This application is a national stage application under 35 U.S.C. § 371 of International Application No. PCT/US2019/057301, filed on Oct. 22, 2019, which claims the benefit of priority under 35 U.S.C. § 119 of Chinese Patent Application Serial No. 201811307488.7, filed on Nov. 5, 2018, the contents of both of which are relied upon and incorporated herein by reference in their entirety.
The disclosure relates to UV patternable organic semiconductor (OSC) polymer blends as semiconducting layers for organic thin-film transistors (OTFTs).
Organic thin-film transistors (OTFTs) have garnered extensive attention as alternatives to conventional silicon-based technologies, which require high temperature and high vacuum deposition processes, as well as complex photolithographic patterning methods. Semiconducting (i.e., organic semiconductor, OSC) layers are one important component of OTFTs which can effectively influence the performance of devices.
Conventional OTFT devices often comprise OSC layers having polymers with structures that lead to gelling, film particles and low reproducibility.
This disclosure presents improved UV patternable OSC polymer blends and use thereof for OSC layers of organic thin-film transistors.
In some embodiments, a polymer blend, comprises: at least one cross-bred organic semiconductor (OSC) polymer and at least one crosslinker, wherein: the at least one cross-bred OSC polymer is a diketopyrrolopyrrole (DPP)-fused thiophene polymeric material, the DPP-fused thiophene polymeric material comprises a first linear alkyl-substituted DPP portion and a second branched alkyl-substituted DPP portion, and the fused thiophene is beta-substituted.
In one aspect, which is combinable with any of the other aspects or embodiments, the crosslinker includes at least one of: acrylates, epoxides, oxetanes, alkenes, alkynes, azides, thiols, allyloxysilanes, phenols, anhydrides, amines, cyanate esters, isocyanate esters, silyl hydrides, cinnamates, coumarins, fluorosulfates, silyl ethers, or a combination thereof.
In one aspect, which is combinable with any of the other aspects or embodiments, the polymer blend further comprises: at least one photoinitiator, wherein the at least one photoinitiator is present in a range of 0.1 wt. % to 10 wt. %.
In one aspect, which is combinable with any of the other aspects or embodiments, the polymer blend further comprises: at least one of antioxidants, lubricants, compatibilizers, leveling agents, or nucleating agents present in a range of 0.05 wt. % to 5 wt. %.
In one aspect, which is combinable with any of the other aspects or embodiments, the first linear alkyl-substituted DPP portion and the second branched alkyl-substituted DPP portion may comprise, independently, the repeat unit of Formula 1 or Formula 2, or a salt, isomer, or analog thereof:
wherein in Formula 1 and Formula 2: m is an integer greater than or equal to one; n is 0, 1, or 2; R1, R2, R3, R4, R5, R6, R7, and R8, may be, independently, hydrogen, substituted or unsubstituted C4 or greater alkyl, substituted or unsubstituted C4 or greater alkenyl, substituted or unsubstituted C4 or greater alkynyl, or C5 or greater cycloalkyl; a, b, c, and d are independently, integers greater than or equal to 3; e and f are integers greater than or equal to zero; X and Y are, independently a covalent bond, an optionally substituted aryl group, an optionally substituted heteroaryl, an optionally substituted fused aryl or fused heteroaryl group, an alkyne or an alkene; and A and B may be, independently, either S or O, with the provisos that: (i) at least one of R1 or R2; one of R3 or R4; one of R5 or R6; and one of R7 or R8 is a substituted or unsubstituted alkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted alkynyl, or cycloalkyl; (ii) if any of R1, R2, R3, or R4 is hydrogen, then none of R5, R6, R7, or R8 are hydrogen; (iii) if any of R5, R6, R7, or R8 is hydrogen, then none of R1, R2, R3, or R4 are hydrogen; (iv) e and f cannot both be 0; (v) if either e or f is 0, then c and d, independently, are integers greater than or equal to 5; and (vi) the polymer having a molecular weight, wherein the molecular weight of the polymer is greater than 10,000.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one crosslinker comprises at least one of: (A) a polymer selected from:
wherein n is an integer greater than or equal to two, or (B) a small-molecule selected from:
or, (C) a combination thereof.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one photoinitiator comprises at least one free radical photoinitiator.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one photoinitiator comprises at least one cationic photoinitiator.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one photoinitiator comprises: 1-hydroxy-cyclohexyl-phenyl-ketone (184); 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 (369); diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO); 2-isopropyl thioxanthone (ITX); 1-[4-(phenylthio) phenyl]-1,2-octanedione 2-(0-benzoyloxime) (HRCURE-OXE01); 2,2-dimethoxy-1,2-diphenylethan-1-one (BDK); benzoyl peroxide (BPO); hydroxyacetophenone (HAP); 2-hydroxy-2-methylprophenone (1173); 2-methyl-4′-(methylthio)-2-morpholinopropiophenone (907); 2-benzyl-2-(dimethylamino)-4′-morpholinobutyrophenone (IHT-PI 910); Ethyl-4-(dimethylamino)benzoate (EDB); methyl o-benzoyl benzoate (OMBB); bis-(2,6 dimethoxy-benzoyl)-phenyl phosphine oxide (BAPO); 4-benzoyl-4′ methyldiphenylsulfide (BMS); benzophenone (BP); 1-chloro-4-propoxy thiozanthone (CPTX); chlorothioxanthone (CTX); 2,2-diethoxyacetophenone (DEAP); diethyl thioxanthone (DETX); 2-dimethyl aminoethyl benzonate (DMB); 2,2-dimethoxy-2-phenyl acetophenone (DMPA); 2-ethyl anthraquinone (2-EA); ethyl-para-N,N-dimethyl-dimethylamino lenzoate (EDAB); 2-ethyl hexyl-dimethylaminolenzoate (EHA); 4,4-bis-(diethylamino)-benzophenone (EMK); methyl benzophenone (MBF); 4-methyl benzophenone (MBP); Michler's ketone (MK); 2-methyl-1-[4(methylthiol)phenyl]-2-morpholino propanone (1) (MMMP); 4-phenylbenzophenone (PBZ); 2,4,6-trimethyl-benzoly-ethoxyl phenyl phosphine oxide (TEPO); bis(4-tert-butylphenyl) iodonium perfluoro-1-butanesulfonate; bis(4-tert-butylphenyl) iodonium p-toluenesulfonate; bis(4-tert-butylphenyl) iodonium triflate; boc-methoxyphenyldiphenylsulfonium triflate; (4-tert-Butylphenyl) diphenylsulfonium triflate; diphenyliodonium hexafluorophosphate; diphenyliodonium nitrate; diphenyliodonium p-toluenesulfonate; diphenyliodonium triflate; (4-fluorophenyl) diphenylsulfonium triflate; N-hydroxynaphthalimide triflate; N-hydroxy-5-norbornene-2,3-dicarboximide perfluoro-1-butanesulfonate; (4-iodophenyl) diphenylsulfonium triflate; (4-methoxyphenyl) diphenylsulfonium triflate; 2-(4-Methoxystyryl)-4,6-bis (trichloromethyl)-1,3,5-triazine; (4-methylthiophenyl) methyl phenyl sulfonium triflate; 1-naphthyl diphenylsulfonium triflate; (4-phenoxyphenyl) diphenylsulfonium triflate; (4-phenylthiophenyl) diphenylsulfonium triflate; triarylsulfonium hexafluoroantimonate salts, mixed 50 wt. % in propylene carbonate; triarylsulfonium hexafluorophosphate salts, mixed 50 wt. % in propylene carbonate; triphenylsulfonium perfluoro-1-butanesufonate; triphenylsulfonium triflate; tris(4-tert-butylphenyl) sulfonium perfluoro-1-butanesulfonate; tris(4-tert-butylphenyl)sulfonium triflate; aryl diazo salts; diaryliodonium salts; triaryl sulfonium salts; aryl ferrocenium salts; or combinations thereof.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one crosslinker comprises C═C bonds, thiols, oxetanes, halides, azides, or combinations thereof.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one cross-bred OSC polymer comprises a repeat unit having: the first linear alkyl-substituted DPP portion, the second branched alkyl-substituted DPP portion, and at least one fused thiophene.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one cross-bred OSC polymer comprises a repeat unit having: the first linear alkyl-substituted DPP portion, the second branched alkyl-substituted DPP portion, and at least two fused thiophenes.
In some embodiments, a method of making a cross-bred organic semiconductor (OSC) polymer, comprises: reacting a first fused thiophene monomer with a first linear alkyl-substituted DPP monomer to form a first DPP-fused thiophene portion; reacting a second fused thiophene monomer with a second branched alkyl-substituted DPP monomer to form a second DPP-fused thiophene portion; and at least one of: reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion; reacting the first DPP-fused thiophene portion with itself, and reacting the second DPP-fused thiophene portion with itself, wherein the fused thiophene is beta-substituted, and wherein the cross-bred OSC polymer comprises both the first DPP-fused thiophene portion and the second DPP-fused thiophene portion.
In one aspect, which is combinable with any of the other aspects or embodiments, the step of reacting the first fused thiophene monomer with the first linear alkyl-substituted DPP monomer comprises:
where n is at least 4.
In one aspect, which is combinable with any of the other aspects or embodiments, the step of reacting the second fused thiophene monomer with the second branched alkyl-substituted DPP monomer comprises:
where n is at least 4.
In one aspect, which is combinable with any of the other aspects or embodiments, the step of reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion comprises:
where n is at least 4.
In one aspect, which is combinable with any of the other aspects or embodiments, the step of reacting the first fused thiophene monomer with the first linear alkyl-substituted DPP monomer; and the step of reacting the second fused thiophene monomer with the second branched alkyl-substituted DPP monomer; and the at least one of: reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion; reacting the first DPP-fused thiophene portion with itself, and reacting the second DPP-fused thiophene portion with itself is conducted in a batch reactor vessel.
In one aspect, which is combinable with any of the other aspects or embodiments, the method further comprises: mixing the first fused thiophene monomer, the first linear alkyl-substituted DPP monomer, the second fused thiophene monomer, and the second branched alkyl-substituted DPP monomer together in a batch reactor vessel.
In one aspect, which is combinable with any of the other aspects or embodiments, the first fused thiophene monomer is the same as the second fused thiophene monomer.
In one aspect, which is combinable with any of the other aspects or embodiments, the steps of: (1) reacting the first fused thiophene monomer with the first linear alkyl-substituted DPP monomer; (2) reacting the second fused thiophene monomer with the second branched alkyl-substituted DPP monomer; and (3) at least one of: reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion; reacting the first DPP-fused thiophene portion with itself, and reacting the second DPP-fused thiophene portion with itself comprises:
where n is at least 4, x is at least 1, y is at least 1.
In one aspect, which is combinable with any of the other aspects or embodiments, the first fused thiophene monomer is different from the second fused thiophene monomer.
In some embodiments, an organic semiconductor device comprises a polymer blend as disclosed herein.
In some embodiments, a cross-bred organic semiconductor (OSC) polymer, comprises a diketopyrrolopyrrole (DPP)-fused thiophene polymeric material, wherein: the DPP-fused thiophene polymeric material comprises a first linear alkyl-substituted DPP portion and a second branched alkyl-substituted DPP portion, the cross-bred OSC polymer comprises both the first linear alkyl-substituted DPP portion and the second branched alkyl-substituted DPP portion, and the fused thiophene is beta-substituted.
In one aspect, which is combinable with any of the other aspects or embodiments, the cross-bred OSC polymer has the structure of:
where n is at least 4, x is at least 1, y is at least 1.
The disclosure will become more fully understood from the following detailed description, taken in conjunction with the accompanying figures, in which:
Reference will now be made in detail to exemplary embodiments which are illustrated in the accompanying drawings. Whenever possible, the same reference numerals will be used throughout the drawings to refer to the same or like parts. The components in the drawings are not necessarily to scale, emphasis instead being placed upon illustrating the principles of the exemplary embodiments. It should be understood that the present application is not limited to the details or methodology set forth in the description or illustrated in the figures. It should also be understood that the terminology is for the purpose of description only and should not be regarded as limiting.
Additionally, any examples set forth in this specification are illustrative, but not limiting, and merely set forth some of the many possible embodiments of the claimed invention.
Other suitable modifications and adaptations of the variety of conditions and parameters normally encountered in the field, and which would be apparent to those skilled in the art, are within the spirit and scope of the disclosure.
The term “alkyl group” refers to a monoradical branched or unbranched saturated hydrocarbon chain having 1 to 40 carbon atoms. This term is exemplified by groups such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, t-butyl, pentyl, n-hexyl, n-heptyl, n-octyl, n-decyl, or tetradecyl, and the like. The alkyl group can be substituted or unsubstituted.
The term “substituted alkyl group” refers to: (1) an alkyl group as defined above, having 1, 2, 3, 4 or 5 substituents, typically 1 to 3 substituents, selected from the group consisting of alkenyl, alkynyl, alkoxy, aralkyl, aldehyde, cycloalkyl, cycloalkenyl, acyl, acylamino, acyl halide, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthiol, ester, heteroarylthio, heterocyclylthio, hydroxyl, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, —SO2-aryl and —SO2-heteroaryl, thioalkyl, vinyl ether. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1, 2, or 3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2; or (2) an alkyl group as defined above that is interrupted by 1-10 atoms independently chosen from oxygen, sulfur and NRa, where Ra is chosen from hydrogen, alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkynyl, aryl, heteroaryl and heterocyclyl. All substituents may be optionally further substituted by alkyl, alkoxy, halogen, CF3, amino, substituted amino, cyano, or —S(O)nRSO, in which RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2; or (3) an alkyl group as defined above that has both 1, 2, 3, 4 or 5 substituents as defined above and is also interrupted by 1-10 atoms as defined above. For example, the alkyl groups can be an alkyl hydroxy group, where any of the hydrogen atoms of the alkyl group are substituted with a hydroxyl group.
The term “alkyl group” as defined herein also includes cycloalkyl groups. The term “cycloalkyl group” as used herein is a non-aromatic carbon-based ring (i.e., carbocyclic) composed of at least three carbon atoms, and in some embodiments from three to 20 carbon atoms, having a single cyclic ring or multiple condensed rings. Examples of single ring cycloalkyl groups include, but are not limited to, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cyclooctyl, and the like. Examples of multiple ring cycloalkyl groups include, but are not limited to, adamantanyl, bicyclo[2.2.1]heptane, 1,3,3-trimethylbicyclo[2.2.1]hept-2-yl, (2,3,3-trimethylbicyclo[2.2.1]hept-2-yl), or carbocyclic groups to which is fused an aryl group, for example indane, and the like. The term cycloalkyl group also includes a heterocycloalkyl group, where at least one of the carbon atoms of the ring is substituted with a heteroatom such as, but not limited to, nitrogen, oxygen, sulfur, or phosphorus.
The term “unsubstituted alkyl group” is defined herein as an alkyl group composed of just carbon and hydrogen.
The term “acyl” denotes a group —C(O)RCO, in which RCO is hydrogen, optionally substituted alkyl, optionally substituted cycloalkyl, optionally substituted heterocyclyl, optionally substituted aryl, and optionally substituted heteroaryl.
The term “aryl group” as used herein is any carbon-based aromatic group (i.e., aromatic carbocyclic) such as having a single ring (e.g., phenyl) or multiple rings (e.g., biphenyl), or multiple condensed (fused) rings (e.g., naphthyl or anthryl). These may include, but are not limited to, benzene, naphthalene, phenyl, etc.
The term “aryl group” also includes “heteroaryl group,” meaning a radical derived from an aromatic cyclic group (i.e., fully unsaturated) having 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, or 15 carbon atoms and 1, 2, 3 or 4 heteroatoms selected from oxygen, nitrogen, sulfur, and phosphorus within at least one ring. In other words, heteroaryl groups are aromatic rings composed of at least three carbon atoms that has at least one heteroatom incorporated within the ring of the aromatic group. Such heteroaryl groups can have a single ring (e.g., pyridyl or furyl) or multiple condensed rings (e.g., indolizinyl, benzothiazolyl, or benzothienyl). Examples of heteroaryls include, but are not limited to, [1,2,4]oxadiazole, [1,3,4]oxadiazole, [1,2,4]thiadiazole, [1,3,4]thiadiazole, pyrrole, imidazole, pyrazole, pyridine, pyrazine, pyrimidine, pyridazine, indolizine, isoindole, indole, indazole, purine, quinolizine, isoquinoline, quinoline, phthalazine, naphthylpyridine, quinoxaline, quinazoline, cinnoline, pteridine, carbazole, carboline, phenanthridine, acridine, phenanthroline, isothiazole, phenazine, isoxazole, phenoxazine, phenothiazine, imidazolidine, imidazoline, triazole, oxazole, thiazole, naphthyridine, and the like as well as N-oxide and N-alkoxy derivatives of nitrogen containing heteroaryl compounds, for example pyridine-N-oxide derivatives.
Unless otherwise constrained by the definition for the heteroaryl substituent, such heteroaryl groups can be optionally substituted with 1 to 5 substituents, typically 1 to 3 substituents selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1-3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The aryl group can be substituted or unsubstituted. Unless otherwise constrained by the definition for the aryl substituent, such aryl groups can optionally be substituted with from 1 to 5 substituents, typically 1 to 3 substituents, selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, aldehyde, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, ester, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1-3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2. In some embodiments, the term “aryl group” is limited to substituted or unsubstituted aryl and heteroaryl rings having from three to 30 carbon atoms.
The term “aralkyl group” as used herein is an aryl group having an alkyl group or an alkylene group as defined herein covalently attached to the aryl group. An example of an aralkyl group is a benzyl group. “Optionally substituted aralkyl” refers to an optionally substituted aryl group covalently linked to an optionally substituted alkyl group or alkylene group. Such aralkyl groups are exemplified by benzyl, phenylethyl, 3-(4-methoxyphenyl)propyl, and the like.
The term “heteroaralkyl” refers to a heteroaryl group covalently linked to an alkylene group, where heteroaryl and alkylene are defined herein. “Optionally substituted heteroaralkyl” refers to an optionally substituted heteroaryl group covalently linked to an optionally substituted alkylene group. Such heteroaralkyl groups are exemplified by 3-pyridylmethyl, quinolin-8-ylethyl, 4-methoxythiazol-2-ylpropyl, and the like.
The term “alkenyl group” refers to a monoradical of a branched or unbranched unsaturated hydrocarbon group typically having from 2 to 40 carbon atoms, more typically 2 to 10 carbon atoms and even more typically 2 to 6 carbon atoms and having 1-6, typically 1, double bond (vinyl). Typical alkenyl groups include ethenyl or vinyl (—CH═CH2), 1-propylene or allyl (—CH2CH═CH2), isopropylene (—C(CH3)═CH2), bicyclo[2.2.1]heptene, and the like. When alkenyl is attached to nitrogen, the double bond cannot be alpha to the nitrogen.
The term “substituted alkenyl group” refers to an alkenyl group as defined above having 1, 2, 3, 4 or 5 substituents, and typically 1, 2, or 3 substituents, selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1, 2, or 3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “cycloalkenyl group” refers to carbocyclic groups of from 3 to 20 carbon atoms having a single cyclic ring or multiple condensed rings with at least one double bond in the ring structure.
The term “alkynyl group” refers to a monoradical of an unsaturated hydrocarbon, typically having from 2 to 40 carbon atoms, more typically 2 to 10 carbon atoms and even more typically 2 to 6 carbon atoms and having at least 1 and typically from 1-6 sites of acetylene (triple bond) unsaturation. Typical alkynyl groups include ethynyl, (—C≡CH), propargyl (or prop-1-yn-3-yl, —CH2C≡CH), and the like. When alkynyl is attached to nitrogen, the triple bond cannot be alpha to the nitrogen.
The term “substituted alkynyl group” refers to an alkynyl group as defined above having 1, 2, 3, 4 or 5 substituents, and typically 1, 2, or 3 substituents, selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2— alkyl, SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1, 2, or 3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “alkylene group” is defined as a diradical of a branched or unbranched saturated hydrocarbon chain, having 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20 carbon atoms, typically 1-10 carbon atoms, more typically 1, 2, 3, 4, 5 or 6 carbon atoms. This term is exemplified by groups such as methylene (—CH2—), ethylene (—CH2CH2—), the propylene isomers (e.g., —CH2CH2CH2— and —CH(CH3)CH2—) and the like.
The term “substituted alkylene group” refers to: (1) an alkylene group as defined above having 1, 2, 3, 4, or 5 substituents selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, —SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1, 2, or 3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2; or (2) an alkylene group as defined above that is interrupted by 1-20 atoms independently chosen from oxygen, sulfur and NRa—, where Ra is chosen from hydrogen, optionally substituted alkyl, cycloalkyl, cycloalkenyl, aryl, heteroaryl and heterocyclyl, or groups selected from carbonyl, carboxyester, carboxyamide and sulfonyl; or (3) an alkylene group as defined above that has both 1, 2, 3, 4 or 5 substituents as defined above and is also interrupted by 1-20 atoms as defined above. Examples of substituted alkylenes are chloromethylene (—CH(Cl)—), aminoethylene (—CH(NH2)CH2—), methylaminoethylene (—CH(NHMe)CH2—), 2-carboxypropylene isomers (—CH2CH(CO2H)CH2—), ethoxyethyl (—CH2CH2O—CH2CH2—), ethylmethylaminoethyl (—CH2CH2N(CH3)CH2CH2—), and the like.
The term “alkoxy group” refers to the group R—O—, where R is an optionally substituted alkyl or optionally substituted cycloalkyl, or R is a group —Y—Z, in which Y is optionally substituted alkylene and Z is optionally substituted alkenyl, optionally substituted alkynyl; or optionally substituted cycloalkenyl, where alkyl, alkenyl, alkynyl, cycloalkyl and cycloalkenyl are as defined herein. Typical alkoxy groups are optionally substituted alkyl-O— and include, by way of example, methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, tert-butoxy, sec-butoxy, n-pentoxy, n-hexoxy, 1,2-dimethylbutoxy, trifluoromethoxy, and the like.
The term “alkylthio group” refers to the group RS—S—, where RS is as defined for alkoxy.
The term “aminocarbonyl” refers to the group —C(O)NRNRN where each RN is independently hydrogen, alkyl, aryl, heteroaryl, heterocyclyl or where both RN groups are joined to form a heterocyclic group (e.g., morpholino). Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1-3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “acylamino” refers to the group —NRNCOC(O)R where each RNCO is independently hydrogen, alkyl, aryl, heteroaryl, or heterocyclyl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1-3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “acyloxy” refers to the groups —O(O)C-alkyl, —O(O)C-cycloalkyl, —O(O)C-aryl, —O(O)C-heteroaryl, and —O(O)C-heterocyclyl. Unless otherwise constrained by the definition, all substituents may be optionally further substituted by alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “aryloxy group” refers to the group aryl-O— wherein the aryl group is as defined above, and includes optionally substituted aryl groups as also defined above.
The term “heteroaryloxy” refers to the group heteroaryl-O—.
The term “amino” refers to the group —NH2.
The term “substituted amino” refers to the group —NRwRw where each Rw is independently selected from the group consisting of hydrogen, alkyl, cycloalkyl, carboxyalkyl (for example, benzyloxycarbonyl), aryl, heteroaryl and heterocyclyl provided that both Rw groups are not hydrogen, or a group —Y—Z, in which Y is optionally substituted alkylene and Z is alkenyl, cycloalkenyl, or alkynyl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1-3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “carboxy” refers to a group —C(O)OH. The term “carboxyalkyl group” refers to the groups —C(O)O-alkyl or —C(O)O-cycloalkyl, where alkyl and cycloalkyl, are as defined herein, and may be optionally further substituted by alkyl, alkenyl, alkynyl, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, in which RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The terms “substituted cycloalkyl group” or “substituted cycloalkenyl group” refer to cycloalkyl or cycloalkenyl groups having 1, 2, 3, 4 or 5 substituents, and typically 1, 2, or 3 substituents, selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1, 2, or 3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “conjugated group” is defined as a linear, branched or cyclic group, or combination thereof, in which p-orbitals of the atoms within the group are connected via delocalization of electrons and wherein the structure can be described as containing alternating single and double or triple bonds and may further contain lone pairs, radicals, or carbenium ions. Conjugated cyclic groups may comprise both aromatic and non-aromatic groups, and may comprise polycyclic or heterocyclic groups, such as diketopyrrolopyrrole. Ideally, conjugated groups are bound in such a way as to continue the conjugation between the thiophene moieties they connect. In some embodiments, “conjugated groups” is limited to conjugated groups having three to 30 carbon atoms.
The term “halogen,” “halo,” or “halide” may be referred to interchangeably and refer to fluoro, bromo, chloro, and iodo.
The term “heterocyclyl” refers to a monoradical saturated or partially unsaturated group having a single ring or multiple condensed rings, having from 1 to 40 carbon atoms and from 1 to 10 hetero atoms, typically 1, 2, 3 or 4 heteroatoms, selected from nitrogen, sulfur, phosphorus, and/or oxygen within the ring. Heterocyclic groups can have a single ring or multiple condensed rings, and include tetrahydrofuranyl, morpholino, piperidinyl, piperazino, dihydropyridino, and the like.
Unless otherwise constrained by the definition for the heterocyclyl substituent, such heterocyclyl groups can be optionally substituted with 1, 2, 3, 4 or 5, and typically 1, 2 or 3 substituents, selected from the group consisting of alkyl, alkenyl, alkynyl, alkoxy, cycloalkyl, cycloalkenyl, acyl, acylamino, acyloxy, amino, aminocarbonyl, alkoxycarbonylamino, azido, cyano, halogen, hydroxy, keto, thiocarbonyl, carboxy, carboxyalkyl, arylthio, heteroarylthio, heterocyclylthio, thiol, alkylthio, aryl, aryloxy, heteroaryl, aminosulfonyl, aminocarbonylamino, heteroaryloxy, heterocyclyl, heterocyclooxy, hydroxyamino, alkoxyamino, nitro, —SO-alkyl, —SO-aryl, —SO-heteroaryl, —SO2-alkyl, —SO2-aryl and —SO2-heteroaryl. Unless otherwise constrained by the definition, all substituents may optionally be further substituted by 1-3 substituents chosen from alkyl, carboxy, carboxyalkyl, aminocarbonyl, hydroxy, alkoxy, halogen, CF3, amino, substituted amino, cyano, and —S(O)nRSO, where RSO is alkyl, aryl, or heteroaryl and n is 0, 1 or 2.
The term “thiol” refers to the group —SH. The term “substituted alkylthio” refers to the group —S-substituted alkyl. The term “arylthiol group” refers to the group aryl-S—, where aryl is as defined as above. The term “heteroarylthiol” refers to the group —S-heteroaryl wherein the heteroaryl group is as defined above including optionally substituted heteroaryl groups as also defined above.
The term “sulfoxide” refers to a group —S(O)RSO, in which RSO is alkyl, aryl, or heteroaryl. The term “substituted sulfoxide” refers to a group —S(O)RSO, in which RSO is substituted alkyl, substituted aryl, or substituted heteroaryl, as defined herein. The term “sulfone” refers to a group —S(O)2RSO, in which RSO is alkyl, aryl, or heteroaryl. The term “substituted sulfone” refers to a group —S(O)2RSO, in which RSO is substituted alkyl, substituted aryl, or substituted heteroaryl, as defined herein.
The term “keto” refers to a group —C(O)—. The term “thiocarbonyl” refers to a group —C(S)—.
As used herein, the term “room temperature” is 20° C. to 25° C.
Disclosed are compounds, compositions, and components that can be used for, can be used in conjunction with, can be used in preparation of, or are products of the disclosed methods and compositions. These and other materials are disclosed herein, and it is understood that when combinations, subsets, interactions, groups, etc. of these materials are disclosed that while specific reference of each various individual and collective combinations and permutation of these compounds may not be explicitly disclosed, each is specifically contemplated and described herein. Thus, if a class of molecules A, B, and C are disclosed as well as a class of molecules D, E, and F and an example of a combination molecule, A-D is disclosed, then even if each is not individually recited, each is individually and collectively contemplated. Thus, in this example, each of the combinations A-E, A-F, B-D, B-E, B-F, C-D, C-E, and C-F are specifically contemplated and should be considered disclosed from disclosure of A, B, and C; D, E, and F; and the example combination A-D. Likewise, any subset or combination of these is also specifically contemplated and disclosed. Thus, for example, the sub-group of A-E, B-F, and C-E are specifically contemplated and should be considered disclosed from disclosure of A, B, and C; D, E, and F; and the example combination A-D. This concept applies to all aspects of this disclosure including, but not limited to, steps in methods of making and using the disclosed compositions. Thus, if there are a variety of additional steps that can be performed it is understood that each of these additional steps can be performed with any specific embodiment or combination of embodiments of the disclosed methods, and that each such combination is specifically contemplated and should be considered disclosed.
A weight percent of a component, unless specifically stated to the contrary, is based on the total weight of the formulation or composition in which the component is included.
Organic semiconductors as functional materials may be used in a variety of applications including, for example, printed electronics, organic transistors, including organic thin-film transistors (OTFTs) and organic field-effect transistors (OFETs), organic light-emitting diodes (OLEDs), organic integrated circuits, organic solar cells, and disposable sensors. Organic transistors may be used in many applications, including smart cards, security tags, and the backplanes of flat panel displays. Organic semiconductors may substantially reduce cost compared to inorganic counterparts, such as silicon. Depositing OSCs from solution may enable fast, large-area fabrication routes such as various printing methods and roll-to-roll processes.
Organic thin-film transistors are particularly interesting because their fabrication processes are less complex as compared with conventional silicon-based technologies. For example, OTFTs generally rely on low temperature deposition and solution processing, which, when used with semiconducting conjugated polymers, can achieve valuable technological attributes, such as compatibility with simple-write printing techniques, general low-cost manufacturing approaches, and flexible plastic substrates. Other potential applications for OTFTs include flexible electronic papers, sensors, memory devices (e.g., radio frequency identification cards (RFIDs)), remote controllable smart tags for supply chain management, large-area flexible displays, and smart cards.
Organic Semiconductor (OSC) Polymer
An OSC polymer may be used to produce organic semiconductor devices. In some examples, a polymer blend comprises an organic semiconductor polymer. In some examples, the OSC polymer has a main backbone that is fully conjugated. In some examples, the OSC is a diketopyrrolopyrrole (DPP) fused thiophene polymeric material. In some examples, the fused thiophene is beta-substituted. This OSC may contain both fused thiophene and diketopyrrolopyrrole units. In some examples, the OSC is used in OTFT applications.
In some examples, the DPP-fused thiophene polymeric material may be modified with long linear and/or branched alkyl side chains to improve solution processing characteristics (e.g., solubility and non-gelling in commonly used organic solvents (see below). Polymeric materials comprising both linear alkyl side chains and branched alkyl side chains may benefit from the advantages of each. For example, better intermolecular stacking of linear alkyl side chain-substituted OSC polymers leads to excellent good OTFT performance, while better solubility of branched alkyl side chain-substituted OSC polymers minimizes gelling and/or reproducibility concerns. In other words, combining the advantageous attributes of the linear alkyl side chains and the branched alkyl side chains in the DPP-fused thiophene polymeric material allows for improved solution processing during formation of the organic semiconductor device (e.g., OTFT).
Thus, in some examples, the OSC polymer is a diketopyrrolopyrrole (DPP)-fused thiophene polymeric material comprising a first linear alkyl-substituted DPP portion and a second branched alkyl-substituted DPP portion (“cross-bred OSC polymers”), whereby the first linear alkyl-substituted DPP portion and the second branched alkyl-substituted DPP portion may comprise, independently, the repeat unit of Formula 1 or Formula 2, or a salt, isomer, or analog thereof:
wherein in Formula 1 and Formula 2: m is an integer greater than or equal to one; n is 0, 1, or 2; R1, R2, R3, R4, R5, R6, R7, and R8, may be, independently, hydrogen, substituted or unsubstituted C4 or greater alkyl, substituted or unsubstituted C4 or greater alkenyl, substituted or unsubstituted C4 or greater alkynyl, or C5 or greater cycloalkyl; a, b, c, and d are independently, integers greater than or equal to 3; e and f are integers greater than or equal to zero; X and Y are, independently a covalent bond, an optionally substituted aryl group, an optionally substituted heteroaryl, an optionally substituted fused aryl or fused heteroaryl group, an alkyne or an alkene; and A and B may be, independently, either S or O, with the provisos that: (i) at least one of R1 or R2; one of R3 or R4; one of R5 or R6; and one of R7 or R8 is a substituted or unsubstituted alkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted alkynyl, or cycloalkyl; (ii) if any of R1, R2, R3, or R4 is hydrogen, then none of R5, R6, R7, or R8 are hydrogen; (iii) if any of R5, R6, R7, or R8 is hydrogen, then none of R1, R2, R3, or R4 are hydrogen; (iv) e and f cannot both be 0; (v) if either e or f is 0, then c and d, independently, are integers greater than or equal to 5; and (iv) the polymer having a molecular weight, wherein the molecular weight of the polymer is greater than 10,000.
In some examples, the cross-bred OSC polymer comprises a repeat unit having: the first linear alkyl-substituted DPP portion, the second branched alkyl-substituted DPP portion, and at least one fused thiophene. In some examples, the cross-bred OSC polymer comprises a repeat unit having: the first linear alkyl-substituted DPP portion, the second branched alkyl-substituted DPP portion, and at least two fused thiophenes.
In some embodiments, the OSC polymers defined in Formula 1 or Formula 2 enable simple transistor fabrication at relatively low temperatures, which is particularly important for the realization of large-area, mechanically flexible electronics. A beta-substituted OSC polymer can also help to improve solubility.
In some examples, the polymers of Formulas 3, 4, and/or 5 (or salts, isomers, or analogs thereof) may be used to formulate the cross-bred OSC polymer comprising a linear alkyl-substituted DPP portion and a branched alkyl-substituted DPP portion. For example, the cross-bred OSC polymer may comprise blends of the polymers of Formulas 3 and 4, or blends of the polymers of Formulas 3 and 5, or blends of the polymers of Formulas 4 and 5, or blends of the polymers of Formulas 3-5. In other words, the cross-bred OSC polymer may be: (A) a random copolymer of the repeating unit of the polymers of Formulas 3 and 4, (B) a random copolymer of the repeating unit of the polymers of Formulas 3 and 5, (C) a random copolymer of the repeating unit of the polymers of Formulas 4 and 5, or (D) a random tri-polymer of the repeating unit of the polymers of Formulas 3-5.
In some examples, the OSC has a solubility of 0.5 mg/mL, 1 mg/mL, 2 mg/mL, 3 mg/mL, 4 mg/mL, 5 mg/mL, or any range defined by any two of those endpoints. In some examples, the OSC has a solubility of 1 mg/mL or more at room temperature.
In some examples, the OSC has hole mobilities of 1 cm2V−1s−1, 2 cm2V−1s, 3 cm2V−1s−1, 4 cm2V−1s−1s, 5 cm2V−1s−1, 10 cm2V−1s−1, or any range defined by any two of those endpoints. The hole mobilities may be equal to or greater than any of these values. In some examples, the OSC has hole mobilities of 1 to 4 cm2V−1s−1. In some examples, the OSC has hole mobilities of 2 cm2V−1s−1. In some examples, the OSC has hole mobilities of 2 cm2V−1s−1 or more.
In some examples, the OSC polymers have On/Off ratios of greater than 105. In some examples, the OSC polymers have On/Off ratios of greater than 106.
In some examples, the OSC polymers have a threshold voltage in thin film transistor devices of 1 V, 2 V, 3V, 4 V, 5 V, 10 V, or any range defined by any two of those endpoints. In some examples, the OSC polymers have a threshold voltage in a range of 1 V to 3 V in thin film transistor devices. In some examples, the OSC polymers have a threshold voltage of 2 V in thin film transistor devices.
In some examples, a method of making a cross-bred organic semiconductor (OSC) polymer, comprises: reacting a first fused thiophene monomer with a first linear alkyl-substituted DPP monomer to form a first DPP-fused thiophene portion; reacting a second fused thiophene monomer with a second branched alkyl-substituted DPP monomer to form a second DPP-fused thiophene portion; and at least one of: reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion; reacting the first DPP-fused thiophene portion with itself, and reacting the second DPP-fused thiophene portion with itself, wherein the fused thiophene is beta-substituted, and wherein the cross-bred OSC polymer comprises both the first DPP-fused thiophene portion and the second DPP-fused thiophene portion.
In some examples, the step of reacting the first fused thiophene monomer with the first linear alkyl-substituted DPP monomer comprises:
where n is at least 4.
In some examples, the step of reacting the second fused thiophene monomer with the second branched alkyl-substituted DPP monomer comprises:
where n is at least 4.
In some examples, the step of reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion comprises:
where n is at least 4.
In some examples, the step of reacting the first fused thiophene monomer with the first linear alkyl-substituted DPP monomer; and the step of reacting the second fused thiophene monomer with the second branched alkyl-substituted DPP monomer; and the at least one of: reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion; reacting the first DPP-fused thiophene portion with itself; and reacting the second DPP-fused thiophene portion with itself is conducted in a batch reactor vessel.
In one aspect, which is combinable with any of the other aspects or embodiments, the method further comprises: mixing the first fused thiophene monomer, the first linear alkyl-substituted DPP monomer, the second fused thiophene monomer, and the second branched alkyl-substituted DPP monomer together in a batch reactor vessel.
In some examples, the first fused thiophene monomer is the same as the second fused thiophene monomer. In some examples, the first fused thiophene monomer is different from the second fused thiophene monomer.
In some examples, the steps of: (1) reacting the first fused thiophene monomer with the first linear alkyl-substituted DPP monomer; (2) reacting the second fused thiophene monomer with the second branched alkyl-substituted DPP monomer; and (3) at least one of: reacting the first DPP-fused thiophene portion and the second DPP-fused thiophene portion; reacting the first DPP-fused thiophene portion with itself; and reacting the second DPP-fused thiophene portion with itself comprises:
where n is at least 4, x is at least 1, y is at least 1.
While the above synthesis mechanism for the cross-bred organic semiconductor polymer (Reactions 1-4) is described as a Stille coupling reaction, other palladium-catalyzed coupling reaction schemes may also be used (e.g., Suzuki-Miyaura coupling, Negishi coupling, Kumada coupling, Hiyama coupling, Sonogashira coupling, Mizoroki-Heck coupling, Buchwald-Hartwig coupling, direct (hetero) arylation, etc.), as well as non-palladium catalyzed reaction schemes (e.g., Grignard reaction, etc.).
Moreover, the donors and/or acceptors are not limited to side chain branching (as shown in Reactions 1-4), but may also include core structures of the donors/acceptors, side chain chemistry (e.g., alkyls, ethers, esters, siloxanes, urethanes, etc.), side chain terminal functionalities (e.g., alkyl, acrylates, epoxides, oxetanes, alkenes, alkynes, azides, thiols, allyloxysilanes, phenols/alcohols, anhydrides, amines, cyanate esters, isocyanate esters, silyl hydrides, cinnamate/coumarin, fluorosulfates, silyl ethers, etc.), among others.
Crosslinker
In some examples, a polymer blend comprises at least one organic semiconductor (OSC) polymer and at least one crosslinker, such that the crosslinker includes at least one of: acrylates, epoxides, oxetanes, alkenes, alkynes, azides, thiols, allyloxysilanes, phenols, anhydrides, amines, cyanate esters, isocyanate esters, silyl hydrides, cinnamates, coumarins, fluorosulfates, silyl ethers, or a combination thereof. In some examples, the at least one crosslinker comprises C═C bonds, thiols, oxetanes, halides, azides, or combinations thereof.
In some examples, the crosslinker may be a small molecule or a polymer that reacts with the OSC polymer by one or a combination of reaction mechanisms, depending on functional moieties present in the crosslinker molecule. For example, crosslinkers comprising thiol groups may react with double bonds in the OSC polymer via thiol-ene click chemistry. In some examples, crosslinkers comprising vinyl groups may react with double bonds in the OSC polymer via addition reaction. In some examples, crosslinkers (comprising thiols, vinyl groups, etc., or combinations thereof) may react with crosslinkable functionalities incorporated in the side chains of OSC polymers. These include, for example, acrylates, epoxides, oxetanes, alkenes, alkynes, azides, thiols, allyloxysilanes, phenols, anhydrides, amines, cyanate esters, isocyanate esters, silyl hydrides, cinnamates, coumarins, fluorosulfates, silyl ethers, or combinations thereof.
In one aspect, which is combinable with any of the other aspects or embodiments, the at least one crosslinker comprises at least one of: (A) a polymer selected from:
wherein n is an integer greater than or equal to two, or (B) a small-molecule selected from:
or, (C) a combination thereof.
Photoinitiator
In some examples, a polymer blend comprises at least one OSC polymer, at least one crosslinker, and at least one photoinitiator.
The photoinitiator is a key component of photocuring products. In some examples, the photoinitiator comprises at least one free radical photoinitiator. Free-radical based photoinitiators include reactive free radicals that initiate photo-polymerization when exposed to UV light. In one example, the mechanism by which photoinitiator TPO initiates thiol-ene free-radical polymerization is shown below.
In some examples, the photoinitiator comprises at least one cationic photoinitiator. Cationic photoinitiators are also called photo-acid generators (PAGs). Once a cationic photoinitiator absorbs UV light, the initiator molecule is converted into a strong acid species, either a Lewis or Brönsted acid, that initiates polymerization. Typical photoacids/photoacid generators include aryl diazo salts, diaryliodonium salts, triaryl sulfonium salts, and aryl ferrocenium salts. In one example, the mechanism by which polymerization proceeds in using PAGs is show n below.
In some examples, the at least one photoinitiator includes: 1-hydroxy-cyclohexyl-phenyl-ketone (184); 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 (369); diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO); 2-isopropyl thioxanthone (ITX); 1-[4-(phenylthio) phenyl]-1,2-octanedione 2-(O-benzoyloxime) (HRCURE-OXE01); 2,2-dimethoxy-1,2-diphenylethan-1-one (BDK); benzoyl peroxide (BPO); hydroxyacetophenone (HAP); 2-hydroxy-2-methylprophenone (1173); 2-methyl-4′-(methylthio)-2-morpholinopropiophenone (907); 2-benzyl-2-(dimethylamino)-4′-morpholinobutyrophenone (IHT-PI 910); Ethyl-4-(dimethylamino)benzoate (EDB); methyl o-benzoyl benzoate (OMBB); bis-(2,6 dimethoxy-benzoyl)-phenyl phosphine oxide (BAPO); 4-benzoyl-4′ methyldiphenylsulfide (BMS); benzophenone (BP); 1-chloro-4-propoxy thiozanthone (CPTX); chlorothioxanthone (CTX); 2,2-diethoxyacetophenone (DEAP); diethyl thioxanthone (DETX); 2-dimethyl aminoethyl benzonate (DMB); 2,2-dimethoxy-2-phenyl acetophenone (DMPA); 2-ethyl anthraquinone (2-EA); ethyl-para-N,N-dimethyl-dimethylamino lenzoate (EDAB); 2-ethyl hexyl-dimethylaminolenzoate (EHA); 4,4-bis-(diethylamino)-benzophenone (EMK); methyl benzophenone (MBF); 4-methyl benzophenone (MBP); Michler's ketone (MK); 2-methyl-1-[4(methylthiol)phenyl]-2-morpholino propanone (1) (MMMP); 4-phenylbenzophenone (PBZ); 2,4,6-trimethyl-benzoly-ethoxyl phenyl phosphine oxide (TEPO); bis(4-tert-butylphenyl) iodonium perfluoro-1-butanesulfonate; bis(4-tert-butylphenyl) iodonium p-toluenesulfonate; bis(4-tert-butylphenyl) iodonium triflate; boc-methoxyphenyldiphenylsulfonium triflate; (4-tert-Butylphenyl) diphenylsulfonium triflate; diphenyliodonium hexafluorophosphate; diphenyliodonium nitrate; diphenyliodonium p-toluenesulfonate; diphenyliodonium triflate; (4-fluorophenyl) diphenylsulfonium triflate; N-hydroxynaphthalimide triflate; N-hydroxy-5-norbornene-2,3-dicarboximide perfluoro-1-butanesulfonate; (4-iodophenyl) diphenylsulfonium triflate; (4-methoxyphenyl) diphenylsulfonium triflate; 2-(4-Methoxystyryl)-4,6-bis (trichloromethyl)-1,3,5-triazine; (4-methylthiophenyl) methyl phenyl sulfonium triflate; 1-naphthyl diphenylsulfonium triflate; (4-phenoxyphenyl) diphenylsulfonium triflate; (4-phenylthiophenyl) diphenylsulfonium triflate; triarylsulfonium hexafluoroantimonate salts, mixed 50 wt. % in propylene carbonate; triarylsulfonium hexafluorophosphate salts, mixed 50 wt. % in propylene carbonate; triphenylsulfonium perfluoro-1-butanesufonate; triphenylsulfonium triflate; tris(4-tert-butylphenyl) sulfonium perfluoro-1-butanesulfonate; tris(4-tert-butylphenyl)sulfonium triflate; aryl diazo salts; diaryliodonium salts; triaryl sulfonium salts; aryl ferrocenium salts; or combinations thereof.
Structures for representative photoinitiators are shown in Table 1 below.
Structures for representative aryl diazo salt, diaryliodonium salt, triaryl sulfonium salt, and aryl ferrocenium salt photoinitiators are shown in Table 2 below.
Additives
In some examples, a polymer blend comprises at least one OSC polymer, at least one crosslinker, at least one photoinitiator, and at least one additive, such as antioxidants (i.e., oxygen inhibitors), lubricants, compatibilizers, leveling agents, nucleating agents, or combinations thereof. In some examples, oxygen inhibitors include phenols, thiols, amines, ethers, phosphites, organic phosphines, hydroxylamines, or combinations thereof.
Polymer Blend
In some examples, the performance of a device comprising the OSC polymer may be improved by blending the OSC polymer with a crosslinker. In some examples, the OSC polymer is blended with a crosslinker in a solvent. In some examples, the solvent is chloroform, methylethylketone, toluene, xylenes, chlorobenzene, 1,2-dichlorobenzene, 1,2,4-trichlorobenzene, tetralin, naphthalene, chloronaphthalene, or combinations thereof. In some examples, a mixture of more than one solvent may be used.
In some examples, the at least one OSC polymer is present in a range of 1 wt. % to 99 wt. %, or in a range of 5 wt. % to 95 wt. %, or in a range of 10 wt. % to 90 wt. %, or in a range of 25 wt. % to 85 wt. %, or in a range of 50 wt. % to 80 wt. %. In some examples, the at least one OSC polymer is present at 1 wt. %, or 2 wt. %, or 3 wt. %, or 5 wt. %, or 10 wt. %, or 15 wt. %, or 20 wt. %, or 25 wt. %, or 30 wt. %, or 35 wt. %, or 40 wt. %, or 50 wt. %, or 60 wt. %, or 70 wt. %, or 80 wt. %, or 90 wt. %, or 95 wt. %, or 99 wt. %, or any range defined by any two of those endpoints.
In some examples, the at least one crosslinker is present in a range of 1 wt. % to 99 wt. %, or in a range of 5 wt. % to 95 wt. %, or in a range of 10 wt. % to 90 wt. %, or in a range of 15 wt. % to 85 wt. %, or in a range of 20 wt. % to 80 wt. %, or in a range of 25 wt. % to 75 wt. %, or in a range of 25 wt. % to 65 wt. %, or in a range of 25 wt. % to 55 wt. %. In some examples, the at least one crosslinker is present at 0.1 wt. %, or 0.2 wt. %, or 0.3 wt. %, or 0.5 wt. %, or 0.8 wt. %, or 1 wt. %, or 2 wt. %, or 3 wt. %, or 5 wt. %, or 10 wt. %, or 15 wt. %, or 20 wt. %, or 25 wt. %, or 30 wt. %, or 35 wt. %, or 40 wt. %, or 45 wt. %, or 50 wt. %, or 55 wt. %, or 60 wt. %, or 65 wt. %, or 70 wt. %, or 75 wt. %, or 80 wt. %, or 85 wt. %, or 90 wt. %, or 95 wt. %, or 99 wt. %, or any range defined by any two of those endpoints. In some examples, the at least one crosslinker comprises a first crosslinker and a second crosslinker, the first crosslinker being present in a range of 30 wt. % to 50 wt. % and the second crosslinker being present in a range of 0.5 wt. % to 25 wt. %.
In some examples, the at least one photoinitiator is present in a range of 0.1 wt. % to 10 wt. %; or in a range of 0.2 wt. % to 8 wt. %, or in a range of 0.3 wt. % to 6 wt. %, or in a range of 0.4 wt. % to 5 wt. %, or in a range of 0.5 wt. % to 4.5 wt. %, or in a range of 0.5 wt. % to 4 wt. %, or in a range of 0.6 wt. % to 3.5 wt. %, or in a range of 0.7 wt. % to 3 wt. %. In some examples, the at least one photoinitiator is present at 0.1 wt. %, or 0.2 wt. %, or 0.3 wt. %, or 0.4 wt. %, or 0.5 wt. %, or 0.6 wt. %, or 0.7 wt. %, or 0.8 wt. %, or 0.9 wt. %, or 1 wt. %, or 1.5 wt. %, or 2 wt. %, or 2.5 wt. %, or 3 wt. %, or 3.5 wt. %, or 4 wt. %, or 4.5 wt. %, or 5 wt. %, or 6 wt. %, or 7 wt. %, or 8 wt. %, or 9 wt. %, or 10 wt. %, or any range defined by any two of those endpoints.
In some examples, the at least one OSC polymer is present in a range of 1 wt. % to 99 wt. %; the at least one crosslinker is present in a range of 1 wt. % to 99 wt. %; and the at least one photoinitiator is present in a range of 0.1 wt. % to 10 wt. %. In some examples, the at least one OSC polymer is present in a range of 50 wt. % to 80 wt. %; and the at least one crosslinker is present in a range of 25 wt. % to 55 wt. %.
In some examples, the at least one antioxidant, lubricant, compatibilizer, leveling agent, or nucleating agent may each be present, independently, in a range of 0.05 wt. % to 5 wt. %, or in a range of 0.1 wt. % to 4.5 wt. %, or in a range of 0.2 wt. % to 4 wt. %, or in a range of 0.3 wt. % to 3.5 wt. %, or in a range of 0.4 wt. % to 3 wt. %, or in a range of 0.5 wt. % to 2.5 wt. %. In some examples, the at least one antioxidant, lubricant, compatibilizer, leveling agent, or nucleating agent may each be present, independently, at 0.05 wt. %, or 0.1 wt. %, or 0.2 wt. %, or 0.3 wt. %, or 0.4 wt. %, or 0.5 wt. %, or 0.6 wt. %, or 0.7 wt. %, or 0.8 wt. %, or 0.9 wt. %, or 1 wt. %, or 1.5 wt. %, or 2 wt. %, or 2.5 wt. %, or 3 wt. %, or 3.5 wt. %, or 4 wt. %, or 4.5 wt. %, or 5 wt. %, or any range defined by any two of those endpoints.
In some examples, the blend comprises at least two of: OSC polymers, crosslinkers, photoinitiators, and additives as described herein. In some examples, the blend comprises at least three of: OSC polymers, crosslinkers, photoinitiators, and additives as described herein. In some examples, the blend comprises at least four of: OSC polymers, crosslinkers, photoinitiators, and additives as described herein.
OTFT Device Fabrication
Applications using OTFT devices require patterning of organic semiconducting materials to prevent undesired high off-currents and crosstalk between adjacent devices. Photolithography is a common patterning technique in semiconductor device fabrication. However, photolithography usually involves harsh O2 plasma during pattern transfer or photoresist removal and aggressive developing solvents which may severely damage the OSC layer and lead to significant deterioration of OTFT device performance. In other words, conjugated organic materials tend to degrade when exposed to light and the chemicals used in photolithography may have an adverse effect on organic thin film transistors. Therefore, patterning of organic semiconducting materials using photolithography is not practical. Moreover, currently available patternable semiconducting polymers with photosensitive side groups require time-consuming molecule design and synthesis. These crosslinked polymers may also have adverse effect on OTFT devices, due to reduction of the effective conjugation of the polymer's crosslinked backbone.
The thin film 104 was prepared as a polymer blend described above comprising at least one organic semiconductor (OSC) polymer, at least one crosslinker, and optionally, at least one photoinitiator and at least one additive, wherein the at least one OSC polymer is a diketopyrrolopyrrole-fused thiophene polymeric material, wherein the fused thiophene is beta-substituted, and wherein the crosslinker includes at least one of: acrylates, epoxides, oxetanes, alkenes, alkynes, azides, thiols, allyloxysilanes, phenols, anhydrides, amines, cyanate esters, isocyanate esters, silyl hydrides, cinnamates, coumarins, fluorosulfates, silyl ethers, or a combination thereof.
In some examples, the blending includes dissolving the at least one OSC polymer in a first organic solvent to form a first solution, dissolving the at least one crosslinker in a second organic solvent to form a second solution, and dissolving at least one photoinitiator in a third organic solvent to form a third solution; and combining the first, second, and third solutions in any suitable order to create the polymer blend. In some examples, the first, second, and third solutions may be combined simultaneously. In some examples, the at least one OSC polymer, at least one crosslinker, and at least one photoinitiator may be prepared together in a single organic solvent. The weight compositions of each component of the polymer blend is as provided above.
In some examples, after the thin film of the blended OSC polymer is deposited over the substrate and before exposing the thin film to UV light, the thin film may be heated at a temperature in a range of 50° C. to 200° C. for a time in a range of 10 sec to 10 min to remove excess solvent.
In a second step (
In the step of
In some examples, after developing the patterned thin film in a solvent to remove the un-patterned region of the thin film, the thin film may be heated at a temperature in a range of 50° C. to 200° C. for a time in a range of 10 sec to 30 min.
Thereafter, the OTFT devices may be completed by forming a gate electrode over the substrate; forming a gate dielectric layer over the substrate; forming patterned source and drain electrodes over the gate dielectric layer; forming an organic semiconductor active layer over the and gate dielectric layer, and forming an insulator layer over the patterned organic semiconductor active layer. (
The embodiments described herein will be further clarified by the following examples.
Example 1 is based on the OFET structure as shown in
In a first step, predetermined amounts of linear alkyl-substituted DPP monomer (‘x’ mol), branched alkyl-substituted DPP monomer (‘y’ mol), and fused thiophene monomer (‘x’+‘y’ mol) are measured along with 2% Pd2(DBA)3 (e.g., catalyst) and 8% o-tolyl phosphine (e.g., ligand) into a 3-neck round bottom flask (“reaction vessel”), which is then vacuumed and filled with inert gas (e.g., N2, Ar, etc.). The reaction vessel is connected with a condenser and chlorobenzene (20 mL) is added to the vessel. A thermocouple is inserted into the reaction vessel and the reaction mixture is heated from room temperature to about 120° C. and stirred in an oil bath for about 1 hr to 2 hrs after the mixture reaches 120° C.
While the reaction mixture is still hot, it is poured directly into a stirred methanol container (300 mL). The empty reaction vessel is washed with methanol and added to the methanol container. Thereafter, concentrated HCl(aq)(4 mL) is added to the methanol container and the combination is mixed overnight. The resulting polymer is then filtered from solution using a Buchner funnel and side arm conical flask with reduced pressure, with the filtrate solution discarded. Then, the polymer is transferred into a Soxhlet thimble (with the polymer not exceeding half height of thimble) and loaded into a Soxhlet extraction apparatus. Polymer Soxhlet extraction is conducted with acetone (300 mL) for 24 hrs. The acetone solution and/or suspension is discarded thereafter.
Soxhlet extraction with hexane (300 mL) is conducted for 24 hrs, with the hexane solution and/or suspension is discarded thereafter. The polymer is then extracted into chloroform (300 mL) until its dissolution limit (i.e., no more material will dissolve). The polymer is precipitated by pouring the chloroform solution into a stirring beaker of acetone (400 mL), and then stirring the solution until it reaches room temperature. Finally, the polymer is filtered from the chloroform solution with a Buchner funnel and side arm conical flask at reduced pressure. The filtrate solution is discarded and the polymer is dried under vacuum.
Example 2 is based on the OFET structure as shown in
An organic semiconductor device is prepared comprising the cross-bred OSC polymer described herein. In some examples, a bottom gate, bottom contact OTFT device can be formed as following: patterning a gold (Au) or silver (Ag) gate electrode onto a substrate, followed by spin-coating a dielectric onto the substrate and treating to obtain a gate dielectric layer. After patterning Au or Ag source and drain electrodes, an OSC layer may be formed by the materials and methods of patterning as described herein to a thickness in a range of 10 nm to 200 nm. In some examples, p-xylene solvent was used to as the medium housing the cross-bred OSC polymer. In some examples, chlorobenzene solvent was used to as the medium housing the cross-bred OSC polymer. After forming the OSC layer, the structure was annealed. Finally, an insulator layer was positioned.
Example 3 is based on the OFET structure as shown in
The device as formed in Example 2 was tested, with the results shown in Table 3 below and
For example, in
Example 4 is based on the OFET structure as shown in
A first solution of cross-bred OSC polymers was prepared comprising a random copolymer of a first DPP-fused thiophene portion (having a first fused thiophene portion and a first linear alkyl-substituted DPP portion, e.g., Formula 5) and a second DPP-fused thiophene portion (having a second fused thiophene portion and a second branched alkyl-substituted DPP portion, e.g., Formula 4) in a relative high boiling point solvent (e.g., chlorobenzene, mesitylene, etc.) with the mole ratio between the first DPP-fused thiophene portion and the second DPP-fused thiophene portion in the copolymer being 3:7, respectively. Moreover, a second solution of non-cross-bred OSC polymers was prepared comprising the polymer of Formula 5 and the polymer of Formula 4 (i.e., each polymer existing distinctly) in the same or similar solvent as in the first solution at a mole ratio of 3:7 (polymer of Formula 5: polymer of Formula 4).
After stirring overnight at about 90° C. in an oil bath, a crosslinker as disclosed herein, was added to the first solution and the second solution in a suitable weight ratio to the cross-bred OSC polymers in the first solution or to the mixture of non-cross-bred polymers in the second solution. Thereafter, selectively, a suitable amount of second crosslinker was added to each the first and second solution and the resulting solution was stirred at room temperature for 20 minutes. A photoinitiator (3 wt. % relative to the cross-bred OSC polymers and the first crosslinker) was added into each solution and the mixture was stirred at room temperature for 2 hrs. A 0.45 μm PTFE filter was used to filter each solution.
The filtered solutions were each separately spun coated as a thin film coating onto a glass substrate, followed by baking at 90° C. Under a photo mask, the glass substrate comprising a film of the first solution and the glass substrate comprising a film of the second solution was cured at 365 nm using a UV lamp with a suitable curing dose. Thereafter, the glass substrates were washed sequentially with mixed solvents such as chlorobenzene/dioxane or chlorobenzene/anisole in different ratios for several times. The photo-patterned OSC polymer thin films on the glass substrates were dried with nitrogen gas.
Thus, as presented herein, improved UV patternable cross-bred OSC polymer blends and use thereof for OSC layers of organic thin-film transistors are disclosed.
Advantages of the UV patternable cross-bred OSC polymer blends include: (1) combining the virtues of multiple individual OSC polymers, each having only one type of donor/acceptor monomers, by forming a novel cross-bred OSC polymer (e.g.,
As utilized herein, the terms “approximately,” “about,” “substantially”, and similar terms are intended to have a broad meaning in harmony with the common and accepted usage by those of ordinary skill in the art to which the subject matter of this disclosure pertains. It should be understood by those of skill in the art who review this disclosure that these terms are intended to allow a description of certain features described and claimed without restricting the scope of these features to the precise numerical ranges provided. Accordingly, these terms should be interpreted as indicating that insubstantial or inconsequential modifications or alterations of the subject matter described and claimed are considered to be within the scope of the invention as recited in the appended claims.
As utilized herein, “optional,” “optionally,” or the like are intended to mean that the subsequently described event or circumstance can or cannot occur, and that the description includes instances where the event or circumstance occurs and instances where it does not occur. The indefinite article “a” or “an” and its corresponding definite article “the” as used herein means at least one, or one or more, unless specified otherwise.
References herein to the positions of elements (e.g., “top,” “bottom,” “above,” “below,” etc.) are merely used to describe the orientation of various elements in the FIGURES. It should be noted that the orientation of various elements may differ according to other exemplary embodiments, and that such variations are intended to be encompassed by the present disclosure.
With respect to the use of substantially any plural and/or singular terms herein, those having skill in the art can translate from the plural to the singular and/or from the singular to the plural as is appropriate to the context and/or application. The various singular/plural permutations may be expressly set forth herein for the sake of clarity.
It will be apparent to those skilled in the art that various modifications and variations can be made without departing from the spirit or scope of the claimed subject matter. Accordingly, the claimed subject matter is not to be restricted except in light of the attached claims and their equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201811307488.7 | Nov 2018 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/057301 | 10/22/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2020/096761 | 5/14/2020 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20100183820 | Seubert | Jul 2010 | A1 |
| 20130085256 | He | Apr 2013 | A1 |
| 20150206616 | He et al. | Jul 2015 | A1 |
| 20160155633 | Zhou | Jun 2016 | A1 |
| 20160222167 | He et al. | Aug 2016 | A1 |
| 20180244838 | Miyamoto et al. | Aug 2018 | A1 |
| 20180248122 | Otsuki | Aug 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 102010499 | Apr 2011 | CN |
| 103946275 | Jul 2014 | CN |
| 104703685 | Jun 2015 | CN |
| 105849170 | Aug 2016 | CN |
| 107406585 | Nov 2017 | CN |
| 107406586 | Nov 2017 | CN |
| 5355857 | Nov 2013 | JP |
| 0210129 | Feb 2002 | WO |
| 2002101129 | Dec 2002 | WO |
| 2017001823 | Jan 2017 | WO |
| Entry |
|---|
| Wang et al., “Inducing Elasticity through Oligo-Siloxane Crosslinks for Intrinsically Stretchable Semiconducting Polymers”, In Advanced Functional Materials, vol. 26, Issue 40, 2016, 25 pages. |
| Yao et al., “Significant Improvement of Semiconducting Performance of the Diketopyrrolopyrrole-Quaterthiophene Conjugated Polymer through Side-Chain Engineering via Hydrogen-Bonding”, in Journal of The American Chemical Society, Issue No. 138, 2016, 22 pages. |
| Zeng et al., “Solar Cells: Two-Dimensional Single-Layer Organic-Inorganic Hybrid Perovskite Semiconductors”, In Advanced Energy Materials, vol. 7, Issue 7, 2017, 7 pages. |
| International Search Report and Written Opinion of the International Searching Authority; PCT/US2019/057301; dated Feb. 10, 2020; 11 pages; European Patent Office. |
| Matthews et al., “Scalable Synthesis of Fused Thiophene-Diketopyrrolopyrrole Semiconducting Polymers Processed from Nonchlorinated Solvents into High Performance Thin Film Transistors”, Chemistry of Materials, vol. 25, No. 5, Mar. 12, 2013, pp. 782-789. |
| Rumer et al., “Organic photovoltaics: Crosslinking for optimal morphology and stability”, Materials Today, vol. 18, No. 8, Oct. 1, 2015, pp. 425-435. |
| Shin et al., “Bis(thienothiophenyl) Diketopyrrolopyrrole-Based Conjugated Polymers with Various Branched Alkyl Side Chains and Their Applications in Thin-Film Transistors and Polymer Solar Cells”, In ACS Applied Materials & Interfaces, vol. 7, No. 5, Jan. 28, 2015 pp. 3280-3288. |
| Yiu et al., “Side-Chain Tunability of Furan-Containing Low-Band-Gap Polymers Provides Control of Structural Order in Efficient Solar Cells” Journal of The American Chemical Society, vol. 134, No. 4, Dec. 22, 2011, pp. 2180-2185. |
| “Welcome to STN International”, STN on the Web, 2016, 4 pages. |
| Chinese Patent Application No. 201811307488.7, Office Action dated Apr. 29, 2023, 4 pages (English Translation only), Chinese Patent Office. |
| Taiwanese Patent Application No. 108138331, Search Report, dated Jul. 5, 2023, 1 page; Taiwanese Patent Office. |
| Number | Date | Country | |
|---|---|---|---|
| 20220006016 A1 | Jan 2022 | US |