from 2 to 4, it being essential that these polyoxyalkylene blocks always include —CH


2


—CHR—O— groups as a common structural element, R being a hydrogen atom, a methyl group or an ethyl group. Such polyoxyalkylene blocks are prepared by ionic addition polymerization of oxirane derivatives, such as ethylene oxide, propylene oxide and butylene oxide. The basic structure of the properties-determining polyoxyalkylene chain is distinguished, however, by generally the combination of only two different polyoxyalkylene units in a polyoxyalkylene chain. Typically, polyoxyethylenes and polyoxypropylenes are used in the polyoxyalkylene-polysiloxane block copolymers of the prior art.




By varying the oxyalkylene units, and in particular by modifying their respective proportions and their sequence in the polymer (random and/or in blocks), a large number of polyoxyalkylene-polysiloxane block copolymers are obtainable.




Because of the restriction to only two polyoxyalkylene units, however, in many cases it has not been possible to date to find the optimum incompatibility/compatibility balance required for certain defoamers, and especially not when their random distribution is permitted.




OBJECT OF THE INVENTION




It is therefore an object of the present invention to provide particularly suitable polyoxyalkylene-polysiloxane block copolymers for defoaming aqueous media, said copolymers making it possible to establish the above-described desired incompatibility/compatibility balance in a targeted manner better than has been possible to date.




SUMMARY OF THE INVENTION




This object is surprisingly achieved by the use of water-insoluble polyoxyalkylene-polysiloxane block copolymers of the general average formula I:











where




R


1


and/or R


7


are R


2


or —[R


4


]


w


—[R


5


]


x


—[R


6


]—R


8


,




R


2


and R


3


are identical or different alkyl radicals, preferably having 1 to 24 carbon atoms or are unsubstituted or substituted aryl radicals, preferably having up to 24 carbon atoms, with phenyl especially preferred,




R


4


is a divalent radical of the formula —O—, —NH—, —NR


2


— or —S— or of the formula






—[O—Si(CH


3


)


2


]


u


—,






 where




u is from 2 to 200,




R


5


is identical or different alkylene radicals, preferably having 1 to 24 carbon atoms, or is






—C


n


H


2n-f


R


2




1


—O—C


m


H


2m-g


R


2




g


—,






 where




f is from 0 to 12,




g is from 0 to 12,




n is from 1 to 18,




m is from 1 to 18,




R


6


is identical or different radicals of the general formula






—O—(C


2


H


4


O)


a


(CH


2


—CH(CH


3


)O)


b


(CH


2


—CR


9


R


10


O)


c


—,






 where




R


9


and R


10


are a methyl radical or




R


9


is a hydrogen atom and R


10


is an ethyl radical,




 but where, taking into account all radicals R


6


, the proportion of C


2


H


4


O groups among the total of all radicals R


6


does not exceed 40% by weight,




a is from 2 to 30,




b is from 2 to 50,




c is from 2 to 40, and




the sum (a+b+c) is from 6 to 100




and the sequence of the individual polyoxyalkylene segments —(C


2


H


4


O)


a


— and —(CH


2


—CH(CH


3


)O)


b


— and —(CH


2


—CR


9


R


10


0)


c


— can be as desired and, in particular, embraces block copolymers, such as random polymers and combinations thereof,




R


8


is a hydrogen, a substituted or unsubstituted alkyl radical, preferably having 1 to 6 carbon atoms, or an acyl radical,




v is from 3 to 200,




w is 0 or 1,




x is 0 or 1,




y is from 0 to 200,




and, if y is 0, R


1


and/or R


7


are/is —[R


4


]


w


—[R


5


]


x


—[R


6


]—R


8


for defoaming aqueous media.




In many cases, polyoxyalkylene-polysiloxane block copolymers which have proven highly suitable are those obtained by means of combinations of two or more polyoxyalkylene units with one or more polysiloxane copolymers. In that case, the distinction in the case of the polyoxyalkylene copolymers can be a distinction in relation either to the relative proportion of the units used for the preparation of this copolymer or to the molecular weight of the whole polyoxyalkylene unit, or else can lie in its functionality.




Different polysiloxane copolymers can be distinguished in accordance with both their molecular mass and their degree of branching or the number and/or relative position of the reactive groups used which are available for linkage.




The mode of action of the compounds of the invention is expressly not that they bring about particularly good compatibilization between constituents of a mixture that differ in polarity. Rather, it is the case that they themselves are just compatible enough not to induce any unwanted side effects such as surface defects, deteriorations in the wetting characteristics, or separation phenomena, but without bringing about the compatibilization of other constituents.




For the present invention it is essential that the polyoxyalkylene-polysiloxane block copolymers of the invention are not water-soluble. This means that a 1:1 mixture (% by weight) with water leads to a nonhomogeneous mixture of the two phases and that no dissolving of the polyoxyalkylene-polysiloxane block copolymers of the invention takes place. However, small fractions of free polyoxyalkylenes may be present in the polyoxyalkylene-polysiloxane block copolymers as a result of their preparation as set out below. Since the preparation of these copolymers essentially obeys the laws of statistics, it is also possible for particularly oxyethylene-rich polyoxyalkylenes to occur, which in turn may be soluble in water. These fractions, however, are very small and in the polyoxyalkylene-polysiloxane block copolymers of the invention are always less than 10% by weight.




The polyoxyalkylene-polysiloxane block copolymers of the invention can be prepared in accordance with customary methods as in the prior art. As the skilled worker is well aware, such methods include in particular the hydrosilylation reaction of additionally olefinically unsaturated polyoxyalkylenes with hydropolysiloxanes, as described for example in U.S. Pat. No. 3,402,192, or the nucleophilic substitution of polyoxyalkylenes with nucleophilic groups on polysiloxanes containing at least one silicon atom substituted by an electronegative group (cf., for example, DE-B-11 65 028). Processes of this kind and the preparation of appropriate polysiloxanes are further described, moreover, for example, in W. Noll “Chemie und Technologie der Silicone”, Verlag Chemie, Weinheim, 1968.




In accordance with the prior art, the polyoxyalkylenes required for this purpose can be obtained by ionic polymerization of ethylene oxide, propylene oxide, n-butylene oxide, and isobutylene oxide.











EXAMPLES




In order to illustrate the claimed compounds, the following polysiloxanes 1 to 3 were reacted, by way of example, with the polyoxyalkylenes 1 to 8:













TABLE 1











Polysiloxane 1




(CH


3


)


3


SiO—[(CH


3


)


2


SiO—]


20


[(CH


3


)


2


HSiO—]


5


Si(CH


3


)


3








Polysiloxane 2




(CH


3


)


2


HSiO—[(CH


3


)


2


SiO—]


30


[(CH


3


)


2


HSiO—]


4


SiH(CH


3


)


2








Polysiloxane 3




(CH


3


)


2


ClSiO—[(CH


3


)


2


SiO—]


13


SiCl(CH


3


)


2








Polyoxy-




H


2


C═CH—CH


2


O—(C


2


H


4


O—)


4


(CH


2


CH(C


2


H


5


)O)


8


H






alkylene 1






Polyoxy-




H


2


C═CH—CH


2


O—(C


2


H


4


O—)


4


(CH


2


CH(CH


3


)O—)


18


H






alkylene 2






Polyoxy-




H


2


C═CH—CH


2


O—(CH


2


CH(CH


3


) O—)


10


(CH


2


CH(C


2


H


5


)O)


6


H






alkylene 3






Polyoxy-




H


2


C═CH —CH


2


O—(C


2


H


4


O—)


12


(CH


2


CH(CH


3


)O—)


4


(CH


2


H


5


)O)


2


H






alkylene 4






Polyoxy-




H


2


C═CH—CH


2


O—(C


2


H


4


0—)


4


(CH


2


CH(CH


3


)O—)


10


(CH


2


CH(C


2


H


5


)O)


6


H






alkylene 5






Polyoxy-




H


3


C—CH


2


—CH


2


—CH


2


O—(C


2


H


4


O—)


4


(CH


2


CH(CH


3


)O—)


18


H






alkylene 6






Polyoxy-




H


3


C—CH


2


—CH


2


—CH


2


O—C


2


H


4


O—)


12


(CH


2


CH(CH


3


O—)


4


(CH


2


CH(C


2


H


5


)O)


2


H






alkylene 7






Polyoxy-




H


3


C—CH


2


—CH


2


—CH


2


O—(C


2


H


4


O—)


4


CH


2


CH(CH


3


)O—)


10


(CH


2


CH(C


2


H


5


)O)


6


H






alkylene 8














The skilled worker is well aware that the compounds are obtained in the form of mixtures of their homologs and that the indices stated denote average values.




In accordance with the Table below, the following polyoxyalkylene-polysiloxane block copolymers were obtained:
















TABLE 2











Polyoxyalkylene





Inventive






Example




Siloxane




(eq %)




(eq %)




yes/no



























1




1




1 (100)









no






2




1




2 (100)









no






3




1




3 (100)









no






4




1




4 (100)









no






5




1




5 (100)









yes






6




2




1 (100)









no






7




2




2 (100)









no






8




2




3 (100)









no






9




2




4 (100)









no






10




2




5 (100)









yes






11




2




5 (50) 




4 (50)




yes






12




3




6 (100)









no






13




3




7 (100)









no






14




3




8 (100)









yes






15




3




8 (50) 




7 (50)




yes














Examples 1 to 11 were prepared in accordance with processes customary from the literature as described, for example, in DE-B-11 65 028; Examples 2 to 15 were prepared in accordance with processes customary from the literature as described, for example, in U.S. Pat. No. 2,846,458.




The skilled worker is well aware that with this mode of preparation, corresponding to the prior art, it is possible for free polyoxyalkylene still to be present in the polyoxyalkylene-polysiloxane block copolymers. As a general rule, this is not disruptive and need not be removed for the subsequent use of the compounds.




For use as defoamers, the water-insoluble polyoxyalkylene-polysiloxane block copolymers of the invention are advantageously formulated as follows:




a) from 72 to 85% by weight of the polyoxyalkylene-polysiloxane block copolymers,




b) from 15 to 28% by weight of a nonionic ethoxylate having a HLB of from 8 to 12, and




c) from 0.1 to 10% by weight, based on the sum a)+b), of an organic or inorganic solid substance.




Examples of nonionic ethoxylates having a HLB (hydrophilic/lipophilic balance; definition as per W. C. Griffin; J. Soc. Cosmet. Chem., Volume 5, page 249, 1954) of 8-12 are fatty acid esters of polyvalent alcohols, the polyethylene glycol derivatives thereof, polyglycol derivatives of fatty acids and fatty alcohols, alkylphenol ethoxylates, and block copolymers of ethylene oxide and propylene oxide (Pluronics). Preference is given to ethoxylates of raw materials obtainable from naturally occurring fats, especially oleyl derivatives and stearyl derivatives.




Examples of the organic or inorganic solid substances are silicas, alumina, alkaline earth metal carbonates, alkaline earth metal salts of long chain fatty acids, the amides thereof, and urea derivatives. These substances may also have been additionally hydrophobicized in accordance with known methods.




The formulated defoamers described above can be used as they are or in the form of their aqueous emulsion. Emulsions are frequently used with preference since they are easier to meter. Particular preference is given to defoamer emulsions whose average particle diameter lies between 1 and 10 μm. Such emulsions then contain between 5 and 50% by weight of the water-insoluble polyoxyalkylene-polysiloxane block copolymers of the invention.




Performance testing takes place in emulsion paints to which defoamer is added conventionally in amounts of from 0.01 to 0.5% by weight based on the emulsion paint.




The following formulations were prepared and tested:














TABLE 3










Polyoxyalkylene-polysiloxane block co-




Inventive






Formulation




polymer from Example




yes/no

























1




1




no






2




2




no






3




3




no






4




4




no






5




5




yes






6




6




no






7




7




no






8




8




no






9




9




no






10




10




yes






11




11




yes






12




12




no






13




13




no






14




14




yes






15




15




yes














The compositions of formulations 1 to 15 are as follows:




75% by weight polyoxyalkylene-polysiloxane block copolymer as per Example 1 to 15




20% by weight oleyl ethoxylate with a HLB of 10




5% by weight silica.




Testing was carried out in the following emulsion paints:




















Emulsion paint 1 (all amounts in % by weight)















Propylene glycol




4.7








Collacral ® AS 35




5.0




BASF







(polyacryalate dispersing agent)







Titanium dioxide




23.1







Mergal ® K7




0.2




Riedel de Haen







(formaldehyde-free preservative)







Butylglycol




2.6







Dowanol ® DPM




1.3




Dow







(dipropylene glycol methyl ether)







Water




6.8







Acronal ® A603




52.3




BASE







(acrylate dipersion)







Rheolate ® 278




4.0




Rheox







(polyurethane-based thickener)













Emulsion paint 2 (all amounts in % by weight)















Water




36.4








Coatex ® P50




0.4




Coatex







(polyurethane-based thickener)







Calgon ® N




0.1




BK Ladenburg







(sodium polyphosphate)







Mergal ® K7




0.2




Riedel de Haen







(formaldehyde-free preservative)







Coatex ® BR100




2.3




Coatex







(polyurethane-base thickener)







Calcidar ® Extra




22.1




Omya







(calcium carbonate)







Titanium dioxide




17.5







Finntalc ® M15




4.7







(talcum)







NaGH, 10%




0.1







Acronal ® 290D




16.2




BASE







(Styrene acrylate disperion)















The emulsion paints were formulated in accordance with the prior art. All raw materials were used without further purification. To end, 0.06% by weight of defoamer (formulation 1 to 15) was added and was incorporated by stirring at 1000 rpm for 1 minute.




A so-called roller test was carried out, the result of which is shown in the Tables below. The roller test firstly allows comparison to be made under conditions close to those in practice and secondly offers the possibility of reasonable differentiation of different formulations.




For the roller test, 40 grams of the test emulsion paint are spread using an open-pored foam roller onto a nonabsorbent test card having a total surface area of 500 cm


2


Prior to the application of the paint, the foam roller is wetted with water. It must be ensured that the additional amount of water introduced into the applied paint is always the same, so that the drying time of the paint always remains the same. The wet film addon is approximately 300 g/m


2


. After 24 hours of drying time, the test cards are examined in accordance with the following criteria:




a) Macrofoam (number of bubbles per 100 cm


2


)




b) Microfoam (number of pinholes in comparison to photos of reference cards on a scale of 1 (very few or no pinholes) to 5 (very large number of pinholes))




c) Wetting defects (none, slight, severe).




The tests were repeated with emulsion paints which had been admixed with defoamer and kept at 50° C. for 6 weeks.




Results for Emulsion Paint 1:
















TABLE 4













Macrofoam




Microfoam




Wetting defects

















Formu-




immedi-





immedi-





immedi-







lation




ate




6 weeks




ate




6 weeks




ate




6 weeks




















none




76




78




5




5




none




none






1




1




3




1




1




none




slight






2




2




4




1




1




none




slight






3




0




1




1




1




severe




severe






4




61




70




3




3




none




slight






5




0




0




1




1




none




none






6




3




6




1




2




none




slight






7




3




4




1




2




slight




slight






8




1




1




1




1




severe




severe






9




62




69




2




3




severe




severe






10




0




1




1




1




none




none






11




0




0




1




1




none




none






12




3




4




1




2




slight




slight






13




48




31




2




2




none




none






14




0




0




1




1




none




none






15




0




1




1




1




none




none














Results for Emulsion Paint 2:
















TABLE 5













Macrofoam




Microfoam




Wetting defects

















Formu-




immedi-





immedi-





immedi-







lation




ate




6 weeks




ate




6 weeks




ate




6 weeks




















none




51




50




3




4




none




none






1




1




2




1




2




none




slight






2




1




3




1




1




none




slight






3




0




2




1




1




severe




severe






4




41




59




2




3




slight




slight






5




0




0




1




1




none




none






6




3




9




1




2




none




slight






7




4




5




1




2




slight




slight






8




0




1




1




1




severe




severe






9




48




54




2




3




severe




severe






10




1




1




1




1




none




none






11




0




1




1




1




none




none






12




6




11




2




2




slight




slight






13




27




27




2




2




none




slight






14




0




0




1




1




none




none






15




0




1




1




1




none




none














It is found that the polyoxyalkylene-polysiloxane block copolymers of the invention, which are present in the formulations 5, 10, 11, 14 and 15, offer outstanding possibilities for adapting their properties to the requirements of defoaming aqueous media. Surprisingly, it is possible to achieve particular effects which are not possible even with comparably insoluble conventional polyoxyalkylene-polysiloxane block copolymers.




The above description is intended to be illustrative and not limiting. Various changes and modifications in the embodiments described herein may occur to those skilled in the art. Those changes can be made without departing from the scope or spirit of the invention.



Claims
  • 1. A defoaming composition which comprises a water-insoluble polyoxyalkylene-polysiloxane block copolymer of the average general formula whereR1 and/or R7 are R2 or —[R4]w—[R5]x—R6—R8, R2 and R3 are identical or different alkyl radicals or are unsubstituted or substituted aryl radicals, R4 is a divalent radical of the formula —O—, —NH—, —NR2—, —S—or of the formula —[O—Si(CH3)2]u—, whereu is from 2 to 200, R5 is identical or different alkylene radicals having 1 to 24 carbon atoms, or is —CnH2n-fR2f—O—CmH2m-gR2g—, where, f is from 0 to 12, g is from 0 to 12, n is from 1 to 18, m is from 1 to 18, R6 is identical or different radicals of the general formula —O—(C2H4O)a(CH2—CH(CH3)O)b(CH2—CR9R10O)c—, whereR9 and R10 are a methyl radical, or R9 is a hydrogen atom and R10 is an ethyl radical, but where, taking into account all radicals R6, the proportion of C2H4O groups among the total of all radicals R6 does not exceed 40% by weight, a is from 2 to 30, b is from 2 to 50, c is from 2 to 40, and the sum (a+b+c) is from 6 to 100 and the sequence of the individual polyoxyalkylene segments —(C2H4O)a— and —(CH2—CH(CH3)O)b— and —(CH2CR9R10O)c— is either random or block or combination thereof, R8 is a hydrogen, a substituted or unsubstituted alkyl radical or an acyl radical, v is from 3 to 200, w is 0 or 1, x is 0 or 1, y is from 0 to 200, and, if y is 0, R1 and/or R7 are/is —[R4]w—[R5]x—R6—R8; a nonionic ethoxylate having a HBL from 8 to 11 and, optionally, a solid; whereby said polysiloxane block copolymer is greater than 90% by weight of all polysiloxane block copolymers in the defoaming composition.
  • 2. A defoaming composition according to claim 1, which is an aqueous emulsion.
  • 3. A cooling lubricant which comprises a cooling lubricant and a defoaming effective amount of a defoaming composition which comprises a water-insoluble polyoxyalkylene-polysiloxane block copolymer of the average general formula whereR1 and/or R7 are R2 or —[R4]w—[R5]x—R6—R8, R2 and R3 are identical or different alkyl radicals or are unsubstituted or substituted aryl radicals, R4 is a divalent radical of the formula —O—, —NH—, —NR2—, —S— or of the formula —[O—Si(CH3)2]u—, whereu is from 2 to 200, R5 is identical or different alkylene radicals having 1 to 24 carbon atoms, or is —CnH2n-fR2f—O—CmH2m-gR2g—, where, f is from 0 to 12, g is from 0 to 12, n is from 1 to 18, m is from 1 to 18, R6 is identical or different radicals of the general formula —O—(C2H4O)a(CH2—CH(CH3)O)b(CH2-CR9R10O)c—, whereR9 and R10 are a methyl radical, or R9 is a hydrogen atom and R10 is an ethyl radical, but where, taking into account all radicals R6, the proportion of C2H4O groups among the total of all radicals R6 does not exceed 40% by weight, a is from 2 to 30, b is from 2 to 50, c is from 2 to 40, and the sum (a+b+c) is from 6 to 100 and the sequence of the individual polyoxyalkylene segments —C2H4O)a— and —(CH2—CH(CH3)O)b— and —(CH2CR9R10O)c— is either random or block or combination thereof, R8 is a hydrogen, a substituted or unsubstituted alkyl radical or an acyl radical, v is from 3 to 200, w is 0 or 1, x is 0 or 1, y is from 0 to 200, and, if y is 0, R1 and/or R7 are/is —[R4]w—[R5]x—R6—R8; whereby said polysiloxane block copolymer is greater than 90% by weight of all polysiloxane block copolymers in the defoaming composition.
  • 4. A polymer dispersion which comprises a polymer dispersion and a defoaming effective amount of a defoaming composition which comprises a water-insoluble polyoxyalkylene-polysiloxane block copolymer of the average general formula whereR1 and/or R7 are R2 or —[R4]w—[R5]x—R6—R8, R2 and R3 are identical or different alkyl radicals or are unsubstituted or substituted aryl radicals, R4 is a divalent radical of the formula —O—, —NH—, —NR2—, —S— or of the formula —[O—Si(CH3)2]u—, whereu is from 2 to 200, R5 is identical or different alkylene radicals having 1 to 24 carbon atoms, or is —CnH2n-fR2f—O—CmH2m-gR2g—, where, f is from 0 to 12, g is from 0 to 12, n is from 1 to 18, m is from 1 to 18, R6 is identical or different radicals of the general formula —O—(C2H4O)a(CH2—CH(CH3)O)b(CH2-CR9R10O)c—, whereR9 and R10 are a methyl radical, or R9 is a hydrogen atom and R10 is an ethyl radical, but where, taking into account all radicals R6, the proportion of C2H4O groups among the total of all radicals R6 does not exceed 40% by weight, a is from 2 to 30, b is from 2 to 50, c is from 2 to 40, and the sum (a+b+c) is from 6 to 100 and the sequence of the individual polyoxyalkylene segments —(C2H4O)a— and —(CH2—CH(CH3)O)b— and —(CH2CR9R10O)c— is either random or block or combination thereof, R8 is a hydrogen, a substituted or unsubstituted alkyl radical or an acyl radical, v is from 3 to 200, w is 0 or 1, x is 0 or 1, y is from 0 to 200, and, if y is 0, R1 and/or R7 are/is —[R4]w—[R5]x—R6—R8; whereby said polysiloxane block copolymer is greater than 90% by weight of all polysiloxane block copolymers in the defoaming composition.
  • 5. A coating material or a printing ink which comprises a coating material or a printing ink and a defoaming effective amount of a defoaming composition which comprises a water-insoluble polyoxyalkylene-polysiloxane block copolymer of the average general formula whereR1 and/or R7 are R2 or —[R4]w—[R5]x—R6—R8, R2 and R3 are identical or different alkyl radicals or are unsubstituted or substituted aryl radicals, R4 is a divalent radical of the formula —O—, —NH—, —NR2—, —S— or of the formula —[O—Si(CH3)2]u—, whereu is from 2 to 200, R5 is identical or different alkylene radicals having 1 to 24 carbon atoms, or is —CnH2n-fR2f—O—CmH2m-gR2g—, where, f is from 0 to 12, g is from 0 to 12, n is from 1 to 18, m is from 1 to 18, R6 is identical or different radicals of the general formula —O—(C2H4O)a(CH2—CH(CH3)O)b(CH2-CR9R10O)c—, whereR9 and R10 are a methyl radical, or R9 is a hydrogen atom and R10 is an ethyl radical, but where, taking into account all radicals R6, the proportion of C2H4O groups among the total of all radicals R6 does not exceed 40% by weight, a is from 2 to 30, b is from 2 to 50, c is from 2 to 40, and the sum (a+b+c) from 6 to 100 and the sequence of the individual polyoxyalkylene segments —(C2H4O)a— and —(CH2—CH(CH3)O)b— and —(CH2CR9R10O)c— is either random or block or combination thereof, R8 a hydrogen, a substituted or unsubstituted alkyl radical or an acyl radical, v is from 3 to 200, w is 0 or 1, x is 0 or 1, y is from 0 to 200, and, if y is 0, R1 and/or R7 are/is —[R4]w—[R5]x—R6—R8; whereby said polysiloxane block copolymer is greater than 90% by weight of all polysiloxane block copolymers in the defoaming composition.
Priority Claims (1)
Number Date Country Kind
199 22 352 May 1999 DE
RELATED APPLICATIONS

This application is a divisional of application U.S. Ser. No. 09/569,901, filed on May 11, 2000, now U.S. Pat. No. 6,433,028, and this application claims priority to German Application 199 22 352.1, filed May 14, 1999. These applications are both herein incorporated by reference.

US Referenced Citations (11)
Number Name Date Kind
2846458 Haluska Aug 1958 A
3402192 Haluska Sep 1968 A
3763021 Householder Oct 1973 A
4122029 Gee et al. Oct 1978 A
4130708 Friedlander et al. Dec 1978 A
4605712 Mueller et al. Aug 1986 A
4769174 Kilgour Sep 1988 A
4906707 Yukimoto Mar 1990 A
6001887 Keup et al. Dec 1999 A
6117963 Boinowitz et al. Sep 2000 A
6162888 Lee et al. Dec 2000 A
Foreign Referenced Citations (3)
Number Date Country
1 012 602 Jul 1957 DE
1 165 028 Sep 1964 DE
867 460 Mar 1998 EP
Non-Patent Literature Citations (2)
Entry
William C. Griffin, “Calculation of HLB Values of Non-ionic Surfactants”, The Journal of the Society of Cosmetic Chemists, vol. V., No. 4, pp. 249-256, Dec. 1954.
Koczo et al., “Mechanisms for Antifoaming Action in Aqueous Systems by Hydrophobic Particles and Insoluble Liquids”, Journal of Colloid and Interface Science, 166, pp. 225-238, 1994, month unknown.