The invention generally relates to perforating tools used in downhole operations, and more particularly to apparatus and methods for improving perforation in a downhole.
After a well has been drilled and casing has been cemented in the well, one or more sections of the casing adjacent to formation zones may be perforated to allow fluids from the formation zones to flow into the well for production to the surface or to allow injection fluids to be applied into the formation zones. A perforating gun string may be lowered into the well to a desired depth, and the guns fired to create openings in the casing and to extend perforations into the surrounding formation.
Shaped charges are commonly used in perforating guns to create openings in the casing and channels in the formation zones. To yield best results for deep penetration, shaped charge liners may be made of pure metals due to their great density and ductility. However, liners made of pure metals may form slug that remains in the penetration channels. As a result, the penetrated hole can be plugged, which may interfere with the influx of production fluids, e.g., oil. To overcome this problem, liners used for downhole operations may be made of metal powders, such as pseudo-alloys. If unsintered, the liners may yield jets that are mainly composed of dispersed fine metal particles. To enhance penetration, powdered metal liners may contain high density metal powders, such as tungsten powders (mass density=19.3 g/cm3), as major components.
U.S. Pat. No. 7,811,354, issued to Leidel et al., discloses the use of a liner for a shaped charge having a high performance powdered metal mixture to achieve improved penetration depths during the perforation of a wellbore. This mixture includes powdered tungsten (92-99%), powdered metal binder (1-8%), and a lubricant, such as graphite, which can be compressively formed into a substantially conically shaped liner.
U.S. Pat. No. 6,564,718, issued to Reese et al., discloses a liner for a shaped charge formed from a mixture of powdered heavy metal and a powdered metal binder. The liner is formed by compression of the mixture into a liner body shape. The mixture contains a range of 90 to 97 percent by weight of powdered heavy metal, and 3 to 10 percent by weight of the powdered metal binder. Specifically, the preferred powdered heavy metal is tungsten, and the preferred powdered metal binder is copper. A lubricant, such as graphite powder or oil, can be intermixed with the powdered metal binder to aid in the formation of the shaped charge liner.
Although these approaches improve the performance of shaped charges, further improvements to methods for fabricating shaped charges that can achieve better penetration in downhole operations would be useful.
This summary is provided to introduce a selection of concepts that are further described below in the detailed description. This summary is not intended to identify key or essential features of the claimed subject matter, nor is it intended to be used as an aid in limiting the scope of the claimed subject matter.
An embodiment of the present disclosure relates to methods for perforating wells. A method in accordance with one embodiment includes positioning a perforating gun in the well and detonating the shaped charge in the well. The perforating gun includes a shaped charge that includes a casing, a liner disposed within an opening of the casing, and an explosive disposed between the casing and the liner. The liner is made of a metal powder blend having a spheroidized metal powder. The spheroidized metal powder includes a spheroidized tungsten powder. The metal powder blend may further include a binder and a lubricant. The binder may include copper or lead. The lubricant may include zinc, tin, aluminum, nickel, antimony, cobalt, zinc alloys, tin alloys, aluminum alloys, or graphite.
Other aspects and advantages of the invention will be apparent from the following description and the appended claims.
Embodiments of utilization of spheroidized tungsten in shaped charge systems are described with reference to the following figures. The same numbers are used throughout the figures to reference like features and components.
Disclosed embodiments relate to shaped charges and methods for fabricating and using the same. Specifically, embodiments relate to shaped charges having liners made of a material comprising spheroidized metal powders (e.g., tungsten powders) for improving fabrication of shaped charges and for improving their performance. For clarity of illustration, the following description may use spheroidized tungsten powders as examples. However, one skilled in the art would appreciate that this description is equally applicable to other spheroidized metal powders known in the art, such as spheroidized molybdenum powders, spheroidized niobium powders, spheroidized tantalum powders, and spheroidized rhenium powders, and a combination thereof. In addition, the following description uses examples having spheroidized metal powders incorporated into shaped charge liners. However, one skilled in the art would also appreciate that spheroidized metal powders may also be incorporated into casings, and a combination of casings and liners.
Perforating gun 106 has perforating charges that are in the form of shaped charges 112. Shaped charges 112 may be mounted on or otherwise carried by a carrier 111 of perforating gun 106, in which carrier 111 may be a carrier strip, a hollow carrier, or other type of carrier. Perforating gun 106 may be fired to create openings in casing 104 and to extend perforations into the surrounding formation 114.
Liner 28 may be made of any suitable materials, including metals, graphite, and ceramic. Upon detonation of a shaped charge, the liner collapses and plastically deforms into a jet of material traveling at high speed to penetrate the target. Because the depth of penetration depends on the density of the penetration jet, the density in part dependent on the liner material, deep penetrations may be achieved by using liners containing dense metals, such as tungsten and lead.
Although pure solid metal liners may generally yield good results for deep penetration due to their higher density and ductility, the residue of the penetration jet may plug the newly created hole, thereby impeding influx of production fluid. In addition, adequate jet formation may not be achieved for pure solid metal liners owing to the lack of a stand-off between the charge and the gun wall and/or well casing. To overcome this problem, liner 28 may be formed by molding, under very high pressure, powdered metal mixture, into a conical shaped rigid body. In operation, when high explosive powders 24 is detonated using detonating cord 26, the force of the detonation collapses liner 28 causing liner 28 to be ejected in the form of a jet traveling at very high speed. These jets can penetrate casing, cement, and formation, thereby forming perforations.
As mentioned above, technology behind deep-penetrating shaped charges may rely on liners made of high density metal powders. Due to the high density associated with tungsten powders, deep penetration may be achieved by using tungsten powders or tungsten alloy as major components of shaped charge liners. Generally, the higher the tungsten content the deeper the penetration will be.
Tungsten powders may be produced by chemically decomposing mineral or ore concentrates of tungsten to produce high purity tungsten or tungsten oxide. Tungsten oxide can be hydrogen-reduced to pure tungsten powders. These tungsten powders are referred to as “as-reduced, irregular tungsten powders” or “normal tungsten powders.” Normal tungsten powders generally have polycrystalline structure, as shown in
To improve fabrication of shaped charges with tungsten powders, shaped charges can contain a form of tungsten, i.e., “spheroidized” or “spray densified” tungsten powders, which improves liner powder flow characteristics. For this purpose, other spheroidized metal powders may also be used, such as spheroidized molybdenum powders, spheroidized niobium powders, spheroidized tantalum powders, and spheroidized rhenium powders, and a combination thereof.
As used herein, the term “spheroidized” metal powders means metal powders having a spherical or substantially spherical shape, such as spheroidized tungsten powders shown in
Spheroidized tungsten powders may be made by any methods known in the art. The starting materials can include tungsten powders that have irregular or polycrystalline shapes. By entraining the irregular shaped particles of normal tungsten powders in an inert gas stream and passing the particles through a high temperature plasma gun or plasma flame (Tflame>4,000° C.), the irregular tungsten particles or powders (Tmelting˜3,700° C.) will be at least partially melted as they pass through the plasma gun to form molten droplets. These droplets may rapidly cool and solidify while in free-fall (as they exit the plasma gun), resulting in substantially spherical or spherical tungsten powders/particles that are amorphous (i.e., non-crystalline).
Spheroidized tungsten powders have a dramatically improved flowability and a higher bulk density. For example, Table 1 shows that both the flowability and bulk density of spheroidized tungsten powders (Spheroidized M65 Grade Tungsten) increase, as compared to those of normal tungsten (M65 Grade Tungsten). Specifically, the Hall flow rate of Spheroidized M65 Grade Tungsten powders is much higher and it takes 7 s for 50 g to flow, whereas there is no flow for M65 Grade Tungsten powders. Hall flow rate measures the ability of a powder to flow through a Hall funnel as described in ASTM Test Method B 213. The Hall flow rate is a function of inter-particle friction. As the friction increases, the Hall flow rate decreases. The spheroid shape greatly reduces the friction between the particles, thereby increasing the Hall flow rates of spheroidized tungsten particles.
In addition, the bulk density of Spheroidized M65 Grade Tungsten powders (9.76 g/cc) is higher than that of M65 Grade Tungsten powders (˜5.5 g/cc). These improved features (both increased density and increased Hall flow rate) of spheroidized tungsten powders would dramatically improve manufacturability of these powders and the shaped charges made of this material would have improved performance. The improved manufacturability of these powders makes it easier to make shaped charges and less likely to cause tool wear. The high bulk density of this material will produce shaped charges with improved properties, such as increased penetration.
Spheroidized tungsten powders would enhance the flowability of liner powder blends, which would result in improved malleability of spheroidized tungsten metal powder blends. The enhanced flowability characteristics of metal powder blends containing spheroidized tungsten powders may enable the fabrication of shaped charge liners or any parts of shaped charges with a high tungsten content, such as greater than 80%, 85%, 90%, 95%, or 99% by weight (wt %) of liners.
Embodiments include shaped charges having liners made of a metal powder blend comprising spheroidized tungsten powders, as well as shaped charges having liners that contain normal tungsten powders and spheroidized tungsten powders—i.e., regular tungsten powders may be completely or partially replaced with spheroidized tungsten powders.
Embodiments include shaped charges having spheroidized tungsten powders incorporated into liners and/or casing. Some embodiments relate to methods for manufacturing a shaped charge as described above.
One skilled in the art would appreciate that the method 50 shown in
Enhanced flowability of liner powder blends containing spheroidized tungsten powders may reduce the possibility of having batch-to-batch variation, which is sometimes observed in shaped charge liners made of normal tungsten powders. Reducing such a variation may improve the efficiency of producing shaped charges and minimize variability in shaped charge quality.
Due to high density of tungsten, it is particularly suitable for fabricating deep-penetrating shaped charges in downhole operations. The spheroidized tungsten particles further imparts desirable properties to this metal for use in shaped charges. For example, spheroidized tungsten powders in liners may improve both the transmission of detonation energy through liners and the manner by which liner particles feed into a shaped charge jet. Furthermore, the higher bulk density of the spheroidized tungsten powders may contribute to deeper penetration.
The performance of shaped charges with liners made of spheroidized tungsten powders have been examined. For example, the spheroidized tungsten powders are used to make PowerJet Omega 2906 charges. These shaped charges are found to have higher performance than regular shaped charges having normal tungsten powders. Tests have also been conducted that utilized design-of-experiment techniques to optimize the following parameters: percentage of spheroidized tungsten powder in liners and liner weight, among other parameters. The test results show that shaped charges with optimized parameters yield an average QC shot penetration of 34.5-inch using 28-g liners that contained 15% spheroidized tungsten. In contrast, shaped charges with normal tungsten powders in liners (similar to those used in current technology) yield an average of 30.5-inch penetration. In other words, there is 13% improvement in performance of shape charges having spheroidized tungsten powders over shaped charges used in current technology.
Perforating devices, such as perforating guns, using shaped charges that contain spheroidized tungsten powders according to some embodiments may be used in perforating operations. For example,
Advantages of embodiments may include one or more of the following. Spheroidized tungsten may have the potential to enhance shaped charge performance characteristics by improving both the transmission of detonation energy through the liner and the manner by which the liner particles feed into a shaped charge jet. The increased bulk density would also enhance the penetration. Thus, some embodiments can produce deeper-penetrating shaped charges by fully or partially substituting spheroidized tungsten for regular tungsten. The enhanced flowability also enables the production of liners that have an ultra-high tungsten content. Thus, some embodiments may have shaped charges with liners containing ultra-high content of tungsten, as in the next generation deep-penetrating shaped charges. The spheroidized tungsten would enable charge performance characteristics to be maintained with a lower overall tungsten content, which would permit a greater control of charge performance variability. Thus, some embodiments include shaped charges with liners containing less tungsten and yet maintaining the performance characteristics. The enhanced flowability of spheroidized tungsten results in less-abrasive liner powder blends, which would extend liner fabrication tool lives and reduce the variability in liner quality. The spheroidized tungsten may reduce the batch-to-batch variation of tungsten, which may be detrimental to shaped charge production efficiency and may impart variability to shaped charge quality. Thus, some embodiments would be easier to manufacture, and the reduced wear on tools and less variability may translate into lower costs of the shaped charges.
Although only a few example embodiments have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the example embodiments without materially departing from utilization of spheroidized tungsten in shaped charge systems. Accordingly, all such modifications are intended to be included within the scope of this disclosure as defined in the following claims. In the claims, means-plus-function clauses are intended to cover the structures described herein as performing the recited function and not only structural equivalents, but also equivalent structures. Thus, although a nail and a screw may not be structural equivalents in that a nail employs a cylindrical surface to secure wooden parts together, whereas a screw employs a helical surface, in the environment of fastening wooden parts, a nail and a screw may be equivalent structures. It is the express intention of the applicant not to invoke 35 U.S.C. § 112, paragraph 6 for any limitations of any of the claims herein, except for those in which the claim expressly uses the words ‘means for’ together with an associated function.
The patent application is a divisional of, and claims priority to, U.S. Non-Provisional application Ser. No. 13/494,419, entitled “Utilization of Spheroidized Tungsten in Shaped Charge Systems”, filed on Jun. 12, 2012.