Patent Application
20170287511
The present invention relates to data storage systems, and more particularly, this invention relates to heat assisted magnetic recording write heads having improved near field transducer (NFT) structure protection during use and methods for making the same.
The heart of a computer is a magnetic disk drive which typically includes a rotating magnetic disk, a slider that has read and write heads, a suspension arm above the rotating disk and an actuator arm that swings the suspension arm to place the read and/or write heads over selected data tracks on the rotating disk. The suspension arm biases the slider into contact with the surface of the disk when the disk is not rotating (in some disk drives, there is a load/unload ramp so contact with the disk does not occur); but, when the disk rotates, air is swirled by the rotating disk adjacent a media facing surface of the slider causing the slider to ride on an air bearing a slight distance from the surface of the rotating disk. When the slider rides on the air bearing the write and read heads are employed for writing magnetic impressions to and reading magnetic signal fields from the rotating disk. The read and write heads are connected to processing circuitry that operates according to a computer program to implement the writing and reading functions.
The ongoing quest for higher storage bit densities in magnetic media used in disk drives has reduced the size (volume) of data cells to the point where the cell dimensions are limited by the grain size of the magnetic material. Although grain size can be reduced further, there is concern that data stored within the cells is no longer thermally stable, as random thermal fluctuations at ambient temperatures are sufficient to erase data. This state is described as the superparamagnetic limit, which determines the maximum theoretical storage density for a given magnetic medium. This limit may be raised by increasing the coercivity of the magnetic medium or lowering the temperature. Lowering the temperature is not a practical option when designing hard disk drives for commercial and consumer use. Raising the coercivity is a practical solution, but requires write heads employing higher magnetic moment materials which will make data recording more challenging.
One solution has been proposed, which employs heat to lower the effective coercivity of a localized region on the magnetic medium surface and writes data within this heated region. The data state becomes “fixed” upon cooling the medium to ambient temperatures. This technique is broadly referred to interchangeably as “heat assisted magnetic recording”, HAMR, or “thermally assisted (magnetic) recording”, TAR or TAMR. HAMR can be applied to both longitudinal and perpendicular recording systems, although the highest density state of the art storage systems are more likely to be perpendicular recording systems. Heating of the media surface has been accomplished by a number of techniques such as focused laser beams or near field optical sources. U.S. Pat. No. 6,999,384 to Stancil et al., which is herein incorporated by reference, discloses near field heating of a magnetic medium.
The heat used in HAMR is provided by a plasmonic nanostructure, namely an NFT, which locally elevates a limited spot on the medium to its Curie temperature of about 600° C. Thus, the thermal and mechanical reliability of the NFT is important. However, the thereto-mechanical response of the NFT when exposed to such high temperatures leads to an undesirable protrusion of the plasmonic structure, thereby making the NFT the minimum fly point over the medium. This increases the risk of damage to the NFT resulting from disk contact during touchdown and the presence of high thermal asperities during back-off operations. However, previous attempts to protect NFTs from such damage have been unable to do so with a desired amount of efficiency.
A system, according to one embodiment, includes: a near field transducer, a return pole, a main pole, a waveguide adjacent the near field transducer, wherein the waveguide extends away from the near field transducer along a direction perpendicular to a media facing surface, at least one cladding layer adjacent to the waveguide, an underlayer positioned behind the near field transducer with respect to the media facing surface, the underlayer extending away from the near field transducer along the direction perpendicular to the media facing surface, and a fill material at least partially surrounding the underlayer, the waveguide and the at least one cladding layer. The underlayer has a lower coefficient of thermal expansion than the fill material.
A method, according to another embodiment, includes: applying light to a near field transducer positioned toward a media facing surface of a magnetic head, the magnetic head having: a return pole, a main pole, a waveguide adjacent the near field transducer, wherein the waveguide extends away from the near field transducer along a direction perpendicular to the media facing surface, at least one cladding layer adjacent to the waveguide, an underlayer positioned behind the near field transducer with respect to the media facing surface, the underlayer extending away from the near field transducer along the direction perpendicular to the media facing surface, and a fill material at least partially surrounding the underlayer, the waveguide and the at least one cladding layer. The underlayer has a lower coefficient of thermal expansion than the fill material Moreover, upon illumination of the near field transducer, a portion of the media facing surface of the magnetic head at the near field transducer exhibits less thermal protrusion toward a magnetic medium than another portion of the media facing surface.
Any of these embodiments may be implemented in a magnetic data storage system such as a disk drive system, which may include a magnetic head, a drive mechanism for passing a magnetic medium (e.g., hard disk) over the magnetic head, and a controller electrically coupled to the magnetic head.
Other aspects and advantages of the present invention will become apparent from the following detailed description, which, when taken in conjunction with the drawings, illustrate by way of example the principles of the invention.
For a fuller understanding of the nature and advantages of the present invention, as well as the preferred mode of use, reference should be made to the following detailed description read in conjunction with the accompanying drawings.
The following description is made for the purpose of illustrating the general principles of the present invention and is not meant to limit the inventive concepts claimed herein. Further, particular features described herein can he used in combination with other described features in each of the various possible combinations and permutations.
Unless otherwise specifically defined herein, all terms are to be given their broadest possible interpretation including meanings implied from the specification as well as meanings understood by those skilled in the art and/or as defined in dictionaries, treatises, etc.
It must also be noted that, as used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless otherwise specified.
The following description discloses several preferred embodiments of disk-based storage systems and/or related systems and methods, as well as operation and/or component parts thereof. Various embodiments described herein may be able to provide added protection for an NFT. By selectively implementing underlayers having certain properties, some of the embodiments described herein may be able to prevent an N/FT from becoming the minimum fly point over the medium, thereby desirably providing greater reliability during recording, as will be described in further detail below.
In one general embodiment, a system includes: a near field transducer, a return pole, a main pole, a waveguide adjacent the near field transducer, wherein the waveguide extends away from the near field transducer along a direction perpendicular to a media. facing surface, at least one cladding layer adjacent to the waveguide, an underlayer positioned behind the near field transducer with respect to the media facing surface, the underlayer extending away from the near field transducer along the direction perpendicular to the media facing surface, and a fill material at least partially surrounding the underlayer, the waveguide and the at least one cladding layer. The underlayer has a lower coefficient of thermal expansion than the fill material.
In another general embodiment, a method includes: applying light to a near field transducer positioned toward a media facing surface of a magnetic head, the magnetic head having: a return pole, a main pole, a waveguide adjacent the near field transducer, wherein the waveguide extends away from the near field transducer along a direction perpendicular o the media facing surface, at least one cladding layer adjacent to the waveguide, an underlayer positioned behind the near field transducer with respect to the media facing surface, the underlayer extending away from the near field transducer along the direction perpendicular to the media facing surface, and a fill material at least partially surrounding the underlayer, the waveguide and the at least one cladding layer. The underlayer has a lower coefficient of thermal expansion than the fill material. Moreover, upon illumination of the near field transducer, a portion of the media facing surface of the magnetic head at the near field transducer exhibits less thermal protrusion toward a magnetic medium than another portion of the media facing surface.
Referring now to
At least one slider 113 is positioned near the disk 112, each slider 113 supporting one or more magnetic read/write heads 121 (e.g., of a magnetic head). As the disk rotates, slider 113 is moved radially in and out over disk surface 122 so that heads 121 may access different tracks of the disk where desired data are recorded and/or to be written. Each slider 113 is attached to an actuator arm 119 by means of a suspension 115. The suspension 115 provides a slight spring force which biases slider 113 against the disk surface 122. Each actuator arm 119 is attached to an actuator 127. The actuator 127 as shown in
During operation of the disk storage system, the rotation of disk 112 generates an air bearing between slider 113 and disk surface 122 which exerts an upward force or lift on the slider. The air bearing thus counter-balances the slight spring force of suspension 115 and supports slider 113 off and slightly above the disk surface by a small, substantially constant spacing during normal operation. Note that in some embodiments, the slider 113 may slide along the disk surface 122.
The various components of the disk storage system are controlled in operation by control signals generated by control unit 129, such as access control signals and internal clock signals. Typically, control unit 129 comprises logic control circuits, storage (e.g., memory), and a microprocessor. The control unit 129 generates control signals to control various system operations such as drive motor control signals on line 123 and head position and seek control signals on line 128. The control signals on line 128 provide the desired current profiles to optimally move and position slider 113 to the desired data track on disk 112. Read and write signals are communicated to and from read/write heads 121 by way of recording channel 125.
The above description of a typical magnetic disk storage system, and the accompanying illustration of
In some embodiments, the disk drive 100 of
With continued reference to the disk drive 100 of
In a typical head, an inductive write head includes a coil layer embedded in one or more insulation layers (insulation stack), the insulation stack being located between first and second pole piece layers. A gap is formed between the first and second pole piece layers of the write portion by a gap layer at or near a media facing surface of the head (sometimes referred to as an air bearing surface in a disk drive) The pole piece layers may be connected at a back gap. Currents are conducted through the coil layer, which produce magnetic fields in the pole pieces. The magnetic fields fringe across the gap at the media facing surface for the purpose of writing bits of magnetic field information in tracks on moving media, such as in circular tracks on a rotating magnetic disk.
The second pole piece layer has a pole tip portion which extends from the media facing surface to a flare point and a yoke portion which extends from the flare point to the back gap. The flare point is where the second pole piece begins to widen (flare) to form the yoke. The placement of the flare point directly affects the magnitude of the magnetic field produced to write information on the recording medium.
In this structure, the magnetic lines of flux extending between the poles of the perpendicular head 218 loop into and out of the overlying coating 214 of the recording medium with the high permeability under layer 212 of the recording medium causing the lines of flux to pass through the overlying coating 214 in a direction generally perpendicular to the surface of the medium to record information in the overlying coating 214 of magnetic material preferably having a high coercivity relative to the under layer 212 in the form of magnetic domains having their axes of magnetization substantially perpendicular to the surface of the medium. The flux is channeled by the soft underlying coating 212 back to the return pole of the head 218.
Perpendicular writing is achieved by forcing flux through the stitch pole 308 into the main pole 306 and then to the surface of the disk positioned toward the media facing surface 318.
In
As previously mentioned, HAMR, or equivalently TAR, is a method of recording information onto a magnetic recording medium. One general motivation for this invention relates to the design of a recessed dielectric waveguide and integration with a near-field optical transducer for HAMR. The waveguide core may be optimally recessed by a distance from the transducer and this space may be filled with low index dielectric material, leading to significant enhancement of the optical efficiency. In one preferred embodiment, the low index dielectric material in the recessed space may be deposited after fabrication of the near-field transducer using an anisotropic deposition followed by deposition of the high index core material.
According to some embodiments, for HAMR to be effective, it may be beneficial to confine heat to about a single data track which may be approximately 40 nm wide or smaller. Candidate near-field optical sources typically use a low-loss metal (Au, Ag, Al, Cu, etc.) shaped in such a way as to concentrate surface charge motion at a tip apex located at the slider media facing surface when light is incident. Oscillating tip charge may create an intense near-field pattern, heating the disk. Sometimes, the metal structure can create resonant charge motion (surface plasmons) to further increase intensity and disk heating. For example, when polarized light is aligned with the corner of a triangular-shaped gold plate, an intense near field pattern may be created at that corner. Resonant charge motion may occur by adjusting the triangle size to match a surface plasmon frequency to the incident light frequency. Another near-field transducer is the notch slot waveguide from microwave circuits applied to optical frequencies (also known as the C aperture). Light polarization may be aligned with the notch and incident light may concentrate surface charge at the tip of the notch.
However, the thermo-mechanical response of the N/FT when exposed to such high temperatures has previously led to an undesirable protrusion of the plasmonic structure, thereby causing the NFT to become the minimum fly point over the medium. This increases the risk of damage to the NFT resulting from disk contact during touchdown and the presence of high thermal asperities during back-off operations. Thus, although minimal clearance (e.g., sub-nanometer clearance) between the head and disk is desired for high areal density in HAMR HDDs, large variations in NFT protrusion during operation has made clearance management for previous attempts very difficult.
Previous attempts to protect the NFT against such damage resulting from interaction between the NTT and the medium have been unable to do so with a desired amount of efficiency. For instance, attempts to preemptively recess the NFT from the media facing surface of a head have proven to be difficult to control due to thermal oxidation. Moreover, recessing the NFT undesirably results in requiring higher operating power to generate sufficient heat at the medium. In other instances, attempts have been made to implement a passive protection pad to prevent a protruded NFT from contacting the medium. However, the extent to which an NFT protrudes varies greatly during use, thereby making the passive protection pad potentially less effective.
In sharp contrast, various embodiments described herein prevent an NFT from becoming the minimum fly point over the medium during operation, thereby desirably providing greater reliability during recording. According to some approaches, NFT protrusion may he reduced by selectively implementing underlayers having reduced coefficients of thermal expansion, as will be described in further detail below.
It should be noted that the dimensions of the components illustrated in
Referring now to
The head 500 also includes an optical waveguide 506, surrounded by cladding layers 508, 510, 512. In various embodiments, the cladding layers 508, 510, 512 may include any material which would be apparent to one of ordinary skill in the art, such as
A12O3, SiO2 etc., and/or their composites. Moreover, the cladding layers 508, 510, 512 may include same, similar or different materials, depending on the desired embodiment.
According to the present embodiment, optical waveguide 506 and cladding layers 508, 510, 512 are adjacent the NFT 523 which is positioned toward a media facing surface 501 of the head 500. As shown, cladding layers 508, 510, 512 are adjacent to the waveguide 506 and the waveguide 506 is positioned behind a side of the NFT 523 farthest from the media facing surface. However, in other embodiments, the waveguide 506 and/or cladding layers 508, 510, 512 may be offset from the NFT 523 in the track direction T, e.g., for embodiments having a nanobeak antenna as would be appreciated by one skilled in the art upon reading the present description.
Moreover, the waveguide 506 and cladding layers 508, 510, 512 extend away from the NFT 523 along a direction H perpendicular to the media facing surface 501. It should be noted that although three cladding layers are shown in the present embodiment, any number of cladding layers may be included, but preferably at least one cladding layer is included.
In some approaches, the optical waveguide 506 may be spaced from the NFT by between about 100 nm and about 10 nm, but may be higher or lower depending on the desired embodiment. One of the cladding layers 510 forms a recess between the waveguide 506 and the NFT 523. Further, cladding layer 510 is also directly adjacent a side of the waveguide 506, e.g., extending parallel to a longitudinal axis of the waveguide 506 in the height direction H (a direction perpendicular to the media facing surface 501). Additionally, another one of the cladding layers 512 extends along a leading edge side of the NFT 523, thereby forming a portion of the media facing surface. Thus, in some embodiments, the waveguide 506 may be positioned adjacent two cladding layers 510, 512, e.g., as illustrated in FIG, 5A.
Optical waveguide 506 preferably extends to the flex side 514 as indicated by the dashed lines. Moreover, the cladding layers 508, 510, 512 are illustrated as extending to at least the flex side 514; although in other embodiments, some or all of the cladding layers may not extend to the flex side 514. The waveguide 506 extends to the flex side 514 having a near field optical source 516, e.g., a laser. The optical source 516 emits light, an optical signal, which is desirably directed along the optical waveguide 506, toward the NFT 523, Thus the waveguide 506 is generally used to deliver light energy to the NFT which creates a small hot-spot on the surface of the medium 528, thereby inducing isolated heating of the medium 528 surface. The waveguide 506 preferably includes a material having a high refractive index (e.g., at least higher than the cladding layers 508, 510, 512), thereby assisting in keeping the optical signal, emitted from the optical source 516, within the waveguide 506. Illustrative materials for the waveguide 506 include, but are not limited to, TaOx, TiOx, NbOx, ZrOx, HfOx, etc., and/or their composites. Other exemplary materials for the waveguide 506 may include Ta2O5, and/or TiO2.
The cladding layers 508, 510, 512 preferably include a material having a low refractive index, e.g., so as to keep the optical signal confined within the sidewalls of the waveguide. In general, a low refractive index material may include any material having refractive index below about 1.75, but could be higher or lower depending on the desired embodiment. In other approaches, the low refractive index may be lower than the refractive index of the waveguide 506. Illustrative materials for the cladding layers 508. 510, 512 include refractive oxides such as AlOx, SiOx, etc. or other conventional materials having a desirably low refractive index.
As shown, the waveguide 506 may have an approximately uniform cross section along its length. The thickness of the waveguide 506 may be nominally between about 200 nm and about 400 nm, but is preferably thicker than the aperture 524,
However, as well known in the art, the waveguide 506 may have a number of other possible designs including a planar solid immersion mirror or planar solid immersion lens which have a non-uniform core cross section along the waveguide's length. Thus, according to various approaches, the waveguide 506 may have any other cross sectional profile as selected by one of ordinary skill in the relevant art, such as a rectangular, square, triangular, circular, etc., cross section.
With continued reference to
It is also preferred that the magnetic lip 522 has a straight and substantially vertical (perpendicular to the plane of deposition) back edge 521, e.g., farthest from the media facing surface of the head 500. Various methods of forming the magnetic lip 522 capable of achieving a substantially vertical back edge 521 may be implemented to manufacture head 500, as would be appreciated by one skilled in the art upon reading the present description.
Additionally, the NFT 523 is illustrated in the present embodiment as including an aperture 524 (e.g., a C aperture) and a conductive metal film main body 526 therebelow, which is in no way intended to limit the invention. Rather, it should be noted that NFT 523 may be of any conventional design, such as an E-antenna, a lollipop, triangular, nanobeak, etc. According to one approach, the aperture 524 may include SiO2.
Looking to the media facing surface view in FIG, SB, the main body 526 is shown as having a notch 527 extending therefrom. The aperture 524 is illustrated as having a “C-shaped” structure, formed by the conductive metal film main body 526 and notch 527 therebelow. However, depending on the desired embodiment, the conductive metal film main body 526 may have any shape. According to one example, the conductive metal film main body 526 may have a circular cross sectional shape with a notch extending therefrom, e.g., as would be appreciated by one skilled in the art as a “lollipop antenna.” it follows that the NFT 523 may be part of an E-antenna, a nanobeak antenna, a lollipop antenna, etc., depending on the desired embodiment.
It follows that the partial cross sectional view of the head 500 in
Referring still to FIG. SA, the aperture 524 and conductive metal film main body 526 of the NFT 523 may be used to assist in performing write operations. As described above, an NFT may be used to heat the magnetic medium, thereby softening the magnetic stability of the magnetic grains thereof. The energy to heat the magnetic medium may be supplied to the NFT 523 from the optical source 516 via the waveguide 506. In preferred embodiments, this allows for the magnetic field concentrated at the magnetic lip 522 to influence the magnetic orientation of the magnetic grains on the medium 528, to perform a write operation. Therefore, it is desirable that the NFT is located adjacent the magnetic lip 522, e.g., as illustrated in FIG. SA.
However, as the NFT 523 is used to heat the magnetic medium, e.g., while performing HAMR, heat is also transferred to the NFT 523 itself and surrounding layers of the head 500, thereby causing them to expand. As mentioned above, the thereto-mechanical response of the NFT when exposed to such high temperatures has previously led to an undesirable protrusion of the plasmonic structure, thereby making the NFT the minimum fly point over the medium during use. This increases the risk of damage to the NFT resulting from disk contact during touchdown and the presence of high thermal asperities during back-off operations. Thus, although minimal clearance (e.g., sub-nanometer clearance) between the head and disk is desired for high areal density in HAMR HDDs, large variations in NFT protrusion during operation has made clearance management for previous attempts significantly difficult.
Previous attempts to protect the NFT against such damage resulting from interaction between the NFT and the medium have significant disadvantages. However, in sharp contrast to previous designs, some of the embodiments described herein are able to reduce NFT protrusion relative to other portions of the writer by selectively implementing underlayers having reduced coefficients of thermal expansion. As a result, the amount of thermal expansion experienced at the media facing surface by the NFT may be selectively reduced, thereby preferably causing the media facing surface at the NFT to exhibits less thermal protrusion toward a magnetic medium than another portion of the media facing surface, as will be described in further detail below.
Referring still to head 500, an underlayer 530 is preferably included at and/or behind the NFT 523 with respect to the media facing surface 501. As will be described in further detail below, the underlayer 530 preferably has one or more materials having a low coefficient of thermal expansion, e.g., at least with respect to that of the fill material 520. Thus, by positioning the underlayer 530 at and/or behind the NFT 523, some of the embodiments may effectively reduce the amount of thermal expansion experienced at and/or near the NFT 523. As a result, this may desirably result in the NFT 523 exhibiting less thermal protrusion toward a magnetic medium than another portion of the media facing surface 501, such as the main pole tip and/or return pole tip.
Underlayer 530 is preferably positioned such that the NFT 523 is at least partially sandwiched between the underlayer 530 and the media facing surface 501. Thus, as shown in
The underlayer 530 may further surround at least a portion of the NFT 523 in some approaches. Thus, at least a portion of the underlayer 530 may extend to the media. facing surface 501, e.g., as shown in
Therefore, it should also be noted that although the underlayer 530 is shown in FIG. SA as extending away from the NFT 523 along the height direction H to the return pole 502 (at the yoke), the underlayer 530 may extend beyond the return pole in some approaches, or may not extend all the way to the return pole 502 in other approaches. The underlayer 530 preferably has a height of less than about 15 microns, e.g., 10 microns, measured in the height direction H. Moreover, the underlayer 530 may have a width of less than about 2 microns, e.g., 1 micron, measured in a direction perpendicular to a plane formed by the intended direction of media travel and the height direction. The underlayer 530 also preferably has a thickness of less than about 5 microns, more preferably less than about 4 microns, e.g., 2 microns, measured along the track direction T, but may be thicker depending on the desired embodiment. For example, portions the underlayer 530 may have a thickness of greater than 5 microns in embodiments having a waveguide and/or cladding layers offset from the NTT, such as in embodiments having a nanobeak antenna. Moreover, the underlayer 530 may be formed using sputtering, masking, milling, etc., or other conventional processes which would be apparent to one skilled in the art upon reading the present description.
As shown in the present embodiment, fill material 520 has been deposited such that it surrounds a number of components of the head 500, including the write coils 518. Additionally, fill material 520 is positioned in a space defined between the return pole 502 and the main pole 504. Thus, the fill material 520 may at least partially surround the underlayer 530, the waveguide 506 and cladding layers 508, 510, 512.
As described above, the underlayer 530 preferably has a lower coefficient of thermal expansion than the fill material 520. Thus, during operation of the head 500, the underlayer 530 will expand less than the fill material 520, thereby preferably causing the media facing surface 501 at the NFT 523 to exhibit less thermal protrusion toward a magnetic medium 528 than another portion of the media facing surface 501, e.g., affected by the higher amount of thermal expansion experienced by the fill material 520. As a result, the reduced thermal expansion experienced by the underlayer 530 prevents the NFT 523 from becoming the minimum fly point over the medium during operation, thereby desirably providing greater reliability during recording. Again, it is preferred that the underlayer 530 is positioned at and/or behind the NFT 523. In other words, it is preferred that the underlayer 530 is present in an NFT region which at least partially surrounds the NFT 523 and/or extends behind the NFT 523 in the height direction H.
The inventors also discovered that implementing an underlayer 530 having a higher thermal conductivity than that of the fill material 520 may provide additional performance improvements. Materials having higher thermal conductivity are able to better dissipate the heat, thereby allowing underlayer 530 to more effectively diffuse the heat generated at the NFT 523 during use, and further reduce the amount of thermal protrusion experienced by the media facing surface 501 at about the NFT 523.
According to an exemplary approach, till material 520 may include alumina and/or other conventional insulation materials. Moreover, depending on the desired embodiment, underlayer 530 preferably includes one or more materials having a low coefficient of thermal expansion, such as fused silica (e.g., amorphous fused silica), aluminum nitride, silicon nitride, silicon carbide, etc. Underlayer 530 also preferably has a higher coefficient of thermal conductivity than that of the fill material 520, e.g., which may be alumina. Table 1 below illustrates the difference between the coefficient of thermal expansion for alumina compared to that of exemplary underlayer materials. The coefficient of thermal conductivity is also shown for each of the respective materials.
As shown, the coefficient of thermal expansion for alumina is much higher than each of the coefficients of thermal expansion for fused silica, aluminum nitride, silicon nitride and silicon carbide respectively, thereby illustrating the difference in thermal expansion experienced by the different materials. Additionally, the thermal conductivity coefficient of aluminum nitride, silicon nitride and silicon carbide is greater than that of alumina, thereby providing a greater amount of heat dispersion than alumina. It should also be noted that the specific underlayer materials listed herein are in no way intended to limit the invention.
Looking to
As shown, the maximum protrusion, which directly corresponds to the minimum fly point over the medium, for a magnetic head without an underlayer and exposed to 16 mW is at the NFL In other words, the maximum amount of thermal protrusion experienced by the media facing surface of the magnetic head without an underlayer is undesirably at the NFT. Conversely, after adding an underlayer having fused silica, the minimum fly point for the magnetic head shifts to a different portion of the media facing surface when exposed to the same energy level of 16 mW. In other words, adding a fused silica underlayer caused the NFT to protrude less, and thereby be recessed with respect to a different portion of the media facing surface experiencing a greater amount of thermal expansion, e.g., caused by the fill material having a higher coefficient of thermal expansion than the underlayer. As a result, the NFT is protected from damage during use, while writing to a magnetic medium.
Moreover, similar results were obtained when modeling the exposure of the same two head designs to a higher energy level of 24 mW. follows that by implementing an underlayer having a coefficient of thermal expansion which is lower than a surrounding fill material, the NFT remains protected under a range of operating conditions, e.g., light energy levels. Operating temperatures of the NFT and surrounding materials may vary greatly during use, and various embodiments described herein desirably ensure continued protection for the NFT despite such fluctuations in operating temperatures, which was not previously achievable, e.g., by pre-recessing the NFT region of the media facing surface.
Although preventing the NFT from becoming the minimum fly point over the medium during operation is desired to avoid head-disk interference (HDI), it is also preferred that the NFT does not become over recessed from the medium. As the NFT is moved farther away from medium, the NFT has less of an effect on the magnetic medium as there is more separation between the NFT and the target (the focused spot on the medium). Thus, the protection afforded by recessing the NFT from the minimum fly point may be weighed against the corresponding loss of write detail when determining a. desired amount of separation between the NFT and the medium. However, it is preferred that the NFT 523 is at least recessed enough to prevent it from becoming the minimum fly point over the medium during operation.
According to an exemplary in-use embodiment of the magnetic head 500 having an underlayer structure which is at least partially surrounded by fill material in
As a result of being illuminated by the light delivered by the waveguide 506, the NFT 523 creates a small hot-spot on the surface of the magnetic medium 528, thereby inducing isolated heating of the medium 528 surface. However, the NFT 523 itself and surrounding materials are also heated by the light energy during operation, thereby leading to protrusion of the media facing surface 501 as a result of thermal expansion. Underlayer 530 helps disperse heat away from the NFT 523 while also minimizing the amount of thermal expansion experienced by the media facing surface 501 at he NFT 523.
It follows that various embodiments described herein may be able to provide added protection for an NFT during operation. By optimizing the size and material properties of one or more underlayer positioned at and/or behind the NFT, protrusion thereof at the media facing surface may be selectively reduced. Moreover, reducing the amount of thermal expansion experienced at about the NFT prevents the NFT from becoming the minimum fly point over the medium during operation, thereby desirably providing greater reliability during recording. Furthermore, implementing materials having increased thermal conductivity at and/or behind the NFT may further improve performance of a magnetic head.
Moreover, any of the approaches described and/or suggested herein may be implemented in embodiments having nanobeak antenna configurations of types known in the art. Thus, process flow(s) similar to and/or the same as any of the embodiments included herein may produce desirable performance results for nanobeak antennas. Further still, various approaches described and/or suggested herein may be implemented in embodiments having front and/or back edge profiles of an NFT antenna which are different than that of a magnetic pole.
It should be noted that methodology presented herein for at least some of the various embodiments may be implemented, in whole or in part, in computer hardware, software, by hand, using specialty equipment, etc, and combinations thereof.
Moreover, any of the dimensions described herein with regard to any of the FIGS. and/or any other embodiment thereof, may be higher or lower than the values listed, depending on the particular sizes and shapes of components in such particular embodiments/,
While various embodiments have been described above, it should be understood that they have been presented by way of example only, and not limitation. Thus, the breadth and scope of an embodiment of the present invention should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.