UV curable paint compostions and method of making and applying same

Abstract

The present invention discloses an ultraviolet light curable paint composition and method for applying and making such a composition to a substrate. Suitable substrates include glass, metals, and various plastics such as polycarbonates. The disclosed composition does not contain any significant amount of volatile organic solvents that do not become incorporated in the coating or are released to ambient after curing.

Description

TECHNICAL FIELD

[0002] The present invention relates to ultraviolet light (UV) curable paint compositions capable of producing coating with enhanced corrosion and weathering resistance; and in particular to UV curable compositions capable of producing paint coatings on a substrate.

BACKGROUND OF THE INVENTION

[0003] UV radiation curable paint compositions are applied to a substrate through spraying, screen printing, dipping or brushing for the protection or decoration of the substrate. In the usual application, a substrate such as metal, glass, or plastic is coated with the paint composition and then UV light is introduced to complete the curing process. The UV curable paint compositions offer many advantages over typical heat curable compositions.

[0004] Heat curable compositions require the use of organic solvents that contain a significant amount of volatile organic compounds (VOCs). These VOCs escape into the atmosphere while the heat curable composition dries. Such solvent based systems are undesirable because of the hazards and expenses associated with VOCs. The hazards include water and air pollution and the expenses include the cost of complying with strict government regulation on solvent emission levels. In contrast, UV curable compositions contain reactive monomers instead of solvents; thus eliminating the detrimental effects of the VOCs.

[0005] Although, the use of heat curable compositions raises environmental concerns, other disadvantages exist with their use as well. Heat curable compositions suffer from slow cure times which lead to decreased productivity. These compositions require high energy for curing due to energy loss as well as the energy required to heat the substrate. Additionally, many heat curable compositions yield poor film properties that result in decreased value of the end product.

[0006] Although UV curable compositions exhibit superior properties and performance over their heat curable counterparts, UV curable compositions themselves suffer from certain disadvantages. Generally, UV compositions have high molecular weights and a substantial degree of cross linkage due to the highly reactive nature of the composition. As a result, many of these compositions suffer from low durability and resin shrinkage. With the use of many such compositions, an inordinately high amount of UV light is required to cure. New formulations that lessen these problems typically suffer from diminished abrasion, chemical, and scratch resistance as well as low thermal stability and adhesion.

[0007] An additional disadvantage of typical UV compositions is their lack of stability which results in dispersion. With some compositions, suspended solids fall out of solution after a period of one to two days. Dispersion adversely affects the gloss and clarity of the finished product. To combat this problem, new compositions have been formulated with higher viscosities which often lessen the flowability of the composition. These viscous formulations rule out spray application and provide for an unsuitably high dipping thickness.

[0008] Accordingly, there exists a need to provide environmentally safe UV curable paint compositions which exhibit improved appearance, weatherability, corrosion resistance and workability. Additionally, there is a need to provide a method of applying an improved composition which furthers the goal of improved performance.

SUMMARY OF INVENTION

[0009] It is an object of the present invention to provide an improved paint composition that is curable by ultraviolet light.

[0010] It is another object of the present invention to provide an improved paint composition that can be applied by spraying, screen printing, dipping, and brushing.

[0011] It is yet another object of the present invention to provide an improved paint composition that is capable of protecting metal surfaces from chemical corrosion and weathering.

[0012] It is still another object of the present invention to provide an improved paint composition that can be used to coat the metal parts in the undercarriage of an automobile.

[0013] It is still another object of the present invention to provide an improved paint composition that comprises at least one aliphatic acrylated oligomer that can be used to coat a metallic substrate such that no significant amount of volatile organic solvents do not become incorporated in the coating after the composition is cured.

[0014] The present invention discloses an ultraviolet light curable paint composition and method for making such a composition that may be used to produce a paint coating on a substrate. The disclosed composition does not contain any significant amount of volatile organic solvents that do not become incorporated in the coating after curing. Specifically, the paint composition contains 5% or less volatile organic solvents by weight. The disclosed invention provides a paint composition that is capable of protecting metal parts from chemical corrosion and weathering. In particular, automobile undercarriage components that are coated with the disclosed paint composition and then cured with ultraviolet light experience improved protection from the harmful effects of salt and adverse weather conditions. Further, the cured paint composition produces a coating with improved appearance and with improved resistance to rubbing off. Automobile undercarriage components include, but are not limited, to suspension swing arms, coil spring brackets, suspension stabilizers, frames, axles, and brake arms. The disclosed invention allows these automobile components to be coated more economically than the standard electronic primer coat basecoat and powder coat that is traditionally used in coating automobile undercarriage components.

[0015] In accordance with one aspect of the invention, an ultraviolet light curable paint composition is provided. The paint composition comprises a mixture of one or more aliphatic acrylated oligomers, wherein the aliphatic acrylated oligomer mixture is present in an amount of about 8% to 60% of the paint composition. All percentages of the paint composition as expressed in this document refer to the weight percentage of the stated component to the total weight of the paint composition.

[0016] The paint composition preferably further comprises an isobornyl acrylate monomer in an amount of about 20% to 60% of the paint composition, a photoinitiator in an amount of about 1% to 16% of the paint composition, a pigmented composition in an amount of 0% to 50%, an optional flow promoting agent in an amount of about 0.1% to 6% of the paint composition, and an optional adhesion promoter in an amount of 1% to 12%.

[0017] In accordance with yet another aspect of the invention, a method is provided for depositing or applying a paint coating on a substrate. The method comprises a first step of applying to the substrate a paint-containing fluid-phase composition (“paint composition”). Suitable methods of applying the paint composition to the substrate include spraying, screen-printing, dipping, and brushing. The paint composition comprises a mixture of aliphatic acrylated oligomers, wherein the aliphatic acrylated oligomer is present in an amount of about 8% to 60% of the paint composition. The paint composition also includes an isobornyl acrylate monomer in an amount of about 20% to 60% of the paint composition, a photoinitiator in an amount of about 1% to 16% of the paint composition, a flow promoting agent in an amount of about 0.1% to 6% of the paint composition, a pigmented composition in an amount of 0% to 50% of the paint composition, and optionally an adhesion promoter in an amount of 1% to 12%.

[0018] The method also includes a second step of illuminating the paint composition on the substrate with an ultraviolet light to cause the paint composition to cure into the paint coating.

[0019] In accordance with this method, the paint composition can be selectively deposited on the substrate at specific locations where paint plating is desired. The paint composition need not be applied to the entire substrate.

BEST MODE FOR CARRYING OUT THE INVENTION

[0020] Paint Compositions

[0021] Reference will now be made in detail to presently preferred compositions or embodiments and methods of the invention, which constitute the best modes of practicing the invention presently known to the inventor.

[0022] The term “alkyl” means a straight or branched hydrocarbon radical having from 1 to 12 carbon atoms and includes, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, undecyl, dodecyl, and the like.

[0023] The term “cycloalkyl” means a saturated hydrocarbon ring which contains from 3 to 20 carbon atoms, for example, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, adamantyl, isobornyl, and the like. Cycloalkyl also includes multicycyclic groups such as bicyclic and tricyclic alkyl groups.

[0024] The term “cycloalkenyl” means hydrocarbon ring having at least one unsaturation which contains from 5 to 20 carbon atoms. Cycloalkenyl also includes multicycyclic groups such as bicyclic and tricyclic groups having at least one unsaturation.

[0025] The terms “alkoxy” and “thioalkoxy” are O-alkyl or S-alkyl as defined above for alkyl.

[0026] The term “aryl” means an aromatic radical. Example of aryl include a phenyl group, a naphthyl group, a phenyl group substituted by 1 to 4 substituents selected from alkyl as defined above, alkoxy as defined above, thioalkoxy as defined above, hydroxy, halogen, trifluoromethyl, amino, alkylamino as defined above for alkyl, dialkylamino as defined for alkyl, N-acetylamino, cyano —SO2NH2, or nitro, or a naphthyl group substituted by 1 to 4 substituents as defined above for a phenyl group substituted by 1 to 4 substituents.

[0027] The term “acrylated aliphatic oligomer” means acrylic acrylates, amine modified polyether acrylates, chlorinated polyester acrylates, melamine acrylates, polybutadiene acrylates, polyester acrylates, polyether acrylates, and urethane acrylates that do not contain an aryl group. Epoxy acrylates, silicon acrylates, and fluorinate acrylates are not included in the definition of acrylated aliphatic oligomer.

[0028] In accordance with one aspect of the invention, a presently preferred ultraviolet light curable paint composition (“paint composition”) is provided. In this preferred embodiment, the paint composition includes a mixture of aliphatic acrylated oligomers. The aliphatic acrylated oligomer mixture is present in an amount of about 8% to 60% of the paint composition. If the paint composition is applied by spraying, the aliphatic acrylated oligomer mixture is more preferably present in an amount of about 30% to 55%, and most preferably about 45%. If the paint composition is applied by screen printing, the aliphatic acrylated oligomer mixture is more preferably present in an amount of about 8% to 60%, and most preferably about 50%. The aliphatic acrylated oligomer preferably comprises one or more urethane oligomers. Suitable aliphatic acrylated oligomers include Radcure Ebecryl 244 (aliphatic urethane diacrylate diluted 10% with 1,6-hexanediol diacrylate), Ebecryl 264 (aliphatic urethane triacrylate diluted 15% with 1,6-hexanediol diacrylate), Ebecryl 284 (aliphatic urethane diacrylate diluted 10% with 1,6-hexanediol diacrylate) commercially available from Radcure UCB Corp. of Smyrna, Ga.; Sartomer CN-961E75 (aliphatic urethane diacrylate blended with 25% ethoxylated trimethylol propane triacylate), CN-961H81 (aliphatic urethane diacrylate blended with 19% 2(2-ethoxyethoxy)ethyl acrylate), CN-963A80 (aliphatic urethane diacrylate blended with 20% tripropylene glycol diacrylate), CN-964 (aliphatic urethane diacrylate), CN-966A80 (aliphatic urethane diacrylate blended with 20% tripropylene glycol diacrylate), CN-982A75 (aliphatic urethane diacrylate blended with 25% tripropylene glycol diacrylate) and CN-983 (aliphatic urethane diacrylate), commercially available from Sartomer Corp. of Exton, Pa.; TAB FAIRAD 8010, 8179, 8205, 8210, 8216, 8264, M-E-15, UVU-316, commercially available from TAB Chemicals of Chicago, Ill.; and Echo Resin ALU-303, commercially available from Echo Resins of Versaille, Mo.; and Genomer 4652, commercially available from Rahn Radiation Curing of Aurora, Ill. The preferred aliphatic acrylated oligomers include Ebecryl 264 and Ebecryl 284. Ebecryl 264 is an aliphatic urethane triacrylate of 1200 molecular weight supplied as an 85% solution in hexanediol diacrylate. Ebecryl 284 is aliphatic urethane diacrylate of 1200 molecular weight diluted 10% with 1,6-hexanediol diacrylate. Combinations of these materials may also be employed herein.

[0029] The paint composition of the present invention also preferably includes an ethylenically unsaturated monomer having Formula I: 1

[0030] wherein R1 is hydrogen or substituted or unsubstituted alkyl (i.e., optionally substituted alkyl); and R2 is substituted or unsubstituted alkyl having more than 4 carbon atoms, cycloalkyl, cycloalkenyl, or substituted or unsubstituted aryl. Preferably R1 is hydrogen or methyl; and R2 is isoborynl, phenyl, benzyl, dicylcopentenyl, diclypentenyl oxyethyl, cyclohexyl, and naphthyl. The most preferred ethyleneically unsaturated monomers are isobornyl acrylate monomers. The isobornyl acrylate monomer is preferably present in an amount of about 20% to 60% of the paint composition. If the paint composition is applied by spraying, the isobornyl acrylate monomer is more preferably present in an amount of about 20% to 50%, and most preferably about 27%. If the paint composition is applied by screen printing, the isobornyl acrylate monomer is more preferably present in an amount of about 20% to 60%, and most preferably about 31%. Suitable isobornyl acrylate monomers include Sartomer SR423 (isobornyl methacrylate): 2

[0031] and SR506 (isobornyl acrylate): 3

[0032] available from Sartomer Corp.; Radcure IBOA (isobornyl acrylate), commercially available from Radcure Corp.; IBOA and IBOMA, commercially available from CPS Chemical of Bradford, England; and Genomer 1121, commercially available from Rahn Radiation Curing. The preferred isobornyl acrylate monomer is Radcure IBOA, commercially available from Radcure Corp. Radcure IBOA is a high purity, low color monomer. Combinations of these materials may also be employed herein.

[0033] The preferred paint composition also preferably includes a pigmented composition in an amount of about 0% to 50% of the paint composition. If the paint composition is applied by spraying, the pigmented composition is more preferably present in an amount of about 1% to 20%, and most preferably about 4%. If the paint composition is applied by screen printing, the pigmented composition is more preferably present in an amount of about 1% to 50%, and most preferably about 2%. Suitable pigmented compositions include Venus #91 pigment and Palegold #400 available from NazDar of Atlanta, Ga.; BB 1355,ST8703, ST 8657, and ST 8003 available from ElementisSpecialties of Jersey City, N.J.; Tint-AYD PC 9003 Titanium Dioxide available from Daniel Products Company of Jersey City, N.J., and Al #200 pigment available from Silberline of Leven, England. The preferred pigment used will depend on the desired color of the paint. For example, if a black paint composition is desired, BB 1355 is the preferred pigment. If the pigment is omitted from the composition, a clear paint composition is obtained. Combinations of these materials may also be employed herein.

[0034] This preferred paint composition also includes a photoinitiator in an amount of about 1% to 16% of the paint composition. If the paint composition is applied by spraying, the photoinitiator is more preferably present in an amount of about 3% to 12%, and most preferably about 10%. If the paint composition is applied by screen printing, the photoinitiator is more preferably present in an amount of about 2% to 16%, and most preferably about 4%. Suitable photoinitiators include Irgacure 184 (1-hydroxycyclohexyl phenyl ketone), 45

[0035] available commercially from Ciba-Geigy Corp., Tarrytown, N.Y.; CYRACURE UVI-6974 (mixed triaryl sulfonium hexafluoroantimonate salts) and cyracure UVI-6990 (mixed triaryl sulfonium hexafluorophosphate salts) available commercially from Union Carbide Chemicals and Plastics Co. Inc., Danbury, Conn.; and Genocure CQ, Genocure BOK, and Genocure M.F., commercially available from Rahn Radiation Curing. The preferred photoinitiator is Irgacure 1700 commercially available from Ciba-Geigy of Tarrytown, N.Y. Combinations of these materials may also be employed herein.

[0036] The preferred paint composition may optionally include a flow promoting agent in an amount of about 0.1% to 6% of the paint composition. If the paint composition is applied by spraying, the flow promoting agent is more preferably present in an amount of about 2% to 6%, and most preferably about 5%. If the paint composition is applied by screen printing, the flow promoting agent is more preferably present in an amount of about 1% to 5%, and most preferably about 4%. Suitable flow promoting agents include Genorad 17, commercially available from Rahn Radiation Curing; and Modaflow, commercially available from Monsanto Chemical Co., St. Louis, Mo. The preferred flow promoting agent is Modaflow which is an ethyl acrylate and 2-ethylhexyl acrylate copolymer that improves the flow of the composition. Combinations of these materials may also be employed herein.

[0037] The preferred paint composition may optionally include an adhesion promoter in an amount of about 1% to 12% of the paint composition. If the paint composition is applied by spraying, the adhesion promoter is more preferably present in an amount of about 1% to 11%, and most preferably about 9%. If the paint composition is applied by screen printing, the adhesion promoter is more preferably present in an amount of about 4% to 11% and most preferably about 9%. Suitable adhesion promoters include Ebecryl 168 (methacrylated acidic adhesion promoter), commercially available from Radcure Corp.; and Sartomer CN 704 (acrylated polyester adhesion promoter) and CD 9052 (trifunctional acid ester), commercially available from Sartomer Corp. The preferred adhesion promoter is Ebecryl 168 which is a methacrylated acidic adhesion promoter. Combinations of these materials may also be employed herein.

[0038] To illustrate, the following example sets forth a presently preferred paint composition according to this aspect of the invention.

EXAMPLE 1

[0039] This example provides a preferred paint composition according to the invention that can be used for applying a black paint coating to a substrate preferably by either spray or flexographic techniques. Suitable substrates include cast iron and other metals. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   22.5
Ebecryl 284   22.5
IBOA          27.1
Ebecryl 168   9.1
Modaflow      4.5
Irgacure 1700 10.4
Black BB1355  3.9
Total         100.00

[0040] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the BB 1355 is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 2

[0041] This example provides a preferred paint composition according to the invention that can be used for applying a black paint coating to a substrate preferably by a spray technique. Suitable substrates include cast iron and other metals. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   16.1
Ebecryl 284   16.1
IBOA          47.9
Ebecryl 168   6.5
Modaflow      3.2
Irgacure 1700 7.4
Black BB1355  2.8
Total         100.00

[0042] In this example, the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the BB 1355 is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 3

[0043] This example provides a preferred paint composition according to the invention that can be used for applying a green paint coating to a substrate preferably by screen printing. Suitable substrates include metals and polycarbonates. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   23.1
Ebecryl 284   26.8
IBOA          31.2
Ebecryl 168   8.9
Modaflow      3.6
Irgacure 1700 4.4
Green ST8703  2.0
Total         100.00

[0044] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the Green ST8703 pigment is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 4

[0045] This example provides a preferred paint composition according to the invention that can be used for applying a orange paint coating to a substrate preferably by screen printing. Suitable substrates include metals and polycarbonate. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   23.1
Ebecryl 284   26.8
IBOA          31.2
Ebecryl 168   8.9
Modaflow      3.6
Irgacure 1700 4.4
Orange ST8657 2.0
Total         100.00

[0046] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the Orange ST8657 pigment is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 5

[0047] This example provides a preferred paint composition according to the invention that can be used for applying a clear paint coating to a substrate preferably by spray or flexographic techniques. Suitable substrates include glass, metals, and polycarbonate. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   22.7
Ebecryl 284   19.7
IBOA          43.2
Ebecryl 168   7.6
Modaflow      3.0
Irgacure 1700 3.8
Total         100.00

[0048] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the Ebecryl 168 adhesion promoter is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 6

[0049] This example provides a preferred paint composition according to the invention that can be used for applying a metallic copper-colored paint coating to a substrate preferably by screen printing. Suitable substrates include metals and polycarbonates. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   27.9
Ebecryl 284   16.9
IBOA          22.2
Ebecryl 168   4.1
Modaflow      3.1
Irgacure 1700 5.3
Palegold #400 20.5
pigment (copper)
Total         100.00

[0050] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the Palegold #400 pigment is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 7

[0051] This example provides a preferred paint composition according to the invention that can be used for applying a metallic aluminum-colored paint coating to a substrate preferably by screen printing. Suitable substrates include metals and polycarbonates. The paint composition was made from the following components:

                Approxmiate
Component       Weight %
Ebecryl 264     20.0
Ebecryl 284     20.0
IBOA            24.0
Ebecryl 168     8.0
Modaflow        4.0
Irgacure 1700   4.0
A1 #200 pigment 20.0
Total           100.00

[0052] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the Al #200 pigment is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 8

[0053] This example provides a preferred paint composition according to the invention that can be used for applying a metallic gold-colored paint coating to a substrate preferably by screen printing. Suitable substrates include metals and polycarbonates. The paint composition was made from the following components:

              Approximate
Component     Weight %
Ebecryl 264   10.5
Ebecryl 284   10.5
IBOA          22.5
Ebecryl 168   4.2
Modaflow      2.2
Irgacure 1700 3.9
Venus #91     46.2
pigment
Total         100.00

[0054] In this example the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the Venus #91 pigment is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

EXAMPLE 9

[0055] This example provides a preferred paint composition according to the invention that can be used for applying a white colored paint coating to a substrate preferably by screen printing. Suitable substrates include metals and polycarbonates. The paint composition was made from the following components:

		A.	B.	C.
		Approximate	Approximate	Approximate
	Component	Weight %	Weight %	Weight %
	Ebecryl 264	4.9	7.8	12.0
	Ebecryl 284	4.3	6.8	10.4
	IBOA	46.7	53.0	40.0
	Ebecryl 168	2.1	2.5	3.1
	Modaflow	1.5	2.4	2.6
	Irgacure 1700	6.7	10.7	14.1
	ST8003	33.8	16.8	17.8
	white pigment
	Total	100.00	100.00	100.00

[0056] In this example, the IBOA and Irgacure 1700 are mixed in a pan with a propeller blade mixer for 30 seconds at a speed of 500 to 1000 rpm. In the next step, the Ebecryl 264, the Ebecryl 284, and the Modaflow are introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the next step, the Ebecryl 168 adhesion promoter is added and mixed for 1 to 2 minutes at a speed of 2000 rpm. In the final step, the ST8003 pigment is introduced into the pan and mixed for 1 to 2 minutes at a speed of 2000 rpm. The temperature during mixing is monitored. The mixing is temporarily suspended if the temperature exceeds 100° F.

[0057] Method for Depositing a Paint Coating on a Substrate

[0058] In accordance with still another aspect of the invention, a method is provided for depositing a paint coating on a suitable substrate. The method comprises a first step of applying a fluid-phase composition (“paint composition”) to the substrate.

[0059] The paint composition comprises an aliphatic acrylated oligomer mixture, the aliphatic acrylated oligomer mixture being present in an amount of about 8% to 60% of the paint composition; an isobornyl acrylate monomer in an amount of about 20% to 60% of the paint composition; an photoinitiator in an amount of about 1% to 16% of the paint composition; a flow promoting agent in an amount of about 0.1% to 6% of the paint composition, a pigment containing composition in an amount of 0% to 50%, and optionally an adhesion promoter in an amount of 1% to 12%. The preferred paint compositions according to this method are those described herein, for example, including the compositions described in examples 1 through 9.

[0060] The paint composition may be applied to the substrate using a number of different techniques. The paint composition may be applied, for example, by direct brush application, or it may be sprayed onto the substrate surface. If automobile undercarriage components are to be coated, the spray technique is particularly useful, in that the components may be spray coated on a conveyorized system. The paint composition may also be applied using a screen printing technique. In such screen printing technique, a “screen” as the term is used in the screen printing industry is used to regulate the flow of liquid composition onto the substrate surface. The paint composition typically would be applied to the screen as the latter contacts the substrate. The paint composition flows through the silk screen to the substrate, whereupon it adheres to the substrate at the desired film thickness. Screen printing techniques suitable for this purpose include known techniques, but wherein the process is adjusted in ways known to persons of ordinary skill in the art to accommodate the viscosity, flowability, etc. of the liquid-phase composition, and the substrate of surface properties. Flexographic techniques using pinch rollers to contact the paint composition with a rolling substrate may be used.

[0061] The method includes a second step of illuminating the paint-containing fluid-phase composition on the substrate with an ultraviolet light to cause the paint-containing fluid-phase composition to cure into the paint coating. This illumination may be carried out in any number of ways, provided the ultraviolet light or radiation impinges upon the paint composition so that the paint composition is caused to polymerize to form the coating, layer, film, etc. If automotive undercarriage components are to be coated, steps of coating the components by spraying and illuminating the coated parts may be sequentially performed in a conveyorized system.

[0062] Curing preferably takes place by free radical polymerization, which is initiated by an ultraviolet radiation source. Various ultraviolet light sources may be used, depending on the application. Preferred ultraviolet radiation sources for a number of applications include known ultraviolet lighting equipment with energy intensity settings of, for example, 125 watts, 200 watts, and 300 watts per square inch.

[0063] Additional advantages and modifications will readily occur to those skilled in the art. Therefore, the invention in its broader aspects is not limited to the specific details, representative devices, and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the spirit or scope of the general inventive concept.

[0064] While embodiments of the invention have been illustrated and described, it is not intended that these embodiments illustrate and describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention.

Claims

1. A method for coating a substrate with a paint composition, the method comprising, a) applying the paint composition to the substrate, wherein the paint composition includes: an aliphatic acrylated oligomer mixture; an ethylenically unsaturated monomer having Formula I: 6 wherein R1 is hydrogen or an optionally substituted alkyl; and R2 is substituted or unsubstituted alkyl having more than 4 carbon atoms, cycloalkyl, cycloalkenyl, or substituted or unsubstituted aryl; a pigmented material; and a photoinitiator; and b) illuminating the paint composition on the metallic substrate with an UV light sufficient to cause the paint composition to cure into the paint coating.

2. The method of claim 1 wherein R1 is hydrogen or methyl; and R2 is isoborynl, phenyl, benzyl, dicylcopentenyl, diclypentenyl oxyethyl, cyclohexyl, and naphthyl.

3. The method of claim 1 wherein the ethylenically unsaturated monomer is an isobornyl acrylate monomer.

4. The method of claim 1 wherein the ethylenically unsaturated monomer is isobornyl methacrylate or isobornyl acrylate.

5. The method of claim 3 wherein: the aliphatic acrylated oligomer mixture in an amount of about 8% to 60% of the weight of the paint composition; the isobornyl acrylate monomer in an amount of about 20% to 60% of the weight of the paint composition; the pigmented material in an amount of about 0% to 50% of the weight of the paint composition; and the photoinitiator in an amount of about 1% to 16% of the weight of the paint composition.

6. The method of claim 5 wherein the paint composition further comprises: an adhesion promoter in an amount of about 1% to 12% of the weight of the paint composition; and a flow promoting agent in an amount of about 0.1% to 6% of the weight of the paint composition.

7. The method of claim 6 wherein the method of applying the paint composition is spraying.

8. The method of claim 7 wherein the paint composition includes: an aliphatic acrylated oligomer mixture in an amount of about 30% to 55% of the weight of the paint composition; an isobornyl acrylate monomer in an amount of about 20% to 50% of the weight of the paint composition; an adhesion promoter in an amount of about 4% to 11% of the weight of the paint composition; a pigmented material in an amount of about 1% to 20% of the weight of the paint composition; a photoinitiator in an amount of about 3% to 12% of the weight of the paint composition; and a flow promoting agent in an amount of about 2% to 6% of the weight of the paint composition.

9. The method of claim 8, wherein, the aliphatic acrylated oligomer mixture is about 45% of the weight of the paint composition; the isobornyl acrylate monomer is about 27% of the weight of the paint composition; the adhesion promoter is about 9% of the weight of the paint composition; the pigmented material is about 4% of the weight of the paint composition; the photoinitiator is about 10% of the weight of the paint composition; and the flow promoting agent is about 5% of the weight of the paint composition.

10. The method of claim 6 wherein the method of applying the paint composition is screen-printing.

11. The method of claim 10 wherein the paint composition includes: an aliphatic acrylated oligomer mixture in an amount of about 8% to 60% of the weight of the paint composition; an isobornyl acrylate monomer in an amount of about 20% to 60% of the weight of the paint composition; an adhesion promoter in an amount of about 1% to 11% of the weight of the paint composition; a pigmented material in an amount of about 1% to 50% of the weight of the paint composition; a photoinitiator in an amount of about 2% to 16% of the weight of the paint composition; and a flow promoting agent in an amount of about 1% to 5% of the weight of the paint composition.

12. The method of claim 11 wherein, the aliphatic acrylated oligomer mixture is about 50% of the weight of the paint composition; the isobornyl acrylate monomer is about 31% of the weight of the paint composition; the adhesion promoter is about 9% of the weight of the paint composition; the pigmented material is about 2% of the weight of the paint composition; the photoinitiator is about 4% of the weight of the paint composition; and the flow promoting agent is about to 4% of the weight of the paint composition.

13. The method of claim 1, wherein the UV light used in illuminating impinges upon the paint composition so that the paint composition is caused to form the coating as it cures.

14. The method of claim 1, wherein the method of applying the paint composition is dipping the substrate into the composition sufficiently to cause the composition to uniformly coat the substrate.

15. The method of 1, wherein the method of applying the paint composition is brushing.

16. The method of 1, wherein the method of applying the paint composition is selectively depositing to the substrate at predetermined locations.

17. A coated substrate made by the method comprising: a) applying a paint composition to the substrate, wherein the paint composition includes: an aliphatic acrylated oligomer mixture; an isobornyl acrylate monomer; a pigmented material; and a photoinitiator; and b) illuminating the paint composition on the metallic substrate with an UV light sufficient to cause the paint composition to cure into the paint coating.

18. The coated substrate of claim 17 wherein: the aliphatic acrylated oligomer mixture in an amount of about 8% to 60% of the weight of the paint composition; the isobornyl acrylate monomer in an amount of about 20% to 60% of the weight of the paint composition; the pigmented material in an amount of about 0% to 50% of the weight of the paint composition; and the photoinitiator in an amount of about 1% to 16% of the weight of the paint composition.

19. The coated substrate of claim 18 wherein the paint composition further comprises: an adhesion promoter in an amount of about 1% to 12% of the weight of the paint composition; and a flow promoting agent in an amount of about 0.1% to 6% of the weight of the paint composition.

20. The coated substrate of claim 19 wherein the method of applying the paint composition is spraying.

21. The coated substrate of claim 20 wherein the paint composition includes: an aliphatic acrylated oligomer mixture in an amount of about 30% to 55% of the weight of the paint composition; an isobornyl acrylate monomer in an amount of about 20% to 50% of the weight of the paint composition; an adhesion promoter in an amount of about 4% to 11% of the weight of the paint composition; a pigmented material in an amount of about 1% to 20% of the weight of the paint composition; a photoinitiator in an amount of about 3% to 12% of the weight of the paint composition; and a flow promoting agent in an amount of about 2% to 6% of the weight of the paint composition.

22. The coated substrate of claim 19 wherein the method of applying the paint composition is screen-printing.

23. The coated substrate of claim 22 the paint composition includes: an aliphatic acrylated oligomer mixture in an amount of about 8% to 60% of the weight of the paint composition; an isobornyl acrylate monomer in an amount of about 20% to 60% of the weight of the paint composition; an adhesion promoter in an amount of about 1% to 11% of the weight of the paint composition; a pigmented material in an amount of about 1% to 50% of the weight of the paint composition; a photoinitiator in an amount of about 2% to 16% of the weight of the paint composition; and a flow promoting agent in an amount of about 1% to 5% of the weight of the paint composition.

24. A method of preparing an ultraviolet (UV) curable paint composition comprising: a) combining an isobornyl acrylate monomer and a photoinitiator in a pan to form a first combination; b) mixing the first combination; c) combining an aliphatic acrylated oligomer mixture and a flow promoting agent, with the first mixture to form a second combination; d) mixing the second combination; e) combining an adhesion promoter with the second mixture to form a third combination; f) mixing the third combination; g) combining a pigment material with the second mixture to form a fourth combination; and h) mixing the fourth combination.